Organic solar cells offer attractive properties for novel applications and continuous advances in material and concept development have led to significant improvements in device performance. To exploit their full potential (roll-to-roll production of flexible and top-illuminated devices, using e.g. opaque metal foil or textile as substrate), highly transparent, conductive, mechanically flexible, and cost-efficient top electrodes are of great importance. The current standard material indium tin oxide (ITO) is rigid, expensive and requires a high energy / high temperature deposition process, limiting ITO (and other transparent conductive oxides) to bottom electrode applications. This work presents fundamental investigations to understand and control the properties of transparent conductors and documents four different approaches to prepare transparent electrodes on top of efficient small molecule organic solar cells, with the aim to replace ITO. Fullerene C60 layers are investigated as completely carbon-based electrodes. For an optimized doping concentration, sheet resistance and transmittance are improved and efficient solar cells are realized. Since the lateral charge transport is still limited, a combination with a microstructured conductor is suggested. Pulsed laser deposition allows for the first time a damage-free preparation of gallium doped zinc oxide (ZnO:Ga) layers on top of organic devices by careful optimization of the deposition atmosphere. ZnO:Ga electrodes with a transmittance of Tvis = 82.7 % and sheet resistance Rs = 83 Ohm/sq are obtained. The formation of local shunts due to ZnO:Ga droplets is identified and then prevented by a shadow mask between the target and the sample, enabling solar cells with similar efficiency (2.9 %) compared to a reference device using a state-of-the-art metal top contact. Another very promising alternative are intrinsically flexible, ultra-thin silver layers. By introducing an oxide interlayer, the adverse interpenetration of silver and organic materials is prevented and the charge extraction from the solar cells is improved. With a second oxide layer on top, the silver electrode is significantly stabilized, leading to an increased solar cell lifetime of 4500 h (factor of 107). Scanning electron micrographs of Ag thin films reveal a poor wetting on organic and oxide substrates, which strongly limits the electrode performance. However, it is significantly improved by a 1 nm thin seed layer. An optimized Au/Ag film reaches Tvis = 78.1 % and Rs = 19 Ohm/sq, superior to ITO. Finally, silver electrodes blended with calcium show a unique microstructure which enables unusually high transmittance (84.3 % at 27.3 Ohm/sq) even above the expectations from bulk material properties and thin film optics. Such values have not been reached for transparent electrodes on top of organic material so far. Solar cells with a Ca:Ag top electrode achieve an efficiency of 7.2 %, which exceeds the 6.9 % of bottom-illuminated reference cells with conventional ITO electrodes and defines a new world record for top-illuminated organic solar cells. With these electrodes, semi-transparent and large-area devices, as well as devices on opaque and flexible substrates are successfully prepared. In summary, it is shown that ZnO:Ga and thin metal electrodes can replace ITO and fill the lack of high performance top electrodes. Moreover, the introduced concepts are not restricted to specific solar cell architectures or organic compounds but are widely applicable for a variety of organic devices.

The aim of this work was to investigate silver nanowire as well as carbon nanotube networks as transparent conducting electrodes for small molecule organic solar cells. In the framework of the nanowire investigations, a low-temperature method at less than 80 °C is developed to obtain highly conductive networks directly after the deposition and without post-processing. In detail, specific non-conductive organic materials act as a matrix where the nanowires are embedded in such that a mutual attraction based on capillary forces and hydrophobic interaction is created. This process is mediated by the ethanol contained in the nanowire dispersion and works only for sublayer materials which exhibit hydrophobic and hydrophilic groups at the same time. In contrast to high-temperature processed reference electrodes (210 °C for 90 min) without matrix, a slightly lower sheet resistance of 10.8 Ohm/sq at a transparency of 80.4 % (including substrate) is obtained by using polyvinylpyrrolidone as the sublayer material. In comparison to annealed silver nanowire networks, the novel approach yields a performance enhancement in corresponding organic solar cells which can compete with ITO-based devices. Furthermore, a novel approach for scalable, highly conductive, and transparent silver nanowire top-electrodes for organic optoelectronic devices is introduced. By utilizing a perfluorinated methacrylate as stabilizer, silver nanowires with high aspect ratio can be transferred into inert solvents which do not dissolve most organic compounds making this modified dispersion compatible with small molecule and polymer-based organic optoelectronic devices. The inert silver nanowire dispersion