Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2003-02-21Bitstream added on 2014-06-13T19:37:38Z : No. of bitstreams: 1 batista_aud_me_arafo.pdf: 1233122 bytes, checksum: 1fb35dc92b6cd4a34a7b7bb1cad4d1ab (MD5) / O objetivo deste estudo foi avaliar a resistência de união à tração e dureza Shore A de dois materiais reembasadores macios (Eversoft e Molloplast-B), processados juntamente com três resinas acrílicas de base de dentadura (SR Triplex, Lucitone 550 e Acron MC), polimerizadas com diferentes ciclos de polimerização. As amostras para o ensaio de tração eram divididas em dois segmentos de resina acrílica, cada um com 60 x 10 x 10 mm, e um segmento central de material reembasador macio, com 3 x 10 x 10 mm. Dez espécimes foram confeccionados para cada combinação resina acrílica/material reembasador, polimerizados por três ciclos diferentes de polimerização, como segue: SR Triplex - 2 horas a 100ºC; Lucitone 550 - 90 minutos a 73ºC, seguido de 2 horas a 100ºC, e Acron MC - energia por microondas por 10 minutos a 850W. As amostras foram testadas em uma máquina de ensaios universais MTS-810, a uma velocidade de 5 mm/min. Os valores médios de resistência de união foram calculados e expressos em megapascals (MPa), e o tipo de falha foi avaliado e anotado como coesiva, adesiva ou mista. As amostras para a avaliação da dureza Shore A consistiam de corpos-de-prova com dimensões de 36 x 7 x 6 mm preparados com os dois materiais macios de reembasamento. Dez amostras de cada material também foram polimerizadas pelos ciclos de polimerização já apresentados e a dureza foi determinada em um durômetro Shore A, de acordo com as normas D-2240 da ASTM. Os dados de ambos os testes foram analisados pela análise de variância e teste de Tukey permitindo concluir que: a) o maior valor de resistência de união foi apresentado pelo material Molloplast-B, quando processado com as resinas acrílicas Lucitone 550 (1,41 +0,15 MPa) e SR Triplex (1,40 + 0,10 MPa),... / The purpose of this study was to evaluate the tensile bond strength and Shore A hardness of two soft denture liners (Eversoft and Molloplast-B), processed against three heat-cured denture base acrylic resins (SR Triplex, Lucitone 550 and Acron MC), and polymerized by different curing cycles (water bath and microwave energy). Tensile specimens consisted of two segments of acrylic resin, each 60 x 10 x 10 mm, and a central segment of soft liner, 3 x 10 x 10 mm. Ten specimens were prepared by each liner/resin combination, and were cured by three different curing cycles, as follows: SR Triplex - boiling water for 2 hours; Lucitone 550 - 73ºC for 90 minutes, plus 2 hours at 100ºC; and Acron MC - microwave activation at 850W for 10 minutes. Specimens were tested in an MTS-810 Universal Testing Machine, at a crosshead speed of 5 mm/min. Mean bond strength was calculated and expressed in megapascals (MPa), and the type of failure was assessed and recorded as being cohesive, adhesive, or mixed. Shore A specimens consisted of 36 x 7 x 6 mm samples prepared with the two soft liners. Ten samples of each liner were polymerized by the curing cycles early presented. Hardness was determined in a Shore A durometer, according the ASTM D-2240 specification. Data from both tests were analyzed by ANOVA and Tukey test, showing that: a) the highest bond strength was presented by Molloplast-B, when processed against Lucitone 550 (1.41 +0.15 MPa) and SR Triplex (1.40 + 0.10 MPa) acrylic resins, and the lowest values were observed for Eversoft, when processed against Acron MC resin (0.38 + 0.06 MPa), b) when polymerized by microwave energy, both Molloplast-B and Eversoft presented their lowest bond strength values, when compared with the groups cured in water bath (p< .05), and c)...(Complete abstract, click electronic access below)

A presente pesquisa teve por objetivo a análise do comportamento de diferentes combinações de liners de um determinado solo com e sem cimentação, submetidos à percolação de líquidos ácidos, com o objetivo de simular o comportamento de campo de liners de aterros especiais, que recebem resíduos à base de pirita. Tal resíduo em contato com água e oxigênio forma solução de ácido sulfúrico. Assim sendo, as pretensões deste trabalho foram a análise do comportamento compressivo de liners formados por um dado tipo de solo compactado, com e sem a adição de cimento, através do emprego de um equipamento de adensamento modificado desenvolvido especialmente para esta pesquisa. Da mesma forma, procedeu-se o estudo dos fenômenos de transporte de contaminantes por meio do liner em estudo, basicamente daqueles que comandam o transporte (difusão, advecção, sorção, retardamento da frente de contaminação e grau de afinidade entre o contaminante e o liner). Ensaios