Introduction: The aim of this study was to evaluate some of the physico-chemical properties of a new root canal sealer. Methodology: The sealers tested were Sealer Plus (MKLife, Porto Alegre, Rio Grande do Sul, Brazil), compared as AH Plus (Dentsply, DeTrey GmbH, Konstanz, Alemanha). For the radiopacity, flow, solubility and fabrication of test specimens relative to setting times the ANSI/ADA No. 57 (2000) and ISO 6876 (2012) specifications were followed. To measure the initial and final setting times the ASTM C266/2008 standard was used. pH was evaluated in the time intervals of 3, 24, 72 and 168 hours). Statistical tests were applied to the results obtained at a level of significance of 5%. Results: The results demonstrated that the Sealer Plus sealer showed a lower radiopacity value than AH Plus sealer (p<0.05), however, this was higher than the minimum value recommended by the specifications; that is 3 mm Al. Relative to flow, the value for Sealer Plus was 19.19 mm and for AH Plus, 19.81 mm (p>0.05). Sealer plus presented initial and final setting times of 138 min. and 210 min., respectively, while the values for AH Plus were 437 min. and 849 min., respectively, (p<0.05). Relative to solubility, Sealer Plus presented 0.21% and AH Plus, 0.27% (p>0.05). None of the sealers showed a significant increase in pH (p>0.05). Conclusion: Sealer Plus sealer presented physico-chemical properties in accordance with ANSI/ADA (2000) No.57 and ISO 6876 (2012) specifications. / Introdução: Este estudo objetivou avaliar algumas propriedades físico-químicas de um novo cimento obturador de canais radiculares. Metodologia: Para os testes de radiopacidade, escoamento, solubilidade e confecção dos corpos de prova para os tempos de presa foram seguidas as especificações nº57 da ANSI/ADA (2000) e ISO 6876 (2012). Para a medição dos tempos de presa, inicial e final, foi empregada a norma ASTM C266/2008. O pH foi avaliado nos períodos de 3, 24, 72 e 168 horas. Sobre os resultados foram aplicados testes estatísticos com nível de significância de 5%. Resultados: Os resultados demonstraram que o cimento Sealer Plus apresentou menor radiopacidade do que o cimento AH Plus (p<0.05), porém, superior ao mínimo recomendado pelas especificações, ou seja, de 3 mm de Al. Com relação ao escoamento, o do Sealer Plus foi 19,19 mm e do AH Plus 19,81 mm (p>0.05). O Sealer Plus apresentou tempos de presa inicial e final de 138 min. e 210 min., respectivamente, enquanto o AH Plus, 437 min. e 849 min., respectivamente, (p<0.05). Em relação à solubilidade, o Sealer Plus apresentou 0,21% e o AH Plus 0,27% (p>0.05). Nenhum dos cimentos apresentou aumento significativo do pH (p>0.05). Conclusão: O cimento Sealer Plus apresentou propriedades físico-químicas de acordo com as especificações nº 57 da ANSI/ADA (2000) e ISO 6876 (2012).

Introduction. At low temperature the preservation of foodstuffs is one of the best ways of their storage and therefore this method is widely used in meat industry. The low temperature suppresses the activity of microorganisms and tissue ferments. Therefore the meat preserved by freezing keeps for a long time its initial properties and there are only minimal changes of food value and taste. At low temperature the activity of ferments slows down but does not stop. Work object. The work object is the determination of the change of physical-chemical properties of meat during freezing and keeping in - 180 C and - 860 C temperature. Work methodics. The research as fulfilled at the laboratory of the evaluation of the cattle meat properties and the meat quality. For the rersearch taken 14 Lithuanian white pig meat samples the mean weight of which was 500 g. were taken. They were put into special freezing bags and were frozen at temperature -180 C, and -860 C. Before freezing it the physical-chemical properties of the meat were determined. Two examples from each meat samples were researched. The determination of the physical-chemical properties of the meat was fulfilled every month. Also were was taken 6 Lithuanian white pig meat samples the mean weight of which was 500 g. Before freezing it the physical-chemical properties of the meat were determined. After that was made green tea extract, 500 ml. Water ant 50 g tea. All extract was inject in to the meat samples. They were put... [to full text]

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-08-05Bitstream added on 2014-06-13T18:51:43Z : No. of bitstreams: 1 caldas_mrgr_me_arafo.pdf: 492580 bytes, checksum: 6bbf6b8719f88e58ede102ebb27a6c6c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho, dividido em dois estudos, foi avaliar: (1) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre o grau de conversão e dureza de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT); e (2) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre a resistência à compressão de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT). No primeiro estudo, para os testes de grau de conversão (GC) e dureza, cinco corpos-de-prova com 4 mm de diâmetro e 2 mm de espessura (ISO 4049), foram confeccionados para cada grupo avaliado. O grau de conversão foi analisado pelo Espectrofotômetro Nexus - 470 FT-IR. Para o teste de dureza