Conselho Nacional de Desenvolvimento Científico e Tecnológico / While seemingly inert appearance, bones are highly dynamic structures, which promote formation, resorption, repair and maintenance of homeostasis. Fractures in bones occur when the load applied to a specific bone region exceeds its resilience. The use of external skeletal fixator (ESF) is a method of fairly common internal stabilization, in which connector bars polymethylmethacrylate (PMMA) are used without criterion in diameter. In these cases, it can break if it gets too thin or too heavy and uncomfortable when bulky. The aim of this study was to test biomechanical through axial compression and bending, considering different connector bar diameter PMMA correlated to bone diameter for use to type Ia ESF. For this, it was collected 24 swine humerus to make measurements of length, diameter, circumference and testing biomechanical. After the bars confected with 1.5 times the average diameter of the bone (group I), the same diameter bone (group II) and 0.5 times the diameter of the bone (group III). The results obtained, it was observed that the connector bars in group II were more resistant than the bones in the compression test. In the bending test, the bones resisted flexion strength when compared to group III. The group II was 4.3 times more resistant than Group III in the same mechanical test. The results allow a direction for making bars PMMA considering bone diameter as a reference. / Apesar do seu aspeto aparentemente inerte, os ossos são estruturas altamente dinâmicas, envolvidas em constante formação, reabsorção, reparação e manutenção da homeostasia. As fraturas ocorrem quando a carga aplicada sobre determinada região do tecido ósseo supera sua capacidade de resistência. A utilização de fixadores esqueléticos externos (FEE) é método de estabilização interna bastante frequente, no qual podem ser utilizadas barras conectoras de polimetilmetacrilato (PMMA) sem preocupação com o diâmetro. Tais barras podem quebrar se ficarem muito delgadas ou tornarem-se desconfortáveis quando volumosas e pesadas. O objetivo deste trabalho foi testar, por meio de ensaio biomecânico de compressão axial e flexão, qual é o diâmetro mais adequado para a barra conectora de PMMA, correlacionado as dimensões da barra com o diâmetro ósseo para FEE tipo Ia. Para tanto, coletaram-se 24 úmeros suínos para a realização de medidas de comprimento, diâmetro, circunferência e os ensaios biomecânicos. Após, confeccionaram-se barras de 1,5 vezes a média do diâmetro ósseo (grupo I), do mesmo diâmetro (grupo II) e 0,5 vez o diâmetro ósseo (grupo III). Com os resultados obtidos ao comparar os valores dos ossos com os dos grupos II e III, verificou-se que as barras conectoras do grupo II mostraram-se mais resistente do que o tecido ósseo no ensaio de compressão. No ensaio de flexão, o osso foi mais resistente à força de flexão quando comparados ao grupo III. O grupo II foi 4,3 vezes mais resistente do que o grupo III nesse mesmo ensaio. O grupo I apresentou secagem incompleta, onde seu comportamento não foi similar com o restante dos grupos, por isso, não participou da estatística do trabalho. Os resultados permitem um direcionamento para confecção de barras de PMMA do mesmo diâmetro ósseo, sendo suficiente para sustentar sem quebrar um FEE tipo Ia.

O Brasil, à semelhança de outros países, está envelhecendo rapidamente. Os indivíduos com mais de 60 anos compõem hoje o segmento que mais cresce em termos proporcionais, mostrando um incremento da ordem de 500%, em 40 anos. A estimativa para o ano de 2020 é de que o Brasil tenha em torno de 32 milhões de indivíduos idosos, e desta população, uma parcela significativa será parcial ou totalmente desdentada, necessitando de aparelhos protéticos. Apesar da Odontologia apresentar avanços científicos notáveis na reabilitação da saúde bucal, muitos ainda usarão estes aparelhos. Sabe-se que o uso contínuo de próteses pode propiciar o desenvolvimento da estomatite protética, cuja etiologia é multifatorial, destacando-se principalmente a má higiene bucal e da prótese, e geralmente associada à presença de Candida albicans. Desta forma, há necessidade de se propor um método de desinfecção, que se mostre eficaz, que seja seguro quanto à toxicidade, que represente baixo risco ocupacional, que seja de fácil manuseio e que não interfira nas propriedades dos materiais utilizados na confecção destes aparelhos. Portanto, a proposição deste trabalho foi avaliar a influência de dois métodos de desinfecção, nas propriedades das resinas acrílicas empregadas na confecção das próteses.As propriedades avaliadas foram: resistência e módulo de flexão, resistência ao impacto Izod, microdureza Knoop, rugosidade, massa específica e grau de inchamento, grau de conversão do monômero, temperatura de transição vítrea, sorção e solubilidade. Os corpos de prova foram confeccionados de acordo com os requisitos de cada ensaio, tanto para os grupos controle (sem tratamento), quanto para os tratados (submetidos a um dos processos de desinfecção). Os tratamentos de desinfecção consistiram de: a) irradiação com energia de microondas na potência de 840 W, durante 1 minuto; b) imersão em ácido peracético durante 5 minutos. A eficácia da desinfecção foi avaliada através de ensaios microbiológicos que consistiram em verificar o crescimento no meio de cultura e na superfície do corpo de prova de Candida albicans, após a desinfecção dos corpos de prova, previamente contaminados com uma cepa conhecida do fungo (ATCC 10231). Como as resinas acrílicas são materiais muito utilizados em todas as áreas de atuação da Odontologia, o conhecimento das suas propriedades é de interesse do cirurgião-dentista. As resinas acrílicas tipo 1 (de termopolimerização), tipo 2 (quimicamente ativada) e tipo 5 (ativada por microondas) foram avaliadas neste trabalho. Os resultados mostraram que as resinas acrílicas tipo 1 e tipo 5 apresentam valores semelhantes em todas as propriedades analisadas. A resina acrílica tipo 2 apresentou valores inferiores àqueles encontrados nas tipo 1 e 5. O ciclo de polimerização com melhores resultados foi aquele proposto pelo respectivo fabricante daresina acrílica. A presença de fibras de nylon e de corante não influenciou as propriedades da resina acrílica tipo 5. Das técnicas de desinfecção, a imersão em ácido peracético apresentou os melhores resultados para todas as propriedades avaliadas ao longo do tempo de 20 meses. Por outro lado a irradiação de microondas, a longo prazo, apresentou os piores resultados para todas as propriedades avaliadas. Ambas as técnicas de desinfecção foram eficazes do ponto de vista microbiológico. Mas, para o uso prolongado, a técnica de desinfecção com ácido peracético pode ser recomendada com toda a