Copolymers are used to increase the interfacial strength of immiscible components and suppress recombination of the minor phase by steric hindrance. The experiments conducted in these studies are designed to investigate in situ polymer loop formation at soft interfaces and functionalized nanotube surfaces. Block copolymers are the most effective type of copolymer for compatibilization because they extend perpendicular to the interface, allowing good entanglement with the homopolymer chains. Multiblock copolymers are more effective than diblock copolymers for strengthening the interface because they can cross the interface multiple times, forming “loops” in each phase that provide entanglement points for the homopolymer. The first part of this dissertation focuses on understanding how telechelic variables influence their effectiveness to compatibilize an immiscible polystyrene (PS)/polyisoprene (PI) homopolymer blend. A fast reacting anhydride and amine telechelic pair (Anh-PS-Anh/NH2-PI-NH2) are compared with a slower reacting epoxy and carboxylic acid pair (Epoxy-PS-Epoxy/COOH-PI-COOH). Different molecular weight pairs are used to investigate the influence of end group concentrations and steric effects. We also investigate how the loading level affects the conversion of one telechelic pair. The PI telechelic has a fluorescent tag, which enables gel permeation chromatography (GPC) with fluorescence detection to be used for determining the amount of tagged PI converted and the molecular weight of the copolymer formed in situ as a function of mixing time. The effectiveness of these telechelic pairs as compatibilizers is quantified by annealing the samples and using scanning electron microscopy (SEM) to measure the domain size of the minor phase as a function of annealing time. The second part of this study investigates the grafting of polymer loops to carboxylated multiwall nanotube (COOH-MWNT) surfaces and determining the reaction rate. These polymer loops will improve the nanotube dispersion by steric hindrance and improve energy transfer by creation of polymer chain entanglements. Fourier transform infrared spectroscopy (FT-IR) is used as a novel technique to measure the quantity of Epoxy-PS-Epoxy grafted to the nanotube surface. In addition, we determined the fraction of telechelics that form loops by further reacting the grafted nanotubes with monocarboxy terminated poly(4-methylstryrene) (COOH-P4MS), which only reacts with unbound Epoxy-PS-Epoxy chain ends.

<p>The objective of this project is to study the production of Li, Be and B isotopes emitted in the interaction of 12C with 12C at incident energies of 200 and 400 MeV.<br /> The energies of these produced fragments were measured with a detector telescope consisting of two silicon detectors at the incident energy of 200 MeV while a third silicon detector was added for the measurements at 400 MeV.</p>

Ein neues, verallgemeinertes Modell für Blasenkoaleszenz und –zerfall wurde entwickelt. Es basiert auf physikalischen Überlegungen und berücksichtigt verschiedene Mechanismen, die zu Blasenkoaleszenz und –zerfall führen können. In einer ausführlichen Literaturrecherche wurden zunächst die verfügbaren Modelle zusammengestellt und analysiert. Es zeigte sich, dass viele widersprüchliche Modelle veröffentlicht wurden. Keins dieser Modelle erlaubt die Vorhersage der Entwicklung der Blasengrößenverteilungen entlang einer Rohrströmung für einen breiten Bereich an Kombinationen von Volumenströmen der Gas- und der Flüssigphase. Das neue Modell wurde ausführlich in einem vereinfachten Testsolver untersucht. Dieser erfasst zwar nicht alle Einzelheiten einer sich entlang des Rohres entwickelten Strömungen, erlaubt aber im Gegensatz zu den CFD-Simulationen eine Vielzahl von Variationsrechnungen zur Untersuchung des Einflusses einzelner Größen und Modelle. Koaleszenz und Zerfall kann nicht getrennt von anderen Phänomenen und Modellen, die diese widerspiegeln, betrachtet werden. Es bestehen enge Wechselwirkungen mit der Turbulenz der Flüssigphase und dem Impulsaustausch zwischen den Phasen. Da die Dissipationsrate der turbulenten kinetischen Energie ein direkter Eingangsparameter für das neue Modell ist, wurde die Turbulenzmodellierung besonders genau untersucht. Zur Validierung des Modells wurde eine TOPFLOW-Experimentalserie zur Luft-Wasser-Strömungen in einem 8 m langen DN200-Rohr genutzt. Die Daten zeichnen sich durch eine hohe Qualität aus und wurden im Rahmen des TOPFLOW-IIVorhabens mit dem Ziel eine Grundlage für die hier vorgestellten Arbeiten zu liefern, gewonnen. Die Vorhersage der Entwicklung der Blasengrößenverteilung entlang des Rohrs konnte im Vergleich zu den bisherigen Standardmodellen für Blasenkoaleszenz und -zerfall in CFX deutlich verbessert werden. Einige quantitative Abweichungen bleiben aber bestehen. Die vollständigen Modellgleichungen sowie eine Implementierung über „User-FORTRAN“ in CFX stehen zur Verfügung und können für weitere Arbeiten zur Simulation polydisperser Blasenströmungen genutzt werden.

