This research investigates composite tubes developed with hybrid preform manufacturing techniques of braiding and filament winding (FW). A quadriaxial braid-wound (QBW) preform [(±45°/0°/90°)2/(±45°/0°)] and a triaxial braided (TB60) preform [(±60°/0°)3] were developed. Quasi-isotropic (QI) fibre orientations were selected for both the lay-ups for comparison of mechanical properties. The large diameter of the tubes led to incomplete surface coverage with (±45°/0°)3 braided preforms (TB45). Circumferential distribution of multiple layers improved the coverage by reducing through the thickness resin pockets. Also addition of hoop winding improved the coverage and consolidated the braided preform. The use of braiding together with FW resulted in an improved fibre volume fraction. Also predicting surface coverage was a fundamental interest for a triaxial braided preform. An equation was proposed for cover factor estimation and was verified by using image analysis. Resin infusion of the preforms was carried out and composite tubes were fabricated. During resin infusion of braided preforms wrinkles were formed. A brief study on wrinkle formation was carried out and the reasons of wrinkle formation for braided tubes were identified based on existing literature. Longitudinal tensioning in conjunction with optimization of fibre amount in a layup and over-winding on braid was established to minimize wrinkle formation. This was primarily due to compaction of braided layers with hoop winding. Hence braid-winding has the additional advantage of manufacturing wrinkle free composite tubes. Finally composite tubes were tested under tension and torsion loads. One of the major findings was the effect of hoop winding on transverse deformation of the braid-wound tubes. As axial fibre percentage for QBW tube was less than that of TB45, the tensile strength was compromised. However presence of hoop winding resulted in lower transverse strain contributing to higher tensile modulus of QBW tubes along with lower Poisson's ratio. Although shear modulus of TB60 tube was exceptionally high for its fibre orientation, for QBW tubes, shear modulus was not significantly higher than that of other tubes. An aluminium tube was also tested for comparing the elastic properties of the QI tubes with those of an isotropic material. QBW tubes specific modulus was higher than that of the aluminium. The shear modulus of the QI and aluminium tubes was estimated by applying the theory for isotropic materials. In comparison to aluminium, for QBW tube the differences between estimated and actual shear modulus was higher. However QBW tube properties were in closer relation to those of the aluminium tube than TB60 tubes. Hence a QBW hybrid layup technique has the potential for manufacturing composite tubes without losing comparative composite material properties.

Les tubes à paroi mince en alliage à mémoire de forme Nickel-Titane (AMF NiTi) sont largement utilisés dans la fabrication de stents auto-expansibles. Leur fonctionnement repose sur la superélasticité (SE), comme de nombreuses autres applications des AMF NiTi dans le domaine biomédical. Le SE est un phénomène cristallographique réversible qui donne aux AMF la capacité de récupérer de grandes déformations par simple déchargement mécanique. En raison de la nature cristallographique du SE, les propriétés mécaniques liées à cet effet devraient être affectées par l'anisotropie inhérente du tube, qui émerge de son processus de fabrication. Cependant, le NiTi est encore souvent considéré comme isotrope dans la conception et l'optimisation de tels dispositifs. L'une des difficultés empêchant l'utilisation de modèles anisotropes est l'absence de caractérisations mécanique de l'anisotropie du tube NiTi. Le présent travail vise à effectuer une telle caractérisation pour un tube superélastique NiTi à paroi mince. Dans une campagne expérimentale, le comportement en traction du tube est analysé à différentes orientations et températures. La technique de corrélation d'image numérique (digital image correlation - DIC) est utilisée pour surveiller la distribution des déformations pendant les essais de traction. Les résultats montrent que toutes les propriétés analysées liées à la SE sont anisotropes. Toutes les dépendances d'orientation sont presque symétriques à 