isotrópicos a altas tensões de confinamento também foram realizados a fim de se estudar a possível desestruturação dos liners quando percolados por resíduos ácidos. Os resultados obtidos destacam a desestruturação de amostras naturais do solo estudado quando percolado por rejeitos ácidos, em todas as concentrações estudadas, tanto em ensaios triaxiais isotrópicos quanto em ensaios de carregamento axial com deformações laterais nulas. Conclui-se que as águas ácidas quando percoladas por meio de um solo com presença de finos, tende a proporcionar um efeito de carreamento de partículas, aumentando conseqüentemente a porosidade, fator este que poderia proporcionar a falha operacional de um liner. / The objective of this work is to analyse the behavior of a liner formatted by different combinations of soil and cement, percolated by low pH waters under different hydraulic gradients and concentration of acid in the percolant, aiming to simulate in laboratory what would happen in the field to liners in contact with pyrite wastes, from mineral coal mining. Pyrite wastes in contact with water and oxygen result in sulphuric acid, what makes the objective of this research the study of the compressive behavior of the liner submitted to the percolation of acid waters, by means of a special column equipment developed during this research, which allows applying an axial load to the sample under flux. Also, the variation of the transport of contaminants values were investigated, basically diffusion, advection, sorption, retardation coefficient, distribution coefficient, hydrodynamic dispersion, ground water velocity and hydraulic conductivity). Triaxial Isotropic tests were carried out under high confinant pressures in order to verify the volume changes of the samples due to the low-pH contamination. The results show that liners formatted only by soil had rearrange of their structure due to acid percolations, according to both column and isotropic tests. The value of the hydrodynamic dispersion was considerated being totally dependent on the diffusion, because the hydraulic conductivity of the differente combination was low. The results also show that low-pH percolations make a rearrange of the fine particles into the sample, because after a grain size distribution test, the fine particles from the top of the samples were detected on the bottom of the sample, what increase the porosity on the top of the samples, what could lead the liner to a failure.

Seguindo a linha de pesquisa de novos materiais geotécnicos, na busca por soluções técnicas a partir do uso de materiais alternativos, o presente estudo avaliou sob enfoque geotécnico o comportamento do resíduo de uma fábrica recicladora de papel localizada no estado do Rio Grande do Sul, Brasil. O objetivo do trabalho consistiu em caracterizar o resíduo e identificar suas propriedades no que se refere ao seu desempenho mecânico e hidráulico, a partir de um programa de ensaios de laboratório. O resíduo in natura possui uma umidade de 256 %, sendo composto de matéria orgânica (de 40 a 45 %), cargas minerais (principalmente caulinita e calcita) e água. As análises para a determinação dos parâmetros de deformabilidade, resistência e condutividade hidráulica foram feitas utilizando-se como variável os valores de umidade de aproximadamente 190, 160 e 130 %. Os parâmetros de compressibilidade unidimensional das amostras do resíduo não apresentaram variabilidade significativa com a variação da umidade de moldagem, obtendo-se valores médios elevados para os índices de compressão (Cc) e descarregamento (Cd) e para os coeficientes de adensamento (Cv), indicativos da alta compressibilidade característica do material. Para a determinação dos parâmetros de resistência do material foram realizados ensaios triaxiais nãodrenados. O ângulo de atrito interno obtido foi de ф’= 53,5°. Durante os ensaios triaxiais foram realizadas medições da condutividade hidráulica antes da fase de cisalhamento das amostras. Os coeficientes de condutividade hidráulica, medidos na fase pré-cisalhamento, atingiram valores da ordem de 10-9 m/s. A capacidade de atingir baixos valores de condutividade hidráulica é uma característica relevante do comportamento deste material e indica a possibilidade de ser utilizado como um material geotécnico alternativo em substituição aos materiais convencionais utilizados em coberturas impermeáveis de aterros (cover liners). / Following the line of research of new geotechnical materials, aiming new technical solutions using alternative materials, the present research evaluated, under geotechnical understanding, the behavior of the waste sludge from a paper recycling plant in Rio Grande do Sul, Brazil. The objective of this research aimed the characterization and the