segurança, no que diz respeito às propriedades avaliadas neste trabalho. / Brazil, similar to other countries, is aging quickly. The individuals with more than 60 years old compose today the segment that more grows in proportional terms, showing an increment of about 500% in 40 years. The estimate for 2020 is that Brazil has around 32 million elderly and a significant parcel of them will be partial or totally toothless, needing prosthetic equipments. In spite of notable scientific advance in the rehabilitation of the oral health, many people still will use these equipments. The continuous use of the prosthesis can propitiate the development of denture stomatitis, whose etiology is multifactorial, being generally, associated to the presence of fungus Candida albicans. Bad oral hygiene and prosthesis is still distinguished as factor of risk. Therefore, it very necessary for the elderly a efficient, safe and easy handling method of disinfection with low occupational risk and that doesn’t intervene with the properties of the materials used in the confection of these prosthetic equipments. The aim of this work is to evaluate the influence of two disinfection methods on the properties of acrylic resin used in the confection of dental prosthesis. Samples had been confectioned in accordance with the requirements of each test for the control groups (without treatment), as for the treated (submitted to one of the disinfection process). The evaluated properties had been resistance and module of flexure, Izod impact, Knoop microhardness, rugosity, specific mass and degree of swelling, degree of conversion of monomer, glass transition temperature, sorption and solubility. The treatments of disinfection had consisted of: a) irradiation with energy of microwaves, in the power of 840 W, during 1 min, or b) immersion in peracetic acid during 5 min. The effectiveness of the disinfection was evaluated by means of microbiological tests, in which was verified the occurrence of growth of Candida albicans through of culture and sample surface. For that, the samples were previously contaminated with one type of fungus (known as ATCC 10231) and, after, submitted to one of the two considered processes of disinfection. The work was studied the behavior of three commercial acrylic resins of dental use: acrylic resins of thermal polymerization, self-polymerization and polymerization for energy of microwaves (type 1, 2 and 5 respectively) from two different suppliers The results had shown that the acrylic resins of type 1 and type 5 presented similar values in all the analyzed properties. The acrylic resins of type 2 had also similar values in all the properties, but statistically lower than ones of type 1 and 5. The best polymerization cycle, which did not modify the resin properties, was that one considered by the respective manufacturer of the acrylic resin. The nylon fiber presence and colouring did not influence the properties of the acrylic resin of type 5. The first irradiation with microwaves significantlyincreased the evaluated properties and the first immersion in peracetic acid did not modify these properties, in comparison to the control groups. After 20 months, the immersion in peracetic acid did not modify the properties of the material, while the microwave irradiation showed alterations in some properties. Both disinfection techniques had been efficient of the microbiological point of view. On the basis of these results, can be concluded that the microwave irradiation after the polymerization of the material (first cycle), can be recommended, since it increased all the values of the evaluated properties, specially to the conversion degree monomer/polymer. Nevertheless, for prolonged use, the disinfection by means of the immersion in peracetic acid must be recommended, it is efficient for elimination of fungal microorganism and security, characterized for the maintenance of the properties of the acrylic resin evaluated in this work.

Placas oclusais são dispositivos intraorais utilizados no manejo de pacientes que apresentam desordens do sono, migrânia do tipo tensional e outros. No entanto são os cirurgiões dentistas que predominantemente utilizam as placas oclusais como tratamento do equilíbrio das arcadas dentárias nas disfunções temporomandibulares, prevenção de desgaste dental em pacientes com hábitos parafuncionais e na prevenção de traumas em atletas. Vários métodos têm sido empregados para reforçar resinas acrílicas, como reforço metálico e atualmente a incorporação de diferentes tipos de fibras tais como: carbono, polietileno e vidro. Contudo a adição de fibras de vidro com partículas menores em algumas propriedades mecânicas ainda permanecem desconhecidas. Objetivo: O objetivo desse estudo foi avaliar algumas propriedades mecânicas como a rugosidade de superfície, microdureza, módulo de elasticidade e resistência flexural em resinas acrílicas após a incorporação de fibras de vidro particuladas pré silanizadas. Material e método: Para avaliação das propriedades foram confeccionados vinte e quatro corpos de prova (65 x 10 x 3 mm) de cada marca comercial de resina acrílica, utilizadas para confecção de placas oclusais, Vipi Flash (autopolimerizável), Vipi Wave (termopolimerizável por calor de microondas), Vipi Crill, Lucitone e QC-20 (termopolimerizáveis por calor de banho de água), sendo doze corpos-de-prova controles, e doze experimentais, com adição de 10% em peso de fibras de vidro particuladas (Reforplás S/A, São Paulo, SP, Brasil). Após a realização do acabamento superficial dos corpos de prova com lixas de carborundum e feltros era realizada a avaliação da rugosidade superficial em rugosímetro (Mitutoyo®) com três leituras ao longo dos corpos-de-prova, a microdureza Vickers era analisada em um microdurômetro (Micro Hardness Tester, Shimadzu, Japan) com cinco mensurações em cada corpo-de-prova, e para avaliar os ensaios de resistência flexural e módulo de elasticidade os corpos-de-prova foram avaliados por meio uma máquina de ensaios universal (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), com velocidade de 5mm/min. Os dados foram analisados estatisticamente, usando testes paramétricos e não paramétricos, de acordo com a distribuição da amostra. Resultados: As médias e desvios padrões do teste de rugosidade superficial em Ra foram Vipi Flash sem fibra (0,10 ± 0,03); Vipi Flash com fibra (0,12 ± 0,01); Vipi Wave sem fibra (0,16 ± 0,02); Vipi Wave com fibra (0,13 ± 0,02); Vipi Cril sem fibra (0,12 ± 0,03); Vipi Crill com fibra (0,15 ± 0,03); Lucitone sem fibra (0,10 ± 0,02); Lucitone com fibra (0,09 ± 0,04); QC-20 sem fibra (0,11 ± 0,02) e QC-20 com fibra (0,18 ± 0,03). As médias e desvios-padrão ao teste de microdureza Knoop com relação às marcas comerciais foram: