Made available in DSpace on 2017-07-24T19:22:25Z (GMT). No. of bitstreams: 1 CRISTIAN HIGASHI.pdf: 3013347 bytes, checksum: 87da650524fbc43c80566136e07331cd (MD5) Previous issue date: 2012-12-07 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this study was to assess the push-out bond strength, nanohardness and Young’s modulus of three resin cements used for luting fiber post. The measurements were taken at cervical (CT), middle (MT) and apical (AT) radicular thirds, at immediate time and after one year of storage in water. Root canals of 57 human teeth were endodontically treated and prepared to cementation of fiber post (White Post DC - FGM) using the cementation systems: Multilink [MUL] (Ivoclar Vivadent), Variolink II + Excite DSC [VAR] (Ivoclar Vivadent) and R RelyXTM Unicem [UNC] (3M ESPE). For the push-out test (n=16), after 24hs of water storage at 37ºC, half the sample (n=8) was transversely sectioned into 6 slices, being 2 slices for each radicular third, which were assess d at 0,5 mm/min. The remaining half (N=8) was kept unsectioned in deionized water at 37ºC for 1 year, followed by sectioning and measuring. For the nanoindentation test, the cemented samples (n=3) were stored in water at 37ºC for 24hs and after were longitudinally sectioned to perform the initial measurements of hardness and elastic’s modulus from cervical to apex. These same samples were stored in deionized water at 37ºC for 1 year and reassessed. The data were analyzed by three-way ANOVA and Tukey’s test (α=0.05). The mean and standard deviation of MUL bond strength (MPa) in AT (19.9 ± 3.9) was higher than MT (15.1 ± 4.7) and CT (14.9 ± 4.2) (p=0.00007). The immediate bond strength of AT (22.0 ± 4.9) decreased significantly after 1 year of water storage (15.1 ±4.1) (p=0.006). The MUL cement obtained higher values of Young’s modulus (GPa) in CT (9.2 ± 1.9) when compared to MT (6.6 ± 2.0) e AT (5.4 ± 2.6)(p=0.01). The AT has the lowest values of hardness (GPa) (0.40 ± 0.10) when compared to MT (0.45 ± 0.12) and CT (0.48 ± 0.11) (p=0.000001). The initial hardness of UNC cement (0.43 ± 0.12) decreased after 1 year of storage in water (0.35 ± 0.14) (p=0.0051). It was concluded that: 1) The bond strength of MUL cement was higher in AT, 2) The AT of the cements suffered higher bond degradation after 1 year of storage water, 3) The Young’s modulus of MUL cement was higher in CT, 4) The AT of all cements had lowest hardness values, 5) After 1 year of storage in water, the UNC cement had a significant decreased of hardness values. / O objetivo deste trabalho foi avaliar a resistência de união, nanodureza e módulo de elasticidade de 3 cimentos resinosos utilizados para cimentar pinos de fibra de vidro. As mensurações foram feitas nos terços cervical [TC], médio [TM] e apical [TA] das raízes, no tempo imediato e após 1 ano de armazenamento em água destilada. Os canais radiculares de 57 dentes humanos unirradiculares foram tratados endodonticamente e preparados para a cimentação dos pinos de fibra de vidro White Post DC (FGM) utilizando os sistemas de cimentação Multilink [MUL] (Ivoclar Vivadent), Variolink II + Excite DSC [VAR] (Ivoclar Vivadent) e RelyXTM Unicem [UNC] (3M ESPE). Para o teste de push-out (n=16), após 24hs de armazenamento em água destilada à 37ºC, metade das amostras (n=8) foram cortadas transversalmente em 6 fatias, sendo 2 fatias para cada terço radicular, que foram testadas à velocidade de 0,5 mm/min. A outra metade das amostras cimentadas (n=8) foram mantidas íntegras em água destilada à 37ºC por 1 ano, seguidos pelos cortes e mensurações. Para o teste de nanoindentação, as amostras cimentadas (n=3) foram armazenadas em água à 37ºC por 24hs e logo após, cortadas longitudinalmente aos seus longos eixos para a realização das mensurações iniciais de nanodureza e módulo de elasticidade do TC até TA. Estas mesmas amostras foram armazenadas em água destilada à 37ºC por 1 ano e retestadas. Os dados foram submetidos a uma análise de variância de três critérios e ao teste de Tukey (α=0,05). A média e desvio padrão dos valores de resistência de união (MPa) do cimento MUL no TA (19,9 ± 3,9) foi maior do que no TM (15,1 ± 4,7) e TC (14,9 ± 4,2) (p=0,00007). A resistência de união imediata do TA (22,0 ± 4,9) diminuiu significativamente após 1 ano de armazenamento em água (15,1 ± 4,1) (p=0,006). O cimento MUL obteve maiores valores de módulo de elasticidade (GPa) no TC (9,2 ± 1,9) em compara ão ao TM (6,6 ± 2,0) e TA (5,4 ± 2,6) (p=0,01). O TA radicular teve os menores valores de nanodureza (GPa)(0,40 ± 0,10) quando comparado com os TM (0,45 ± 0,12) e TC (0,48 ± 0,11) (p=0,000001). A nanodureza inicial do cimento UNC (0,43 ± 0,12) diminui após 1 ano de armazenamento em água (0,35 ± 0,14) (p=0,0051). Concluiuse que: 1) A resistência do cimento MUL foi maior no TA; 2) O TA dos cimentos sofreu uma maior degradação da união após o armazenamento de 1 ano em água; 3) O módulo de elasticidade do cimento MUL foi maior no TC; 4) O TA de todos os cimentos teve menores valores de dureza; 5) O cimento UNC teve uma diminuição significativa dos valores de nanodureza após 1 ano de ar azenamento em água. Palavras-chave: Cimento resinoso. Pino de fibra. Dentina radicular.

