Made available in DSpace on 2015-04-14T13:58:54Z (GMT). No. of bitstreams: 1 443125.pdf: 1527521 bytes, checksum: 2c9a9ef7ac02480e7ed3b2734a8acc04 (MD5) Previous issue date: 2012-08-22 / Peripheral nerve injury accident is a common type of lesion that can cause loss of mobility and decrease the quality of life. Despite advances in the biomedical area, there are few cases where there is complete functional recovery of a damaged nerve. The application of biodegradable polymers such as poly(lactide-co-glycolide) (PLGA), shows a viable alternative of treatment in peripheral nerves injuries for presenting mechanical strength, biocompatibility and controlled degradation, being also an excellent material for drug delivery. A PLGA scaffold should be porous with pore sizes on the order of micro-and nanometer, which offers the possibility to insert growth factors, promoting a constant release of these biological structures. The aim of this research is to produce porous scaffolds of PLGA. This was achieved by dissolving the polymer in chloroform, adding a porogenic compound. A titanium rod with 2mm in diameter was deeped in the suspension obtained and dried in a hood, obtaining a layer of PLGA / porogen agent on the surface of the rod. In sequence, the rod was immersed in a solution of PLGA with chloroform. After dried for 2 hours in a hood, the titanium rods were submerged in deionized water for 48 hours, during which the water was changed every 8 hours in order to remove the porogenic agent. After this process, the tubular structures formed were easily removed from the rods. Finally, the prepared tubes were divided into groups and treated with different concentrations of sodium hydroxide, to create pores in the order of nanometers, and subsequently vacuum dried for 48 hours. The structures obtained were characterized by XRD, FTIR, SEM and the in vitro degradation was monitored by GPC. / Danos a nervos perif?ricos s?o formas comuns de les?es que podem causar perda de mobilidade e diminuir a qualidade de vida. Apesar dos avan?os no campo biom?dico, existem poucos casos em que h? recupera??o funcional completa de um nervo danificado. A aplica??o de pol?meros biodegrad?veis tais como PLGA, apresenta uma alternativa vi?vel no tratamento de les?es de nervos perif?ricos por possuir resist?ncia mec?nica, biocompatibilidade e degrada??o controlada. Uma matriz de PLGA deve apresentar poros na ordem de micr?metros e nan?metros, oferecendo a possibilidade de inclus?o de fatores de crescimento e possivelmente promovendo uma liberta??o constante destas estruturas biol?gicas. O objetivo desta pesquisa ? produzir matrizes porosas de PLGA. Isto foi realizado atrav?s da dissolu??o do pol?mero em clorof?rmio, seguida da adi??o de um composto porog?nico. Uma haste de tit?nio com 2mm de di?metro foi imersa na suspens?o obtida e quando retirada, foi seca em capela, obtendo uma camada de PLGA/agente porog?nico na superf?cie da haste. Na sequ?ncia, a haste foi imersa em uma solu??o de PLGA com clorof?rmio. Ap?s seca durante 2h em capela, as hastes de tit?nio foram submersas em ?gua deionizada durante 48h, durante as quais, a ?gua foi trocada a cada 8h, para remo??o do agente porog?nico. Ap?s este processo, as estruturas tubulares formadas s?o facilmente removidas das hastes. Finalmente, os tubos confeccionados foram divididos em grupos, e tratados com diferentes concentra??es de hidr?xido de s?dio, para cria??o de poros na ordem de nan?metros, sendo, subsequentemente, secos em forno a v?cuo durante 48h. As estruturas obtidas foram caracterizadas por XRD, FTIR, MEV e a degrada??o in vitro foi acompanhada por GPC.