Vipi Flash sem fibra (15,35 ± 0,3); Vipi Flash com fibra (15,51 ± 0,4); Vipi Wave sem fibra (16,60 ± 0,8); Vipi Wave com fibra (17,25 ± 0,9); Vipi Cril sem fibra (17,78 ± 2,27); Vipi Crill com fibra (18,02 ± 1,0); Lucitone sem fibra (15,72 ± 0,3); Lucitone com fibra (16,69 ± 0,6); QC-20 sem fibra (15,91 ± 0,4) e QC-20 com fibra (15,63 ± 0,2). As médias e desvios-padrão ao teste de módulo de elasticidade foram: Vipi Flash sem fibra (2952,76 ± 292,12); Vipi Flash com fibra (3373,49 ± 403,76); Vipi Wave sem fibra (2511,69 ± 304,09); Vipi Wave com fibra (3225,01 ± 248,66); Vipi Cril sem fibra (2745,61± 288,86); Vipi Crill com fibra (3671,67 ± 329,91); Lucitone sem fibra (1904,53 ± 149,05); Lucitone com fibra (3056,87 ± 126,11); QC-20 sem fibra (1913,86 ± 147,80) e QC-20 com fibra (2858,32 ± 185,26). As médias e desvios-padrão ao teste de resistência flexural foram Vipi Flash sem fibra (81,62 ± 4,82); Vipi Flash com fibra (83,98 ± 4,98); Vipi Wave sem fibra (83,52 ± 8,79); Vipi Wave com fibra (88,98± 8,47); Vipi Cril sem fibra (64,17± 5,46); Vipi Crill com fibra (93,37 ± 9,97); Lucitone sem fibra (74,71± 9,43); Lucitone com fibra (87,29 ± 4,73); QC-20 sem fibra (75,80 ± 8,82) e QC-20 com fibra (81,67± 12,97). Conclusão: Conclui-se que a incorporação de fibras provocou alterações em praticamente todas as propriedades analisadas, sendo, portanto facilmente utilizável como um reforço adicional às resinas acrílicas. Com relação à dureza superficial as resinas acrílicas termopolimerizável por banho de água e termopolimerizável por calor de microondas apresentaram maiores valores quando comparados com a resina acrílica autopolimerizável. Além disso, a adição de fibras de vidro particuladas aumentou os valores de rugosidade de algumas resinas acrílicas Vipi Crill, Vipi Flash e Vipi Wave e se manteve constante nas resinas Lucitone e QC-20. A adição de fibra de vidro não aumentou significantemente a microdureza Knoop nos grupos em estudo. Com relação à resistência flexural as fibras de vidro particuladas aumentaram significantemente todos os valores, assim como o módulo de elasticidade das resinas acrílicas reforçadas pela adição de fibras de vidro. / Intraoral Occlusal splints are devices used in the management of patients with sleep disorders, migraine type tension and others. But dentists who are predominantly using the plates as a treatment of occlusal balance of the dental arches in temporomandibular disorders, prevention of tooth wear in patients with habits and prevention of injuries in athletes. Several methods have been used to strengthen acrylic resins, such as metal reinforcement and are currently incorporating different types of fibers such as carbon, polyethylene and glass. However the addition of glass fibers with smaller particles on mechanical properties are still unknown. Objective: The objective of this study was to evaluate some mechanical properties such as surface roughness, hardness, elastic modulus and flexural strength in acrylic resins after the incorporation of glass fiber particulate pre silanized. Methods: To evaluate the properties were made twenty-four specimens (65 x 10 x 3 mm) of each brand of acrylic resin, used for fabrication of occlusal splints, Vipi Flash (self-curing), Vipi Wave (by thermo microwave heat), Vipi CRILL, Lucitone and QC-20 (thermo heat water bath), with twelve specimes controls, and twelve experimental, with the addition of 10 wt% glass fiber particulate (Reforplás S / A, São Paulo, Brazil). After completion of the roughness of the specimens with grit carborundum and felt it was evaluated the surface roughness on roughness tester (Mitutoyo ®) with three readings over the specimes, the microhardness was examined with a hardness ( Micro Hardness Tester, Shimadzu, Japan) with five measurements in each specime, and evaluate the tests for flexural strength and modulus of elasticity of the specimes was evaluated using a universal testing machine (Emic DL 2000 ®, Emic, São José dos Pinhais, PR, Brazil), with speed 5mm/min. The data were statistically analyzed using parametric and nonparametric tests, according to the sample distribution. Results: The mean and standard deviation of the test surface roughness were Vipi Flash without fiber (0.10 ± 0.03); Flash Vipi with fiber (0.12 ± 0.01); Vipi Wave without fiber (0, 16 ± 0.02); Vipi Wave with fiber (0.13 ± 0.02); Vipi Cril without fiber (0.12 ± 0.03); Vipi CRILL with fiber (0.15 ± 0.03); Lucitone without fiber (0.10 ± 0.02); Lucitone with fiber (0.09 ± 0.04), QC-20 fiber without (0.11 ± 0.02) and QC-20 with fiber (0.18 ± 0.03). Means and standard deviations for Knoop microhardness test with respect to trademarks were Vipi Flash without fiber (15.35 ± 0.3); Flash Vipi with fiber (15.51 ± 0.4); Vipi Wave without fiber (16.60 ± 0.8); Vipi Wave with fiber (17.25 ± 0.9); Vipi Cril without fiber (17.78 ± 2.27); Vipi CRILL with fiber (18.02 ± 1.0 ); Lucitone without fiber (15.72 ± 0.3); Lucitone with fiber (16.69 ± 0.6), QC-20 without fiber (15.91 ± 0.4) and QC-20 with fiber (15 , 63 ± 0.2). Means and standard deviations to test elastic modulus were Vipi Flash without fiber (2952.76 ± 292.12); Flash Vipi with fiber (3373.49 ± 403.76); Vipi Wave without fiber (2511.69 ± 304.09); Vipi Wave with fiber (3225.01 ± 248.66); Vipi Cril without fiber (2745.61 ± 288.86); Vipi CRILL with fiber (3671.67 ± 329.91); Lucitone without fiber (1904.53 ± 149.05); Lucitone with fiber (3056.87 ± 126.11), QC-20 without fiber (1913.86 ± 147.80) and QC-20 with fiber (2858.32 ± 185 26). Means and standard deviations for flexural strength were Vipi Flash without fiber (81.62 ± 4.82); Flash Vipi with fiber (83.98 ± 4.98); Vipi Wave without fiber (83.52 ± 8 , 79); Vipi Wave with fiber (88.98 ± 8.47); Vipi Cril without fiber (64.17 ± 5.46); Vipi CRILL with fiber (93.37 ± 9.97); Lucitone without fiber ( 74.71 ± 9.43); Lucitone with fiber (87.29 ± 4.73), QC-20 without fiber (75.80 ± 8.82) and QC-20 with fiber (81.67 ± 12.97). Conclusion: the conclusion is that the incorporation of fibers resulted in changes in almost all properties examined, and thus easily used as an additional reinforcement for acrylic resins. With respect to the surface roughness of acrylic resins by thermo water bath and microwave thermo heat showed higher values when compared with acrylic resin. Moreover, the addition of glass fiber particulate increased the roughness values of some acrylic resins Vipi CRILL, Vipi Flash and Vipi Wave and remained constant in the resins Lucitone and QC-20. The addition of glass fiber does not increase significantly the microhardness in the groups. With respect to flexural strength glass fiber particulate significantly increased all values, as well as the modulus of acrylic resin reinforced by the addition of glass fibers.

