Magnetic and Magneto-Transport Properties of Hard Magnetic Thin Film Systems / Magnetische und magnetoresistive Eigenschaften von hartmagnetischen DünnschichtsystemenMatthes, Patrick 21 March 2016 (has links) (PDF)
The present thesis is about the investigation of ferromagnetic thin film systems with respect to exchange coupling, magnetization reversal behavior and effects appearing in magnetic heterostructures, namely the exchange bias and the giant magnetoresistance effect. For this purpose, DC magnetron sputtered thin films and multilayers with perpendicular magnetic anisotropy were prepared on single crystalline and rigid as well as flexible amorphous substrates.
The first part concentrates on magnetic data storage applications based on the combination of the concept of bit patterned media and three dimensional magnetic memory, consisting of at least two exchange decoupled ferromagnetic storage layers. Here, [Co/Pt] multilayers, revealing different magnetic anisotropies, have been applied as storage layers and as spacer material Pt and Ru was employed. By the characterization of the magnetization reversal behavior the exchange coupling in dependence of the spacer layer thickness was studied. Furthermore, with regard to the concept of bit patterned media, the layers were also grown on self-assembled silica particles, leading to an exchange decoupled single-domain magnetic dot array, which was studied by magnetic force microscope imaging and angular dependent magneto-optic Kerr effect magnetometry to evaluate the reversal mechanism and its dependence on the array dimensions, mainly the diameter of the silica particles and layer thicknesses. To complete the study, micromagnetic simulations were performed to access smaller dimensions and to investigate the dependence of intralayer as well as interlayer coupling on the magnetization reversal of the dot array with multiple storage layers.
The second part focuses on the investigation of the giant magnetoresistance effect in systems with perpendicular magnetic anisotropy, where L10 -chemically ordered FePt alloys and [Co/Pt] as well as [Co/Pd] multilayers were utilized. In case of FePt, where high temperatures during the deposition are necessary to induce the chemical ordering, diffusion and alloying of the spacer material often prevent a sufficient exchange decoupling of the ferromagnetic layers. However, with Ru as spacer material a giant magnetoresistance effect could be achieved. Large improvements of the magnetoresistive behavior of such trilayer structures are presented for [Co/Pt] and [Co/Pd] multilayers, which can be deposited at room temperature not limiting the choice of spacer as well as substrate material. Furthermore, in systems consisting of one ferromagnet with perpendicular magnetic anisotropy and one ferromagnet with in-plane magnetic easy axis, a linear and almost hysteresis-free field dependence of the electrical resistance was observed and the behavior for various thickness series has been intensively studied. Finally, the corrosion resistance in dependence of the capping layer material as well as the magnetoresistance of a strained flexible pseudo-spin-valve structure is presented.
In addition, in chapter 2.5.2 an experimental study of an improved crystal growth of FePt at comparable low temperatures by molecular beam epitaxy and further promoted by a surfactant mediated growth using Sb is shown. Auger electron spectroscopy as well as Rutherford backscattering spectrometry were carried out to confirm the surface segregation of Sb and magnetic characterization revealed an increase of magnetic anisotropy in comparison to reference layers without Sb. / Die vorliegende Dissertation beschäftigt sich mit der Untersuchung ferromagnetischer Dünnschichtsysteme im Hinblick auf die Austauchkopplung, das Ummagnetisierungsverhalten und Effekte wie z.B. den Exchange Bias Effekt oder den Riesenmagnetwiderstandseffekt (GMR), welche in derartigen Heterostrukturen auftreten können. Die Probenpräparation erfolgte mittels DC Magnetronsputtern, wobei auf einkristallinen aber auch flexiblen sowie starren amorphen Substraten abgeschieden wurde.