Les mousses liquides sont très utilisées dans l'industrie comme dans la vie quotidienne. Cependant, leur stabilité n'est ni complètement comprise ni complètement maîtrisée, la formulation étant essentiellement empirique. Il est donc difficile d'une part de prédire la capacité d'une solution de tensioactifs à générer des mousses et d'autre part de prédire et de contrôler leur déstabilisation. Ce travail de thèse propose des expériences conceptuellement simples qui s'appuient sur le caractère multi-échelle des mousses pour tenter d'établir des liens clairs entre physico-chimie et mécanismes de déstabilisation. Dans un premier temps, nous avons revisité une expérience d'entraînement de films liquides sur un cadre pour illustrer la stabilité des films lors de la génération des mousses ou pendant un réarrangement (processus T1). Nous avons mis en lumière l'existence de deux régimes. Un régime dit non confiné, pour lequel la stabilité des films et réduite et dépend de la physico-chimie. Un régime dit confiné pour lequel le rôle de la physico-chimie est limité et la stabilité est majoritairement contrôlée par l'hydrodynamique.Dans un second temps nous nous sommes intéressés à l'influence de la physico-chimie et de la fraction liquide sur la compétition entre coalescence et mûrissement grâce à l'étude d'une unique couche de bulles (mousse 2D). Nous proposons une méthode de mesure in situ de la perméabilité des films par l'étude simple et rapide du régime transitoire du mûrissement de mousses 2D. Nous avons observé une corrélation entre coefficient de diffusion du gaz contenu dans les bulles et perméabilité.Enfin nous décrivons les résultats d'une expérience spatiale sur le vieillissement à temps long des mousses humides (fraction liquide supérieure à 30% en volume), extrêmement difficile sur Terre à cause du drainage gravitaire, et à laquelle nous avons participé.

