Análise da influência da morfologia porosa de implantes de titânio no processo de crescimento ósseoMoreira, Anderson Camargo January 2013 (has links)
Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-graduação em Ciências e Engenharia de Materiais, Florianópolis, 2013. / Made available in DSpace on 2014-08-06T17:13:20Z (GMT). No. of bitstreams: 1
321931.pdf: 10691516 bytes, checksum: bc7e3518f2b190bc8afed68069d5d8dd (MD5)
Previous issue date: 2013 / O tecido ósseo está sempre suscetível a lesões, causadas por agentes
externos ou patologias, onde em alguns casos a intervenção cirúrgica
para instalação de implantes se faz necessária. Dentre os biomateriais
utilizados como sustentação para a regeneração óssea, os implantes
porosos processados a base de titânio apresentam uma combinação de
fatores que viabilizam o seu emprego, entre eles, apropriadas
propriedades químicas e mecânicas. Além da biocompatibilidade, a
caracterização estrutural desses materiais é de relevante importância,
pois suas características morfológicas também influenciam o processo
de regeneração óssea. Este projeto tem como objetivo principal a
caracterização de dois grupos de implantes de titânio com morfologias
porosas distintas, além da avaliação do crescimento ósseo em suas fases
porosas, uma vez que as amostras foram implantadas em tecidos ósseos
de coelhos. As análises estruturais e de quantificação óssea foram
realizadas por meio da análise de imagens tridimensionais adquiridas
com a microtomografia de raios X. As amostras foram processadas por
meio da técnica da metalurgia do pó, usando Titânio puro grau 1 como
matéria prima e bicarbonato de amônio como agente gerador de poros.
Diferentes granulometrias e proporções dos pós utilizados asseguraram
diferenças morfológicas entre os dois grupos de implantes. As amostras
foram implantadas em tíbias de coelhos, onde os períodos de
permanência no tecido ósseo de 7, 14, 21, 28 e 35 dias foram
respeitados para a avaliação do processo osseointegrativo. Foram
analisados os parâmetros estruturais de porosidade, tamanho de poros e
conexões, número de coordenação, permeabilidade, área superficial e
grau de esfericidade dos poros de cada grupo. As correlações
investigadas entre a fração de poros ocupada por osso e os parâmetros
físicos indicaram a influência da morfologia porosa no processo de
reparação óssea. Os resultados encontrados contribuirão para a
otimização de biomateriais porosos direcionando o seu processamento
para atingir propriedades que melhorem o desempenho dos implantes <br> / Bone tissue is susceptible to injuries induced by pathologies or
accidents. In some cases, a surgical intervention to implant devices is
necessary. Biomaterials are often used as scaffolds to bone recuperation.
To be applied as a scaffold, porous titanium implants are a good choice
due to their chemical and mechanical properties. Besides the
biocompatibility, biomaterial implants must to offer other structural
parameters which permit the bone ingrowth process. In this work, two
groups of porous titanium implants were processed by powder
metallurgy with distinct pore morphology. Pure titanium and ammonium
bicarbonate (as pore former) were used in the samples processing.
Different quantities and grain sizes of the powders provided different
pore morphology for the groups. The implants were introduced into
rabbits bone tissues for 7, 14, 21, 28 and 35 days. Therefore, the aim of
this work is to characterize the pore phase of the titanium porous
implants, and also to quantify the pore fraction occupied by neo-bone
formation. The measurements were accomplished by means of X-ray
microtomography image analysis. Structural parameters such as
porosity, pore size, throat size, interconnectivity, permeability, surface
area and pore sphericity were analyzed. The correlations between bone
neoformation data and structural parameters indicate the influence of the
pore shape on osseointegration process. The results of this work can be
useful to improve the porous biomaterial processing.
