O presente trabalho se propôs a avaliar, por meio de análise fotoelástica, o comportamento biomecânico de próteses parciais fixas cimentadas sobre implantes cone Morse (Titamax CM 4.0x11mm, Neodent) com coroas isoladas ou unidas, simulando a reabilitação de áreas posteriores com e sem a presença de elemento dental distal aos implantes, e ainda variando o tipo de material de recobrimento estético empregado na restauração protética (cerâmica ou resina), quando sobre estas próteses foram aplicadas diferentes tipos de cargas estáticas. Foi confeccionado um modelo fotoelástico simulando um espaço protético intercalado, com ausência do segundo pré-molar e primeiro molar, reabilitado por meio de quatro tipos de coroas cimentadas sobre dois implantes adjacentes: UC - coroas unidas com recobrimento estético em cerâmica; IC - coroas individuais com recobrimento estético em cerâmica; UR - coroas unidas com recobrimento estético em resina; IR - coroas individuais com recobrimento estético em resina. Análise fotoelástica qualitativa foi realizada sob diferentes condições de aplicação de carga na superfície oclusal das coroas: oclusal distribuída (10kgf), puntiforme simultânea (10kgf), puntiforme alternada no molar e no pré-molar (5kgf). A primeira análise foi feita na presença de contato proximal efetivo entre as próteses e o dente a distal dos implantes. A segunda análise foi realizada após a eliminação da coroa do dente distal no modelo fotoelástico. Registros fotográficos foram obtidos de cada situação de análise, a fim de facilitar a observação e comparação do padrão de distribuição das franjas isocromáticas em torno dos implantes. De acordo com os resultados obtidos, pode-se concluir que as restaurações cimentadas provocaram tensões no modelo fotoelástico mesmo quando da ausência de cargas oclusais. A ferulização das restaurações em cerâmica promoveu melhores distribuições das tensões isocromáticas em torno dos implantes. A presença do pilar distal com ponto de contato efetivo e ajustado nas restaurações modificou a distribuição das tensões isocromáticas, sendo que os estresses gerados pelas cargas oclusais foram também dissipados pelas réplicas dos dentes e transmitidos ao sistema fotoelástico. Ressalta-se a importância da obtenção de oclusão bem ajustada e equilibrada, para que haja adequada distribuição de forças aos implantes e osso de suporte, garantindo maior longevidade e previsibilidade de sucesso. / The purpose of this study was to evaluate the biomechanical behavior of fixed prostheses cemented over morse taper implants simulating a posterior rehabilitation with or without distal teeth to the implants, by use of a photoelastic stress analysis technique. Non-segmented or segmented ceramic or resin crowns were constructed over the implants and were evaluated when different static loads were applied. A photoelastic model simulating a prosthetic space without the second premolar and the first molar was done. The edentulous space was rehabilitated with crowns cemented over morse taper implants: UC = non-segmented ceramic crowns; IC = segmented ceramic crowns; UR = non-segmented resin crowns, and IR = segmented resin crowns. Qualitative photoelastic analysis was done with different loads conditions at the occlusal surface of the crowns: distributed occlusal (10kgf), punctiform over the first molar and second premolar simultaneously (5kgf), and punctiform over the first molar or second premolar alternatively (5kgf). The first analysis was done when the proximal contact was present between the crowns and the distal teeth to implants. The second was done after the remotion of the distal teeth at the photoelastic model. The resulting stress in all areas of the model was monitored and recorded photographically in the field of a circular polariscope. The fringe pattern findings were collected for the loadings subjected to each condition and loading position. According to the results obtained it would be concluded that the cemented restorations promoted stress even without occlusal loads. The ferulization of the ceramic restorations promoted a better stress distribution around the implants. The presence of the distal teeth with an effective and adjusted contact point modified the stress distribution. Stresses generated by occlusal loads was distributed by the replicas of the teeth and transmitted to the photoelastic system. The adjusted and balanced occlusion is important to the correct load distribution to the implants and support bone, which assure a better prognostic to the rehabilitation.