Im ersten Teil der Arbeit werden Untersuchungen mit dem Hintergrund einer Anwendung als magnetischer Datenträger vorgestellt. Konkret werden hier die Konzepte Bit Patterned Media (BPM) und 3D Speicher miteinander kombiniert. Letzteres Konzept basiert auf der Verwendung wenigstens zweier austauschentkoppelter ferromagnetischer Schichten, für welche [Co/Pt] Multilagen mit unterschiedlicher magnetischer Anisotropie verwendet wurden. Als Zwischenschichtmaterial diente Pt und Ru. Durch die Charakterisierung des Ummagnetisierungsverhaltens wurde die Austauschkopplung in Abhängigkeit der Zwischenschichtdicke untersucht. Darüber hinaus wurden jene Schichtstapel zur Realisierung des BPM-Konzeptes auf selbstangeordnete SiO2 Partikel mit unterschiedlichen Durchmessern aufgebracht, durch welche sich lateral austauschentkoppelte, eindomänige magnetische Nanostrukturen erzeugen lassen. Zur Untersuchung des Ummagnetisierungsverhaltens und der jeweiligen Größenabhängigkeiten (maßgeblich Durchmesser und Schichtdicke) wurden diese mittels Magnetkraftmikroskopie sowie winkelabhängiger magnetooptischer Kerr Effekt Magnetometrie untersucht. Zur weiteren Vertiefung des Verständnisses noch kleinerer Strukturgrößen erfolgten mikromagnetische Simulationen, bei denen die magnetischen Wechselwirkungen lateral (benachbarte 3D Elemente) als auch vertikal (Wechselwirkungen ferromagnetischer Schichten innerhalb eines 3D Elementes) im Interesse standen, sowie deren Auswirkungen auf das Ummagnetisierungsverhalten des gesamten Feldes.
Der Fokus des zweiten Teils liegt auf der Untersuchung des Riesenmagnetwiderstandseffektes in Systemen mit senkrechter Sensitivität. Dafür sind ferromagnetische Schichten mit senkrechter magnetischer Anisotropie nötig, wobei hier die chemisch geordnete L10-Phase der FePt Legierung und [Co/Pt] sowie [Co/Pd] Multilagen Anwendung fanden. Für eine chemische Ordnung der FePt Legierung sind hohe Temperaturen während der Schichtabscheidung notwendig, welche eine hinreichende Austauschentkopplung beider ferromagnetischer Schichten meist nicht gewährleisten. Grund dafür sind einsetzende Diffusionsprozesse als auch Legierungsbildungen mit dem Zwischenschichtmaterial. In der vorliegenden Arbeit konnte der GMR Effekt daher ausschließlich mit einer Ru Zwischenschicht in FePt basierten Trilagensystemen nachgewiesen und charakterisiert werden. Enorme Verbesserungen der magnetoresistiven Eigenschaften werden im Anschluss für [Co/Pt] und vor allem [Co/Pd] Multilagen vorgestellt. Diese Schichtsysteme mit senkrechter magnetischer Anisotropie können bei Raumtemperatur präpariert werden und stellen daher keine weiteren Anforderungen an das Zwischenschichtmaterial sowie die verwendeten Substrate. Hier wurden neben Systemen mit ausschließlich senkrechter magnetischer Anisotropie auch Systeme mit gekreuzten magnetischen Anisotropien intensiv untersucht, da diese durch einen linearen und weitgehend hysteresefreien R(H) Verlauf imHinblick auf Sensoranwendungen enorme Vorteile bieten. Letztendlich wurde die Korrosionsbeständigkeit in Abhängigkeit des Deckschichtmaterials als auch die mechanische Belastbarkeit von auf flexiblen Substraten abgeschiedenen GMR-Schichtstapeln untersucht.
Zusätzlich wird in Kapitel 2.5.2 eine experimentelle Studie zum Surfactant-gesteuerten Wachstum der FePt Legierung mittels Molekularstrahlepitaxie vorgestellt. Als Surfactant dient Sb, wodurch die Kristallinität bei geringer Depositionstemperatur deutlich verbessert werden konnte. Die Oberflächensegregation von Sb wurde mittels Auger Elektronenspektroskopie und Rutherford Rückstreuspektrometrie verifiziert und die Charakterisierung magnetischer Eigenschaften belegt einen Anstieg der magnetischen Anisotropieenergie im Vergleich zu Referenzproben ohne Sb.
|
12 |
Rapid thermal annealing of FePt and FePt/Cu thin filmsBrombacher, Christoph 14 February 2011 (has links) (PDF)
Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets.