A importância das restaurações provisórias no tratamento reabilitador oral é inquestionável. Os materiais utilizados para a execução destas restaurações, entretanto, são críticos com relação à resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. A proposta deste trabalho foi determinar o efeito de diversos reforços sobre a resistência flexional, o módulo de elasticidade e o tipo de fratura apresentados por espécimes confeccionados em uma resina poli(metilmetacrilato) (PMMA), quando submetidos a um teste de carga de três pontos. Sete tipos de reforços constituíram os grupos experimentais com dez espécimes cada: um fio de aço com 0,7 mm de diâmetro; um fio de amarrilho trançado; uma fibra de vidro trançada Interlig® (Angelus®); uma fibra de vidro entrelaçada Splint-It!® (Jeneric-ron®); uma fibra de vidro unidirecional Fibrante® (Angelus®); uma fibra de poli(etileno) Connect® (Kerr®) e uma fibra cerâmica flexível GlasSpan® (GlasSpan®). O grupo controle, também com dez amostras, foi composto de espécimes não reforçados. A confecção dos espécimes, o ensaio mecânico e cálculo da resistência flexional e do módulo de elasticidade foram realizados seguindo norma ISO 10477 – modificada. A análise dos resultados (ANOVA, p < 0,05), para ambas as propriedades, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados com fio de aço com 0,7 mm; fibra Interlig® e fibra Connect® aumentaram significantemente a resistência flexional, e que os grupos reforçados com fio de aço com 0,7 mm; fibra Interlig®; fibra Splint-It!®; fibra Connect® e fibra GlasSpan®, aumentaram o módulo de elasticidade, em relação ao grupo controle. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial. / Provisional restorations are essential components of oral rehabilitation treatment. The strength and durability features are, however, critical whe n long-term treatment is needed. The aim of this work was to measure the flexural strength, the elastic modulus and the type of fracture of poly (methyl methacrylate) (PMMA) resin specimens when submitted to a three-point-bend test. Seven types of reinforcements constituted the experimental groups with ten specimens each: a 0.7 mm of diameter wire; an orthodontic braided wire; a braided fiberglass Interlig® (Angelus®); an woven fiberglass Splint-It!® (Jeneric-Pentron®); a roving fiberglass Fibrante® (Angelus®); a braided poly(ethylene) fiber Connect® (Kerr®) and a flexible ceramic fiber GlasSpan® (GlasSpan®). The control group, also with ten samples, included not reinforced specimens. All specimens were made and test according to modified ISO specification No. 10477. The analysis of the results (ANOVA, p < 0.05), for both properties, showed significant differences between groups. Tukey\'s test detected higher figures for groups reinforced with wire of 0.7 mm of diameter wire; Interlig® and Connect® when flexural strength was concerned. Groups reinforced with a wire 0.7 mm of diameter; Interlig®; Splint-It!®; Connect® and GlasSpan®, increased the elastic modulus, when compared to the control group. The fractures analysis contributed with the elaboration of new index system dividing them in four types: Absent, Partial, Total Not Separated and Total Separated. It was observed that the reinforced specimens fractures were more favorable, occurring, predominantly, in the Absent and Partial types.

O presente trabalho verificou a alteração dimensional dos guias cirúrgicos confeccionados em resina acrílica para cirurgia ortognática quando submetidos à esterilização por meio de plasma de peróxido de hidrogênio. Foram utilizados 15 corpos de prova confeccionados em resina acrílica quimicamente ativada a partir de moldes metálicos em três espessuras: 1,5 mm, 3,0 mm e 5,0 mm, em um total de 45. A imagem de cada corpo de prova foi digitalizada antes e após o processo de esterilização e processada pelo programa Photoshop® CS2. Foi realizada a vetorização das imagens pelo programa Corel Trace ® 12 para mensuração pelo programa Corel Drawn ® 12. Os resultados foram submetidos ao teste estatístico dos postos sinalizados de Wilcoxon, ao nível de significância de 0,05%. Os resultados obtidos foram que nos corpos de prova de 1,5 mm de espessura não houve diferença estatisticamente significante entre as mensurações realizadas antes e após o processo de esterilização (P>0,05), porem, nas espessuras de 3,0 mm e 5,0 mm houve pelo menos uma das medidas estatisticamente diferentes (p=0,011 e p=0,017, respectivamente). Fato este que nos levou a acreditar que o processo de esterilização não leva a alteração dimensional, porem em volumes maiores provavelmente houve uma contração de polimerização diretamente proporcional. / Dimensional alterations in surgical splints made of acrylic resin used in orthognathic surgery were evaluated after hydrogen peroxide gas plasma sterilization. Fifteen specimens of resin acrylic was made by a metal model master with three different thickness: 1,5 mm, 3,0 mm and 5,0 mm, totally 45 specimens. Specimens digital image was acquired before and after sterilization and process by Photoshop® CD2 software. The images were transformed in vector form by Corel Trace® 12 software. The measures were performed by Corel Draw® 12 software. The results were submitted to Wilcoxon statistic method, 0.05 level of confidence. The results showed no statistical differences in 1.5 mm specimens (p0,307) before and after sterilization process but, in 3.0 and 5.0 mm, there was at least one measure statistically different (p=0,011 and p=0,017, respectively). It was possible to conclude that the sterilization process did not lead to dimensional alteration but, in higher thickness probably had happen a proportional polymerization contraction.

