This project mainly investigated how the niobium(Nb) content influences the microstructure and mechanical properties of grey cast iron. Considering the mechanism, the study also analyzes the relationship between microstructure and mechanical properties. Generally, the work is based on 127 test bars/samples from two cylinder heads and three batches of plates, which were studied by measuring tensile strength, microhardness, graphite size, carbide amount and chemistry. The result data has been evaluated with statistical methods. The experiments mainly included the preparation of the samples for test and analysis. The mechanical properties in this study are evaluated by the tensile strength of the grey cast iron. Meanwhile, various microscopies were applied to observe how niobium and cooling rate influence the microstructure. Finally, from the analysis results, it tells that the niobium does affect the tensile strength of grey cast iron. Higher the niobium content is, higher the tensile strength is. The computed result based on the data also shows niobium’s strong effect. The faster cooling rate will increase the tensile strength and pearlite microhardness of grey cast iron as well. The carbide amount of grey cast iron can be increased by the addition of niobium content. Furthermore, some future work needs to be done to explain the unsolved problem in this result. The reasons of why a specific position A-2-d of plates has high values of tensile strength demand more microstructure investigation. For the niobium influence, more experiments and data containing a larger range of niobium content also need to be done to prove the mathematics results in this report. / Detta projekt undersökte huvudsakligen hur innehållet av niob (Nb) påverkar gråstålens mikrostruktur och mekaniska egenskaper. Med tanke på mekanismen analyserar undersökningen även förhållandet mellan mikrostruktur och mekaniska egenskaper. Arbetet baseras i allmänhet på 127 provstänger / prover från två cylinderhuvuden och tre satser av plattor, vilka studerades genom mätning av draghållfasthet, mikrohårdhet, grafitstorlek, karbidmängd och kemi. Resultatdata har utvärderats med statistiska metoder. Experimenten inbegriper huvudsakligen beredningen av proven för test och analys. De mekaniska egenskaperna i denna studie utvärderas av gråstålets draghållfasthet. Under tiden applicerades olika mikroskopier för att observera hur niob- och kylhastigheten påverkar mikrostrukturen. Slutligen, från analysresultaten, berättar den att niobet påverkar draghållfastheten hos grågjutjärn. Ju högre niobinnehållet är, desto högre är draghållfastheten. Det beräknade resultatet baserat på data visar också niobins starka effekt. Den snabbare kylhastigheten ökar också draghållfastheten och pearliten-mikrohårdheten hos grågjutjärn. Karbidmängden av grågjutjärn kan ökas genom tillsats av niobhalt. Vidare måste vissa framtida arbeten göras för att förklara det olösta problemet i detta resultat. Skälen till varför en specifik position A-2-d av plattor har höga dragkrafter kräver mer mikrostrukturundersökning. För niobinpåverkan måste fler experiment och data som innehåller ett större antal niobinnehåll också göras för att bevisa matematikresultaten i denna rapport.