45° de l'axe du tube. Certaines propriétés dépendent également de la température, dépendance qui est également anisotrope. Une approche thermodynamique basée sur l'énergie libre de Gibbs est utilisée pour analyser ces dépendances d'orientation et de température. Avec cette analyse, il a été possible de relier l'hystérésis mécanique de la SE et les contributions irréversibles présentes dans le système. Enfin, l'influence de l'anisotropie sur la distribution des déformations est vérifiée. L'accent est mis sur l'analyse du phénomène de localisation de la déformation tout au long du chargement et du déchargement. L'inclinaison de la bande de localisation est caractérisée et évaluée avec une approche de plasticité. L'angle de la bande avant observé avec DIC est prédit en utilisant des données de vitesse de déformation globale. / Thin walled tubes of Nickel-Titanium shape memory alloys (NiTi SMA) are widely used in the fabrication of self-expandable stents. The operation of stents relies on the superelastic effect (SE), as many other applications of NiTi SMA in the biomedical field. The SE is a reversible crystallographic phenomenon that gives SMA the ability to recover large strains through simple unload. Due to the crystallographic nature of the SE, the mechanical properties related to this effect are expected to be affected by the inherent anisotropy of the tube, which emerges from its fabrication process. However, NiTi is still often treated as isotropic in the design and optimization of such devices. One of the difficulties preventing the use of anisotropic models is a lack of mechanical characterizations about the NiTi tube's anisotropy. The present work aims to perform such characterization for a thin walled NiTi superelastic tube. In an experimental campaign, the tensile behaviour of the tube is analysed at different orientations and temperatures. Digital Image Correlation (DIC) technique is used to monitor the strain distribution during tensile tests. Results show that all the analysed properties related with SE are anisotropic. All the orientation dependencies are nearly symmetrical to 45° from the tube's axis. Some properties are also dependent on temperature, a dependence that is also anisotropic. A thermodynamic approach based on the Gibbs free energy is used to analyse these orientation and temperature dependencies. With this analysis it was possible to relate the SE stress hysteresis and thermodynamic irreversible energy contributions. Finally, the influence of anisotropy on the strain distribution of tensile samples is verified. Focus is given to the analysis of the strain localization phenomenon throughout loading and unloading. The inclination of the localization front band is characterized and evaluated with a plasticity approach. The front angle observed with DIC is predicted using global strain rate data.

O presente trabalho tem como objetivo avaliar as tensões atuantes no conjunto conector e duto flexível de camadas não aderentes durante ensaios com carregamentos axiais de tração e fadiga. Estes ensaios são utilizados para a qualificação de dutos flexíveis. Foram desenvolvidos e patenteados alguns modelos de conectores contemplando apenas a parte estrutural. Ensaios preliminares de tração e fadiga, com dois conectores diferentes e um segmento de riser de dimensões reduzidas, foram realizados visando a seleção do modelo de melhor desempenho em um pórtico. O conector de melhor desempenho foi então ensaiado em uma bancada com dimensões que atendessem ao documento da Petrobras a I-ET 3500.00.6500-291-PAZ-001 - Non standartized Prototype qualification tests of flexible pipes (2007). Tanto os ensaios do pórtico como o de bancada, foram monitorados com strain gages colados nos tendões da armadura externa de tração próximos aos conectores. O foco deste trabalho está nas armaduras de tração na interface com a resina do conector. Questões quanto ao desempenho da mesma em fadiga são de grande importância prática. Complementando a parte experimental, foram construídos modelos sólidos tridimensionais, baseados no Método dos Elementos Finitos para análise das tensões. A comparação dos resultados das diferentes metodologias validou o modelo numérico possibilitando melhor entendimento das variações de tensões nas armaduras de tração na interface com os conectores. Isso