|
182 |
Análise comparativa da topografia e presença de impurezas de implantes dentais com superfície texturizada por meio de microscopia eletrônica de varredura (MEV)Castro, Kavio Narciso de Oliveira January 2004 (has links)
Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia. / Made available in DSpace on 2012-10-21T13:08:28Z (GMT). No. of bitstreams: 1
203835.pdf: 10797340 bytes, checksum: bfd0a2cbac605c338cdfb3cadf47f950 (MD5) / O objetivo desta análise comparativa foi observar qualitativamente, por meio de Microscopia Eletrônica de Varredura (MEV), as variações microscópicas topográficas e a presença de impurezas em cinco fabricantes de implantes osteointegráveis submetidos a diferentes processos de texturização: Conexão (Grupo 1); 3i (Grupo 2); Neodent (Grupo 3); SIN (Grupo 4); Titanium fix (Grupo 5). De acordo com os resultados foi possível concluir que, no aspecto topográfico os fabricantes SIN (G4) e 3i (G2) foram estatisticamente equivalentes, em um nível de significância de 1% e melhores que todos os demais, exibindo uma característica topográfica desejável. Os fabricantes Conexão (G1), Neodent (G3) e Titanium fix (G5) mostraram diferenças significantes entre si, em um nível de significância de 1% e padrões de texturização variáveis. No aspecto presença de impurezas os fabricantes Neodent (G3) e Conexão (G1) foram equivalentes entre si, em um nível de significância de 1% e melhores que todos os demais, mostrando superfícies mais livres de impurezas que todos os demais. Os fabricantes SIN (G4) e 3i (G2) foram equivalentes entre si, em um nível de significância de 1%, exibindo superfícies com uma certa quantidade de impurezas e melhores que o fabricante Titanium fix, que se mostrou inferior a todos os demais, exibindo superfícies com grande quantidade de impurezas.
|
183 |
Proposta protocolar para avaliar in vitro o crescimento e adesão celulares frente a implantes de titânio c.p. com quatro texturas superficiais obtidas por usinagemMakowiecky, Edson January 2002 (has links)
Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia / Made available in DSpace on 2012-10-19T15:29:55Z (GMT). No. of bitstreams: 0Bitstream added on 2014-09-26T01:57:59Z : No. of bitstreams: 1
182038.pdf: 8962650 bytes, checksum: 18471b0f80e7a5054554eaf43450f159 (MD5) / A biocompatibilidade promove a oportunidade de investigar e comparar os resultados fenomenológicos gerados pelos estudos laboratoriais in vitro, investigações in vivo, em animais e, em humanos. Este trabalho situa-se entre estudos que visam beneficiar processos de osseointegração, fundamentais no desenvolvimento dos implantes, por meio de estudos in vitro. Trata-se da proposta de um protocolo para avaliar in vitro, em culturas de células osteoprogenitoras e células osteoblásticas provenientes de maxilares humanos, o crescimento e adesão celulares frente à quatro diferentes rugosidades obtidas por usinagem na superfície de amostras de cilindro de titânio c.p. seccionados.
|
184 |
Degradação fotocatalítica de corante e efluente têxtilSauer, Ticiane January 2002 (has links)
Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico / Made available in DSpace on 2012-10-20T00:37:38Z (GMT). No. of bitstreams: 0 / A indústria têxtil consome quantidade considerável de água durante os processos de tingimento e acabamento. Os corantes são extensivamente usados e os efluentes descarregados em rios ou plantas de tratamento público são altamente contaminados. Este trabalho tem por objetivo apresentar uma investigação detalhada da adsorção e degradação fotocatalítica do corante safira procion HEXL, um corante azo da classe reativa, e avaliar a descolorização do efluente de tingimento de tecidos proveniente de duas empresas do Estado de Santa Catarina. Os resultados experimentais foram obtidos num reator descontínuo, iluminado com lâmpada de mercúrio de 80, 125 ou 250 watts. O fotocatalisador utilizado nos testes foi o TiO2 P-25(Degussa). A adsorção do corante no semicondutor mostra uma forte dependência no pH e segue o modelo de adsorção de Langmuir. A cinética de fotodegradação do corante é discutida em termos do modelo de Langmuir e Hishellwood. O efeito do pH, quantidade de catalisador, intensidade da luz UV e concentração de peróxido de hidrogênio são discutidos. A eficiência fotônica do sistema é apresentada usando fenol como composto padrão. O efluente teve o mesmo comportamento apresentado pelo corante Safira Procion, obtendo os melhores resultados em pH´s ácidos. A adsorção dos corantes sobre o catalisador é muito pequena, quando comparada a descolorização total, indicando que os corantes são efetivamente degradados.
