Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T20:09:39Z (GMT). No. of bitstreams: 1 Salgueiro_MonicadaConsolacaoCanuto_M.pdf: 1786496 bytes, checksum: 328be71506e20df2b34115521d2da4f3 (MD5) Previous issue date: 2005 / Resumo: O objetivo deste trabalho foi avaliar a resistência à tração de pinos intra-radiculares estéticos, com diferentes formas, fixados com cimento resinoso dual com diferentes proporções de catalisador em relação a base. Foram utilizados 60 incisivos bovinos com dimensões semelhantes. A coroa foi separada da raiz através de um disco diamantado dupla face no comprimento de 16 mm a partir do ápice. Em seguida, todos os canais radiculares foram obturados e as raízes receberam uma marca a 2,0 mm simulando o limite amelo-cementário e uma camada de resina composta foi inserida na região apical da raiz para aumentar a retenção da mesma no bloco de resina de poliestireno durante o ensaio mecânico. As amostras foram distribuídas, aleatoriamente,em seis grupos experimentais (n=10), sendo que em 30 raízes foram fixados os pinos cônico liso e nas outras 30 raízes os pinos paralelo serrilhado.Para a cimentação dos pinos, as raízes foram desobturadas em 12mm com broca Gates Gliden n° 3 e para o preparo do canal foi usada a broca específica para cada pino. Em seguida, os pinos foram fixados aplicando-se o sistema adesivo Single Bond (3M) e o cimento resinoso dual Rely X (3M) com diferentes proporções de base/catalisador (b/c):G1 - pinos paralelo serrilhado cimentados na proporção 1:1, G2 - pinos paralelo serrilhado cimentados na proporção 1:2, G3 - pinos paralelo serrilhado cimentados na proporção 1:3, G4 - pinos cônico liso cimentados na proporção 1:1, G5 ¿ pinos cônico liso cimentados na proporção 1:2,G6- pinos cônico liso cimentados na proporção 1:3. Após armazenagem por uma semana em estufa a 37°C, as amostras foram submeti.das ao ensaio de resistência à tração numa Instron a velocidade de 1mm/mim, até o deslocamento do pino. Os dados foram submetidos à análise de variância que evidenciou diferença estatística significativa para os fatores Pinos e Proporção, não havendo diferença estatística para a interação pino x proporção. Para melhor evidenciar esse resultado foi aplicado para cada fator o teste de Variação Múltipla de Tukey (LSMEANS) que mostrou que quando se triplicou a proporção do catalisador em relação à base a média de resistência à tração foi superior com diferença estatística significativa para a média da proporção 1:1. Em relação ao fator pino, os pinos paralelo serrilhado apresentaram a maior média de resistência à tração independente da proporção base/catalisador utilizada / Abstract: The objective of this work was to evaluate the tensile strenght of aesthetic bolts intra-radiculares, with different forms, settled with dual resinous cement with different ratios of catalyser in relation the base. 60 bovine incisors with similar dimensions had been used. The crown was separate of the root through a diamantado record double face in the length of 16 mm from the apex. After that, all the canals radiculares had been obturados and the raÍzes had received a mark 2,0 mm simulating the amelo-cementário limit and a composed resin layer was inserted in the apical region of the root to increase the retention of the same one in the polystyrene resin block during the mechanical assay. The samples had been distributed, aleatoriamente, in six experimental groups (n=10), being that in 30 raízes the bolts had been fixed conical smooth and in the others 30 raízes the bolts parallel serrated. For the face-hardenings of the bolts, the raízes had been desobturadas in 12 mm with drill Gates Gliden n° 3 and for the preparation of the canal the specific drill for each bolt was used. Afier that, the bolts had been fixed applying the adhesive system Single Bond (3M) and the resinous cement dual Rely X (3M) with different ratios of base/catalisador (b/c): Gl - bolts parallel serrated cemented in ratio 1:1, G2 ¿bolts parallel serrated cemented in ratio 1:2, G3 - bolts parallel serrated cemented in ratio 1:3, G4 - cemented bolts conical smooth in ratio 1:1, G5 - emented bolts conical smooth in ratio 1:2, G6 - cemented bolts conical smooth in ratio 1:3. Afier storage per one week in greenhouse 37°C, the samples had been submitted to the assay of tensile strenght in a Instron the speed of 1mm/mim, until the displacement of the bolt. The data had been submitted to the variance analysis that evidenced difference significant statistics for the factors Bolts and Ratio, not having difference statistics for the interaction bolt x ratio. Better to evidence this result the test of Multiple Variation of Tukey was applied for each factor (LSMEANS) that it showed that when if tripled the ratio of the catalyser in relation to the base the average of tensile strenght was superior with difference significant statistics for the average of ratio 1:1. In relation to the factor bolt, the bolts parallel serrated had presented the average greater of independent tensile strenght of the used base/catalisador ratio / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T01:41:39Z (GMT). No. of bitstreams: 1 Pacheco_JoaoFelipeMota_D.pdf: 4282811 bytes, checksum: 41703a5d88ddb80855223eb94057a90b (MD5) Previous issue date: 1997 / Resumo: O objetivo deste estudo foi avaliar a influência de diferentes tratamentos na superfície do polímero de vidro Artglass (HERAEUS, Kulzer - Germany). Foi verificado também o efeito do agente de silanização (Porcelain Primer - BISCO, lnc. ltasca IL), do ativador superficial de compósitos (Composite Activator BISCO, lnc. ltasca IL) e do líquido para reparos do sistema Artglass na resistência à tração com o sistema adesivo All Bond 2 (BISCO, lnc. ltasca