possibilitou responder a importantes questões quanto ao desempenho em fadiga bem como possíveis melhorias no projeto de conectores para dutos flexíveis. Existem trabalhos referentes à análise de tensões dos tendões nos conectores considerando o estado plano de tensões. O presente estudo dos tendões usando modelos tridimensionais, abordagem não encontrada em literatura aberta, avalia melhor a concentração de tensões nos tendões na entrada do conector. A motivação deste estudo se deve tanto à falta de informações detalhadas das tensões e deformações nos tendões na interface com o conector, como pela importância das mesmas, em componentes vitais à explotação de petróleo Offshore. / This aim of this work is to evaluate stresses which actuate on a system made up of a unbonded flexible pipe and a end fitting during static and dynamic axial loading mechanical tests. These tests are used as a means of qualification of flexible pipes. The structural design of models of end fittings were developed and patented. Preliminary static and dynamic tests with two different end fittings and a smalldimensioned riser segment were performed in a frame in view of selecting the bestperforming type. After this evaluation, the end fitting with the best performance was tested in a rig with dimensions according to Petrobras document I-ET 3500.00.6500-291-PAZ- 001 - Non standartized Prototype qualification tests of flexible pipes (2007). Tests performed in the frame and on the rig were monitored with resistance strain gages attached to wires of the external armor, on the interface with the end fitting resin, since performance of this region under fatigue is of utmost practical importance. Three-dimensional solid models were built using the Finite Element Modelling (FEM) method, as a way of validating experimental results. Comparison of results obtained from the different methodologies validated the numerical model, allowing a better understanding of the variations of stresses in the interface of the riser with the end fitting. This led to the solution of many doubts regarding fatigue performance as well as possible improvements in the design of flexible riser end fittings. Existing work published in literature considers only plane stress; the present study, based on 3D models which are not found in literature, is thought to better describe the stress concentration on the wires at the end fitting interface. The motivation of this work relies on the lack of detailed information of the stress and strain to which wires are subjected at the interface with the end fitting, as well as the importance of these in vital components for offshore oil exploration.

Fundação de Amparo à Pesquisa do Estado do Rio de Janeiro / O objetivo deste estudo foi avaliar o efeito da microestrutura dentinária na adesão de cimentos endodônticos modernos através: do desenvolvimento de uma metodologia para caracterizar microestruturalmente a dentina; da avaliação da resistência de união (através de ensaios de tração) dos cimentos endodônticos Epiphany SE, iRoot SP e AH Plus; da correlação dos dados obtidos da caracterização da microestrutura dentinária e dos ensaios de tração. Trinta terceiros molares inclusos, recém extraídos, foram embutidos em resina epóxi e seccionados 0,5mm abaixo da junção esmalte-dentina. Doze amostras foram eliminadas durante à preparação metalográfica devido à exposição da câmara pulpar. De cada dente, uma área de análise (AA) com 3,25 mm de diâmetro foi mapeada utilizando técnicas de microscopia ótica digital para: captura de ~400 imagens formando um mosaico; análise digital de imagens, obtendo os resultados de quantidade de túbulos (QT) e de fração de área de túbulos (FAT) do mosaico; conversão da imagem do mosaico em um mapa colorido em que as cores estão diretamente relacionadas à densidade de área tubular. As dezoito amostras restantes foram divididas em 3 grupos (N=6), de acordo com o cimento utilizado, para confecção dos corpos de prova para os ensaios de tração. Os valores de da resistência de união (RU) obtidos foram analisados estatisticamente com teste não-pareado t com correção de Welch e pelo teste F para comparar variâncias Os dados de FAT e de QT foram submetidos ao teste de D'Agostino & Pearson revelando-se não normais (P>0,05), o que indica grande variabilidade da