Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-06-19Bitstream added on 2014-06-13T20:58:53Z : No. of bitstreams: 1 carvalho_cf_me_sjc.pdf: 1809025 bytes, checksum: bd4ee4f9a60dfdd8304d67de208703e4 (MD5) / O objetivo deste estudo foi avaliar e comparar a adaptação marginal de restaurações, confeccionadas em dois tipos de sistemas cerâmicos: CEREC inLab (VITA) e IPS Empress 2 (Ivoclar-Vivadent) , após a cimentação com cimento resinoso RelyX (3M). Foram preparados 20 pré-molares humanos com cavidade MOD inlay, reproduzidos com silicone de adição, e obtidos modelos em gesso tipo IV, sobre os quais foram confeccionadas as restaurações conforme as recomendações dos fabricantes. Dez inlays no sistema IPS Empress 2 e 10 inlays no sistema CEREC inLab. As restaurações foram cimentadas sob pressão constante de 1,5 Kgf por 10 min, com cimento resinoso, com pré-tratamento. As desadaptações marginais foram avaliadas em MEV, com magnificação de 200x, em 50 pontos eqüidistantes. As médias foram analisadas pelo teste estatístico t(Student) de amostras dependentes.Resultando em uma diferenca estatisticamente significante entre as desadaptaçoes marginais no sistema IPS Empress (93,8'mais ou menos'15,5'mü'm)que se mostraram menores que no sistema CEREC inLab (114,4'mais ou menos'10,6'mü'm). Quando se comparou os valores médios entre as faces proximais (116,51.21,85'mü') e oclusal (112,26'mais ou menos'8,49'mü) do sistema Cerec Inlab, e faces proximais (87,12'mais ou menos'27,98,'mü') e oclusal (100,47'mais ou menos'22,23'mü')do sistema IPS Empress 2, verifica-se que esses valores não diferem estatisticamente. Ainda assim, conclui-se que as médias obtidas são aceitavéis clinicamente. / This study has the proposal to evaluate the marginal adaptation of two system all-ceramic class II inlays one of laboratory-made heat-pressed ceramics (IPS Empress 2) and other computer-aided manufacturing ( CEREC inLab) after cementation with resin cement . Extracted human premolars were prepared to receive mesio occluso distal (MOD) ceramic inlays for 10 IPS Empress restorations and 10 CEREC inLab restorations. The impression material used was a polivinilsyloxane addition silicone by the double impression technique. The impressions of prepared teeth were cast in type IV dental stone. The restaurations were made following the manufacturer's recommendations. The inlays were luted on human premolars with resin cement in accordance with the manufacturer's recommended pré-treatment. The marginal gaps were investigated scanning electron microscopy with magnification of 200x. The results were analyzed by t (student) statistic test.The means marginal gap for IPS Empress 2 wal 93,8'mais ou menos'15,5'mü'm significantly smaller than that od 114,4'mais ou menos'10,6'mü'm calculated a the CEREC in Lab system.The gaps of the inlays at the occlusal margin and of the approximal margin showed no significantly differences in two system. It may be concluded that mensuarement value are clinically acceptable.

Orientador: Ângela Cristina Cilense Zuanon / Banca: José Luiz Guimarães Figueiredo / Banca: Lourdes Aparecida Martins dos Santos-Pinto / Resumo: Este trabalho teve como objetivo determinar a influência da excitação ultra-sônica aplicada em dois cimentos de ionômero de vidro nos momentos inicias de sua reação de presa, avaliando a rugosidade superficial e a perda de massa após ensaio de escovação. Os materiais foram o Fuji IX GP (GC Corporation) e Ketac Molar Easymix (3M ESPE), manipulados de acordo com as instruções dos fabricantes e inseridos em matriz confeccionada com dente bovino. Foram confeccionados 16 espécimes de cada material, dos quais a metade recebeu excitação com ondas de ultra-som (PROFI III BIOS - Dabi Atlante) por um período de 30 segundos. Todos os corpos foram pesados diariamente, em balança analítica (Sartoruis), até a estabilização de sua massa, a qual foi alcançada após 20 dias da manipulação. Logo após foi realizada a leitura da rugosidade inicial (rugosímetro Surfcorder SE 1700 - Japão). Em seguida os mesmos foram submetidos ao ensaio de escovação, totalizando 30.000 ciclos. Nova leitura de rugosidade superficial e seqüência de pesagem foram realizadas. Para a análise estatística foram utilizados os testes de Análise de Variância (MANOVA) e t-Student onde a diferença estatística foi determinada por p= 0,05. Observou-se diferença estatística significante na rugosidade superficial antes e após o ensaio de escovação (p= 0,00). Porém não houve diferença estatística na rugosidade quando considerada a aplicação de ondas de ultra-som (p= 0,06). A média de rugosidade após ensaio de escovação para o Fuji IX GP foi de 0,767æm e 0,643æm com e sem a aplicação de ondas de ultra-som respectivamente e para o Ketac Molar Easymix esses valores foram de 0,759æm e 0,757æm para as mesmas condições experimentais. Na interação material, excitação ultra-sônica e ensaio de escovação foi observada diferença... Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this work was to determine the influence of ultrasonic excitation in two glass ionomer cements (GICs) evaluating the superficial roughness and mass loss after toothbrushing test. The GICs tested were Fuji IX GP (GC Corporation) and Ketac Molar Easymix (3M ESPE). The cements were manipulated according to the manufacturesþ instructions and inserted in a bovine tooth matrix. For each material 16 specimens were made. Eight specimens of them were excited with ultrasonic waves (PROFI III BIOS - Dabi Atlante) for 30s. All specimens were weighed daily in an analytical balance (Sartoruis) until their mass stabilization which was reached after twenty days. Next, the initial superficial roughness reading was performed (Surfcorder SE 1700 - Japan). After that, toothbrushing test was performed, and 30.000 cycles were applied. Soon after, a new superficial roughness reading and a sequence of weighing were performed. The statistical analysis was made through MANOVA test and t-Student where p= 0.05 determined a significant statistical difference. A difference on the superficial roughness was observed before and after toothbrushing (p=0.00). However, there was no statistical difference when the ultrasonic waves were used (p=0.06). After toothbrushing test Fuji IX GP roughness average was 0.767æm and 0.643æm with and without the use of ultrasound waves respectively while Ketac Molar Easymix showed 0.759æm and 0.757æm in the same experimental conditions. In the interaction: material, ultrasonic excitation, and toothbrushing test, a significant statistical difference was observed (p=0.004) which was due to the toothbrushing test and not to the use of ultrasonic waves. The mean of weigh loss was 0.45mg for Fuji IX GP with ultrasound excitation, and 0.61mg without this procedure; Ketac Molar Easymix showed 0.27mg and 0.16mg respectively. However, there was no statistica... (Complete abstract, click electronic access below) / Mestre

