21 |
Comparison of physical properties of oxidative sintered pellets produced with UG2 or metallurgical grade South African chromite : a case study / Ralph Ivor GlastonburyGlastonbury, Ralph Ivor January 2014 (has links)
The Bushveld Igneous Complex (BIC) in South Africa holds approximately three
quarters of the world’s viable chromite ore deposits. Most chromite is used for the
production of ferrochromium (FeCr), which is a relatively crude alloy. Several chromite
seams exist in the BIC. The most economically viable seams are the lower group 6 (LG6),
the middle group 1 and 2 (MG1 and 2) and the upper group 2 (UG2) seams. The LG and MG
seams are exploited specifically for their chromium content, whereas the UG2 seam is mainly
exploited for platinum group minerals (PGM). However, the upgraded UG2 chromite in the
PGM tailing is increasingly being used as a feedstock for FeCr production. Many different
process variations exist for FeCr production. However, the process option applied in most
green and brown field FeCr expansion projects during the last two decades in South Africa
has been the oxidative sintered process (also referred to as the Outotec or Outokumpu
process). Notwithstanding the common application of the oxidative sintered pelletised feed
technology in the South African FeCr industry, and the increased utilisation of beneficiated
UG2 ore, a direct comparison of the physical properties of oxidative sintered pellets produced
from UG2 with the physical properties of that produced with conventional metallurgical
grade chromite ore is currently lacking in the peer-reviewed scientific literature. Therefore,
the physical properties of oxidative sintered pellets produced from a typical beneficiated
South African UG2 ore were compared with the physical properties of that produced with
conventional South African metallurgical grade chromite ore in this study.
The results indicated that the case study metallurgical grade chromite ore required
13 kWh/t more energy to mill than the case study UG2 ore prior to pelletisation, which can
lead to substantial cost savings. The compressive strength of the oxidative sintered pellets of
both case study ores statistically showed that oxidative sintered pellets made from UG2 ore
Abstract
were the same or better than those prepared from metallurgical grade chromite ore. A
comparison of the abrasion strengths of the oxidative sintered pellets of both case study ores
indicated that the pellets prepared from UG2 ore were superior compared to the metallurgical
grade pellets. The reasons for the superior UG2 pellet strength were investigated with
backscatter-, secondary electron- and elemental X-ray mapping scanning electron microscopy
(SEM), which indicated that differences in crystalline structures at least partially contributed
to the differences observed. Results presented here can be utilised by FeCr producers to
better quantify the advantages and disadvantages associated with the use of UG2 ore for FeCr
production. / MSc (Chemistry), North-West University, Potchefstroom Campus, 2014
|
22 |
"Estudo da influência do zircônio e gálio nas propriedades magnéticas e na microestrutura dos imãs permanentes à base de praseodímio" / STUDY OF THE INFLUENCE OF ZIRCONIUM AND GALLIUM ON THE MAGNETIC PROPERTIES AND MICROSTRUCTURES OF PRASEODYMIUM-BASED PERMANENT MAGNETSFusco, Alexandre Giardini 18 August 2006 (has links)