Foram confeccionados 50 corpos de prova, divididos em 30 próteses totais superiores e 20 bases de provas permanentes, padronizados, para se avaliar a alteração dimensional da base de prova permanente, com dupla polimerização, processada em forno de microondas convencional; base de prova permanente com dupla polimerização, processada no método convencional; e a prótese total em uma única polimerização. Para essa análise, essas próteses foram divididas em 5 grupos: grupo I – prótese total convencional – banho de água (controle); grupo II – base de prova permanente processada convencionalmente; grupo III – base de prova permanente processada em forno de microondas convencional; grupo IV – prótese total superior padronizada com base de prova permanente processada convencionalmente, com as bases do grupo II; grupo V – prótese total superior com base de prova permanente, processada no forno de microondas convencional, com as bases de prova do grupo III. Para avaliar essa alteração foi usado o recurso do scaneamento da região posterior das próteses, “Post-dam", desses corpos de prova. Após esse processo, a imagem capturada foi levada para o programa Photoshop 8.0 determinando a região de avaliação. Após essa seleção, a imagem é acessada no CorelTrace 11 para ser transformada em preto e branco e vetorizada, sendo, então, levada para o CorelDraw 11 para ser feita a medição do espaço da região posterior, entre o modelo e a base de prova/prótese total, para permitir a análise dos valores da alteração dimensional dos corpos de prova em questão, após o processamento. Os resultados mostram que: 1) a diferença da variação média para os lados esquerdo, centro e direito, respectivamente, na ordem de décimos ou centésimos de milímetros, para o grupo IV e I (0,07; 0,08 e 0,09); para o grupo V e I (0,10; 0,32 e 0,25) e para o grupo V e IV (0,17; 0,24 e 0,16) não pode ser considerada relevante clinicamente para afetar o ajuste da prótese na boca e promover a ocorrência de maiores transtornos clínicos; 2) A alteração média das áreas do lado esquerdo e direito para o grupo I, II e IV obtiveram uma homogeneidade na alteração, diferindo os Grupos III e V em relação aos outros, não existindo porém, diferença significante a nível de 5% entre as áreas desses segmentos; 3) A análise da variância do índice da área dos cinco (5) grupos não apresentou resultado significante que desabonasse a utilização de qualquer um dos métodos para a confecção da prótese total. No entanto, mais estudos devem ser realizados com o intuito de se aprimorar o uso do forno de microondas para o processamentos da prótese. / The 50 samples of pattern maxillary complete denture were processed, divided in 30 maxillary complete denture and 20 permanent proof base, to evaluated of dimensional changes in the permanent proof base with twice polymerization, process in microwave oven, to compare with the others two groups, the complete denture with conventional process and the complete denture with permanent proof base with twice polymerization in a conventional process. To evaluated this complete dentures they were divided in 5 groups: group I – conventional complete denture; group II – proof base conventional process; group III – proof base in microwave process; group IV – complete denture using the proof base of the group, with the conventional process and the group; group V – complete denture using the proof base of the group III, microwave process. To evaluated this alteration used the scanner in the “Post-dam", in this samples. After this proceding the image was putting in the Adobe Photoshop 8.0 program to determinate what region was evaluated. After this selection, the image access in the CorelTrace 11 program and transformed in black and white, and after to access in the CorelDraw 11 that was measured the region between the cast and the complete/permanent proof base, to allow the analysis of the values the dimensional alteration of the proof body, after the process. The results show: 1) The linear dimensional alteration the difference mean variation for the left, center and right sides, respectively, it was in decimal order or centesimal of millimeters, for the group IV and I (0,07; 0,08 and 0,09); and for the group V and I were (0,10; 0,32 and 0,25) and for the group V and IV (0,17; 0,24 and 0,16) and it cannot be considered clinically relevant to affect the prosthesis adjustment in the mouth, and promote the occurrence of more clinical disruptions; 2) The dimensional alterations in the areas (left and right side) of the proof bodies of the three groups I, II and IV were uniform, and the groups III and V weren’t homogeneous, but there is not a statically significant difference, about 5%, between the segment left and right areas; 3) The variation of the area index about five groups there is not a statically significant that couldn’t use of the both method to build the complete denture. Although, more studies are important to realize with the objective to improve the use the microwave over to process the denture.

Restauração provisória é uma importante fase da reabilitação bucal com prótese parcial fixa, deve fornecer proteção pulpar e periodontal, apresentar integridade marginal e estética, ter durabilidade suficiente para resistir às forças mastigatórias. Pacientes com bruxismo ou aqueles cujo tratamento requer períodos longos de uso das restaurações provisórias necessitam de material com melhores propriedades mecânicas. Vários métodos têm sido empregados para reforçar próteses fixas provisórias, como fios metálicos, reforço metálico e incorporação de diferentes tipos de fibras, como carbono, polietileno e vidro, nas resinas para restaurações provisórias. O objetivo desse estudo foi avaliar alteração de cor e propriedades mecânicas de resistência flexural, módulo de elasticidade e carga de ruptura em resinas acrílicas com incorporação de fibras de vidro silanizadas. Para avaliação de cor foram confeccionados quarenta corpos-de-prova circulares (15 x 3mm) de cada marca comercial de resina acrílica quimicamente ativada, usada para confecção de restaurações provisórias, Dencor (Clássico Ltda., São Paulo-SP, Brasil), Duralay (Reliance, Worth-IL, EUA) e Trim Plus II (Bosworth Company, Skokie-IL, EUA), sendo vinte corpos-de-prova controles, e vinte experimentais, com adição de 10% em peso de fibras de vidro moídas (Reforplás S/A, São Paulo, SP, Brasil). Após a realização do acabamento superficial dos corpos-de-prova com lixas de carborundum e feltros era realizada a avaliação dos componentes de cor (L*, a*, b*) em espectrocolorímetro portátil (BYK-Gardner GmbH, Gerestried, Alemanha), com três mensurações em cada corpo-de-prova. Para os ensaios de resistência flexural, módulo de elasticidade e carga de ruptura foram confeccionados 40 corpos-de-prova retangulares (10mm de comprimento, 65mm de largura e 3mm de espessura) de cada marca de resina, sendo vinte do grupo controle e vinte do experimental (com fibras). Os corpos-de-prova foram testados em uma máquina de ensaios universal (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), usando três, com velocidade de 5mm/min. Os dados foram analisados estatisticamente, usando testes paramétricos e não paramétricos, de acordo com a distribuição da amostra. Todos os componentes de cor (L*, a* e b*) foram alterados após a incorporação de fibras de vidro, com exceção do componente b* da resina Duralay. Para o ensaio de resistência flexural, a análise de variância evidenciou significância estatística (p<0,01) apenas para o fator resinas (Duralay: 85,748 N/mm2 (± 8,04) ,Trim Plus: 86,860 N/mm2 (± 7,73) e Dencor: 97,400 N/mm2 (± 8,18)).Na avaliação do módulo de elasticidade, a análise de variância mostrou significância estatística (p<0,01) para o fator tratamentos, sem fibra: 2572,138 MPa (± 290,92) e com fibras: 3446,691 MPa (± 411,13), e para a interação, evidenciando que a incorporação de fibras aumentou o módulo de elasticidade das três resinas avaliadas.Na carga de ruptura, a análise de Variância evidenciou significância estatística (p<0,01) para os fatores tratamentos, sem fibras: 482,607 N (± 53,18322) e com fibras: 557,53 N (± 59,49652), resinas Duralay: 494,06 N (± 86,63), Trim Plus: 525,177 N (± 42,85) e Dencor: 540,971 N (± 58,40). Conclui-se que a incorporação de fibras provocou alterações nos componentes de cor e aumentou ambos, módulo de elasticidade e carga de ruptura, contudo não alterou a resistência flexural. / Provisional restoration is an important rehabilitation phase in fixed prosthodontic therapy, it should provide pulpal and periodontal protection, showing marginal integrity and esthetics, should also have enough durability in order to resist to the forces of mastication. Patients with bruxism or those, whose treatment require long-term use of provisional restorations, need material with better mechanical properties. Several methods have been applied to reinforce fixed partial dentures, as well as metal wires, metal reinforcement and the application of different types of fibers, such as carbon, polyethylene and glass in the resins for temporary restorations. The aim of this study was to evaluate the color change as well as the mechanical properties of flexural strength, elastic modulus and load rupture in acrylic resin with silanized glass fibers. In order to evaluate the color, it was fabricated forty circular specimens (15 x 3mm) of each commercial brand of the resins chemically activated, used to make provisional restorations, Dencor (Clássico Ltda., São Paulo-SP, Brasil), Duralay (Reliance, Worth-IL, EUA) e Trim Plus II (Bosworth Company, Skokie-IL, EUA). Twenty specimens were control and the other twenty were experimental with an addition of 10% in glass fiber weights (Reforplás S/A, São Paulo, SP, Brasil). After the superficial finishing of the specimens with silicon carbide paper and rag wheel, it was done an evaluation of the color parameters (L*, a*, b*) with a portable spectrocolorimeter (BYK-Gardner GmbH, Gerestried, Alemanha), in three measures in each specimens. For the flexural strength, elastic modulus and load rupture, forty rectangular specimens were fabricated (10mm in length, 65mm wide and 3mm of thickness) of each resin brand and twenty were experimental with fibers. The specimens were tested on an universal machine (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), using a 3- point bending testing device at a crosshead speed of 5 mm/mim. The data was statistically analyzed using parametric and non-parametric tests, according to the sample distribution. All the color parameter (L*, a* e b*) were altered after putting glass fibers, except the parameter b* from resin Duralay. For flexural resistance, the variance analyzes showed significance statistic (p<0,01) just for the resins ( Duralay: 85,748 N/mm2 (± 8,04) ,Trim Plus: 86,860 N/mm2 (± 7,73) and Dencor: 97,400 N/mm2 (± 8,18)). In the elastic modulus evaluation, the variance analyses showed significance statistic (p<0,01) for the treatment factors, without fibers (2572,138 MPa (± 290,92)) and with fibers (3446,691 (± 411,13)). Regarding the interaction, it showed that the incorporation of the fibers increased the elastic modulus in the three resins analyzed. Regarding the load rupture, the variance analyzed showed significance statistic of (p<0,01) for the treatment factors with fibers: 482,607 N (± 53,18322) and without fibers: 557,53 N (± 59,49652), resins (Duralay: 494,06 N (± 86,63), Trim Plus:525,177 N(± 42,85) e Dencor: 540,971 N (± 58,40)). The results of this study indicated that the incorporation of the fibers caused alterations in the color components and increased both elastic modulus and load rupture; therefore, it didnt increase the flexural resistance.

