Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets. In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO2 particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L10 phase. The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L10 order, rapid thermal annealing can lead to the formation of chemically ordered FePt fifilms with (001) texture on amorphous SiO2/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneuosly to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 °C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO2 particle templates with periods down to 50 nm. The addition of Cu improves the (001) texture formation and chemcial ordering for annealing temperatures T < 600 °C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated using e-beam and nanoimprint lithography have been investigated.

The homo and hetero dimerisation of two spectroscopically different chromophores were studied, namely: 4,4-difluoro-4-bora-3a,4a-diazas-indacene (g-BODIPY) and its 5-styryl-derivative (r-BODIPY). Various spectroscopic properties of the r-BODIPY in different common solvents were determined. It was shown that g- and r-BODIPY in the ground state can form homo- as well as hetero dimers. We demonstrate that the ganglioside GM1 in lipid bilayers of 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC) exhibits a non-uniform lateral distribution, which is an argument in favour of self-aggregation of GM1 being an intrinsic property of the GM1. This was concluded from energy transfer/migration studies of BODIPY-labelled gangliosides. An algorithm is presented that quantitatively accounts for donor–donor energy migration (DDEM) among fluorophore-labelled proteins forming regular non-covalent polymers. The DDEM algorithm is based on Monte Carlo (MC) and Brownian dynamics (BD) simulations and applies to the calculation of fluorescence depolarisation data, such as the fluorescence anisotropy. Thereby local orientations, as well as reorienting motions of the fluorescent groups are considered in the absence and presence of DDEM among them. A new method, in which a genetic algorithm (GA) was combined with BD and MC simulations, was developed to analyse fluorescence depolarisation data collected by the time-correlated single photon counting technique. It was applied to study g-BODIPY-labelled filamentous actin (F-actin). The technique registered the local order and reorienting motions of the fluorophores, which were covalently coupled to cysteine 374 (C374) in actin and interacted by means of electronic energy migration within the polymer. Analyses of F-actin samples composed of different fractions of labelled actin molecules revealed the known helical organiszation of F-actin, and demonstrated the usefulness of this technique for structure determination of complex protein polymers. The distance from the filament axis to the fluorophore was found to be considerably less than expected from the proposed position of C374 at a high filament radius. In addition, polymerisation experiments with BODIPY-actin suggest a 25-fold more efficient signal for filament formation than pyrene-actin.

No description available.

No description available.

No description available.

No description available.

Die Ursache für das idiopathische Stottern ist bis zum jetzigen Zeitpunkt unbekannt. Typischerweise beginnt die Redeflussstörung im Vorschulalter. Es wird davon ausgegangen, dass 1% der Bevölkerung an Stottern leidet. Bei der Frage nach pathophysiologischen Hintergründen von Sprech- und Sprachstörungen ist der Zusammenhang zwischen einer pathologischen, funktionellen Lateralisierung und einer morphologischen Asymmetrie im Bereich von neuronalen Netzwerken der Sprachbildung bereits seit längerem Gegenstand der Forschung. Im Rahmen der vorliegenden Arbeit wurde die Lateralisierung von Sprache bei 17 stotternden Probanden und 20, im Alter entsprechenden, flüssig sprechenden Probanden untersucht. Hierbei wurde die Sprachlateralisierung mithilfe der fMRT sowohl mit einem Satz- als auch mit einem Wortgenerierungsparadigma ermittelt. Ausgehend von den in der fMRT ermittelten Sprachzentren wurde die angrenzende weiße Substanz unter Verwendung der DTI auf eine Asymmetrie hin untersucht. Im Vergleich zu der Gruppe der Normalprobanden zeigten die schwer stotternden Probanden eine Verschiebung der Indexwerte, deren endgültige Ursache offen bleibt. Gesteigerte funktionelle Aktivierung in Bereichen der rechtshemisphärischen Analoga der Sprachzentren scheint ein möglicher Erklärungsansatz. Vorausgegangene funktionelle Untersuchungen u. a. mittels PET und fMRT bei stotternden Probanden belegten eine Überaktivierung von Teilen des motorischen Kortex sowie eine atypische Lateralisierung bei der Produktion von Sprache mit rechtsseitiger Lateralisierung oder eine bilaterale Aktivität. Darüber hinaus zeigte sich eine morphologische Veränderung, im Sinne einer Abnahme einer linkshemisphärischen Asymmetrie bei den schwer stotternden Probanden, besonders in der an das Wernicke-Areal angrenzenden weißen Substanz. Mithilfe der VBM konnten in mehreren früheren Studien morphologische Unterschiede bei Stotternden gezeigt werden. Gegenüber dem rein morphologischen Untersuchungsansatz vorangegangener Untersuchungen berücksichtigte die Kombination der funktionellen und der diffusionsgewichteten Analyse stärker die intraindividuelle Variabilität der Sprachzentren.

No description available.