Coroas cerâmicas apoiadas sobre infra-estruturas de alumina densamente sinterizada configuram-se como excelentes opções para a reabilitação protética em casos de exigência estética, contudo, o aumento do conteúdo cristalino inviabiliza seu condicionamento por ácidos deixando a maneira ideal de cimentá-las ainda desconhecida. Coroas Procera AllCeram apresentam, em sua face interna, micro irregularidades interessantes ao embricamento e adesão resinosa, dispensando manobras de condicionamento. Objetivo: O objetivo deste trabalho foi avaliar a influência de elevadas temperaturas (500ºC à 950ºC) necessárias à cocção da porcelana de revestimento, na textura superficial da alumina, bem como o papel de um agente primer (Ivoclar Vivadent) na força de adesão entre alumina e cimento resinoso. Material e métodos: Sessenta (60) cilindros de alumina (3,5mm X 16mm) com rugosidade superficial idêntica à dos copings Procera foram divididos em quatro grupos (n=15). Grupo 1): Espécimes não submetidos a variação térmica, sendo G1a Sem aplicação do primer e G1b Com aplicação do primer e Grupo 2): Espécimes submetidos aos ciclos térmicos para cocção da porcelana feldspática, sendo G2a Sem aplicação do primer e G2b Com aplicação do primer. Sobre os cilindros aplicou-se porção do cimento resinoso químico MultiLink Ivoclar. Os espécimes foram levados a uma máquina de ensaios Universal para teste de cisalhamento a uma velocidade de 0.5mm/min e os dados submetidos à análise de variância a um critério e teste de comparações múltiplas de Tukey. Resultados: A força de adesão para cada um dos grupos foi: G1a = 2.468 MPa; G1b = 4.265 MPa; G2a = 2.339MPa e G2b = 4.185 MPa. Diferenças significantes foram observadas entre os grupos: G1a X G1b; G1a X G2b; G1b X G2a e G2a X G2b. Conclusões: Ciclos térmicos não produziram alterações na micro-estrutura superficial da alumina, tampouco comprometeram sua adesão ao cimento. O agente primer aumentou a força de união entre alumina e cimento resinoso. Fraturas coesivas do agente cimentante foram observadas apenas em alguns espécimes primer-tratados. / High-strength alumina based ceramic crowns are widely used in dentistry due to their favorable esthetic, however, the large amount of crystalline contents jeopardizes their acid etching property and the ideal luting remains unclear. Procera AllCeram restorations exhibits on their intaglio surface micro irregularities optimizing the bonding to resin, with no need for additional conditioning procedures. Purpose: The aim of the present study was to evaluate the influence of high thermal cycles (500ºC to 950ºC) needed to porcelain firing on alumina´s intaglio surface, as well as, the role of a primer agent (Ivoclar Vivadent) on shear bond strength between alumina and resin cement. Material and Methods: Sixty alumina cylinders (3,5mm X 16mm) with intaglio roughness of the Procera AllCeram copings were randomly divided into four groups (n=15). Group 1) Samples no submitted to thermal cycles variation, were G1a - no primer application and G1b - primer treated and Group 2: Samples submitted to thermal feldspathic porcelain firing cycles, were G2a - specimens no primer treated and G2b - primer treated specimens. Over the cylinders top a self-cure resin cement (Multilink Ivoclar) portion was applied. The specimens were loaded to failure in shear mode using a universal testing machine at a crosshead speed of 0,5mm/min. Data were analyzed with one-way analysis of variance and Tukey´s multiple comparison test. Results: The shear bond strength for each group was: G1a = 2.468 MPa; G1b = 4.265 MPa; G2a = 2.339 MPa e G2b = 4.185 MPa. Significant difference was found between the groups G1a X G1b; G1a X G2b; G1b X G2a e G2a X G2b. Conclusions: Thermal cycles did not change alumina´s surface micro structure, besides did not compromised it´s bonding strength to resin cement. Primer agent enhanced shear bond strength between alumina and resin cement. Luting agent´s cohesive fractures were observed only in some primer treated specimens.

Este estudo avaliou, in vitro, a influência da radioterapia na resistência de união (RU) e na interface adesiva entre diferentes cimentos resinosos e dentina radicular. Sessenta caninos superiores foram distribuídos em 2 grupos (n=30) de acordo com a irradiação: não irradiados e irradiados. Os dentes do grupo irradiado foram submetidos à radioterapia com raios-X de 6 MV em frações de 2 Gy, com 30 ciclos, perfazendo 60 Gy. Os dentes foram seccionados para obtenção de raízes com 16 mm de comprimento, sendo realizado em seguida o preparo biomecânico com instrumento Reciproc R50 e obturação pela técnica de condensação lateral com cimento a base resina epóxica. Cada grupo foi subdividido de acordo com o cimento resinoso utilizado para a cimentação dos pinos de fibra de vidro (n=10): RelyX U200; Panavia F 2.0; RelyX ARC. Os pinos foram submetidos a tratamento de superfície com ácido fluorídrico 10% e cimentados de acordo com as recomendações de cada fabricante. Após a cimentação dos pinos, os dentes foram seccionados transversalmente em slices de 1 mm de espessura, obtendo-se 3 slices de cada terço da raiz. Os slices mais cervicais de cada terço foram utilizados para avaliar a RU, por meio do teste de push-out com velocidade de 0,5 mm/min, e posterior análise do padrão de falha em estereomicroscópio. Os slices mais apicais de cada terço foram selecionados para análise da interface cimento/dentina em MEV com aumentos de 100, 1000, 2000 e 4000X. Os dados de RU e adaptação da interface cimento/dentina foram submetidos à análise estatística pelos testes de ANOVA e Tukey, e Kruskal-Wallis e Duns, respectivamente. Os espécimes irradiados apresentaram menores valores de RU (8,23&plusmn;4,26) comparados aos dentes não irradiados (11,88&plusmn;6,42) (p<0,00001). Quanto aos cimentos resinosos, o RelyX U200 apresentou maiores valores na RU (15,17&plusmn;5,89) comparado aos cimentos RelyX ARC (7,68&plusmn;4,22) (p<0,0001) e Panavia F 2.0 (7,32&plusmn;2,71) (p<0,0001). O terço cervical apresentou maiores valores de RU (13,08&plusmn;6,10) comparado aos terços médio (9,72&plusmn;5,03) e apical (7,38&plusmn;4,53) (p<0,0001). O padrão de falhas mostrou ocorrência de falhas coesivas na dentina para os espécimes irradiados. Na análise da interface cimendo/dentina por MEV, observou-se