|
185 |
Estudo da aplicação de mínima quantidade de fluido no fresamento de acabamento da liga Ti-6Al-4V / Study of minimal quantity of fluid applying in Ti-6Al-4V alloy end millingGarcia, Ubirajara [UNESP] 27 May 2015 (has links) (PDF)
Made available in DSpace on 2015-12-10T14:24:26Z (GMT). No. of bitstreams: 0
Previous issue date: 2015-05-27. Added 1 bitstream(s) on 2015-12-10T14:30:39Z : No. of bitstreams: 1
000852079_20160527.pdf: 384748 bytes, checksum: d13287fe4bb4e50857976157165dd2ee (MD5) Bitstreams deleted on 2016-05-30T11:37:07Z: 000852079_20160527.pdf,. Added 1 bitstream(s) on 2016-05-30T11:37:52Z : No. of bitstreams: 1
000852079.pdf: 3951366 bytes, checksum: 259ae6df8d263a1d123b5707ff472b77 (MD5) / Reduzir o uso de fluidos de corte em operações de usinagem é uma meta que tem sido buscada na indústria devido aos problemas ecológicos e de saúde humana, causados pelos fluidos de corte. No entanto, os fluidos de corte ainda promovem uma vida de ferramenta mais longa para muitas operações de usinagem. Este é o caso da operação de fresamento de acabamento da liga de titânio Ti6Al4V usando pastilhas de metal duro recobertas. Portanto, o objetivo deste trabalho é estudar condições de corte mais adequadas para o uso da técnica de mínima quantidade de fluido, ou seja, condições que tornem a vida da ferramenta na técnica MQF, mais próximas ou superiores àquelas obtidas com corte sem lubri-refrigeração e corte com jorro de fluido, sem prejudicar a rugosidade da peça. Para alcançar estes objetivos vários experimentos de fresamento de acabamento foram realizados, variando-se a velocidade de corte e taxa de avanço com aplicação da técnica MQF com o uso de três diferentes fluidos comparados com o corte sem lubri-refrigeração e corte com jorro de fluido. A principal conclusão deste estudo foi que a aplicação da técnica MQF no processo de fresamento de acabamento do Ti-6Al-4V aumenta a vida da ferramenta, melhorando a produtividade e rugosidade, quando mantidas as mesmas condições de corte originalmente propostas / To reduce cutting fluids use in machining operations is one goal that has been searched in industrial companies, due to ecological and human health problems caused by the cutting fluid. However, the cutting fluids still provide a longer tool life for many machining operations. This is the case of Ti6Al4V titanium alloy end milling operation using coated carbide inserts. Therefore, this work objective is to study cutting conditions more suitable for minimum quantity of fluid technique use, i.e., conditions which make tool life in MQF technique, closer or over to that obtained with dry cutting and cutting with fluid fload, without damaging the workpiece roughness. To reach these goals several end milling experiments were carried out, varying up cutting speed and feed rate with MQF technique application with three different fluids compared with dry cutting and cutting with fluid fload. The main study conclusion was that applying the MQF technique in Ti-6Al-4V end milling process increases tool life, improving productivity and roughness, when kept up the same cutting conditions proposed originally
|
186 |
Caracterização físico-química, morfológica, análise mecânica e de elementos finitos 3D, de diferentes placas e parafusos metálicos e técnicas de fixação interna, empregadas em fraturas de ângulo mandibularGuastaldi, Fernando Pozzi Semeghini [UNESP] 26 April 2013 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:31:07Z (GMT). No. of bitstreams: 0
Previous issue date: 2013-04-26Bitstream added on 2014-06-13T20:21:53Z : No. of bitstreams: 1
guastaldi_fps_dr_araca.pdf: 2507066 bytes, checksum: a269643c19104677e351a0d2217af1fc (MD5) / Proposição: Realizar uma caracterização físico-química, morfológica e comparar o comportamento mecânico de uma liga experimental de Ti-Mo, ao sistema de fixação análogo à base de Ti, em fraturas de ângulo mandibular, favoráveis ao deslocamento. Adicionalmente, análises de elementos finitos 3D foram realizadas para avaliar o padrão de distribuição de tensões nas placas e nos parafusos. Material e Método: Vinte e oito réplicas de mandίbulas de poliuretano foram usadas e uniformemente seccionadas na região do ângulo mandibular esquerdo. Estas foram divididas em 4 grupos considerando o material das placas e as técnicas de fixação interna: grupo Eng 1P, uma placa (zona de tensão da mandίbula) e 4 parafusos de 6 mm de comprimento; grupo Eng 2P, duas placas (uma na zona de tensão da mandίbula e a outra na