Vickers, os corpos-de-prova foram levados ao Durômetro Micromet 2100 (Buehler, EUA) onde foi utilizada uma carga de 50 gramas força (gf) e tempo de 30 segundos. Para cada corpo-de-prova oito medidas foram realizadas nas superfícies de topo e base. Os dados obtidos para o GC e dureza foram analisados estatisticamente pelo teste de Análise de Variância (ANOVA) e Tukey. No segundo estudo, para o teste de resistência à compressão foram confeccionados oito corpos-de-prova com 8 mm de altura e 4 mm de diâmetro. O teste foi realizado na máquina de ensaio universal EMIC com célula de carga de 5 kN à velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente pelo teste ANOVA e o teste Tamhane. Os resultados demonstraram que o GC e dureza foram influenciados pelas ponteiras, sendo a dureza também influenciada pelo tipo de resina composta utilizada. A resina composta microhíbrida fotoativada com a ponteira de fibra óptica apresentou maiores valores do GC e dureza... / The aim of this work, divided into two studies, was evaluate: (1) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the degree of conversion and hardness one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins; and (2) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the compressive strength of one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins. In the first study, to test the degree of conversion (GC) and hardness, five samples 4 mm in diameter and 2 mm in thickness (ISO 4049) were made for each group evaluated. The degree of conversion was evaluated by Fourier transform infrared spectroscopy (FT-IR). For the Vickers hardness test, the samples were brought to the durometer Micromet 2100 (Buehler, USA) where was used a load of 50 gram force (gf) and time of 30 seconds. For each sample test measurements were performed eigth measures on the surfaces of top and bottom. The data obtained for the GC and hardness test were statistically analyzed by Analysis of Variance (ANOVA) and Tukey’s test. In the second study to test the compressive strength eight samples (4 mm in diameter and 8 mm in thickness) were made for each group evaluated, and the test was conducted in a universal testing machine EMIC with load cell 5 kN and speed of 0,5 mm/min. The data were statistically analyzed by ANOVA test and Tamhane’s test. The results showed that the GC and hardness were influenced by the light guide tip, and the hardness also influenced by the type of resin used. The microhybrid composite resin photo-activated with the fiber optic light tip had higher values of GC and hardness. The lowest values of GC and hardness were observed with nanofilled composite resin photoactivated... (Complete abstract click electronic access below)

Submitted by Katiane Souza (katyane.souza@gmail.com) on 2016-03-18T14:28:21Z No. of bitstreams: 1 arquivototal.pdf: 1675528 bytes, checksum: 5e143d476010233aba62144feb3256f7 (MD5) / Made available in DSpace on 2016-03-18T14:28:21Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 1675528 bytes, checksum: 5e143d476010233aba62144feb3256f7 (MD5) Previous issue date: 2012-05-17 / The difficulty of implementing no tillage in the Northeast region of Brazil occurs due to low rainfall, which limits the plant growth and high rates of decomposition. In the Brejo Paraibano microregion, beyond this aspect, another problem is related to changes in the use of soil, without considering their potentialities and limitations, which provided serious damage to conservation. In order to select cover crops for no tillage and understand the soil degradation due to changes in use, was implanted two experiments completely randomized. The experiment of cultural residues was conducted in the Chã of Jardim farm, of Center of Agrarian Sciences of UFPB, and the treatments consisted of three residues of grass species (Brachiaria decumbens), corn (Zea mays) and sorghum (Sorghum bicolor) and three legumes species: pigeon pea (Canavalia ensiformis), guandu (Cajanus cajan) and leucena (Leucaena leucocephala). The residues were placed in litter bags and placed in the experimental field under the litter, in the presence and absence of nitrogen. The experiment about use of soil was conduced in three systems: native secondary forest, cultivation of sabiá (Mimosa caesalpiniaefolia) and pasture (Brachiaria decumbens). In each area, soil samples were collected at four depths for physical and chemical analisys, fractionation of organic matter and root density. The physical analisys consisted of the separation of aggregates size, grain size, density and total porosity of soil. The chemical ones consisted of determining the pH and concentration of calcium, magnesium, phosphorus, potassium, sodium, aluminum and C. The organic matter was fractionated into fulvic acid fraction (FAF), humic acid fraction (HAF) and humin (HUM). They were quantified deposition and accumulation of litter and its rate of decomposition in areas of woodland and thrush. In the pasture, one evaluated the production of forage. In the case of crop residues, it was observed that the rate of decomposition of the grass is slower than that of legumes, however, this rate is equivalent in the last months of the evaluated year. The grasses