maior desadaptação nos dentes submetidos à radioterapia. Em relação aos cimentos resinosos, foi observada maior adaptação com RelyX U200 e RelyX ARC comparados à Panavia F 2.0. Na análise qualitativa em MEV observou-se presença de fraturas e microfraturas na dentina radicular e menor presença de fibras colágenas em dentes irradiados. Para o cimento resinoso RelyX U200 e Panavia F 2.0 observou-se interface justaposta do cimento com a dentina radicular em dentes irradiados e não irradiados, sendo que para o cimento resinoso RelyX ARC foi observada formação de camada híbrida e tags de maneira similar para dentes irradiados e não irradiados. Concluiu-se que a radioterapia resultou na redução da resistência de união e na maior desadaptação da interface cimento resinoso/dentina radicular e que o cimento resinoso autoadesivo se apresentou como melhor alternativa para cimentação de pinos de fibra de vidro em dentes irradiados. / This in vitro study, evaluated the influency of radiotherapy on bond strength (BS) and adhesive interface between different resin cements and root dentin. Sixty maxillary canines were selected and distributed into two groups (n = 30) according to the irradiation protocol: non-irradiated and irradiated. The irradiated group were submitted to X-ray radiotherapy of 6 MV in fractions of 2 Gy, with 30 cycles, until complete 60 Gy. The teeth were sectioned to obtain 16 mm of root length, followed by biomechanical preparation with R50 reciproc instrument and obturation using the lateral condensation technique with epoxy resin-based sealer. Then, each group was subdivided according to the resin cement used for the glass fiber post cementation (n = 10): RelyX U200, Panavia F 2.0 and RelyX ARC. The posts were submitted to surface treatment with 10% hydrofluoric acid, and then cemented according to the manufacturer instructions. After the posts cementation, the teeth were sectioned transversely into 1 mm thick slices, and 3 slices were obtained from each root third. The most cervical slice of each third was used to evaluate the BS by the push-out test at 0.5 mm/min of velocity and the failure pattern was analyzed using stereomicroscopy. The most apical slice of each third was selected for SEM analysis, which were prepared and metalized. The dentin/cement interface analysis was performed at the following magnification: 100, 1000, 2000 and 4000X. The BS data and dentin/cement interface adaptation were submitted to statistical analysis by ANOVA, Tukey and Kruskal-Wallis, and Duns tests respectively. The irradiated specimens had lower BS values (8.23 &plusmn; 4.26) compared to non-irradiated group (11.88 &plusmn; 6.42) (p <0.00001). Regarding the resin cements, the RelyX U200 showed the higher values in BS (15.17 &plusmn; 5.89) compared to RelyX ARC (7.68 &plusmn; 4.22) and Panavia F 2.0 (7 , 32 &plusmn; 2.71) (p <0.0001). In addition, the cervical third presented higher BS values (13.08 &plusmn; 6.10) when compared to the middle (9.72 &plusmn; 5.03) and apical (7.38 &plusmn; 4.53) thirds (p <0.0001). The failure pattern showed cohesive failures in root dentin of the irradiated specimens. In the SEM dentin/cement interface analysis, a greater misadaptation was observed for the teeth submitted to radiotherapy. Regarding the resin cements, a better adaptation was observed for the RelyX U200 and RelyX ARC compared to the Panavia F 2.0. In the SEM qualitative analysis of the irradiated teeth, was possible to observe the presence of fractures and microfractures in the root dentin and a small number of collagen fibers. The resin cements RelyX U200 and Panavia F 2.0 showed a juxtaposed interface of the cement with the root dentin in irradiated and non-irradiated teeth, being that for the RelyX ARC cement the presence of hybrid layer and tags was similar for irradiated and non-irradiated groups. It was concluded that the radiotherapy promoted reduction of the bond strength and increase the gaps in the dentin/resin cement interface and the self-adhesive resin cement is the best alternative for glass fiber posts cementation in irradiated teeth.

Objetivos: o presente estudo teve como objetivo determinar a aplicabilidade e eficácia adesiva de diferentes monômeros ácidos quando aplicados em formulações de cimentos resinosos autoadesivos experimentais sob o grau de conversão, propriedades físico-químicas e resistência de união à dentina e à zircônia tetragonal policristalina estabilizada por ítrea (Y-TZP), após um período de 3 meses de armazenamento em água. Material: dois tipos de cimentos do tipo pasta-pasta foram formulados contendo monômeros convencionais UDMA, HEMA, BISGMA, TEGDMA e monômeros ácidos 2MP e GDMAP como matriz orgânica. Um grupo contendo apenas monômeros convencionais foi formulado como grupo controle. Os componentes canforoquinona/EDMAB e peróxido de benzoíla/DHPT foram empregados como sistema de ativação dual. O sal sódico do ácido benzenosulfônico 98% (BAS) foi incorporado nos grupos experimentais. Partículas de carga foram incorporadas na proporção ±55% em peso final. Método: A técnica de espectroscopia no infravermelho (FT-IR) foi empregada para análise do grau de conversão (n=3) imediato e após 24 h. A avaliação do pH (n=3) foi feita através do emprego de um equipamento medidor de pH. Os corpos de provas foram imersos em água destilada e o pH foi analisado de forma imediata e após 5 min, 24 h e 48 h. Os testes de sorção e solubilidade (n=6) e espessura de película (n=5) seguiram as recomendações da ISO 4049. A análise de resistência de união (n=12) foi realizada em dentina e Y-TZP, através do teste de cisalhamento em área reduzida após um protocolo de envelhecimento em água destilada por 3 meses. No caso da Y-TZP, metade dos espécimes receberam um tratamento superficial cojet (30 ?m), associado a aplicação de um agente de união silano. O padrão de fratura foi analisado com o auxílio de um estereomicroscópio. Resultados: O grupo controle (91,7%) e o grupo formulado com 2MP (92%) apresentaram superiores valores de grau de conversão em relação ao grupo GDMAP (77,7%). O pH dos grupos experimentais 2MP e GDMAP se apresentou mais ácido após 48 h em comparação ao grupo controle. Em contrapartida, esses grupos experimentais apresentaram uma maior sorção e solubilidade em relação ao grupo controle. A espessura da