Made available in DSpace on 2015-04-14T13:59:01Z (GMT). No. of bitstreams: 1 451790.pdf: 380413 bytes, checksum: 93bdbfaddeeadb736f607d61d5cef5ab (MD5) Previous issue date: 2013-08-23 / The mechanisms of initiation, transport and deposition of sediment in turbidity currents have been studied because of its potential environmental impact and for containing the main hydrocarbon reservoirs. Several research groups have performed simulations of these phenomena in reduced models, using the coal 205 as sediment. However, this material has limitations on its use in noninvasive imaging techniques for monitoring of turbidity currents in tanks of hydraulic simulation. Thus, this study aimed the preparation of polymer nanocomposites with the potential to replace the coal 205 in these simulations. Polymer nanocomposites based on thermosetting matrices containing inorganic filler (clay, graphite and carbon black) were prepared.By means of scanning electron microscopy (SEM) and transmission electron microscopy (TEM) micrographs it was possible to verify that the fillers incorporated into polymer matrices showed nanometric dimensions and were dispersed homogeneously, except the carbon black that presented some points of agglomeration. The forms of particles are also evaluated by SEM , classified as semi-angular and semi-rounded. The electrical properties were investigated using electrical impedance spectroscopy. The materials studied presented values of settling velocities and density near the coal 205. Thus, all nanocomposites prepared exhibited the desired characteristics to replace the coal 205 in tank hydraulics simulation. / Os mecanismos de inicia??o, transporte e deposi??o de sedimentos em correntes de turbidez v?m sendo estudados devido ao seu potencial impacto ambiental. Al?m disso, os mecanismos de forma??o cont?m os principais reservat?rios de hidrocarbonetos. Grupos de pesquisas t?m realizado simula??es desses fen?menos, em modelos reduzidos, utilizando o carv?o 205 como sedimento. Por?m, esse material apresenta limita??es quanto ao seu uso em t?cnicas de imageamento n?o invasivo para acompanhamento das correntes de turbidez em tanques de simula??o hidr?ulica. Assim, essa pesquisa teve como objetivo preparar material polim?rico com o potencial de substituir o carv?o 205 nessas simula??es. Foram preparados nanocomp?sitos baseados em matrizes termorfixas contendo carga inorg?nica (argila, grafite e negro de fumo). Por meio de micrografias de microscopia eletr?nica de varredura (MEV) e microscopia eletr?nica de transmiss?o (MET) foi poss?vel verificar que as cargas incorporadas ?s matrizes polim?ricas apresentavam dimens?es nanom?tricas e estavam dispersas homogeneamente, exceto o negro de fumo que apresentou alguns pontos de aglomera??o. Tamb?m por MEV foram avaliadas as formas das part?culas, as quais foram classificadas como semi-angulares e semi-arredondadas. As propriedades el?tricas foram investigadas por meio de espectroscopia por imped?ncia el?trica. Os materiais avaliados apresentaram velocidades de queda e massa espec?fica pr?ximas as do carv?o 205. Assim, todos os nanocomp?sitos preparados apresentaram caracter?sticas desejadas para substituir o carv?o 205 em tanques de simula??o hidr?ulica.

Made available in DSpace on 2015-04-14T13:59:02Z (GMT). No. of bitstreams: 1 452931.pdf: 3193003 bytes, checksum: 17279c114312e7c4576c7e96d9be1750 (MD5) Previous issue date: 2013-03-27 / Thermoplastic elastomers, like triblock copolymers, more specifically SBS with linear arrangement, were used to obtain polymeric nanocomposites. Employing spherical TiO2 nanofiller and nanofiller clay with lamellar structure, through mixing method, based on solvent followed by dispersion into mechanical stirring and ultrasound batch, which nanofiller were incorporated in quantities of 0,5%, 1%, 2% and 3% relative to the polymeric matrix mass. The characterization was done using thermal mechanical analytical methods like thermal gravimetric analysis (TGA) and dynamic mechanical thermal analysis (DMTA). The monitoring of the morphological structure of nanocomposite and nanofiller was performed by scanning electron microscopy. The results indicate the availability of the proposed technique for incorporation of nanofillers into the matrix and highlight the requirement for surface treatments for improved performance. The use of nanofillers with distinct characteristics can be used for directing the studies of the relation with charge and polymeric matrix and evaluation of properties in charge-matrix interface. / Elast?meros termopl?sticos do tipo copol?meros tribloco, especificamente neste trabalho copol?meros SBS de arranjo linear foram utilizados para a obten??o de nanocomp?sitos. Empregou-se a utiliza??o de nanocargas esf?ricas de TiO2, e nanocargas de argila, com estrutura lamelar, atrav?s de m?todo de mistura em base solvente seguido por dispers?o em agita??o mec?nica e banho de ultrassom, onde foram incorporadas as nanocargas nas quantidades de 0,5%, 1%, 2% e 3%, em rela??o ? massa da matriz polim?rica. A caracteriza??o foi realizada por m?todos anal?ticos t?rmico-mec?nicos, como TGA, e DMTA, e o acompanhamento da estrutura morfol?gica do nanocomp?sito e da nanocarga utilizada foi feito por micrografias atrav?s de microscopia eletr?nica de varredura (MEV). Os resultados obtidos indicam a viabilidade da t?cnica proposta para incorpora??o de nanocargas na matriz e evidenciam a necessidade de tratamentos superficiais para melhorias no desempenho. A utiliza??o de nanocargas com caracter?sticas morfol?gicas distintas serve como par?metro para o direcionamento de estudos sobre a rela??o carga-matriz polim?rica e avalia??o de propriedades na interface carga-matriz.

