The continuous development of hot forming tool steels has resulted in steels with improved mechanical properties. A change in alloying composition, primarily a decreased silicon content, makes them tougher and more wear resistant at elevated temperatures. However, it is at the expense of their machinability. The aim of this study is to explain the mechanisms behind this negative side effect. Hot work tool steels of H13 type with different Si content were characterised mechanically, and evaluated analytically and by dedicated machining tests. Machining tests verified that materials with low Si content displayed reduced machinability due to their stronger tendency to adhere to the cutting edge. Three hypotheses were tested. The first hypothesis, that the improved toughness of the low Si steels is the reason behind their relatively poor machinability, was rejected after machining tests with one low Si steel heat treated to the same relatively low toughness as conventional hot work tool steels. The second hypothesis, that a change in oxidation properties, also associated with the change in Si composition, lies behind the reduced machinability was investigated by dedicated tests and evaluations. It was found that the oxide thickness increased with reduced Si content and that there was an enrichment of Cr at the oxide/steel interface. The differences in oxide thickness and the possible differences in oxidation properties may influence the machinability of the materials through their different abilities to adhere to the cutting edge. The third hypothesis, that a high enough temperature to initiate phase transformation from ferrite to austenite is generated during machining of the tool steels, was also investigated. This may lead to a reduced machinability because higher austenite content is directly related to higher compressive stresses and higher cutting forces. This causes accelerated tool wear. This hypothesis was verified by ThermoCalc calculation of austenite content in the steels, which showed a good agreement with Gleeble compression tests and cutting force measurements. This thesis confirms that a reduced Si content in conventional H13 steel improves the toughness, reduces the oxidation resistance and lowers the ferrite-to-austenite transformation temperature. The reduction in austenite temperature is probably the most important factor behind the reduced machinability.

Chromium martensitic hot-work tool steel (AISI H13) is commonly used as die material in hot forming techniques such as die casting, hot rolling, extrusion and hot forging. They are developed to endure the severe conditions by high mechanical properties attained by a complex microstructure. Even though the hot-work tool steel has been improved over the years by alloying and heat treatment, damages still occur. Thermal fatigue is believed to be one of the most common failure mechanisms in hot forming tools. In this thesis tools used in hot forging and die casting were examined to determine damage, material response, thermal fatigue crack initiation and propagation. Different chromium martensitic hot-work tool steels, heat treated at four different austenitizing temperatures were experimentally tested in thermal fatigue and isothermal fatigue. The materials were then evaluated using X-ray line broadening analysis and transmission electron microscopy to explore the relation between fatigue softening and the change in microstructure. The high temperature fatigue softening was also simulated using an elasto-plastic, non-linear kinematic and isotropic model. The model was implemented in a numerical simulation to support the integration of die design, tool steel properties and its use. It was found that the dominant damage mechanisms in the investigated tools were thermal fatigue and that tool material experiences a three stage softening at high temperature loading. The primary stage was concluded to be influenced by the dislocation density and the second stage by the temper resistance i.e. carbide morphology. The microstructural changes during the softening stages were also connected to the non-linear kinematic and isotropic model. The general aim of this thesis is to increase the knowledge of the chromium martensitic hot-work tool steel damage, performance and microstructure.

Many phenomena determining the microstructure of a tool steel and consequently the properties of the material, are governed by multicomponent diffusion. The diffusion driven reactions that take place during, for example, tempering of a hot-work tool steel or when the microstructure develops during hot isostatic pressing of cold-work tool steel, are dependent on the types and amounts of alloying elements. In order for computational methods to be usable, these alloying effects need to be understood and incorporated in the models. In this work the influence of some typical tool steel alloying elements on the coarsening behavior of precipitates is investigated. Experimental coarsening studies are performed and the impact of the diffusion mobility descriptions and the thermodynamic descriptions are investigated by means of DICTRA coarsening calculations. The kinetic descriptions for diffusion in the body centered-cubic phase in the case of the chromium-iron-vanadium system and the chromium-iron-molybdenum system are improved by assessments of diffusion mobility parameters, and are shown to have a large impact on the calculated coarsening rate for vanadium-rich and molybdenum-rich precipitates. The effect of cobalt is examined by a coarsening experiment for vanandiumrich carbides and by a diffusion couple experiment for the investigation of the vanadium interdiffusion. The presence of cobalt is experimentally shown to have retarding effect on the coarsening rate of the carbides, but not on the vanadium diffusion. The coarsening rate of nitrogen-rich precipitates is compared to the coarsening rate of carbon-rich precipitates, and a lower coarsening rate for nitrides compared to carbides can be confirmed. Correlation between coarsening calculations and experiments is obtained suggesting that the thermodynamic description of the two systems is the underlaying reason for the different coarsening rates. Further, calculations utilizing the DICTRA software are combined with experimental investigations in order to study the possibility to apply computational methods for compound material development and explore application areas for high nitrogen alloyed tool steels produced by powder metallurgy. / <p>QC 20121011</p>