In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO2 particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L10 phase.
The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L10 order, rapid thermal annealing can lead to the formation of chemically ordered FePt fifilms with (001) texture on amorphous SiO2/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneuosly to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 °C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO2 particle templates with periods down to 50 nm.
The addition of Cu improves the (001) texture formation and chemcial ordering for annealing temperatures T < 600 °C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated using e-beam and nanoimprint lithography have been investigated.
|
13 |
Rapid thermal annealing of FePt and FePt/Cu thin filmsBrombacher, Christoph 10 January 2011 (has links)
Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets.
In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO2 particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L10 phase.
The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L10 order, rapid thermal annealing can lead to the formation of chemically ordered FePt fifilms with (001) texture on amorphous SiO2/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneuosly to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 °C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO2 particle templates with periods down to 50 nm.
The addition of Cu improves the (001) texture formation and chemcial ordering for annealing temperatures T < 600 °C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated using e-beam and nanoimprint lithography have been investigated.
|
14 |
Perpendicular Magnetic Anisotropy Thin Films and Nanostructures for Future Recording Media ApplicationsGanss, Fabian 18 November 2022 (has links)
The increasing demand for nearline storage capacity in data centers calls for a continued enhancement in hard disk drive recording density far beyond one terabit per square inch. The thermal stability limit forces the drive manufacturers to develop new concepts in order to achieve this in the long term. Potential solutions are microwave-assisted magnetic recording (MAMR), heat-assisted magnetic recording (HAMR) and bit-patterned media (BPM).
A simple example of BPM based on sputter-deposited Co/Pd multilayers and prepatterned substrates at hypothetical recording densities up to one terabit per square inch was studied by magnetic force microscopy (MFM). This system achieved promising results at lower densities, but an actual application for data storage, especially at one terabit per square inch and higher densities, requires elaborate optimizations.
For some time now, FePt thin films have attracted much attention as prospective recording layers for high-density magnetic data storage due to their high magnetic anisotropy. The use of FePt films in HAMR is especially promising. This application has been tested successfully by Seagate and its key customers in recent years and is about to be introduced into the nearline hard disk drive market. It requires a tuning of the magnetic properties of FePt, especially of its Curie temperature. The addition of Cu proved to be effective in this regard and can also facilitate the formation of the crucial L10 structure and (001) texture during rapid thermal annealing of sputter-deposited thin films.
Such films were prepared as bilayers of Cu and FePt on Si substrates, annealed for 30 s, and analyzed by X-ray diffraction (XRD) and SQUID vibrating sample magnetometry (SQUID-VSM). The influence of large Cu additions on important properties like lattice parameters, mosaicity, magnetic anisotropy and Curie temperature is discussed. The chemical long-range order was calculated from the XRD data, and a dedicated chapter of this thesis covers the most important factors to be considered in such calculations for textured thin films and other samples.
The feasibility of creating patterned Fe-Cu-Pt films with perpendicular magnetic anisotropy, as needed for a combination of HAMR and BPM, by deposition through a PMMA mask, a lift-off process and subsequent annealing was investigated as well. The results indicate that the chosen approach might not lead to the required (001) texture when the nanostructures are small enough to compete with today's recording densities, so that either a continuous film might need to be etched after annealing or a seed layer might be required to induce the texture.:1. Motivation: Magnetic Data Storage
2. Experimental Techniques
3. Co/Pd Multilayers on Prepatterned Substrates
4. Fe-Pt and Fe-Cu-Pt Alloys
5. Rapid Thermal Annealing of FePt and FePt/Cu Films
6. Order Parameter Calculation
7. Summary
|
15 |
Magnetic and Magneto-Transport Properties of Hard Magnetic Thin Film SystemsMatthes, Patrick 21 December 2015 (has links)
The present thesis is about the investigation of ferromagnetic thin film systems with respect to exchange coupling, magnetization reversal behavior and effects appearing in magnetic heterostructures, namely the exchange bias and the giant magnetoresistance effect. For this purpose, DC magnetron sputtered thin films and multilayers with perpendicular magnetic anisotropy were prepared on single crystalline and rigid as well as flexible amorphous substrates.