IL) associado ao cimento Choice Porcelain Venner System (BISCO, lnc. ltasca IL). Foram confeccionadas duzentos e quarenta amostras e divididas em 12 grupos com 20 amostras cada. Cada grupo foi submetido aos seguintes tratamentos: grupo 1 - jateamento com óxido de alumínio; grupo 2 - jateamento com óxido de alumínio e aplicação do Porcelain Primer; grupo 3 jateamento com óxido de alumínio e aplicação do Composite Activator; grupo 4 - jateamento com óxido de alumínio e aplicação do Artglass Liquid; grupo 5 - condicionamento com ácido fosfórico; grupo 6 - condicionamento com ácido fosfórico e aplicação do Porcelain Primer; grupo 7 - condicionamento com ácido fosfórico e aplicação do Composite Activator; grupo 8 condicionamento com ácido fosfórico e aplicação do Artglass Liquid; grupo 9 - condicionamento com ácido fluorídrico; grupo 10 - condicionamento COIIJ ácido fluorídrico e aplicação do Porcelain Primer; grupo 11 - condicionamento com ácido fluorídrico e aplicação do Composite Activator; grupo 12 - condicionamento com ácido fluorídrico e aplicação do Artglass Liquid. Após o tratamento, as amostras foram unidas em pares com auxílio do sistema adesivo e do cimento resinoso manipulados de acordo com as instruções do fabricante. Em seguida, os corpos-de-prova foram armazenados a 37 'GRAUS'C com umidade relativa do ar em 100%, durante 24 horas e, logo após, foram submetidos a 500 ciclos térmicos ajustados às temperaturas de 5'GRAUS'C, 37°C e 60°C, com duração de 30 segundos cada. Decorrido o período de 48 horas, os corpos-de-prova foram submetidos ao ensaio de tração em uma máquina de ensaio universal (Otto Wolpert Werke, Germany), a uma velocidade de 6 mm/minuto. As médias dos resultados obtidos foram: grupo 1 - 11,46 MPa; grupo 2 - 12,28 MPa; grupo 3 - 9,45 MPa, grupo 4 - 11,53 MPa; grupo 5 - 3,83 MPa; grupo 6 - 4,84 MPa; grupo 7 - 3,94 MPa; grupo 8 - 5,67 MPa; grupo 9 - 6,51 MPa; grupo 10 - 6,36 MPa; grupo 11 - 7,86 MPa; grupo 12 - 8,34 MPa. A seguir os resultados foram submetidos análise de variância e ao Teste de Tukey. Após os testes de resistência à tração as amostras foram examinadas em lupa estereoscópica com aumento de 16 vezes, onde foi verificado predomínio de fraturas coesivas do polímero de vidro para os grupos tratados com jateamento com óxido de alumínio. O efeito dos tratamentos de superfície foi analisado com auxílio de um microscópio eletrônico de varredura (Zeiss DSM 960, Germany). Os resultados indicaram que o maior valor de resistência de união foi obtido através do jateamento com óxido de alumínio associado ao agente de silanização. Nos demais grupos onde também foi realizado o jateamento com óxido de alumínio os valores de resistência de união foram superiores e diferentes estatisticamente, quando comparados aos outros grupos, com exceção da associação do ácido fluorídrico com o Composite Activator, que não diferiu do grupo 3. A análise através de M.E.V. das superfícies tratadas demonstrou um padrão morfológico mais favorável ao imbricamento micromecânico produzido com o jateamento com óxido de alumínio / Abstract: The purpose of this study was to evaluate the influence of different superficial treatment of glass polymeric material Artglass (Heraeus, Kulzer). The effect of the silane agent application (Porcelain Primer - Bisco, lnc., ltasca, IL), a superficial Composite activator mixture (Composite Activator - Disco, Inc., ltasca, lL) and also the Artglass Liquid was verified in the tensile strength with adhesive system AllBond 2 (Bisco, lnc., !tasca, lL) associated with the resin cement Choice Porcelain Venner System (Bisco, lnc., !tasca, IL). Two hundred and torty samples were made and divided into 12 groups. Each group contained 20 samples submitted to treatments: Group 1 sandblasting with aluminum oxide; Group 2 - sandblasting with aluminum oxide and Porcelain Primer application; Group 3 - sandblasting with aluminum oxide and Composite Activator application; Group 4 - sandblasting with aluminum oxide and Artglass liquid application; Group 5 - acid etching with phosphoric acid; Group 6 - acid etching with phosphoric acid and Porcelain Primer application; Group 7 - acid etching with phosphoric acid and Composite Activator application; Group 8 acid etching with phosphoric acid and Artglass Liquid application; Group 9 acid etching with hydrofluoridric acid; Group 10 - acid etching with hydrofluoridric acid and Porcelain Primer application; Group 11 - acid etching with hydrotluoridric acid and Composite Activator application; Group 12 - acid etching with. hydrofluoridric acid and Artglass Liquid application. Following the treatment, the samples were bonded into pairs with the adhesive system and the resin cement, applied according with the manufacturer's instructions. Then, the samples were stored in 37° with a relative humidity of 100% during 24 hours. Submitted into 500 thermal circles, adjusted to 5 'DEGREE'C, 37 'DEGREE'C and 60'DEGREE'C, lasting 30 second each. After 48 hours, the samples were submitted to a tensile strength test in a Universal test machine (Otto Wolpert Werke, Germany) with a crosshead speed 6 mm / minute. The average results were : Group 1 - 11,46 MPa; Group 2 - 12,28 MPa; Group 3 - 9,45 MPa; Group 4 - 11,53 MPa; Group 5 - 3,83 MPa; Group 6 - 4,84 MPa; Group 7 - 3.94 MPa; Group 8 - 5,67 MPA; Group 9 - 6,51 MPA; Group 10 6,36 MPa; Group 11 - 7,86 MPa; Group 12 - 8,34 MPa. ThereFore, the results were submitted to Anova and Tukey Test. Then the samples were examined in a stereoscopic magnifying glass (x16), where it was verified the prevailing of cohesive rupture of the Glass Polymer in the groups treated with aluminum oxide sandblasting. The efFect of the superficial treatments was analyzed by a Scanning Electron Microscopy. The results indicated that sandblasting with aluminum oxide associated with the silane agent attained the biggest value of the bond strength. ln groups where the aluminum oxide sandblasting was performed the values presented were higher and statistically significant comparing with the others groups, except the association between hydrotluoridric acid and Composite Activator, which did not differ from group 3. The analysis of the treated surface was made using the Scanning Electron Microscopy and showed a more suitable morphologic pattem to the micromechanic retention produced with aluminum oxide sandblasting / Doutorado / Doutor em Materiais Dentários