zona de compressão), a primeira fixada com 4 parafusos de 6 mm de comprimento e a segunda com 4 parafusos de 12 mm de comprimento, sendo todo o material de fixação do sistema 2.0-mm. Os mesmos grupos foram criados para a liga Ti-15Mo. Cada grupo foi submetido a uma carga vertical linear no primeiro molar. As médias e os desvios-padrão foram comparados para avaliação estatίstica (ANOVA; p < .05). Adicionalmente, foi construído um modelo de elementos finitos 3D considerando as mesmas variáveis para avaliar as tensões equivalentes de von Mises (σvM) nas placas e nos parafusos. Resultados: Diferença estatisticamente significativa (p < .05) foi encontrada quando foi realizada a comparação entre ambas as técnicas de fixação (1 e 2 placas), independentemente do material das placas (cpTi and Ti-15Mo). Quando considerado os valores das tensões equivalentes de von Mises (σvM) para... / Purpose: Perform a physico-chemical and morphological characterization and compare the mechanical behavior of an experimental Ti-Mo alloy to the analogous metallic Ti-based fixation system, for mandibular angle fractures, favorable to displacement. Additionally, finite element analysis was performed to assess the stress distribution in the plates and screws. Material and Method: Twenty eight polyurethane mandible replicas were used and uniformly sectioned on the left mandibular angle. These were divided into 4 groups considering the material of the plates and the internal fixation techniques: group Eng 1P, one 2.0-mm plate (tension zone of the mandible) and 4 screws 6 mm long; group Eng 2P, two 2.0-mm plates (one in the tension zone of the mandible and the other in the compression zone), the first fixed with 4 screws 6 mm long and the second with 4 screws 12 mm long. The same groups were created for the titanium alloy (Ti-15Mo). Each group was subjected to linear vertical loading at the first molar. Means and standard deviations were compared with respect to statistical significance (ANOVA; p < .05). Additionally, an three-dimensional finite element model reproducing the characteristics of the specimens used in the mechanical tests were created to evaluate the von Mises equivalent stress (σvM) in the plates and screws. Results: Statistically significant difference (p < .05) was found when the comparison between both internal fixation techniques (1 and 2 plates) was performed, regardless the materials of the plates (cpTi and Ti-15Mo). When considering the von Mises equivalent stress (σvM) values for the comparison between both groups (Eng and Ti-15Mo) with 1 plate, an decrease of 10.5% in the plate and an decrease of 29.0% in the screws... (Complete abstract click electronic access below)
|
187 |
Efeito do tratamento de superfície na osseointegração de implantes dentários da liga TI-7,5MoOliveira, João Augusto Guedes de [UNESP] 27 January 2012 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0
Previous issue date: 2012-01-27Bitstream added on 2014-06-13T19:03:28Z : No. of bitstreams: 1
oliveira_jag_dr_guara.pdf: 2054384 bytes, checksum: 2056494b4d46299584c8acf22e9f6838 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Os Biomateriais Metálicos são utilizados para reforçar ou para restaurar a forma e função de tecidos duros. Os implantes e próteses são utilizados para substituir ombros, joelhos, quadris e dentes perdidos entre outros. Nos últimos anos, varias ligas de titânio para aplicações biomédicas foram avaliadas. Neste trabalho, a influência do tratamento de superfície biomimético na osseointegração de implantes dentários da liga Ti-7,5Mo foi avaliada. Os lingotes foram obtidos a partir de titânio e molibdênio utilizando um forno a arco voltaico. Eles foram submetidos a tratamento térmico e conformados a frio em prensa rotativa. Posteriormente foram confeccionados implantes (2,0 mm de diâmetro e 2,5 mm de comprimento) sob medida os quais submetidos ao tratamento de superfície biomimético. Os implantes foram inseridos e analisados histológica realizada após 28 dias. A caracterização microestrutural e mecânica da liga Ti-7,5Mo também foi realizada. Aliga Ti-7,5Mo exibiu baixo modulo de elasticidade e elevada relação resistência/modulo. O uso do tratamento de superfície biomimético promoveu um aumento da osseointegração sobre a superfície dos implantes / Metallic biomaterials are used to reinforce or to restore form and function of hard tissues. Implants and prosthesis are used to replace shoulders, knees, hips and teeth. In the last years, several