Tese de mestrado. Engenharia Biomédica. Faculdade de Engenharia. Universidade do Porto, Faculdade de Medicina Dentária. Universidade do Porto. 2008

No description available.

Dissertation submitted for obtain the degree of Doctor of Philosophy, at the University of Porto, Faculty of Engineering

The success of alloplastic bone grafts is still limited because of inadequate osseointegration. In this study, TiO2 nanocrystals (21 nanometers) were synthesized by wet-chemical co-precipitation Their structure, size and purity were determined by Raman spectroscopy (RAMAN) and x-ray diffraction (XRD). Optical microscopy was used to evaluate inflammation arising from intraosseous implants in guinea pigs as recommended by the World Dental Federation (FDI). Ten guinea pigs were used receiving two implants each. Half of the guinea pigs were observed at four weeks and the rest at twelve weeks. 24 slides were prepared with 144 histological cuts, stained with hematoxylin-eosinand and analyzed for inflammation response by two independent observers. It was determined that inflammation was absent/mild at both time periods due to low cellular variability and direct and structural bone apposition on and around the material without visible separation or signs of rejection. These characteristics were observed in all samples. Nanotopography analysis and Atomic Force Microscopy (AFM) showed integration between the new bone and the implanted material. Therefore, through the methodology used, it was possible to evidence osseointegration and biocompatibility in alloplastic material at the nanoscale. / O sucesso dos enxertos ósseos como material aloplástico apresenta-se, ainda, limitado, devido à sua não capacidade de efetiva osseointegração. Neste estudo, sintetizamos nanocristais de TiO2 com tamanho médio de 21 nanometros através de uma via úmida, por co-precipitação. Verificamos suas propriedades físicas, quanto à estrutura, tamanho e grau de pureza, por espectroscopia micro Raman (RAMAN) e Difração de Raios X (DRX). Por microscopia ótica avaliamos a resposta inflamatória, através de implantes intra-ósseos em cobaias guinea pigs, (cavia porcellus), como recomendado pela Federação Dentária Internacional (FDI). Dez cobaias foram utilizadas nos períodos experimentais de quatro e doze semanas. Cada animal recebeu dois implantes. De cada implante foram confeccionados 24 lâminas com 144 cortes histológicos, corados com hematoxilina-eosina e analisadas as respostas inflamatórias, por dois observadores independentes. Verificaram respostas ausentes/suaves em ambos os períodos, devido à baixa variabilidade celular e aposição óssea direta e estrutural respeitando e contornando o material, sem apresentar uma superfície de separação visível, sem sinais de rejeição. Característica observada em todas as amostras. Por análise da nanotopografia, com Microscopia de Força Atômica (AFM), evidênciamos a integração entre o osso neoformado e o material implantado. Assim, através da metodologia empregada foi possível evidenciar os fenômenos da osseointegração e biocompatibilidade em um material aloplástico em escala nanométrica. / Mestre em Odontologia

Orientador: José Eduardo Junho de Araújo / Banca: Cícero Eleutério da Silva Filho / Banca: Yasmin Rodarte Carvalho / Resumo: Com o objetivo de avaliar histopatologicamente o comportamento pulpar pós-cimentação de coroas totais metálicas (CTM) com um cimento de fosfato de zinco (Lee Smith, Vigodent) e dois cimentos de ionômero vítreo (Ketac-Cem, ESPE; Vidrion C, SSWhite), foram realizados 27 preparos coronários em pré-molares íntegros indicados para exodontia com a finalidade de tratamento ortodôntico. As exodontias foram realizadas após três, dez e trinta dias da cimentação. Para o exame histopatólogico a polpa foi removida do dente e corada pelo hematoxilina e eosina. Os resultados mostraram que aos três dias, que seis das nove polpas apresentavam alguma reação inflamatória, o comportamento entre os cimentos foi diferente quanto ao grau de resposta inflamatória, a reação inflamatória persistiu após trinta dias com o Lee Smith (CFZ) e Ketac-Cem (CIV), o grupo do Vidrion C (CIV) foi o qual apresentou melhor biocompatibilidade. A metodologia usada permitiu uma avaliação das condições pulpares em um período mais curto que o processo convencional de descalcificação, entretanto não possibilitou a observação da interação polpa/dentina / Abstract: The purpose of this study was to conduct an histological evaluation of pulp rections of teeth after cementation of complete metal crowns with one of the following luting agents: zinc phosphate cement (ZPC) (Lee Smith, Vigodent) and two glass ionomer cements (Ketac Cem, ESPE, Vidrion C, SSWhite). Twenty seven sound bicuspids scheduled for extraction by orthodontic treatment were prepared for complete crowns, casts were made and luted with one of the above cements. Three, ten and thirty days after cementation the teeth were removed, split in two halves and the pulps detached from one of the halves, stained with H.E. and pulpal reactions assessed by optical microscopy. Results showed dissimilar inflammatory responses that were associated to the different cementing agents. For specimens of the ZPC and Ketac-Cem groups the inflammatory reaction subsided for 30 days. For the Vidrion C group only 2 out of 9 specimens showed pulpal inflammatory reactions. Therefore, regarding biocompatibility, best results were seen with the specimens ofthe Vidríon C group. The method allowed a quick assessment of pulp conditions when compared to the traditional decalcifiyng process. However, observations of dentin-pulp relationships could not be noticed / Mestre