The first part concentrates on magnetic data storage applications based on the combination of the concept of bit patterned media and three dimensional magnetic memory, consisting of at least two exchange decoupled ferromagnetic storage layers. Here, [Co/Pt] multilayers, revealing different magnetic anisotropies, have been applied as storage layers and as spacer material Pt and Ru was employed. By the characterization of the magnetization reversal behavior the exchange coupling in dependence of the spacer layer thickness was studied. Furthermore, with regard to the concept of bit patterned media, the layers were also grown on self-assembled silica particles, leading to an exchange decoupled single-domain magnetic dot array, which was studied by magnetic force microscope imaging and angular dependent magneto-optic Kerr effect magnetometry to evaluate the reversal mechanism and its dependence on the array dimensions, mainly the diameter of the silica particles and layer thicknesses. To complete the study, micromagnetic simulations were performed to access smaller dimensions and to investigate the dependence of intralayer as well as interlayer coupling on the magnetization reversal of the dot array with multiple storage layers.
The second part focuses on the investigation of the giant magnetoresistance effect in systems with perpendicular magnetic anisotropy, where L10 -chemically ordered FePt alloys and [Co/Pt] as well as [Co/Pd] multilayers were utilized. In case of FePt, where high temperatures during the deposition are necessary to induce the chemical ordering, diffusion and alloying of the spacer material often prevent a sufficient exchange decoupling of the ferromagnetic layers. However, with Ru as spacer material a giant magnetoresistance effect could be achieved. Large improvements of the magnetoresistive behavior of such trilayer structures are presented for [Co/Pt] and [Co/Pd] multilayers, which can be deposited at room temperature not limiting the choice of spacer as well as substrate material. Furthermore, in systems consisting of one ferromagnet with perpendicular magnetic anisotropy and one ferromagnet with in-plane magnetic easy axis, a linear and almost hysteresis-free field dependence of the electrical resistance was observed and the behavior for various thickness series has been intensively studied. Finally, the corrosion resistance in dependence of the capping layer material as well as the magnetoresistance of a strained flexible pseudo-spin-valve structure is presented.
In addition, in chapter 2.5.2 an experimental study of an improved crystal growth of FePt at comparable low temperatures by molecular beam epitaxy and further promoted by a surfactant mediated growth using Sb is shown. Auger electron spectroscopy as well as Rutherford backscattering spectrometry were carried out to confirm the surface segregation of Sb and magnetic characterization revealed an increase of magnetic anisotropy in comparison to reference layers without Sb. / Die vorliegende Dissertation beschäftigt sich mit der Untersuchung ferromagnetischer Dünnschichtsysteme im Hinblick auf die Austauchkopplung, das Ummagnetisierungsverhalten und Effekte wie z.B. den Exchange Bias Effekt oder den Riesenmagnetwiderstandseffekt (GMR), welche in derartigen Heterostrukturen auftreten können. Die Probenpräparation erfolgte mittels DC Magnetronsputtern, wobei auf einkristallinen aber auch flexiblen sowie starren amorphen Substraten abgeschieden wurde.
