Orientador: Fernando Galembeck / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-14T14:09:30Z (GMT). No. of bitstreams: 1 Linares_ElisangelaMoura_M.pdf: 5164980 bytes, checksum: d9e4505544f0a48a985e78fccc9e1832 (MD5) Previous issue date: 2009 / Resumo: Este trabalho mostra o efeito da distribuição de espécies iônicas na morfologia e nas propriedades mecânicas de filmes de blendas de látices, e também demonstra o uso da técnica de microscopia eletrônica de transmissão por energia filtrada (EFTEM) para caracterização morfológica das blendas e de seus nanocompósitos com argila, explorando a região de baixa perda de energia de elétrons. Blendas de látex de borracha natural (NR)/poli(estireno-acrilato de butila) [P(S-BA] e NR/poli(cloreto de vinila) [PVC] foram investigadas, utilizando-se microscopia de varredura de potencial elétrico (SEPM). Através dos mapas de potencial elétrico, foi verificada a ocorrência de migração de espécies iônicas da blenda de uma fase polimérica para a outra, durante a preparação da blenda. Esta migração é espontânea, porque permite a redução da energia do sistema através da diminuição da repulsão eletrostática entre íons, distribuindo-os entre as fases, e é direcionada para o polímero que inicialmente tem menor concentração de cargas e apresenta maior constante dielétrica. Os domínios formados pelos dois componentes da blenda apresentam sinais de carga opostos, o que contribui para o aumento na compatibilidade, através da adesão eletrostática. Os espectros de baixa perda de energia mostram diferenças nas estruturas moleculares dos polímeros das blendas. Essas diferenças se expressam através de mudanças de contraste em imagens de perda de energia (mapas moleculares) adquiridas entre 20 e 90 eV. Blendas de NR/P(S-BA), P(S-BA)/PVC, P(S-BA)/poli(estirenometacrilato de 2-hidroxietila) e seus respectivos nanocompósitos foram analisados por EFTEM que revelou domínios em escala nanométrica, mesmo tendo pequenas diferenças na composição química, sem a necessidade de corar a amostra. Nos nanocompósitos, a disposição das lamelas de argila foi revelada graças ao cancelamento do contraste entre os polímeros. / Abstract: This work shows the effect of ionic specie distribution on the morphology and on the mechanical properties of latex blend films, as well as it demonstrates the use of energy-filtered transmission electron microscopy (EFTEM) technique to morphological characterization of these blends and its clay nanocomposites, by exploring the low-loss electron energy region. Natural rubber (NR)/poly(styrenebutyl acrylate) [P(S-BA)] and NR/poly(vinyl chloride) [PVC] blends were investigated by scanning electric potential microscopy (SEPM). Using the electric potential maps, it has been observed ionic specie migration from one polymer phase towards the other, during blend preparation. The migration is spontaneous because it allows the reduction of system energy thanks to the decreasing of ionion electrostatic repulsion given by ion distribution throughout the phases. The migration is directed towards the polymer that has initially the lower charge concentration and that presents the higher dielectric constant. The domains formed by the two blend component present opposite charge signals, which contribute to compatibility enhancement through electrostatic adhesion. Low-energy-loss electron spectra show differences on molecular structure of polymers that form the blends. Such differences are expressed through contrast changing in low-energyloss images (molecular maps) acquired between 20 and 90 eV. NR/P(S-BA), P(SBA)/ PVC, P(S-BA)/poly(styrene-2-hydroxyethyl metacrylate) and their respective clay nanocomposites have been analyzed by EFTEM without staining and it revealed nano-sized domains, even when chemical composition was slightly different. Clay platelet distribution within nanocomposites was revealed due to contrast canceling of polymer domains on EFTEM images. / Mestrado / Físico-Química / Mestre em Química

No description available.