yields highly performing top-electrodes with a sheet resistance of 10.0 Ohm/sq at 80.0 % transparency (including substrate) directly after low-temperature deposition at 30 °C and without further post-processing. In comparison to similarly prepared reference devices comprising a thin-metal film as transparent top-electrode, reasonable power conversion efficiencies are demonstrated by spray-coating this dispersion directly on simple, air-exposed small molecule-based organic solar cells. Moreover, a deeper understanding of the percolation behavior of silver nanowire networks has been achieved. Herein, direct measurements of the basic network parameters, including the wire-to-wire junction resistance and the resistance of a single nanowire of pristine and annealed networks have been carried out for the first time. By putting the values into a simulation routine, a good accordance between measurement and simulation is achieved. Thus, an examination of the electrical limit of the nanowire system used in this work can be realized by extrapolating the junction resistance down to zero. The annealed silver nanowires are fairly close to the limit with a theoretical enhancement range of only 20 % (common absolute sheet resistance of approximately 10 Ohm/sq) such that a significant performance improvement is only expected by an enlargement of the nanowire length or by the implementation of new network geometries. In addition, carbon nanotube networks are investigated as alternative network-type, transparent bottom-electrode for organic small molecule solar cells. For that purpose, cleaning and structuring as well as planarization procedures are developed and optimized which maintain the optoelectronic performance of the carbon nanotube electrodes. Furthermore, a hybrid electrode consisting of silver nanowires covered with carbon nanotubes is fabricated yielding organic solar cells with only 0.47 % power conversion efficiency. In contrast, optimized electrodes comprising only carbon nanotubes show significantly higher efficiency. In comparison to identically prepared ITO devices, comparable or lower power conversion efficiencies of 3.96 % (in p-i-n stack), 4.83 % (in cascade cell) as well as 4.81 % (in p-n-i-p architecture) are demonstrated. For an inverted n-i-p stack design, the highest power conversion efficiency of 5.42 % is achieved.

Following a 15-year-long investigation on graphene, two-dimensional (2D) carbon-rich conjugated frameworks (CCFs) have attracted growing research interest as a new generation of multifunctional materials. Typical 2D CCFs include 2D π-conjugated polymers (also classified as 2D π-conjugated covalent organic frameworks) and 2D π-conjugated metal–organic frameworks, which are characterized by layer-stacked periodic frameworks with high in-plane π-conjugation. These unique structures endow 2D CCFs with regular porosities, large specific surface areas, and superior chemical stability. In addition, 2D CCFs exhibit certain notable properties (e.g., excellent electronic conductivity, designable topologies, and defined catalytic/redox-active sites), which have motivated increasing efforts to explore 2D CCFs for electrochemical energy applications. In this Perspective, the structural features and synthetic principles of 2D CCFs are briefly introduced. Moreover, we discuss recent achievements in 2D CCFs designed for various electrochemical energy conversion (electrocatalysis) and storage (supercapacitors and batteries) applications. Particular emphasis is placed on analyzing the precise structural regulation of 2D CCFs. Finally, we provide an outlook about the future development of synthetic 2D CCFs for electrochemical applications, which concerns novel monomer design, chemical methodology/strategy establishment, and a roadmap toward practical applications.

No description available.

Im Rahmen dieser Arbeit wurde die Akustomigrationsresistenz von in Kupfertechnologie hergestellten SAW-Strukturen charakterisiert und diese mit dem Schädigungsverhalten von Al-basierten SAW-Strukturen unter gleichen Belastungsbedingungen verglichen. Dies wurde durch die Anwendung einer speziellen Power-SAW-Teststruktur ermöglicht. Das Schädigungsniveau wurde hierbei über die irreversible Verschiebung der Peakfrequenz bzw. durch Änderungen im elektrischen Widerstand sowie durch mikroskopische Untersuchung der Mikrostruktur beurteilt. Die durchgeführten SAW-Belastungsexperimente mit HF-Leistungen bis zu 4,5 W zeigten, dass das entwickelte Ta-Si-N/Cu/Ta-Si-N-System im Vergleich zur Al/Ti-Metallisierung eine Akustomigrationsresistenz besitzt, die um mehr als drei Größenordnungen höher ist als jene der Al/Ti-Metallisierung. Hohe SAW-Belastungen verursachten sowohl im Al- als auch im Cu-Testwandler Hügel- und Lochbildung. Während die Hügel in der Al/Ti-Metallisierung senkrecht zur Oberfläche bis zu einer Höhe von 1 µm und die Löcher bis hinab an die Ti-Schicht wuchsen, bildeten sich in den extrem belasteten Cu-basierten Wandlern nur flache Hügel und schmale Löcher aus, welche noch mit der Deckschicht vollständig bedeckt waren. Anhand von REM/EBSD, TEM sowie FIB-Untersuchungen konnte ein relevanter Zusammenhang zwischen der Mikrostruktur und dem Schädigungsverhalten aufgezeigt werden.