Made available in DSpace on 2015-04-14T13:59:09Z (GMT). No. of bitstreams: 1 460217.pdf: 1794171 bytes, checksum: 9f89fb6e90ac2a056b535eb35119531e (MD5) Previous issue date: 2014-08-01 / The growth of the polymer market leads to new application niches for these materials with present different properties when compared to the conventional ones, such as composites and nanocomposites, making key the search and the development of these products. Polyurethanes (PUs) are among the most versatile polymers in the world today. To improve the performance of a polyurethane, a common method is to incorporate fillers into the polymer, such as inorganic particles. Thus, this work proposes a study of obtaining and comparing PU nanocomposites by in situ polymerization using natural inorganic filler such as talc and synthetic talc (Ni-talc). The quantities defined Ni-talc were 0.5%, 1%, 2%, 3% and 5% on the mass of polyurethane formed during the polymerization reaction. To follow the results of the technical Infrared Spectroscopy were used Fourier transform (FTIR), differential scanning calorimetry (DSC), Thermogravimetric Analysis (TGA), Gel Permeation Chromatography (GPC), dynamic mechanical analysis (DMTA), Microscopy Scanning Electron (SEM), Analysis of X-Ray Diffraction (XRD) and Analysis of Specific Surface Area (BET). The XRD results showed that intercalation of polymer matrix in the nanocomposites structure. The Ni-talc exhibited better thermal properties when compared to natural talc. The nanocomposites with 0.5, 1 and 2% Ni-talc showed the best strain results in low deformation volues in relation to the pure PU, while the stress-strain results from natural talc nanocomposite shows higher strain values at higher deformation. / O crescimento do mercado de pol?meros surge como novos nichos de aplica??o para materiais com propriedades diferentes das existentes, tais como os comp?sitos e nanocomp?sitos, tornando fundamental a busca e o desenvolvimento destes produtos. Os poliuretanos (PU s) est?o dentre os pol?meros mais vers?teis no mundo atual. Para melhorar ainda mais o desempenho de um poliuretano, um m?todo comum ? a incorpora??o de cargas ao pol?mero, como as part?culas inorg?nicas. Desta maneira, este trabalho prop?e um estudo de obten??o e de compara??o de nanocomp?sitos de PU por polimeriza??o in situ, usando como carga inorg?nica talco natural e talco sint?tico (Ni-talco). As quantidades, definidas de Ni-talco, foram 0,5%, 1%, 2%, 3% e 5% em rela??o ? massa de poliuretano formada durante a rea??o de polimeriza??o. Na caracteriza??o dos resultados foram utilizadas as t?cnicas de Espectroscopia de Infravermelho por Transformada de Fourier (FTIR), Calorimetria Explorat?ria Diferencial (DSC), An?lise Termogravim?trica (TGA), Cromatografia de Permea??o em Gel (GPC), An?lise Din?mico Mec?nica (DMTA), Microscopia Eletr?nica de Varredura (MEV), An?lise de Difra??o de Raios-X (DRX) e An?lise da ?rea Superficial Espec?fica (BET). As an?lises de DRX mostraram que h? forma??o de uma estrutura intercalada entre a matriz polim?rica e as nanoparticulas. O Ni-talco mostrou melhores propriedades t?rmicas quando comparado com o talco natural. Os nanocomp?sitos com 0,5, 1 e 2% de Ni-talco mostraram os melhores resultados de tens?o em baixas deforma??es que o PU puro, enquanto que os resultados de tens?o-deforma??o do nanocomp?sito de talco natural mostraram valores de tens?o superiores em deforma??es mais elevadas.