Restauração provisória é uma importante fase da reabilitação bucal com prótese parcial fixa, deve fornecer proteção pulpar e periodontal, apresentar integridade marginal e estética, ter durabilidade suficiente para resistir às forças mastigatórias. Pacientes com bruxismo ou aqueles cujo tratamento requer períodos longos de uso das restaurações provisórias necessitam de material com melhores propriedades mecânicas. Vários métodos têm sido empregados para reforçar próteses fixas provisórias, como fios metálicos, reforço metálico e incorporação de diferentes tipos de fibras, como carbono, polietileno e vidro, nas resinas para restaurações provisórias. O objetivo desse estudo foi avaliar alteração de cor e propriedades mecânicas de resistência flexural, módulo de elasticidade e carga de ruptura em resinas acrílicas com incorporação de fibras de vidro silanizadas. Para avaliação de cor foram confeccionados quarenta corpos-de-prova circulares (15 x 3mm) de cada marca comercial de resina acrílica quimicamente ativada, usada para confecção de restaurações provisórias, Dencor (Clássico Ltda., São Paulo-SP, Brasil), Duralay (Reliance, Worth-IL, EUA) e Trim Plus II (Bosworth Company, Skokie-IL, EUA), sendo vinte corpos-de-prova controles, e vinte experimentais, com adição de 10% em peso de fibras de vidro moídas (Reforplás S/A, São Paulo, SP, Brasil). Após a realização do acabamento superficial dos corpos-de-prova com lixas de carborundum e feltros era realizada a avaliação dos componentes de cor (L*, a*, b*) em espectrocolorímetro portátil (BYK-Gardner GmbH, Gerestried, Alemanha), com três mensurações em cada corpo-de-prova. Para os ensaios de resistência flexural, módulo de elasticidade e carga de ruptura foram confeccionados 40 corpos-de-prova retangulares (10mm de comprimento, 65mm de largura e 3mm de espessura) de cada marca de resina, sendo vinte do grupo controle e vinte do experimental (com fibras). Os corpos-de-prova foram testados em uma máquina de ensaios universal (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), usando três, com velocidade de 5mm/min. Os dados foram analisados estatisticamente, usando testes paramétricos e não paramétricos, de acordo com a distribuição da amostra. Todos os componentes de cor (L*, a* e b*) foram alterados após a incorporação de fibras de vidro, com exceção do componente b* da resina Duralay. Para o ensaio de resistência flexural, a análise de variância evidenciou significância estatística (p<0,01) apenas para o fator resinas (Duralay: 85,748 N/mm2 (± 8,04) ,Trim Plus: 86,860 N/mm2 (± 7,73) e Dencor: 97,400 N/mm2 (± 8,18)).Na avaliação do módulo de elasticidade, a análise de variância mostrou significância estatística (p<0,01) para o fator tratamentos, sem fibra: 2572,138 MPa (± 290,92) e com fibras: 3446,691 MPa (± 411,13), e para a interação, evidenciando que a incorporação de fibras aumentou o módulo de elasticidade das três resinas avaliadas.Na carga de ruptura, a análise de Variância evidenciou significância estatística (p<0,01) para os fatores tratamentos, sem fibras: 482,607 N (± 53,18322) e com fibras: 557,53 N (± 59,49652), resinas Duralay: 494,06 N (± 86,63), Trim Plus: 525,177 N (± 42,85) e Dencor: 540,971 N (± 58,40). Conclui-se que a incorporação de fibras provocou alterações nos componentes de cor e aumentou ambos, módulo de elasticidade e carga de ruptura, contudo não alterou a resistência flexural. / Provisional restoration is an important rehabilitation phase in fixed prosthodontic therapy, it should provide pulpal and periodontal protection, showing marginal integrity and esthetics, should also have enough durability in order to resist to the forces of mastication. Patients with bruxism or those, whose treatment require long-term use of provisional restorations, need material with better mechanical properties. Several methods have been applied to reinforce fixed partial dentures, as well as metal wires, metal reinforcement and the application of different types of fibers, such as carbon, polyethylene and glass in the resins for temporary restorations. The aim of this study was to evaluate the color change as well as the mechanical properties of flexural strength, elastic modulus and load rupture in acrylic resin with silanized glass fibers. In order to evaluate the color, it was fabricated forty circular specimens (15 x 3mm) of each commercial brand of the resins chemically activated, used to make provisional restorations, Dencor (Clássico Ltda., São Paulo-SP, Brasil), Duralay (Reliance, Worth-IL, EUA) e Trim Plus II (Bosworth Company, Skokie-IL, EUA). Twenty specimens were control and the other twenty were experimental with an addition of 10% in glass fiber weights (Reforplás S/A, São Paulo, SP, Brasil). After the superficial finishing of the specimens with silicon carbide paper and rag wheel, it was done an evaluation of the color parameters (L*, a*, b*) with a portable spectrocolorimeter (BYK-Gardner GmbH, Gerestried, Alemanha), in three measures in each specimens. For the flexural strength, elastic modulus and load rupture, forty rectangular specimens were fabricated (10mm in length, 65mm wide and 3mm of thickness) of each resin brand and twenty were experimental with fibers. The specimens were tested on an universal machine (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), using a 3- point bending testing device at a crosshead speed of 5 mm/mim. The data was statistically analyzed using parametric and non-parametric tests, according to the sample distribution. All the color parameter (L*, a* e b*) were altered after putting glass fibers, except the parameter b* from resin Duralay. For flexural resistance, the variance analyzes showed significance statistic (p<0,01) just for the resins ( Duralay: 85,748 N/mm2 (± 8,04) ,Trim Plus: 86,860 N/mm2 (± 7,73) and Dencor: 97,400 N/mm2 (± 8,18)). In the elastic modulus evaluation, the variance analyses showed significance statistic (p<0,01) for the treatment factors, without fibers (2572,138 MPa (± 290,92)) and with fibers (3446,691 (± 411,13)). Regarding the interaction, it showed that the incorporation of the fibers increased the elastic modulus in the three resins analyzed. Regarding the load rupture, the variance analyzed showed significance statistic of (p<0,01) for the treatment factors with fibers: 482,607 N (± 53,18322) and without fibers: 557,53 N (± 59,49652), resins (Duralay: 494,06 N (± 86,63), Trim Plus:525,177 N(± 42,85) e Dencor: 540,971 N (± 58,40)). The results of this study indicated that the incorporation of the fibers caused alterations in the color components and increased both elastic modulus and load rupture; therefore, it didnt increase the flexural resistance.