Submitted by Aline Cardoso Pereira (aline.cardosopereira@hotmail.com) on 2018-08-02T22:27:37Z No. of bitstreams: 1 DISSERTAÇÃO DE MESTRADO - ALINE C. PEREIRA.pdf: 2161021 bytes, checksum: 07880c29666b475277e0461208a4bf5a (MD5) / Approved for entry into archive by Isabel Pereira de Matos (isabel@fmva.unesp.br) on 2018-08-03T18:51:33Z (GMT) No. of bitstreams: 1 pereira_ac_me_araca_int.pdf: 2161021 bytes, checksum: 07880c29666b475277e0461208a4bf5a (MD5) / Made available in DSpace on 2018-08-03T18:51:33Z (GMT). No. of bitstreams: 1 pereira_ac_me_araca_int.pdf: 2161021 bytes, checksum: 07880c29666b475277e0461208a4bf5a (MD5) Previous issue date: 2018-06-15 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / As ceratites ulcerativas são comuns na rotina do médico veterinário de pequenos animais, visto que a córnea é uma estrutura vulnerável devido sua exposição ao meio externo. Por compreender uma das estruturas responsáveis pela refração luminosa e participante do mecanismo de formação da imagem, é de extrema importância a integridade da anatomia e transparência da córnea para esta continuar desempenhando suas funções. Estudos ainda são realizados com o intuito de viabilizar opções terapêuticas cirúrgicas para o tratamento de úlceras de córnea complicadas, tentando alcançar uma cicatrização com um menor dano à estrutura corneal e menor opacidade cicatricial, devolvendo a transparência da córnea. Visto que os polímeros biodegradáveis tem se mostrado alvo de pesquisas atuais para aplicações médicas, com este estudo objetivou-se avaliar originalmente a biocompatibilidade da membrana do polímero poli(butileno adipato-co-tereftalato) (PBAT) na córnea e posterior aplicação clínica deste material nas ceratites ulcerativas profundas. Para tal, foi realizada avaliação clínica experimental e histopatológica após enxertia interlamelar do PBAT em córnea de coelhos, ao longo de 60 dias, e acompanhamento da evolução clínica do emprego da membrana de PBAT no tratamento de ceratites ulcerativas complicadas em cães, comparando ao uso do enxerto conjuntival, ao longo de 90 dias. Devido aos baixos sinais de inflamação corneal clínicos e histopatológicos nos coelhos e a cicatrização corneal em todos os cães, sem ocorrência de déficit visual, com o presente estudo acreditamos ter viabilizado mais uma opção terapêutica para as ceratites ulcerativas na medicina veterinária. / Ulcerative keratitis are common in the routine of a small animals veterinary doctor, given that the cornea is a vulnerable structure due to its exposure to external environment. For containing one of the structures responsible for light refraction and participant in the mechanism of formation of images, it is of extreme importance the integrity and transparency of the cornea in order for it to continue to develop its functions. Studies are still performed with the intent of making feasible surgical therapeutic options for the treatment of complicated corneal ulcers, trying to reach cicatrization with less damage to the corneal structure and less scar opacity, seeking corneal transparency. Given that biodegradable polymers have been target of current research for medical applications, the objective of this study was to evaluate originally the biocompatibility of the poly (butylene adipate-co-terephthalate) polymer (PBAT) in the cornea and posterior clinical application of this material in deep ulcerative keratitis. It was performed clinical and histopathological evaluation after interlamellar grafting of PBAT in the cornea of rabbits, over 60 days, and follow-up of the clinical evolution of PBAT membrane in the treatment of complicated ulcerative keratitis in dogs, comparing to the use of conjunctival graft, over 90 days. Due to low levels of clinical and histopathological corneal inflammation found in rabbits and corneal cicatrization in all dogs, without occurence of visual deficit, with this study we believe it was made feasible another therapeutic option for ulcerative keratitis in veterinary medicine.