amostragem. O cimento Epiphany SE apresentou uma resistência de união significativamente menor que o cimento AH Plus (P <0,05). Os corpos de prova do iRoot SP falharam prematuramente e não foram analisados. A aplicação do teste r de Spearman não demonstrou correlação significativa entre FAT e RU (P>0,05). O MEV de pressão variável foi utilizado para avaliar qualitativamente a superfície de fratura após os ensaios de tração. A análise revelou um padrão de fratura mista para o AH Plus e o Epiphany SE, além de diferenças no tamanho e na forma das partículas desses cimentos, o que pode influenciar no comportamento mecânico. Dentro da amostragem realizada, não se encontrou correlação significativa entre microestrutura dentinária e a resistência de união. / The present study aimed at evaluating the effect of dentine microstructure on the adhesion of modern endodontic sealers through: the development of a method to characterize the microstructure of dentine; the measurement of tensile strength of the sealers Epiphany SE, iRoot SP and AH Plus; the correlation between the data obtained from microstructural characterization and tensile tests. Thirty recently extracted unerupted third molars were mounted in epoxy resin and sectioned 0.5 mm below the enamel-dentine junction. Twelve samples were descarded because pulp chamber exposure during the metallographic procedure. From each tooth an analysis region 3,25 mm in diameter was mapped employing digital optical microscopy techniques to acquire ~ 400 images assembled in mosaic form; image analysis to produce results of tubule count (QT) and area fraction (FAT) in the mosaic; conversion of the mosaic image onto a color map in which colors are directly related to tubule area density. The remaining 18 samples were divided into 3 groups (N=6), according to sealer type, to prepare tensile test specimens. The values of bond strenght (RU) were statistically analyzed with the unpaired t test with Welch correction, and by the F test to compare variances. The FAT and QT data were submitted to the D'Agostino & Pearson test, and were shown to be non-normal (P>0.05), what indicates great sampling variability. The Epiphany SE sealer showed much lower values of RU as compared to AH Plus (P<0.05). The CPs of iRoot SP failed prematurely and were not analyzed. The application of the Spearman r test did not show significant correlation between FAT and RU (P>0.05). A variable pressure SEM was used to qualitatively evaluate the fracture surface after the tensile tests. The analysis revealed a pattern of mixed fracture for AH Plus and Epiphany SE, and differences in size and shape of sealer particles, what can have an influence on mechanical behavior. Within the employed sampling, no significant correlation between microstructure and bond strenght was found.

Orientador: João Neudenir Arioli Filho / Banca: Sérgio Russi / Banca: Sergio Sualdini Nogueira / Banca: Cláudia Helena Lovato da Silva / Banca: Helena de Freitas Oliveira Paranhos / Resumo: O objetivo deste estudo foi analisar a influência da incorporação de três desinfetantes (hipoclorito de sódio a 1%, glutaraldeído alcalino a 2% e digluconato de clorexidina a 2%) em duas diferentes porcentagens de substituição da água da espatulação (50 e 100%) de dois gessos tipo IV, FujiRock EP (M1) e Rock Plus (M2), avaliando-se a resistência à compressão e à tração diametral. Os corpos-de-prova foram obtidos a partir de matrizes metálicas bipartidas com 20 mm de diâmetro e 40 mm de altura (resistência à compressão) e 20 mm de diâmetro e 10 mm de altura (resistência à tração diametral). As matrizes foram fixadas sobre uma placa de vidro, o gesso foi manipulado na proporção água/pó recomendada pelos fabricantes (M1:20ml/100g e M2:19 ml/100g), em um espatulador mecânico por 30 segundos, e vazado sob vibração. Para cada ensaio foram confeccionados sete grupos para cada gesso (n=10). Os grupos foram: CONTROLE (Água destilada), G50 (substituição de 50% da água de espatulação por glutaraldeído), G100 (100% de glutaraldeído), C50 (substituição de 50% da água por clorexidina), C100 (100% de clorexidina), H50 (substituição de 50% da água por hipoclorito) e H100 (100% de hipoclorito). Após a presa os corpos-de-prova foram removidos das matrizes e armazenados à temperatura ambiente. Os ensaio de compressão e tração diametral foram realizados 24 horas após o vazamento, em uma máquina de ensaios MTS-810, com célula de carga de 100 KN à velocidade de 0,5mm/min. Os valores médios de resistência à compressão e à tração diametral (MPa) foram submetidos à análise de variância e teste de Tukey, com nível de significância de 95%, permitindo concluir que: (a) a incorporação das substâncias desinfetantes estudadas afetou a resistência à compressão de ambos os gessos analisados; (b) as diferentes proporções de incorporação das substâncias... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this study was to evaluate the compressive and diametral tensile strength of two Type IV dental stones, FujiRock EP (M1) e Rock Plus (M2), mixed with three disinfectant solutions (sodium hypochlorite 1%, chlorhexidine digluconate 2% and glutaraldehyde 2%) in two different proportions of gauging water (50% and 100%). Compressive samples consisted of cylindrical specimens, each having a diameter of 20 mm and length of 40 mm, and diametral tensile specimens consisted of discshaped specimens, having a diameter of 20 mm and length of 10 mm, obtained from split metal molds. The stone was mixed with the solutions previously outlined at the water-powder ratio recommended by the manufacturers (M1:20ml/100g e M2:19 ml/100g), mechanically spatulated under vacuum (Turbomix) for 30 seconds, and gently vibrated in the molds. Seven groups were prepared for each test, with 10 samples each, as follows: CONTROL (distilled water), G50 (substitution of 50% of gauging water by glutaraldehyde), G100 (only glutaraldehyde), C50 (substitution of 50% of gauging water by chlorhexidine digluconate), C100 (only chlorhexidine digluconate), H50 (substitution of 50% of gauging water by sodium hypochlorite) and H100 (only sodium hypochlorite). Specimens were removed from the molds after they set. Compressive strength and diametral tensile strength was determined 24 hours the specimens were cast, in an MTS-810 testing machine, with a cross-head speed of 0,5mm/min. Mean compressive and diametral tensile strength was calculated and expressed in megapascals (MPa). Data from both tests were analyzed by ANOVA and Tukey test, showing that: (a) chemical disinfectants incorporation reduced the compressive strength of type IV dental stones evaluated; (b) the use of two different proportions of gauging water substitution by disinfectants (50% and 100%) has affected the compressive strength of only one die stone (M1); (c) chemical disinfectants incorporation did not reduced. / Doutor

Orientador: Sizenando de Toledo Porto Neto / Banca: Marcelo Ferrarezi de Andrade / Banca: Maria Salete Machado Cândido / Banca: Alberto Magno Gonçalves / Banca: Edson Alves de Campos / Resumo: Este trabalho teve como objetivo avaliar in vitro a força de união da resina composta à dentina tratada com quatro adesivos dentinários, sendo dois sistemas universais simplificados (G1- Prime & Bond® NT/ Dentsply, G2- Single Bond/ 3M) e dois auto-condicionantes (G3- AdheSE® / Vivadent, G4- Adper- PromptL-Pop/ 3M). Para a realização deste estudo, foram selecionados 20 terceiros molares humanos íntegros e livres de cárie, que tiveram suas superfícies oclusais cortadas em 3mm. Após o corte, cada grupo de dentes receberam seus respectivos sistemas de tratamento adesivo, pré-selecionados. Todas as amostras de dentes foram restauradas com a resina composta Tetric Ceram® / IvoclarVivadent, termocicladas em 550 ciclos e cortadas. Dessa forma, obtendo-se espécimes de 1,0mm2 l0,1mm2 que foram levados a uma Máquina de Teste Universal onde foi realizado o ensaio de microtração. Os tipos de fraturas foram analisados, mediante microscopia óptica (40X) e as fraturas mais representativas foram levadas à microscopia eletrônica de varredura. Os resultados mostraram que os sistemas universais simplificados (G1 e G2) apresentaram valores de resistência de união mais elevados do que os sistemas auto-condicionantes (G3 e G4). A maioria das fraturas encontradas foram do tipo adesiva para os grupos G3 e G4, enquanto nos grupos G1 e G2 87% dos modos de fraturas foram distribuídas entre adesivas e coesivas da resina. / Abstract: This work had with aim to evaluate "in vitro" the bond strength of composite resin to dentine bonded with four dentin adhesives. In this study, were used two one-step