SILVA, M. S. Estudo da Influência da fase sigma na fragilização do aço inoxidável superaustenítico ASTM A744 Gr. CN3MN: microdureza e resistência à corrosão localizada. 2016. 77 f. Dissertação (Mestrado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2016. / Submitted by Hohana Sanders (hohanasanders@hotmail.com) on 2016-07-15T11:50:26Z No. of bitstreams: 1 2016_dis_mssilva.pdf: 5729538 bytes, checksum: bbf25d3d0ea13f6e4b03ae6ef4fdfa3c (MD5) / Approved for entry into archive by Marlene Sousa (mmarlene@ufc.br) on 2016-07-18T14:12:43Z (GMT) No. of bitstreams: 1 2016_dis_mssilva.pdf: 5729538 bytes, checksum: bbf25d3d0ea13f6e4b03ae6ef4fdfa3c (MD5) / Made available in DSpace on 2016-07-18T14:12:43Z (GMT). No. of bitstreams: 1 2016_dis_mssilva.pdf: 5729538 bytes, checksum: bbf25d3d0ea13f6e4b03ae6ef4fdfa3c (MD5) Previous issue date: 2016-03-31 / Super austenitic stainless steels are mainly characterized by their high resistance to corrosion in different environments. The work environment temperature may favor the formation of phases that may affect the mechanical and corrosion-resistance properties of these steels. As a result of the amount of Mo, Ni and Cr, the precipitation occurs in secondary phases, being more common the phases sigma () and qui (). In order to evaluate the pit corrosion resistance as a result of σ phase quantification in the super austenitic studied, the following solubilization treatments were conducted: 1170 ºC for 2h and 1200 ºC for 4h and 8h (for formation of different volumetric fractions of the σ phase). Characterizations by means of optical and electron microscopy techniques were carried out before and after the cyclic polarization, as well as the use of the electron backscatter diffraction (EBSD), in addition to the open circuit potential (OCP) monitoring, verification of critical pit temperature (CPT) and measures of Vickers microhardness of phase precipitation in evaluate the effect mechanical properties. The results obtained were compared to the material as-received state (gross fusion), which was to subject to similarly analyzed. The presence of phase σ was verified in all conditions, with difference as regards the volumetric fraction as a result of the treatment applied. It may be then perceived that the solution annealing temperature increase promotes the volumetric fraction sigma phase increase, resulting in the material resistance reduction and Vickers microhardness increase. After the cyclic polarization unverified pit corrosion in any sample. For the sample with received the verification of critical pit temperature was 55 ° C, could not be verified pit corrosion other conditions. With the increase in the volume fraction of sigma phase it was possible to check the increase in hardness in the solubilized sample at 1200 ° C for 4 hours. / Aços inoxidáveis superausteníticos são caracterizados principalmente por sua alta resistência à corrosão em diversos ambientes. A temperatura do ambiente de trabalho pode favorecer a formação de fases que podem afetar as propriedades mecânicas e de resistência à corrosão desses aços. Em decorrência da quantidade de Mo, Ni e Cr ocorre precipitação de fases secundárias, sendo mais comuns as fases sigma () e qui (). Para avaliação da resistência a corrosão por pites em decorrência da quantificação da fase  no superaustenítico estudado, foram realizados os seguintes tratamentos térmicos de solubilização: 1170oC por 2h e 1200oC 4h e 8h (para formação de diferentes frações volumétricas da fase σ). Foram realizadas caracterizações por meio das técnicas de microscopia óptica e eletrônica antes e após a polarização cíclica, assim como a utilização da técnica de dispersão de elétrons retroespalhados (EBSD), além do monitoramento do potencial de circuito aberto (OCP), verificação da temperatura crítica de pite (CPT) e medidas de microdureza Vickers para avaliação do efeito da precipitação de fases nas propriedades mecânicas. Os resultados obtidos foram comparados ao estado como recebido do material (bruto de fusão) que também foi submetido às mesmas análises. Verificou-se a presença da fase σ em todas as condições, havendo diferença quanto a fração volumétrica em função do tratamento aplicado, pode-se então perceber que o aumento da temperatura de solubilização promove o aumento da fração volumétrica da fase sigma, acarretando a redução da resistência do material e aumento da microdureza Vickers. Após a polarização cíclica não foi verificado pite em nenhuma das amostras. Para a amostra com o recebida a temperatura crítica de pite verificada foi de 55 oC, para as demais condições não foi possível verificar pite. Com o aumento da fração volumétrica da fase sigma foi possível verificar o aumento da dureza na amostra solubilizada a 1200 oC por 4 horas.