Nesse trabalho estudou-se a influência da adição de 0,5 % at. de zircônio (Zr) e gálio (Ga) nos ímãs permanentes à base de praseodímio (Pr) HD sinterizados obtidos por uma mistura de ligas. As ligas utilizadas foram: Pr12,6Fe68,3Co11,6B6Zr0,5Ga1, Pr16Fe75,5B8Zr0,5 e Pr13Fe80,5B6Zr0,5. A investigação foi realizada a partir das medidas das propriedades magnéticas e da microestrutura. Inicialmente, compararam-se as fases das ligas com as fases obtidas nos ímãs sinterizados. Posteriormente, os ímãs foram submetidos a um ciclo de tratamento térmico (de duas horas a 1000º C com resfriamento rápido até 10 horas, em seguida, de cinco horas nas mesmas condições, até 35 horas). Para o entendimento do papel de cada aditivo na fase magneticamente dura (fase Φ), foram analisadas as mudanças na microestrutura e relacionadas com as mudanças nas propriedades magnéticas. O Ga e Zr atuam como refinadores da fase Φ (matriz). O Ga atua no grão da fase Φ possibilitando a estabilidade da sua forma e melhorias das propriedades magnéticas. Para o ímã Pr14,3Fe71,9Co5,8B7Zr0,5Ga0,5 a evolução das propriedades magnéticas, após 15 h de tratamento térmico, foi: remanência de (1,25±0,02) T para (1,30±0,02) T, coercividade intrínseca de (1,11±0,02) T para (0,87±0,02) T, fator de quadratura de (0,68±0,02) para (0,89±0,02) e produto de energia de (285±5) kJ/m3 para (317±5) kJ/m3. O Zr tem uma atuação dual. Inibe o crescimento desordenado do grão e aumenta a anisotropia, mas, ao alojar-se no contorno de grão, gera domínios reversos prejudicando a coercividade intrínseca. Para o ímã Pr14.5Fe78B7Zr0.5 a evolução das propriedades magnéticas, após 15 h de tratamento térmico, foi: remanência (1,19±0,02) T para (1,25±0,02) T, coercividade de (0,74±0,02) T para (0,94±0,02) T, fator de quadratura de (0,88±0,02) para (0,85±0,02) e produto de energia (258±5) kJ/m para (291±5) kJ/m. Para o ímã Pr3316Fe75.5B8Zr0.5 a evolução das propriedades magnéticas, após 20 h de tratamento térmico, foi: remanência (1,17±0,02) T para (1,24±0,02) T, coercividade de (0,90±0,02) T para (1,22±0,02) T, fator de quadratura de (0,93±0,02) para (0,66±0,02) e produto de energia (258±5) kJ/m3 para (272±5) kJ/m3. / In this work was studied the influence of the addition of 0.5 at. % of zirconium and gallium on praseodymium-based HD sintered magnets obtained using a mixture of alloys. The alloys used in this study were: Pr12.6Fe68.3Co11.6B6Zr0.5Ga1, Pr16Fe75.5B8Zr0.5, Pr13Fe80.5B6Zr0.5. The investigation started by measuring the magnetic properties and observing the microstructure of the magnets. After that, the magnets were annealed at 1000ºC for 2 hours followed by rapid cooling, in a total of 10 hours. This heat treatment was followed by 5 hours at the same temperature up to a total of 35 hours. Changes in the microstructure were compared to the change in the magnetic properties aiming at a proper understanding of the role of each added element in relation to the magnetically hard phase (phase Φ). It has been shown that gallium and zirconium act as grain refiners of the matrix phase Φ. Gallium acts in the grain and favoring of the shape stability and improvement of the magnetic properties. For the Pr14.3Fe71.9Co5.8B7Zr0.5Ga0.5 sintered magnet the evolution of the magnetic properties after 15 hours heat treatment was: remanence from (1.25±0.02) T to (1.30±0.02) T, intrinsic coercivity from (1.11±0.02) T to (0.87±0.02) T, squareness factor from (0.68±0.02) to (0.82±0.02) and energy product from (285±5) kJ/m3 to (317±5) kJ/m3. Zirconium has two effects on the sintered magnets. Firstly, avoiding random grain growth and enhancing anisotropy. However, by concentrating on the grain boundaries, yield reverse domains and is detrimental to the intrinsic coercivity. For the sintered Pr14.5Fe78B7Zr0.5 magnet the evolution of the magnetic properties achieved after a heat treatment of 15 hours was: remanence from (1.19±0.02) T to (1.25±0.02) T, coercivity from (0.74±0.02) T to (0.94±0.02) T, squareness factor from (0.88±0.02) to (0,85±0.02) and energy product from (258±5) kJ/m to (291±5) kJ/m. For the Pr3316Fe75.5B8Zr0.5 sintered magnet the evolution of magnetic properties after 20 hours heat treatment was: remanence from (1.17±0,02) T to (1.24±0.02) T, coercivity from (0.90±0,02) T to (1.22±0.02) T, squareness factor from (0,93±0,02) to (0.66±0.02) and energy product from (258±5) kJ/m3 to (291±5) kJ/m3.