Additive manufacturing (AM) is a promising manufacturing process that provides that ability to fabricate components with complex geometries with relatively low lead times compared to other manufacturing processes. This allows for more freedom of design, as prototypes can easily be produced throughout the development process. AM is also especially beneficial in tooling applications, where internal geometries such as cooling channels are required in order to improve the quality of the manufactured parts. These geometries are more difficult to produce with more conventional manufacturing methods such as forging or casting. Currently, Laser Powder Bed Fusion (LPBF) shows the most promise in the field of Additive Manufacturing (AM) of metals, as it offers the freedom to produce complex components with little post processing required. Additionally, post processing with Hot Isostatic Pressing (HIP) can be implemented to significantly enhance the final properties of the material.  The LPBF-process can produce many different defects within the parts such as: part porosity and lack of fusion. This is mainly due to the layer-by-layer configuration of the process. Parts can also experience large thermal fluctuations and rapid cooling rates which can generate large residual stresses. This can result in significant cracking in certain high alloyed materials which can impact part quality and  material properties. If the cracking is severe enough, it will result in failure of the entire component and render the entire parts completely useless. Post processing with HIP may remove some of these defects and reduce the residual stresses in the material and thus produce a material with properties that are satisfactory. The purpose of this thesis is to investigate the processability of a high alloy cold work tool steel with LPBF. The main focus is the influence of the processing parameters and part geometry on the quality of the produced parts. Furthermore, the influence of the processing parameters on defects and microstructure will also be investigated. The aim is to produce parts that can be enhanced with HIP as a post processing treatment. Additionally, the impact of HIP on the properties of the part will also be investigated in order to determine if the there are any improvements in terms ofreduction in part defects and the removal of any undesired microstructural features which are produced from the process. The experimental results showed that the processability of the tool steel is difficult. Several sample volumes were produced with varying processing parameters and scanning strategies, and all the specimens from all sample volumes exhibited some cracking. Parts produced with a combination of contouring and hatching strategy, where there is an internal structure showed the most promise, as these parts exhibited the least amount of severe cracking. However, additional research of the processing parameters and scanning strategies is required in order to reduce the amount of cracking of the external shell structure and thus, achieve proper densification of the parts when post processing with HIP. / Additiv tillverkning (AM) är en lovande tillverkningsprocess som ger möjligheten att tillverka komponenter med komplexa geometrier med relativt låga ledtider jämfört med andra tillverkningsprocesser. Detta ger större frihet i under designprocessen eftersom prototyper enkelt kan produceras under hela utvecklingsprocessen. AM är också särskilt fördelaktigt i verktygstillämpningar, där interna geometrier såsom kylkanaler krävs för att förbättra kvaliteten på de tillverkade delarna. Dessa geometrier är svårare att tillverka med mer konventionella tillverkningsmetoder som smidning eller gjutning. För närvarande visar det sig att Laser Powder Bed Fusion (LPBF) är det mest lovande inom området additiv tillverkning av metaller, eftersom processen erbjuder friheten att producera komplexa komponenter samt att efterbearbetning som krävs blir mindre. Dessutom kan efterbearbetning med Hot Isostatic Pressing (HIP) implementeras för att avsevärt förbättra materialets slutliga egenskaper. LPBF-processen kan ge upphov till många olika defekter i delarna såsom: delporositet och lack of fusion. Detta beror främst på att processen sker lagervis vilket kan ge upphov att många småfel. Delar kan också uppleva stora termiska fluktuationer och snabba kylningshastigheter som kan generera stora restspänningar. Det kan resultera i stor sprickbildning i vissa höglegerade material vilket kan påverka delarnas kvalitet och materialegenskaper. Om sprickorna som bildas är stora eller djupa nog kommer detta att resultera i att hela komponenten blir oanvändbar. Efterbearbetning med HIP kan ta bort en del av dessa defekter och minska restspänningarna i materialet och därmed producera ett material med goda egenskaper. Syftet med detta arbete är att undersöka bearbetbarheten hos ett höglegerat kallbearbetningsstål med som produceras med LPBF. Huvudfokus är påverkan av processparametrar och detaljgeometrin på kvaliteten på de producerade delarna. Vidare kommer också processparametrarnas inverkan på defekter och mikrostruktur att undersökas. Syftet är att producera delar som kan förbättras med HIP som efterbehandlingsbehandling. Dessutom kommer effekterna av HIP på delens egenskaper också att undersökas för att avgöra om det finns några förbättringar i termer av minskning av deldefekter och avlägsnande av alla oönskade mikrostrukturella egenskaper som produceras från processen. De experimentella resultaten visade att verktygsstålets bearbetbarhet är svår. Flera provvolymer producerades med varierande processparametrar och skanningsstrategier, och alla prover från alla provvolymer uppvisade viss sprickbildning. Delar som tillverkats med en kombination av kontur och hatch, där det finns en inre struktur visade sig mest lovande, eftersom dessa delar uppvisade minst sprickbildning. Ytterligare arbete av processparametrarna och skanningsstrategier krävs dock för att minska mängden sprickbildning i den yttre skalstrukturen och därmed uppnå korrekt förtätning av delarna vid efterbearbetning med HIP.