Dissertação (Mestrado em Engenharia de Materiais) - Centro Universitário FEI, São Bernardo do Campo, 2018

REIS, F. E. U. Avaliação das propriedades mecânicas e de resistência a corrosão em ligas modelo de aço inoxidável 25Cr 6Mo 5Ni com e sem adição de Boro. 2015. 135 f. Tese (Doutorado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-12-16T11:47:50Z No. of bitstreams: 1 2015_tese_feureis.pdf: 8321442 bytes, checksum: 45ac0d919d3b68b116798b0e3d6832af (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-12-18T12:11:09Z (GMT) No. of bitstreams: 1 2015_tese_feureis.pdf: 8321442 bytes, checksum: 45ac0d919d3b68b116798b0e3d6832af (MD5) / Made available in DSpace on 2015-12-18T12:11:09Z (GMT). No. of bitstreams: 1 2015_tese_feureis.pdf: 8321442 bytes, checksum: 45ac0d919d3b68b116798b0e3d6832af (MD5) Previous issue date: 2015-12-04 / Superferritic stainless steels are widely used in heat exchangers and in petrochemical power plant because of their excellent mechanical properties coupled to corrosion resistance in chloride rich environments. In this research new superferritic alloys with high Cr, Mo, and Ni contents were produced for oil industry applications. Therefore, two superferritic stainless steels model alloys were developed, one with 0.07% B addition and another one without this alloying element. The phase diagrams for both materials were carried out by Thermo-Calc computacional program. Microstructure characterization was performed using the following techniques: optical and scanning electron microscopy, energy-dispersive spectroscopy, and Xray diffraction. The mechanical properties were assessed by hardness measurements, Charpy impacts and tensile tests. Corrosion resistance of the model alloys in aqueous solution 0.6 M NaCl was investigated by open circuit potential, potentiodynamic cyclic anodic polarization, and electrochemical impedance spectroscopy. Furthermore, critical pitting temperature was determined. The results showed that the superferritic stainless steel model alloy without B addition achieved better mechanical properties than the one of the two commercial superferritic stainless steels alloys. The corrosion resistance of this alloy was similar to the one of the superaustenitic stainless steels, and superduplex in aqueous solution 0.6 M NaCl. However, there was the formation of eutectoid lamellar constituent like perlite for the superferritic stainless steel model alloy with B addition. This eutectoid constituent was deleterious to mechanical properties, as well as to corrosion resistance for the material developed and studied in this thesis. / Os aços inoxidáveis superferríticos são amplamente utilizados em trocadores de calor e em plantas petroquímicas, devido a suas excelentes propriedades mecânicas associadas à resistência à corrosão em ambientes ricos em cloreto. Nesta pesquisa foram produzidas novas ligas superferríticas com elevados teores de Cr, Mo e Ni para aplicação em plantas petrolíferas. Portanto, foram desenvolvidas duas ligas modelo de aço inoxidável superferrítico, uma com 0,07% de B e outra sem adição deste elemento de liga. Os diagramas de fases para os materiais foram construídos a partir do programa computacional Thermo-Calc. A caracterização microestrutural foi realizada usando as técnicas; microscopia óptica, microscopia eletrônica de varredura, espectroscopia de energia dispersiva de raios-X e difração de raios-X. As propriedades mecânicas foram avaliadas por medidas de dureza, ensaios de impacto Charpy e ensaios de tração. A resistência à corrosão das ligas modelo, em solução aquosa de 0,6M NaCl, foi avaliada por monitoramento do potencial de circuito aberto, polarização potenciodinâmica cíclica e espectroscopia de impedância eletroquímica. Além de determinar a temperatura crítica de pite. Os resultados obtidos demonstram que, a liga modelo de aço inoxidável superferrítico sem boro apresentou melhores propriedades mecânicas, comparada com duas ligas de aço inoxidável superferrítico comerciais. A resistência à corrosão dessa liga foi similar a um aço inoxidável superaustenítico e a um aço inoxidável superduplex, em solução aquosa de 0,6M de NaCl. Entretanto, para a liga modelo com boro, ocorreu a formação de um constituinte eutetóide lamelar semelhante à perlita. Este constituinte eutetóide é deletério para as propriedades mecânicas, assim como, na resistência à corrosão do material desenvolvido e estudado nesta tese.

De historier vi berättar för varandra berättas med ett syfte. Men vem berättar dem och med vilket bakomliggande syfte? I denna kvalitativa studie som bedrivs som en komparativ flerfallstudie undersöks och jämförs användningen av det existentiella historiebruket i lokalhistoriska publikationer. Författarna till dessa publikationer har antingen en samisk kulturell bakgrund eller en kulturell bakgrund som kan ses svara mot nybyggarkulturen. De lokalhistoriska publikationerna handlar om orterna Arvidsjaur och Glommersträsk samt de personer som där levde. Uppsatsen visar på hur författarna drivs av en tydlig personlig tendens och att valet av berättelser har ett bakomliggande syfte. Uppsatsen visar även hur författarna konstruerar ett ”vi” och ”dom” som primärt definieras av antingen etnicitet eller moraliskt handlande och att de använder denna konstruktion för att styrka det historiska narrativ författarna vill förmedla. / The stories we tell each other aret old with a purpose. But who tells them and for what reason? In this qualitative study, witch is conducted as a comparative multiple-case study, the use of existential history use in local history publications is examined and compared. The autors of these publications have eather Sami cultural background or a cultural background that can be seen as corresponding to the settler culture. The local history publications are about the places Arvidsjaur and Glommersträsk as well as the peaople who lived there. The essay shows how the authors are driven by a clear personal tendency and that the choice of stories has an underlying purpose. The essay also shows how the authors construct a ”we” and ”them” that is primarily defined by eather ethnicity or moral action and that they use this constuction to strengthen the historical narrative the authors want to convey.