showed no differences, but the guandu showed slower rate of decomposition amongst the legumes. Nitrogen fertilization did not affect the waste decomposition rate. In the case of the changes in the use of the soil, the amount of clay, DMPAs, DMPAu and the relationship DMPAu / DMPAs and porosity showed higher values in the area under forest. The soil density was lower in the area under forest. The development of roots was higher in areas under forest and pasture. The waste disposal was greater in the area under sabiá and the N, P and K were higher in these residues, which shows the sabiá capacity in nutrient cycling. The accumulation of litter in the soil was higher in the area under forest. The decomposition rate of the waste was 48% in area under sabiá and 40% in that one under forest. The percentage of C, H + Al, Al, and CTC potential and aluminum saturation (m) are higher in the soil in the area under forest. The soil pH, the base saturation (V) and the concentrations of Na and K are similar in areas under pasture and under sabiá and larger than that under forest. The percentages of Ca, Mg and available P and SB and effective CTC did not differ among the studied areas. The C of the soil is best preserved in the area under forest in function of higher levels in HAF and HUM fractions and the lowest ratio EA / HUM. In turn, the replacement from the grass for sabiá begins to recover the levels of C lost in the area under pasture, with intermediate fraction values of HAF and HUM, demonstrating the sabiá ability to recover soil quality. / A dificuldade de implantar a semeadura direta na região Nordeste do Brasil ocorre devido às baixas precipitações pluviais, que limita o crescimento vegetal e as elevadas taxas de decomposição de resíduos. Na microrregião do Brejo Paraibano, além desse aspecto, outra preocupação é a mudança no uso do solo, sem considerar as suas potencialidades e limitações, o que tem proporcionado graves prejuízos à sua conservação. Com objetivo de selecionar plantas de cobertura para a semeadura direta e entender a degradação do solo devido às mudanças de uso, foram implantados dois experimentos em delineamento inteiramente casualizado. O experimento de resíduos culturais foi conduzido na Fazenda experimental Chã do Jardim, do Centro de Ciências Agrárias da UFPB, e os tratamentos constaram de três resíduos de gramíneas: braquiária (Brachiaria decumbens), milho (Zea mays) e sorgo (Sorghum bicolor) e três de leguminosas: feijão de porco (Canavalia ensiformis), guandu (Cajanus cajan) e leucena (Leucaena leucocephala). Os resíduos foram colocados em sacolas náilon e dispostas no campo sob a serrapilheira, na presença e ausência de adubação nitrogenada. O experimento sobre uso do solo foi conduzido em três sistemas: mata nativa secundária, cultivo de sabiá (Mimosa caesalpiniaefolia) e pastagem de braquiária (Brachiaria decumbens). Em cada área foram coletadas amostras de solo, em quatro profundidades para análises físicas, químicas, fracionamento da matéria orgânica e densidade de raízes. As análises físicas constaram de separação de tamanhos de agregados, granulometria, densidade e porosidade total do solo. As químicas constaram da determinação do pH e dos teores de cálcio, magnésio, fósforo, potássio, sódio, alumínio e C. A matéria orgânica foi fracionada nas frações ácido fúlvico (FAF), ácido húmico (FAH) e humina (HUM). Nas áreas de mata e sabiá foram quantificados a deposição e acúmulo de serrapilheira, bem como sua taxa de decomposição. Na pastagem, avaliou-se a produção de forragem. Quanto aos resíduos de culturas, observou-se que a taxa de decomposição das gramíneas é mais lenta que a das leguminosas, porém essa taxa se equivale nos últimos meses de avaliação. As gramíneas não apresentaram diferenças entre si, mas o guandu apresentou taxa de decomposição mais lenta entre as leguminosas. A adubação nitrogenada não afetou a taxa de decomposição dos resíduos. Quanto às mudanças no uso do solo, a quantidade de argila, o DMPAs, DMPAu e a relação DMPAu/DMPAs e a porosidade apresentaram maiores valores na área sob mata. A densidade do solo foi menor na área sob mata. O desenvolvimento de raízes foi maior nas áreas sob mata e pasto. A deposição de resíduos foi maior na área sob sabiá e os teores de N, P e K nesses resíduos foram maiores, o que mostra a capacidade do sabiá em ciclar nutrientes. O acúmulo de serrapilheira no solo foi maior na área sob mata. A taxa de decomposição dos resíduos foi de 48% na área sob sabiá e 40% na sob mata. Os teores de C, H+Al, Al, e a CTC potencial e a saturação por alumínio (m) no solo são maiores na área sob mata. O pH do solo, a saturação de bases (V) e os teores de Na e K foram semelhantes nas áreas sob sabiá e sob pasto e maiores que na sob mata. Os teores de Ca, Mg e P disponível e a SB e a CTC efetiva não diferem entre as áreas estudadas. O C do solo está mais preservado na área sob mata em função dos maiores teores nas frações FAH e HUM e da menor relação EA/HUM. Por sua vez, a substituição do pasto por sabiá começa a recuperar os teores de C perdidos na área sob pasto, com valores intermediários das frações FAH e HUM, demonstrando a capacidade do sabiá em recuperar a qualidade do solo.