Made available in DSpace on 2015-04-14T13:59:09Z (GMT). No. of bitstreams: 1 459626.pdf: 120396 bytes, checksum: a65ae75d299912b9f56c5f620ace594e (MD5) Previous issue date: 2014-03-28 / This research is related to the investigation of new approaches for noninvasive imaging that allow registering the internal architecture of sedimentary deposits generated in hydraulic simulation tanks. The simulations are conducted to better understand the behavior of turbiditic currents, one of the principal process responsible for the deposition of sediments in deep oceanic waters. For this reason it is purpose of this work the preparation of polymer nanocomposite with inorganic filler for non-destructive testing, with properties and characteristics similar to Coal 205, material currently used in these simulations. The prepared composites presented specific weight and settling velocity speed values similar to Coal 205 and it was observed that the incorporation of the filler and the different dyes did not affected significantly the desired characteristics. / Este trabalho de pesquisa est? relacionado com a investiga??o de novas abordagens de imageamento n?o-invasivo que permitam registrar a arquitetura interna de dep?sitos sedimentares gerados em tanques de simula??o hidr?ulica. Estas simula??es s?o realizadas para melhor compreens?o do comportamento das correntes de densidade, que constituem uma das principais respons?veis pela deposi??o de sedimentos em ?guas oce?nicas profundas. Para isto foi proposta deste trabalho o preparo de comp?sito polim?rico com carga inorg?nica para ensaios n?o destrutivos, com as propriedades e caracter?sticas semelhantes ao Carv?o 205, material atualmente utilizado nas simula??es. Os comp?sitos preparados apresentaram valores de peso espec?fico e velocidade de queda compar?veis com os do Carv?o 205 e observou-se que a incorpora??o de corante e carga n?o influencia significativamente as caracter?sticas desejadas. Desta forma, os comp?sitos preparados se mostram com potencial para uso nas simula??es de correntes de densidade n?o conservativas.

Made available in DSpace on 2015-04-14T13:59:14Z (GMT). No. of bitstreams: 1 466225.pdf: 8821107 bytes, checksum: 29eac7664f9d5e8636f822b7baf681b7 (MD5) Previous issue date: 2015-03-04 / In this work, molecular dynamics (MD) simulations were carried out to study the ion-irradiation induced effects on ultrathin molecular films. The energy deposited by the ions is computationally simulated using a simple thermal spike with particles interacting via the Lennard-Jones potential. It was investigated the effect of thin and ultrathin (2 60 nm) films thickness variation in the dimensions of the defects created on the surface crater s diameter (Dc) and depth (Cd) and ridge (rim) volume. Crystalline and amorphous systems were modeled, and different radius and temperature combinations were investigated for the simulated cylindrical track. Qualitative and quantitative results obtained from crystalline and amorphous samples were compared. The analysis of the system s dynamics after the track energy got transferred into atomic motion allowed to identify the mechanisms responsible for the formation of the surface defects. Crater size is mostly determined by evaporation and melt flow from the hot track, while the rim size is determined both by melt flow and coherent displacement of particles due to the large pressure developed in the excited track. We find a large dependence on the dimensions of the surface defects, and in the number of sputtered particles, with the film thickness (h) below a critical value hcr?tico. The critical thickness for the rim volume, more sensitive to the confinement of the film, was found to be higher than the hcr?tico for Dc, since mechanisms involved in the formation of both effects are different. Also from a critical h on, the sputtering yield got smaller as the film thickness decreased. The sputtered particles depth of