Submitted by Maykon Nascimento (maykon.albani@hotmail.com) on 2015-12-15T18:33:05Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Avaliacao da resistencia a corrosao de revestimentos da liga UNS N06625 depositados pelo processo PTA P.pdf: 6159981 bytes, checksum: 50da99c404daae3acef07ae743845d6a (MD5) / Approved for entry into archive by Morgana Andrade (morgana.andrade@ufes.br) on 2015-12-30T15:51:09Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Avaliacao da resistencia a corrosao de revestimentos da liga UNS N06625 depositados pelo processo PTA P.pdf: 6159981 bytes, checksum: 50da99c404daae3acef07ae743845d6a (MD5) / Made available in DSpace on 2015-12-30T15:51:09Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Avaliacao da resistencia a corrosao de revestimentos da liga UNS N06625 depositados pelo processo PTA P.pdf: 6159981 bytes, checksum: 50da99c404daae3acef07ae743845d6a (MD5) Previous issue date: 2015 / A busca por materiais versáteis que associem elevada resistência à corrosão em ambientes severos e propriedades mecânicas, a fim de atender as mais exigentes condições de serviço tornou-se um desafio para a indústria petroquímica, termoelétrica, naval, dentre outras. Neste contexto, a soldagem de revestimento com ligas à base de níquel se torna uma interessante opção para a construção e o reparo de equipamentos para aplicações em ambiente de corrosão severa, permitindo alcançar as características desejadas, com significativa redução de custos. Em determinadas aplicações a alta diluição dos revestimentos deve ser controlada devido aos altos teores de ferro alcançados. O objetivo deste trabalho foi avaliar a corrosão intergranular e corrosão por pite de revestimentos da liga UNS N06625, com diferentes teores de diluições, depositados pela técnica Plasma com Arco Transferido Alimentado com Pó (PTA-P) sobre um substrato de aço carbono ASTM A36. Com a avaliação e caracterização do Inconel 625 buscou-se compreender o impacto da diluição na microestrutura, propriedades e no revestimento produzido. Foram realizadas análises das propriedades mecânicas dos revestimentos por meio de ensaios de microdureza. A caracterização microestrutural consistiu de análises de microscopia ótica, Microscopia Eletrônica de Varredura (MEV) e análise de composição química por EDS. Ensaios de reativação eletroquímica potenciodinâmica de duplo ciclo (DL-EPR) e polarização potenciodinâmica cíclica foram realizados para avaliar a resistência à corrosão intergranular e por pite, respectivamente. Através deste trabalho foi possível observar que a diferença de diluição influencia de forma suave na microdureza do revestimento. As microestruturas dos revestimentos apresentaram matriz γ com fases secundárias interdendríticas. Os revestimentos não apresentaram corrosão intergranular nas condições ensaiadas e a susceptibilidade da corrosão por pite somente pôde ser avaliada através da histerese apresentada pelas curvas de polarização. / The search for versatile materials that associate high corrosion resistance and high mechanical properties in severe environments, in order to meet the more demanding operational conditions has become a challenge for the petrochemical, thermoelectric, naval and other industries. In this context, weld overlay with nickel-based alloys becomes an interesting option for construction and repair of equipments for applications in severe corrosion environments, allowing to achieve the desired characteristics with significant cost reduction. In specific applications the high overlay dilution must be controlled due to high iron content encountered. The objective of this work is to evaluate the intergranular and pitting corrosion of the alloy UNS N06625, with different dilution values, deposited through Plasma Transferred Arc with Powder (PTA-P) welding technique on an ASTM A36 carbon steel substrate. With the evaluation and characterization of the alloy UNS N06625 aimed the comprehension of the dilution effect on the coating microstructure and properties. The mechanical properties tests were analyzed through microhardness tests. The microstructural characterization consisted of analyses with the optical microscope, with the Scanning Electron Microscope (SEM) and chemical composition with the EDS module. Double-Loop Electrochemical Potentiokinetic Reactivation Test (DL-EPR) and Cyclic Potentiodynamic Polarization tests were done to evaluate intergranular and pitting corrosion resistance, respectively. With this work it was possible to observe that the dilution difference influences in a smooth way in the coating microhardness. The microstructures presented aγ matrix with secondary interdendritic phases. The coatings did not present intergranular corrosion in the test conditions and the pitting corrosion susceptibility was able to be evaluated only through the hysteresis presented in the polarization curves.