Die Basis für den therapeutischen Einsatz elektrischer Felder bei der Behandlung von Knochenbrüchen liegt in der Existenz von belastungsabhängigen elektrischen Potentialen im Knochen. Die zellulären Wirkungsmechanismen sind jedoch unverstanden. Um zu untersuchen, ob und wie elektrische Felder Wachstum und Differenzierung von Knochenzellen beeinflussen, wurden humane Osteosarcomazellen (HOS TE85) und aus Minischweinen isolierte primäre Osteoblasten mit elektrischen Feldern im Frequenzbereich von 0.1 Hz bis 100 kHz befeldet und verschiedene zelluläre Parameter zeitabhängig gemessen. Das elektrische Feld wurde mittels platinierten Platinelektroden appliziert, um ausreichend hohe Feldstärken bei gleichzeitig guter Kontrolle über die im Gewebe erzeugte Wellenform zu gewährleisten. Beim Einsatz von Elektroden müssen jedoch elektrochemische Reaktionen an der Elektrodenoberfläche berücksichtigt werden. Daher wurden verschiedene Elektroden für die in vivo- und in vitro-Stimulation mit elektrischen und numerischen Methoden untersucht und verglichen. Das führte einerseits zur Erarbeitung verschiedener Kriterien zur Auswahl geeigneter Elektrodenmaterialien und -geometrien. Andererseits konnten detaillierte Angaben zur effektiven Feldstärke und Feldverlauf in der Zellebene sowie zu elektrochemisch bedingten Nebenwirkungen gemacht werden. Es konnte gezeigt werden, dass elektrische Felder das Signalsystem und den Stoffwechsel von Knochenzellen im gesamten untersuchten Frequenzbereich beeinflussen. Die Richtung des Nettoeffekts war jedoch im oberen und im unteren Frequenzbereich unterschiedlich. Im Frequenzbereich über 1 kHz fanden wir immer eine Erhöhung des Wachstums und der Konzentration der "second messenger" und eine Herabsetzung der Konzentration der reaktiven Sauerstoffverbindungen (ROS). Bei Frequenzen unter 1 kHz wurde dagegen eine Erhöhung der Aktivität der alkalischen Phosphatase und des oxidativen Stress beobachtet. Signifikante Effekte traten jedoch nur bei Feldstärken oberhalb 100 V/m auf. Hinweise auf bevorzugte Frequenzen oder Wellenformen, die für "Fenstereffekte" sprechen würden, konnten nicht gefunden werden. Da alle zellulären Parameter an einem einheitlichen System gemessen wurden, ließen sich die Ergebnisse in ein Modell der feldinduzierten Signaltransduktion integrieren. Prinzipiell muss man von einem gemeinsamen Effekt mehrerer Signalwege ausgehen. Dabei kann die Erhöhung der intrazellulären Kalziumkonzentration als ein genereller Mechanismus der Feldwirkung angesehen werden. Dafür sind sowohl der Influx als auch die Freisetzung von Kalzium aus intrazellulären Speichern verantwortlich. Es konnte weiterhin gezeigt werden, dass auch cGMP und Prostaglandin E2, jedoch nicht cAMP an der Vermittlung der Feldwirkung beteiligt ist. Außerdem wurde die Translokation der mitogen-aktivierten Proteinkinase (MAPK) beeinflusst. Trotzdem sind die beobachteten Effekte relativ schwach im Vergleich zu publizierten klinischen Erfolgen. Es muss daher in vivo Verstärkungsmechanismen geben, die durch Untersuchungen an Zellkulturen nicht erfasst werden können. / The therapeutic use of electric fields in the treatment bone fracture healing is based on the existence of different load dependent electric potentials in bone. However, the cellular mechanisms of field action are still not understood. We investigated the effect of electric fields on proliferation and differentiation of human osteosarcoma cells (HOS TE85) and primary osteoblasts isolated from mini pigs. The cells were exposed to electric fields (0.1 Hz - 100 kHz) and various cellular parameters were measured. The field was applied using platinized platinum electrodes ensuring sufficiently strong electric fields and a well controlled wave form in the tissue. Nevertheless, in this case electrochemical reactions which occur at the electrode surface have to be taken into account. That’s