A dureza é uma propriedade bastante utilizada para comparar tanto os materiais restauradores como os tecidos biológicos. É definida pela resistência do material à deformação plástica e mensurada pela relação da força aplicada e a área de endentação. Para esse estudo foram utilizados dois materiais: amálgama e resina composta e dois tecidos dentais: dentina e esmalte bovinos. No total foram confeccionados 20 espécimes, divididos em 4 grupos: A (Amálgama), R (Resina Composta), D (Dentina) e E (Esmalte) de acordo com cada superfície. Para os grupos A e R foram confeccionadas cavidades que foram restauradas com os respectivos materiais, no grupo E teve a superfície apenas planificada e o grupo D teve desgaste até a exposição de dentina. Para os testes foram utilizados os endentadores Vickers e Knoop; as cargas de 25, 50 e 100gf em cinco tempos de endentação 5, 15, 30, 45, e 60s. Os valores dos testes foram submetidos à análise estatística pelo teste Kruskall-Wallis e Student-Newman-Keuls (p<0,05). Os resultados permitiram concluir que para o amálgama deve se utilizar no mínimo uma carga de 50gf em um tempo mínimo de 30s tanto para a Vickers como para a Knoop. Na resina composta uma carga de 50gf e tempo de 45s para a Knoop e na dureza Vickers não apresentou diferenças. Na dentina a carga ideal é de pelo menos 50gf em qualquer dos tempos na dureza Vickers e Knoop. E o esmalte uma carga de 100gf para qualquer tempo na dureza Knoop. / The hardness is a mechanical property utilized to compare restorative materials such as biological tissue and can be defined as the resistance of material for a permanent impression and a number related to the applied force and the surface area. As each material has its own mechanical characteristic, for this study utilized two materials: amalgam and composite resin and two dental tissues: bovine dentin and enamel. In total were 20 specimes, divided among 4 groups: A, R, D, E equivalent for each superficial. The groups A and R received cavities preparation that were restored into with the respective materials, the group D had the superficial wore until exposure of the dentin and the group E was so planning. For the microhardness testing were utilized Vickers and Knoop indenter; loads of 25, 50 and 100gf in 5 time of application 5, 15, 30, 45 e 60 seconds. The values were submitted for statistical analysis by Kruskall-Wallis and Student-Newman-Keus tests (p<0.05). Due to the results, it is concluded that the amalgam presented a minimum load adequated of 50gf and a time of application of 30 seconds as the Vickers as Knoop. In the composite resin the minimum load was 50gf and time was 45s for Knoop, the Vickers didnt have statistical diference. In dentin the minimum load was 50gf for all studies times for two tests. And the enamel presented the minimum load adequated was 100gf for all the times in the Knoop microhardness, the Vickers test didnt have statistical diference.

Made available in DSpace on 2017-07-24T19:22:15Z (GMT). No. of bitstreams: 1 Patricia Grau.pdf: 1130070 bytes, checksum: 82d9701d69189e5390f051daffb18268 (MD5) Previous issue date: 2005-11-17 / The aim of this investigation was to analyze the bond strength between a Second Generation Laboratorial Resin and dentin structure, verifying the effect of the internal treatment with silano agent, using two resin cement systems. The oclusal surface of twenty third human molars was removed and later polished. Blocks were constructed using the Second Generation Laboratorial Resin GradiaTM directly on the dentin structure. The 4 evaluated groups were: I) chemical resin cement sandblasting/silano; II) chemical resin cement sandblasting; III) dual resin cement sandblastings/silano/ and IV) dual resin cement sandblasting. Bonded sticks (0.9 mm² ± 0.2 mm²) were gotten by means of parallel and perpendicular cuts in the bonding interface. Each stick was fixed by its extremities to the modified device for the micro-tensile test in order to locate the area of adhesion perpendicular to the long axle of the force, in the universal assay machine (EMIC) crosshead speed 1mm/min. The final values of bond strength were express in MPa. The fracture modes were analyzed under 40X magnification. The data were submitted to two-way ANOVA and Tukey´s test (α=0.05). Results: The average values in MPa presented by each group were: I) 19.10±2.88; II) 13.67±3.31, III) 11.95±3.96; IV) 25.14±5.66. The analysis two-way ANOVA showed that the factor Treatment was significant (p=0.05), as well as the interaction of the factors Treatment and Type of cement (p=0.0001). The factor Type of cement was not significant (p=0.25). Conclusion: They were not statistical differences between the bond strength of the two resin cements, the internal treatment was significant, for the dual cement the application of the silano agent lowed the values of bond strength in the chemical cement the application of the silano increased the values of adhesive resistance, being not significant. The fracture modes were predominantly adhesive between the Second Generation Laboratorial Resin of and the resin cement. / O objetivo deste trabalho foi analisar a resistência adesiva entre o substrato dentinário e uma Resina Laboratorial de