Materiais odontológicos inovadores que apresentem propriedades antimicrobianas são altamente desejáveis na cavidade oral. O objetivo deste estudo foi avaliar a atividade antimicrobiana do vanadato de prata nanoestruturado (&beta;-AgVO3) incorporado em duas resinas acrílicas frente a Candida albicans, Streptococcus mutans, Staphylococcus aureus e Pseudomonas aeruginosa, além de examinar as propriedades mecânicas e o padrão de incorporação do nanomaterial nas resinas. O nanomaterial foi caracterizado por difração de raios X (DRX), espectroscopia no infravermelho por transformada de Fourier (FTIV), análise elementar por energia dispersiva (EDS) e microscopia eletrônica de varredura (MEV). As propriedades antimicrobianas das resinas acrílicas incorporadas com diferentes porcentagens de &beta;-AgVO3 foram investigadas pelo método de redução do XTT, unidades formadoras de colônias (UFC) e microscopia confocal à laser e o comportamento mecânico por meio de ensaios de dureza e rugosidade superficial, resistência à flexão, à compressão e ao impacto. O padrão de incorporação do &beta;-AgVO3 nas resinas foi analisado por microscopia eletrônica de varredura (MEV) e análise elementar por energia dispersiva (EDS). Os dados foram analisados por ANOVA, Tukey e pelo teste Generalized Linear Models (&alpha;=0,05). Para ambas as resinas, em relação ao grupo controle, a incorporação de 5% e 10% de &beta;-AgVO3 reduziram significantemente a atividade metabólica de C. albicans e P. aeruginosa (p<0,05), enquanto que para S. mutans houve redução significante apenas com a incorporação de 10% (p<0,05). Não houve diferença na atividade metabólica pelo método do XTT frente a S. aureus (p> 0,05). Para ambas as resinas, observou-se uma redução significativa no número de UFC/mL de C. albicans para o grupo incorporado com 10% de &beta;-AgVO3 e de S. mutans para os grupos com 2,5%, 5% e 10% do nanomaterial (p<0,05). Para S. aureus e P. aeruginosa, houve redução significante com a incorporação de 5% e 10% (p<0,05). A dureza superficial da resina termopolimerizável permaneceu inalterada pela incorporação do nanomaterial (p>0,05) e da autopolimerizável aumentou com 0,5% (p<0,05). Concentrações maiores que 1% promoveram redução na resistência flexural das resinas (p<0,05) enquanto que a rugosidade superficial permaneceu inalterada (p>0,05). A resistência à compressão da resina autopolimerizável permaneceu inalterada (p>0,05) e da termopolimerizável reduziu com a incorporação de 0,5% e 10% (p<0,05). As concentrações de 5% e 10% promoveram redução significante na resistência ao impacto das resinas, em relação ao controle (p<0,05). A caracterização das resinas quanto a dispersão da carga utilizada mostrou a presença de domínios de &beta;-AgVO3 ao longo da matriz polimérica seguindo um padrão circular. Conclui-se que o método proposto foi capaz de promover atividade antimicrobiana às resinas acrílicas frente aos micro-organismos avaliados, sendo a mesma dependente da concentração do nanomaterial. Porém, alterações na dispersão do &beta;-AgVO3 na matriz dos polímeros são necessárias para não sacrificar as propriedades mecânicas e para potencializar o efeito antimicrobiano / Innovative dental materials that have antimicrobial properties are highly desirable in the oral cavity. The aim of this study was to evaluate the antimicrobial activity of nanostructured silver vanadate (&beta;-AgVO3) incorporated into two acrylic resins against Candida albicans, Streptococcus mutans, Staphylococcus aureus and Pseudomonas aeruginosa, while examining the mechanical properties and the pattern of nanomaterial incorporation into resins. The nanomaterial was characterized by X-ray diffraction (XRD), infrared spectroscopy Fourier transform (FTIR), elemental analysis by energy dispersive (EDS) and scanning electron microscopy (SEM). The antimicrobial properties of acrylic resins incorporated with different percentages of &beta;-AgVO3 were investigated by the reduction of XTT method, colony forming units (CFU) and confocal laser microscopy and the mechanical behavior through hardness, surface roughness, flexural, compression and impact tests. The pattern of incorporation of &beta;-AgVO3 resins was analyzed by scanning electron microscopy (SEM) and elemental analysis by energy dispersive (EDS). Data were analyzed by ANOVA, Tukey test and the Generalized Linear Models (&alpha; = 0.05). For both resins, compared to the control group, the incorporation of 5% and 10% &beta;-AgVO3 caused a significantly reduced in the metabolic activity of C. albicans and P. aeruginosa (p <0.05), while for S. mutans significant reduction was observed only with the incorporation of 10% (p <0.05). There was no difference in metabolic activity by XTT method against S. aureus (p> 0.05). For both resins, there was a significant reduction in the number of CFU / mL for C. albicans incorporated group with 10% &beta;-AgVO3 and S. mutans in groups with 2.5%, 5% and 10% of nanomaterial (p <0.05). For P. aeruginosa and S. aureus, there was a significant decrease with the incorporation of 5% to 10% (p <0.05). The surface hardness of the heat-cured resin was unchanged by the incorporation of the nanomaterial (p <0.05) and increased self-cured with 0.5% (p <0.05). Concentrations above 1% promote the reduction in flexural strength of the resins (p <0.05) while the surface roughness remained unchanged (P> 0.05). The compressive strength of the self-cured resin remained unchanged (P> 0.05) and heat-cured reduced with the incorporation of 0.5% and 10% (p <0.05). Concentrations of 5% and 10% caused a significant reduction in impact strength of resins, compared to control (p <0.05). The characterization of the resins as the dispersion of the filler used showed the presence of &beta;-AgVO3 domains along the polymer matrix following a circular pattern. It was concluded that the proposed method was able to promote antimicrobial activity to acrylic resins against microorganisms evaluated, with the same concentration dependent of the nanomaterial. However, changes in the &beta;-AgVO3 dispersion in the polymer matrix are necessary to do not sacrifice the mechanical properties and to enhance the antimicrobial effect