O Aço Inoxidável Super Duplex UNS S32760 é um aço de alta liga com estrutura composta por uma matriz ferrítica com ilhas austeníticas, em proporções aproximadamente iguais. Esta estrutura lhe confere boas propriedades como: resistência à corrosão, em particular à corrosão por pite e por fresta, excelentes propriedades mecânicas, boa soldabilidade, alta condutividade térmica, baixo coeficiente de expansão térmica e excelente tenacidade. Suas principais aplicações geralmente ocorrem em ambientes com alta concentração de cloreto, como por exemplo, em tubos para transporte de óleo e gás, equipamentos para transporte ou em contato com materiais rico sem cloretos, em tanques e vasos para a indústria química e petroquímica. Estas aplicações tornam importante a determinação da temperatura crítica de pite (TCP). A ASTM normatiza essa determinação com as normas G-150 e G-48, que abrangem aços inoxidáveis austeníticos comuns e ligas à base de níquel, não existindo uma condição especifica para o teste em aços super duplex. O objetivo deste trabalho é a caracterização eletroquímica e o desenvolvimento de uma metodologia para a determinação da temperatura crítica de pite de aços super duplex UNS S32760. Devido à falta de normatização para estes materiais uma combinação das normas ASTM G-48 e G-150 foi empregada neste trabalho. Utilizou-se como meio uma solução contendo FeCl3 6% e HCl 1%, em massa. Foram empregadas como técnicas medidas de potencial de circuito aberto em função do tempo de imersão, curvas de polarização potenciostática anódica, cronoamperometria, espectroscopia de impedância eletroquímica (EIE), microscopia ótica (MO), microscopia eletrônica de varredura (MEV) e espectroscopia por dispersão de energia (EDS). Foram realizados tratamentos dos dados experimentais, abordando-os de maneiras diferentes para que a melhor resposta fosse obtida na determinação da TCP das ligas. Duas amostras diferentes deste material foram estudadas, uma amostra comercial e uma amostra desenvolvida pelo laboratório de pesquisa e desenvolvimento da Villares Metals, com diferentes teores de cromo e molibdênio. Apesar da variação na composição química das amostras, nas análises por MEV e EDS, as mesmas se mostraram semelhantes, quando apenas polidas, apresentando os mesmos tipos de precipitado. A microscopia ótica possibilitou visualizar a diferença na proporção de fases entre as duas ligas e as características morfológicas das mesmas. Analisando mais detalhada e minuciosamente os dados eletroquímicos, foi determinado que o melhor valor de densidade de corrente a ser utilizada como parâmetro na determinação da TCP , é 25±5 µAcm-2. Utilizando este parâmetro foi mostrado que a TCP determinada é menor, quando comparada com a obtida pelas normas convencionais. A combinação das diferentes técnicas permite afirmar que a metodologia empregada determina de maneira bem mais precisa a TCP. / UNS S32760 super duplex stainless steel is a high alloy steel, containing a ferrítica matrix and austenitic islands as structure at equal proportions approximately. This structure results in good properties as high resistance to corrosion, particularly to pitting and crevice corrosion, excellent mechanical properties, good weldability, high thermic conductivity, low thermic expansion coefficient, and excellent tenacity. Their principal applications are in high chloride concentration media, for example in tubes for oil and gas, in transport equipment when in contact with high chloride concentration materials, tanks and vases for chemical and petrochemical industries. Due to these applications the evaluation of the pitting critical temperature is mandatory for these materials. G-150 and G-48 ASTM Standards are recommended for conventional stainless steels and nickel alloys, but there is not any specific standard for super duplex stainless steels. The main of this work is the characterization and the development of a methodology to evaluate the critical pitting temperature for USS S32760 super duplex stainless steels. Due to the absence of standard analyses for this materials, a combination of G-48 and G-150 standards were employed. The medium was 6% FeCl3 by mass and 1% HCl by mass solution. Open circuit potential measurements, anodic potentiostatic polarization curves, chronoamperometry, electrochemical impedance spectroscopy (EIS), optical microscopy (OM), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS) were used as techniques. Different treatments for the experimental results were used in order to obtain the best value for TCP of these alloys. Two different samples of this material were studied: a commercial sample and a new composition developed at P&D Villares Metals industry, with different contents in chromium and molybdenum. The materials studied presented the same kinds of inclusions, according to SEM and EDS analyses. OM analysis showed the proportionality between the ferritic and austenitic phases and their morphological characteristics. The electrochemical studies suggest the 25 ± 5 µAcm-2 value for current density to be used in the CPT e valuation. The CPT obtained is lower when compared to those one using conventional standards. The combination of different techniques permits to conclude that the proposed methodology evaluates the CPT w ith higher precision.