why various electrodes for in vivo and in vitro stimulation are characterized by electrical and numerical methods leading not only to criteria for choosing electrode materials and geometries, but also providing detailed knowledge about the electric field induced in the tissue and electrochemically induced side effects. We found that cellular signaling as well as proliferation and differentiation of bone cells are influenced by electric fields in the whole investigated frequency range. Proliferation and the second messenger concentrations are increased at frequencies above 1 kHz, whereas below 1 kHz the alkaline phosphatase activity is increased. Significant effects were found only for electric fields above 100 V/m, but we could not find any hints on preferred frequencies or wave forms ruling out "window effects". Because all cellular parameters were measured within one experimental system, the results can be summarized in a signal transduction model for the action of electric fields. Generally, a common action of multiple signaling pathways has to be assumed. The increase of the intracellular calcium concentration can be considered as a general mechanism of field action. This increase is caused by calcium release from intracellular calcium stores as well as influx of extracellular calcium. Additionally, the concentration of cGMP and prostaglandin E2, but not that of cAMP is increased by the electric field. Furthermore, the translocation of the mitogen activated protein kinase (MAPK) is influenced. Nevertheless, the field effects found are weak compared to those published in clinical studies. We suppose that there are amplifying mechanisms in vivo which could not be seen during in vitro investigations.

Transparente Elektroden finden breite Verwendung in unterschiedlichen kommerziellen Produkten. Dünnschichtsolarzellen basieren ebenso auf diesen Funktionsschichten wie Displays oder organische Leuchtdioden. Im Falle von Dünnschichtsolarzellen kann durch gezielte Einstellung der Oberflächentextur der transparenten Elektrode ein entscheidender Einfluss auf die erreichbare Effizienz genommen werden. Dabei wird eine Verlängerung der Weglänge des Lichtes im Absorbermaterial durch Mehrfachreflexionen angestrebt. Häufig werden dafür Schichten transparenter leitfähiger Oxide (TCO) gezielt texturiert. Eine weitere Möglichkeit zur Erzeugung transparenter Elektroden stellt die Verwendung feiner Metallgitter dar. Diese ermöglichen hohe Leitfähigkeiten im Bereich der Gitterstege und hohe Transparenz im Bereich zwischen den Stegen. In dieser Arbeit sollte ein auf nasschemischen Prozessen basierendes Verfahren entwickelt werden, mit dem es möglich ist, sowohl strukturierte TCO-Elektroden als auch Metallgitter unterschiedlicher Geometrien gezielt herzustellen. Die Leistungsfähigkeit der Elektroden sollte anhand der Integration in entsprechende Bauteile bewertet werden. Namentlich sollte dieser Prozess für Cd2SnO4 (engl. Cadmium Tin Oxide, CTO) als ein TCO-Material hoher Transparenz und Leitfähigkeit sowie für Silber und Kupfer als metallische Systeme anwendbar sein. Als zielführende Methode kam die Nanoprägelithographie (von engl. Nanoimprint Lithography, NIL) zum Einsatz. Dieses Verfahren erlaubt die schnelle, einfache und kostengünstige Herstellung strukturierter Oberflächen. Grundsätzlich wird dazu ein strukturierter Elastomerstempel in eine Schicht eines zu vernetzenden Materials gepresst. Während des Pressens findet die Vernetzung statt. Nach anschließender Separation von Stempel und Schicht resultiert eine strukturierte Oberfläche. Gängige Präkursorensysteme für anorganische Verbindungen, bei denen Vernetzungsprozesse ablaufen, stellen Sol-Gel-Methoden und sogenannte polymere Präkursoren dar. Für letztere werden Metallzitrate mit Ethylenglykol verestert, um ein vernetztes Polymer zu generieren. Nach thermischem Entfernen der Organik bleibt