origin zorigem was obtained as a function of h. As a result from simulations with amorphous films it was obtained zorigem<h/2. Results from simulations were compared to recent experimental data. / Neste trabalho, simula??es por din?mica molecular (MD) foram empregadas para estudar efeitos induzidos pela irradia??o i?nica de alta energia em filmes moleculares ultrafinos. A energia depositada pelos ?ons ? computacionalmente simulada usando um modelo simples de thermal spike com part?culas interagindo pelo potencial de Lennard-Jones. Foi investigado o efeito da varia??o da espessura de filmes ultrafinos (2 60 nm) nas dimens?es dos defeitos criados na superf?cie - di?metro (Dc) e profundidade (Cd) da cratera e volume da protuber?ncia (rim). Foram modelados sistemas cristalino e amorfo, e investigadas diferentes combina??es de raio e temperatura da trilha de excita??o gerada pelos ?ons. Os resultados qualitativos e quantitativos obtidos usando os s?lidos cristalino e o amorfo foram comparados. A an?lise da din?mica do sistema ap?s a energia da trilha i?nica ser transferida para movimento at?mico permitiu identificar os mecanismos respons?veis pela forma??o dos defeitos de superf?cie. O tamanho da cratera ? determinado principalmente pela eje??o de material e pelo fluxo de material fundido da trilha superaquecida, enquanto o rim tem origem tanto no fluxo de material derretido quanto no deslocamento coerente de um pulso de press?o oriundo do centro da trilha excitada. Foi encontrada uma forte depend?ncia entre as dimens?es dos defeitos de superf?cie, e no n?mero de part?culas ejetadas (sputtering), quando a espessura do filme (h) ? menor que um valor cr?tico hcr?tico. A espessura cr?tica para o volume do rim, mais sens?vel ao confinamento do filme, foi maior que para o Dc, devido aos diferentes mecanismos envolvidos. O sputtering foi cada vez menor com a redu??o de h a partir tamb?m de um valor cr?tico de h. Tamb?m foram obtidas a profundidade de origem zorigem das part?culas ejetadas, e o sputtering em fun??o de h. Para os filmes amorfos se obteve zorigem<h/2. Resultados das simula??es foram comparados com dados experimentais recentes. Os melhores resultados das simula??es obtiveram ?tima correla??o qualitativa para Dc e para o volume do rim.

Made available in DSpace on 2015-04-14T13:59:18Z (GMT). No. of bitstreams: 1 396270.pdf: 2684268 bytes, checksum: 3af158eac27cc24bbc459e3435a85cf7 (MD5) Previous issue date: 2007-03-27 / O presente trabalho est? relacionado com a s?ntese de ligantes org?nicos bipirid?nicos e bitiof?nicos e a posterior coordena??o desses ligantes a sais de metais de transi??o, formando pol?meros de coordena??o ou pol?meros em rede. Os pol?meros de coordena??o s?o formados por estruturas org?nicas diferentemente substitu?das coordenadas a metais de transi??o, repetindo-se continuamente. S?o compostos de grande interesse devido aos aspectos relacionados com o formato das estruturas em rede, apresentando algumas propriedades tais como, magnetismo, condutividade ou luminesc?ncia. Os ligantes org?nicos foram obtidos a partir da condensa??o de aminas arom?ticas e alif?ticas, como a 1,2-fenilenodiamina ou 1,2-etilenodiamina, com piridinas e tiofenos diferentemente substitu?dos, em presen?a de ?cido f?rmico, formando os diferentes ligantes org?nicos, chamados tamb?m de espa?adores. Esses ligantes foram posteriormente coordenados a sais de cobalto, n?quel e pal?dio, em um sistema bif?sico THF / Etanol, visando ? s?ntese dos pol?meros de coordena??o. A caracteriza??o dos ligantes foi feita por espectroscopia no infravermelho, espectroscopia de resson?ncia magn?tica nuclear de 1H e 13C e difra??o de raios-X de monocristais. A an?lise morfol?gica dos pol?meros sintetizados foi realizada por microscopia eletr?nica de varredura, MEV, mostrando a presen?a de compostos com estruturas lamelares extremamente ordenadas, al?m da comprova??o da presen?a dos metais n?quel, cobalto e pal?dio.