adhesive systems (G1- Prime & Bond® NT/Dentsply, G2-Single Bond/ 3M)and two self-etching adhesive systems (G3- AdheSE® /Vivadent, G4- Adper Prompt L-Pop/3M). For this, were chosen twenty human healthy third molars, that had their oclusal surfaces cut in 3mm. After the cut, each group of teeth received their respectives adhesive systems, even then chosen. All the samples were restored with the composite Tetric Ceram® / IvoclarVivadent, thermocycled 550 times and cut. Then, obtaining specimens of 1,0mm2 l 0,1mm2 that were made a test of micro tensile bond strength in a Universal Test Machine. The fractures were analyzed in a optical microscope (40X), and the more representative fractures were then analyzed at scanning electronic microscope. The results revealed that the one-step adhesive systems (G1 and G2) showed higher values of bond strength compared to the self-etching adhesive systems (G3 and G4). The fractures more commum were the adhesive type in the G3 and G4 groups, while in the G1 and G2 groups, 87% of the fractures were the adhesive and cohesion of resin types. / Doutor

Resumo: A proposta deste estudo foi avaliar por meio do teste de microtração a resistência de união de um sistema adesivo irradiado com laser de Nd:YAG em dentina preparada com laser de Er:YAG. Estudos prévios têm demonstrado que a irradiação com laser após a aplicação do sistema adesivo é eficiente em alcançar alta força de união à tensão e ao cisalhamento. O laser de Er:YAG (Twinlight, Fotona, Eslovênia) com fluência de 60 J/cm2 foi usado para o tratamento da dentina. A irradiação do adesivo foi realizada usando o laser de Nd:YAG (Twinlight, Fotona, Eslovênia) com fluência de 100 J/cm2. As restaurações foram executadas com Adper Single Bond 2/Z250 (3M/ESPE, EUA). Vinte terceiros molares recentemente extraídos e livres de cárie foram empregados. Os dentes foram divididos em quatro grupos experimentais (n = 5): (G1) grupo controle onde não houve irradiação; (G2) irradiação do sistema adesivo com laser de Nd:YAG; (G3) tratamento da dentina com laser de Er:YAG; (G4) tratamento da dentina com laser de Er:YAG mais irradiação do sistema adesivo com laser de Nd:YAG. Um dente de cada grupo foi preparado para avaliação da interface adesiva sob microscopia eletrônica de varredura (MEV). Adicionalmente foi realizada a análise do padrão de fraturas, resultante dos ensaios mecânicos, sob microscopia óptica digital. Os testes de microtração foram realizados em uma máquina de ensaios mecânicos com célula de carga de 1 kN a uma velocidade de 0,5 mm/min. A análise estatística (ANOVA e teste de Tukey), dos dados referentes aos ensaios mecânicos, evidenciaram diferença estatística significante entre os grupos G1 e G3, G1 e G4, G2 e G3, e G2 e G4 e semelhança entre os grupos G1 e G2, e G3 e G4. As fraturas adesivas foram predominantes em todos os grupos experimentais. / Abstract: The purpose of this study was to verify through micro tensile bond test the bond strength of an adhesive system irradiated with Nd:YAG laser in dentine treated with Er:YAG laser. Previous studies had shown that laser irradiation after the application of an adhesive system is efficient in achieving higher shear bond and tensile bond strength. Er:YAG laser (Twinlight, Fotona, Slovenia) with fluency of the 60 J/cm2 was used for the treatment of the dentine. The irradiation of the adhesive was performed using the Nd:YAG laser (Twinlight, Fotona, Slovenia) with the fluency of the 100 J/cm2. Dental restorations were performed with Adper Single Bond 2/Z250 (3m/ESPE, USA). Twenty caries free extracted human third molars were used. The teeth were divided in four experimental groups (n = 5): (G1) control group where there was no irradiation; (G2) irradiation of the adhesive system with the Nd:YAG laser; (G3) treatment of the dentin with Er:YAG laser; (G4) treatment of the dentin with Er:YAG laser plus irradiation of the adhesive system with Nd:YAG laser. One tooth of each group was prepared for evaluation of adhesive interface under scanning electron microscopy (SEM). In addition was performed an evaluation of the bond failures under digital optic microscopy. The micro tensile bond tests were performed in a MTS universal testing machine with 1 kN load cell at cross-head speed 0,5 mm/min. The statistical analysis (ANOVA and Tukey test) showed difference significant statistics between the groups G1 and G3, G1 and G4, G2 and G3, and G2 and G4; and similarity between the groups G1 and G2, and G3 and G4. The adhesive failures were predominant in all experimental groups. / Orientador: Rosane de Fátima Zanirato Lizarelli / Coorientador: Marcelo Ferrarezi de Andrade / Banca: José Eduardo Pelizon Pelino / Banca: Sizenando de Toledo Porto Neto / Mestre