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / Superferritic stainless steels are widely used in heat exchangers and in petrochemical power plant because of their excellent mechanical properties coupled to corrosion resistance in chloride rich environments. In this research new superferritic alloys with high Cr, Mo, and Ni contents were produced for oil industry applications. Therefore, two superferritic stainless steels model alloys were developed, one with 0.07% B addition and another one without this alloying element. The phase diagrams for both materials were carried out by Thermo-Calc computacional program. Microstructure characterization was performed using the following techniques: optical and scanning electron microscopy, energy-dispersive spectroscopy, and Xray diffraction. The mechanical properties were assessed by hardness measurements, Charpy impacts and tensile tests. Corrosion resistance of the model alloys in aqueous solution 0.6 M NaCl was investigated by open circuit potential, potentiodynamic cyclic anodic polarization, and electrochemical impedance spectroscopy. Furthermore, critical pitting temperature was determined. The results showed that the superferritic stainless steel model alloy without B addition achieved better mechanical properties than the one of the two commercial superferritic stainless steels alloys. The corrosion resistance of this alloy was similar to the one of the superaustenitic stainless steels, and superduplex in aqueous solution 0.6 M NaCl. However, there was the formation of eutectoid lamellar constituent like perlite for the superferritic stainless steel model alloy with B addition. This eutectoid constituent was deleterious to mechanical properties, as well as to corrosion resistance for the material developed and studied in this thesis. / Os aÃos inoxidÃveis superferrÃticos sÃo amplamente utilizados em trocadores de calor e em plantas petroquÃmicas, devido a suas excelentes propriedades mecÃnicas associadas à resistÃncia à corrosÃo em ambientes ricos em cloreto. Nesta pesquisa foram produzidas novas ligas superferrÃticas com elevados teores de Cr, Mo e Ni para aplicaÃÃo em plantas petrolÃferas. Portanto, foram desenvolvidas duas ligas modelo de aÃo inoxidÃvel superferrÃtico, uma com 0,07% de B e outra sem adiÃÃo deste elemento de liga. Os diagramas de fases para os materiais foram construÃdos a partir do programa computacional Thermo-Calc. A caracterizaÃÃo microestrutural foi realizada usando as tÃcnicas; microscopia Ãptica, microscopia eletrÃnica de varredura, espectroscopia de energia dispersiva de raios-X e difraÃÃo de raios-X. As propriedades mecÃnicas foram avaliadas por medidas de dureza, ensaios de impacto Charpy e ensaios de traÃÃo. A resistÃncia à corrosÃo das ligas modelo, em soluÃÃo aquosa de 0,6M NaCl, foi avaliada por monitoramento do potencial de circuito aberto, polarizaÃÃo potenciodinÃmica cÃclica e espectroscopia de impedÃncia eletroquÃmica. AlÃm de determinar a temperatura crÃtica de pite. Os resultados obtidos demonstram que, a liga modelo de aÃo inoxidÃvel superferrÃtico sem boro apresentou melhores propriedades mecÃnicas, comparada com duas ligas de aÃo inoxidÃvel superferrÃtico comerciais. A resistÃncia à corrosÃo dessa liga foi similar a um aÃo inoxidÃvel superaustenÃtico e a um aÃo inoxidÃvel superduplex, em soluÃÃo aquosa de 0,6M de NaCl. Entretanto, para a liga modelo com boro, ocorreu a formaÃÃo de um constituinte eutetÃide lamelar semelhante à perlita. Este constituinte eutetÃide à deletÃrio para as propriedades mecÃnicas, assim como, na resistÃncia à corrosÃo do material desenvolvido e estudado nesta tese.

O Aço Inoxidável Super Duplex UNS S32760 é um aço de alta liga com estrutura composta por uma matriz ferrítica com ilhas austeníticas, em proporções aproximadamente iguais. Esta estrutura lhe confere boas propriedades como: resistência à corrosão, em particular à corrosão por pite e por fresta, excelentes propriedades mecânicas, boa soldabilidade, alta condutividade térmica, baixo coeficiente de expansão térmica e excelente tenacidade. Suas principais aplicações geralmente ocorrem em ambientes com alta concentração de cloreto, como por exemplo, em tubos para transporte de óleo e gás, equipamentos para transporte ou em contato com materiais rico sem cloretos, em tanques e vasos para a indústria química e petroquímica. Estas aplicações tornam importante a determinação da temperatura crítica de pite (TCP). A ASTM normatiza essa determinação com as normas G-150 e G-48, que abrangem aços inoxidáveis austeníticos comuns e ligas à base de níquel, não existindo uma condição especifica para o teste em aços super duplex. O objetivo deste trabalho é a caracterização eletroquímica e o desenvolvimento de uma metodologia para a determinação da temperatura crítica de pite de aços super duplex UNS S32760. Devido à falta de normatização para estes materiais uma combinação das normas ASTM G-48 e G-150 foi empregada neste trabalho. Utilizou-se como meio uma solução contendo FeCl3 6% e HCl 1%, em massa. Foram empregadas como técnicas medidas de potencial de circuito aberto em função do tempo de imersão, curvas de polarização potenciostática anódica, cronoamperometria, espectroscopia de impedância eletroquímica (EIE), microscopia ótica (MO), microscopia eletrônica de varredura (MEV) e espectroscopia por dispersão de energia (EDS). Foram realizados tratamentos dos dados experimentais, abordando-os de maneiras diferentes para que a melhor resposta fosse obtida na determinação da TCP das ligas. Duas amostras diferentes deste material foram estudadas, uma amostra comercial e uma amostra desenvolvida