titanium alloys for biomedical applications have been studied. In the present work, influence of biomimetic surface treatment in osseointegration of Ti-7.5Mo dental implant was evaluated. Ingots were obtained from titanium and molybdenum by using an arc-melting furnace. They were submitted to heat treatment and cold worked by swaging. Then, screw-shaped implants (2.0 mm diameter by 2.5 mm length) were custom made and they were submitted biomimetic surface treatment. Implants were implanted in the rat’s femur and histological analysis was realized after 28 days. Also, microstructural and mechanical properties of Ti-7.5Mo alloy were evaluated. Ti-7.5Mo showed low elasticity modulus and higher ratio strength/modulus. Results obtained suggest that Ti-7.5Mo exhibited excellent bulk properties. The use of the biomimetic surface treatment was able to promote an increase of osseointegration on surface of dental implants
|
188 |
Influência de diferentes íons sobre a erosão dentáriaMagalhães, Ana Carolina [UNESP] 01 February 2008 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:33:01Z (GMT). No. of bitstreams: 0
Previous issue date: 2008-02-01Bitstream added on 2014-06-13T21:05:43Z : No. of bitstreams: 1
magalhaes_ac_dr_araca.pdf: 9195485 bytes, checksum: 4cb23013433fabac2d92dd96f48d89fc (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Esta tese teve como objetivo mostrar a ação de diferentes íons sobre a erosão dentária. O 1o Capítulo abordou o efeito da suplementação de um refrigerante (Sprite Light®), pela adição de cálcio 1 mM, flúor 0,047 mM, ferro 1 mM e fósforo 1 mM associados ou não (9 grupos, n=10 blocos/grupo), na redução da erosão do esmalte dentário bovino in vitro. A ciclagem de pH foi realizada por 24 h. Os blocos foram imersos no refrigerante puro ou modificado, seis vezes ao dia (1 min), sendo que nos intervalos (59 min) e nas 18 h restantes foram mantidos em saliva artificial. A alteração do esmalte foi avaliada por perfilometria e microdureza superficial. Somente os grupos como Ca e Ca+F foram efetivos em reduzir o desgaste do esmalte. O 2º Capítulo relatou o efeito da aplicação tópica de uma solução de tetrafluoreto de titânio (TiF4 4%) sobre a erosão do esmalte humano in situ. Para tal, 10 voluntários utilizaram aparelho palatino com 2 blocos de esmalte divididos em 2 fileiras correspondentes à: erosão sem aplicação prévia de TiF4 (ERO+ no-F); e erosão com aplicação prévia de TiF4 (ERO+F). No 1º dia da fase in situ, os voluntários utilizaram o aparelho para permitir a formação da película adquirida. No 2º dia, aplicou-se a solução em uma fileira (F) durante 1 min enquanto na outra nada foi realizado (controle). Na seqüência, o aparelho foi recolocado na boca dos voluntários. Do 3º ao 7º dia, o desafio erosivo foi realizado por meio da imersão do aparelho em refrigerante tipo cola por 5 min, 4x/dia. A alteração do esmalte foi avaliada por microdureza superficial, perfilometria e microscópio eletrônico de varredura com espectroscopia por energia dispersiva (MEV-EED). / The objective of this thesis was to show the effect of different ions on dental erosion. In the 1st Chapter, the effect of a modified soft drink (Sprite Light®) with 1 mM calcium, 0.047 mM fluoride, 1 mM iron and 1 mM phosphorus alone or together (9 groups, n= 10 samples/group) on the inhibition of dental bovine enamel erosion was evaluated in vitro. During 24 h, the samples were subjected to 6 pH-cycles. In each cycle, the samples were immersed in modified or pure drink (1min) and in artificial saliva (59 min). In the remaining 18 h, the samples were stored in artificial saliva. The enamel alteration was evaluated by profilometry and surface microhardness. Only groups with Ca and Ca+F were effective on enamel wear reduction. The 2nd Chapter showed the effect of a titanium tetrafluoride solution (4% TiF4) on human enamel erosion in situ. For this, 10 volunteers wore palatal appliances with 2 enamel samples divided into 2 rows: Erosion without previous TiF4 application (ERO+ no-F) and erosion with previous TiF4 application (ERO+F). During the 1st day, the formation of a salivary pellicle was allowed. In the 2nd day, the TiF4 solution was applied on one row (ERO+F), whereas on the other row no treatment was performed (ERO+ no-F). From the 3rd until 7th day, the samples were subjected to erosion by immersion of the appliance in cola drink (5 min), 4 times a day. The enamel alterations were evaluated by surface microhardness, profilometry, scanning electron microscopy and x-ray energy dispersive spectroscopy (SEM-EDS). The application of 4% TiF4 solution increased the enamel loss by erosion. It was possible to detect titanium and to see a surface coating with micro cracks on the part of treated enamel. The 3th and 4th Chapters showed the effect of an experimental 4% TiF4 varnish on dental caries and erosion in vitro, respectively.