Orientador: Josimeri Hebling / Banca: Ricardo Marins de Carvalho / Banca: Elisa Maria Aparecida Giro / Resumo: A resistência adesiva de um sistema auto-condicionante e um convencional simplificado, Clearfil SE Bond e Single Bond, respectivamente, quando aplicados à dentina superficial tratada com diferentes agentes condicionadores, foi avaliada por meio de ensaios mecânicos de microtração. Superfícies planas de dentina, obtidas removendo-se a superfície oclusal de 30 terceiros molares humanos foram polidas com lixa de granulação 600 antes da aplicação de diferentes agentes condicionadores, SE Primer, ácido fosfórico ou EDTA. O primer acidificado SE Primer foi aplicado sobre a superfície por 20 segundos, seguido de suave secagem com jatos de ar. O ácido fosfórico a 37% foi aplicado por 15 segundos, seguido de lavagem e remoção do excesso de água com papel absorvente e a solução de EDTA 0,5M pH7,2 foi aplicada por 30 segundos, também seguida de lavagem e secagem. Com exceção das superfícies que receberam a aplicação do primer acidificado, as demais foram mantidas úmidas para a posterior aplicação dos sistemas adesivos avaliados. Sobre a superfície coberta pelo sistema adesivo foi construída uma coroa em resina composta Z250 e os dentes foram mantidos em água a 37% por 24h. Após 500 ciclos térmicos em temperaturas de 5o e 55oC, cortes paralelos no sentido mesio-distal e cortes perpendiculares aos primeiros, no sentido vestibulo-lingual, permitiram a obtenção de amostras com área de secção transversal quadrangular de 1,0mm2 em número mínimo de 10 para cada dente. Cada amostra foi colada a um dispositivo especialmente desenvolvido, e este foi acoplado à uma máquina universal de testes operada à velocidade de 0,5mm/min. O lado correspondente à dentina de aproximadamente 50% das superfícies fraturadas após o ensaio mecânico foi analizado em MEV. Os resultados mostraram que o maior valor médio de resistência adesiva foi observado para a associação SE Primer... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: Microtensile bond strength of a self-etching primer and a conventional one-bottle system, Clearfi SE Bond and Single Bond, respectively, bonded to superficial dentin treated with different conditioners was investigated. Flat dentin surfaces obtained by removing the occlusal enamel with a diamond saw were ground with 600-grit SiCs under wet conditions to create the smear layer before the conditioners application. Three different dentin conditioning was performed, SE Primer, phosphoric acid and EDTA. The SE Primer was applied on dentin for 20 seconds followed by slight air-drying. Phosphoric acid (37%) was applied for 15 seconds followed by rinsing. EDTA 0.5M pH7.2 was applied for 30 seconds, also followed by water rinsing. Except for the surfaces that received the SE Primer conditioner, the surfaces were left moist by blot-drying the excess water. The adhesive systems were applied and a 5mm high composite resin (Z250) was built up covering the whole surface. After 24h of storage in water at 37oC the teeth were thermocycled for 500 cycles at preset temperatures of 5o and 55oC. The teeth were sectioned with a diamond saw, perpendicular to the adhesive interface to produce beams with 1.0mm2 of adhesive area. These specimens were then attached to a testing apparatus and a tensile load was applied by a universal machine at a crosshead speed of 0.5mm/min. After the micro-tensile bond test, the dentin side of 50% of the fractured surfaces was examined under a scanning electron microscope. The highest tensile bond strength mean was found for the association of SE Primer and Single Bond, 58.51MPa, followed by the association Clearfil SE Bond and EDTA, 47.81MPa. The remaining associations showed mean tensile bond strength statistically similar, except for the association Single Bond and EDTA, which showed the lowest... (Complete abstract, click electronic address below). / Mestre