película formada foi semelhante em todos os grupos testados (p=0,266). Em dentina o grupo controle (27,0 MPa) e GDMAP (24,1 MPa) não apresentaram diferença estatística após 3 meses de estocagem. O grupo 2MP (13,7 MPa) apresentou resultados inferiores aos demais grupos. O tratamento de superfície empregado não foi capaz de manter ou de elevar os valores de resistência de união à Y-TZP após o período de envelhecimento em água. Todos os grupos experimentais apresentaram falhas precoces ou baixos valores de resistência de união após 3 meses, independente da presença ou não do tratamento de superfície. Conclusão: os grupos experimentais 2MP e GDMAP apresentaram resultados promissores. Entretanto, a adesão dos CRAs experimentais testados em Y-TZP ainda se apresenta frágil e instável. / Objectives: the purpose of this study was to evaluate the applicability and adhesive efficiency of different acid monomers utilized in formulations of experimental self-adhesive resin cement under degree of conversion, physico-chemical properties and bond strength to dentin and Y-TZP after 3 months aging period. Materials: two paste-paste luting agents were formulated containing UDMA, HEMA, BISGMA, TEGDMA and acid adhesive monomers 2MP and GDMAP as organic matrix. The control group was formulated containing only conventional monomers. Camphoroquinone/EDMAB and benzoyl peroxide/DHPT were used as dual activation system. BAS salt was incorporated into the experimental groups. Filler particles were added in a proportion of ±55% final weight. Method: Infrared spectroscopy technique (FTIR) was employed for degree of conversion analysis (n=3) immediately and after 24 hours. The pH assessment (n=3) was made using a pH meter. All the specimens were immersed in distilled water and pH assessment was performed immediately and after 5 min, 24 h and 48 h. Tests for sorption and solubility (n=6) and thickness (n=6) were carried out according to ISO 4049 recommendations. Bond strength analysis (n=12) was performed in dentin and Y-TZP through microshear after an aging 3 months protocol in distilled water. Regarding Y-TZP, half of the specimens were submitted to a cojet surface treatment (30 ?m) in association to silane bonding agent application. Fracture toughness standard was evaluated with the assistance of a stereomicroscope. Results: The control (91,7%) and 2MP (92%) groups presented higher degree of conversion than GDMAP group (77,7%). The 2MP and GDMAP experimental groups showed the highest pH compared to control group. In contrast, experimental groups showed a high hydrolytic degradation. The thickness of the formed film was similar among all the tested groups (p=0,266). Regarding the dentin, control and GDMAP groups had statistically similar bond strength (27,0 and 24,1 MPa respectively) after 3 months storage. While 2MP group (13,7 MPa) showed lower results compared the other groups. The surface treatment employed was not capable to maintain or elevate bond strength to Y-TZP results after the aging period in water. All experimental groups showed low bond strength values and even early failures after 3 months, regardless the surface treatment or its abscence. Conclusion: the experimental groups 2MP and GDMAP presented promising results. However, chemical adhesion to Y-TZP still remains weak and instable.

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-06-19Bitstream added on 2014-06-13T20:58:53Z : No. of bitstreams: 1 carvalho_cf_me_sjc.pdf: 1809025 bytes, checksum: bd4ee4f9a60dfdd8304d67de208703e4 (MD5) / O objetivo deste estudo foi avaliar e comparar a adaptação marginal de restaurações, confeccionadas em dois tipos de sistemas cerâmicos: CEREC inLab (VITA) e IPS Empress 2 (Ivoclar-Vivadent) , após a cimentação com cimento resinoso RelyX (3M). Foram preparados 20 pré-molares humanos com cavidade MOD inlay, reproduzidos com silicone de adição, e obtidos modelos em gesso tipo IV, sobre os quais foram confeccionadas as restaurações conforme as recomendações dos fabricantes. Dez inlays no sistema IPS Empress 2 e 10 inlays no sistema CEREC inLab. As restaurações foram cimentadas sob pressão constante de 1,5 Kgf por 10 min, com cimento resinoso, com pré-tratamento. As desadaptações marginais foram avaliadas em MEV, com magnificação de 200x, em 50 pontos eqüidistantes. As médias foram analisadas pelo teste estatístico t(Student) de amostras dependentes.Resultando em uma diferenca estatisticamente significante entre as desadaptaçoes marginais no sistema IPS Empress (93,8'mais ou menos'15,5'mü'm)que se mostraram menores que no sistema CEREC inLab (114,4'mais ou menos'10,6'mü'm). Quando se comparou os valores médios entre as faces proximais (116,51.21,85'mü') e oclusal (112,26'mais ou menos'8,49'mü) do sistema Cerec Inlab, e faces proximais (87,12'mais ou menos'27,98,'mü') e oclusal (100,47'mais ou menos'22,23'mü')do sistema IPS Empress 2, verifica-se que esses valores não diferem estatisticamente. Ainda assim, conclui-se que as médias obtidas são aceitavéis clinicamente. / This study has the proposal to evaluate the marginal adaptation of two system all-ceramic class II inlays one of laboratory-made heat-pressed ceramics (IPS Empress 2) and other computer-aided manufacturing ( CEREC inLab) after cementation with resin cement . Extracted human premolars were prepared to receive mesio occluso distal (MOD) ceramic inlays for 10 IPS Empress restorations and 10 CEREC inLab restorations. The impression material used was a polivinilsyloxane addition silicone by the double impression technique. The impressions of prepared teeth were cast in type IV dental stone. The restaurations were made following the manufacturer's recommendations. The inlays were luted on human premolars with resin cement in accordance with the manufacturer's recommended pré-treatment. The marginal gaps were investigated scanning electron microscopy with magnification of 200x. The results were analyzed by t (student) statistic test.The means marginal gap for IPS Empress 2 wal 93,8'mais ou menos'15,5'mü'm significantly smaller than that od 114,4'mais ou menos'10,6'mü'm calculated a the CEREC in Lab system.The gaps of the inlays at the occlusal margin and of the approximal margin showed no significantly differences in two system. It may be concluded that mensuarement value are clinically acceptable.