|
189 |
Osteogênese in vitro em amostras de titânio com diferente porosidadesNascimento, Rodrigo Dias [UNESP] 27 April 2009 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:33:24Z (GMT). No. of bitstreams: 0
Previous issue date: 2009-04-27Bitstream added on 2014-06-13T20:05:14Z : No. of bitstreams: 1
nascimento_rd_dr_sjc.pdf: 665145 bytes, checksum: eb26b18d83008dbc3f700ae579c575a4 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Alterações nas propriedades físicas e químicas na superfície do titânio (Ti) buscam acelerar e melhorar a osseointegração. Além disso, a criação de substratos porosos, além de beneficiar fenômenos celulares, propiciaria uma maior resistência mecânica na interface osseointegrada devido ao crescimento de tecido ósseo para o interior dos poros. O objetivo deste estudo foi avaliar a influência da porosidade de amostras de Ti na osteogênese in vitro em amostras de titânio. Foram confeccionadas por metalurgia do pó, discos de titânio puro grau 2 com 12 mm de diâmetro e 3 mm de altura, que foram divididos em três grupos: a) G1: controle - titânio denso; b) G2: 30% de porosidade e poros com 300 μm; c) G3: 40% de porosidade e poros com 300 μm. Inicialmente, a superfície de 03 espécimes de cada grupo foi caracterizada por meio de analise metalográfica, visando confirmar a quantidade, área, morfologia e interligação dos poros. Para a realização da pesquisa, células osteogênicas obtidas da calvária de ratos recém-nascidos foram cultivadas sobre as amostras de cada grupo e avaliadas quanto à adesão celular, após 24 horas, proliferação e viabilidade celular, após 7, 10 e 14 dias. A diferenciação celular foi avaliada através da mensuração do conteúdo de proteína total, atividade da fosfatase alcalina e formação de matriz nodular mineralizada nos períodos de 7, 10 e 14 dias. Os resultados obtidos com os testes ANOVA e Tukey (5%) indicaram que houve adesão celular em todas as superfícies e que esta não interferiu nos resultados. As superfícies porosas (G2 e G3) favoreceram a proliferação celular quando comparadas as superfícies densas. O conteúdo de proteína total e a formação de matriz mineralizada foram significantemente maiores nas amostras de G3. Entretanto, não houve diferença estatística nos valores da atividade da fosfatase alcalina... / Changes in physical and chemical properties on the surface of titanium seek to accelerate and improve osseointegration. Furthermore, the creation of porous substrates, provide greater strength in the osseointegrated interface due to the bone ingrowth. The aim of this study was to evaluate the influence of porosity on osteogenesis in vitro in samples of titanium. Were made by the powder metallurgy, discs of pure titanium grade 2 with 12 mm diameter and 3 mm in height, which were divided into three groups: a) G1: control - titanium machined b) G2: 30% porosity and pore with 300 μm c) G3: 40% of porosity and pore size of 300 μm. Initially, the area of 03 specimens of each group was characterized by metallography analysis, to confirm the quantity, area, shape and interconnection of pores. To conduct the study, osteogenic cells derived from calvaria of newborn rats were cultured on the samples of each group and evaluated for adhesion, after 24 hours, proliferation and cell viability after 3, 7 and 10 days. The cell differentiation was assessed by measuring the total protein content, alkaline phosphatase activity and bone-like nodule formation at 7, 10 and 14 days. The results obtained with ANOVA and Tukey tests (5%) indicated that there was cell adhesion on all surfaces and it does not interfere in the results. The porous surfaces (G2 and G3) provide better results in cell proliferation when compared to smooth surfaces. The content of total protein and the formation of bonelike nodules were significantly higher in samples from G3. However, there was no statistical difference in the values of alkaline phosphatase activity between the experimental groups. These results suggest a correlation between the surface topography of the samples and the phenomena of adherence, proliferation and cell differentiation.