Segunda Geração, verificando o efeito do tratamento interno da peça com agente silano, utilizando dois sistemas de cimentos resinosos. A superfície oclusal de vinte terceiros molares humanos foi removida, e posteriormente polida. Foram confeccionadas peças em forma de blocos, utilizando a resina Laboratorial de Segunda Geração GradiaTM, diretamente sobre a estrutura dentinária. Os 4 grupos avaliados foram: I) jateamento/silano/cimento resinoso químico; II) jateamento/cimento resinoso químico; III) jateamento/silano/cimento resinoso dual e IV) jateamento/cimento resinoso dual. Os espécimes em forma de “palitos” de 0,9 mm² ± 0,2 mm² foram obtidos mediante cortes paralelos e perpendiculares a interface de união. Os “palitos” foram fixado pelas suas extremidades a um dispositivo de modo a posicionar a área de adesão perpendicular ao longo eixo da força de tração em uma máquina de ensaio universal (EMIC) a uma velocidade de 1mm/min. Os modos de fratura foram analisados com lupa esteroscópica (40X). Os dados obtidos foram submetidos à análise de variância para dois critérios e teste de Tukey (α=0,05). Resultados: Os valores médios em MPa apresentados por cada grupo foram: I) 19,10±2,88; II) 13,67±3,31, III) 11,95±3,96; IV) 25,14±5,66. A análise de variância de dois fatores demonstrou que o fator Tratamento da peça foi estatisticamente significante (p=0,05), assim como a interação dos fatores Tratamento da peça e Tipo de cimento (p=0,001). O fator Tipo de cimento não foi estatisticamente significante (p=0,25). Conclusão: Não houve diferenças estatísticas entre os cimentos resinosos testados, o tratamento interno da peça foi estatisticamente significante, para o cimento dual a aplicação do agente silano diminuiu estatisticamente os valores de resistência adesiva e no cimento químico os valores de resistência adesiva foram aumentados pela aplicação do agente silano não sendo estatisticamente significante. As modos de fratura foram predominantemente adesivas entre a Resina Laboratorial de Segunda Geração e o Cimento Resinoso.

Made available in DSpace on 2017-07-24T19:22:22Z (GMT). No. of bitstreams: 1 VeridianaCamilotti.pdf: 624713 bytes, checksum: f2d0756374875dd344e9aeeecdaac9cc (MD5) Previous issue date: 2005-12-15 / The following study aims to evaluate the influence between the different light sources in curing light of resin cement. The occlusal surfaces of twenty recently extractew undamaged third human molars were removed in order to expose dentine surface. Immediately after, the bond system (Adper Single Bond/3M ESPE ) and resin cement (RelyX ARC/ 3 M ESPE) was applied in accordance with manufacturer instructions. Second generation laboratory resin of 4 mm thickness was applied over tooth and light curing proceeded. According to light sources employed the teeth were divided in four groups: G1 – Control Optilux 401/ Demetron (QTH); G2 – L.E.Demetron/Demetron (LEDs ); G3 – Ultra-Lume LED5 (LEDs) e G4 – Optilight CL/ Gnatus (LEDs). Restored teeth were stored in physiologic serum for 24 h. After stored, teeth were sectioned into vestibule-tongue and mesial-distal to delimit an area with approximately 1 mm², the third cut was made on the base of the tooth in order to release the samples. The microtensile test was employed to reveal the bond strength values in MPa. The data underwent statistical analysis with p<0,05. No statistical significancent difference was found betweem the groups. In conclusion the resin cement bon strength of dual fotoative with LEDs showed similar adhesive resistance test those revelead when halogen lamp was used, and that there also were not differences among the different apparels LEDs used in that study. / Avaliou-se a influência de diferentes fontes de luz na fotoativação de um cimento resinoso dual. A superfície oclusal de 20 terceiros molares humanos hígidos foi removida para expor a superfície dentinária. Em seguida, foi aplicado sistema adesivo (Adper Single Bond/3M ESPE ) e cimento resinoso dual (RelyX ARC/ 3 M ESPE), de acordo com as recomendações do fabricante. A resina laboratorial de segunda geração (Gradia™ GC® América Inc), com espessura de 4 mm, foi adaptada sobre o dente e procedeu-se à fotoativação. De acordo com o aparelho de luz empregado, os elementos dentais foram divididos em 4 grupos: G1 – controle Optilux 401/ Demetron (QTH); G2 – L.E.Demetron 1/Demetron (LEDs ); G3 – Ultra- Lume LED5/Ultradent (LEDs) e G4 – Optilight CL/ Gnatus (LEDs). Os dentes restaurados foram armazenados em soro fisiológico por 24 h. Após o armazenamento, os dentes foram seccionados no sentido vestíbulo-lingual e mésiodistal, para delimitar uma área de 1 mm². Um terceiro corte na base do dente foi realizado com o objetivo de “soltar” os espécimes. O teste de micro-tração foi empregado para fornecer os valores da resistência adesiva em MPa. Os dados foram submetidos à análise estatística pelo teste ANOVA com p<0,05. Não houve diferenças estatisticamente significante entre os grupos testados. Concluiu-se que a resistência adesiva da interace adesiva fotoativado com LEDs foi semelhante à resistência adesiva obtida quando a lâmpada halógena foi utilizada e que também não houve diferenças entre os diferentes aparelhos LEDs empregados nesse estudo.