Im ersten Teil der Arbeit werden Untersuchungen mit dem Hintergrund einer Anwendung als magnetischer Datenträger vorgestellt. Konkret werden hier die Konzepte Bit Patterned Media (BPM) und 3D Speicher miteinander kombiniert. Letzteres Konzept basiert auf der Verwendung wenigstens zweier austauschentkoppelter ferromagnetischer Schichten, für welche [Co/Pt] Multilagen mit unterschiedlicher magnetischer Anisotropie verwendet wurden. Als Zwischenschichtmaterial diente Pt und Ru. Durch die Charakterisierung des Ummagnetisierungsverhaltens wurde die Austauschkopplung in Abhängigkeit der Zwischenschichtdicke untersucht. Darüber hinaus wurden jene Schichtstapel zur Realisierung des BPM-Konzeptes auf selbstangeordnete SiO2 Partikel mit unterschiedlichen Durchmessern aufgebracht, durch welche sich lateral austauschentkoppelte, eindomänige magnetische Nanostrukturen erzeugen lassen. Zur Untersuchung des Ummagnetisierungsverhaltens und der jeweiligen Größenabhängigkeiten (maßgeblich Durchmesser und Schichtdicke) wurden diese mittels Magnetkraftmikroskopie sowie winkelabhängiger magnetooptischer Kerr Effekt Magnetometrie untersucht. Zur weiteren Vertiefung des Verständnisses noch kleinerer Strukturgrößen erfolgten mikromagnetische Simulationen, bei denen die magnetischen Wechselwirkungen lateral (benachbarte 3D Elemente) als auch vertikal (Wechselwirkungen ferromagnetischer Schichten innerhalb eines 3D Elementes) im Interesse standen, sowie deren Auswirkungen auf das Ummagnetisierungsverhalten des gesamten Feldes.
Der Fokus des zweiten Teils liegt auf der Untersuchung des Riesenmagnetwiderstandseffektes in Systemen mit senkrechter Sensitivität. Dafür sind ferromagnetische Schichten mit senkrechter magnetischer Anisotropie nötig, wobei hier die chemisch geordnete L10-Phase der FePt Legierung und [Co/Pt] sowie [Co/Pd] Multilagen Anwendung fanden. Für eine chemische Ordnung der FePt Legierung sind hohe Temperaturen während der Schichtabscheidung notwendig, welche eine hinreichende Austauschentkopplung beider ferromagnetischer Schichten meist nicht gewährleisten. Grund dafür sind einsetzende Diffusionsprozesse als auch Legierungsbildungen mit dem Zwischenschichtmaterial. In der vorliegenden Arbeit konnte der GMR Effekt daher ausschließlich mit einer Ru Zwischenschicht in FePt basierten Trilagensystemen nachgewiesen und charakterisiert werden. Enorme Verbesserungen der magnetoresistiven Eigenschaften werden im Anschluss für [Co/Pt] und vor allem [Co/Pd] Multilagen vorgestellt. Diese Schichtsysteme mit senkrechter magnetischer Anisotropie können bei Raumtemperatur präpariert werden und stellen daher keine weiteren Anforderungen an das Zwischenschichtmaterial sowie die verwendeten Substrate. Hier wurden neben Systemen mit ausschließlich senkrechter magnetischer Anisotropie auch Systeme mit gekreuzten magnetischen Anisotropien intensiv untersucht, da diese durch einen linearen und weitgehend hysteresefreien R(H) Verlauf imHinblick auf Sensoranwendungen enorme Vorteile bieten. Letztendlich wurde die Korrosionsbeständigkeit in Abhängigkeit des Deckschichtmaterials als auch die mechanische Belastbarkeit von auf flexiblen Substraten abgeschiedenen GMR-Schichtstapeln untersucht.
Zusätzlich wird in Kapitel 2.5.2 eine experimentelle Studie zum Surfactant-gesteuerten Wachstum der FePt Legierung mittels Molekularstrahlepitaxie vorgestellt. Als Surfactant dient Sb, wodurch die Kristallinität bei geringer Depositionstemperatur deutlich verbessert werden konnte. Die Oberflächensegregation von Sb wurde mittels Auger Elektronenspektroskopie und Rutherford Rückstreuspektrometrie verifiziert und die Charakterisierung magnetischer Eigenschaften belegt einen Anstieg der magnetischen Anisotropieenergie im Vergleich zu Referenzproben ohne Sb.
|