Ingeniero Civil Químico / En los últimos años se ha extendido el uso de materiales que destacan, principalmente, por su biocompatibilidad, razón por la cual son utilizados en aplicaciones biomédicas. El ácido poliláctico (PLA) es un biopolímero que, además de ser biocompatible, es biodegradable. Estas características lo hacen ser un material muy utilizado en biomedicina. Sin embargo, las aplicaciones biomédicas requieren la consideración de diversas propiedades del material, pues se busca lograr una estabilidad en la interacción con sistemas biológicos. De esta forma, el interés es desarrollar materiales multifuncionales que presenten propiedades optimizadas, tales como mecánicas, bioactividad, propiedad antibacteriana, conductividad eléctrica, entre otras. La presente memoria se centra en el desarrollo de nanocompuestos poliméricos de PLA con derivados del grafito (óxido de grafeno, GO, y óxido de grafeno térmicamente reducido, TrGO) mediante mezclado en fundido. Así, se busca evaluar las propiedades antimicrobianas, biocompatibles, mecánicas y eléctricas de los materiales desarrollados. Los ensayos microbiológicos indican que el compuesto con 5% en peso GO logra un 100% de efectividad en contra de ambas bacterias estudiadas (E. coli y S. aureus). Mismo resultado se obtiene cuando se genera una corriente eléctrica por la placa de 10% en peso de TrGO. Por otro lado, para los compósitos con GO aumenta la proliferación celular, mientras que para el TrGO se logra el mismo valor de viabilidad que para el PLA, en células SaOS-2. Esto indica que los compósitos desarrollados tienen una buena biocompatibilidad, sin riesgo de toxicidad para su uso con tejidos vivos. En particular, los compósitos con GO emergen como una alternativa pues mejoran la proliferación de las células. El módulo de elasticidad aumentó su valor tanto para los compuestos con GO como para los con TrGO. Sin embargo, este crecimiento se acentúa para los primeros, donde se logra aumentar un 14% el módulo a una concentración de solo 2% en peso de GO. Además, para compósitos con ambas partículas la elongación a la rotura disminuyó. La conductividad eléctrica de los compósitos depende fuertemente del tipo de relleno utilizado, logrando una conductividad eléctrica de 10−2[𝑆������𝑆������/𝑚������𝑚������] para un contenido de 10% en peso de TrGO. En contraste, para los compósitos con GO no se obtuvo conductividad, ya que, a diferencia del grafeno, esta nanopartícula no es conductora. De esta forma, el estudio indica que se mejoraron las propiedades antibacteriales, biocompatibles, mecánicas y eléctricas de los nanocompósitos de PLA al agregar rellenos de GO y TrGO. Así, los materiales desarrollados pueden ser utilizados en aplicaciones biomédicas e interaccionar con sistemas biológicos sin problemas.

No description available.

Orientador: João Sinézio de Carvalho Campos / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-27T19:06:13Z (GMT). No. of bitstreams: 1 Conceicao_RafaelNovaesda_M.pdf: 10111957 bytes, checksum: 9168b5514bd29d6ead99888af5052aab (MD5) Previous issue date: 2015 / Resumo: É bem conhecida a necessidade de energia elétrica para o bem estar e desenvolvimento tecnológico da população em nosso planeta. Ao lado dos avanços científicos de novas tecnologias para geração, existem interesses na melhoria do transporte da energia. Dentre estes se encontram materiais para isolação elétrica de barras estatóricas, quer sejam para melhorar a isolação ou mesmo para reduzir custos. Assim, o presente trabalho visa apresentar resultados da aplicação de uma nova resina epóxi bisfenólica (DGEBF) (RN) à base de nanopartículas de sílica e comparar suas propriedades com a resina epóxi bisfenólica (DGEBA) (RE), atualmente utilizada para a isolação de hidrogeradores. Neste sentido, fabricaram-se protótipos de barras estatóricas, destinadas a hidrogeradores, sendo as resinas impregnadas em sistema VPI (Vácuo-Pressão-Impregnação) e avaliaram-se as propriedades físico-químicas pelas técnicas de viscosimetria, TGA, DSC, MEV e EDS. As propriedades elétricas foram avaliadas pelas técnicas de fator de dissipação (tan delta), descargas parciais, envelhecimento acelerado (VET) e tensão de ruptura. Dentre os resultados das propriedades físico-químicas pode-se comprovar um aumento inicial de três vezes o valor de viscosidade para resina RN em comparação com RE. Entretanto, não houve detrimento das características dielétricas em função da viscosidade, o que foi comprovado através dos resultados de tan delta e VET. Obteve-se um valor de Tg de 116°C e 145°C para RN e RE, respectivamente, o que limitaria a aplicação da resina em geradores por estar abaixo da temperatura de operação. Dentre os resultados dos testes elétricos para as resinas observou-se que: (i) o fator de dissipação e de envelhecimento são praticamente os mesmos para ambas as resinas; (ii) o valor de tip-up resultaram em 0,014 % para RE e 0,020 % para a resina RN, sendo que a norma EN 50209 exige que seja