The current study aimed to evaluate the effect of irrigating and chelating solutions on bond strength of fiber glass posts cemented with RelyX U200. 60 single-rooted premolars were sectioned at 14 mm from the apex, prepared with ProTaper Universal system until F3 instrument and filled with F3 master cone and AH Plus sealer. Root canal filling was partially removed, remaining 4 mm of guta-percha at the apical third. Specimens were randomly divided into 5 experimental groups (n=12), according to the solution used before fiber post cementation (dentin surface treatment), as described: EDTA 17% (EDTA); QMix (QM); SmearClear (SC); NaOCl 2.5% (NaOCl) and saline solution as control group (SS). Ultrasonic activation was performed three times, during 20 seconds each and root canals were dried with paper points. Exacto N2 glass fiber posts were cemented with RelyX U200. Rhodamine B dye was mixed to RelyX U200 in one specimen per group, in order to provide fluorescence for confocal laser scanning microscopy (CLSM) assessment. A cutting machine was used for root s sectioning, providing 3 slices, one for each root third. Next, push-out test was performed. Stereomicroscope and CLSM were used to analyze the failure mode and to illustrate the pattern of distribution of RelyX U200 inside dentinal tubules, respectively. Bond strength mean were calculated and ANOVA and Bonferroni tests were used for statistical analysis. SS showed the higher mean of bond strength values, superior to QM, SC (P < .05). NaOCl presented intermediary bond strength values, similar to EDTA and SS (P > .05). QM and SC showed the lowest mean of bond strength (P < .05). In conclusion, SS and NaOCl associated to ultrasonic activation seems to be adequate solutions for root canal cleaning before fiber post cementation with RelyX U200, while chelating solutions, such as EDTA, QMix and SmearClear, should not be used for dentin pre-treatment when cementing with RelyX U200. / O presente estudo tem por objetivo avaliar o efeito de diferentes soluções irrigantes e quelantes na resistência adesiva de pinos de fibra de vidro cimentados com cimento autoadesivo RelyX U200. 60 pré-molares inferiores extraídos de humanos, padronizados em 14 mm, foram preparados com o sistema ProTaper Universal até o instrumento F3, obturados com cimento AH Plus e cones F3 do mesmo sistema. Os espécimes foram desobturados parcialmente, restando 4 mm apicais de material obturador e realocados em quatro grupos experimentais e um controle (n=12), de acordo com a solução de tratamento de superfície dentinária prévia à cimentação dos pinos: EDTA 17% (EDTA), QMix (QM), SmearClear (SC), Soro Fisiológico (SS) e NaOCl 2,5% (NaOCl). As soluções foram ativadas por ultrassom em três etapas, durante 20 segundos cada e os canais foram secos com pontas de papel absorventes. Os pinos de fibra de vidro do Sistema Exacto Translúcido N2 foram cimentados com RelyX U200. Em um espécime por grupo foi incorporada Rodamina B ao cimento autoadesivo como marcador fluorescente para análise em Microscopia Confocal à laser (MECL). Foram seccionados 3slices por espécime, sendo 1 slice por terço radicular, e submetidos ao teste de push-out na máquina de ensaio universal EMIC. Estereomicroscópio e MECL foram utilizados para analisar o padrão de falha dos espécimes e o padrão de penetração do cimento autoadesivo nos túbulos dentinários, respectivamente. A média de resistência adesiva de cada espécime foi calculada. Testes ANOVA e Bonferroni foram utilizados para analisar as diferenças entre os grupos. SS demonstrou a maior média de resistência adesiva, sendo superior aos grupos QM, SC (P <.05). NaOCl apresentou valores intermediários de resistência adesiva, similares ao EDTA e SS (P > .05). QM e SC apresentaram as menores médias de resistência adesiva (P < .05). Pode-se concluir que o uso de SS e NaOCl parece ser adequado para lavagem do canal prévia à cimentação de pinos de fibra de vidro, com uso de cimento resinoso autoadesivo RelyX U200. O uso de soluções quelantes como EDTA, QM e SC parece interferir negativamente nos valores de resistência adesiva.