Made available in DSpace on 2014-06-11T19:30:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-09-02Bitstream added on 2014-06-13T18:40:31Z : No. of bitstreams: 1 brancaliao_sr_dr_botfca.pdf: 1373956 bytes, checksum: 1e926e113d10f2a0394a14dd71456450 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O experimento, conduzido em Nitossolo Vermelho distroférrico, na Fazenda Experimental Lageado-FCA-UNESP-Botucatu, , teve por objetivo estudar no sistema de semeadura direta as prováveis alterações das propriedades físicas e químicas e das frações húmicas do solo, através da utilização da cultura do milheto em pré-safra a cultura da soja, em três épocas de semeadura e sob cinco manejos da fitomassa. O delineamento experimental foi o de blocos casualizados, com esquema de parcelas subdivididas, com quatro repetições. As parcelas foram representadas por três épocas de semeadura da cultura do milheto (E1, E2 e E3). As subparcelas foram representadas por manejos da ceifa da fitomassa, sendo: Manejo 1 (M1) - ceifa a cada florescimento e retirada da fitomassa; manejo 2 (M2) - ceifa a cada florescimento e permanência da fitomassa; manejo 3 (M3) - ceifa no florescimento e retirada da fitomassa; manejo 4 (M4) - ceifa no florescimento e permanência da fitomassa e manejo 5 (M5) - livre crescimento. Foram coletadas amostras de solo com estrutura deformada e indeformada para a realização das análises físicas e químicas. Tanto para a análise física quanto para a química, as mesmas profundidades foram amostradas: 0-0,05, 0,05-0,10, 0,10-0,20 e 0,20-0,40 m. Para o fracionamento químico da matéria orgânica, amostrou-se de 0-0,05 e 0,05-0,10 m. Em relação 2 as culturas avaliou-se a altura de plantas e a produtividade da soja e para o milheto, o seu sistema radicular, a quantidade de massa seca produzida pela parte aérea e a porcentagem de fitomassa em cobertura deixada sobre o solo. A produtividade de massa de matéria seca foi maior na primeira época de semeadura, excetuando-se o M3 para a segunda época e do M2 para a terceira época de semeadura. A segunda época de semeadura proporcionou maior fitomassa em cobertura... / This work was carried out at Lageado Experimental Station' FCA' Unesp' Botucatu, from October 2001 until April 2004, consisting in a millet' soybean succession, in a no-tillage system, at three sowing, and the aim was evaluate the physicals and chemicals and humics fractions of a Nitossolo Vermelho Distroférrico. The experimental design used was randomized blocks, in a split-plot schedule with four replications, having the sowing (S1, S2, S3) as parcel and harvest handling as subparcel. Where the harvest handling were 1 (H1)' harvest each blooming and covering withdrawal; 2 (H2)' harvest each blooming and covering permanency; 3 (H3)' only in the first harvest on blooming and covering withdrawal; H4 - only in the first harvest on blooming and covering permanency, and H5 'free growing, with no harvest. Disturbed and undisturbed samples were collected from four soil layers (0-0,05, 0,05-0,10 and 0,10-0,20 m) to evaluate the physical and chemical properties. The physical parameters measured were: bulk density, total porosity, macroporosity, microporosity, total clay, disperse clay, floculation degree, aggregation stability (dry sieving) and penetration resistance (Compact Test); the chemicals was: pH, organic mater, exchangele basis (Ca, Mg, K), cationic exchangeable capacity (CEC) and the quantification of the humic fractions (C-AH, C-AF and C-HU) All the parameters were performed on Department of Natural Research's (Soil Science-FCA), in different depths 0-0,05, 0,05-0,10, 0,10-0,20 e 0,20-0,40 m. About the humic fractions were analyseds only 0-0,05 e 0,05-0,10 m. The pearl millet matter drought mass productivity decreased in the order S1 > S2 >S3. The soil cover provided by fitomassa of milheto was larger in the S2 > S2 and S3 and in the H4 (with only fitomassa cut and permanence)... (Complete abstract, click eletronic address below)

Made available in DSpace on 2014-07-29T14:52:04Z (GMT). No. of bitstreams: 1 LUIZ ANTONIO SILVA.pdf: 1203248 bytes, checksum: 1d9898676ecca5fbd4b789ee1c605a3c (MD5) Previous issue date: 2006-08-30 / The objective of this wok was to monitor sustainability indicators of soil involving the cotton plant in different crop rotation and succession systems, as well as to evaluate cover crop species which best adapt and that have longer longevity of decomposition as well as their effects on the physical and chemical properties and characteristics of soil. The field trials were developed in two sites. One experiment was conducted on the experimental Farm of Campus II of the UFG, in the town of Goiânia-GO and the other in the experimental area of the Fundação GO, in the town of Santa Helena de Goiás- GO. Both plant mass yield and decomposition longevity were evaluated in Goiânia by the litterbag process as well as also the physical and chemical characteristics of soil and cotton seed yield kg ha-1 and grain soybean kg ha-1, upon the effect of different cover crop species. The single covers which provided increased dry plant mass yields were grain sorghum followed by feather-grass, Crotalária + Millet and Brachiaria and in longevity, the decomposition of the plant mass was maximum in the first 22 