The demand for Advanced High Strength Steel (AHSS) in the automotive industry is increasing day by day. It is mainly motivated by the fact that AHSS can be used as thin sheets while having high strengths. It enables weight reduction of the automobiles which consequently increases the fuel efficiency and has proven to be less harmful to the environment. It is also expected that AHSS will have even higher strength in the near future. Cold work tools steels with 5 wt.% Cr are commonly used to process AHSS. Therefore, the tool steel must meet the challenges in the future, i.e. have even higher hardness, compressive strength and toughness. One way of increasing the mechanical properties of the tool steel is by improving the heat treatment parameters. However, it is not possible without a deeper understanding of the heat treatment process. Therefore, this work presents investigations related to phase transformations occurring in a 5 wt.% Cr cold work tool steel during heat treatment. Furthermore, the influence of austenitisation and tempering temperatures on the microstructure and mechanical properties were investigated. The studies revealed that a higher austenitisation temperature can be used to achieve a higher hardness, good compressive strength and adequate toughnessof the steel. However, too high austenitisation temperature may result inexcessive coarsening of prior austenite grains which reduced the impact toughness. It was also found that retained austenite can transform during tempering by two different mechanisms. Firstly, when tempering at 525°C, carbides precipitate in retained austenite lowering its stability and permitting a transformation to marten site on cooling. Secondly, when tempering at 600°Cfor extended holding time retained austenite isothermally transforms to ferrite and carbides. This occurs by precipitation of carbides in retained austenite followed by a final transformation to ferrite and carbides.These results were used to understand the standard tempering procedure of the 5 wt.% Cr cold work tool steel. Furthermore, alternative heat treatment procedures are discussed based on the important findings presented in this thesis.

Hot-work tool steels make up an important group of steels that are able to perform with good strength and toughness properties at elevated temperatures and stresses. They are able to gain this behavior through their alloy composition and heat treatment, which relies on the precipitation of alloy carbides to counter the loss in strength as the tempered material becomes more ductile. As demand grows for materials that are suitable for even harsher applications and that show improved mechanical qualities, the steel industry must continuously investigate the development of new steel grades. Within this context, the present work focuses on examining the mechanical properties and microstructure of two hot-work tool steels, of which one is a representative steel grade (Steel A) and the second a higher-alloyed variant (Steel B), at different tempering conditions. To complement the experimental work, precipitation simulations are used to monitor the progression of secondary carbide precipitation and to examine the predicted microstructural changes through varying the alloy composition. The study finds that Steel B does not actually have improved properties with respect to Steel A and suggests that the precipitation behavior of both steels is virtually identical. Despite this, the simulation work reveals that this behavior can change dramatically to favor more positive hardness contributions by increasing the alloy content of V. In short, with the project being part of an ongoing investigation, there remain several areas of analysis that need to be completed before offering a complete picture that can ultimately play a part in the development of a new hot-work tool steel grade.