In the present work, the influence of the morphology of thin ferromagnetic films on their static as well as dynamic magnetic properties was investigated by means of broadband ferromagnetic resonance (FMR). Using an ion beam erosion process the surface of the substrates was periodically modulated (ripples), where the modulation wavelength is determined by the ion energy. In this way a well-controllable roughness profile evolves ranging from a few ten up to several hundreds of nanometers in wavelength. The substrate’s surface profile in turn is repeated by films grown on top offering an easy and fast approach to investigate morphology influences on the magnetic properties. This work aims on modifications of the magnetic anisotropy as well as the FMR linewidth of the magnetic relaxation process. Prior to magnetic investigations the existing FMR setup was extended to measure FMR spectra at a fixed microwave frequency while sweeping the external magnetic field. Furthermore, a software toolbox was developed to perform the data processing and evaluation. Starting with the morphology influence on the magnetic anisotropy 10 nm thin Fe, Co, and Ni81Fe19 (Permalloy ≡ Py) films were deposited on rippled Si substrates. Due to Si displacements during ion erosion and natural oxidation the rippled Si substrates exhibit an amorphous surface causing a polycrystalline material growth. This leads to a suppression of magneto-crystalline anisotropy leaving only morphology-induced anisotropy contributions. Here, a uniaxial magnetic anisotropy (UMA) was observed that aligns its easy axis with the ripple ridges, whereas its strength decays with increasing ripple wavelength for all materials. From thickness-dependent measurements two characteristic regions were determined with competing uniaxial volume and surface anisotropy contributions. Underlined by micromagnetic simulations a dominant volume contribution was found in the thin region accompanied by magnetic moments nearly following the surface corrugation. In the thick region the UMA is controlled by dipolar stray fields at the surface. In contrast to Si, ion eroded MgO keeps its crystal structure offering epitaxial growth of 10 nm thin single-crystalline Fe films. Consequently, a superposition of morphology-induced UMA and magneto-crystalline cubic anisotropy was observed. The direction of the ripple ridges is predetermined by the incident ion beam, which allows to freely orient the UMA’s direction with respect to the cubic anisotropy, offering a possibility for anisotropy engineering. In comparison to the planar reference case rippled magnetic films exhibit lower intrinsic and extrinsic relaxation contributions. For the final part, 30 nm Py was grown on rippled Si covering modulation wavelengths λ ranging from 27 to 432 nm. Using magnetic force microscopy and holography measurements the dipolar stray fields above and inside the magnetic layer were characterized. For λ ≥ 222 nm, the stray fields act as scattering centers for spin waves triggering two-magnon scattering (TMS). This causes an apparent line broadening generating distinct peaks in the frequency-dependent linewidth whose position can be tuned by altering λ. These effects are understood in the framework of a perturbation theory of spin waves in periodically perturbed films recently presented in the literature. Furthermore, the in-plane angular dependence of the linewidth revealed a two-fold symmetry, which is not present for vanishing TMS at small λ. / In Rahmen dieser Arbeit wurde der Einfluss der Morphologie eines dünnen ferromagnetischen Films auf dessen statische und dynamische Eigenschaften mittels breitbandiger ferromag- netischer Resonanz (FMR) untersucht. Durch Ionenstrahl-Erosion wurde die Oberfläche des verwendeten Substrats periodisch moduliert (Ripple), wobei die Wellenlänge der Modulation durch die Ionenenergie bestimmt ist. Dies ermöglicht die kontrollierte Herstellung rauer Oberflächen mit Wellenlängen zwischen wenigen zehn bis zu einigen hundert Nanometern. Werden auf diesen Oberflächen Filme abgeschieden, übernehmen diese die Modulation. Somit ergibt sich eine einfache und schnelle Untersuchungsmöglichkeit der magnetischen Filmeigenschaften in Hinblick auf die Morphologie. Das Ziel dieser Arbeit ist die Untersuchung von Morphologieeinflüssen auf die magnetische Anisotropie sowie FMR-Linienbreite. Im Vorfeld der magnetischer Untersuchungen wurde der bestehende FMR-Aufbau um einen Messmodus erweitert, sodass Messungen bei fester Mikrowellenfrequenz und gleichzeitigem Durchfahren eines externen magnetischen Feldes möglich wurden. Weiterhin wurde ein Softwarepaket für die Datenauswertung entwickelt. Beginnend mit dem Morphologieeinfluss auf die magnetische Anisotropie wurden 10 nm dünne Fe, Co und Ni81Fe19 (Permalloy ≡ Py) Filme auf periodisch moduliertem Si abgeschieden. Durch Versetzungen während der Ionenstrahl-Erosion und Bildung einer natürlichen Oxidschicht bildet sich bei den verwendeten Substraten eine amorphe Oberfläche, was zu polykristallinem Schichtwachstum führt. Dadurch wird die magneto-kristalline Anisotropie unterdrückt und morphologie-induzierte Beiträge bestimmen die Anisotropie. Beobachtet wurde eine induzierte uniaxiale magnetische Anisotropie (UMA), deren leichte Richtung sich entlang der Ripple-Wellenzüge ausrichtet. Mittels schichtdickenabhängigen Messungen wurden zwei charakteristische Regionen mit konkurrierender uniaxialer Volumen- und Oberflächenanisotropie ermittelt. Dabei ist die Volumenkomponente im Bereich dünner Schichten vorherrschend und die magnetischen Momente richten sich entlang der Oberflächenmodulation aus. Für dickere Schichten ist die UMA dahingegen durch dipolare Streufelder bestimmt. Die experimentellen Funde werden in beiden Bereichen durch mikromagnetische Simulationen untermauert. Im Gegensatz zu erodiertem Si behält MgO seine Kristallstruktur, was epitaktisch gewachsene, einkristalline Fe-Schichten von 10 nm Dicke ermöglicht. Folglich wurde eine Überlagerung aus induzierter und kristalliner Anisotropie beobachtet. Dadurch, dass die Richtung der Ripple durch die Richtung des Ionenstrahls während der Erosion vorgegeben wird, lässt sich die UMA frei gegen die kristalline Anisotropie drehen, was wiederum Möglichkeiten zur gezielten Beeinflussung der Anisotropie bietet. Im Hinblick auf die dynamischen magnetischen Eigenschaften führen Ripple zu einer Verringerung der intrinsischen und extrinsischen Relaxationsbeiträge. Für den letzten Teil der Arbeit wurde 30 nm dünnes Py auf Si-Ripple gewachsen, wobei ein Wellenlängenbereich von λ = 27 nm bis 432 nm abgedeckt wurde. Mit Hilfe von magnetischer Kraftmikroskopie und Holographie wurden die dipolaren Streufelder über und in den Filmen untersucht. Ab λ ≥ 222 nm ermöglichen diese dipolaren Felder eine Streuung von Spinwellen, sodass Zwei-Magnonen-Streuung (TMS) auftritt. Dies führt zu einer scheinbaren Linienverbreiterung und äußert sich durch einzelne Peaks in der frequenzabhängigen Linienbreite. Letztere lassen sich in ihrer Frequenzposition durch die Wellenlänge des Substrates beeinflussen und können mittels einer kürzlich in der Literatur veröffentlichten Störungstheorie für Spinwellen in periodisch gestörten Filmen erklärt werden. Weiterhin wurde in der winkelabhängigen Linienbreite eine zweifache Symmetrie beobachtet, welche durch die TMS hervorgerufen wird und folglich nicht bei kleinen Wellenlängen zu beobachten ist.