|
23 |
Estudo microestrutural e propriedades magnéticas em ímãs permanentes sinterizados a base de PrFeCoBNb com adições de elementos de ligas / Microstructural study and magnetic properties of PrFeCoBNb-based permanent sintered magnets with alloy additionsMendes Neto, Teofilo 08 July 2011 (has links)
Neste estudo, as propriedades magnéticas dos ímãs sinterizados, produzidos a partir de uma mistura de ligas Pr16Fe76B8 e Pr14FebalCo16B6Nb0,1Mx, onde M= Al, Cu, P, Si, Gd, Ga, Dy, Tb e x= 0,1, 0,3, 0,5 % at. em iguais proporções, foram correlacionadas com as características microestruturais através de microscopia eletrônica de varredura (MEV) e de transmissão (MET). Utilizou-se microscopia eletrônica de varredura (MEV) e processamento computacional das micrografias, na investigação das características associadas ao tamanho e formato dos grãos magnéticos (Φ). A correlação utilizada indicou que fatores de quadratura superiores estão associados a grãos mais arredondados e com distribuição de tamanho mais estreita. Considerando que a variação no tamanho de grão e os valores de coercividade não se mostraram conclusivas com MEV, utilizou-se o recurso da microscopia eletrônica de transmissão (MET), microanálise com EDS e padrão de difração eletrônica. A associação da coercividade com a microestrutura foi feita com base nas investigações das fases não magnéticas, ricas em praseodímio dos pontos triplos e nos contornos de grãos. Com o microscópio de transmissão de alta resolução (HRTEM), foi possível observar a presença de uma camada contínua e regular entre os grãos da fase magnética para o ímã com adição de Ga 0,25% at. A modificação da microestrutura no contorno de grão do ímã com adição de Ga pode ser indicada como responsável pelo aumento de 10% na coercividade (1100 mT) comparado com o ímã Pr15FebalCo8B7Nb0,05. / In this study the magnetic properties of sintered magnets, prepared with a mixture of Pr16Fe76B8 and Pr14FebalCo16B6Nb0.1Mx alloys, where M = Al, Cu, P, Si, Gd, Ga, Dy, Tb and x = 0.1, 0.3, 0.5 at.% in the same proportions, were correlated with the microstructural features by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). SEM and computer processing of the micrographs were used in order to provide the characteristics associated with the size and shape of the magnetic grains (Φ phase). The correlation used shows that superior squareness factors are associated with rounder and narrower size distribution grains. Considering that the variation in the grain size and coercivity values were not conclusive with SEM, it has been used TEM, micro analysis by EDS and electron diffraction pattern. The coercivity relation with the microstructure was based on investigations of non-magnetic phases, in triple points, and in the grain boundary. With a high resolution transmission microscope (HRTEM), it was possible to observe a regular and continuous layer between the grains of the magnetic phase for the magnet with 0.25 at.% of Ga. The presence of such boundary can be indicated as responsible for higher coercivity values of this magnet. Microstructure was modified in the grain boundary by Ga addition and can be indicated as responsible for coercivity value (1100 mT) 10% higher than Pr15FebalCo8B7Nb0.05 magnet.
|
24 |
Efeito da ferro-oxidação a vapor antes e após operação de usinagem na resistência ao desgaste de ferro sinterizado / Effect of steam treatment before and after machining operation on wear resistance of sintered steelGuimarães, Ramiro Carlos 01 April 2008 (has links)
Neste trabalho verificou-se o efeito da ferroxidação a vapor, aplicada antes e após operações de usinagem de acabamento final, na resistência ao desgaste de um ferro sinterizado, utilizado na fabricação de bielas usadas em mancais de deslizamento de compressor hermético. Ensaios micrográficos, de dureza e microdureza, ensaios de perfil e circularidade, testes de vida acelerados em um compressor hermético doméstico de refrigeração e ensaios de microdesgaste, usando-se o mesmo tipo de óleo aplicado em compressores, ou abrasivos com diferentes granulometrias, foram realizados em peças e amostras com e sem a camada ferroxidada. Verificou-se que a camada ferroxidada apresentou valores de durezas superiores ao do substrato em 130%. No caso das amostras ferroxidadas, os resultados indicaram significativa melhora na resistência ao desgaste tanto no teste de aplicação direta no compressor, demonstrado nos testes de perfis e de circularidades, como nos ensaios de microdesgaste, evidenciando a grande efetividade desse tratamento no aumento da resistência ao desgaste nas condições testadas neste trabalho. / The intent of this work was to verify the effect of steam treatment applied before and after finishing machining operations on wear resistance of sintered steel used in the manufacturing of connecting rod applied in sliding bearings of hermetic compressor. Micrographic tests, hardness and micro hardness, test profile and roundness, accelerated endurance test in domestic refrigeration hermetic compressor and micro wear test using the same oil used in the compressor or abrasive with different grain size were made on parts and samples with and without oxide layer. It was verified that the oxide layer indicated hardness values over 130% than that of the substrate. In the case of layer oxide, the results showed significant improvement on wear resistance in the direct compressor application shown by test profile and roundness as well as micro wear test, showing the high efficiency of treatment increasing the wear resistance in the conditions tested in this work.