Este estudo in vitro teve como objetivo a comparação de diferentes protocolos para fotoativação de restaurações em resina composta por meio de teste de microdureza e análise da adaptação marginal com microscopia eletrônica de varredura. Foram confeccionadas restaurações de 2mmx4mmx2mm com a resina composta Premisa (Kerr) em 30 dentes bovinos. Durante o procedimento restaurador, o método de fotoativação teve variação, sendo um grupo ativado com o método contínuo (grupo controle) durante 20 segundos, utilizando o fotoativador Elipar Freelight 2; outro grupo utilizou o mesmo equipamento fotoativador, com variação da distância da ponta ativadora, a fim da promoção de um método soft-start (grupo soft-start), tendo distância inicial de 6mm por 20 segundos, seguido de distância mínima por mais 10 segundos; e um terceiro grupo utilizou a tecnologia PLS (grupo DEMI), fornecida pelo equipamento DEMI, que fornece uma luz pulsada e permite a polimerização adequada de uma resina composta em 5 segundos (segundo o fabricante). Após 24 horas de restaurados, mantidos em estufa a 37ºC, os dentes foram seccionados no sentido inciso cervical resultando em 60 corpos de prova, sendo metade deles utilizados em cada teste (N=10). As metades tiveram as superfícies correspondentes ao corte transversal lixadas até a obtenção de superfícies planas e polidas, sendo que 30 delas foram selecionadas aleatoriamente para o teste de microdureza Knoop em 3 diferentes profundidades e as outras 30 metades foram replicadas em resina epóxica para leitura em microscopia eletrônica de varredura. Com as imagens obtidas foram feitas medidas de porcentagem de perímetro de restauração com desadaptação marginal e largura da maior fenda encontrada. Foram aplicados testes estatísticos de análise de variância split plot para os resultados de dureza e one way para a adaptação marginal. Em relação à dureza, os testes mostraram não haver diferença estatisticamente significante entre os grupos avaliados, enquanto houve diferença nas diferentes profundidades (p<0,0001), sendo a dureza na região profunda maior do que na média, que foi maior do que na superficial. Para a adaptação marginal, os testes não mostraram diferença estatisticamente significante para a largura de maior fenda encontrada entre os grupos controle e DEMI, somente o grupo soft-start foi diferente dos outros grupos (p=0,0064), tendo ele os menores valores. Apesar de a porcentagem de perímetro com desadaptação marginal ter apresentado valores com grandes valores de desvio padrão, foi encontrada diferença estatisticamente significante entre os grupos controle e DEMI, mas não entre os grupos DEMI e soft-start. O teste de correlação de Pearson demonstrou correlação linear positiva entre largura da maior fenda encontrada e porcentagem de perímetro com desadaptação marginal. Foi possível a conclusão de que o protocolo de fotoativação soft-start melhorou a adaptação marginal das restaurações em resina composta, sem alterar a dureza do material; o equipamento fotoativador DEMI, com a utilização da tecnologia PLS, teve resultados sem diferença estatisticamente significante na avaliação da adaptação marginal, quando comparados ao grupo controle; nenhum dos protocolos de fotoativação testados causou alteração na dureza da resina composta fotoativada, quando comparadas entre si, havendo aumento dessa propriedade conforme houve aumento da profundidade. / This in vitro study aimed to compare different protocols for the photoactivation of composite resin restorations using microhardness test and analysis of marginal adaptation with scanning electron microscopy. Restorations with 2mmx4mmx2mm were made in 30 bovine teeth using the composite resin Premisa (Kerr). During the restorative procedure, the polymerization method had change, being one group activated with the continuous method (control group) for 20 seconds using the curing unit Elipar Freelight 2, another group used the same curing unit equipment, varying the distance from the activator tip in order to promote a soft-start method (soft-start group), with initial distance of 6mm for 20 seconds, followed by minimum distance for 10 seconds, and a third group used technology PLS (DEMI group) supplied from the DEMI, which provides a pulsed light and allows an adequate polymerization of a resin composite in 5 seconds (according to manufacturer). 24 hours after restoration, maintained at 37 ° C, the teeth were sectioned incisocervical towards resulting in 60 specimens, half of them being used in each test (N = 10). The halves were sanded on the transversal section surfaces to obtain flat and polished surfaces, of which 30 were randomly selected for Knoop microhardness testing in 3 different depths and the other 30 halves were replicated in epoxy resin for microscopy scanning electron reading. Measures of percentage of perimeter with marginal desadaptation and width of the largest slot found were made with the obtained images. Split plot analysis of variance tests were applied to hardness results and one way to the marginal adaptation. Regarding the hardness, tests showed no statistically significant difference among the groups, while there were differences at different depths (p<0,0001), being the hardness of the deep region highest than the medium, which was higher than the superficial. For marginal adaptation, tests showed no statistically significant difference for the width of the largest slot found between the control group and DEMI, only the soft-start group was different from the other groups (p=0,0064), having the lowest values. Despite the large standard deviations shown by the percentage of perimeter with marginal desadaptation, statistically significant difference was found between the control and DEMI, but not between groups DEMI and soft-start. The Pearson correlation test showed positive linear correlation between the width of the largest slot found and the percentage of perimeter with marginal desadaptation. It was possible to conclude that the soft-start photoactivation protocol improved the marginal adaptation of composite resin restorations, without changing the hardness of the material; DEMI curing unit equipment, using PLS technology, showed no statistically significant difference in the evaluation of marginal adaptation, comparing with the control group; none of the protocols tested photoactivation caused change in hardness of composite resin when compared to each other, with an increase of this property as the depth increased.