pelo laboratório de pesquisa e desenvolvimento da Villares Metals, com diferentes teores de cromo e molibdênio. Apesar da variação na composição química das amostras, nas análises por MEV e EDS, as mesmas se mostraram semelhantes, quando apenas polidas, apresentando os mesmos tipos de precipitado. A microscopia ótica possibilitou visualizar a diferença na proporção de fases entre as duas ligas e as características morfológicas das mesmas. Analisando mais detalhada e minuciosamente os dados eletroquímicos, foi determinado que o melhor valor de densidade de corrente a ser utilizada como parâmetro na determinação da TCP , é 25±5 µAcm-2. Utilizando este parâmetro foi mostrado que a TCP determinada é menor, quando comparada com a obtida pelas normas convencionais. A combinação das diferentes técnicas permite afirmar que a metodologia empregada determina de maneira bem mais precisa a TCP. / UNS S32760 super duplex stainless steel is a high alloy steel, containing a ferrítica matrix and austenitic islands as structure at equal proportions approximately. This structure results in good properties as high resistance to corrosion, particularly to pitting and crevice corrosion, excellent mechanical properties, good weldability, high thermic conductivity, low thermic expansion coefficient, and excellent tenacity. Their principal applications are in high chloride concentration media, for example in tubes for oil and gas, in transport equipment when in contact with high chloride concentration materials, tanks and vases for chemical and petrochemical industries. Due to these applications the evaluation of the pitting critical temperature is mandatory for these materials. G-150 and G-48 ASTM Standards are recommended for conventional stainless steels and nickel alloys, but there is not any specific standard for super duplex stainless steels. The main of this work is the characterization and the development of a methodology to evaluate the critical pitting temperature for USS S32760 super duplex stainless steels. Due to the absence of standard analyses for this materials, a combination of G-48 and G-150 standards were employed. The medium was 6% FeCl3 by mass and 1% HCl by mass solution. Open circuit potential measurements, anodic potentiostatic polarization curves, chronoamperometry, electrochemical impedance spectroscopy (EIS), optical microscopy (OM), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS) were used as techniques. Different treatments for the experimental results were used in order to obtain the best value for TCP of these alloys. Two different samples of this material were studied: a commercial sample and a new composition developed at P&D Villares Metals industry, with different contents in chromium and molybdenum. The materials studied presented the same kinds of inclusions, according to SEM and EDS analyses. OM analysis showed the proportionality between the ferritic and austenitic phases and their morphological characteristics. The electrochemical studies suggest the 25 ± 5 µAcm-2 value for current density to be used in the CPT e valuation. The CPT obtained is lower when compared to those one using conventional standards. The combination of different techniques permits to conclude that the proposed methodology evaluates the CPT w ith higher precision.

O desenvolvimento dos aços inoxidáveis Super-Martensíticos (SM) nasce da necessidade de implementar novas tecnologias, mais econômicas e amigáveis ao meio ambiente. Os aços inoxidáveis SM são uma derivação dos aços inoxidáveis martensíticos convencionais, diferenciando-se basicamente no menor teor de carbono, na adição de Ni e Mo. Foram desenvolvidos como uma alternativa para aços inoxidáveis duplex no uso de dutos para a extração de petróleo offshore em meados dos anos 90. Para que esses aços apresentem as propriedades mecânicas de resistência à tração e tenacidade é necessário que sejam realizados tratamentos de austenitização, seguido de têmpera, e de revenimento, onde, particularmente para este último, há várias opções de tempos e temperaturas. Como os tratamentos térmicos geram as propriedades mecânicas através de transformações de fase (precipitação) podem ocorrer alterações da resistência à corrosão. São conhecidos os efeitos benéficos da adição de Nb em aços inoxidáveis tradicionais. Por isso, o objetivo desta pesquisa foi estudar aços inoxidáveis SM contendo Nb. Foi pesquisada a influência da temperatura de revenimento sobre a resistência à corrosão de três aços inoxidáveis SM, os quais contêm 13% Cr, 5% Ni, 1% a 2% Mo, com e sem adições de Nb. No presente trabalho, foram denominados de SM2MoNb, SM2Mo e SM1MoNb, que representam aços com 2% Mo, 1% Mo e 0,11% Nb. Dado que os principais tipos de corrosão para aços inoxidáveis são a corrosão por pite (por cloreto) e a corrosão intergranular (sensitização), optou-se por determinar os Potenciais de Pite (Ep) e os Graus de Sensitização (GS) em função da temperatura de revenimento. Os aços passaram por recozimento a 1050°C por 48 horas, para eliminação de fase ferrita delta. Em seguida foram tratados a 1050 °C por 30 minutos, com resfriamento ao ar, para uniformização do tamanho de grão. A estrutura martensítica obtida recebeu tratamentos de revenimento em temperaturas de: 550 °C, 575 °C, 600 °C, 625 °C, 650 °C e 700 °C, por 2 horas. O GS foi medido através da técnica de reativação eletroquímica potenciodinâmica na versão ciclo duplo (DL-EPR), utilizando-se eletrólito de 1M H2SO4 + 0,01M KSCN. Para determinar o Ep foram realizados ensaios de polarização potenciodinâmica em 0,6M NaCl. Os resultados obtidos foram discutidos através das variações microestruturais