Orientador: Altair A. Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T00:02:27Z (GMT). No. of bitstreams: 1 Mello_JoseAntonioNunesde_D.pdf: 2954501 bytes, checksum: a0971bb352ee05fe0cb36fed63855884 (MD5) Previous issue date: 2001 / Resumo: A técnica de injeção de resina na mufla é um eficiente e preciso método de confeccionar próteses. Contudo, este processo pode alterar as propriedades químicas e mecânicas da resina. Este estudo avaliou o efeito De um sistema de injeção de resina na mufla, no ciclo de polimerização no microondas sob pressão (resina Onda-cryl). O grupo controle foi formado pela técnica da compressão (GI, 3 min a 360 W + 4 min a O W + 3 min a 810 W). Os outros foram pela técnica de injeção (G2, 3 min a 360 W + 4 min a O W + 3 min a 810 W), e técnica de injeção com polimerização sob pressão (G3, 6 min a 180 W + 4 min a O W + 3 min a 810 W /0,1 MPa). Monômero residual (MR), resistência ao impacto (RS), resistência à flexão (RF) e microdureza superficial (MDS) foram avaliados. A análise de variância e a comparação utilizando o teste de Tukey, mostraram diferença entre os grupos, cujas médias estão seguidas por letras distintas na mesma coluna (a=5%). O sistema de injeção de resina na mufla diminuiu o nível de monômero residual e a resistência à flexão, e não teve efeito sobre a resistência ao impacto e microdureza superficial da resina / Abstract: Injection molded technique is an efficient and accurate method for processing dentures. However, the process may cause adverse effects upon chemical and physical properties of the restn. This study evaluated the effects of injection-molded system, upon a microwave polymerization cycle under pressure (Onda-cryl resin). Control group was formed by compression molded (Gl, 3 min 360 W + 4 min O W + 3 min 810 W). The others were by Injection molded (G2, 3 min 360 W + 4 min O W + 3 min 810 W), and injection molded and polymerization under pressure (G3, 6 min 180 W + 4 min O W + 3 min 810 W / 0.1 MPa). Residual monomer (RM), impact strength (1S), flexural strength (FS) and surface Knoop hardness (SKH) were evaluated. The results of analysis of variance and the means comparison using Tukey test showed difference between the groups. The means followed by different letters showed significant difference (a=5%). Injection molded system decreased RM and FS, and did not affect IS and KH of the restn / Doutorado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Nilson Tadeu Mascia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-12T16:59:12Z (GMT). No. of bitstreams: 1 Todeschini_Rodrigo_M.pdf: 5391907 bytes, checksum: 209282e318155e52af17d68ae99c2ffb (MD5) Previous issue date: 2009 / Resumo: A realização de ensaios uniaxiais e biaxiais permite uma melhor compreensão do comportamento mecânico de um material que possui direções principais de resistência e é sem dúvida uma forma que pesquisadores encontraram para obter resultados condizentes com a situação real que uma determinada estrutura apresenta. O presente trabalho teve como objetivo o estudo do critério de resistência proposto por Tsai e Wu, realizando-se ensaios uniaxiais e biaxiais. A avaliação do critério ficou restrita ao ensaio de compressão, devido às dificuldades de se realizar ensaios biaxiais de tração. Com o ensaio biaxial de compressão, tensões em duas direções principais foram simultaneamente desenvolvidas, utilizando-se um equipamento de ensaio tradicional para uma direção e na direção perpendicular um equipamento tipo alicate desenvolvido para este fim. O parâmetro estudado foi o 12 F , parâmetro este que designa a possibilidade da superfície de ruptura ser aberta ou fechada, considerando-se que para a segurança de um projeto é imprescindível obter uma superfície fechada para o critério de resistência adotado. Observa-se, além disso, que o parâmetro 12 F foi obtido no ensaio biaxial de compressão de forma direta. Para as espécies de madeira Pinus elliottii e Goupia glabra (Cupiúba), obtiveram-se valores experimentais satisfatórios, sendo algumas inconsistências observadas em função da heterogeneidade do material. / Abstract: The completion of the uniaxial and biaxial tests permits a better understanding of the mechanical behavior of a material that has main failure directions and it is undoubtedly a method that researchers identified to achieve consistent results with the actual situation that a particular structure presents. This study aimed at studying the strength criterion proposed by Tsai and Wu, performing uniaxial and biaxial tests. The evaluation of this criterion was restricted to compression biaxial tests due to the difficulties presented by tension biaxial tests. With a compression biaxial test, the stresses in two main directions were simultaneously carried out, using a standard equipment test for one direction and for the perpendicular direction an equipment type pliers especially developed for this purpose. The failure parameter studied was 12 F , which evaluates the possibility of failure surface to be opened or closed, also considering that for the safety of design it is essential to obtain a closed surface for the failure criterion adopted. Furthermore, it was noted that in the compression biaxial test the parameter 12 F was obtained directly. For the species of wood Pinus elliottii and Goupia glabra (Cupiúba), the experimental values obtained were satisfactory with some inconsistencies observed in the light of the heterogeneity of the material. / Mestrado / Estruturas / Mestre em Engenharia Civil