Orientador: Mario Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T10:42:08Z (GMT). No. of bitstreams: 1 Alonso_RobertaCarolineBruschi_D.pdf: 2828251 bytes, checksum: 644a34bfa8b27efb0da35a9b5d7f13de (MD5) Previous issue date: 2007 / Resumo: A formação de fendas em restaurações de compósito foi caracterizada neste estudo, abrangendo-se técnicas de avaliação, fatores modificadores e a relação com a resistência de união das restaurações à estrutura dental. No capítulo 1, objetivou-se validar a técnica do corante para avaliação das fendas através da comparação com a observação em Microscopia Eletrõnica de Varredura (MEV). Vinte incisivos bovinos foram selecionados e desgastados até expor uma área plana em dentina, onde duas cavidades foram preparadas e restauradas com o compósito Filtek 2250 ou Filtek Flow. As amostras foram polidas e réplicas foram obtidas em resina epóxica. As réplicas foram observadas em MEV para determinar a porcentagem de fenda ao longo da margem cavitária. Na técnica do corante, Caries Detector (Kuraray) foi aplicado sobre as restaurações durante 5s. A imagem digital das restaurações coradas foi analisada com o software Image Tool para determinar a porcentagem de fendas. Os dados foram submetidos a ANOVA e teste de correlação de Pearson. Filtek Flow apresentou 35,54% e 33,52%, e Filtek 2250 26,68% e 29,11% de fendas, quando avaliadas em MEV e pela técnica do corante, respectivamente. Não houve diferença significativa entre os compósitos independente do método de avaliação, havendo forte correlação positiva (r=0,83) entre eles. Concluiu-se que a técnica do corante pode ser utilizada para avaliação das fendas com confiabilidade dos resultados. No capítulo 2, o efeito de métodos de fotoativação modulados na' adaptação marginal e intema de restaurações confeccionadas com diferentes compósitos foi determinado. Sessenta terceiros molares foram selecionados, seccionados (2 fragmentos) e tiveram a superfície vestibular ou palatina ou lingual desgastada para expor uma área plana em esmalte, onde uma cavidade foi confeccionada. Os dentes foram distribuídos em 12 grupos (n=lO), segundo o compósito restaurador (Filtek 2250, Herculite XRV e Heliomolar) e o método de foto ativação (Luz continua; Soft-Start; Pulse delay; Luz intermitente). O teste de adaptação marginal (técnica do corante) foi conduzido da mesma maneira descrita anterionnente. Após, os espécimes foram seccionados dividindo a restauração em 4 fatias, que foram coradas e o mesmo procedimento de avaliação da adaptação marginal foi realizado para determinar a adaptação intema. Assim, põde-se observar que todas as restaurações apresentaram perfeito selamento das margens extemas. Considerando as fendas intemas, os métodos modulados geraram redução significativa nas fendas quando comparados à luz contínua, independe do compósito empregado. Filtek 2250 apresentou a melhor adaptação interna, independente do método de fotoativação. A interação tipo de compósito e método de fotoativação não foi significativa. Conclui-se que os métodos de fotoativação modulados são eficientes na redução da formação de fendas internas e que podem ser indicados para a prática clínica, independente do compósito empregado. No capítulo 3, o objetivo foi relacionar a resistência da união à adaptação marginal e interna de restaurações fotoativadas por diferentes métodos. A resistência da união foi mensurada em cavidades tronco-conicas confeccionadas em dentes bovinos através do teste push-out (Instron). A adaptação marginal e interna das restaurações foi verificada da mesma maneira descrita anteriormente. Em ambos os testes, as cavidades foram restauradas com o compósito Esthet-X, sendo as amostras distribuídas em 5 grupos (n=10), de acordo com o método de fotoativação: G 1 - Luz contínua; G2 - Luz contínua baixa intensipade; G3 - Soft-start; G4 - Luz Intermitente; G5 - Pulse Delay. A dose de energia foi padronizada em 14J. Os dados foram submetidos a ANOVA e teste de Tukey. Considerando resistência da únião, G5 (7,2 MPa) apresentou resultados significativamente melhores que G 1 (4,6 MPa). G2, G3 e G4 tiveram médias intermediárias, não havendo diferenças significativas entre esses grupos e entre eles e G 1 ou G5. Considerando adaptação marginal, não houve diferença significativa entre os grupos. Na adaptação interna (que incluía o substrato dentinário), o resultado foi inverso ao do teste de resistência de união, ou seja, G5 (2,8%) teve menor média de fendas que G 1 (10,1%). Concluiu-se que a modulação da energia luminosa pode acarretar em aumento da resistência da união e redução na formação de fendas internas, havendo relação inversa entre resistência da união e formação de fendas internas / Abstract: Gap formation in composite restorations has been characterized in this dissertation by way of evaluation techniques, modifying factors and the relationship between bond strength of the restorations and the dental structure. In Chapter 1 the objective was to compare the dye staining technique to Scanning Electron Microscopy (SEM) evaluation of gap formation in order to validate the dye technique. Twenty bovine incisors were selected and ground so as to expose a flat dentin area in which two circular cavities were prepared and restored using Filtek 2250 or Filtek Flow. The specimens were polished and replicas were obtained in epoxy resin. Replicas were observed in SEM to determine the percentage of gap fonnation in the margins of the restorations. In dye staining technique, the Caries Detector was applied on each restoration for 5 seconds. Digital images of the stained restorations were analyzed using Image Tool to determine gap percentage. Data were submitted to ANOVA and Pearson's correlation. Filtek Flow showed 35.54% and 33.52% of gap and Filtek 2250 showed 26.68% and 29.11%, when evaluated using SEM and Dye staining technique, respectively. There was no difference between the composites, regardless of the evaluation technique. There was a strong positive correlation (r=0.83) between the results obtained through the tested methods to assess marginal gap. This led to the conclusion that dye staining technique can be reliably employed to evaluate the gap fonnation in composite restorations. Chapter 2 aims at determining the effect of modulated photoactivation methods on gap fonnation of restorations using different composites. Sixty third molars were selected, sectioned (2 fragments) and ground so as to expose a flat enamel area in which a cavity was prepared. The specimens were distributed into twelve groups (n=10), according to the restorative composite (Filtek 2250, Herculite XRV, and Heliomolar) and the