identification of the waste properties – mechanical and hydraulic performance, through laboratory tests. The natural waste has 256% of water content, and is composed by organic matter (ranging from 40 to 45 %), mineral charges (mainly Kaolinite and Calcite) and water. The tests for the determination of deformability, strength and hydraulic conductivity parameters were carried out under 190%, 160% and 130 % of water content. The one-dimensional compressibility parameters of the waste sludge did not show a significant variability with the variation of the molding water content, where the average values were high for the compression (Cc) and swelling (Cd) coefficients as well as for the consolidation coefficient (Cv), which can be considered as an indicative of high compressibility (characteristic of the material). For the determination of the strength parameters of the material, it was carried out undrained triaxial tests. The internal friction angle was ф’= 53,5°. During the triaxial tests, measurements of hydraulic conductivity were performed, previously shearing. The hydraulic conductivity coefficients measured during the pre-shearing phase, reached values around 10-9 m/s. The capacity for reaching low values of hydraulic conductivity is a considerable characteristic of the behavior of this material, what shows the possibility of its use as an alternative geotechnical material substituting the conventional materials used as cover liners

Submitted by Sâmia Carolina Mota Cavalcanti Sacorague (samiacmc@gmail.com) on 2016-04-01T02:29:04Z No. of bitstreams: 1 Tese Oficial Sacorague.pdf: 138789678 bytes, checksum: 64a0549f6b21193b17f2359358326d21 (MD5) / Approved for entry into archive by Juliano Benedito Ferreira (julianoferreira@reitoria.unesp.br) on 2016-04-05T16:34:30Z (GMT) No. of bitstreams: 1 sacorague_scm_dr_sjc.pdf: 138789678 bytes, checksum: 64a0549f6b21193b17f2359358326d21 (MD5) / Made available in DSpace on 2016-04-05T16:34:30Z (GMT). No. of bitstreams: 1 sacorague_scm_dr_sjc.pdf: 138789678 bytes, checksum: 64a0549f6b21193b17f2359358326d21 (MD5) Previous issue date: 2016-02-03 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desta pesquisa foi sintetizar e caracterizar partículas de sílica recobertas com nanopartículas de prata, e avaliar a influência destas quando incorporadas à resina acrílica termicamente ativada e reembasador rígido, em suas características mecânicas e microbiológicas. Uma solução de sílica foi sintetizada pelo método de hidrólise controlada do tetraetilortosilicato (TEOS) em meio alcoólico. Foi adicionada a essa uma solução de nitrato de prata, em duas molaridades (10 mmols e 30 mmols) formando partículas do tipo núcleo-casca. Após centrifugação e secagem, cada pó obtido foi adicionado em duas concentrações: 0.5% e 2%, às resinas analisadas. Foram confeccionadas barras retangulares (n=9) de 30 x 10x 3mm para realização do teste de resistência a flexão de três pontos, rugosidade e ângulo de contato; e 120 amostras em forma de disco (2 mmx10 mm) para análise microbiológica. Como grupo controle teve-se amostras sem nanopartículas. As nanopartículas foram analisadas em microscopia eletrônica de varredura com microanalisador por energia dispersiva de raios-X integrado (EDS), Difratômetro de Raios-X e microscopia eletrônica de transmissão. Uma suspensão de Candida albicans foi utilizada para análise de aderência fúngica, halo de inibição e concentração inibitória mínima. As fotomicrografias mostraram que as nanopartículas de 10 mmols apresentam uma distribuição mais homogênea e menor agregação das nanopartículas de prata na superfície da sílica do que as de 30 mmols. Os resultados indicaram que a resistência a flexão foi afetada negativamente, em ambos materiais, com a adição de 2% de partículas, independente da molaridade. A adição das partículas não alterou a molhabilidade da superfície dos materiais, nem a rugosidade, exceto do grupo de reembasador com partículas de 10mmols, em ambas concentrações. As partículas não apresentaram ação antifúngica para os materiais testados em nenhuma concentração, nem houve a formação de halo. Entretanto, a solução apresentou concentração inibitória mínima a partir de 2.000 ppm. Concluiu-se que em baixas concentrações as nanopartículas não afetaram as características mecânica e de superfície da resina acrílica e do reembasador, entretanto elas não inibiram a formação de biofilme por C. albicans sob os materiais. / This research aimed to synthesize, characterize, and evaluate the influence of the addition of silica-silver core/shell particles in mechanical and antifungal characteristics of thermally active acrylic resins or hard reliner . Silica solution was produced by controlled hydrolysis method of tetraethylorthosilicate (TEOS) in an alcoholic. It was added a silver nitrate solution in two molarities, 10 and 30 milimols, forming core-shell particles. After centrifugation and drying, each obtained powder was added in two concentrations 0.5% and 2% in the resins analyzed. Rectangular samples (n=9) with 30 x10 x3 mm were made to three point bend test), roughness and contact angle, and 120 samples in disc (2 mmx10 mm) for microbiological analysis Samples without particles were used as control. The nanoparticles were analyzed by scanning electron microscopy with dispersive energy microanalyzer integrated X-rays (EDS), X-ray diffractometer and transmission electron microscopy. Candida albicans suspension was used to adhesion test, inhibition zone and minimum inhibitory concentration. Photomicrograph showed that nanoparticles with 10 milimols show a distribution more uniform and less aggregation of silver nanoparticles on the silica surface than 30 millimols. The Three point bend test results showed that the flexural strength was negatively affected in both materials, with the addition of 2% particles, in both molarity. The addition of the nanoparticles did not change the surface wettability or roughness of the materials, except for except the reliner group with 10mmols, in both concentrations. The nanoparticles showed no antifungal action for the materials tested at any concentration, neither was zone innibition. However, the solution presented minimal inhibitory concentration to 2.000 ppm. We conclude that low concentrations nanoparticles do not affect the mechanical characteristics and surface of the acrylic resin or reliner, however they do not reduce biofilm adhesion by C. albicans in the materials.

Made available in DSpace on 2014-06-11T19:35:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-04-04Bitstream added on 2014-06-13T20:06:12Z : No. of bitstreams: 1 goncalves_ar_dr_arafo.pdf: 1974874 bytes, checksum: cb90cfb07e456ba101c0f7c18597c3d6 (MD5) / Esse estudo avaliou o efeito da desinfecção química e por irradiação com microondas sobre a estabilidade dimensional e a resistência ao cisalhamento entre uma resina termopolimerizável para base de prótese (Lucitone 550-L) e quatro resinas autopolimerizáveis para reembasamento (Kooliner- K, New Truliner-NT, Tokuso Rebase-TR, Ufi Gel Hard -UGH). Foi avaliada também a resistência ao cisalhamento de corpos-de-prova reembasados com a resina L. Para cada material, 48 corpos-de-prova (50 mm diâmetro x 0.5 mm espessura) foram preparados, seguindo-se as recomendações dos fabricantes, utilizando-se uma matriz metálica circular com pontos de referência (A, B, C e D). Um projetor de perfil Nikon foi utilizado para mensurar a distância entre os pontos de referências (AB e CD) na matriz metálica e nos corpos-de-prova. Os corpos-de-prova foram divididos em 6 grupos (n=8) e as mensurações foram realizadas após as seguintes condições experimentais: G1- 2 ciclos de desinfecção química (corpos-de-prova imersos em solução de perborato de sódio a 3,8% aquecida a 50º C por 10 minutos); G2- 2 ciclos de desinfecção com microondas (corpos-de-prova imersos em 200 mL de água e irradiados com 650 W por 6 minutos); G3- 7 ciclos de desinfecção química; G4- 7 ciclos de desinfecção com microondas; C1- grupo controle 1- após a polimerização para as resinas de reembasamento e após imersão em água a 37° C por 48 + 2 horas para a resina de base; C2- grupo controle 2- corpos-de-prova imersos em água a 37° C por 7 dias. Para os grupos G3 e G4, os corpos-de-prova foram mantidos em água a 37° C entre os ciclos de desinfecção. As diferenças entre as mensurações realizadas nos corpos-de-prova e as da matriz foram calculadas e expressas em porcentagem de alteração dimensional linear. Para avaliar a resistência de união, foram confeccionados cilindros... / This study evaluated the effect of chemical and microwave disinfection on the linear dimensional change and the shear bond strength between one heat-polymerizing denture base acrylic resin (Lucitone 550-L) and four autopolymerizing reline resins (Kooliner- K, New Truliner-NT, Tokuso Rebase-TR, Ufi Gel Hard -UGH). Also, the shear bond strength of specimens relined with the denture base resin L was evaluated, for comparison. For each material, 48 disks (50 mm diameter and 0.5 mm thickness) were made by using a stainless steel split mold with reference points (A, B, C and D), following the manufacturers' instructions. A Nikon optical comparator was used to measure the distances between the reference points (AB and CD) on the stainless steel mold and on the specimens. Specimens were divided into 6 groups (n=8) and the measurements were made after the following conditions: G1- 2 cycles of chemical disinfection (specimens immersed in 3,8% sodium perborate