days standing out the mixture Mucuna + grain sorghum which showed highest residual plant mass yield. Most of the treatments involving the cover plant species in Goiânia presented the values of resistance to penetration (RP) within the ranges considered from high to low. Crotalária (Crotalária juncea) presented in Goiânia the lowest RP in solo, this being able to be the best option for the farming system management. The lowest values of RP found at Santa Helena were obtained by the cover crops Pigeon pea, Millet and grain sorghum. The crop rotation systems studied did no differ as to the effect of soil density, total porosity, macroporosity, microporosity and average diameter of aggregates. The elements P and Ca proved limiting as well as pH, V% and CEC for the cotton crop. There was no influence of the cover crop species on yield of the cotton plant and soybean. / O objetivo do trabalho foi de monitorar indicadores de sustentabilidade do solo envolvendo o algodoeiro em diferentes sistemas de rotação e sucessão de culturas, como também avaliar espécies vegetais de coberturas que melhor se adaptem e que tenham maior longevidade de decomposição, bem como seus efeitos nas propriedades e características físicas e químicas do solo. Os ensaios em campo foram desenvolvidos em dois locais. Um experimento foi conduzido na Fazenda Experimental Escola de Agronomia e Engenharia de Alimentos da Universidade Federal de Goiás no Campus Samambaia, no município de Goiânia, GO e o outro na área experimental da Fundação GO, no município de Santa Helena GO. Foram avaliadas a produção de fitomassa e a longevidade de sua decomposição em Goiânia, pelo processo de saco serapilheira litter-bag , como também as propriedades e características físicas e químicas do solo e a produção do algodão em caroço kg e de soja em grão kg, sob o efeito de diferentes espécies de coberturas. As coberturas que proporcionaram maiores produções de fitomassa seca foram o sorgo granífero, seguido do capim-pé-de-galinha, crotalária + milheto e braquiária, e em longevidade, a decomposição da fitomassa foi máxima nos primeiros 22 dias, com destaque para o consórcio mucuna + sorgo granífero que apresentou maior produção de fitomassa residual. A maioria dos tratamentos envolvendo as espécies vegetais de coberturas no experimento conduzido em Goiânia apresentou os valores de resistência à penetração (RP) dentro das faixas consideradas de alta a baixa. A crotalária apresentou a menor RP no solo, podendo ser esta a melhor opção para o manejo de sistemas agrícolas. Os menores valores de RP no experimento conduzido em Santa Helena foram obtidos pelas coberturas feijão guandu, milheto e o sorgo granífero. Os sistemas de rotação de culturas estudados não diferiram quanto aos efeitos na densidade do solo, porosidade total, macroporosidade, microporosidade e no diâmetro médio de agregados. Os elementos P e Ca mostraram limitantes, assim como o pH, V% e CTC para a cultura do algodoeiro. Não houve influência das espécies de coberturas na produtividade do algodoeiro e da soja.

O objetivo desse estudo foi realizar a caracterização do cimento resinoso autoadesivo RelyX U200 aditivado de nanotubos de dióxido de titânio (nt-TiO2) em diferentes concentrações (0,3, 0,6, e 0,9% em peso) quanto às suas propriedades físico-químicas, mecânicas e biológica. Duas condições de polimerização foram analisadas: autopolimerizável (grupos: AC, A03, A06 e A09) e dual (grupos: DC, D03, D06 e D09). Para análise do grau de conversão foi utilizada a espectroscopia de infravermelho com transformada de Fourier com registro do espectro nos tempos de 3, 6, 9, 12 e 15 minutos. Os picos das bandas de comprimento de onda de 1638 cm-1 e de 1608 cm-1 foram identificados para cálculo do grau de conversão. Os dados foram submetidos à ANOVA de medidas repetidas seguido de comparações múltiplas de Tukey (=0,05). A análise de sorção e solubilidade foi realizada por meio da confecção de discos de cimento resinoso (10 mm ø × 2 mm) (n=8) monitorados quanto à sua massa depois de ciclos de hidratação/desidratação. A resistência à flexão em 3 pontos e módulo de elasticidade foram mensurados por meio de barras (2 × 2 × 25 mm) de cimento resinoso (n=10) levadas à máquina universal de ensaios. Para análise de Dureza Knoop utilizou-se microdurômetro com carga de 50g /10 segundos. Nos discos de cimento resinoso de 10 mm ø × 2 mm foram realizadas 5 endentações equidistantes 0,5mm e medidas em aumento de 50×. Para resistência de união ao cisalhamento, sobre discos de zircônia sinterizados foi aplicado o cimento resinoso (n=10) nas dimensões de 3 mm ø × 2 mm. Por meio de dispositivo foram levados à máquina universal de ensaios. Os dados encontrados de sorção e solubilidade e de cada propriedade mecânica foram submetidos aos testes ANOVA a dois critérios e de comparações múltiplas de Tukey (=0,05). Exceto para resistência ao cisalhamento que se utilizou o teste de comparação de Fischer (=0,05). Para viabilidade celular (n=8) foi realizado teste de MTT apenas na condição dual. Os grupos estudados foram: DC, D03, D06, D09, CP (controle positivo), CN (controle negativo). Após 24, 48 e 72 horas os níveis de absorbâncias foram analisados por meio de espectrofotometria no leitor de ELISA. Os dados foram submetidos aos testes ANOVA a dois