Orientadores: Maria Beatriz Borges de Araujo Magnani, Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T18:10:24Z (GMT). No. of bitstreams: 1 Romano_FabioLourenco_D.pdf: 2297898 bytes, checksum: 5ecd4de7f0dd31f6b954e634f32893ef (MD5) Previous issue date: 2009 / Resumo: O objetivo neste estudo foi avaliar clinicamente e em laboratório, a taxa de descolagem e a resistência ao cisalhamento de bráquetes metálicos colados com compósitos ortodônticos. O experimento clínico consistiu de 20 pacientes (10,5-15,1 anos de idade), que procuraram tratamento ortodôntico corretivo. Nestes pacientes foram colados bráquetes de 2° pré-molar a 2° pré-molar no arco superior e inferior com os sistemas adesivos: Concise Ortodôntico, Transbond XT convencional, Transbond XT sem agente de união e Transbond XT em esmalte preparado com ácido-primer Transbond Plus Self Etching Primer (TPSEP). Todos os sistemas foram utilizados em todos os pacientes, em rodízio pelos quadrantes, sendo que, a mesma sequência de colagem se repetiu em cada cinco pacientes. Arcos iniciais foram inseridos uma semana após a colagem dos bráquetes. Os pacientes foram avaliados durante seis meses para quantificar o número de bráquetes descolados. Ao final do período de observação ocorreram 8 descolagens com Concise Ortodôntico, 2 com Transbond XT convencional, 9 com Transbond XT sem agente de união e 1 com TPSEP + Transbond XT. Pelo Método de Kaplan-Meier foram encontradas diferenças estatísticas significantes na taxa de descolagem entre os materiais (P=0,0198) e o teste Logrank identificou estas diferenças. O Transbond XT convencional e TPSEP + Transbond XT foram estatisticamente superiores (apresentaram menos descolagens) em relação ao Concise Ortodôntico e Transbond XT sem agente de união (P<0,05). Entre os materiais Transbond XT convencional e TPSEP + Transbond XT não foram encontradas diferenças estatísticas significantes, assim como, entre Concise Ortodôntico e Transbond XT sem agente de união (P>0,05). O experimento laboratorial teve como objetivo avaliar a resistência ao cisalhamento de bráquetes metálicos colados com o novo compósito ortodôntico Transbond Plus Color Change (TPCC, 3M Unitek) em diferentes preparações de esmalte e analisar após a descolagem o Índice de Remanescente de Adesivo (IRA). Foram utilizados 72 pré-molares humanos divididos em seis grupos (n=12). No Grupo 1 (controle) foi utilizado o compósito Transbond XT convencionalmente. Nos demais grupos (2 a 6) utilizou-se o TPCC nas seguintes condições de esmalte: ácido fosfórico e XT primer; ácido-primer TPSEP; somente ácido fosfórico; ácido fosfórico, XT primer e saliva; TPSEP e saliva, respectivamente. Após a colagem dos bráquetes e fotoativação, os corpos de prova foram armazenados em água destilada em estufa a 37°C por 24 horas. Em seguida, os bráquetes foram carregados em máquina Instron à velocidade de 0,5 mm/min. e o IRA avaliado em lupa estereoscópica. Osvalores médios de resistência ao cisalhamento (MPa) foram: Grupo 1- 24,6; Grupo 2-18,7; Grupo 3-17,5; Grupo 4-19,7; Grupo 5-17,5 e Grupo 6-14,8. Os dados foram submetidos à ANOVA e ao teste de Tukey (5%). O Grupo 1 apresentou maior média e diferiu estatisticamente dos grupos 3, 5 e 6 (P<0,05) e sem diferença estatística significante em relação aos grupos 2 e 4 (P>0,05). Entre os grupos 2, 3, 4, 5 e 6 não foram encontradas diferenças estatísticas significantes (P>0,05). A colagem de bráquetes com TPCC apresentou valores comparáveis ao Transbond XT convencional e o tipo de preparo de superfície não influenciou esta adesão / Abstract: The aim of this study was to assess clinically and laboratory the bracket failure rate and shear bond strength of metallic brackets bonded with orthodontic composites. The in vivo study consisted of 20 patients aged between 10.5 to 15.1 years old who had sought corrective orthodontic treatment. Brackets were bonded of the second premolar - second premolar to their upper and lower arches using the adhesive systems: Orthodontic Concise, conventional Transbond XT, Transbond XT without primer, and Transbond XT applied to enamel etched with Transbond Plus Self-etching Primer (TPSEP). All the adhesive systems were used in all patients on a quadrant-rotation basis by repeating the same bonding sequence in every 5 patients. Initial archwires were inserted a week after the brackets bonding. The patients were evaluated during six months in order to quantify the number of brackets failure regarding each adhesive system. At the end of the observation period, 8 brackets failure rates were observed for Orthodontic Concise, 2 for conventional Transbond XT, 9 for Transbond XT without primer, and 1 with Transbond XT + TPSEP. By using the Kaplan-Meier methods, statistically significant differences were found between the materials (p=.0198), and the Logrank test identified these differences. It was observed that conventional Transbond XT and Transbond XT + TPSEP were statistically superior (fewer debonded brackets) compared to Orthodontic Concise and Transbond XT without primer (P<.05). However, no statistically significant differences were found between conventional Transbond XT and TPSEP + Transbond XT as well as between Orthodontic Concise and Transbond XT without primer (P>.05). The in vitro study aimed