das Metalloxid zurück. Im Rahmen dieser Arbeit ist ein Präkursorensystem entwickelt worden, das Metallionen komplexiert, auf Glassubstrate beschichtet werden kann und eine thermische Polymerisation erlaubt. Aus dem erhaltenen polymeren Präkursor konnten die Zielverbindungen durch thermisches Zersetzen einerseits in Pulverform und andererseits über vorhergehende Schleuderbeschichtung in Form dünner Schichten erhalten werden. Im Falle des kubischen Cd2SnO4 wurde im Rahmen dieser Arbeit erstmals eine Nanopulver-Synthese mit phasenreinem Produkt aus flüssigem Präkursor beschrieben. Dafür stellten sich der Anteil der verwendeten organischen Bestandteile sowie die Zersetzungsgeschwindigkeit als entscheidende Einflussparameter heraus. Zudem wurden CTO Dünnschichten mit dem beschriebene Präkursor hergestellt. Eine optimale Brenntemperatur zur Erzeugung phasenreiner CTO-Schichten von 700 ‰ wurde ermittelt. Die Zersetzungsgeschwindigkeit (bzw. Aufheizrate) beeinflusste die Oberflächenmorphologie der erhaltenen Schichten maßgeblich. Eine schrittweise Zersetzung (100 ‰°C, 200 °C‰, Zieltemperatur) führte dabei in effizienter Weise zu kompakten Schichten. Diese zeigten sehr gute optische und elektronische Eigenschaften. So konnten etwa 300 nm dicke CTO-Schichten mit spezifischen Widerständen von ca. 1 • 10^(−5) Ohm m bei einer Transmission von etwa 80 % (inklusive Glassubstrat) erhalten werden. Derartige CTO-Schichten konnten erfolgreich als transparente Frontelektroden für a-Si Dünnschichtsolarzellen verwendet werden. Ein positiver Einfluss periodischer Linienstrukturen auf die Lichteinfangeigenschaften und den resultierenden Photostrom im Vergleich zu flachen CTO-Schichten wurde bestätigt. Auch für die Herstellung von CdTe-Dünnschichtsolarzellen konnten die CTO-Schichten erfolgreich eingesetzt werden. Die erreichten Effizienzen lagen jedoch lediglich im Bereich von 3 bis 3,6 %. Ein signifikanter Unterschied zwischen flachen und strukturierten Proben konnte nicht ausgemacht werden. Durch die reduzierenden Eigenschaften von Zitronensäure und Ethylenglykol gegenüber Ag+ und Cu2+ Ionen war es möglich, die Metalle in elementarer Form durch einfache thermische Behandlung des Präkursors zu erhalten. Während dieser Prozess für silberhaltige Systeme relativ einfach zu realisieren war, musste bei kupferhaltigen Proben die Bildung oxidischer Nebenphasen festgestellt werden. So war für Letzteres eine reduktive Nachbehandlung vollständig oxidierter Proben im Wasserstoffplasma zielführend und lieferte leitfähige Dünnschichten mit hohem Cu(0)-Anteil. Im Falle von Silber führte eine geeignete thermische Behandlung der Präkursorschicht zu dünnen, leitfähigen Silberschichten mit spezifischen Widerständen von ca. 6 • 10^(−8) Ohm m (Festkörper: ca.1 • 10^(−8) Ohm m). Die Übertragung des NIL-Prozesses gelang sowohl für silber- als auch kupferhaltige Systeme. Mit NIL-strukturierten Silberdünnschichten gelang so die Herstellung semitransparenter Elektroden mit spezifischen Widerständen von 2,2 • 10^(−7) Ohm m, welche in Elektrolumineszenzbauteilen verwendet wurden. Aufgrund der relativ niedrigen Temperaturen, die für die Zersetzung des Silberpräkursors nötig waren (ca. 250 ‰ ), war die Fertigung entsprechender Elektroden und Bauteile auch auf Polyimidfolien möglich. Insgesamt bleibt die Erkenntnis, dass NIL-strukturierte dünne Schichten erfolgreich in optoelektronische Bauteile integriert werden konnten. Variable Präkursorsysteme erlauben die Herstellung verschiedener Schichten und somit Anwendungen in unterschiedlichen Bauteilen. Polymere Präkursoren haben sich als geeignet für dieses Vorgehen erwiesen und können relativ einfach auf diverse oxidische Stoffsysteme übertragen werden. Gleichzeitig eignen sie sich zur Herstellung metallischer transparenter Elektroden durch NIL-Strukturierung, was insbesondere im Hinblick auf flexible Bauteile von Vorteil ist.