photoactivation method (Continuous Light, Soft-Start, Pulse Delay, and Intermittent Light) applied. Marginal adaptation test was conducted in the same way described before (dye staining technique). The specimens were then sectioned in 4 slices, all of which were stained, and the same evaluation procedure used to determine marginal adaptation was employed to evaluate internal gap fonnation. All restorations showed perfect sealing of the enamel outer margins. With regards to internal adaptation, modulated photoactivation methods showed a significant reduction on gap fonnation when compared under continuous light, regardless of the composite. Filtek 2250 showed the best internal adaptation, regardless of the photoactivation method. The interaction between restorative composite and photoactivation method was not significant. The conclusion was that modulated photoactivation methods decrease the internal gap formation of composite restorations and should thus be encouraged on clínical practice, regardless of the type of composite. In Chapter 3, the aim was to evaluate the relationship between bond strength and marginal and internal adaptation of composite restorations photocured by different methods. Bond strength was measured in conical cavities prepared in bovine incisors using push-out test (Instron). Marginal and internal adaptation testswere conducted in the same way as before (dye staining technique). For both tests, cavities were filled with Esthet X resin composite. The specimens were distributed into 5 groups (n= 1 O) according to photoactivation method: G 1 - continuous light; G2 low intensity continuous light; G3 - soft start; G4 - intermittent light; G5 - pulse delay. 14J was the standard energy dose. Data were submitted to ANOVA and Tukey's test. Regarding bond strength, G5 (7.2 MPa) was statistically superior to Gl (4.6 MPa). G2, G3 and G4 showed intermediate mean values, which were not different from each other or from G 1 or G5. Regarding marginal adaptation, there was no statistical difference among the groups. Internal adaptation results (that included dentin substrate) were the opposite of bond strength results. G5 (2.8%) showed a reduction on gap formation when compared to Gl (10.1%). In conclusion, it may be said that the modulated photocuring methods can increase bond strength while decreasing internal gap formation. An opposite relationship was observed regarding push-out bond strength and internal adaptation of composite restorations / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T10:33:11Z (GMT). No. of bitstreams: 1 Correr-Nolasco_GiseleMaria_D.pdf: 6596776 bytes, checksum: 63d7c0e65d2597ab8ee9132bae660714 (MD5) Previous issue date: 2007 / Resumo: A cavidade bucal é considerada um ambiente agressivo onde a estrutura dentária e os materiais restauradores estão constantemente sujeitos a desafios térmicos, mecânicos e químicos. A associação destes fatores está diretamente relacionada à longevidade/estabilidade das restaurações, bem como à preservação da estrutura dentária. A exposição da estrutura dentária e dos materiais restauradores resinosos aos agentes da dieta pode causar erosão dental, amolecimento e aumento da rugosidade de restaurações resinosas, deixando-as mais susceptíveis ao desgaste. Dessa forma, os objetivos desta tese fundamentada em três capítulos foram: (1) avaliar o efeito do armazenamento em longo prazo em diferentes soluções simuladoras da dieta na rugosidade superficial de materiais restauradores resinosos; (2) avaliar o efeito da associação dos desafios erosivo e abrasivo no desgaste do esmalte decíduo e permanente; (3) avaliar o efeito da associação dos desafios corrosivo e abrasivo no desgaste de materiais restauradores resinosos. No capítulo 1, sessenta amostras de diferentes materiais restauradores (Filtek Z250, Esthet X, Filtek Flow, Dyract AP e Vitremer) foram armazenadas em 5 líquidos simuladores da dieta (água destilada, ácido lático, ácido cítrico, refrigerante a base de cola (Coca-Cola) e álcool) por até 6 meses. A rugosidade superficial das amostras foi mensurada após o polimento (baseline), 1 semana, 1 mês, 3 meses e 6 meses de armazenamento. Houve aumento significativo na rugosidade superficial apenas para Esthet X armazenado em Coca-Cola e em ácido cítrico após 1 e 3 meses, respectivamente; e para Dyract AP armazenado em água destilada após 6 meses. No capítulo 2, foram obtidas amostras planas de esmalte decíduo e permanente (n=10), as quais foram submetidas ao desgaste (100.000 ciclos a 1,9 Hz) em meio neutro (água deionizada) e meio ácido (ácido cítrico). Antes e após o desgaste, as amostras foram analisadas em perfilÃ'metro (MTS 3D Profiler). A alteração do volume e a profundidade máxima do desgaste foram quantificadas utilizando o software Ansur 3D. O esmalte decíduo apresentou maior desgaste que o esmalte permanente, independentemente do meio. O meio ácido proporcionou maior desgaste do que o meio neutro (p<0,05). Diferença significativa entre meio neutro e ácido foi observada apenas para o esmalte decíduo. No capítulo 3, dez amostras de cada material [Filtek Supreme (S), Point 4 (P), Dyract AP (D) e Fuji II LC (F)] foram confeccionadas e submetidas ao desgaste (100.000 ciclos a 1,9 Hz) em meio neutro (água) e meio ácido (ácido cítrico). Antes e após o desgaste, as amostras foram analisadas em perfilÃ'metro (MTS 3D Profiler). A alteração do volume e a profundidade máxima do desgaste foram quantificadas utilizando o software Ansur 3D. Diferença significativa no desgaste dos materiais foi observada (S=P<D<F), independentemente do meio. O meio ácido gerou maior desgaste nos materiais comparado ao meio neutro (p<0,05). Não houve diferença significativa entre o meio neutro e meio ácido para todos os materiais quando analisados individualmente. Concluindo, a degradação química dos materiais restauradores resinosos é material e solução dependente. O desafio ácido aumenta a susceptibilidade ao desgaste dos materiais restauradores resinosos e do esmalte dental, especialmente esmalte decíduo / Abstract: The oral cavity can be considered a hostil environment. The dental structure and the restorative materials are constantly subjected to thermal, mechanical and chemical stresses. The interplay of these factors is directly related with the longevity/stability of the restorative treatment, and also with the dental structure preservation. The effect of diet constituents on dental structure and restorative materials can be dental erosion, softening and roughening of resin-based restorations. These phenomena increase the susceptibility of tooth and material wear. This way, the objectives of this work are: (1) to