at assessing the shear bond strength of metallic brackets bonded to different enamel surfaces using the Transbond Plus Color Change composite (TPCC, 3M Unitek) as well as to analyse the Adhesive Remnant Index (ARI). Seventy-two human premolars were used for study, with all samples being divided into six groups (n =12). In Group 1 (control), Transbond XT composite was conventionally used. In other groups (2-6), TPCC was used under the following enamel conditions: phosphoric acid and XT primer; TPSEP; phosphoric acid only; phosphoric acid, XT primer and saliva; and TPSEP and saliva, respectively. After bracket bonding and photo-activation, the samples were stored in distilled water for 24 hours at 37°C in a stove. Next, the brackets were debonded by using an Instron machine at crosshead speed of 0.5 mm/min, and the ARI were evaluated by using a stereoscopic magnifying glass. The mean shear strength values (MPa) were the following: Group 1, 24.6; Group 2, 18.7; Group 3, 17.5; Group 4, 19.7; Group 5, 17.5; and Group 6, 14.8. Data were submitted to both ANOVA and Tukey's test (5%). Group 1 was found to be statistically superior to Groups 3, 5, and 6 (P<.05), with no statistically significant difference compared to Groups 2 and 4 (P>.05). No statistically significant differences were found between Groups 2, 3, 4, 5 and 6 (P>.05). The bracket bonding using TPCC composite showed values comparable to the conventional Transbond XT, and the type of enamel preparation had no influence / Doutorado / Ortodontia / Doutor em Radiologia Odontológica

Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:49:05Z (GMT). No. of bitstreams: 1 Antunes_AlbertoNogueiradaGama_M.pdf: 2715470 bytes, checksum: f02dda3ea737577e7f386991ff69db32 (MD5) Previous issue date: 2007 / Resumo: Este estudo avaliou o efeito de diferentes tratamentos na superfície de resina composta utilizada para restaurações indiretas e do armazenamento em água na resistência de união com cimento auto-adesivo. Quarenta blocos cilíndricos de compósito MZ100 com dimensões de 4x10mm (altura x diâmetro) foram cimentados dois a dois com o cimento RelyX Unicem. Vinte corpos-deprova foram divididos, em cinco grupos de acordo com o tratamento de superfície. G1 (controle)- Sem tratamento; G2- Jateamento com partículas de óxido de alumínio (Al2O3); G3- Aplicação do condicionador de metal; G4- Jateamento com partículas de óxido de alumínio seguido da aplicação do condicionador de metal; G5- Jateamento com partículas de óxido de alumínio e aplicação do silano. Após a cimentação (24 horas), os conjuntos foram seccionados, produzindo espécimes em forma de palito com aproximadamente 0,8mm2 de área. Após a obtenção dos palitos, o ensaio de tração foi executado, em uma máquina de ensaio universal (Instron) sob velocidade de 0,5mm/min em dois períodos de tempo: 48 horas e 40 dias após a cimentação. As médias de resistência de união em 48 horas foram G1 = 45,48MPa; G2 = 47,17MPa; G3 = 36,16MPa; G4 = 41,68MPa; G5 = 45,84MPa. Após quarenta dias de armazenamento as médias de resistência de união foram: G1 = 48,07MPa; G2 = 42,56MPa; G3 = 37,84MPa; G4 = 34,17MPa; G5 = 45,59MPa. No período de teste de 48 horas e 40 dias a aplicação do condicionador de metal resultou em valores de resistência de união menores em relação aos outros tratamentos. O armazenamento de quarenta dias produziu redução estatisticamente significativa na resistência de união para o G4. Os demais grupos não apresentaram diferenças estatisticamente significante (p>0,05) / Abstract: The aim of this study was to evaluate the effect of different treatments and water storage on bond strength of an indirect resin cemented using self-adhesive luting cement. Forty cylindrical blocks (4X10mm) were cemented together in pairs using RelyX Unicem cement. Twenty samples were divided in groups of five according to surface treatment. G1 (control)- no surface treatment was applied; G2- Surface was sandblasted with Al2O3 particles; G3- surface was treated with metal conditioner; G4- samples were sandblasted with Al2O3 particles and metal conditioner was applied; G5- samples were sandblasted with Al2O3 and silane agent was applied. The pairs were sectioned twenty four hours after cementation, producing beams with cross-section area of 0.8mm2 approximately. Microtensile testing was performed 48 hours and 40 days after luting procedure using a universal testing machine (Instrom) at a crosshead speed of 0,5mm/min. The means obtained for microtensile bond strength after 24 hours were: G1 = 45.48MPa; G2 = 47.17MPa; G3 = 36.16MPa; G4 = 41.68MPa; G5 = 45.84MPa. After forty days of storage the means obtained for microtensile bond strength were: G1= 48.07MPa; G2 = 42.56MPa; G3= 37.84MPa; G4 = 34.17MPa; G5 = 45.59MPa. After 48 hours and 40 days, the application of Alloy primer resulted in the lowest microtensile bond strength values when compared to all the other treatments. Water storage for 40 days produced a statistically significant reduction of microtensile bond strength values for group G4. Other groups did not reveal statistically significant reduction of bond strength after storage (p>0,05) / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:14:43Z (GMT). No. of bitstreams: 1 Silva_AnaPaulaBritoda_M.pdf: 4666067 bytes, checksum: 6eaa4a564293d2a7a9e71635aad24d2f (MD5) Previous issue date: 2006 / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito do tempo de aplicação de gel de ascorbil a 3% (AE) sobre a resistência de união ao esmalte bovino tratado previamente com peróxido de carbamida a 10% (PC), estabelecendo o padrão de fratura através de microscopia eletrônica de varredura (MEV). Sessenta incisivos bovinos foram selecionados, limpos e armazenados em solução salina de