Orientador: Carlos Frederico de Oliveira Graeff / Banca: Luis Augusto Sousa Marques da Rocha / Banca: Carlos Roberto Grandini / Banca: Mariselma Ferreira / Banca: Rondinelli Donizetti Herculano / Resumo: O latéx ou Borracha natural (BN) oriundo da seringueira possui diversas características que o tornam uma excelente biomaterial que favorece o crescimento e reparação de tecidos, pele e ossos. Porém, a maioria das pesquisas encontradas na literatura com membranas da BN utiliza mistura de diferentes clones ou conservantes químicos, a fim de evitar a coagulação da BN na coleta. Neste trabalho, comparou-se a BN proveniente de cinco clonos de seringueira, buscando identificar diferenças na biocompatibilidade e bioatividade, comparando métodos de coleta convencionais e sem utilização de conservantes, visando encontrar a BN ideal para produção de biomateriais. Após a coleta da BN, as membranas foram preparadas de forma asséptica e esterelizadas. Nos testes de biocompatibilidade in vitro, as membranas permaneceram em contato direto com as culturas por três períodos. E nos testes in vitro, as membranas foram implantadas no tecido subcutâneo de coelhos adultos machos. Os testes de bioatividade foram realizados por meio de implantes das membranas de BN com melhor desempenho nos testes de bioatividade, associado ao selante de fibrina em defeitos críticos no crânio de coelhos adultos. Os resultados apontam a biocompatibilidade das membranas de BN obtidos de todos os clones. Alguns induziram maior proliferação celular, sugerindo maior bioatividade. O método de coleta influenciou na resposta do biomaterial. Amostras conservdas com hidróxido de amônio apresentaram efeitos citotóxicos e genotóxicos em culturas e necrose, aumento de células inflamatórias nos tecidos implantados. As membranas testadas são bioativas e favoreceram a regeneração tecidual, apresentando um resultado superior ao PTFE. Os dois clones testados não apresentam diferenças na bioatividade. Concluímos que todos os clones são biocompatíveis... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The latex derived from rubber trees has several features that make it an excellent biomaterial to promote the growth and repair of tissues, skin and bones. Most research with latex membranes uses a mixture of different clones or chemical preservations in the collection process. In this study, we compared five clones of latex rubber, seeking to identify their diferences in bioactivity and biocompatibility in order to find a latex that is ideal for the production of biomaterials, as well to compare smapling methods with and without the use of preservatives. After collection, the latex membranes were prepaerd aseptically and sterilized. In the in vitro tests, the membranes remained in direct contact with crops for three periods. In the in vivo tests, the membranes were implanted subcutaneously in rabbits. The results indicated the biocompatibility of the membranes obatined from all clones. Some induced greater cell proliferation, suggesting greater bioactivity. Regarding the collection method, we found that the biomaterial samples preserved with ammonia showed cytotoxic and genotoxic effects in cultures, necrosis, and increased inflammatory cells inflammatory cells in tissues implanted. The membranes are bioactive and promote the tissue regeneration, an outcome superior to PTFE. The two clones tested did not show differences in bioactivity. We conclude that all clones are biocompatible and non-genotoxic. The two clones selected for bioactivity test not show significant in the bioactivity. The collection of BN without the use of preservatives is the most suitable for the production of biomaterials... (Complete abstract click electronic access below) / Doutor

Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2007 / Bibliografia: f. 64-68 / O vitrocerâmico de Anortita é um material biocompatível que apresenta propriedades de materiais inteligentes, pois sofre degradação de acordo com a variação do pH do meio em que se encontra. Essa característica faz com que a Anortita seja de especial inte / Anortita glass-ceramic is a biocompatible material that shows intelligent material properties, since its degradation occurs depending on pH variation. This characteristic is particularly interesting when regarding clinical applications in which the materi

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia / Made available in DSpace on 2013-06-25T22:25:29Z (GMT). No. of bitstreams: 1 310428.pdf: 1725310 bytes, checksum: 9f49e9537954cd759ff4aac120cee16c (MD5) / O objetivo deste estudo foi avaliar a biocompatibilidade dos cimentos iRoot SP, MTA FILLAPEX, DiaRoot e MTA BRANCO através da análise da reação tecidual estimulada após a implantação de tubos de dentina preenchidos com os cimentos, em tecido subcutâneo de ratos. Foram utilizados 32 ratos, divididos em 4 grupos, de acordo com os materiais e períodos experimentais de 7, 15, 30 e 90 dias. Quatro tubos de dentina preenchidos com os cimentos e um quinto tubo, deixado vazio (controle), foram implantados no tecido subcutâneo de cada um dos ratos em 5 sítios, na região dorsal. Passados os períodos experimentais, foi realizada a eutanásia dos animais e os tubos e tecidos circundantes foram excisados em bloco. Após a fixação do tecido, os tubos de dentina foram cuidadosamente removidos e o tecido foi processado para inclusão em parafina. Foi realizada a coloração de Hematoxilina e Eosina para observação da morfologia tecidual, e os seguintes critérios foram avaliados: organização, composição e espessura da cápsula conjuntiva, intensidade da inflamação, presença de células gigantes multinucleadas (CGMNs), macrófagos, necrose tecidual e neovascularização. Também foi realizada a técnica de Von Kossa para avaliação de estruturas calcificadas, bem como análise em microscópio de luz polarizada, para observação de cristais de calcita. Os dados foram submetidos ao teste exato de Fischer e/ou Kruskal-Wallis a um nível de significância de 5%. Não foram observadas diferenças significativas entre os grupos em relação à intensidade da reação inflamatória, espessura e organização da cápsula conjuntiva nos diferentes períodos experimentais. Foram observadas diferenças significativas em relação à presença de CGMNs, macrófagos e necrose tecidual, sendo estas variáveis mais frequentes nos espécimes do MTA FILLAPEX e no iRoot SP. Em todos os grupos foi observada positividade ao Von Kossa, relacionada às áreas de necrose, porém, não foram detectados cristais de calcita. Todos os cimentos demonstraram biocompatibilidade, visto que as reações teciduais foram atenuando-se ao longo do tempo, exceto o MTA FILLAPEX que, aos 90 dias, ainda estimulou uma reação inflamatória moderada no tecido adjacente, necrose tecidual, presença de células gigantes multinucleadas e macrófagos fagocitando partículas do cimento. / The aim of this study was to evaluate the biocompatibility of the sealers iRoot SP, MTA FILLAPEX, DiaRoot BioAggregate and MTA BRANCO through the analysis of the tissue reaction stimulated by the implantation of dentin tubes filled with the sealers in the subcutaneous tissue of rats. We used 32 rats, divided into 4 groups of 8 animals, according to the materials and experimental periods of 7, 15, 30 and 90 days. Four dentin tubes, each filled with one of the experimental sealers and a fifth tube, left empty (control), were implanted in the subcutaneous tissue of each rat at 5 locations equidistant, in the dorsal area. After the experimental periods, the animals were submitted to euthanasia and the tubes with surrounding tissue were excised. After fixation, the dentin tubes were carefully removed and the surrounding tissue was processed for parafin inclusion. Staining was performed with Hematoxylin and Eosin to evaluate tissue morphology using the following criteria: organization, composition and thickness of the connective capsule, intensity of inflammation, presence of multinucleated giant cells, macrophages, tissue necrosis and neovascularization. Von Kossa staining was also performed as well as microscope evaluation under polarized light to observe calcite crystals. Data were analysed using Fisher#s exact test and the Kruskal-Wallis test at a significance level of 5%. There was no statistically significant difference among the scores of different groups regarding the intensity of the inflammatory reaction, thickness or organization of the connective capsule in the different experimental periods. Statiscally significant differences were observed between the groups regarding the presence of multinucleated giant cells, macrophages and necrosis, more visible in MTA FILLAPEX and iRoot SP. In all groups were observed Von Kossa positivity related to areas of necrosis but calcite crystals were not detected. All sealers were found to be biocompatible since the tissue reactions decreased during the experimental periods, except in the case of MTA FILLAPEX that, at 90 days, still stimulated a moderate inflammatory reaction in the adjacent tissue, tissue necrosis, presence of multinucleated giant cells and macrophages phagocyting particles of the sealer.