evaluate the effect of long-term storage in different food-simulating media on surface roughness of resin-based materials; (2) to evaluate the effect of the association of erosive and abrasive challenges on deciduous and permanent wear; (3) to evaluate the effect of the association of corrosive and abrasive challenges on resin-based materials wear. In the first chapter, sixty specimens of different material categories (Filtek Z250, Esthet X, Filtek Flow, Dyract AP, and Vitremer) were stored in five food-simulating solutions (distilled water, lactic acid, citric acid, carbonated soft drink (Coca-Cola), and ethanol) for 6 months. The surface roughness was measured after polishing (baseline), 1 week, 1, 3, and 6 months of storage. Significant difference was observed for Esthet X specimens stored in Coca-Cola and in citric acid after 1 and 3 months, respectively; and for Dyract AP specimens stored in distilled water after 6 months. In the second chapter, deciduous and permanent flat enamel specimens (n=10) were obtained. The specimens were subjected to the wear test (100,000 cycles at 1.9 Hz) in neutral (water) or acidic (citric acid) media. Specimens were profiled before and after the wear test using the MTS 3D Profiler. Volume loss and maximum depth were quantified by the Ansur 3D software. Deciduous enamel showed more wear than permanent enamel, regardless the media. The acidic media produced more wear than the neutral media (p<0.05). Significant difference was observed between neutral and acidic conditions only for deciduous enamel. In the third chapter, ten specimens were produced from each material [Filtek Supreme (S), Point 4 (P), Dyract AP (D), and Fuji II LC (F)]. The specimens were submitted to the wear test (100,000 cycles at 1.9 Hz) in neutral (water) and acidic (citric acid) media. Specimens were profiled before and after the wear test using the MTS 3D Profiler. Volume loss and maximum depth were quantified by the Ansur 3D software. Significant differences were observed for the material wear (S=P<D<F), regardless the media condition. Acidic media produced more wear than neutral media (p<0,05). There were no significant differences between neutral and acidic condition for all materials, when individually analyzed. Concluding, the chemical degradation of resin-based materials is material and solution dependent. The acidic media produced more material and tooth wear, especially for deciduous enamel / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Avaliou-se a resistência à fratura de dentes pré-molares, com e sem bisel no ângulo cavo-superficial, restaurados com resina composta. Noventa dentes prémolares superiores foram divididos em 9 grupos. O grupo 1, considerado controle positivo, constituiu-se de dentes hígidos. Os grupos de 2 a 9 receberam cavidades de Classe II MOD, com medidas padronizadas. Os grupos de 6 a 9, além das cavidades, tiveram os tetos das câmaras pulpares removidos. Para os grupos 2, 3, 6 e 7, o ângulo cavo-superficial apresentou-se nítido e sem bisel; grupos 4 e 8, bisel côncavo em toda cavidade; grupos 5 e 9, bisel apenas na porção oclusal da cavidade. Os dentes dos grupos 2 e 6 não foram restaurados, sendo considerados controle negativo. Para os demais grupos, procedeu-se a restauração das cavidades com sistema restaurador adesivo pela técnica direta. Todos os espécimes foram avaliados quanto a resistência à fratura, em uma maquina de teste universal (Emic - DL 2000), com célula de carga de 500Kgf, regulada a uma carga máxima de 450Kgf, com uma leitura mínima de 0,05Kgf de precisão. Os resultados foram submetidos à análise de variância a um critério e ao teste de Tukey para comparação entre os grupos. Constatou-se que houve diferença significante entre os grupos estudados, quando considerados os diferentes tratamentos do ângulo cavo-superficial (variável independente) e a resistência à fratura obtida (variável dependente) (p<0,05). A remoção de tecido dentário pela confecção de cavidades diminuiu a resistência à fratura do órgão dentário, sendo que em intervenções mais extensas, com a remoção de estrutura de reforço, como o teto da câmara pulpar, esta resistência se apresentou ainda menor. A confecção de bisel em todo o ângulo cavo-superficial, em cavidades de Classe II, proveu um aumento significante da resistência à fratura, quando comparado aos dentes que apresentaram o ângulo cavo-superficial nítido e sem bisel, tanto em dentes com ou sem remoção do teto da câmara pulpar. Além disso, dentes que apresentaram bisel em todo o ângulo cavo-superficial de cavidades de Classe II, tanto com ou sem intervenção endodôntica, mostraram os melhores padrões de fratura, preservando quase que em sua totalidade a integridade do remanescente dentário. / The fracture resistance of upper premolar teeth with and without cavosurface bevel, restored with composite resin material was evaluated. Ninety upper premolar teeth were divided into 9 groups. The group 1, considered as a positive control, was composed of sound teeth. Groups 2 to 9 receive Class II MOD preparation cavities with standardized measures. Groups from 6 to 9 had the roof of the pulp chamber removed. In groups 2, 3, 6, and 7, the cavosurface angle was evident and without bevel; groups 4 and 8, a concave bevel around the entire cavity; groups 5 and 9, the bevel was only placed in the oclusal portion of the cavity. Teeth in groups 2 and 6 were not restored, and considered as negative controls. In the other groups, cavities were directly restored with an adhesive resin system. All specimens were evaluated until load to fracture in a Universal Testing Machine (Emic DL 2000), with a load cell of 500Kgf, maximum load of 450Kgf, and 0,05kgf of standard error. Results were submitted to one-way analysis of variance and Tukey\'s test for group comparisons. There was a significant difference among the studied groups regarding the different treatments on the cavosurface angle (independent variable) and the fracture resistance (dependent variable) (p<0.05). Removal of tooth structure through cavity preparation diminished the fracture resistance values, being that in more extensive preparation (removal of the roof of pulp chamber), this value was lower. The bevel placed around the entire cavosurface angle in Class II cavities significantly increased the fracture resistance, when compared to teeth with a clear cavosurface angle but without bevel, either in teeth with or without removal of the roof of pulp chamber. Besides, teeth with bevel around the entire cavosurface angle with or without endodontic therapy showed the best fracture patterns, almost completely preserving tooth integrity.