Ce travail s'inscrit dans le contexte de la modélisation et de la prévision de la durée de vie des aubes de turbine haute pression des turbines à gaz. Ces pièces sont réalisées en superalliage monocristallin base nickel tel que le MC2, matériau principal de l'étude. En service, ces dernières sont soumises à des conditions extrêmes de température et de contrainte. Des régimes d'urgence, dits O.E.I. (.One Engine Inoperative.), peuvent aussi survenir sur un hélicoptère bi-moteur : un des deux moteurs s'arrête ce qui provoque une augmentation de la température en sortie de chambre de combustion pour le moteur restant en fonctionnement. Dans le cadre de ce travail, le comportement anisotherme en fluage et en fatigue/fluage du superalliage monocristallin a été étudié afin de déterminer les répercussions des surchauffes à 1200. sur le comportement mécanique ultérieur à 1050. Il a pu être déterminé que le temps de pré-endommagement avant la surchauffe joue un rôle capital vis-à-vis de la durée de vie post-surchauffe. Cette influence est très dépendante de l'état microstructural du matériau sur lequel est réalisée la surchauffe (morphologie des précipités γ ', contraintes de cohérence entre les phases γ et γ '). Du point de vue des mécanismes d'endommagement, il a aussi été constaté que le niveau de température a une importance majeure en modifiant les contraintes de cohérence entre les deux phases γ et γ '. L'état microstructural jouant un rôle majeur sur la durée de vie lors des essais isothermes et anisothermes, une étude de l'évolution de la microstructure γ /γ' autour des particules de phase intermétallique μ a été faite, ainsi qu'une mesure expérimentale de l'évolution de la porosité, mesurée par des analyses tomographiques grâce à des essais de fluage multi-interrompus à haute température. Ceci a permis d'aboutir à un paramètre de dommage, à la frontière entre métallurgie et mécanique, prenant en compte les évolutions microstructurales. La coalescence orientée se déroulant à haute température, connue sous le nom de mise en radeaux, a une forte influence sur le comportement et l'endommagement des superalliages monocristallins. Ainsi, un nouveau modèle de mise en radeaux, prenant en compte la vitesse de sollicitation, a été implémenté dans le modèle de plasticité cristalline couplé comportement/endommagement Polystar. Ceci a permis d'améliorer la modélisation des essais longs. D'autres modifications ont été effectuées afin d'améliorer la modélisation lors des essais cycliques et de relaxation. Ce nouveau modèle a été testé et validé sur une éprouvette bi-entaillée générant des champs mécaniques multiaxiaux pendant un essai de fluage complexe anisotherme.

Introduced in 1991, solid ink color printing technology is widely used in the office printing, prepress proofing, and wide format color printing markets. Ink droplets are first deposited on a rotating drum and then transferred to paper to reproduce images with high print quality. The objective of this thesis is to develop scientific knowledge of ink droplet deposition, which is needed for precise image buildup on the drum surface. The first problem studied in the thesis is droplet formation from the printhead with varied working voltages and jetting frequencies. Attention is paid to the formation of satellite droplets, the contraction of ligaments and the startup of high frequency jetting. The jetting conditions for obtaining consistent droplet generation with satellites are determined. A theoretical model is developed to predict the lifetime of ligaments. The second problem we studied is the deposition of single droplets on solid surfaces. The surface texture and final shape of deposited droplets are correlated with impact conditions, which include printhead temperature, substrate temperature, distance from printhead to substrate, and the type of substrate surface. An analytical model is developed to evaluate the interaction of oscillation and viscous damping in the droplet during impact. The third problem covered in the thesis is the deposition of multiple ink droplets on the drum surface. Interaction between droplets causes drawback effect, which degrades print quality. We define a parameter to quantify the drawback effect with varied deposition conditions. A simple model is provided to predict conditions for making continuous lines based on the results of two ink droplets deposition. To understand the hydrodynamics in causing drawback effect, a series of experiments using large liquid droplets are carried out. Focus is put on the evolution of spread length and dynamics of contact line. Correlations for maximum and minimum spread lengths are developed, which are used to reveal the cause of drawback effect in the deposition of ink droplets.