Este estudo avaliou, in vitro, a influência da radioterapia na resistência de união (RU) e na interface adesiva entre diferentes cimentos resinosos e dentina radicular. Sessenta caninos superiores foram distribuídos em 2 grupos (n=30) de acordo com a irradiação: não irradiados e irradiados. Os dentes do grupo irradiado foram submetidos à radioterapia com raios-X de 6 MV em frações de 2 Gy, com 30 ciclos, perfazendo 60 Gy. Os dentes foram seccionados para obtenção de raízes com 16 mm de comprimento, sendo realizado em seguida o preparo biomecânico com instrumento Reciproc R50 e obturação pela técnica de condensação lateral com cimento a base resina epóxica. Cada grupo foi subdividido de acordo com o cimento resinoso utilizado para a cimentação dos pinos de fibra de vidro (n=10): RelyX U200; Panavia F 2.0; RelyX ARC. Os pinos foram submetidos a tratamento de superfície com ácido fluorídrico 10% e cimentados de acordo com as recomendações de cada fabricante. Após a cimentação dos pinos, os dentes foram seccionados transversalmente em slices de 1 mm de espessura, obtendo-se 3 slices de cada terço da raiz. Os slices mais cervicais de cada terço foram utilizados para avaliar a RU, por meio do teste de push-out com velocidade de 0,5 mm/min, e posterior análise do padrão de falha em estereomicroscópio. Os slices mais apicais de cada terço foram selecionados para análise da interface cimento/dentina em MEV com aumentos de 100, 1000, 2000 e 4000X. Os dados de RU e adaptação da interface cimento/dentina foram submetidos à análise estatística pelos testes de ANOVA e Tukey, e Kruskal-Wallis e Duns, respectivamente. Os espécimes irradiados apresentaram menores valores de RU (8,23&plusmn;4,26) comparados aos dentes não irradiados (11,88&plusmn;6,42) (p<0,00001). Quanto aos cimentos resinosos, o RelyX U200 apresentou maiores valores na RU (15,17&plusmn;5,89) comparado aos cimentos RelyX ARC (7,68&plusmn;4,22) (p<0,0001) e Panavia F 2.0 (7,32&plusmn;2,71) (p<0,0001). O terço cervical apresentou maiores valores de RU (13,08&plusmn;6,10) comparado aos terços médio (9,72&plusmn;5,03) e apical (7,38&plusmn;4,53) (p<0,0001). O padrão de falhas mostrou ocorrência de falhas coesivas na dentina para os espécimes irradiados. Na análise da interface cimendo/dentina por MEV, observou-se maior desadaptação nos dentes submetidos à radioterapia. Em relação aos cimentos resinosos, foi observada maior adaptação com RelyX U200 e RelyX ARC comparados à Panavia F 2.0. Na análise qualitativa em MEV observou-se presença de fraturas e microfraturas na dentina radicular e menor presença de fibras colágenas em dentes irradiados. Para o cimento resinoso RelyX U200 e Panavia F 2.0 observou-se interface justaposta do cimento com a dentina radicular em dentes irradiados e não irradiados, sendo que para o cimento resinoso RelyX ARC foi observada formação de camada híbrida e tags de maneira similar para dentes irradiados e não irradiados. Concluiu-se que a radioterapia resultou na redução da resistência de união e na maior desadaptação da interface cimento resinoso/dentina radicular e que o cimento resinoso autoadesivo se apresentou como melhor alternativa para cimentação de pinos de fibra de vidro em dentes irradiados. / This in vitro study, evaluated the influency of radiotherapy on bond strength (BS) and adhesive interface between different resin cements and root dentin. Sixty maxillary canines were selected and distributed into two groups (n = 30) according to the irradiation protocol: non-irradiated and irradiated. The irradiated group were submitted to X-ray radiotherapy of 6 MV in fractions of 2 Gy, with 30 cycles, until complete 60 Gy. The teeth were sectioned to obtain 16 mm of root length, followed by biomechanical preparation with R50 reciproc instrument and obturation using the lateral condensation technique with epoxy resin-based sealer. Then, each group was subdivided according to the resin cement used for the glass fiber post cementation (n = 10): RelyX U200, Panavia F 2.0 and RelyX ARC. The posts were submitted to surface treatment with 10% hydrofluoric acid, and then cemented according to the manufacturer instructions. After the posts cementation, the teeth were sectioned transversely into 1 mm thick slices, and 3 slices were obtained from each root third. The most cervical slice of each third was used to evaluate the BS by the push-out test at 0.5 mm/min of velocity and the failure pattern was analyzed using stereomicroscopy. The most apical slice of each third was selected for SEM analysis, which were prepared and metalized. The dentin/cement interface analysis was performed at the following magnification: 100, 1000, 2000 and 4000X. The BS data and dentin/cement interface adaptation were submitted to statistical analysis by ANOVA, Tukey and Kruskal-Wallis, and Duns tests respectively. The irradiated specimens had lower BS values (8.23 &plusmn; 4.26) compared to non-irradiated group (11.88 &plusmn; 6.42) (p <0.00001). Regarding the resin cements, the RelyX U200 showed the higher values in BS (15.17 &plusmn; 5.89) compared to RelyX ARC (7.68 &plusmn; 4.22) and Panavia F 2.0 (7 , 32 &plusmn; 2.71) (p <0.0001). In addition, the cervical third presented higher BS values (13.08 &plusmn; 6.10) when compared to the middle (9.72 &plusmn; 5.03) and apical (7.38 &plusmn; 4.53) thirds (p <0.0001). The failure pattern showed cohesive failures in root dentin of the irradiated specimens. In the SEM dentin/cement interface analysis, a greater misadaptation was observed for the teeth submitted to radiotherapy. Regarding the resin cements, a better adaptation was observed for the RelyX U200 and RelyX ARC compared to the Panavia F 2.0. In the SEM qualitative analysis of the irradiated teeth, was possible to observe the presence of fractures and microfractures in the root dentin and a small number of collagen fibers. The resin cements RelyX U200 and Panavia F 2.0 showed a juxtaposed interface of the cement with the root dentin in irradiated and non-irradiated teeth, being that for the RelyX ARC cement the presence of hybrid layer and tags was similar for irradiated and non-irradiated groups. It was concluded that the radiotherapy promoted reduction of the bond strength and increase the gaps in the dentin/resin cement interface and the self-adhesive resin cement is the best alternative for glass fiber posts cementation in irradiated teeth.