Neste estudo, foi avaliada a resistência ao desgaste abrasivo de uma resina composta, através de três diferentes métodos: do disco retificado, por escovação e do nanodurômetro. Nos dois primeiros métodos, foram utilizados 20 espécimes da resina Filtek Z250 (10 da cor Incisal e 10 da cor C4, ambos fotopolimerizados por 30 segundos cada) e 10 de polimetilmetacrilato (PMMA), atuando estes últimos como padrão de referência. Para os ensaios com o nanodurômetro, foi utilizado apenas um espécime de cada cor, assim como um único de PMMA, em cujas superfícies planas foram efetuadas sete medições, o que foi considerado equivalente a sete espécimes. No método do disco retificado, cada espécime de resina composta era confeccionado diretamente numa cavidade semicircular, localizada na periferia de um disco-suporte; os espécimes de PMMA consistiam em discos constituídos exclusivamente por este material; o desgaste de cada espécime era promovido por um disco de porcelana e seu conseqüente deslocamento era detectado por um palpador; assim, a taxa de desgaste era estabelecida, expressa em milímetros cúbicos por newton por segundo (mm3/N.s). No método de escovação, cada espécime cilíndrico ficava preso numa placa metálica, a qual era fixada no interior da máquina de escovação; sua perda de massa (em miligramas) era verificada através de uma balança analítica. No método do nanodurômetro, existiu apenas um espécime ci líndrico para cada condição, em cuja face plana superior eram feitos sete sulcos (equivalentes a sete espécimes); o coeficiente de atrito permitia estabelecer a respectiva resistência ao desgaste. Para cada método utilizado, os dados foram tratados estatisticamente, através de análise de variância (ANOVA) e de teste de Tukey. Pôde-se concluir que, através do disco retificado, a taxa de desgaste (em mm3/N.s) dos materiais foi: Incisal (0,6807) > C4 (0,5012) > PMMA (0,1439); que, através da escovação, a taxa de desgaste (em mg) foi de 5,40 para Incisal, de 9,35 para C4 e de 5,88 para PMMA, sem diferença significante apenas entre Incisal e PMMA, os mais resistentes; e que, através do nanodurômtero, a resistência ao desgaste abrasivo (expressa pelo coeficiente de atrito) foi de 0,207 para Incisal, de 0,214 para C4 e de 0,281 para PMMA, sem diferença significante agora apenas entre Incisal e C4, os menos resistentes. / Abrasive wear of a composite resin, using three different methods (ground disc, toothbrushing and nanodurometer). The aim at this study was to evaluate the resistance to abrasive wear of a composite resin, using three different methods: ground disc, toothbrushing and nanodurometer. At the first two methods were employed 20 specimens of Filtek Z250 composite resin (10 of Incisal and 10 of C4, both the colors cured for 30 seconds each one) and 10 of polymethylmethacrylate (PMMA), the latter acting as a reference standard. For the tests with the nanodurometer it was used only one specimen of each color, as well as just one of PMMA, in whose flat surfaces seven measurements were made, what was considered equivalent to seven specimens. At the ground disc method, each composite resin specimen was directly made on a semicircular cavity located on the periphery of a supporting disc; PMMA specimens consisted of discs made up exclusively with this material; the wear of each specimen was promoted by a ceramic disc and its consequent displacement was detected by a sensor; thus, the wear rate was established, expressed in cubic millimeters per newton per second (mm3/N.s). At the toothbrushing method, each cylindrical specimen was trapped in a metal plate, which was fixed inside the machine brushing; its weight loss (in milligrams) was verified by an analytical balance. At the nanodurometer method, there was only one cylindrical specimen for each condition, in whose flat upper face seven grooves were made (what was equivalent to seven specimens); the coefficient of friction was used to establish its wear resistance. For each method, data were statistically analyzed by ANOVA and Tukey\'s test. It could be concluded that, by ground disc method, materials wear rate (in mm3/N.s) was Incisal (0.6807) > C4 (0.5012) > PMMA (0.1439); by brushing method, materials wear rate (in mg) was 5.40 for Incisal, 9.35 for C4 and 5.88 for PMMA, without significant difference only between Incisal and PMMA (the toughest); by nanodurometer method, abrasive wear resistance (expressed by the coefficient of friction) was 0.207 for Incisal, 0.214 for C4 and 0.281 for PMMA, now without significant difference just between Incisal and C4, the least resistant.