inferior a 0,25% e (iii) a estimativa do tempo de vida útil obtida foi de cerca de 40 anos para os dois tipos de resina, o que é aplicável para maioria dos enrolamentos em operação. Neste sentido sugere-se que a resina RN pode ser uma boa alternativa a resina RE, com um desempenho elétrico equivalente, desde que ajustadas suas condições de processamento e temperatura de aplicação / Abstract: It is well know the demand of electrical energy for the wellbeing and technological development of the population in our planet. Among the scientific development of new technologies for generation, are interests to optimize the energy transport. Among them are materials for electrical insulation of stator bars, whether for improving the insulation or even to reduce the costs. Therefore, the present work aim to present the results of the employment of a new bisphenolic epoxy resin (DGEBF) (RN) containing silica nanoparticles and compare its properties with the bisphenolic epoxy resin (DGEBA) (RE) currently used for the insulation of hydrogenerators. In this context, it was manufactured prototype stator bars, designed for hydrogenerators, being the resins impregnated through VPI (Vacuum-Pressure-Impregnation) system and their physicochemical properties evaluated with the technics of viscosimetry, TGA, DSC, MEV and EDS. The electrical properties were evaluated with the tests of dissipation factor (tan delta), partial discharges, voltage endurance test (VET) and breakdown. Among the results of the physicochemical properties it was possible to verify an initial increase of three times the value of viscosity for RN resin compared to RE. However there was no detriment of the dielectric characteristics depending on the viscosity, what was proven with the results of dissipation factor and VET. It was obtained a value of Tg of 116°C and 145°C for RN and RE respectively, what could limit its employment for hydrogenerators as being below the operational temperature. Among the results of electrical tests for the resins it was observed that: (i) the dissipation factor and VET are practically the same for both resins; (ii) the tip-up value resulted in 0,014% for RE and 0,020% for RN, being required lower than 0,25% according to the norm EN 50209 and (iii) the estimating lifecycle was approximately 40 years for both types of resin, what is applicable for most windings under operation. In this context it is suggested that the RN resin can be a good alternative for RE resin with an equivalent performance once the process conditions and employment temperature are adjusted / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

Submitted by Fernanda Rodrigues de Lima (fernanda.rlima@ufpe.br) on 2018-10-08T21:28:27Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) / Approved for entry into archive by Alice Araujo (alice.caraujo@ufpe.br) on 2018-11-22T17:28:36Z (GMT) No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) / Made available in DSpace on 2018-11-22T17:28:36Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) Previous issue date: 2015-03-19 / CNPq / A utilização de semicondutores orgânicos como materiais ativos em dispositivos optoeletrônicos é uma área de intensa pesquisa e inovação nos dias de hoje. Células solares baseadas em blendas de polímeros condutores ganharam muita atenção devido a suas características mecânicas e bom rendimento, ao que se combina um baixo custo de fabricação. Neste trabalho, investigamos a influência de aspectos óticos e estruturais dos materiais utilizados sobre o transporte eletrônico em dispositivos fotovoltaicos moleculares à base de polihexiltiofeno (P3HT) e 5-(2-etil-hehilóxi)-1,4-fenileno vinileno (MEHPPV) associados com fulerenos funcionalizados (PCBO), e de nanopartículas de ouro recobertas com polianilina (PANI-AuNPs). Os filmes de P3HT e MEH:PPV foram depositados a partir das soluções coloidais por meio da técnica de spin-coating, sendo cada um dos polímeros solubilizado em clorobenzeno. Através de medidas de corrente-tensão realizadas sob luz "solar simulada", e tendo a temperatura, a tensão aplicada e a área ativa dos dispositivos como parâmetros de controle, estimamos a eficiência de conversão de energia. Vale ressaltar que normalmente as técnicas convencionais utilizadas para medir mobilidade elétrica se utilizam de arranjos elétricos e ópticos acoplados, como é o caso das medidas de Tempo de Voo (TOF). Neste trabalho, como método alternativo, nos baseamos em medidas de espectroscopia de impedância elétrica na ausência de luz e com varredura na frequência para estimar a mobilidade dos portadores de carga negativos no interior dos dispositivos. Além disso, avaliamos o efeito de fatores da preparação (velocidade de rotação, temperatura de annealing e concentração de PANI-AuNPs) dos diferentes dispositivos fotovoltaicos sobre a eficiência e a mobilidade eletrônica, de modo a estabelecer a dinâmica de condução nas diferentes células solares orgânicas nanoestruturadas investigadas. / The