Pelas fraturas que sofrem os dentes caninos, torna-se necessário tratá-los endodonticamente, e repará-los proteticamente. Porém, novas fraturas coronais, com ou sem perda de coroa metálica podem se repetir. Muitas técnicas restauradoras priorizam os dentes com maior percentual de porção coronal, porque a extensa área de coroa remanescente assegura execução facilitada, favorecendo a recuperação do elemento dental e garantindo sucesso do assentamento da peça metálica. As pesquisas realizadas para se conseguir novos tratamentos utilizam dentes naturais para simular a realidade. Não há banco de dentes rotineiro na Odontologia Veterinária. O uso de dentes naturais de animais encontra restrições por conta da grande diversidade de raças e de porte entre cães, consequentemente no tamanho e na anatomia dos dentes. Existe ainda a carência de disponibilidade de amostras naturais na quantidade necessária para desenvolver tais estudos. O material artificial capaz de substituir os dentes naturais pode estar nas resinas compostas fotopolimerizáveis que apresentam propriedades mecânicas semelhantes às da dentina. Para se replicar o dente natural em resina composta, foi criado um molde em resina acrílica transparente. A literatura deste assunto é escassa ou mesmo inexiste. Com a construção de dentes artificiais muitas pesquisas podem ser realizadas, pois as amostras dentárias serão padronizadas de acordo com a necessidade de cada estudo a ser desenvolvido. Neste trabalho objetivou-se reproduzir quarenta dentes artificiais (réplicas) para demonstrar a possibilidade do padrão de cópia a partir do uso de um molde de resina acrílica. Os resultados mostraram que as réplicas foram similares ao dente natural. / Due to the fractures that canine teeth suffer, it is necessary to treat these teeth endodonticaly and restore them prosthetically (with pin, post core and metallic crown) in its coronal portion. However a new coronal fracture can happen with or without loss of the prosthodontic work. Many of the techniques aim at the teeth with larger extension of remaining area of crown, which favors the crown preparation and fixation of the prosthesis. Many researches use natural teeth to simulate the real conditions. In Veterinary Dentistry there is no routine bank of teeth. However there is a variety of dog breeds with different sizes, as well as a great variety in extension of the teeth. Additionally there is large numbers of natural teeth available enough for use in all researches. The material that can substitute the natural teeth seems to be the photo polymerized composite resin, which has similar mechanical properties to dentin. To replicate the natural teeth in composite resin, a mold was created in acrylic transparent resin. Literature of this subject is spares or inexistent. With artificial replication of teeth many researches can be achieved, once the samples of teeth can be standardized, according to which study. This project aimed to reproduce 40 replicas to demonstrate the possibility of copy from a transparent acrylic mold. Results showed that the replicas were similar to the natural tooth.