A importância das restaurações provisórias no tratamento reabilitador oral é inquestionável. Os materiais utilizados para a execução destas restaurações, entretanto, são críticos com relação à resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. A proposta deste trabalho foi determinar o efeito de diversos reforços sobre a resistência flexional, o módulo de elasticidade e o tipo de fratura apresentados por espécimes confeccionados em uma resina poli(metilmetacrilato) (PMMA), quando submetidos a um teste de carga de três pontos. Sete tipos de reforços constituíram os grupos experimentais com dez espécimes cada: um fio de aço com 0,7 mm de diâmetro; um fio de amarrilho trançado; uma fibra de vidro trançada Interlig® (Angelus®); uma fibra de vidro entrelaçada Splint-It!® (Jeneric-ron®); uma fibra de vidro unidirecional Fibrante® (Angelus®); uma fibra de poli(etileno) Connect® (Kerr®) e uma fibra cerâmica flexível GlasSpan® (GlasSpan®). O grupo controle, também com dez amostras, foi composto de espécimes não reforçados. A confecção dos espécimes, o ensaio mecânico e cálculo da resistência flexional e do módulo de elasticidade foram realizados seguindo norma ISO 10477 – modificada. A análise dos resultados (ANOVA, p < 0,05), para ambas as propriedades, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados com fio de aço com 0,7 mm; fibra Interlig® e fibra Connect® aumentaram significantemente a resistência flexional, e que os grupos reforçados com fio de aço com 0,7 mm; fibra Interlig®; fibra Splint-It!®; fibra Connect® e fibra GlasSpan®, aumentaram o módulo de elasticidade, em relação ao grupo controle. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial. / Provisional restorations are essential components of oral rehabilitation treatment. The strength and durability features are, however, critical whe n long-term treatment is needed. The aim of this work was to measure the flexural strength, the elastic modulus and the type of fracture of poly (methyl methacrylate) (PMMA) resin specimens when submitted to a three-point-bend test. Seven types of reinforcements constituted the experimental groups with ten specimens each: a 0.7 mm of diameter wire; an orthodontic braided wire; a braided fiberglass Interlig® (Angelus®); an woven fiberglass Splint-It!® (Jeneric-Pentron®); a roving fiberglass Fibrante® (Angelus®); a braided poly(ethylene) fiber Connect® (Kerr®) and a flexible ceramic fiber GlasSpan® (GlasSpan®). The control group, also with ten samples, included not reinforced specimens. All specimens were made and test according to modified ISO specification No. 10477. The analysis of the results (ANOVA, p < 0.05), for both properties, showed significant differences between groups. Tukey\'s test detected higher figures for groups reinforced with wire of 0.7 mm of diameter wire; Interlig® and Connect® when flexural strength was concerned. Groups reinforced with a wire 0.7 mm of diameter; Interlig®; Splint-It!®; Connect® and GlasSpan®, increased the elastic modulus, when compared to the control group. The fractures analysis contributed with the elaboration of new index system dividing them in four types: Absent, Partial, Total Not Separated and Total Separated. It was observed that the reinforced specimens fractures were more favorable, occurring, predominantly, in the Absent and Partial types.

Submitted by Rosangela Silva (rosangela.silva3@unioeste.br) on 2018-05-15T19:35:27Z No. of bitstreams: 2 Saulo Vinicius da Rosa.pdf: 2244692 bytes, checksum: e13fed6b2f75e2fa2861bf064a121ca7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-05-15T19:35:27Z (GMT). No. of bitstreams: 2 Saulo Vinicius da Rosa.pdf: 2244692 bytes, checksum: e13fed6b2f75e2fa2861bf064a121ca7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-03-03 / Bulk fill resins can be used as dentin replacements, requiring coating by another composite resin, such as a nano-hybrid resin, or they can be used without the need for a new composite resin for their protection. The objective of this work was to evaluate the bond strength of repairs made between different composite resins, after aging in different solutions. Five composite resins were used, one conventional and four bulk fill composites. 2x2x5 mm CP were made in silicone mold and aged for 30 days, after which the resins were given the surface treatment and soon after the repair, becoming a CP with 2x2x10mm. All the resins were combined. The mean values obtained for each test specimen were submitted to the Shapiro Kruskall Wallis test, followed by the Dunn test, p <0.05. The results showed that, after aging in distilled water, Aura bulk fill as base showed statistical differences when compared to the composite resins Z350 (1.27 + 0.95) and Tetric Ceram bulk fill (3.72 + 1.74), the composite resin Tetric Ceram bulk fill used as a base showed that there was statistical difference when Filtek bulk fill composite resin 4,81 (+1,20) was used and when Z350 resin (2.22 + 0.63) and Tetric Ceram bulk fill (2.54 + 0.52). After aging in water / ethanol solution, no statistically significant differences were found between all possible combinations. After aging in nitric acid solution, when Aura bulk fill was used as base there were statistical differences between the repair with Tetric Ceram bulk fill (4.02 + 0.82) and Z350 (1.71 + 1.09 ), when Filtek bulk fill used as base there were statistical differences between Z350 (2.30 + 0.62) and Filtek bulk fill 4.02 (+1.85) used for the repair, with Tetric ceram bulk fill as base there were statistical differences when compared to the composite resin Filtek bulk fill 4,04 (+1,07) and Z350 (1,99 + 0,76). According to the results obtained it was possible to verify that, in the majority of the comparisons made among the composite resins evaluated in this study, the composite resins bulk fill obtained better values of bond strength when the composite resins themselves were united bulk fill and the worst values when they received the repair with the composite resin when immersed in acidic solutions and distilled water, it was not possible to observe statistically significant differences when immersing in water / ethane. / As resinas “bulk fill” podem ser utilizadas como substitutas da dentina, necessitando de recobrimento por outra resina composta, como uma resina nano- híbrida, ou ainda podem ser utilizadas sem a necessidade de uma nova resina composta para sua proteção. O objetivo desse trabalho foi avaliar a resistência de união de reparos confeccionados entre diferentes resinas compostas, após envelhecimento em diferentes soluções. Foram utilizadas cinco resinas compostas, sendo uma convencional e quatro resinas compostas “bulk fill”. Foram confeccionados CP de 2x2x5 mm em molde de silicone e envelhecidas por 30 dias, após esse período as resinas receberam o tratamento de superfície e logo após o reparo, tornando-se um CP com 2x2x10mm. Todas as resinas foram combinadas entre si. Os valores médios obtidos para cada corpo de prova foram submetidos ao teste de Shapiro Kruskall Wallis, seguido do pós teste de Dunn, p < 0,05. Os resultados mostraram que após o envelhecimento em água destilada, a Aura bulk fill como base mostrou diferenças estatísticas quando comparadas as resinas compostas Z350 (1,27+0,95) e Tetric Ceram bulk fill (3,72+1,74), a resina composta Tetric Ceram bulk fill utilizada como base mostrou que houve diferença estatística quando utilizada a resina composta Filtek bulk fill 4,81(+1,20) e quando utilizada a resina Z350 (2,22+0,63) e Tetric Ceram bulk fill (2,54+0,52). Após o envelhecimento em solução água/etanol não foram encontradas diferenças estatisticamente significantes entre todas as combinações possíveis. Após o envelhecimento em solução de ácido nítrico, quando a Aura bulk fill foi utilizada como base houve diferenças estatísticas entre o reparo com a Tetric Ceram bulk fill (4,02+0,82) e a Z350 (1,71+1,09), já quando Filtek bulk fill utilizada como base houve diferenças estatísticas entre a Z350 (2,30+0,62) que e a Filtek bulk fill 4,02(+1,85) usadas para o reparo, com a Tetric ceram bulk fill como base houve diferenças estatísticas quando comparadas a resina composta Filtek bulk fill 4,04(+1,07) e a Z350 (1,99+0,76). De acordo com os resultados obtidos foi possível verificar que, na maioria das comparações realizadas entre as resinas compostas avaliadas nesse estudo, as resinas compostas bulk fill obtiveram melhores valores de resistência a união quando unidas as próprias resinas compostas bulk fill e os piores valores quando receberam o reparo com a resina composta quando imersas em soluções ácidas e na água destilada, já na imersão em água/etano não foi possível observar diferenças estatisticamente significantes.