Materiais odontológicos inovadores que apresentem propriedades antimicrobianas são altamente desejáveis na cavidade oral. O objetivo deste estudo foi avaliar a atividade antimicrobiana do vanadato de prata nanoestruturado (&beta;-AgVO3) incorporado em duas resinas acrílicas frente a Candida albicans, Streptococcus mutans, Staphylococcus aureus e Pseudomonas aeruginosa, além de examinar as propriedades mecânicas e o padrão de incorporação do nanomaterial nas resinas. O nanomaterial foi caracterizado por difração de raios X (DRX), espectroscopia no infravermelho por transformada de Fourier (FTIV), análise elementar por energia dispersiva (EDS) e microscopia eletrônica de varredura (MEV). As propriedades antimicrobianas das resinas acrílicas incorporadas com diferentes porcentagens de &beta;-AgVO3 foram investigadas pelo método de redução do XTT, unidades formadoras de colônias (UFC) e microscopia confocal à laser e o comportamento mecânico por meio de ensaios de dureza e rugosidade superficial, resistência à flexão, à compressão e ao impacto. O padrão de incorporação do &beta;-AgVO3 nas resinas foi analisado por microscopia eletrônica de varredura (MEV) e análise elementar por energia dispersiva (EDS). Os dados foram analisados por ANOVA, Tukey e pelo teste Generalized Linear Models (&alpha;=0,05). Para ambas as resinas, em relação ao grupo controle, a incorporação de 5% e 10% de &beta;-AgVO3 reduziram significantemente a atividade metabólica de C. albicans e P. aeruginosa (p<0,05), enquanto que para S. mutans houve redução significante apenas com a incorporação de 10% (p<0,05). Não houve diferença na atividade metabólica pelo método do XTT frente a S. aureus (p> 0,05). Para ambas as resinas, observou-se uma redução significativa no número de UFC/mL de C. albicans para o grupo incorporado com 10% de &beta;-AgVO3 e de S. mutans para os grupos com 2,5%, 5% e 10% do nanomaterial (p<0,05). Para S. aureus e P. aeruginosa, houve redução significante com a incorporação de 5% e 10% (p<0,05). A dureza superficial da resina termopolimerizável permaneceu inalterada pela incorporação do nanomaterial (p>0,05) e da autopolimerizável aumentou com 0,5% (p<0,05). Concentrações maiores que 1% promoveram redução na resistência flexural das resinas (p<0,05) enquanto que a rugosidade superficial permaneceu inalterada (p>0,05). A resistência à compressão da resina autopolimerizável permaneceu inalterada (p>0,05) e da termopolimerizável reduziu com a incorporação de 0,5% e 10% (p<0,05). As concentrações de 5% e 10% promoveram redução significante na resistência ao impacto das resinas, em relação ao controle (p<0,05). A caracterização das resinas quanto a dispersão da carga utilizada mostrou a presença de domínios de &beta;-AgVO3 ao longo da matriz polimérica seguindo um padrão circular. Conclui-se que o método proposto foi capaz de promover atividade antimicrobiana às resinas acrílicas frente aos micro-organismos avaliados, sendo a mesma dependente da concentração do nanomaterial. Porém, alterações na dispersão do &beta;-AgVO3 na matriz dos polímeros são necessárias para não sacrificar as propriedades mecânicas e para potencializar o efeito antimicrobiano / Innovative dental materials that have antimicrobial properties are highly desirable in the oral cavity. The aim of this study was to evaluate the antimicrobial activity of nanostructured silver vanadate (&beta;-AgVO3) incorporated into two acrylic resins against Candida albicans, Streptococcus mutans, Staphylococcus aureus and Pseudomonas aeruginosa, while examining the mechanical properties and the pattern of nanomaterial incorporation into resins. The nanomaterial was characterized by X-ray diffraction (XRD), infrared spectroscopy Fourier transform (FTIR), elemental analysis by energy dispersive (EDS) and scanning electron microscopy (SEM). The antimicrobial properties of acrylic resins incorporated with different percentages of &beta;-AgVO3 were investigated by the reduction of XTT method, colony forming units (CFU) and confocal laser microscopy and the mechanical behavior through hardness, surface roughness, flexural, compression and impact tests. The pattern of incorporation of &beta;-AgVO3 resins was analyzed by scanning electron microscopy (SEM) and elemental analysis by energy dispersive (EDS). Data were analyzed by ANOVA, Tukey test and the Generalized Linear Models (&alpha; = 0.05). For both resins, compared to the control group, the incorporation of 5% and 10% &beta;-AgVO3 caused a significantly reduced in the metabolic activity of C. albicans and P. aeruginosa (p <0.05), while for S. mutans significant reduction was observed only with the incorporation of 10% (p <0.05). There was no difference in metabolic activity by XTT method against S. aureus (p> 0.05). For both resins, there was a significant reduction in the number of CFU / mL for C. albicans incorporated group with 10% &beta;-AgVO3 and S. mutans in groups with 2.5%, 5% and 10% of nanomaterial (p <0.05). For P. aeruginosa and S. aureus, there was a significant decrease with the incorporation of 5% to 10% (p <0.05). The surface hardness of the heat-cured resin was unchanged by the incorporation of the nanomaterial (p <0.05) and increased self-cured with 0.5% (p <0.05). Concentrations above 1% promote the reduction in flexural strength of the resins (p <0.05) while the surface roughness remained unchanged (P> 0.05). The compressive strength of the self-cured resin remained unchanged (P> 0.05) and heat-cured reduced with the incorporation of 0.5% and 10% (p <0.05). Concentrations of 5% and 10% caused a significant reduction in impact strength of resins, compared to control (p <0.05). The characterization of the resins as the dispersion of the filler used showed the presence of &beta;-AgVO3 domains along the polymer matrix following a circular pattern. It was concluded that the proposed method was able to promote antimicrobial activity to acrylic resins against microorganisms evaluated, with the same concentration dependent of the nanomaterial. However, changes in the &beta;-AgVO3 dispersion in the polymer matrix are necessary to do not sacrifice the mechanical properties and to enhance the antimicrobial effect