solution at 50° C for 10 minutes); G2- 2 cycles of microwave disinfection (specimens immersed in 200 mL of water, and irradiated with 650 W for 6 min); G3- 7 cycles of chemical disinfection; G4- 7 cycles of microwave irradiation; G5- after polymerization for the reline resins and after the specimens had been stored in water at 37° C for 48 + 2 hours; G6- specimens immersed in water at 37° C for seven days. For the groups G3 and G4, the specimens were disinfected daily, and stored in water at 37° C between disinfection. The differences between the measurements made on the specimens and on the stainless steel mold were calculated and expressed as percentage of linear dimensional changes. To evaluate the bond strength, cylinders (20mm x 20mm) of the resin L were processed (in water at 70°C for 90 minutes, and 30 minutes at boiling temperature), according to the manufacturer's instructions ...(Complete abstract, click electronic access below)

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-07-28Bitstream added on 2014-06-13T20:25:49Z : No. of bitstreams: 1 ribeiro_rc_dr_arafo.pdf: 3026200 bytes, checksum: e7d101d0ede455ed6dd85a16d9ab477c (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Este estudo avaliou o efeito da desinfecção por micro-ondas sobre o desempenho clínico e a quantificação de micro-organismos de um reembasador rígido em diferentes intervalos de tempo. Foram selecionados 40 pacientes de ambos os sexos com idade entre 30 e 75 anos, utilizando prótese total superior com necessidade de reembasamento. Essas próteses foram reembasadas com o material Tokuyama Rebase II. Logo após o reembasamento, foi avaliado o escoamento e a lisura do material, classificando-os em satisfatório ou insatisfatório. Em seguida, a amostra foi separada em dois grupos: grupo GC (controle) – os pacientes higienizaram sua prótese três vezes ao dia por meio de escovação com sabão de coco. Além disso, a prótese foi retirada durante a noite, ficando imersa em água e grupo GD (desinfecção por micro-ondas) – nesse grupo, além da escovação com escova dental macia e sabão de coco, foi realizada a desinfecção da prótese por micro-ondas uma vez por semana utilizando a potência de 650W e o tempo de 3 minutos. No período noturno, a prótese também foi imersa em água. O material reembasador foi avaliado por dois profissionais treinados trabalhando separadamente após 7 dias, 15 dias, 1 mês, 3 meses, 6 meses, 9 meses e 1 ano. Foram analisadas as seguintes características: estabilidade de cor, brilho, descoloração ou manchamento, irritação dos tecidos orais, separação ou fratura do material e rugosidade superficial. Além disso, foi realizada a quantificação de micro-organismos presentes na superfície interna da prótese em todos os períodos experimentais. Os dados obtidos foram analisados por análise de variância e pelos testes de Tukey e Friedman, ao nível de significância de 5%. O material apresentou lisura e escoamento satisfatórios em todas as análises após o reembasamento. As próteses reembasadas submetidas à desinfecção... / This study evaluated the effect of disinfection method on the clinical performance and quantification of microbial of a hard chairside reline resin after 1-year service period. Forty adult patients aged between 30 and 75 years, who required denture reline treatment, participated in this study. Tokuyama Rebase II was used to reline complete maxillary dentures. Immediately after the reline, assessment of the flow and smoothness was rated by the clinician as satisfactory and unsatisfactory. The edentulous subjects were randomly divided into 2 groups (n=20) and dentures were cleansed according to two methods: CG (control group)- brushing with coconut soap and soft toothbrush; DG (disinfection group)-brushing according to previous methods and microwave disinfection once a week for 3 min at 650W. Furthermore, all dentures were immersed in water at night. Evaluations were conducted by two examiners working separately. Color stability, gloss, staining or material discoloration, irritation to oral tissue, detachment or frature of material and surface roughness were assessed at 7 and 15 days, 1, 3, 6 and 9 months and 1 year post-placement. Quantitative microbial cultures were taken from the tissue side of each maxillary denture at all experimental periods. The data were analyzed by ANOVA and Friedman and Tukey tests. A 95% confindence level was used. Flow and smoothness of the material during relining were considered to be good or satisfactory in all the cases. Values color alterations of DG were significantly lower than those of CG (P<0.05). Color change observed after 15 days are greater than values obtained at 7 days recall (P<0.05). All color changes observed for the CG were considered noticeable (between 1.5 and 3.0 NBS). In disinfection group, color change was slight (between 0.5 and 1.5 NBS). There were statistically significant... (Complete abstract click electronic access below)