O número de idosos vem crescendo em todo o mundo devido a um aumento na expectativa de vida e diminuição da taxa de natalidade. Concomitantemente, os avanços da ciência e da tecnologia na área da saúde poderiam contribuir para a manutenção de dentes por períodos mais prolongados, gerando um crescente número de idosos com dentes na boca. O objetivo dessa pesquisa foi conhecer a condição dentária e restauradora de pacientes idosos de um centro público que oferece tratamento dentário em São Paulo, Brasil. Materiais e métodos: Foram avaliados pacientes (60 anos ou mais) que compareceram ao serviço de triagem do CRI-Norte. Todos os pacientes foram entrevistados inicialmente (dados pessoais, história odontológica, hábitos de higiene). Pacientes dentados foram submetidos a um exame clínico: dentes perdidos, condição dos dentes e restaurações presentes. Para comparação foram utilizados os testes ANOVA e Qui-quadrado (p<0.05). Resultados: Foram avaliados 177 pacientes desdentados (54%) e 148 dentados, sendo 66% do sexo feminino e 34% masculino. 49,8% possuíam entre 60-69 anos e 63% nasceram na Região Sudeste. 73% dos pacientes não se consultavam com um dentista durante a infância, nem possuíam o hábito de realizar consultas periódicas durante a vida adulta (72%). Pacientes dentados (20%) frequentaram o consultório odontológico mais regularmente que os desdentados (8%). 80% dos pacientes dentados relataram escovar os dentes de 1 a 2 vezes por dia e 64% não fazem uso do fio dental. 32% dos pacientes apresentavam entre 5 e 19 dentes e apenas 6,5% apresentavam mais de 20 dentes na boca. Dentre os pacientes desdentados, 70% eram mulheres e 30% eram homens. O CPOD encontrado foi de 26, com predominância do componente perdido (média=21). Dentes inferiores anteriores são os mais retidos pela população idosa (41%). 14,6% dos dentes avaliados apresentaram lesão cariosa (63% lesões coronárias e 37% radiculares). A face coronária mais atingida por cárie foi a mesial (27%). 33% dos dentes presentes apresentaram restaurações sendo 60% satisfatórias e 40% insatisfatórias. 41% das restaurações de amálgama apresentaram-se satisfatórias com diferença estatística comparada a resina composta (13%). Em relação às faces coronárias restauradas, a oclusal foi a que mais apresentou essa condição (31%). Os pré molares foram os dentes com mais restaurações radiculares (48%). 40% dos pacientes apresentaram lesão cervical não cariosa (54% das lesões ocorreram em dentes anteriores), Pré molares (38%) e incisivos (34%) são os dentes mais atingidos por esse tipo de perda de estrutura. Em relação ao desgaste incisal/oclusal, 73% dos pacientes apresentaram essa condição (98% das lesões ocorreram em dentes anteriores). Conclusão: Conclui-se que no serviço público o número de pacientes idosos totalmente desdentados é relevante. Uma pequena parcela dos pacientes apresenta mais que 20 dentes, sendo que muitas restaurações não apresentam-se satisfatórias. O amálgama é a restauração que mais se manteve satisfatoriamente. Uma maior atenção deve ser dada aos tratamentos realizados e à conservação deles na população idosa. / The number of elderly people is increasing all over the world due to increased life expectancy and decreasing birth rate. Simultaneously, the progress of science and technology in health could contribute to the maintenance of teeth in the mouth for longer periods, generating an increasing number of older patients with teeth in the mouth.Objective: Identify the restorative and dental status of elderly patients at a public service in Sao Paulo-Brazil. Methods: Patients (60 years or older) who attended the dental service of CRI-Norte, in São Paulo, Brazil were evaluated. They were submitted to an initial interview which consisted in: personal data, dental history and hygienic habits. Dentate patients were submitted to a clinical examination to evaluate the status of the remaining teeth and conditions of restorations. ANOVA and Chi-square tests (p <0.05) were used for comparison. Results: 177 edentulous and 148 dentate patients were evaluated (66% female and 34% male). 49.8% were 60-69 years old and 65% were born in Southeastern Brazil. 73% had not been to a dental office during childhood and 72% had not regularly been to the dentist\'s in adult life. 20% of dentate and 8% of edentulous attended a dental office regularly. 80% of dentate brushed their teeth 1-2x per day and 64% did not use dental floss. 32% of patients had 5-19 teeth and 6.5% had over 20 teeth. 41% were anterior mandibular teeth. The number of decayed, missing and filled teeth was 26, with prevalence of missing component (mean =21); 14,6% had caries (37% radicular). 33% of the teeth presented restorations (40% unsatisfactory). 41% of amalgam restorations were satisfactory with statistical difference from composite resin (13%). Pre molars were the most radicular restored teeth (48%) with statistical difference between other teeth. 40% of patients presented non-carious lesions; 73% presented incisal/occlusal wear (98% anterior teeth). Conclusion: The number of edentulous patients is relevant. Few patients have more than 20 teeth, and many restorations are not satisfactory. Amalgam is the material that presented the best survive hability. Greater attention should be given to the performed dental treatments and their conservation in the elderly population, increasing their quality of oral health.