|
25 |
"Estudo da influência do zircônio e gálio nas propriedades magnéticas e na microestrutura dos imãs permanentes à base de praseodímio" / STUDY OF THE INFLUENCE OF ZIRCONIUM AND GALLIUM ON THE MAGNETIC PROPERTIES AND MICROSTRUCTURES OF PRASEODYMIUM-BASED PERMANENT MAGNETSAlexandre Giardini Fusco 18 August 2006 (has links)
Nesse trabalho estudou-se a influência da adição de 0,5 % at. de zircônio (Zr) e gálio (Ga) nos ímãs permanentes à base de praseodímio (Pr) HD sinterizados obtidos por uma mistura de ligas. As ligas utilizadas foram: Pr12,6Fe68,3Co11,6B6Zr0,5Ga1, Pr16Fe75,5B8Zr0,5 e Pr13Fe80,5B6Zr0,5. A investigação foi realizada a partir das medidas das propriedades magnéticas e da microestrutura. Inicialmente, compararam-se as fases das ligas com as fases obtidas nos ímãs sinterizados. Posteriormente, os ímãs foram submetidos a um ciclo de tratamento térmico (de duas horas a 1000º C com resfriamento rápido até 10 horas, em seguida, de cinco horas nas mesmas condições, até 35 horas). Para o entendimento do papel de cada aditivo na fase magneticamente dura (fase Φ), foram analisadas as mudanças na microestrutura e relacionadas com as mudanças nas propriedades magnéticas. O Ga e Zr atuam como refinadores da fase Φ (matriz). O Ga atua no grão da fase Φ possibilitando a estabilidade da sua forma e melhorias das propriedades magnéticas. Para o ímã Pr14,3Fe71,9Co5,8B7Zr0,5Ga0,5 a evolução das propriedades magnéticas, após 15 h de tratamento térmico, foi: remanência de (1,25±0,02) T para (1,30±0,02) T, coercividade intrínseca de (1,11±0,02) T para (0,87±0,02) T, fator de quadratura de (0,68±0,02) para (0,89±0,02) e produto de energia de (285±5) kJ/m3 para (317±5) kJ/m3. O Zr tem uma atuação dual. Inibe o crescimento desordenado do grão e aumenta a anisotropia, mas, ao alojar-se no contorno de grão, gera domínios reversos prejudicando a coercividade intrínseca. Para o ímã Pr14.5Fe78B7Zr0.5 a evolução das propriedades magnéticas, após 15 h de tratamento térmico, foi: remanência (1,19±0,02) T para (1,25±0,02) T, coercividade de (0,74±0,02) T para (0,94±0,02) T, fator de quadratura de (0,88±0,02) para (0,85±0,02) e produto de energia (258±5) kJ/m para (291±5) kJ/m. Para o ímã Pr3316Fe75.5B8Zr0.5 a evolução das propriedades magnéticas, após 20 h de tratamento térmico, foi: remanência (1,17±0,02) T para (1,24±0,02) T, coercividade de (0,90±0,02) T para (1,22±0,02) T, fator de quadratura de (0,93±0,02) para (0,66±0,02) e produto de energia (258±5) kJ/m3 para (272±5) kJ/m3. / In this work was studied the influence of the addition of 0.5 at. % of zirconium and gallium on praseodymium-based HD sintered magnets obtained using a mixture of alloys. The alloys used in this study were: Pr12.6Fe68.3Co11.6B6Zr0.5Ga1, Pr16Fe75.5B8Zr0.5, Pr13Fe80.5B6Zr0.5. The investigation started by measuring the magnetic properties and observing the microstructure of the magnets. After that, the magnets were annealed at 1000ºC for 2 hours followed by rapid cooling, in a total of 10 hours. This heat treatment was followed by 5 hours at the same temperature up to a total of 35 hours. Changes in the microstructure were compared to the change in the magnetic properties aiming at a proper understanding of the role of each added element in relation to the magnetically hard phase (phase Φ). It has been shown that gallium and zirconium act as grain refiners of the matrix phase Φ. Gallium acts in the grain and favoring of the shape stability and improvement of the magnetic properties. For the Pr14.3Fe71.9Co5.8B7Zr0.5Ga0.5 sintered magnet the evolution of the magnetic properties after 15 hours heat treatment was: remanence from (1.25±0.02) T to (1.30±0.02) T, intrinsic coercivity from (1.11±0.02) T to (0.87±0.02) T, squareness factor from (0.68±0.02) to (0.82±0.02) and energy product from (285±5) kJ/m3 to (317±5) kJ/m3. Zirconium has two effects on the sintered magnets. Firstly, avoiding random grain growth and enhancing anisotropy. However, by concentrating on the