critérios e de comparações múltiplas de Tukey (=0,05). Os resultados mostraram que a adição de nt-TiO2, independente da concentração, aumentou os valores de grau de conversão do cimento resinoso para a condição autopolimerizável e dual em todos os tempos estudados. Já para sorção e solubilidade não houve influência nos resultados da concentração de nanotubos inseridos e da condição de polimerização. Para resistência flexural, a adição de nt-TiO2 nas concentrações de 0,3% (A03) e 0,9% (A09) resultou em dados similares ao controle na condição dual (DC). O valor médio de módulo de elasticidade aumentou com a adição de 0,9% (A09), similar a todos os grupos da condição dual, em que adição de nt-TiO2 não influenciou os resultados. A adição de 0,6% (A06 e D06) e 0,9% (A09 e D09) de nt-TiO2 ao cimento aumentou os valores de dureza quando comparado aos grupos controle (AC e DC). Para resistência de união ao cisalhamento, a concentração de 0,3% de nt-TiO2 (A03 e D03) aumentou os valores quando comparado aos grupos A06, D06, A09 e D09 porém sem diferença para os grupos controle (AC e DC). Para viabilidade celular no período de 24h, os grupos D03, D06 e D09 obtiveram resultado similar ao grupo CP, já o grupo DC apresentou valores de absorbância inferiores ao CP, usado como parâmetro de comparação. Em 48 e 72h, todos os grupos experimentais não demonstraram diferença significativa em comparação ao grupo CP. O grupo CN apresentou diferença para os demais em todos dos tempos estudados. A adição de nt-TiO2 ao cimento resinoso autoadesivo representa uma estratégia promissora para potencializar suas propriedades físico-químicas e mecânicas sem prejuízo das propriedades biológicas. / The aim of this study was to characterize the self-adhesive resin cement RelyX U200 additive, titanium dioxide nanotubes (nt-TiO2), at different concentrations (0.3%, 0.6%, and 0.9% by weight) and to determine their physicochemical, mechanical and biological properties. Two polymerization conditions were analyzed: self-curing (groups AC, A03, A06 and A09) and dual-curing (groups DC, D03, D06 and D09). To analyze the conversion degree, Fourier transform infrared spectroscopy was used, and the spectrum was recorded at 3, 6, 9, 12 and 15 minutes. The peaks of the wavelength bands, 1638 cm-1 and 1608 cm-1, were identified to calculate the degree of conversion. The data were subjected to a repeated-measures ANOVA followed by a Tukey multiple-comparison test (=0.05). The sorption and solubility analysis was performed by making resin-cement discs (10 mm ø × 2 mm) (n=8) and monitoring their masses after the hydration/dehydration cycles. The 3-point flexural strength and the modulus of elasticity of resin-cement bars (2 × 2 × 25 mm) (n=10) were measured using a universal testing machine. The Knoop microhardness was analyzed with a load of 50 g and a time of 10 seconds. On each resin cement disc, 5 equidistant indentations of 0.5 mm were made, and the measures were increased by 50×. To test bonding shear strength, resin cement was applied to sintered zirconia discs (3 mm ø × 2 mm) (n=10). The bonded discs were then taken to the universal testing machine. Their sorption, solubility and each mechanical property were submitted to a two-way ANOVA and a Tukey multiple-comparison test (=0.05). The shear strength was submitted to a Fischer comparison test (=0.05). To test cell viability (n=8), a MTT assay was performed using only the dual-curing condition. The studied groups were: DC, D03, D06, D09, CP (positive control) and CN (negative control). After 24, 48 and 72 hours, the absorbance levels were analyzed using an ELISA spectrophotometry reader. The data were submitted to a two-way ANOVA and a Tukey multiple-comparison test (=0.05). The results showed that the addition of nt-TiO2, regardless of concentration, increased the conversion degree values for the self-curing resin cement and for the dual-curing at all times studied. The sorption and solubility were not influenced by the concentration of the nanotubes or the polymerization condition. Regarding flexural strength, the addition of the nt-TiO2 in concentrations of either 0.3% (A03) or 0.9% (A09) resulted in data similar to those in the dual-curing control (DC) condition. The average modulus of elasticity increased with the addition of 0.9% nt-TiO2 (A09), and as with all the groups in the dual-curing condition, the addition of nt-TiO2 did not affect the results. The addition of either 0.6% (A06 and D06) or 0.9% (A09 and D09) of nt-TiO2 cement increased hardness values relative to the control groups (AC and DC). The group with a 0.3% concentration of nt-TiO2 (A03 and D03) showed higher bonding shear strength values than several of the groups with higher concentrations (A06, D06 and D09), but the A09 group had no difference relative to either control group (AC or DC). For cell viability in the 24-h period, the D03 D06 and D09 groups achieved a result similar to that of the CP group with significant difference to the DC group that had lower absorbance values. At the benchmarks of 48 and 72 h, and only the CN group showed a significant difference compared to others. The addition of nt-TiO2 is a promising strategy for improving the physical-chemical and mechanical properties without prejudice the biological properties.