This paper reports a novel and remarkably facile approach towards vertically aligned nanosheets on three-dimensional (3D) Ni foams. Conducting polypyrrole (PPy) sheets were grown on Ni foam through the volatilization of the environmentally friendly solvent from an ethanol–water solution of pyrrole (Py), followed by the polymerization of the coated Py in ammonium persulfate (APS) solution. The PPy-decorated Ni foams and commercial activated carbon (AC) modified Ni foams were employed as the two electrodes for the assembly of flexible all-solid-state asymmetric supercapacitors. The sheet-like structure of PPy and the macroporous feature of the Ni foam, which render large electrode–electrolyte interfaces, resulted in good capacitive performance of the supercapacitors. Moreover, a high energy density of ca. 14 Wh kg−1 and a high power density of 6.2 kW kg−1 were achieved for the all-solid-state asymmetric supercapacitors due to the wide cell voltage window.

This paper reports a novel and remarkably facile approach towards vertically aligned nanosheets on three-dimensional (3D) Ni foams. Conducting polypyrrole (PPy) sheets were grown on Ni foam through the volatilization of the environmentally friendly solvent from an ethanol–water solution of pyrrole (Py), followed by the polymerization of the coated Py in ammonium persulfate (APS) solution. The PPy-decorated Ni foams and commercial activated carbon (AC) modified Ni foams were employed as the two electrodes for the assembly of flexible all-solid-state asymmetric supercapacitors. The sheet-like structure of PPy and the macroporous feature of the Ni foam, which render large electrode–electrolyte interfaces, resulted in good capacitive performance of the supercapacitors. Moreover, a high energy density of ca. 14 Wh kg−1 and a high power density of 6.2 kW kg−1 were achieved for the all-solid-state asymmetric supercapacitors due to the wide cell voltage window.

An EU-funded project Fit-4-AMandA aims to establish a technological roadmap to scale-up from less than hundred stacks/year (manual assembly) to 50,000 stacks/year (automated assembly) in 2020 and beyond. Existing membrane-electrode assembly (MEA) and stack were redesigned/adapted for manufacturability and automation. The technology and machine system for the automated assembly of polymer-electrolyte-membrane fuel cell (PEMFC) stacks were developed, manufactured and are currently being tested. Fast in-line non-destructive quality-assurance methods for automated production of MEAs and stack assembly are being developed and implemented. For the final period of the project, a validation of the designs, hardware, tools and software for the automated production of MEAs and stack assembly as well as an integration of one of the prototype stacks manufactured by the automated processes into a light-commercial vehicle followed by a field-testing are scheduled. / Die breite Markteinführung von wasserstoffbasierten Antriebssystemen verlangt zunehmend nach einer kosteneffizienten und serientauglichen Produktion von Brennstoffzellenstacks. So sehen die Ziele der Europäischen Union vor, die Herstellung von aktuell unter 100 Stacks pro Jahr auf 50.000 Stacks pro Jahr bis zum Jahr 2020 zu erhöhen. Um dies zu erreichen, sollen im Rahmen des vom Fuel Cell and Hydrogen Joint Undertaking (FCH JU) der europäischen Union geförderten Projektes Fit-4-AMandA automatisierte Anlagen für solche Stückzahlen befähigt werden. Der Beitrag beschreibt, wie die bereits verfügbare Membran-Elektroden-Einheit (MEA) und der Stack bezüglich Herstellbarkeit und Automatisierung konstruktiv umgestaltet und angepasst wurden. Die neu entwickelte Technologie und das Maschinensystem für die automatisierte Montage von PEM-FC-Stacks sowie Verfahren der INLINE-Qualitätssicherung und der zerstörungsfreien Prüfung werden mit ihren Implementierungsmöglichkeiten in die automatisierte Fertigungsstrecke vorgestellt. Ein Ausblick gibt eine Übersicht über die weiteren Entwicklungsschritte wie die Validierung der Entwürfe, der Hard- und Software für die automatisierte Produktion der MEAs und Stacks. Eine vorgesehene spätere Integration der so gefertigten Stacks in ein Fahrzeug und die damit verbundenen Feldtests zur Untersuchung der Reproduzierbarkeit und Zuverlässigkeit der Stacks werden abschließend dargestellt. Die Förderung des Projektes erfolgt im Rahmen der Finanzhilfevereinbarung Nr. 735606 des FCH JU der EU.