grain boundaries, yield reverse domains and is detrimental to the intrinsic coercivity. For the sintered Pr14.5Fe78B7Zr0.5 magnet the evolution of the magnetic properties achieved after a heat treatment of 15 hours was: remanence from (1.19±0.02) T to (1.25±0.02) T, coercivity from (0.74±0.02) T to (0.94±0.02) T, squareness factor from (0.88±0.02) to (0,85±0.02) and energy product from (258±5) kJ/m to (291±5) kJ/m. For the Pr3316Fe75.5B8Zr0.5 sintered magnet the evolution of magnetic properties after 20 hours heat treatment was: remanence from (1.17±0,02) T to (1.24±0.02) T, coercivity from (0.90±0,02) T to (1.22±0.02) T, squareness factor from (0,93±0,02) to (0.66±0.02) and energy product from (258±5) kJ/m3 to (291±5) kJ/m3.
|
26 |
Estudo microestrutural e propriedades magnéticas em ímãs permanentes sinterizados a base de PrFeCoBNb com adições de elementos de ligas / Microstructural study and magnetic properties of PrFeCoBNb-based permanent sintered magnets with alloy additionsTeofilo Mendes Neto 08 July 2011 (has links)
Neste estudo, as propriedades magnéticas dos ímãs sinterizados, produzidos a partir de uma mistura de ligas Pr16Fe76B8 e Pr14FebalCo16B6Nb0,1Mx, onde M= Al, Cu, P, Si, Gd, Ga, Dy, Tb e x= 0,1, 0,3, 0,5 % at. em iguais proporções, foram correlacionadas com as características microestruturais através de microscopia eletrônica de varredura (MEV) e de transmissão (MET). Utilizou-se microscopia eletrônica de varredura (MEV) e processamento computacional das micrografias, na investigação das características associadas ao tamanho e formato dos grãos magnéticos (Φ). A correlação utilizada indicou que fatores de quadratura superiores estão associados a grãos mais arredondados e com distribuição de tamanho mais estreita. Considerando que a variação no tamanho de grão e os valores de coercividade não se mostraram conclusivas com MEV, utilizou-se o recurso da microscopia eletrônica de transmissão (MET), microanálise com EDS e padrão de difração eletrônica. A associação da coercividade com a microestrutura foi feita com base nas investigações das fases não magnéticas, ricas em praseodímio dos pontos triplos e nos contornos de grãos. Com o microscópio de transmissão de alta resolução (HRTEM), foi possível observar a presença de uma camada contínua e regular entre os grãos da fase magnética para o ímã com adição de Ga 0,25% at. A modificação da microestrutura no contorno de grão do ímã com adição de Ga pode ser indicada como responsável pelo aumento de 10% na coercividade (1100 mT) comparado com o ímã Pr15FebalCo8B7Nb0,05. / In this study the magnetic properties of sintered magnets, prepared with a mixture of Pr16Fe76B8 and Pr14FebalCo16B6Nb0.1Mx alloys, where M = Al, Cu, P, Si, Gd, Ga, Dy, Tb and x = 0.1, 0.3, 0.5 at.% in the same proportions, were correlated with the microstructural features by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). SEM and computer processing of the micrographs were used in order to provide the characteristics associated with the size and shape of the magnetic grains (Φ phase). The correlation used shows that superior squareness factors are associated with rounder and narrower size distribution grains. Considering that the variation in the grain size and coercivity values were not conclusive with SEM, it has been used TEM, micro analysis by EDS and electron diffraction pattern. The coercivity relation with the microstructure was based on investigations of non-magnetic phases, in triple points, and in the grain boundary. With a high resolution transmission microscope (HRTEM), it was possible to observe a regular and continuous layer between the grains of the magnetic phase for the magnet with 0.25 at.% of Ga. The presence of such boundary can be indicated as responsible for higher coercivity values of this magnet. Microstructure was modified in the grain boundary by Ga addition and can be indicated as responsible for coercivity value (1100 mT) 10% higher than Pr15FebalCo8B7Nb0.05 magnet.