MnSi(111) films were grown on Si(111) substrates by solid phase epitaxy (SPE) and molecular beam epitaxy (MBE) to determine their magnetic structures. A lattice mismatch of -3.1% causes an in-plane tensile strain in the film, which is partially relaxed by misfit dislocations. A correlation between the thickness dependence of the Curie temperature (TC) and strain is hypothesized to be due to the presence of interstitial defects. The in-plane tensile strain leads to an increase in the unit cell volume that results in an increased TC as large as TC = 45 K compared to TC = 29.5 K for bulk MnSi crystals. The epitaxially induced tensile stress in the MnSi thin films creates an easy-plane uniaxial anisotropy. The magnetoelastic coefficient was obtained from superconducting quantum interference device (SQUID) magnetometry measurements combined with transmission electron microscopy (TEM) and x-ray diffraction (XRD) data. The experimental value agrees with the coefficient determined from density functional calculations, which supports the conclusion that the uniaxial anisotropy originates from the magnetoelastic coupling. Interfacial roughness obscured the magnetic structure of the SPE films, which motivated the search for a better method of film growth. MBE grown films displayed much lower interfacial roughness that enabled a determination of the magnetic structure using SQUID and polarized neutron reflectometry (PNR). Out-of-plane magnetic field measurements on MBE grown MnSi(111) thin films on Si(111) substrates show the formation of a helical conical phase with a wavelength of 2?/Q = 13.9 ± 0.1 nm. The presence of both left-handed and right-handed magnetic chiralities is found to be due to the existence of inversion domains that result from the non-centrosymmetric crystal structure of MnSi. The magnetic frustration created at the domain boundaries explains an observed glassy behaviour in the magnetic response of the films. PNR and SQUID measurements of MnSi thin films performed in an in-plane magnetic field show a complex magnetic behaviour. Experimental results combined with theoretical results obtained from a Dzyaloshinskii model with an added easy-plane uniaxial anisotropy reveals the existence of numerous magnetic modulated states that do not exist in bulk MnSi. It is demonstrated in this thesis that modulated chiral magnetic states can be investigated with epitaxially grown MnSi(111) thin films on insulating Si substrates, which offers opportunities to investigate spin-dependent transport in chiral magnetic heterostructures based on this system.