Submitted by PPG Engenharia e Tecnologia de Materiais (engenharia.pg.materiais@pucrs.br) on 2018-06-25T13:24:34Z No. of bitstreams: 1 Dissserta??o final_Lucas Weber Dias.pdf: 2263503 bytes, checksum: ea9c29b6b538c56ea795610f7bc5a808 (MD5) / Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2018-06-29T13:30:33Z (GMT) No. of bitstreams: 1 Dissserta??o final_Lucas Weber Dias.pdf: 2263503 bytes, checksum: ea9c29b6b538c56ea795610f7bc5a808 (MD5) / Made available in DSpace on 2018-06-29T13:38:08Z (GMT). No. of bitstreams: 1 Dissserta??o final_Lucas Weber Dias.pdf: 2263503 bytes, checksum: ea9c29b6b538c56ea795610f7bc5a808 (MD5) Previous issue date: 2017-08-29 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / The main function of the packaging is to protect the cosmetic from the external environment, avoiding undesirable changes in the product that is contained inside, and thus indispensable for its storage and transpotation. However, its disposal improperly generates a large volume of solid waste, which is directly related to the environmental impact. One of the alternatives to minimize this impact is the use of packages made from biodegradable polymeric films based on polyacrylic acid (PLA), poly (lactic acid ? co- glycolic acid) (PLGA) and polycaprolactone (PCL), blends of theses polymers and incorporation of Zeolites 13x. The thermal, mechanical optical, water vapor barrier and degradation time in saline solution of polymeric systems are evaluated for application as cosmetic packaging. The technique used for the preparation of the polymer films was that of Solvent Casting. The polymer films were characterized by the techniques of UV-Vis Spectrophotometry, Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA), Scsannig Electron Microscopy (SEM), transparency, water vapor permeability, mechanical assay and absorption spectroscopy atomic. The transmittance results showed that the PCL and PLA blends showed greater blockage to the passage of radiation (190 - 1100nm) and water vapor permeability. The incorporation of PLA or PLGA to the pure PCL resulted in material with batter thermal properties, but more rigid and brittle, not modifying the degradation process until 120 days of incubation. The incorporation of 15% Zeolite 13x into the PCL/PLA blends did not significantly modify the properties evaluated. / As embalagens t?m como principal fun??o, proteger o cosm?tico do meio externo, evitando que ocorram altera??es indesej?veis no produto que est? contido no seu interior, sendo assim indispens?vel para o seu armazenamento e transporte. Por?m, o seu descarte de forma inadequada gera um grande volume de res?duos s?lidos, que est? diretamente relacionado com o impacto ambiental. Uma das alternativas para minimizar este impacto ? a utiliza??o de embalagens confeccionadas a partir de pol?meros biodegrad?veis. Desta maneira, o presente trabalho tem como objetivo a prepara??o e caracteriza??o de filmes polim?ricos biodegrad?veis baseados em Poli ? ?cido l?ctico (PLA), Poli (?cido l?ctico ? co- ?cido glic?lico) (PLGA) e Policaprolactona (PCL), blendas destes pol?meros e incorpora??o de Ze?litas 13x. S?o avaliadas as propriedades t?rmicas, mec?nicas, ?pticas, de barreira a vapor de ?gua e o tempo de degrada??o em solu??o salina dos sistemas polim?ricos, visando aplica??o como embalagem para cosm?ticos. A t?cnica utilizada para a prepara??o dos filmes polim?ricos foi a de Solvent Casting. Os filmes polim?ricos foram caracterizados pelas t?cnicas de Espectrofotometria UV-Vis, Calorimetria Explorat?ria Diferencial (DSC), An?lise Termogravim?trica (TGA), Microscopia Eletr?nica de Varredura (MEV-FEG), transpar?ncia, permeabilidade a vapor de ?gua, ensaio mec?nico e Espectroscopia de absor??o at?mica. Os resultados de transmit?ncia mostraram que a blenda de PCL e PLA apresentou maior bloqueio ? passagem de radia??o (190 nm ? 1100 nm) e ? permeabilidade de vapor de ?gua. A incorpora??o de PLA ou PLGA ao PCL puro resultou num material com melhores propriedades t?rmicas, por?m mais r?gido e quebradi?o, n?o modificando o processo de degrada??o at? 120 dias de incuba??o. A incorpora??o de 15% Ze?lita 13x ? blenda de PCL/PLA n?o modificou significativamente as propriedades avaliadas.