|
190 |
Influência do Diabetes mellitus e da insulinoterapia sobre a osseointegração: avaliação histométrica em coelhosMargonar, Rogério [UNESP] January 2005 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:33:28Z (GMT). No. of bitstreams: 0
Previous issue date: 2005Bitstream added on 2014-06-13T21:06:11Z : No. of bitstreams: 1
margonar_r_dr_arafo.pdf: 636857 bytes, checksum: a2ff7c5e1668a51d2ac5f3e8e722334f (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / A indicação de implantes dentais osseointegráveis para pacientes com comprometimento sistêmico como o Diabetes Mellitus permanece controversa. O objetivo deste estudo foi avaliar, por meio de parâmetros histométricos, a influência do Diabetes Mellitus e da insulinoterapia sobre a osseointegração. Foram utilizados 34 coelhos adultos da raça Nova Zelândia, os quais foram divididos nos seguintes grupos: grupo controle (C), grupo diabético induzido (D) e grupo diabético tratado com insulina (DTI). A indução do diabetes foi realizada por administração de Aloxana (115 mg/kg). Os coelhos do grupo DTI receberam tratamento com injeção subcutânea de insulina (10 U/ dia) e os demais receberam solução salina (0,9%) pela mesma via. Cada animal recebeu dois implantes para análise histométrica. Após 4, 8 e 12 semanas, os animais foram sacrificados e as peças reduzidas para processamento histológico. Os três grupos não apresentaram diferenças em relação a área óssea (AO). Entretanto, o Grupo C apresentou maior extensão de contato osso/implante (ECOI) nos três períodos experimentais P<0,001 e os Grupos D e DTI não mostraram diferenças estatística em relação a ECOI P= 0,75. Assim, pode-se concluir que o Diabettes Mellitus influenciou negativamente a osseointegração de implantes colocados em tíbias de coelhos e a insulinoterapia não alterou este efeito. / The indication for the placement of osseointegrated dental implants in patients with systemic illness, like diabetes, remains controversial. The purpose of this study was to evaluate, through the histrometric parameters , the influence of Diabetes Mellitus and its treatment with insulin, on osseointegration around implants. Thirty four New Zealand adult rabbits were separated in 3 groups: control group (C), diabetes group (D) and insulin treatment diabetes group (DTI). Aloxana (115mg/kg) was used in diabetes induction. The DTI group received treatment with insulin (10 U/ day) and the others received saline solution (0,9%). After 1 week, implants were placed bilaterally in the tibiae of rabbits. After 4, 8 and 12 weeks, the animals were sacrificed and the implants were analyzed. The bone area didn'tþ show statistically greater values to the D, C e DTI groups. The C group showed statistically greater values bone contact with the surface implant than D and DTI groups in all periods (p<0,001). The groups D and DTI didn't showed any significant differences between each other in any period evaluated for bone implant contact (p=0,765). Thus, it may be concluded that Diabettes Mellitus can negatively influence the osseointegration around implants in tibiae of rabbits and insulin therapy did not altered this effect.
|
Page generated in 0.0914 seconds