Seguindo a linha de pesquisa de novos materiais geotécnicos, na busca por soluções técnicas a partir do uso de materiais alternativos, o presente estudo avaliou sob enfoque geotécnico o comportamento do resíduo de uma fábrica recicladora de papel localizada no estado do Rio Grande do Sul, Brasil. O objetivo do trabalho consistiu em caracterizar o resíduo e identificar suas propriedades no que se refere ao seu desempenho mecânico e hidráulico, a partir de um programa de ensaios de laboratório. O resíduo in natura possui uma umidade de 256 %, sendo composto de matéria orgânica (de 40 a 45 %), cargas minerais (principalmente caulinita e calcita) e água. As análises para a determinação dos parâmetros de deformabilidade, resistência e condutividade hidráulica foram feitas utilizando-se como variável os valores de umidade de aproximadamente 190, 160 e 130 %. Os parâmetros de compressibilidade unidimensional das amostras do resíduo não apresentaram variabilidade significativa com a variação da umidade de moldagem, obtendo-se valores médios elevados para os índices de compressão (Cc) e descarregamento (Cd) e para os coeficientes de adensamento (Cv), indicativos da alta compressibilidade característica do material. Para a determinação dos parâmetros de resistência do material foram realizados ensaios triaxiais nãodrenados. O ângulo de atrito interno obtido foi de ф’= 53,5°. Durante os ensaios triaxiais foram realizadas medições da condutividade hidráulica antes da fase de cisalhamento das amostras. Os coeficientes de condutividade hidráulica, medidos na fase pré-cisalhamento, atingiram valores da ordem de 10-9 m/s. A capacidade de atingir baixos valores de condutividade hidráulica é uma característica relevante do comportamento deste material e indica a possibilidade de ser utilizado como um material geotécnico alternativo em substituição aos materiais convencionais utilizados em coberturas impermeáveis de aterros (cover liners). / Following the line of research of new geotechnical materials, aiming new technical solutions using alternative materials, the present research evaluated, under geotechnical understanding, the behavior of the waste sludge from a paper recycling plant in Rio Grande do Sul, Brazil. The objective of this research aimed the characterization and the identification of the waste properties – mechanical and hydraulic performance, through laboratory tests. The natural waste has 256% of water content, and is composed by organic matter (ranging from 40 to 45 %), mineral charges (mainly Kaolinite and Calcite) and water. The tests for the determination of deformability, strength and hydraulic conductivity parameters were carried out under 190%, 160% and 130 % of water content. The one-dimensional compressibility parameters of the waste sludge did not show a significant variability with the variation of the molding water content, where the average values were high for the compression (Cc) and swelling (Cd) coefficients as well as for the consolidation coefficient (Cv), which can be considered as an indicative of high compressibility (characteristic of the material). For the determination of the strength parameters of the material, it was carried out undrained triaxial tests. The internal friction angle was ф’= 53,5°. During the triaxial tests, measurements of hydraulic conductivity were performed, previously shearing. The hydraulic conductivity coefficients measured during the pre-shearing phase, reached values around 10-9 m/s. The capacity for reaching low values of hydraulic conductivity is a considerable characteristic of the behavior of this material, what shows the possibility of its use as an alternative geotechnical material substituting the conventional materials used as cover liners

Orientador: João Neudenir Arioli Filho / Banca: Francisco de Assis Mollo Junior / Banca: Maximiliano Piero Neisser / Resumo: O objetivo deste estudo foi avaliar a resistência de união à tração e dureza Shore A de dois materiais reembasadores macios (Eversoft e Molloplast-B), processados juntamente com três resinas acrílicas de base de dentadura (SR Triplex, Lucitone 550 e Acron MC), polimerizadas com diferentes ciclos de polimerização. As amostras para o ensaio de tração eram divididas em dois segmentos de resina acrílica, cada um com 60 x 10 x 10 mm, e um segmento central de material reembasador macio, com 3 x 10 x 10 mm. Dez espécimes foram confeccionados para cada combinação resina acrílica/material reembasador, polimerizados por três ciclos diferentes de polimerização, como segue: SR Triplex - 2 horas