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2015-07-07T13:31:06Z No. of bitstreams: 1 471664 - Texto Completo.pdf: 1025603 bytes, checksum: cc2bf12cfe7084c63f710f9fd2c36364 (MD5) / Made available in DSpace on 2015-07-07T13:31:06Z (GMT). No. of bitstreams: 1 471664 - Texto Completo.pdf: 1025603 bytes, checksum: cc2bf12cfe7084c63f710f9fd2c36364 (MD5) Previous issue date: 2015-03-25 / The repair of injured peripheral nerves is one of the most difficult tasks in neurosurgery. Among the techniques used is distinguished using the artificial tube for nerve guidance during the regeneration process. The preparation of composites based on biodegradable polymers and conducting polymers related to growth factors, have been proposed as a promising approach for improving regeneration of injured peripheral nerves. However, it should be considered that during the regeneration process is necessary to have a control over the dosage and the time of release of the drug in question not to jeopardize the recovery process.In this work were based membranes prepared PLGA (lactic-co-glycolic poly-acid), polypyrrole (PPy) and Tacrolimus as a growth factor. Was reported as a factor of the process of degradation and the relationship between the composition of membrane PLGA / PPy / Tacrolimus with the release of the drug in the first days of incubation. It was found that membranes with higher PLGA thicker, resulting in a lower weight loss and delayed release of Tacrolimus. In this work PLGA membranes containing search polypyrrole nanofibers (PPy) and Tacrolimus, as a growth factor, were prepared by the solvent evaporation method. The process of degradation and drug release were assessed 28 days of incubation. It was observed that membranes with a higher concentration of PLGA. / A repara??o de nervos perif?ricos lesionados ? uma das tarefas mais dif?ceis na neurocirurgia. Entre as t?cnicas utilizadas destaca-se a utiliza??o de tubos artificiais para orientar o nervo durante o processo de regenera??o. A prepara??o de comp?sitos baseados em pol?meros biodegrad?veis e pol?meros condutores, associados a fatores de crescimento, t?m sido proposta como uma abordagem promissora para melhorar a regenera??o de nervos perif?ricos lesionados. Por?m, deve ser considerado que durante o processo de regenera??o ? necess?rio ter um controle sobre a dosagem e o tempo de libera??o do f?rmaco em quest?o para n?o prejudicar o processo de recupera??o.Assim, neste trabalho foram preparadas membranas baseadas em PLGA (poli-?cido l?ctico-co-glic?lico), polipirrol (PPy) e Tacrolimus como fator de crescimento. Foi avaliado o processo de degrada??o e a rela??o entre a composi??o de membranas de PLGA/PPy/Tacrolimus com a libera??o do f?rmaco nos primeiros dias de incuba??o. Foi verificado que membrana com maior quantidade de PLGA, mais espessa, resultou numa menor perda massa e retardou a libera??o do tacrolimus. Neste trabalho de pesquisa membranas de PLGA contendo nanofibras de polipirrol (PPy) e Tacrolimus, como fator de crescimento, foram preparadas por meio da metodologia da evapora??o do solvente. O processo de degrada??o e a libera??o do f?rmaco foram avaliados durante 28 dias de incuba??o. Foi observado que membranas com uma maior concentra??o do PLGA.

Submitted by Sara Ribeiro (sara.ribeiro@ucb.br) on 2017-11-08T13:12:56Z No. of bitstreams: 1 AmandaCarolineMarquesSa??deTese2016.pdf: 1482640 bytes, checksum: 98c7088a3903d189fcf2c6a44b4fcdc7 (MD5) / Approved for entry into archive by Sara Ribeiro (sara.ribeiro@ucb.br) on 2017-11-09T11:04:49Z (GMT) No. of bitstreams: 1 AmandaCarolineMarquesSa??deTese2016.pdf: 1482640 bytes, checksum: 98c7088a3903d189fcf2c6a44b4fcdc7 (MD5) / Made available in DSpace on 2017-11-09T11:04:49Z (GMT). No. of bitstreams: 1 AmandaCarolineMarquesSa??deTese2016.pdf: 1482640 bytes, checksum: 98c7088a3903d189fcf2c6a44b4fcdc7 (MD5) Previous issue date: 2016-11-01 / Bacteria are becoming resistant to a growing number of conventional antibiotics at a worrisome rate. Therefore, there is an increasing demand for new antimicrobial therapeutics. Antimicrobial peptides (AMPs) are one of promising alternatives for conventional antibiotics and are thought to be less likely to induce resistance. AMPs have been coupled to molecular scaffolds for