encontradas. Foram empregadas técnicas de microscopia ótica (MO), microscopia eletrônica de varredura (MEV), simulação termodinâmica de fases através do programa Thermo-Calc e determinação de austenita revertida mediante difração de raios X (DRX) e ferritoscópio. A quantificação da austenita por DRX identificou que a partir de 600 °C há formação desta fase, apresentando máximo em 650 °C, e novamente diminuindo para zero a 700 °C. Por sua vez, o método do ferritoscópio detectou austenita nas condições em que a analise de DRX indicou valor nulo, sendo as mais críticas a do material temperado (sem revenimento) e do aço revenido a 700 °C. Propõe-se que tais diferenças entre os dois métodos se deve à morfologia fina da austenia retida, a qual deve estar localizada entre as agulhas de martensita. Os resultados foram discutidos em termos da precipitação de Cr23C6, Mo6C, NbC, fase Chi, austenita e ferrita, bem como das consequências do empobrecimento em Cr e Mo, gerados por tais microconstituintes. São propostos três mecanismos para explicar a sensitização: o primeiro é devido a precipitação de Cr23C6, o segundo a precipitação de fase Chi (rica em Cr e Mo) e o terceiro é devido a formação de ferrita durante o revenimento. O melhor desempenho quanto ao GS foi obtido para os revenimentos a 575 °C e 600°C, por 2 horas. Os resultados de Ep indicaram que o aço SM2MoNb, revenido a 575°C, tem o melhor desempenho quanto à resistência à corrosão por cloreto. Isso associado ao baixo GS coloca este aço, com este tratamento térmico, numa posição de destaque para aplicações onde a resistência à corrosão é um critério de seleção de material, uma vez que, segundo a literatura a temperatura de 575 °C está no intervalo de temperaturas de revenimento onde são obtidas as melhores propriedades mecânicas. / Supermartensitic (SM) stainless steels were developed in response to the need of new technologies that are more economical and environmentally friendly. SM steels are different from classic martensitic stainless steels due to their lower carbon content and the addition of Mo and Ni. SM steels were developed as an alternative for duplex stainless steels in oil extraction pipelines offshore in the mid-1990s. To acquire the desired mechanical properties quenching and tempering treatments can be conducted, with tempering which can be performed in different temperatures and times. Since the previous heat treatments change the mechanical properties by phase transformations (precipitation), changes in the corrosion resistance properties can be expected. The beneficial effects of Nb additions in traditional stainless steels are well known. Therefore, the aim of this investigation was to study the influence of tempering temperature on the corrosion resistance of three SM stainless steels, containing 13% Cr, 5% Ni, 1-2% Mo, with and without Nb. The steels used in this investigation were denominated SM2MoNb, SM2Mo and SM1MoNb, according to their Mo (2% or 1%) and Nb (0.11%) content. Considering that the usual types of corrosion observed in stainless steels are pitting and intergranular corrosion, the pitting potential (Ep) and the degree of sensitization (DOS) were determined in function of tempering temperature. The steels were annealed at 1050° C during 48 hours to eliminate delta ferrite phase. Afterwards, the samples were normalized for 30 minutes at 1050 ºC (air cooling) to standardize the grain size. Finally, the samples were tempered at 550 °C, 575 °C, 600 °C, 625 °C, 650 °C or 700 °C, for two hours. The DOS was measured through double loop electrochemical potentiodynamic reactivation technique (DL-EPR), using as electrolyte a solution containing 1 M H2SO4 + 0.01 M KSCN. To determine the Ep, potentiodynamic polarization tests were carried out in a 0.6 M NaCl solution. The results were discussed based on the observed microstructural changes. Optical microscopy (OM), scanning electron microscopy (SEM), phase diagram simulation using Thermo-Calc software and quantification of reversed/retained austenite were done using the following two methods: X-ray diffraction (XRD) and magnetic measurements with a ferritscope. The quantification analysis by XRD showed the formation of austenite above a temperature of 600 °C, reaching the maximum volume at 650 °C and decreasing again to zero at 700 °C. However, the ferritscope measurements detected the presence of austenite in the whole temperature range. The largest difference between the two methods used was observed for the specimens only quenched and quenched/tempered at 700 °C. It is proposed that the observed differences between XRD and ferritscope methods correspond to the presence of nanometric retained austenite, which is localized among the martensite laths. The results were discussed based on the precipitation of Cr23C6, Mo6C, NbC, Chi-phase, austenite and ferrite, and by the resulting Cr and Mo depletion caused by the precipitation of these microconstituents. Three mechanisms were proposed to explain the degree of sensitization: i) Cr23C6 precipitation, ii) Chi-phase (Cr and Mo enrichment) precipitation and, iii) ferrite formation during the tempering treatment. The best performance in terms of DOS was obtained for the tempering conditions of 575 ºC and 600 ºC. In addition, the Ep results showed that the steel SM2MoNb tempered at 575 °C offers the best pitting corrosion resistance in chloride environment. Therefore, the previous results can be used as criteria for best material and tempering temperature selection. Moreover, according to published literature, 575 °C is within the temperature range that offers the best mechanical properties.