timol a 0,1%. Sessenta fragmentos de 25mm2 foram obtidos da superfície vestibular, utilizando-se discos diamantados de dupla-face, em baixa rotação, sob constante irrigação. Os fragmentos foram cobertos com fina camada de cera 7 e embebidos em cilíndro por resina autopolimerizável de poliestireno. Posteriormente, foram divididos aleatoriamente em seis grupos, sendo dois controles: GS (saliva, durante todo o experimento) e GP (PC, por seis horas, durante 14 dias) e quatro experimentais, que após a utilização diária do PC, foram submetidos à aplicação de gel antioxidante por 15, 30, 60 ou 120 minutos, respectivamente (GPA15, GPA30, GPA60 e GPA120). Imediatamente após o tratamento, os fragmentos foram condicionados com ácido fosfórico a 37% (Dentsply) e restaurados com sistema adesivo Adper Single Bond (3M-ESPE) e três incrementos horizontais de resina TPH (Dentsply). Finalizado o tratamento restaurador, os fragmentos foram preparados para o ensaio de microtração. Cortes seriados foram realizados em cada amostra para obtenção de duas fatias centralizadas de, aproximadamente, 1mm de espessura. Posteriormente, com auxílio de uma broca 1093FF, foi confeccionado em cada fatia, uma constrição, com área adesiva de, aproximadamente, 1mm2, em forma de ampulheta. Os testes de microtração foram realizados em máquina de ensaio EMIC, com velocidade de 0,5mm/min. A ANOVA e o Teste de Dunnet indicaram haver diferença estatisticamente significativa entre os grupos testados. Comparando-se o controle positivo (GS) com os demais, verificou-se que apenas o controle negativo (GP) diferiu estatisticamente. Quando se comparou o GP com os outros grupos, foi observada diferença estatística com o GS e o GPA120. Para comparação apenas entre os grupos experimentais (GPA15, GPA30, GPA60 e GPA120), foi aplicado o teste ANOVA e análise de regressão polinomial, que revelaram não haver diferença estatisticamente significativa para o fator tempo, de forma isolada. Foi detectada, através de observações em microscopia eletrônica de varredura, presença de pequenas bolhas no grupo clareado. Os padrões de fratura demonstraram maior número de falhas mistas, para todos os grupos testados. O gel de ascorbil a 3%, aplicado no tempo de duas horas, parece ser o mais indicado, para recuperar os valores de resistência de união ao esmalte clareado com peróxido de carbamida a 10% / Abstract: The purpose of this in vitro study was to evaluate the effect that elapsed time (15 min, 30 min, 1 hour e 2 hours) of a 3% ascorbil gel (AE) onto the bond strength to bovine enamel previously treated with carbamide peroxide at 10%, defining the fracture pattern through electronic scanning microscopy. Sixty bovine incisors were selected, cleaned, and stored in saline solution of timol at 0.1%. Sixty fragments of 25mm2 were obtained by the use of double-face diamond discs, in low rotation, under constant irrigation, perpendicularly to buccal surfaces. The fragments were relieved with a thin layer of wax n° 7 and steep in a cylinder by a self-curing polyester resin. Afterwards, they were random divided into six groups according to the type of treatment to be employed (GS- Positive Control- Saliva, during experiment; GP- Negative Control- PC, 14 days/6hours, GPA15- PC, 14days/6hours + AE, 15 min; GPA30- PC, 14days/6hours + AE, 30 min; GPA60-PC, 14days/6hours + AE, 1 hour; GPA120- PC, 14days/6hours + AE, 2 hours). After treatments, the groups were etched with fosforic acid 35% (Dentsply) and restored with adhesive system Adaper Single Bond (3M-ESPE) and three horizontal increments of resin TPH (Dentsply). Concluded the restorative treatment, the fragments were immediately prepared for microtensile procedure. Serial cuts were performed in each sample to obtain two centralized slices 1mm thick. Afterwards, using a 1093 FF drill, an hourglass was done in each slice, with adhesive area of approximately 1mm2. The microtensile tests were performed in an mechanical test machine, at 0.5 mm/min speed. ANOVA and Dunnett test indicated that there was statistical difference between groups tested. When compared positive control group (GS) with the other groups, it was observed that only the negative control group (GP) was statistically different. These results were confirmed, when the negative control group was compared with others, in which it was observed statistic diference to GS and GPA120. When the experimental groups were compared though regressive polinominal analise it was not found statistical difference only to the time factor. On Electronic Scanning Microscopy observations, were detected the presence of bubbles of the bleached group. The fracture standards demonstrated higher number of mixed failures to all the groups. The 3% ascorbil gel (AE) used for two hours seems to be the most recommended to reverse the strength to bleached enamel with carbamide peroxide 10% / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Roseana da Exaltação Trevisan / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-15T00:22:28Z (GMT). No. of bitstreams: 1 PereaCorimaya_RodrigoLuis_M.pdf: 2032359 bytes, checksum: 4a5d338de38fffae7ef6f96cce297aaa (MD5) Previous issue date: 2009 / Resumo: No desenvolvimento deste trabalho utilizou-se o ensaio de auto-restrição TEKKEN com o propósito de adequar este teste para a avaliação do trincamento da junta soldada do aço API X80. Para a execução das soldas foi usado o processo de soldagem a arco com eletrodo tubular (FCAW), utilizando o aço API X80 e os eletrodos E71T-1 e E 71T8-K6. O desenvolvimento experimental realizou-se através do planejamento fatorial 23 (PF); as variáveis de influência estudadas foram: a temperatura de preaquecimento, o tipo de arame tubular e o tipo de chanfro do teste. Como