biomedical applications such as hydrogels for wound dressings and covering implants. Here AMPs were chemically conjugated to the CR4 hydrophilic polymers. The CPF_C1 is a short peptide isolated from Xenopus clivii, the original sequence was modified one called LCPF_C1, aiming to create some distance between the first glycine and the azide added on the N terminus (on the coupled sequence). The conjugation between the AMP and the CR4 polymer used a click chemistry reaction with two steps, dependent of a hetero crosslinker (DBCO???PEG4???NHS Ester). Dynamic light scattering (DLS) and fluorimeter assays were used to evaluate the efficiency of coupling. MALDI-ToF analysis showed 3 molecules of LCPF_C1 peptide for each CR4 polymer. Moreover, microrheology showed changes on hybrids increasing the viscosity. Finally, the compounds were evaluate against four different bacteria: Staphylococcus aureus, Klebsiela pneumoneae carbapenemases (Kpc), Escherichia coli and Pseudomonas aeruginosa. It was possible to observe MIC???s against P. aeruginosa of 11 mM by using the peptide (LCPF_C1) and 55 mM for the original sequence. When the hibrids were compared to the free polymer was not found MIC values against K. pneumoneae (CR-Kp). On the other hand, the hibrids showed three times less activity than the free polymer against P. aeruginosa. No MIC values were found aganst S. aureus. Finally, against E. coli was observed a MIC value of 1000 mM for the free CR4 and 250 mM for the hibrids. On this way, the present work showed the possibility to functionalize biopolymers by using bioactive molecules coupled to biopolimers, changing the physical-chemical characteristics and increasing they applicability against bacterial infections. / Uma taxa alarmante de bact??rias tem se tornado resistente a um grande n??mero de antimicrobianos convencionais. Desta forma, a demanda por novas terapias antimicrobianas tem aumentado proporcionalmente. Assim, o uso de pept??deos antimicrobianos (PAMs) consistem em uma promissora alternativa para antibacterianos convencionais, particularmente podendo ser acoplado a estruturas moleculares para aplica????es biom??dicas, como hidrog??is para curativos e cobertura de implantes. No presente trabalho, PAMs foram quimicamente conjugados ao pol??mero hidrof??lico inspirado nas prote??nas naturais col??geno e seda CR4. O pept??deo CPF_C1 consiste em um pept??deo contendo 17 res??duos de amino??cidos isolado de Xenopus clivii, com atividade comparada ?? bact??rias Gram-negativas e -positivas. Para este estudo, a sequ??ncia original do CPF-C1 foi modificada e intitulada LCPF_C1, objetivando aumentar a dist??ncia entre a primeira glicina e a azida adicionada na por????o N-terminal. A conjuga????o entre o PAM e o pol??mero CR4 foi realizada por meio de click chemistry reaction em dois passos, dependentes do hetero crosslinker (DBCO???PEG4???NHS Ester). Ensaios de espalhamento de luz din??mico (DLS) e fluorimetria foram utilizados para avaliar a efici??ncia de acoplamento e demonstraram a presen??a do pept??deo acoplado ao pol??mero. An??lises de MALDI-ToF demonstraram 3 mol??culas do pept??deo LCPF-C1 para cada mol??cula do pol??mero CR4. Al??m disso, dados de microrreologia demonstraram mudan??as nos h??bridos como aumento de viscosidade. Finalmente, os compostos foram avaliados contra quatro bact??rias diferentes: Staphylococcus aureus, K. pneumoneae carbapenemase (Kpc), Escherichia coli e Pseudomonas aeruginosa. Foi poss??vel observar para P. aeruginosa MICs de 11 mM utilizando o pept??deo (LCPF_C1) e 55 mM para a sequ??ncia original. Quando comparados aos h??bridos em rela????o a atividade do pol??mero livre n??o foi encontrado valor de MIC contra K. pneumoneae (CR-Kp). Por outro lado, os h??bridos demonstraram um MIC cerca de tr??s vezes menor que o pol??mero livre contra P. aeruginosa. Nenhum valor de MIC foi encontrado contra S. aureus. Finalmente, contra E. coli observou-se MIC de 1000 mM para o pol??mero CR4 e 250 mM para os h??bridos. Desta forma o presente trabalho demonstrou a possibilidade de funcionalizar biopol??meros por meio do acoplamento de mol??culas bioativas, alterando suas caracter??sticas f??sico-qu??micas e aumentando sua aplicabilidade contra infec????es bacterianas.