Este estudo comparou a performance de quarto agentes cimentantes com diferentes estratégias adesivas para cimentação de pinos de fibra de vidro em canais radiculares, através do teste de resistência adesiva e avaliando a dureza em diferentes profundidades. Para isto, foram utilizadas 60 raízes bovinas tratadas endodonticamente. Foram cimentados pinos de fibra de vidro Rebilda Post 20 de acordo com os seguintes protocolos divididos nos seguintes grupos: Grupos QM: Adesivo autocondicionante dual Futurabond DC + cimento resinoso dual Bifix QM; Group SE: Cimento resinoso autocondicionante de polimerização dual Bifix SE; Group RB: Adesivo autocondicionante de polimerização dual Futurabond DC + Resina Rebilda; Group XB: aplicação do adesivo autocondicionante de polimerização dual Futurabond DC + resina composta do tipo \"bulk fill\" X-tra Base. As raízes foram cortadas em fatias de 1mm e separadas em terços, sendo obtidos 2 corpos de prova por terço. Foram avaliadas a resistência adesiva (n=10) e a microdureza (n=5), após uma semana e após 4 meses de armazenamento em água. Para o teste de resistência adesiva (push- out) uma fatia de cada terço foi testada depois de uma semana e as outras 3 fatias provenientes do mesmo dente avaliadas após 4 meses. O ensaio de push out foi realizado a uma velocidade de 0,5mm/min até o deslocamento do pino e/ou fratura da interface adesiva. Para o teste de microdureza 20 dentes foram selecionados aleatoriamente e de cada dente foram obtidas seis 6 fatias que foram armazenadas em água destilada por uma semana até a mensuração em microdurômetro, após uma semana e após 4 meses. Os corpos de prova foram submetidos ao teste de microdureza Knoop em microdurômetro HMV-2000 (Shimadzu, Tokyo, Japan), cinco endentações foram realizadas na camada de cimento de cada fatia. Os dados referentes aos testes de resistência adesiva (push- out) e microdureza foram submetidas análise de variância 3 fatores (ANOVA), teste de tukey (p<0,05) e teste de correlação de Person. Os valores de resistência adesiva não apresentaram diferenças estatísticas significantes quando observado os valores de resistência adesiva entre os grupos QM, RB e XB (p>=0.05), porém menores valores de resistência adesiva foram observados no Grupo SE. Quando considerada a variável envelhecimento não foram encontradas diferenças na resistência adesiva medida em uma semana e 4 meses (p>=0.05). Para a microdureza diferenças estatisticamente significantes foram encontradas nos diferentes terços da raiz (p<0.05). Os agentes cimentantes apresentaram diferenças estatísticas significantes na dureza (p<0.05). O grupo XB apresentou os maiores valores seguido por QM, RB e SE. Os grupos SE, RB e XB não apresentaram 80% da dureza máxima nas fatias correspondentes a região apical do canal radicular. O teste de Person mostrou haver correlação positiva linear entre a resistência adesiva e a dureza medidas antes e após o envelhecimento. O uso cimento resinoso dual, associado a uma aplicação anterior do sistema adesivo, ainda é a escolha mais segura, pois apresentou valores de força de adesão elevados, associados a valores de dureza adequados, mesmo em regiões apicais do canal radicular. / This study compared the performance of four cementitious agents with different adhesive strategies for cementing fiberglass pins in root canals, through the adhesive strength test and evaluating the hardness at different depths. For this, 60 endodontically treated bovine roots were used. Rebilda Post 20 fiberglass pins were cemented according to the following protocols divided into the following groups: QM groups: dual self-etching adhesive Futurabond DC + resin cement Bifix QM; Group SE: Dual polymerization resin cement Bifix SE; Group RB: application of self-etching dual-polymerization adhesive Futurabond DC + resin Rebilda; Group XB: application of the self-etching adhesive for dual polymerization Futurabond DC + composite resin of the bulk fill type X-tra Base. The roots were cut into 1mm slices and separated into thirds, obtaining 2 specimens per third. Bond strength (n =10) and microhardness (n = 5) were evaluated after one week and after 4 months of storage in water. For the push-out test one slice of each third was tested after one week and the other 3 slices from the same tooth evaluated after 4 months. The push out test was performed at a speed of 0.5mm / min until the pin displacement and / or fracture of the adhesive interface. For the microtensile test, 20 teeth were randomly selected and six slices were obtained from each tooth, which were stored in distilled water for one week until microdurometer measurement, after one week and after four months. The specimens were submitted to the Knoop microhardness test in HMV-2000 microdurometer (Shimadzu, Tokyo, Japan), five indentations were performed in the cement layer of each slice. The data for the tests of bond strenght (push-out) and microhardness were submitted to analysis of variance 3 factors (ANOVA) and Tukey test (p <0.05) and Person correlation test. The bond strength values did not present significant statistical differences when the adhesive strength values were observed between the groups QM, RB and XB (p>=0.05), but lower values of adhesive strength were observed in the SE Group. When the aging variable was considered, differences in adhesive strength measured at one week and 4 months (p>=0.05) were not found. For microhardness, statistically significant differences were found in the different thirds of the root (p <0.05). The cementing agents presented significant statistical differences in the hardness (p <0.05). The XB group presented the highest values followed by QM, RB and SE. The groups SE, RB and XB did not present 80% of the maximum hardness in the slices corresponding to the apical region of the root canal. The Person test showed a linear positive correlation between the adhesive strength and the hardness measured before and after aging. The use of dual resin cement, combined with a previous application of the adhesive system, is still the safest choice, since it presented high values of bond strength, associated with adequate hardness values, even in apical regions of the root canal.