variável de resposta foi avaliada a presença de trincas na junta soldada. Os resultados obtidos foram discutidos em função de duas energias de soldagem definidas em 2,0 kJ/mm e 1,0kJ/mm. A variação do insumo de calor teve como propósito aumentar a taxa de resfriamento e, consequentemente, aumentar a restrição do teste, induzindo ao trincamento a frio na junta soldada. Também foram avaliados o teor de hidrogênio residual, a microestrutura e a dureza resultantes. Neste trabalho concluiu-se que, apesar do alto teor de hidrogênio residual encontrado, da elevada taxa de resfriamento imposta durante o processo de soldagem e da presença de microestrutura suscetível, não foi observada a formação de trincas nos corpos de prova. Estes resultados foram atribuídos a inadequação do teste TEKKEN sobre o estudo da suscetibilidade ao trincamento do aço API X80. / Abstract: In the development of this work was used the self-restraint TEKKEN test with the purpose to adequate this test for the evaluation of the cracking in the welded joint of API X80 steel. The Flux Cored Arc Welding (FCAW) process and the cored wires E71T-1 and E 71T8-K6 were used for the accomplishment in the welds of API X80 steel. The experimental were carried out with a factorial design 23 (PF); the input variables studied were: preheat temperature, the wire cored kind and the groove kind of the test. The output variable was always the presence of cracking in the weld joint. The results obtained were discussed in function of two heat input defined in: 2,0 kJ/mm and 1,0kJ/mm. The variation of the heat input was have the purpose of increase the cooling rate and, consequently increased the restraint of the test, to induced cold cracking in the weld joint. It was also evaluated the content of residual hydrogen, the microstructure and the hardness obtained. In this work can be concluded that, in the spite of, high content of residual hydrogen founded, and the high cooling rate, during the welding and the presence of susceptibility microstructure was not observed the formation of cracks in the test pieces. These results were attributed to the inadequate TEKKEN test over the susceptibility cracking API X80 steel studied. / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Orientador: Marcelo Giannini / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-15T12:58:19Z (GMT). No. of bitstreams: 1 Pinto_CristianeFranco_D.pdf: 8181087 bytes, checksum: 41321386cc6d99055932efad6dad9919 (MD5) Previous issue date: 2010 / Resumo: O objetivo deste estudo foi avaliar sistemas adesivos, tecidos dentais adjacentes (esmalte ou dentina) às restaurações e a união formada entre os adesivos e as estruturas dentais frente aos desafios cariogênicos in situ e in vitro. Para o estudo foram utilizados dentes bovinos e blocos dos tecidos dentais (esmalte e dentina) que foram restaurados com dois sistemas adesivos e resina composta. No estudo in situ; 11 voluntários utilizaram dispositivos palatinos contendo 2 amostras do grupo controle (substrato hígido sem preparo cavitário) de esmalte e dentina, e 6 amostras restauradas com os sistemas adesivos Clearfil Protect Bond (PB) ou One-Up Bond F Plus (OP) (em fases distintas) e com o compósito Filtek Z350. O desafio cariogênico consistiu de 2 fases (cada fase com um adesivo), sendo cada fase de 14 dias com intervalo de 10 dias entre elas. Os voluntários utilizaram solução de sacarose a 20%, 8X/dia e dentifrício fluoretado 3X/dia. Após cada etapa, o biofilme dental formado foi coletado e analisado. As amostras foram analisadas através de Microscopia de Luz Polarizada (MLP) e Microdureza Knoop para observação da extensão da lesão de cárie. Para o estudo in vitro foi realizado o preparo dos substratos e foram restaurados em esmalte e em dentina seguindo os grupos experimentais: 1-adesivo PB sem desafio cariogênico (DC); 2- adesivo PB com DC; 3- adesivo OP sem DC; 4- adesivo OP com DC. A partir dos blocos dentais restaurados foram obtidos espécimes para o ensaio de resistência da união com formato de paralelepípedos (palitos) e fatias para análise da interface da união em Microscopia Eletrônica de Transmissão (MET). Os espécimes (palitos ou fatias) foram submetidos à ciclagem de pH durante 8 dias. O resultado do ensaio de microdureza em esmalte e dentina mostrou maiores valores para PB nas profundidades mais superficiais e as imagens de MLP mostraram uma menor extensão da área de desmineralização para o adesivo PB que para o adesivo OP. Na análise bacteriológica, o adesivo PB levou a menor quantidade de colônias de Streptococcus totais e do grupo mutans em esmalte. A resistência de união não foi afetada pela ciclagem de pH e foi semelhante em esmalte para ambos adesivos, entretanto, em dentina, o adesivo PB apresentou maior resistência de união que o adesivo OP. Os adesivos produziram hibridização nos tecidos dentais, sem formações de fendas na interface de união. Concluiu-se que o adesivo PB produziu menor extensão de desmineralização dos substratos dentais após o desafio cariogênico e maior microdureza Knoop nas profundidades mais superficiais. Em algumas condições deste estudo, o adesivo PB reduziu a formações de colônias bacterianas. Embora a união formada pelos adesivos em esmalte foi semelhante, o adesivo PB mostrou maior resistência de união em dentina. / Abstract: The aim of this study was to evaluate adhesive systems, mineralized dental tissues (enamel and dentin) around restorations and the bonding formed by adhesives and dental structures in conditions of cariogenic challenge in situ and in vitro. This study used dental blocks (enamel/ dentin) from bovine teeth, which were restored with adhesive systems and a resin composite. For the in situ study: volunteers (n=11) wore