use of organic semiconductors as active materials in optoelectronic devices is nowadays an area of intense research and innovation. Solar cells based on blends of conductive polymers have deserved a lot of attention due to their mechanical characteristics and good efficiency, which could be attained with low manufacturing costs. In this study, we investigated the influence of optical and structural aspects of the material used for the electron transport in molecular-based photovoltaic devices polihe-xiltiofeno (P3HT) and 5-(2-ethylhehiloxi)-1,4-phenylene vinylene (MEH-PPV) associated with functionalized fullerenes (PCBO) and gold nanoparticles coated with polyaniline (PANI-AuNPs). The P3HT films and MEH:PPV were deposited from colloidal solutions through the spin-coating technique, where in each case the corresponding polymer was previously solubilized in chlorobenzene. Through current-voltage measurements performed under "simulated sunlight", and taking the temperature, the applied voltage and the active area of the devices as control parameters, we were able to estimate the corresponding energy conversion efficiency. It is noteworthy that usually the conventional techniques used to measure electric mobility involve the use of coupled electrical and optical arrangements, such as is the case of the flight time (TOF) method. In this work, based on electrical impedance spectroscopic methods, in the absence of both incident light and scanning frequency, we were able to estimate the mobility of negative charge carriers within the device. Furthermore, we evaluated the effect of the preparation factors (rotation speed, temperature and annealing concentration of PANI-AuNPs) of different photovoltaic devices on the efficiency and electron mobility in order to establish different driving dynamics in organic solar cells nanostructured investigated.

Orientador: Dayse Iara dos Santos / Resumo: O desenvolvimento de materiais cerâmicos é um campo de pesquisa cujos resultados são extremamente promissores para aplicações tecnológicas. Particularmente, no caso dos materiais nanoestruturados baseados no óxido titânio, observa-se grande potencial de aplicação em dispositivos optoeletrônicos, bem como, para processos de fotocatálise, visto que apresenta um bandgap direto de 3,2 eV. Além disso, o aperfeiçoamento das propriedades ópticas, por meio da interação entre óxidos de diferentes bandas eletrônicas, têm sido estudado por muitos autores. Por esta razão, compósitos nanoestruturados formados de dois ou mais óxidos, cujas propriedades são distintas quando isolados, têm sido sintetizados juntos e caracterizados a fim de avaliar possíveis interações sinérgicas. Neste trabalho, foram preparados e caracterizados os compósitos TiO2/CuO, TiO2/ZnO e TiO2/ZrO2. As sínteses foram realizadas pelo método Sol-gel original e pelo método Poliol modificado, e ambos os processos se mostraram propícios para a obtenção de nanocompósitos e óxidos nanoparticulados. O método Poliol produziu compósitos formados de partículas micrométricas de dióxido de titânio revestidas do segundo óxido, enquanto o processo Sol-gel resultou em material constituído de agregados de nanocristais com alta mesoporosidade. Por meio da difração de raios X dos pós tratados gradualmente até 1000 °C observou-se que a formação e cristalização dos óxidos ocorrem em temperatura mais alta quando o material é resultante do ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The development of ceramic materials is a field of research whose results are extremely promising for technological applications. Particularly, in the case of nanostructured materials based on titanium oxide, there is a great potential for application in optoelectronic devices, as well as for photocatalysis processes, since it has a direct bandgap of 3.2 eV. In addition, the improvement of the optical properties through the interaction between oxides of different electronic bands has been studied by many authors. For this reason, nanostructured composites formed of two or more oxides, whose properties are distinct when isolated, have been synthesized together and characterized in order to evaluate possible synergistic interactions. In this work the TiO2 / CuO, TiO2 / ZnO and TiO2 / ZrO2 composites were prepared and characterized. The syntheses were carried out using the original Sol-gel method and the modified Polyol method, and both processes proved to be suitable for nanocomposites and nanoparticulate oxides. The polyol method produced composites formed of micrometric titanium dioxide particles coated with the second oxide, while the sol-gel process resulted in material composed of nanocrystalline aggregates with high mesoporosity. By X-ray diffraction of the powders gradually treated to 1000 °C it was observed that the formation and crystallization of the oxides occur at a higher temperature when the material is produced by the Sol-gel process. With the observation of the ... (Complete abstract click electronic access below) / Doutor

Conselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPq / The search for more productive seeds and with better transport and storage conditions has developed the interest of companies and researchers. In this section, nanotechnology, in particular, polymer / clay nanocomposites has proved to be an excellent alternative. By means of these nanomaterials it is possible to transport assets that allow the plant to better growth, productivity and germination rates, through the transport of fertilizers, agrochemicals or even essential micronutrients. The aim of this work was to synthesize and study nanocomposites polymer / clay; poly (hydroxyethyl methacrylate), pure laponite (pHEMA / Lap) and enriched with manganese micronutrients (pHEMA / LapMn). These materials aim to provide water and concomitantly provide nutrients to the seeds. The best formulation for the samples, amounts of polymer and clay was studied, and from this the micronutrient was incorporated into the formulation. The materials were characterized by absorption spectroscopy in the infrared region (FTIR), X-ray diffractometry (XRD) and thermogravimetry (TG). In addition, the water uptake capacity of the samples was evaluated. TG results showed an increase in thermal stability due to the interaction of the polymer chain with the clay. The XRD study showed that pure Lap and Lap Mn presented similar basal spacing to that found in the literature and that the nanocomposite had an exfoliated structure of the materials. The observation of the degree of swelling of the samples showed that the nanocomposites showed a capacity of water absorption 10% higher than the pure hydrogel. The seed coating affected the germination rate of the seeds, showing an optimization of this process. / A busca por sementes mais produtivas e com melhores condições de transporte e armazenamento tem desenvolvido o interesse de empresas e pesquisadores. Nesta vertente, a nanotecnologia, em especial, os nanocompósitos polímero/argila tem se mostrado uma excelente alternativa. Por meio destes nanomateriais é possível transportar ativos que possibilitem a planta melhor crescimento, produtividade e taxas de germinação, por meio do transporte de fertilizantes, agroquímicos ou até micronutrientes essenciais. Neste trabalho buscou-se sintetizar e estudar nanocompósitos polímero/argila; poli(metacrilato de hidroxietila) (pHEMA), laponita pura (pHEMA/Lap) e enriquecida com micronutrientes manganês (pHEMA/LapMn). Estes materiais tem por objetivo fornecer água e concomitantemente fornecer nutrientes para as sementes. Estudou-se qual a melhor formulação para as amostras, quantidades de polímero e de argila e a partir desta incorporou-se o micronutriente a formulação. Os materiais foram caracterizados por espectroscopia de absorção na região do infravermelho (FTIR), difratometria de raios X (DRX) e termogravimetria (TG). Além disso, a capacidade de absorção de água das amostras foi avaliada. Houve aumento da estabilidade térmica decorrente da interação da cadeia polimérica com a argila. O estudo por DRX mostrou que a Lap pura e a Lap Mn apresentaram espaçamento basal similar ao encontrado na literatura e que o nanocompósito apresentou estrutura esfoliada dos materiais. A observação do grau de intumescimento das amostras mostrou que os nanocompósitos apresentaram uma capacidade de absorção de água 10% superior à do hidrogel puro. O revestimento das sementes prejudicou a taxa de germinação das mesmas mostrando-se necessário uma otimização deste processo. / São Cristóvão, SE

Orientador: Devaney Ribeiro do Carmo / Resumo: Neste trabalho, novos nanocompósitos híbridos a base de silsesquioxano e nitroprussiato de cobalto e zinco foram preparados, seguindo dois métodos de síntese. Os materiais preparados foram caracterizados empregando diferentes técnicas: Espectroscopia na Região do Infravermelho por transformada de Fourier (FTIR), Espectroscopia Raman, Espectroscopia de Reflectância Difusa UV/Vis, Ressonância Magnética Nuclear (RMN), Difração de Raios-X (DRX), Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Energia Dispersiva de Raios-X (EDX), Microscopia Eletrônica de Transmissão (MET) e Análise Termogravimétrica (TGA). Após a obtenção dos nanocompósitos com complexos metálicos de nitroprussiato (ACCoN e ACZnN), realizou-se um estudo sistemático sobre o comportamento voltamétrico desses materiais, empregando técnicas eletroquímicas, tais como: Voltametria Cíclica (VC) e Voltametria de Pulso Diferencial (VPD), utilizando eletrodos de pasta de grafite. O eletrodo de pasta de grafite contendo ACCoN mostrou-se sensível a concentrações de hidrazina e isoniazida. Já o eletrodo de pasta de grafite contendo ACZnN foi aplicado na detecção de N-acetilcisteína e isoniazida com sucesso. Após os testes de eletro-oxidação catalítica dessas substâncias, realizou-se uma investigação da influência dos principais interferentes, de forma que a interferência observada não se mostrou significativa. Avaliou-se também a recuperação destas substâncias a partir de amostras de água da torneira e urina sint... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In this work, new nanocomposites based on silsesquioxane and cobalt and zinc nitroprusside were prepared, following two synthetic methods. The prepared materials were characterized by different techniques: Fourier Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, UV-Vis Diffuse Reflectance Spectroscopy, Nuclear Magnetic Resonance (NMR), X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive X-ray spectroscopy (EDX), Transmission Electron Microscopy (TEM), Thermogravimetric Analysis (TGA). After obtaining the nanocomposites with metallic nitroprusside complexes, it was carried out a systematic study on the voltammetric behavior of these materials, using electrochemical techniques, such as: Cyclic Voltametry (CV) and Differential Pulse Voltammetry (DPV), using graphite paste electrodes. The graphite paste electrode containing ACCoN was sensitive to concentrations of hydrazine and isoniazid. The graphite paste electrode containing ACZnN was applied to the detection of N-acetylcysteine and isoniazid, with success. After catalytic electrooxidation tests of these substances, it was investigated the influence of the main interferents, so that the noticed interferences were not significant. Also, it was evaluated the recovery of these substances from samples of tap water and synthetic urine. By this way, the binuclear hybrid nanocomposites formed (ACCoN and ACZnN) are potential candidates for the construction of electrochemical sensors in the hydrazi... (Complete abstract click electronic access below) / Doutor

Orientador: Sidney Jose Lima Ribeiro / Coorientador: Hernane da Silva Barud / Banca: Patrícia Bento da Silva / Banca: Rosana Maria Nascimento de Assunção / Resumo: A celulose bacteriana (CB) é um nanomaterial que pode ser obtido a partir de bactérias do gênero Gluconacetobacter. O material é formado por uma rede de fios nanométricos que lhe confere enorme área superficial, surpreendente capacidade de absorção e retenção de água, boa elasticidade e fácil moldabilidade. O material também é biodegradável, biocompatível, atóxico e não alergênico. A CB pode ser sintetizada a partir de uma variedade de fontes de carbono, através de bactérias que são capazes de converter glicose à celulose como parte de seu metabolismo. Assim, a glicose atua não somente como fonte de energia para o microrganismo, mas também como precursora da biossíntese de CB. A CB produzida na superfície do meio de cultura pela bactéria Gluconacetobacter xylinus foi utilizada para a produção in situ de nanocompósitos com propriedades químicas e físicas modificadas devido a presença de laponita (LPN) que possui composição bem definida e livre de impurezas insolúveis, como partículas de sílica e óxidos de ferro. As dimensões nanométricas dessas argilas, aliadas ao seu formato circular e capacidade de produzir materiais transparentes, como filmes e dispersões, auxiliam na obtenção de nanocompósitos de alta homogeneidade. Neste trabalho foi realizada a preparação e caracterização de nanocompósitos de CB, por meio da incorporação "in situ" de LPN. Os filmes CB/LPN foram caracterizados morfologicamente, por microscopia eletrônica de varredura com EDS e microscopia de força atômica... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Bacterial cellulose (CB) is a nanomaterial that can be obtained from bacteria of the genus Gluconacetobacter. The material is formed by a network of nanometric wires that gives it enormous surface area, surprising capacity of water abs orption and retention, good elasticity and easy moldability. The material is also biodegradable, biocompatible, non - toxic and non - allergenic. CB can be synthesized from a variety of carbon sources, through bacteria that are able to convert glucose to cellu lose as part of their metabolism. Thus, glucose acts not only as a source of energy for the microorganism, but also as a precursor of CB biosynthesis. The CB produced on the surface of the culture medium trough the bacterium Gluconacetobacter xylinus was u sed for the in situ production of nanocomposites with chemical and physical properties m odified due to the presence of l aponite (LPN) that has a well defined composition and free of insoluble impurities, as particles of silica and iron oxides. The nanometr ic dimensions of these clays, combined with their circular shape and the ability to produce transparent materials, such as films and dispersions, help to obtain nanocomposites of high homogeneity. In this work the preparation and characterization of CB nan ocomposites was carried out by the in situ incorporation of LPN. The CB/LPN films were characterized morphologically by scanning electron microscopy with EDS and atomic force microscopy. Structurally, by X - ray diffraction, t he... (Complete abstract click electronic access below) / Mestre