För att nå de Globala målen 2030 kommer vi som samhälle att behöva minska vårt globala ekologiska fotavtryck avsevärt. Textilbranschen står idag för en betydande del av detta ekologiska fotavtryck både genom markanvändning, klimatpåverkande utsläpp, förorening av mark och vatten med mera. Detta har lett till att man inom textilbranschen idag efterfrågar allt mera hållbara lösningar. Det finns ett antal sorters garn som bidrar med lägre miljöpåverkan på olika sätt, dock förekommer dessa idag mindre frekvent på marknaden. Dessa material skulle kunna vara en del av lösningen på textilindustrins stora miljöpåverkan idag. Ett av dessa material som vi valt att titta närmare på var pappersgarn, som vid framställning förbrukar betydligt mindre resurser som vatten, tillsatskemikalier och energi (Fakirov 2015). Pappersgarnets utveckling har dock än så länge begränsats av dess styvhet och dåliga stickbarhet. Detta projektetet har syftat till att försöka minska pappersgarnets styvhet och öka dess stickbarhet genom att tvinna det med olika antal garnsnodd av viskosgarn. Vi tvinnade ett entrådigt 17 tex hampaviskosgarn på 100, 300 och 500 garnsnodd/meter med kärnspunnen metoden. Sedan behandlades garnet med fettsyra för att motverka sprödheten och förbereda för stickning. Garnet stickades på en rundstickmaskin med bindningen slätstickning. Tester som gjordes på garn var dragprovning och friktion. På trikån utfördes också dragprovning(bristning) men även styvhetsprovning samt nötningsprovning. Trikå av blandgarn visades sig tillföra mjukare känsla på tyget jämfört med endast papper. Vid dragprovning av trikå framkom det att större andel av viskos tillför mer styrka i och med att det behövdes högre tryck samt tid för att uppnå brott på trikån. Tvinning med olika antal garnsnodd av viskosgarn har visat sig medföra små skillnader gällande stickbarhet då det tidvis uppstod hål på de fyra olika tyger som stickades under stickningsprocessen. Garner av 300- och 500 garnsnodd/meter hade dock flest svaga punkter (brott på pappersgarnet) utan att uppvisa synbara hål på tyget. Skillnader i styvhet av trikån var kännbara mellan alla tygen, dock gick det inte att få användbara resultat från styvhetsprovaren då denna testmetod var olämplig för den valda trikåbindningen eftersom tyget rullade sig. / To achieve the Global Goals 2030, we as a society will need to significantly reduce our global ecological footprint. The textile industry of today accounts for a significant part of this ecological footprint both through use of land, climate-affecting emissions, soil- and water pollution and more. This has led to an increasing demand for more sustainable solutions in the textile industry. There are a number of types of yarn that have a lower environmental impact. Many of them however have quite a lower market share today. One of these materials that we chose to take a closer look at was paper yarn, which in it’s production consumes significantly less resources than other usual yarns on the market (Fakirov 2015). However, the development of use of paper yarn has so far been limited by its rigidity and poor knitability. This project has aimed to try to reduce the stiffness of the paper yarn and increase its knitability. This was done by twisting different numbers of twist/meter of viscose yarn, around the paper yarn. We twisted a single-threaded 17 tex hemp viscose yarn around the paper yarn at 100, 300 and 500 twist/meter with the core-spun method. Then the yarn was treated with fatty acid to counteract the brittleness and prepare it for knitting. The yarn was knitted on a circular knitting machine with a single jersey stitch. Tests done on yarn were tensile testing and friction testing. The tricot also was subjected to tensile testing (rupture), stiffness testing and abrasion testing. Viscose mixed yarn knitwear was found to have a softer feeling of the fabric compared to just knitted paper yarn. During tensile testing of tricot, it was found that a larger proportion of viscose adds more strength as higher pressure was needed as well as time to achieve a stretch in the tricot. Twisting with different twists of viscose yarn has been shown to cause small differences in knitability as there were occasional holes in the paper yarn knit during the knitting process. Yarns of 300 and 500 twist/meter, however, had the most weak points without showing visible holes on the fabric. Differences in the stiffness of the tricot were noticeable between all the fabrics, however, it was not possible to obtain useful results from the stiffness tester as this test method was probably unsuitable for the selected tricot binding because the fabric rolled.

The strength of leaf fibers and the nutritional value of the edible fruit of several yucca species native to the U.S. southwest were studied to aid in the determination of species best suited for commercial cultivation by the Navajo Nation. The leaves were softened in an autoclave to facilitate the removal of the leaf matrix, conditioned in environmentally controlled chambers, and the fibers were broken using a texture analyzer. The fibers were frozen and cross sectioned and photographed to determine cross sectional area. Official methods were used to determine the nutritional content of the fruit. The mean tensile strength of Y. angustissima, Y. baccata, and Y. glauca was 484 ±79, 710±174, and 388±104 MPa, respectively. Fibers from the leaves of Y. baccata had a significantly higher tensile strength than the leaves of the other two species. Nutritional profiling of the fruit of Y. angustissima and Y. baccata indicated that the fruit of both species are good sources of vitamin C (73-119 mg/100g) and thiamin (0.20 to 0.22 mg/100g). Because of its edible fruit and superior leaf fiber tensile strength, Y. baccata is recommended as the best species for cultivation and commercialization.