Made available in DSpace on 2016-03-15T19:36:40Z (GMT). No. of bitstreams: 1 Isac Almeida da Silva.pdf: 4184474 bytes, checksum: 7cd309b008fc6810e46b803fd11e6463 (MD5) Previous issue date: 2014-02-05 / The so-called low-temperature physics had its development from studies of the dutch physicist Karmelingh Onnes, in the early twentieth century (1908), when he first got the liquefaction of helium. Studying thereafter the behavior of chemicals at low temperatures, three years after he found that resistance to the passage of electric current of mercury fell to zero for temperature equal to 4,2 K or -269ºC. This phenomenon came to be called superconductivity. In the following years many metallic superconductors were found, all, however, with a very low critical temperature. Intending to raising this temperature, doping in composite superconductors, such as BSCCO BiSrCaCuO have been made. In this research, physical and chemical properties of BSCCO composite were studied and discussed. This was done after different sintering routes. The precursor solutions were prepared by M. Pechini method, obtaining a material in powder form that was milled, calcinated, pressed, sintered, and then the characterization of samples was carried out using X-ray diffraction (XRD), electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The crystal structure of the material was refined by Rietveld method, by factors of disagreement Rwp = 5,43% e RBragg = 2,54%, checking 91,3% of phase 2234 BSCCO composite, which it is highly superconducting and rarely obtained together with 8,7% of other phases. / A denominada física de baixas temperaturas teve o seu desenvolvimento a partir dos estudos do físico holandês Karmelingh Onnes, no início do século XX (1908), quando pela primeira vez obteve a liquefação do hélio. Estudando a partir de então o comportamento de elementos químicos a baixas temperaturas, ele constatou três anos depois que a resistência à passagem da corrente elétrica do mercúrio sofreu uma queda a zero, quando à temperatura de 4,2 K, - 269 °C. Este fenômeno passou a ser chamado de supercondutividade. Nos anos seguintes muitos materiais metálicos supercondutores foram encontrados, todos, porém, com uma temperatura crítica baixíssima. Com a intenção de elevar esta temperatura, dopagens em compósitos supercondutores, tais como o BSCCO BiSrCaCuO vêm sendo efetuadas. Neste trabalho foram estudadas, discutidas e comparadas as propriedades físicas e químicas do compósito BSCCO após rotas distintas de sinterização. As soluções precursoras foram preparadas pelo método de M. Pechini, obtendo-se um material em forma de pó que, após moagem, calcinação, prensagem e sinterização, foram caracterizados, utilizando-se difração de raios X (DRX), microscopia eletrônica (MEV) e espectroscopia de energia dispersiva (EDS).. A estrutura cristalina do material obtido foi refinada até fatores de discordância Rwp = 5,43% e RBragg = 2,54%, verificando-se a presença de 91,3% da fase 2234 do compósito BSCCO, altamente supercondutora e de rara obtenção e 8,7% de outras fases.

Made available in DSpace on 2014-08-20T14:30:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-05-17 / In this study dental composites containing a novel monomodal inorganic matrix based on submicron Ba-Al-Si glass particles (NanoFine NF180, Schott) were prepared and evaluated. Composites with particles of similar composition but micron-sized (UltraFine UF1.0, Schott) served as a reference. The study was carried out in two phases: (i) characterization of the inorganic particles, involving x-ray microanalysis and granulometry; (ii) preparation and characterization of micron and submicron composites involving analysis of the morphology of the composites and measurements of radiopacity, degree of C=C conversion, hardness, flexural strength and modulus, work-of-fracture, surface roughness and gloss before and after toothbrushing abrasion and compressive creep. The composites were formulated from the same co-monomer based on Bis-GMA, Bis-EMA8, UDMA and TEGDMA at a 7:7:5:1 (w/w) ratio, with photoinitiators added. A mass of 75% of micron and 78% of submicron particles were incorporated based on pilot studies. Quantitative data restricted to direct comparisons between the composites were analyzed using t-tests. Roughness and gloss data for the comparison between the composites before and after toothbrushing were submitted to Repeated Measures Analysis of Variance and Student-Newman-Keuls test (5%). Both inorganic systems showed narrow grain size range (175±30 and 1000±200nm), with differences restricted to the size and specific area of the particles, which determined differences in the amount of silane used (13% for submicron and 3.2% for micron particles). Particles from both systems were homogeneously dispersed in the resin phase, although the submicron particles occupied larger area of the material s surface. The composites showed statistically similar results for radiopacity, flexural strength, work-of-fracture, and creep. The submicron composite had significantly higher hardness than the micron composite, whereas significantly lower flexural modulus and C=C conversion. No significant differences in roughness between the composites were observed before toothbrushing, while the submicron composite showed significantly higher gloss. The abrasion increased significantly the roughness and reduced the gloss of both materials. Surface roughness was still similar and the gloss of the submicron composite significantly higher after toothbrushing. In conclusion, the monomodal submicron glass filler system tested showed potential for application in the development of restorative dental composites, especially because of the esthetic