a 100ºC; Lucitone 550 - 90 minutos a 73ºC, seguido de 2 horas a 100ºC, e Acron MC - energia por microondas por 10 minutos a 850W. As amostras foram testadas em uma máquina de ensaios universais MTS-810, a uma velocidade de 5 mm/min. Os valores médios de resistência de união foram calculados e expressos em megapascals (MPa), e o tipo de falha foi avaliado e anotado como coesiva, adesiva ou mista. As amostras para a avaliação da dureza Shore A consistiam de corpos-de-prova com dimensões de 36 x 7 x 6 mm preparados com os dois materiais macios de reembasamento. Dez amostras de cada material também foram polimerizadas pelos ciclos de polimerização já apresentados e a dureza foi determinada em um durômetro Shore A, de acordo com as normas D-2240 da ASTM. Os dados de ambos os testes foram analisados pela análise de variância e teste de Tukey permitindo concluir que: a) o maior valor de resistência de união foi apresentado pelo material Molloplast-B, quando processado com as resinas acrílicas Lucitone 550 (1,41 +0,15 MPa) e SR Triplex (1,40 + 0,10 MPa),... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this study was to evaluate the tensile bond strength and Shore A hardness of two soft denture liners (Eversoft and Molloplast-B), processed against three heat-cured denture base acrylic resins (SR Triplex, Lucitone 550 and Acron MC), and polymerized by different curing cycles (water bath and microwave energy). Tensile specimens consisted of two segments of acrylic resin, each 60 x 10 x 10 mm, and a central segment of soft liner, 3 x 10 x 10 mm. Ten specimens were prepared by each liner/resin combination, and were cured by three different curing cycles, as follows: SR Triplex - boiling water for 2 hours; Lucitone 550 - 73ºC for 90 minutes, plus 2 hours at 100ºC; and Acron MC - microwave activation at 850W for 10 minutes. Specimens were tested in an MTS-810 Universal Testing Machine, at a crosshead speed of 5 mm/min. Mean bond strength was calculated and expressed in megapascals (MPa), and the type of failure was assessed and recorded as being cohesive, adhesive, or mixed. Shore A specimens consisted of 36 x 7 x 6 mm samples prepared with the two soft liners. Ten samples of each liner were polymerized by the curing cycles early presented. Hardness was determined in a Shore A durometer, according the ASTM D-2240 specification. Data from both tests were analyzed by ANOVA and Tukey test, showing that: a) the highest bond strength was presented by Molloplast-B, when processed against Lucitone 550 (1.41 +0.15 MPa) and SR Triplex (1.40 + 0.10 MPa) acrylic resins, and the lowest values were observed for Eversoft, when processed against Acron MC resin (0.38 + 0.06 MPa), b) when polymerized by microwave energy, both Molloplast-B and Eversoft presented their lowest bond strength values, when compared with the groups cured in water bath (p< .05), and c)...(Complete abstract, click electronic access below) / Mestre

Orientador: João Neudenir Arioli Filho / Banca: Sergio Sualdini Nogueira / Banca: Mauro Antônio de Arruda Nóbilo / Resumo: O objetivo deste estudo foi avaliar o efeito de técnicas de desinfecção utilizando soluções de glutaraldeído 2%, hipoclorito de sódio 5%, clorexidina 5% e energia por microondas sobre a dureza e rugosidade de superfície dos materiais reembasadores macios Ufi Gel , Molloplast-B, Eversoft e Mucopren soft. Quarenta corpos-de-prova de cada material com dimensões de 36x7x6 mm foram processados em muflas plásticas para microondas e polimerizados de acordo com as recomendações dos fabricantes. As amostras foram divididas em grupos (n=10) e submetidas à desinfecção por 10 minutos nas soluções químicas e, em forno de microondas doméstico por período de 3 minutos à 500W. As leituras de dureza e rugosidade foram realizadas 24 horas após a confecção dos corpos de prova e após aplicação do 1° e 2° ciclo de desinfecção, respectivamente. As leituras de dureza foram realizadas sobre uma das faces do corpo de prova com auxílio de durômetro Shore A. Sobre a face oposta foram realizadas as leituras de rugosidade com rugosímetro Surf-Corder SE 1700. Os dados obtidos foram submetidos à análise de variância e teste de Tukey ao nível de significância de 1%. Conclui-se que a aplicação de dois ciclos de desinfecção não produziu alterações na dureza dos materiais utilizados. Porém, houve diminuição na rugosidade após o primeiro ciclo de desinfecção. A técnica de desinfecção com solução de glutaraldeído 2% promoveu os maiores valores de dureza nos materiais Molloplast-B, Mucopren soft e Ufi Gel. Já o material Eversoft não apresentou alteração nos valores de dureza e rugosidade de superfície em nenhuma das técnicas de desinfecção. / Abstract: The aim of this study was to assess the effect of disinfections