|
27 |
Estudo experimental das principais características de um dressador sinterizado com ênfase na dissipação de calor / Experimental study on the main characteristics of sintered dressing tools with emphasis on heat dissipationSilva Junior, Carlos Elias da 07 April 2004 (has links)
No processo de retificação a dressagem desempenha um papel fundamental, uma vez que ela é responsável pela topografia da superfície de trabalho do rebolo, podendo afetar os resultados da retificação em termos da integridade superficial e precisão dimensional da peça, bem como a confiabilidade do processo. Portanto, como parte integrante da operação de retificação, a dressagem pode melhorar significativamente a qualidade das peças retificadas caso melhores dressadores sejam produzidos. Este trabalho tem o objetivo de estudar as principais características necessárias ao projeto de dressadores sinterizados que utilizam diamantes sintéticos de perfil constante e verificar experimentalmente a distribuição de temperaturas no dressador, obtidas através de ensaios práticos e simulação computacional pelo método dos elementos finitos. O modelo utilizado contém algumas limitações, porém os resultados obtidos mostraram que os níveis de temperaturas no dressador foram afetados pelos parâmetros de dressagem considerados no trabalho, a saber, a profundidade de dressagem (\'a IND. d\'), o grau de recobrimento de dressagem (\'U IND. d\') e a vazão do fluido refrigerante (Q). O desgaste do dressador foi afetado apenas pelos parâmetros de dressagem. / In grinding operations, dressing tools are of major importance, since they are responsible for the topography of the wheel working surface and, consequently, can affect the grinding results in terms of surface integrity, dimensional accuracy and process reliability. Therefore, as an important part of the grinding operation, dressing can significantly improve the quality of ground parts if better dressing tools are produced. This work studies the main needs for designing sintered dressing tools made with constant cross sectional synthetic diamonds. It also analyses the temperature distribution over a novel dressing tool design using experimental measurements to feed computacional simulation by the finite element method (FEM). The temperature model employed showed some limitations but the obtained results indicated that temperature levels over the dressing tool were affected by the dressing parameters considered in this work, namely the dressing depth of cut (\'a IND. d\'), the dressing overlapping parameter (\'U IND. d\') and the flow rate (Q). Additionally, one can say that the dressing tool wear was affected only by the dressing parameters
|
28 |
EFEITO DE TiO2 K2O , E Na2 FASE VÍTREA E NAS PROPRIEDADES DE PORCELANAS TRIAXIAIS.Przybysz, Aldo 16 December 2011 (has links)
Made available in DSpace on 2017-07-21T20:42:35Z (GMT). No. of bitstreams: 1
Aldo Przybysk.pdf: 5897401 bytes, checksum: e936e1a74fbf323168d821498cfabea7 (MD5)
Previous issue date: 2011-12-16 / Porcelains are manufactured from natural raw material, in which are inclined the presence of diverse impurities. The presence of impurity can modify significantly the various characteristics of the porcelain, mainly the mechanical characteristics. Then, the understanding about the mechanism of actuation of these impurities is fundamentally important to reach the desired characteristics. In this dissertation, it was studied the effects of the addition of oxide generators additives on the microstructural development and on the properties of aluminous porcelain, siliceous and aluminous-siliceous, aiming to understand the actuation mechanism of these additives and what is their influence with the variation of ceramic mass composition. It had been chosen three types of porcelain: Porcelain of Alumina-Feldspar-Kaolin system, Silica-Feldspar-Kaolin and Alumina-Silica-Feldspar-Kaolin. In each composition it was added the additives, which were mixed wet in balls mill, and dry in stove. The resulting powders from these mixtures were pressed and sintered. The sintered porcelains were characterized by apparent density measurement, water absorption, linear contraction, porosity percentage, X-ray diffraction, electronic microscopy scan, EDS microanalyses and rupture module by three points flexion. In the aluminous, siliceous and the aluminous-siliceous porcelains compositions, the presence of additives reduced the values of the modules