properties compared with the micron system / Neste estudo, foram preparados e avaliados compósitos odontológicos contendo nova matriz inorgânica monomodal baseada em partículas de vidro de Ba-Al-Si (NanoFine NF180, Schott) de tamanho submicrométrico. Compósitos contendo partículas de composição similar, porém tamanho micrométrico (UltraFine UF1.0, Schott), foram testados como referência. O estudo se desenvolveu em duas fases: (i) caracterização de partículas inorgânicas, envolvendo microanálise de raios-x e granulometria; (ii) obtenção e caracterização de compósitos micro e submicrométricos envolvendo análise da morfologia dos compósitos preparados e determinação da radiopacidade, grau de conversão de C=C, dureza, resistência e módulo de flexão, trabalho de fratura, rugosidade e brilho da superfície antes e após desgaste por abrasão e escoamento compressivo (creep). Os compósitos foram formulados a partir do mesmo co-monômero baseado em Bis-GMA, Bis-EMA8, UDMA e TEGDMA, na razão 7:7:5:1 (m/m), ao qual fotoiniciadores foram adicionados. Foi acrescentada massa de 75% do sistema micrométrico e 78% do submicrométrico, com base em estudos-piloto. Os dados quantitativos restritos à comparação direta entre os compósitos foram analisados utilizando testes-t. Os dados de rugosidade e brilho na comparação dos compósitos antes e após a escovação foram submetidos à Análise de Variância para Medidas Repetidas e teste de Student-Newman-Keuls (5%). Ambos sistemas inorgânicos apresentaram estreita faixa do tamanho de grão (175±30 e 1000±200nm), com diferenças entre as partículas restritas ao tamanho e área específica, o que determinou diferença na quantidade de silano utilizada (13% para submicrométricas e 3,2% para micrométricas). As partículas de ambos sistemas foram dispersas de forma homogênea na matriz resinosa, embora as submicrométricas ocuparam maior área da superfície do material. Os compósitos apresentaram resultados estatisticamente similares para radiopacidade, resistência à flexão, trabalho de fratura e escoamento compressivo. O compósito submicrométrico apresentou dureza significativamente superior ao material micrométrico, enquanto módulo de elasticidade e grau de conversão foram significativamente menores. Não foi observada diferença significativa na rugosidade entre os compósitos antes da escovação, enquanto o compósito submicrométrico mostrou brilho significativamente maior. A abrasão aumentou significativamente a rugosidade e reduziu significativamente o brilho de ambos materiais. A rugosidade continuou estatisticamente similar e o brilho do compósito submicrométrico significativamente maior após a abrasão. Em conclusão, o sistema monomodal submicrométrico de carga de vidro testado apresentou potencial de utilização no desenvolvimento de compósitos restauradores odontológicos, especialmente em função de suas propriedades estéticas comparadas ao sistema micrométrico

Introduction: The aim of this study was to evaluate some of the physico-chemical properties of a new root canal sealer. Methodology: The sealers tested were Sealer Plus (MKLife, Porto Alegre, Rio Grande do Sul, Brazil), compared as AH Plus (Dentsply, DeTrey GmbH, Konstanz, Alemanha). For the radiopacity, flow, solubility and fabrication of test specimens relative to setting times the ANSI/ADA No. 57 (2000) and ISO 6876 (2012) specifications were followed. To measure the initial and final setting times the ASTM C266/2008 standard was used. pH was evaluated in the time intervals of 3, 24, 72 and 168 hours). Statistical tests were applied to the results obtained at a level of significance of 5%. Results: The results demonstrated that the Sealer Plus sealer showed a lower radiopacity value than AH Plus sealer (p<0.05), however, this was higher than the minimum value recommended by the specifications; that is 3 mm Al. Relative to flow, the value for Sealer Plus was 19.19 mm and for AH Plus, 19.81 mm (p>0.05). Sealer plus presented initial and final setting times of 138 min. and 210 min., respectively, while the values for AH Plus were 437 min. and 849 min., respectively, (p<0.05). Relative to solubility, Sealer Plus presented 0.21% and AH Plus, 0.27% (p>0.05). None of the sealers showed a significant increase in pH (p>0.05). Conclusion: Sealer Plus sealer presented physico-chemical properties in accordance with ANSI/ADA (2000) No.57 and ISO 6876 (2012) specifications. / Introdução: Este estudo objetivou avaliar algumas propriedades físico-químicas de um novo cimento obturador de canais radiculares. Metodologia: Para os testes de radiopacidade, escoamento, solubilidade e confecção dos corpos de prova para os tempos de presa foram seguidas as especificações nº57 da ANSI/ADA (2000) e ISO 6876 (2012). Para a medição dos tempos de presa, inicial e final, foi empregada a norma ASTM C266/2008. O pH foi avaliado nos períodos de 3, 24, 72 e 168 horas. Sobre os resultados foram aplicados testes estatísticos com nível de significância de 5%. Resultados: Os resultados demonstraram que o cimento Sealer Plus apresentou menor radiopacidade do que o cimento AH Plus (p<0.05), porém, superior ao mínimo recomendado pelas especificações, ou seja, de 3 mm de Al. Com relação ao escoamento, o do Sealer Plus foi 19,19 mm e do AH Plus 19,81 mm (p>0.05). O Sealer Plus apresentou tempos de presa inicial e final de 138 min. e 210 min., respectivamente, enquanto o AH Plus, 437 min. e 849 min., respectivamente, (p<0.05). Em relação à solubilidade, o Sealer Plus apresentou 0,21% e o AH Plus 0,27% (p>0.05). Nenhum dos cimentos apresentou aumento significativo do pH (p>0.05). Conclusão: O cimento Sealer Plus apresentou propriedades físico-químicas de acordo com as especificações nº 57 da ANSI/ADA (2000) e ISO 6876 (2012).