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-01-12T12:51:08Z No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Approved for entry into archive by Diamantino Mayra (mayra.diamantino@ufjf.edu.br) on 2017-01-31T11:16:46Z (GMT) No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Made available in DSpace on 2017-01-31T11:16:46Z (GMT). No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) Previous issue date: 2009-12-10 / O presente estudo teve como objetivo avaliar a influência do tratamento da dentina radicular com clorexidina a 2% e ácido cítrico a 10% na resistência de união de pinos de fibra de vidro cimentados com cimento resinoso RelyX Ultimate (3M ESPE) associado a um adesivo autocondicionante Single Bond Universal (3M ESPE). Quarenta e cinco dentes humanos unirradiculares foram selecionados e seccionados na junção cemento-esmalte, padronizando-os com 14 mm de comprimento. Após tratamento endodôntico, as raízes foram divididas aleatoriamente em 3 grupos (n=15) de acordo com o tratamento prévio do conduto radicular: G1, nenhum tratamento; G2, aplicação de gel de clorexidina a 2% (Rioquímica®) por 60 segundos; G3, aplicação de ácido cítrico a 10% (Idem per Idem Farmácia de Manipulação Ltda) por 60 segundos. Posteriormente, foi aplicado o adesivo nos condutos e nos pinos de fibra de vidro (White Post, FGM) e estes foram cimentados com cimento resinoso (RelyX Ultimate - 3M ESPE), sendo fotopolimerizados por 40 segundos. As raízes foram seccionadas axialmente em discos de 2 mm e os espécimes foram submetidos ao teste de push-out. As médias dos valores obtidos (MPa) foram analisadas por meio dos testes one-way ANOVA e Tukey (α=0,05) e os tipos de falhas analisadas em estereomicroscópio com aumento de 8,0X. Os resultados mostraram que não houve diferença estatisticamente significativa entres os grupos avaliados, assim como quando comparados os terços radiculares em cada grupo (p>0,05), entretanto resultados significantes foram encontrados entre os grupos G1 e G2 na região cervical (p=0,045). Falhas mista e adesiva entre cimento e dentina foram mais prevalentes. Pôde-se concluir que o uso da clorexidina a 2% no conduto radicular pode interferir na resistência de união de pinos de fibra de vidro e que o ácido cítrico não influenciou nos resultados. / The aim of this study was to investigate the influence of root dentine treatment with 2% chlorhexidine and 10% citric acid on bond strength of fiberglass post cemented with self-etching cement. Forty five human single-rooted teeth were selected and sectioned in the cement-enamel junction, standardizing them with 14 mm length. After endodontic treatment the roots were randomly divided in 3 groups (n=15) according to the previous treatment of the root canal: G1, no treatment; G2, application of 2% chlorhexidine (Rioquímica®) for 60s; G3, application of 10% citric acid (Idem per Idem - Farmácia de Manipulação Ltda) for 60s. Subsequently, the self-etching adhesive Single Bond Universal (3M ESPE) was applied in the canals and on the fiberglass post (White Post, FGM) and these ones were cemented with resin cement (RelyX Ultimate - 3M ESPE), and light polymerized for 40s. The roots were sectioned transversely in slides of 2 mm thickness and the push-out test was performed. Data were analyzed by one-way ANOVA and Tukey test (α=0.05) and the types of failures were analyzed under stereomicroscopy (8.0X). The results show that there was no statistically significant difference between the groups, as well as when comparising bond strength in root thirds in each group (p>0.05), however, significant results were found between groups G1 and G2 in the cervical third (p=0.045). Mixed and adhesive failures between cement and dentine were predominant. It can be concluded that the use of 2% chlorhexidine in the root canal can interfere in the fiberglass posts bond strength.

Coroas cerâmicas apoiadas sobre infra-estruturas de alumina densamente sinterizada configuram-se como excelentes opções para a reabilitação protética em casos de exigência estética, contudo, o aumento do conteúdo cristalino inviabiliza seu condicionamento por ácidos deixando a maneira ideal de cimentá-las ainda desconhecida. Coroas Procera AllCeram apresentam, em sua face interna, micro irregularidades interessantes ao embricamento e adesão resinosa, dispensando manobras de condicionamento. Objetivo: O objetivo deste trabalho foi avaliar a influência de elevadas temperaturas (500ºC à 950ºC) necessárias à cocção da porcelana de revestimento, na textura superficial da alumina, bem como o papel de um agente primer (Ivoclar Vivadent) na força de adesão entre alumina e cimento resinoso. Material e métodos: Sessenta (60) cilindros de alumina (3,5mm X 16mm) com rugosidade superficial idêntica à dos copings Procera foram divididos em quatro grupos (n=15). Grupo 1): Espécimes não submetidos a variação térmica, sendo G1a Sem aplicação do primer e G1b Com aplicação do primer e Grupo 2): Espécimes submetidos aos ciclos térmicos para cocção da porcelana feldspática, sendo G2a Sem aplicação do primer e G2b Com aplicação do primer. Sobre os cilindros aplicou-se porção do cimento resinoso químico MultiLink Ivoclar. Os espécimes foram levados a uma máquina de ensaios Universal para teste de cisalhamento a uma velocidade de 0.5mm/min e os dados submetidos à análise de variância a um critério e teste de comparações múltiplas de Tukey. Resultados: A força de adesão para cada um dos grupos foi: G1a = 2.468 MPa; G1b = 4.265 MPa; G2a = 2.339MPa e G2b = 4.185 MPa. Diferenças significantes foram observadas entre os grupos: G1a X G1b; G1a X G2b; G1b X G2a e G2a X G2b. Conclusões: Ciclos térmicos não produziram alterações na micro-estrutura superficial da alumina, tampouco comprometeram sua adesão ao cimento. O agente primer aumentou a força de união entre alumina e cimento resinoso. Fraturas coesivas do agente cimentante foram observadas apenas em alguns espécimes primer-tratados. / High-strength alumina based ceramic crowns are widely used in dentistry due to their favorable esthetic, however, the large amount of crystalline contents jeopardizes their acid etching property and the ideal luting remains unclear. Procera AllCeram restorations exhibits on their intaglio surface micro irregularities optimizing the bonding to resin, with no need for additional conditioning procedures. Purpose: The aim of the present study was to evaluate the influence of high thermal cycles (500ºC to 950ºC) needed to porcelain firing on alumina´s intaglio surface, as well as, the role of a primer agent (Ivoclar Vivadent) on shear bond strength between alumina and resin cement. Material and Methods: Sixty alumina cylinders (3,5mm X 16mm) with intaglio roughness of the Procera AllCeram copings were randomly divided into four groups (n=15). Group 1) Samples no submitted to thermal cycles variation, were G1a - no primer application and G1b - primer treated and Group 2: Samples submitted to thermal feldspathic porcelain firing cycles, were G2a - specimens no primer treated and G2b - primer treated specimens. Over the cylinders top a self-cure resin cement (Multilink Ivoclar) portion was applied. The specimens were loaded to failure in shear mode using a universal testing machine at a crosshead speed of 0,5mm/min. Data were analyzed with one-way analysis of variance and Tukey´s multiple comparison test. Results: The shear bond strength for each group was: G1a = 2.468 MPa; G1b = 4.265 MPa; G2a = 2.339 MPa e G2b = 4.185 MPa. Significant difference was found between the groups G1a X G1b; G1a X G2b; G1b X G2a e G2a X G2b. Conclusions: Thermal cycles did not change alumina´s surface micro structure, besides did not compromised it´s bonding strength to resin cement. Primer agent enhanced shear bond strength between alumina and resin cement. Luting agent´s cohesive fractures were observed only in some primer treated specimens.