Ce travail de thèse s'est focalisé sur l'étude des alliages Fe-14%Cr nanorenforcés par dispersion d'oxydes obtenus par broyage à haute énergie à partir de poudres pré-alliées de la matrice et d'Y2O3. L'objectif était double : (i) étudier la cinétique de précipitation, en particulier la phase de coalescence, des oxydes en fonction de la teneur en élément d'addition (Ti, Y, O) lors de traitements thermiques à haute température et postérieurs à l'étape de consolidation, et (ii) d'analyser les hétérogénéités de déformations élastiques et élastoplastiques dans ces aciers en fonction de l'avancement de la précipitation. La microstructure et la nanostructure ont été étudiées par microscopie électronique en transmission (MET) et diffusion de neutrons aux petits angles (DNPA). L'ensemble de ces techniques a permis de mettre en évidence des comportements différents selon les teneurs en éléments d'addition. En particulier, l'ajout de titane induit un ralentissement très net de la coalescence des particules contrairement aux ajouts d'oxygène et d'yttrium. Ces variations de teneurs initiales influent sur la forme, la structure cristallographique des particules, sur les relations d'orientations avec la matrice et en voie de conséquence, sur les cinétiques de précipitation. Par conséquent, assurer un rapport Ti /Y supérieur à 1 et limiter l'apport en oxygène sont des garants de la stabilité des nanoparticules à hautes températures dans les aciers ODS. Le phénomène de recristallisation a également été observé à haute température dans les matériaux dans lesquels la coalescence des oxydes est largement avancée. Afin de corréler l'évolution des microstructures avec celle des propriétés mécaniques, une modélisation macroscopique du durcissement a ensuite été réalisée, en distinguant les différentes contributions (nanoparticules, taille de grains et dislocations). Le durcissement calculé à partir des observations expérimentales est en très bon accord avec les valeurs mesurées. Ces calculs rendent bien compte des variations entre alliages et mettent en évidence l'influence prépondérante de la taille des particules sur la dureté des matériaux. Enfin une étude fine des hétérogénéités de déformation des grains en fonction de leur orientation cristallographique a été menée par diffraction de neutrons. Ces résultats ont été confrontés à un calcul micromécanique en champ moyen. Cette dernière partie a montré l'existence de comportements locaux différents dans des matériaux présentant des comportements macroscopiques similaires.

Introduced in 1991, solid ink color printing technology is widely used in the office printing, prepress proofing, and wide format color printing markets. Ink droplets are first deposited on a rotating drum and then transferred to paper to reproduce images with high print quality. The objective of this thesis is to develop scientific knowledge of ink droplet deposition, which is needed for precise image buildup on the drum surface. The first problem studied in the thesis is droplet formation from the printhead with varied working voltages and jetting frequencies. Attention is paid to the formation of satellite droplets, the contraction of ligaments and the startup of high frequency jetting. The jetting conditions for obtaining consistent droplet generation with satellites are determined. A theoretical model is developed to predict the lifetime of ligaments. The second problem we studied is the deposition of single droplets on solid surfaces. The surface texture and final shape of deposited droplets are correlated with impact conditions, which include printhead temperature, substrate temperature, distance from printhead to substrate, and the type of substrate surface. An analytical model is developed to evaluate the interaction of oscillation and viscous damping in the droplet during impact. The third problem covered in the thesis is the deposition of multiple ink droplets on the drum surface. Interaction between droplets causes drawback effect, which degrades print quality. We define a parameter to quantify the drawback effect with varied deposition conditions. A simple model is provided to predict conditions for making continuous lines based on the results of two ink droplets deposition. To understand the hydrodynamics in causing drawback effect, a series of experiments using large liquid droplets are carried out. Focus is put on the evolution of spread length and dynamics of contact line. Correlations for maximum and minimum spread lengths are developed, which are used to reveal the cause of drawback effect in the deposition of ink droplets.

Several challenges are still holding back the technological transfer of printed electronics to industry in spite of recent progresses. In this thesis work, the printing method of inks based on silver nanoparticles (<Ø>=25 nm) was optimized according to its rheology and to the fluid/substrate interactions for the fabrication of electrical interconnections with a thickness of 500 nm. These lines were printed on silicon or flexible substrates and annealed either by conventional (oven or infrared) or selective methods (microwave) at temperatures comprised between 100 and 300 °C.A better understanding of the relationship between process and microstructure of these printed thin films, based on several crystallographic equipments (XRD, EBSD and EDX), led to the optimization of nanocrystallites growth with an activation energy of about 3 to 5 kJ*mol-1. In addition to the low residual stress (70 MPa), this optimization is used to achieve low electrical resistivity (3.4 μOhm*cm) associated with a greater coherence of the crystal lattices at grain boundaries. The probability of electron scattering at such interfaces can be further reduced using an innovative approach of oriented crystallite growth by atomic interdiffusion from the substrate.The low mechanical stiffness (E<50 GPa) of these porous lines requires a reinforcement step either by crystalline texturation or by electroless growth to withstand the assembly and wire-bonding steps. The fabrication of a functional demonstrator thus validated the printing technology for the manufacture of electronic components.