Made available in DSpace on 2014-06-11T19:25:36Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-08-26Bitstream added on 2014-06-13T19:53:33Z : No. of bitstreams: 1 kanamura_ms_me_botfm.pdf: 2849170 bytes, checksum: 08cc2f979c93a13d548fc6f0228e430f (MD5) / Universidade Estadual Paulista (UNESP) / Apesar da existência de inúmeros tipos de implantes para reposição de volume em cavidades anoftálmicas, até o momento, nenhum deles pode ser considerado ideal, o que faz com que seja necessário continuar buscando novas soluções. Avaliar a biocompatibilidade de esferas de silicone gelatinosas e rígidas, quando colocadas em cavidades evisceradas de coelhos, comparando-as. Estudo prospectivo e experimental, no qual foram utilizados 30 coelhos albinos, espécie Orictolagus cuniculus, submetidos à cirurgia de evisceração do olho direito, sendo feita a colocação de esferas de silicone gelatinosas ou rígidas na cavidade escleral. Os animais foram sacrificados sete, 30 e 90 dias após a colocação das esferas. Os parâmetros avaliados foram: avaliação clínica diária, ultrassonografia da cavidade eviscerada 15 dias após o procedimento, análise histológica do conteúdo orbitário sete, 30 e 90 dias após a cirurgia, com análise morfométrica da pseudocápsula que se formou ao redor das esferas. Os resultados obtidos foram submetidos à avaliação estatística para comparação dos resultados entre e dentro dos grupos experimentais. Durante o seguimento, ocorreram três extrusões de esferas, duas das quais pertencentes ao grupo das esferas rígidas e uma, do grupo das esferas gelatinosas. O exame ultrassonográfico mostrou ausência de coleções ou processo inflamatório ao redor das esferas e boa integração das mesmas com os tecidos orbitários. Ao exame histológico observou-se semelhança de resposta tecidual com ambas as esferas. O exame morfométrico apontou para superioridade das esferas gelatinosas no tocante a espessura da pseudocápsula, que foi menos espessa, principalmente na avaliação feita no setor posterior da cavidade escleral. Todos os parâmetros estudados mostraram que as esferas de silicone... / Despite the existence of many types of implants for volume replacement in anophthalmic sockets, so far, none can be considered ideal implant, which makes it necessary to continue searching for new solutions. To evaluate the biocompatibility of soft and rigid silicone spheres placed in scleral cavities of eviscerated rabbits, comparing them. Prospctive and experimental study using 30 rabbits, specie Orictolagus cuniculus, underwent evisceration surgery of the right eye and replacement of orbital volume with spheres composed by gelatinous (soft) or rigid silicone. The animals were sacrificed seven, 30 and 90 days after surgery. The studies parameters were: daily clinical assessment, ultrasound of the orbit 15 days after the procedure, histological analysis of the orbital contents seven, 30 and 90 days after surgery and morphometric evaluation in the pseudocapsule in all the animals. Statistical analysis for comparison between and within groups was done. During follow-up occurred three spheres extrusions, two of which belonging to the group of rigid spheres and one from gelatinous sphere group. Ultrasound examination showed no inflammation or collections around spheres and good integration with the orbital tissues. The histological evaluation proved both materials had similar response and the morphometric evaluation showed thinner pseudocapsule formation around the gelatinous sphere, mainly in the posterior scleral region. All the parameters evaluated showed both spheres had good tecidual integration to the orbital tissue in rabbit eviscerated eyes. Therefore, gelatinous silicone sphere induced thinner psedudocapsule formation. The authors agree the gelatinous silicone spheres might be helpful to be used... (Complete abstract click electronic access below)