Det talas allt oftare om de problem som världens plastanvändning åsamkar miljön genom exempelvis nedskräpning och mikroplaster. Det finns många olika typer och användningsområden för plast. Den typ som anses värst i avseende till miljöpåverkan är plasten som används en gång och sedan förlorar sin funktion, det som idag kallas engångsplast. Ett av de vanligaste områdena där engångsplast används är inom förpackningsindustrin för livsmedel. År 2019/2020 växte en projektidé bland en grupp elever om att se över alternativa förpackningsmaterial till främst frukt och grönt i matvaruhandeln. Idéen utvecklades och vid en expo på Textilhögskolan år 2020 presenterades ett citrusnät för ekologiska citroner stickat på en manuell stickmaskin i pappersgarn. Som fortsättning på arbetet är nu nästa steg att undersöka möjligheterna att sticka en motsvarande prototyp på en industriell maskin och vilka utmaningar som följer. Stickningen genomfördes i Borås på Textilhögskolans trikålabb. Maskinen som användes är en flatsticksmaskin av typen STOLL CMS822 HP knit and wear. Pappersgarn av olika garnnummer kom uteslutande från företaget OJO+ Fibers och baseras på pappersmassa från manillaplantan. Två bindningar stickades, en mesh-bindning och en stickning med flotteringar. Mesh-bindningen testades även med garn av olika garnnummer och olika antal ingående garn. De viktigaste parametrarna för möjligheten att sticka på industriell flatsticksmaskin visade sig vara garnets styrka, styvhet samt maskinens delning. Efter två separata produktionsgenomgångar genomfördes en visuell bedömning som avgjorde vilka stickningar som lämpade sig att gå vidare till ett dragprovstest. Standarden som användes för dragprovstest var (SS-EN ISO 13934–1:2013) och genomfördes på en Tinius Olsen H10KT (Elastocon). Fem provkroppar av varje stickning testades först i torrt- och sedan vått tillstånd genom blötläggning enligt standard. För att jämföra data från dragprovstestningen genomfördes en variansanalys för att upptäcka eventuella skillnader mellan de olika konstruktionerna. Variansanalys genomfördes även inom varje grupp för att undersöka skillnader mellan torra och våta prover av samma konstruktion. Resultatet från dragprovet visar en stor spridning i datamaterialet. På grund av spridningen går det inte att statistiskt säkerställa några slutsatser kring vilken konstruktion som är starkast. Främsta anledningen till spridningen är avvikelser från standarden som var nödvändiga för att genomföra testingen samt faktumet att (SS-EN ISO 13934–1:2013) huvudsakligen är till för vävda varor, ej stickade. Två av mesh-konstruktionerna kunde påvisa signifikant skillnad i mätresultatet mellan de våta respektive torra proverna, som då visade en svag tendens till att de våta proverna klarade högre spänning. Detta kan komma till användning för att enkelt öka garnets styrka vid stickning. / There’s an ongoing worldwide discussion regarding the environmental impact of plastic use. Single- use plastic is considered one of the most problematic due to the loss of functionality after one use. A common industry using single-use plastic is the food packaging industry. In 2019/2020, a project idea grew to review alternative packaging materials for fruits and vegetables. A prototype was presented at the Swedish School av Textile’s expo in 2020, a citrus net hand-knitted in paper yarn for organic lemons. The next step was to investigate the possibility of knitting paper nets on industrial machines and what difficulties may arise. The knitting was carried out in the Textilhögskolan in Borås machine hall on a flat knitting machine, a STOLL CMS822 HP knit and wear. The paper yarn used came exclusively from OJO+ Fibers and was made from pulp from the manilla plant. Two bindings were knitted, one mesh and one with floatations. The mesh binding was knitted in multiple variations, yarn of different yarn numbers and numbers of ingoing yarns. The most important parameters for knitting on industrial machines turned out to be the strength of the yarn, stiffness and gauge of the machine. A visual assessment was carried out after two separate production reviews and determined which knits were suitable to proceed to a tensile test. The standard used for tensile tests was (SS-EN ISO 13934-1:2013) on a Tinius Olsen H10KT (Elastocon). Five specimens of each knit were tested, first in the dry state and then in the wet state. A variance analysis compared the data from the tensile test, partly between the different constructions and between dry and wet samples within each group. The result shows a large spread within the data material, which cannot determine with certainty any conclusions about which construction is the strongest. The main reason for this spread is necessary deviations from the standard and the fact that (SS-EN ISO 13934-1:2013) is mainly for woven goods, not knitted ones. Two mesh constructions demonstrated a significant difference in results between the wet and dry samples. A weak tendency showed wet samples withstanding higher stress than dry ones, which could be a solution to increase the strength of the yarn while knitting.

京都大学 / 新制・課程博士 / 博士(工学) / 甲第24228号 / 工博第5056号 / 新制||工||1789(附属図書館) / 京都大学大学院工学研究科マイクロエンジニアリング専攻 / (主査)教授 土屋 智由, 教授 平方 寛之, 教授 江利口 浩二 / 学位規則第4条第1項該当 / Doctor of Philosophy (Engineering) / Kyoto University / DFAM

Heart valve disease is currently one of the leading forms of heart disease. Current literature has shown that endothelin I, angiotension II and 5-HT are vasoactive agents which cause concentration dependent contractions in aortic valve leaflet tissue. This study tested the mechanical properties of leaflets cut in the radial direction after they were exposed to the agents at varied concentrations or for 0.5, 6 or 24 hours. The elastic modulus, ultimate tensile strength and the yield strength were calculated. In the time trials the elastic modulus and the ultimate tensile strength both showed a significant increase at 24-hours. However, there were no significant differences found between the concentrations. Indicating the amount of vasoactive agent is not as significant as the length of exposure.

An evaluation of aged hot-mix asphalt (HMA) pavements was accomplished to develop a method for improving the prediction of remaining fatigue life of aged HMA surfaces. This is important for both planning Department of Defense airfield maintenance funds and for predicting the performance of operating surfaces in the theater of operation. This study involved the evaluation of HMA at several military airfields. After field inspections and field testing, slab samples were carried to the U.S. Army Engineer Research and Development Center for laboratory testing. Laboratory testing included the determination of mixture and binder properties, indirect tensile strength tests on cored specimens, and beam fatigue tests. The results from this study were used to develop improved fatigue performance predictions for field-aged HMA pavements.

No description available.

No description available.

No description available.