of rupture, nevertheless for the major of the samples added to these additives, the sintering temperature was reduced. It was verified that in every composition and with every additive used, actuate directly on the formation of the liquid stage, and it is this stage that during the sintering, modifies the other present stage and then, modify the microstructure and consequently the mechanical characteristics of the porcelain. / As porcelanas são fabricadas a partir de matérias primas naturais, as quais estão sujeitas a presença de diversas impurezas. A presença de impurezas pode alterar de maneira significativa as diversas propriedades das porcelanas, principalmente as propriedades mecânicas. Com isso o entendimento do mecanismo de atuação destas impurezas é de fundamental importância para se atingir as propriedades desejadas. Nesta dissertação foram estudados os efeitos da adição de aditivos geradores de óxidos no desenvolvimento microestrutural e nas propriedades de porcelanas aluminosas, silicosas e aluminosas silicosas, com o objetivo de se entender o mecanismo de atuação destes aditivos e qual a influência destes com a variação de composição da massa cerâmica. Foram escolhidos três tipos de porcelanas: porcelana de sistemas Alumina-Feldspato-Caulim, Sílica-Feldspato-Caulim e Alumina-Sílica-Feldspato-Caulim. A cada composição foram adicionados os aditivos, os quais foram misturados a úmido em moinho de bolas e secos em estufa. Os pós resultantes destas misturas foram prensados e sinterizados. As porcelanas sinterizadas foram caracterizadas através de medidas de densidade aparente, absorção de água, retração linear, porcentagem de porosidade, difração de raios X, microscopia eletrônica de varredura, microanálise via EDS e módulo de ruptura por flexão em três pontos. Nas composições de porcelanas aluminosas, silicosas e alumino-silicosas, a presença de aditivos diminuiu os valores do módulo de ruptura. Porém para a maioria das amostras dopadas com estes aditivos, a temperatura de sinterização diminuiu. Foi verificado que em todas as composições e com todos os aditivos utilizados, atuam diretamente na formação da fase líquida e é esta fase que durante a sinterização modifica as demais fases presentes e assim, altera a microestrutura e consequentemente afeta as propriedades mecânicas da porcelana.
|
29 |
ESTUDO DA INCORPORAÇÃO DE VIDRO DE PARA-BRISA EM MASSA DE PORCELANA SILICOSA E ALUMINOSASantos, Araldo Augusto Tisque dos 08 August 2012 (has links)
Made available in DSpace on 2017-07-21T20:42:38Z (GMT). No. of bitstreams: 1
Araldo Augusto Tisque dos Santos.pdf: 3494228 bytes, checksum: 10aa5475f02c7ee4a3913a8571815ebc (MD5)
Previous issue date: 2012-08-08 / The glass is not a biodegradable material, which causes an environmental problem when it is discarded. However, it is a material that can be 100% recycled, or even re-used, but the laminated glass (glass windshields) is not accepted for recycling, this because it is a glass of low particle size and also by the difficulty of separating the glass polymer film, while this type of glass consisting of two or more layers of glass held together by one or more layers of a polymer called polyvinyl butyral (PVB). Thus it is necessary to find alternative means which allow recycling. In this thesis was studied the possibility of incorporating laminated glass in the ceramic bodies of siliceous and aluminous porcelain, replacing feldspar which acts as a flux these two ceramic bodies. The objective of this research is to verify the changes that the incorporation of glass windshields because the glassy phase of siliceous and aluminous porcelain and reflections that these changes have on the ceramic properties. Was chosen for this particle sizes of two glass laminate, and a thin, rough and added to another ceramic body in amounts of 5%, 10% and 15%, by weight replacing the same amount of feldspar. The powders of these mixtures were pressed and sintered at three different temperatures. Sintered porcelains were characterized through measurements of porosity, bulk density, water absorption, modulus of rupture by three point bending, X-ray diffraction, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS). The compositions siliceous and aluminous porcelain were introduced laminated glass of finer showed very similar results to those of composition without addition of laminated glass. / O vidro não é um material biodegradável, causando um problema