Cette thèse est consacrée à l'étude de systèmes subissant des coagulations et fragmentations succesives. Dans le cas déterministe, on travaille avec des solutions mesures de l'équation de coagulation - multifragmentation. On étudie aussi la contrepartie stochastique de ces systèmes : les processus de coalescence - multifragmentation qui sont des processus de Markov à sauts. Dans un premier temps, on étudie le phénomène de coagulation seul. D'un côté, l'équation de Smoluchowski est une équation intégro-différentielle déterministe. D'un autre côté, on considère le processus stochastique connu sous le nom de Marcus-Lushnikov qui peut être regardé comme une approximation de la solution de l'équation de Smoluchowski. Nous étudions la vitesse de convergence par rapport à la distance de type Wassertein entre les mesures lorsque le nombre de particules tend vers l'infini. Notre étude est basée sur l'homogénéité du noyau de coagulation $K$. On complémente les calculs pour obtenir un résultat qui peut être interprété comme une généralisation de la Loi des Grands Nombres. Des conditions générales et suffisantes sur des mesures discrètes et continues $mu_0$ sont données pour qu'une suite de mesures $mu_0^n$ à support compact existe. On a donc trouvé un taux de convergence satisfaisant du processus Marcus-Lushnikov vers la solution de l'équation de Smoluchowski par rapport à la distance de type Wassertein égale à $1/sqrt{n}$. Dans un deuxième temps on présente les résultats des simulations ayant pour objectif de vérifier numériquement le taux de convergence déduit précédemment pour les noyaux de coagulation qui y sont étudiés. Finalement, on considère un modèle prenant en compte aussi un phénomène de fragmentation où un nombre infini de fragments à chaque dislocation est permis. Dans la première partie on considère le cas déterministe, dans la deuxième partie on étudie un processus stochastique qui peut être interprété comme la version macroscopique de ce modèle. D'abord, on considère l'équation intégro-partielle différentielle de coagulation - multifragmentation qui décrit l'évolution en temps de la concentration $\mu_t(x)$ de particules de masse $x>0$. Le noyau de coagulation $K$ est supposé satisfaire une propriété de $\lambda$-homogénéité pour $lambda in (0,1]$, le noyau de fragmentation $F$ est supposé borné et la mesure $beta$ sur l'ensemble de ratios est conservative. Lorsque le moment d'ordre $lambda$ de la condition initial $mu_0$ est fini, on est capable de montrer existence et unicité d'une solution mesure de l'équation de coagulation - multifragmentation. Ensuite, on considère la version stochastique de cette équation, le processus de coalescence - fragmentation est un processus de Markov càdlàg avec espace d'états l'ensemble de suites ordonnées et est défini par un générateur infinitésimal donné. On a utilisé une représentation Poissonienne de ce processus et la distance $\delta_{\lambda}$ entre deux processus. Grâce à cette méthode on est capable de construire une version finie de ce processus et de coupler deux processus démarrant d'états initiaux différents. Lorsque l'état initial possède un moment d'ordre $lambda$ fini, on prouve existence et unicité de ces processus comme la limite de suites de processus finis. Tout comme dans le cas déterministe, le noyau de coagulation $K$ est supposé satisfaire une propriété d'homogénéité. Les hypothèses concernant la mesure $\beta$ sont exactement les mêmes. D'un autre côté, le noyau de fragmentation $F$ est supposé borné sur tout compact dans $(0,\infty)$. Ce résultat est meilleur que celui du cas déterministe, cette amélioration est due à la propriété intrinsèque de masse totale non-explosive que possède un système avec un moment fini d'ordre $\lambda$.