The present interview revolves around electronic mal of employees as a work tool and his relationship with the right of privacy and secrecy of telecommunications. Thus, it attempts to figure out the nature of electronic mail and other technologies as work tools, making difference from this same technologies in a personal context. / La presente entrevista gira en torno al correo electrónico del empleado como herramienta de trabajo y su interrelación con el derecho de la intimidad y el secreto de las telecomunicaciones. Así, se intenta descifrar cuál es la naturaleza del correo electrónico y otras tecnologías como herramientas de trabajo, a diferencia de las tecnologías de uso personal.

Im Rahmen der vorliegenden Arbeit wurde die drahtbasierte additive Fertigung mittels Elektronstrahls (WEBAM) unter Nutzung einer lateralen Drahtzuführung und des Warmarbeitsstahls X37CrMoV5-1 untersucht. Die Schwerpunkte lagen auf der Analyse des Einflusses der Prozessparameter, der Drahtführungstechniken (schleppend, stechend und seitlich), des Substratwerkstoffes und des Materialübergangs auf die Prozessstabilität sowie die Auftraggeometrie. Das Ziel war die prozesssichere Herstellung von 3D-Geometrien mit bidirektionaler und kontinuierlicher Aufbaustrategie. Die Untersuchungen zeigten, dass die Auftraggeometrie und insbesondere der Materialübergang wesentlich vom Substratwerkstoff abhängig waren. Anhand eines aufgestellten Prozessfensters wurde ein Parametersatz ermittelt, welcher unabhängig von der Drahtführungstechnik nahezu identische Auftraggeometrien erzeugte. Mit Hilfe einer dynamischen Anpassung des Positionsversatzes für die jeweilige Drahtführungstechnik konnten rissfreie Aufbauten mit bidirektionaler, alternierender Aufbaustrategie generiert werden. Diese Aufbauten wurden anschließend hinsichtlich der Mikrostruktur sowie der mechanischen Eigenschaften in Abhängigkeit vom Wärmebehandlungszustand charakterisiert. Die Prozessstabilität und Reproduzierbarkeit konnte anhand von mehreren aufgebauten 3D-Geometrien mit hoher Konturtreu demonstriert werden.

Additive manufacturing (AM) is an emerging and interesting technology that enables some of theproduct development projects (PDPs) to produce products that have mechanical and tribologicalproperties comparable to products that are conventionally manufactured. Selective laser melting(SLM) is an additive manufacturing technology that is predominantly used for the production of metalbased components (i.e. it could be pure metal, alloys, and metal matrix composites). This workevaluates and ranks two different steel grades produced with SLM technology in tribological andcutting tool applications at AB Sandvik Coromant. The two steel grades used in this work were Cofree maraging steel alloy and Co-free W360 AMPO alloy. Both the grades are Cobalt free, hencedeveloped as a sustainable alternative for the future. The W360 AMPO alloy is a hot-work tool steelwith high temperature wear resistance and heat resistance. The work covers the characterization ofmicrostructure and chemical composition, mechanical properties, and tribological properties toevaluate the performance of the tool steel grades when used as tool bodies in drilling applications.The microstructure and chemical composition of the additive manufactured and heat-treated tool steelswere analyzed using SEM and EDS. The mechanical properties were evaluated using micro-Vickersindentation and scratch testing while the tribological properties were evaluated using pin-on-disctesting where counter material used was quenched and tempered steel. The application test included asimulated chip wear test using chip breakers (CB’s) and an actual drilling test, both performed at ABSandvik Coromant. To study the effect of surface topography on the adhesion tendency, the simulatedchip wear test was performed on both milled and grounded chip breaker (CB) samples. The drillingtest was done with three different test-set ups; function test, 30° inclined exit, and forced tool life test.The cellular microstructure was observed on Co-free maraging steel alloy sample, while themicrostructure was tempered martensite in W360 AMPO alloy. Elemental analysis revealed thechemical composition of the two steel grades. The measured hardness for both the samples Co-freemaraging steel alloy and W360 AMPO was found to be within the specification of demands (50-52HRC), although the hardness of W360 AMPO was a bit higher than Co-free maraging steel alloy. Theresults of the pin-on-disc tests showed that the wear resistance of the W360 AMPO alloy issignificantly higher than that of the Co-free maraging steel alloy, the tribo-system used was similarwhen compared to the actual application. Also, after analyzing the pin made up of quenched andtempered steel 34CrNiMo6 (SS2541) it can be seen that due to the W360 AMPO sample the volumeloss of the pin is almost 4 times when compared to Co-free maraging steel alloy. The result from thesimulated chip wear test showed that W360 AMPO has better wear characteristics. Adhesion ofworkpiece material (SS2541) was observed on both samples. In the simulated chip wear test, thesurface topography effect was studied by performing a test on milled and grounded CBs. GroundedCBs showed less adhesion tendency compared with milled CBs on both samples but the wearcharacteristics were similar irrespective of the surface roughness. The result from the drilling testshowed wear scar was predominant on a drill with Co-free maraging steel alloy and a drill with W360AMPO alloy was intact. Future possible investigations proposed after findings from experimentalresults may lead to future work.