with 2% glutaraldehyde, 5% sodium hypoclorite, 5% chlorhexidine solution and microwave oven on hardness and roughness of soft denture liners Ufi Gel, Molloplast-B, Eversoft and Mucopren soft. Forty samples (36x7x6 mm) of each material were processed in special microwave flasks according to manufacturers' recommendation. Ten specimens of each material were immersed in each disinfectant solution for ten minutes or placed in a microwave oven for 3 minutes at 500W. The surface roughness and hardness values were recorded after 24 hours (control), and also at each two cycles of disinfection. Hardness readings were made on the sample surface with Shore A durometer according to the ASTM D-2240 specifications. The surface roughness was verified on the other surface using a Surf-Coder SE 1700 perfilometer. Data were submitted at analysis of variance and Tukey's test to 1% of level. The application of two disinfection cycles did not change the hardness values significantly. However, after the first cycle of disinfection, means of surface roughness were lower than those observed for the control. The glutaraldehyde solution promoted the highest values of hardness on Molloplast-B, Mucopren soft and Ufi Gel materials. The Eversoft did not show changes in hardness and surface roughness independent of disinfection technique. / Mestre

A presente pesquisa teve por objetivo a análise do comportamento de diferentes combinações de liners de um determinado solo com e sem cimentação, submetidos à percolação de líquidos ácidos, com o objetivo de simular o comportamento de campo de liners de aterros especiais, que recebem resíduos à base de pirita. Tal resíduo em contato com água e oxigênio forma solução de ácido sulfúrico. Assim sendo, as pretensões deste trabalho foram a análise do comportamento compressivo de liners formados por um dado tipo de solo compactado, com e sem a adição de cimento, através do emprego de um equipamento de adensamento modificado desenvolvido especialmente para esta pesquisa. Da mesma forma, procedeu-se o estudo dos fenômenos de transporte de contaminantes por meio do liner em estudo, basicamente daqueles que comandam o transporte (difusão, advecção, sorção, retardamento da frente de contaminação e grau de afinidade entre o contaminante e o liner). Ensaios isotrópicos a altas tensões de confinamento também foram realizados a fim de se estudar a possível desestruturação dos liners quando percolados por resíduos ácidos. Os resultados obtidos destacam a desestruturação de amostras naturais do solo estudado quando percolado por rejeitos ácidos, em todas as concentrações estudadas, tanto em ensaios triaxiais isotrópicos quanto em ensaios de carregamento axial com deformações laterais nulas. Conclui-se que as águas ácidas quando percoladas por meio de um solo com presença de finos, tende a proporcionar um efeito de carreamento de partículas, aumentando conseqüentemente a porosidade, fator este que poderia proporcionar a falha operacional de um liner. / The objective of this work is to analyse the behavior of a liner formatted by different combinations of soil and cement, percolated by low pH waters under different hydraulic gradients and concentration of acid in the percolant, aiming to simulate in laboratory what would happen in the field to liners in contact with pyrite wastes, from mineral coal mining. Pyrite wastes in contact with water and oxygen result in sulphuric acid, what makes the objective of this research the study of the compressive behavior of the liner submitted to the percolation of acid waters, by means of a special column equipment developed during this research, which allows applying an axial load to the sample under flux. Also, the variation of the transport of contaminants values were investigated, basically diffusion, advection, sorption, retardation coefficient, distribution coefficient, hydrodynamic dispersion, ground water velocity and hydraulic conductivity). Triaxial Isotropic tests were carried out under high confinant pressures in order to verify the volume changes of the samples due to the low-pH contamination. The results show that liners formatted only by soil had rearrange of their structure due to acid percolations, according to both column and isotropic tests. The value of the hydrodynamic dispersion was considerated being totally dependent on the diffusion, because the hydraulic conductivity of the differente combination was low. The results also show that low-pH percolations make a rearrange of the fine particles into the sample, because after a grain size distribution test, the fine particles from the top of the samples were detected on the bottom of the sample, what increase the porosity on the top of the samples, what could lead the liner to a failure.