A danificaÃÃo e a falha do concreto sÃo largamente investigadas no ramo da MecÃnica do Dano em Meios ContÃnuos. VÃrios modelos existem na literatura e descrevem muito bem uma variedade de fenÃmenos observados, dependendo de sua complexidade. O principal objetivo deste trabalho à investigar e modelar os efeitos da corrosÃo no dano e falha das propriedades do concreto. Inicialmente, foram feitos ensaios de traÃÃo e de compressÃo em alguns corpos-de- prova intactos sem que tivessem sido submetidos a nenhuma corrosÃo para determinar o comportamento mecÃnico do concreto. Outros foram submetidos a uma cÃmara de corrosÃo acelerada Salt Spray ( durante perÃodos de tempo diferentes) para determinar esse comportamento considerando a corrosÃo. Para o ensaio de traÃÃo, foi desenvolvido um dispositivo composto de peÃas de aÃo, onde se pode realizar esse ensaio de tal maneira a se obter os grÃficos de tensÃo deformaÃÃo utilizando corpos-de-prova cilÃndricos iguais aos usados para a compressÃo. Com esses resultados experimentais, utilizando a MecÃnica do Dano em Meios ContÃnuos, um modelo elÃstico aclopado ao dano à usado para modelar o comportamento do concreto. Em um primeiro estÃgio, a elasticidade isotrÃpica e o dano isotrÃpico ( somente com uma variÃvel escalar D) sÃo usados, mas incluindo-se os efeitos da corrosÃo. Nos resultados, à analisada a evoluÃÃo do dano no concreto em relaÃÃo ao tempo de exposiÃÃo dos corpos-de-prova na cÃmara de corrosÃo acelerada Salt Spray e em funÃÃo dos carregamentos mecÃnicos. / A danificaÃÃo e a falha do concreto sÃo largamente investigadas no ramo da MecÃnica do Dano em Meios ContÃnuos. VÃrios modelos existem na literatura e descrevem muito bem uma variedade de fenÃmenos observados, dependendo de sua complexidade. O principal objetivo deste trabalho à investigar e modelar os efeitos da corrosÃo no dano e falha das propriedades do concreto. Inicialmente, foram feitos ensaios de traÃÃo e de compressÃo em alguns corpos-de- prova intactos sem que tivessem sido submetidos a nenhuma corrosÃo para determinar o comportamento mecÃnico do concreto. Outros foram submetidos a uma cÃmara de corrosÃo acelerada Salt Spray ( durante perÃodos de tempo diferentes) para determinar esse comportamento considerando a corrosÃo. Para o ensaio de traÃÃo, foi desenvolvido um dispositivo composto de peÃas de aÃo, onde se pode realizar esse ensaio de tal maneira a se obter os grÃficos de tensÃo deformaÃÃo utilizando corpos-de-prova cilÃndricos iguais aos usados para a compressÃo. Com esses resultados experimentais, utilizando a MecÃnica do Dano em Meios ContÃnuos, um modelo elÃstico aclopado ao dano à usado para modelar o comportamento do concreto. Em um primeiro estÃgio, a elasticidade isotrÃpica e o dano isotrÃpico ( somente com uma variÃvel escalar D) sÃo usados, mas incluindo-se os efeitos da corrosÃo. Nos resultados, à analisada a evoluÃÃo do dano no concreto em relaÃÃo ao tempo de exposiÃÃo dos corpos-de-prova na cÃmara de corrosÃo acelerada Salt Spray e em funÃÃo dos carregamentos mecÃnicos.

Neste trabalho apresenta-se um estudo do comportamento estrutural de cestas protendidas, tendo em vista a sua utilização em coberturas pênseis de grandes áreas livres. A partir da Técnica do Meio Contínuo obtêm-se as equações que permitem analisar as cestas protendidas quanto a esforços e deslocamentos. Fazem-se considerações sobre o sistema de equações encontrado visando a sua resolução mediante o emprego de programa computacional como instrumento de cálculo. Apresentam-se exemplos numéricos e os resultados são comparados com os obtidos em outros trabalhos. Fazem-se algumas considerações a respeito do projeto e do cálculo de cestas protendidas, além de algumas indicações sobre a continuidade da pesquisa. / This work presents a continuous medium method analysis of cable nets and their applications as suspended roofs for large free spans. lnitially the theory of the method is presented and later applied to get the system of differential equation that represents the problem. Finally this system is numerically solved with computational procedures. Some examples are presented and the results compared with those obtained with others methods and numerical procedures. Some analysis and design considerations and further developments in this subject are also included.