The main problem encountered in this thesis is the lack of research and knowledge of selective laser melted-printing with Uddeholm Dievar®. This absence of information could cause issues regarding quality and properties of the alloy as well as uncertainty regarding an appropriate heat treatment cycle. This thesis mainly focuses on observing the changes that occur in the microstructure when Uddeholm Dievar® is manufactured through the additive manufacturing (AM) method known as selective laser melting (SLM). The SLM- method consists of a high-power laser that melts together thin layers of powder, one layer at a time, until a three-dimensional product is created according to selected drawings. The methodology on which this thesis is based on is the execution of a theoretical study, scientific experiments and thermodynamic calculations. Analysis of the microstructure is performed using a scanning electron microscope with techniques such as Energy-dispersive X-ray spectroscopy (EDS) and Electron backscatter diffraction (EBSD). The purpose of the methods are to map the constituent elements of the alloy and observe the orientation of the crystallographic phases in the atomic lattice respectively. The results show that the powder, both before and after printing, mainly consists of martensite with a low amount of residual austenite. The amount of primary carbides is relatively low and has been classified as MC (V-rich) and/or M6C (Mo- rich) type. The remaining residual austenite could be explained by the segregation of constituent alloying elements, where the carbon content is a dominant factor to why the MS -temperature lowers significantly causing the presence of retained austenite even though SLM has a cooling rate that varies between 103 and 108 [K/s]. / Det huvudsakliga problemet som denna avhandling behandlar är bristen på forskning och kunskap inom selective laser melting (SLM) 3D-printing med Uddeholm Dievar®. Avsaknaden kan leda till sämre kvalité och produktegenskaper hos legeringen. Det kan även leda till ovisshet gällande val av lämplig värmebehandling. Arbetet fokuserar på att dokumentera utformningen av stålets mikrostruktur när Uddeholm Dievar® tillverkas med den additiva tillverkningsmetoden SLM. Tillverkningsprocessen består av en högeffektslaser som detaljerat smälter samman tunna lager pulver, ett lager i taget, tills att en tredimensionell produkt skapats utefter valda ritningar. Använda metoder är; utförandet av en teoretisk studie, vetenskapliga experiment och thermodynamiska beräkningar. Analys av mikrostrukturen genomförs med hjälp av svepelektronmikroskåp där teknikerna Energy-dispersive X-ray spectroscopy (EDS) och Electron backscatter diffraction (EBSD) används. Syftet med EDS är att kartlägga de ingående elementen i legeringen, syftet med EBSD är att se orientering av de kristallografiska faserna i atomgittret. Resultaten visar på att legeringen, både före och efter printing, till största del består av martensit med en låg mängd restaustenit. Mängden primärkarbider är relativt låg och har klassifiserats som typen MC (V-rik) och/eller M6C (Mo- rik). Den kvarstående restausteniten kan möjligen förklaras av segringen av ingående legeringsämnen där kolhalten är en dominerande faktor som sänker MS-temperaturen. Detta gör att restaustenit förekommer trots den höga kylhastigheten som varierar mellan 103 och 108 [K/s] i SLM.