intra-oral appliance containing 2 dental fragments without restoration (enamel or dentin) and six dental blocks with restorations made with self-etching primers Clearfil Protect Bond (PB) or One-up Bond F Plus (OP) (in two phases) and the Filtek Z350 composite: The cariogênico challenge was performed in two phases of 14 days (each phase with one adhesive). The volunteers dropped 20% sucrose solution 8x/day and used fluoridated dentifrice 3x/day. After each phase, the biofilm was collected and analyzed. The samples were analyzed by cross-sectional microhardness and polarized light microscopy (PLM) to determine the demineralization depth. For the in vitro study, bovine were prepared and bonded in enamel and dentine with Clearfil Protect Bond (PB) or One-Up Bond F Plus (OP) and restored with Filtek Z-350 composite resin, according to the groups: 1- PB without CC; 2- PB with CC; 3- OP without CC; 4- OP with CC. Restored teeth were sectioned in order to obtain sticks for microtensile bond strength or slabs for transmission electron microscopy. The specimens were submitted to pHcycling, which consisted of DE (8h/day) and RE (16h/day) cycles at 37ºC during days. Microhardness analysis showed that the enamel and dentin around restorations PB had higher values in superficial depths, and the PLM showed that PB resulted in lower demineralization depth than OP. The biofilm investigation indicated that PB produced lower number of bacterial colony of Streptococcus totais and mutans in enamel. The results showed that the pH-cycling regimen did not affect the bond strength to enamel or dentin for both adhesives; however, the bond strength to dentin was higher for PB. The adhesives produced hybridization and no gaps formation in both dental tissues. In conclusion, PB adhesive may result in lower enamel demineralization around restoration and higher microhardness in superficial depths. In some conditions, PB adhesive reduced the number of bacterial colony. Although the adhesives in enamel formed similar bonded interfaces, PB produced higher bond strength to dentin than OP. / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Marcelo Ferraz Mesquita / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-15T15:52:10Z (GMT). No. of bitstreams: 1 Silva_JoaquimAlbertoda_D.pdf: 1108935 bytes, checksum: 15a0a956cee4dcf34973383fda778eb8 (MD5) Previous issue date: 2010 / Resumo: O objetivo neste estudo foi comparar o efeito de dois métodos de envelhecimento acelerado (termociclagem e simulação do intemperismo natural) sobre a propriedade de deformação permanente de dois reembasadores resilientes permanentes usados como forradores de próteses removíveis, um à base de silicone (UP) e outro à base resina acrílica (DF), submetidos ou não à aplicação de selante de superfície. Foram confeccionados 120 corpos-de-prova (12,7 mm de diâmetro, e 19 mm de comprimento), distribuídos aleatoriamente em doze grupos (n=10) e submetidos a envelhecimento acelerado (2.000 ciclos) por meio da termociclagem, ou simulação do intemperismo natural (67 ciclos). Para o ensaio, foi utilizado um aparelho mecânico descrito na especificação no18 da A.D.A., com aplicação de carga compressiva (750 gf) durante 30 segundos. Para comparações do mesmo material com e sem selante e entre os materiais no mesmo intervalo de envelhecimento, foi realizada a análise estatística pelo teste de Mann-Whitney (p=0,05). Os testes de Kruskal-Wallis associado ao método de Dunn foram utilizados para comparação do efeito das técnicas de envelhecimento em cada material (p=0,05). O reembasador à base de silicone apresentou menor deformação permanente que o à base de resina, independente do método de envelhecimento (P<0,05). Foi observado que a aplicação do selante de superfície teve efeito sobre a deformação permanente apenas no grupo do material à base de silicone submetido à termociclagem, e que o envelhecimento acelerado promoveu aumento na deformação permanente apenas para o material à base de resina acrílica. / Abstract: This study was performed in order to compare the effects of two different accelerated aging methods on the property of permanent deformation of two permanent softliners. The softliners selected were an auto-polymerizing acrylic resin based and an auto-polymerizing silicone based. The use of surface sealer was also evaluated on both relining materials. For the permanent deformation test specimens were manufactured with 12.7 mm of diameter and 19 mm length, according to A.D.A. specification number 18. A total of 120 specimens were manufactured, sixty of each relining material. All specimens were randomly distributed into twelve groups (n=10) and later submitted to one of the accelerated aging processes (2000 thermocycling cycles or 67 cycles in an EQUV chamber). The permanent deformation test was performed with a mechanical device described in the specification number 18 of A.D.A. with a compressive load of 750 gf applied during 30 seconds. All data was submitted to statistical analysis. MannWhitney test was performed in order to compare the effect of the surface sealer on each material and to compare the permanent deformation of the materials in the same aging group (p=0.05). Kruskal-Wallis and Dunn tests were performed to compare all aging groups of each material (p=0.05). After analysis of the results it was observed that the silicone based reliner presented lower permanent deformation than the acrylic resin based reliner, regardless of the aging procedure. The surface sealer coating was effective only for the thermocycled silicone group and the accelerated aging processes affected only the permanent deformation of the acrylic resin based material. / Doutorado / Protese Dental / Doutor em Clínica Odontológica