ambiental quando o mesmo é descartado. Entretanto é um material que pode ser 100% reciclado, ou até mesmo reutilizado, mas o vidro laminado (vidro de para brisas) não é aceito para a reciclagem, isto por se tratar de um vidro de baixa granulometria e também pela dificuldade de separar o vidro do filme polimérico, sendo que este tipo de vidro composto por duas ou mais camadas de vidro unidas por uma ou mais camadas de um polímero chamado de polivinil butiral (PVB). Assim se torna necessário encontrar meios alternativos que permitam a reciclagem desse material. Nessa dissertação foi estudada a possibilidade da incorporação do vidro laminado nas massas cerâmicas de porcelana aluminosa e silicosa, substituindo o feldspato que atua como fundente nessas duas massas cerâmicas. O objetivo dessa pesquisa é de verificar as mudanças que a incorporação do vidro de para brisas causa na fase vítrea da porcelana aluminosa e silicosa e os reflexos que essas mudanças apresentam nas propriedades cerâmicas. Para isso foi escolhido duas granulometrias de vidro laminado, sendo uma fina e outra grosseira e adicionadas à massa cerâmica nas quantidades de 5%, 10% e 15%, em peso substituindo a mesma quantidade de feldspato. Os pós dessas misturas foram prensados e sinterizados em três temperaturas diferentes. As porcelanas sinterizadas foram então caracterizadas através de medidas de porosidade aparente, densidade aparente, absorção de água, módulo de ruptura por flexão de três pontas, difração de raios X, microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS). As composições de porcelana aluminosa e silicosa que foram introduzidos o vidro laminado de granulometria fina apresentaram resultados muito próximos aos das de composição sem adição de vidro laminado.
|
30 |
Estudo experimental das principais características de um dressador sinterizado com ênfase na dissipação de calor / Experimental study on the main characteristics of sintered dressing tools with emphasis on heat dissipationCarlos Elias da Silva Junior 07 April 2004 (has links)
No processo de retificação a dressagem desempenha um papel fundamental, uma vez que ela é responsável pela topografia da superfície de trabalho do rebolo, podendo afetar os resultados da retificação em termos da integridade superficial e precisão dimensional da peça, bem como a confiabilidade do processo. Portanto, como parte integrante da operação de retificação, a dressagem pode melhorar significativamente a qualidade das peças retificadas caso melhores dressadores sejam produzidos. Este trabalho tem o objetivo de estudar as principais características necessárias ao projeto de dressadores sinterizados que utilizam diamantes sintéticos de perfil constante e verificar experimentalmente a distribuição de temperaturas no dressador, obtidas através de ensaios práticos e simulação computacional pelo método dos elementos finitos. O modelo utilizado contém algumas limitações, porém os resultados obtidos mostraram que os níveis de temperaturas no dressador foram afetados pelos parâmetros de dressagem considerados no trabalho, a saber, a profundidade de dressagem (\'a IND. d\'), o grau de recobrimento de dressagem (\'U IND. d\') e a vazão do fluido refrigerante (Q). O desgaste do dressador foi afetado apenas pelos parâmetros de dressagem. / In grinding operations, dressing tools are of major importance, since they are responsible for the topography of the wheel working surface and, consequently, can affect the grinding results in terms of surface integrity, dimensional accuracy and process reliability. Therefore, as an important part of the grinding operation, dressing can significantly improve the quality of ground parts if better dressing tools are produced. This work studies the main needs for designing sintered dressing tools made with constant cross sectional synthetic diamonds. It also analyses the temperature distribution over a novel dressing tool design using experimental measurements to feed computacional simulation by the finite element method (FEM). The temperature model employed showed some limitations but the obtained results indicated that temperature levels over the dressing tool were affected by the dressing parameters considered in this work, namely the dressing depth of cut (\'a IND. d\'), the dressing overlapping parameter (\'U IND. d\') and the flow rate (Q). Additionally, one can say that the dressing tool wear was affected only by the dressing parameters
|