Os aços inoxidáveis endurecidos por precipitação vêm sendo largamente empregados na indústria aeronáutica, por combinar resistência mecânica, tenacidade à fratura e resistência à corrosão. E deste modo, são materiais que possibilitam a substituição dos aços carbonos utilizados atualmente, que necessitam de tratamento superficial adicional, como o cádmio, para melhorar a resistência à corrosão. A utilização desses revestimentos traz desvantagens como o custo, a fabricação, a susceptibilidade à fragilização por hidrogênio além dos aspectos ambientais. Neste contexto, o aço endurecido por precipitação UNS S46500, designado como Custom 465® foi avaliado considerando o efeito da temperatura de envelhecimento sobre as propriedades mecânicas e a resistência à corrosão por pite. Amostras tratadas nas condições solubilizada e envelhecida a 510ºC (H950) e 538ºC (H1000) foram submetidas ao ensaio de tração, caracterização microestrutural e ensaios de polarização potenciodinâmica (PP) para determinar a resistência à corrosão por pite. Os exames microestruturais foram realizados com auxílio de microscopia óptica (MO), microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS) e difração de raios X. Também foram realizadas análises utilizando o software Thermo-Calc. A resistência à corrosão por pite foi avaliada em solução 0,6M NaCl com adições crescentes de Na2SO4. Os resultados obtidos nos ensaios de PP nas duas condições de tratamento térmico foram comparados entre si e com resultados disponíveis na literatura (CALDERÓN-HERNANDEZ, 2012) para o aço inoxidável UNS S30403 (304L). Os exames e análises da microestrutura revelaram que o aço Custom 465® envelhecido apresenta uma matriz martensítica, precipitados de fase chi, austenita e precipitados Ni3Ti. O tratamento H950 apresentou maior resistência mecânica e menor alongamento do que o tratamento H1000. Tal comportamento foi devido à produção de maior porcentagem de fase chi e menor porcentagem de austenita nesse tratamento de envelhecimento. Os diferentes tratamentos térmicos, condição solubilizada, H950 e H1000 apresentaram praticamente a mesma resistência à corrosão por pite. Por outro lado, o aço Custom 465® apresentou ótima resposta à inibição da nucleação de pite com adições crescentes de sulfato em meio de 0,6M NaCl, sendo que a condição H1000 se sobressai sobre a H950 nessa questão. Além disso, através da adição de sulfato foi 7 possível obter maior resistência a corrosão por pite do aço Custom 465® comparativamente ao aço 304L. Tal comportamento foi discutido em termos da afinidade química entre níquel, cloreto e sulfato, levando a maior resistência à corrosão por pite quando o aço contém maior teor de níquel (que é o caso do aço Custom 465®). Este trabalho indicou que o critério na escolha do tratamento de envelhecimento do aço Custom 465® deve ser o das propriedades mecânicas almejadas, uma vez que a resistência à corrosão por pite mostrou-se praticamente independente do tratamento térmico. / The precipitation hardened stainless steels have been widely used in the aircraft industry to combine mechanical strength, fracture toughness and corrosion resistance. And therefore, are materials that enable replacement of the carbon steels used today, which require additional surface treatment, such as cadmium plating, to improve the corrosion resistance. The use of such coatings brings disadvantages such as cost, manufacturing, susceptibility to hydrogen embrittlement beyond environmental aspects. In this context, the precipitation hardened steel UNS S46500, known as Custom 465® were evaluated for the effect of aging temperature on the mechanical properties and the resistance to pitting corrosion .Treated samples in solubilized and aged condition at 510°C (H950) and 538ºC (H1000) were subjected to tensile strength test, microstructural characterization and potentiodynamic polarization (PP) tests to determine the pitting corrosion resistance. The microstructural studies were performed with the aid of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction. Analyzes were also performed using the Thermo -Calc software. The resistance to pitting corrosion was evaluated at 0.6M NaCl solution with increasing additions of Na2SO4. The results obtained from tests of PP in both heat treatment conditions were compared with each other and with results available in the literature (CALDERÓN HERNANDEZ, 2012) to stainless steel UNS S30403 (304L). The analysis of the microstructure revealed that the steel aged Custom 465 ® presents a martensitic matrix, chi precipitates, Ni3Ti precipitates and austenite phase. The H950 age treatment had higher mechanical strength and lower elongation than the treatment H1000. Such behavior was due to the production of higher percentage of chi and a lower percentage of austenite phase in aging treatment. The different heat treatments, solubilized condition, H950 and H1000 showed almost the same pitting corrosion resistance. On the other hand, the Custom 465® showed good response to pitting inhibition with increasing nucleating additions of sulfate in 0.6M NaCl, with enhanced result for H1000 condition. Furthermore, by adding sulfate was possible to obtain greater pitting corrosion resistance of Custom 465® compared to the 304L steel. This behavior has been discussed in terms of the chemical affinity between nickel, chloride and sulphate, leading to higher pitting corrosion resistance when the steel contains a higher nickel 9 content (which is the case of steel Custom 465®). This study indicates that the criterion in selecting the aging heat treatment of Custom 465® steel must be the desired mechanical properties, since the pitting corrosion resistance was found to be substantially independent of heat treatment.