Esse estudo avaliou in vitro o efeito dos desafios erosivo ou erosivo/abrasivo sobre materiais restauradores contendo fluoreto ou cálcio e sobre as estruturas dentárias adjacentes às restaurações realizadas com esses materiais. Fragmentos de esmalte e de dentina bovinos (4 mm × 4 mm × 2 mm), foram incluídos em resina acrílica e planificados. Uma cavidade padrão com dimensões 1,2 mm × 4 mm × 1,5 mm foi preparada nos espécimes, e restaurada de acordo com o material a ser testado: 1. Z350 - resina composta (Filtek Z350, 3M ESPE); 2. VB - compósito experimental contendo apenas vidros de bário; 3. DCPD30% - compósito experimental contendo 10% de vidros de bário e 30% partículas de fosfato di-cálcio di-hidratado (DCPD) funcionalizadas com dimetacrilato de dietilenoglicol (DEGDMA); 4. DCPD60% - compósito experimental contendo 60% partículas de DCPD funcionalizadas com DEGDMA; 5. Beautifil - GIOMER (Beautifil II, Shofu Dental Corporation); 6. Fuji IX - cimento de ionômero de vidro convencional de alta viscosidade (Fuji IX, GC Corporation); 7. Fuji II LC - cimento de ionômero de vidro modificado por resina (Fuji II LC, GC Corporation). Na sequência, os espécimes foram polidos e submetidos a dois tipos de tratamentos: erosão somente (n=10) ou erosão mais abrasão por escovação (n=10). A erosão foi realizada pela imersão dos espécimes em ácido cítrico a 0,3% (pH~2,6) por 5 min, seguido de 60 min de imersão em saliva artificial. Esse procedimento foi repetido 4×/dia, por 5 dias. A escovação foi realizada com uma suspensão de dentifrício padrão (Colgate Total 12 Mint Clean; 1450 ppm F-, como NaF) por 15 s (2 min de exposição total a suspensão de dentifrício), 2×/dia, 30 min após o primeiro e o quarto desafios erosivos. Ao final da ciclagem, a perda superficial (em ?m) do esmalte, da dentina e dos materiais restauradores foi determinada com um perfilômetro ótico. Para cada modelo (erosão e erosão-abrasão), os dados de perda superficial de esmalte, dentina e restauração foram analisados de maneira independente. Os dados foram analisados pelos testes de Kruskal-Wallis e Tukey. O nível de significância utilizado foi de 5%. No modelo de erosão, para esmalte, ambos cimentos ionoméricos apresentaram menor perda superficial do que o compósito Z350, apesar de Fuji II LC não ter se diferenciado significativamente dos grupos Beautifil e DCPD30%. Os outros grupos não foram diferentes de Z350 nem entre si. Para dentina, nenhum dos grupos foi diferente de Z350, com exceção de DCPD60%, o qual apresentou a maior perda superficial. Ambos cimentos ionoméricos apresentaram menor perda do que DCPD30%, Beautifil e DCPD60%. Em relação à restauração, os materiais Z350, Beautifil, VB, DCPD30% apresentaram perda superficial mínima, sem diferenças entre eles. Os cimentos ionoméricos apresentaram os maiores valores de perda, não se diferenciando de DCPD60%. No modelo erosão-abrasão, para esmalte, a menor perda superficial foi observada em Fuji II LC, sem diferença da Beautifil. Os outros grupos não se diferenciaram entre si nem da Beautifil. Para dentina, os grupos DCPD60%, Beautifil, Fuji II LC, Z350 e Fuji IX não se diferenciaram e, apresentaram menor perda superficial do que VB. Os cinco grupos citados também não foram diferentes de DCPD30%, com exceção de Fuji IX. Em relação à restauração, a maior perda foi observada para Fuji IX, sem diferenças de Fuji II LC e Beautifil. DCPD30%, Z350, VB e DCPD60% apresentaram valores mínimos de perda superficial, sem diferenças entre si. Concluiu-se que o cimento ionomérico Fuji II LC foi único capaz de proteger o esmalte adjacente à restauração contra desafios erosivos e erosivos/abrasivos, apesar de ter sido um dos materiais mais susceptíveis ao desgaste por ambos desafios. Para dentina, nenhum material exibiu efeito protetor. / This in vitro study evaluated the effect of erosive or erosive/abrasive challenges on restorative materials containing fluoride and calcium, and on the dental hard tissues adjacent to restorations performed with these materials. Enamel and dentin specimens (4 mm × 4 mm × 2 mm), obtained from bovine incisors, were embedded in acrylic resin, flattened and polished. In the specimens, a standard cavity of 1,2 mm × 4 mm × 1,5 mm was prepared and restored with the following materials: 1. Z350 - Composite resin without actives, Filtek Z350 (3MESPE); 2. VB - experimental composite containing barium glass only; 3. DCPD30% - experimental composite containing 10% of barium glass and 30% of DCPD particles functionalized with DEGDMA; 4. DCPD60% - experimental composite containing 60% of DCPD particles functionalized with DEGDMA; 5. Beautifil - GIOMER (Beautifil II, Shofu Dental Corporation); 6. Fuji IX - high viscosity glass ionomer (Fuji IX, GC Corporation); 7. Fuji II LC - resin-modified glass ionomer (Fuji II LC, GC Corporation). The specimens were polished again and then submitted to one of the two treatments: erosion only (n=10) or erosion plus toothbrushing abrasion (n=10). Erosion was performed by immersing the specimens in 0.3% citric acid solution (p~2.6), for 5 min, followed by 60 min exposure to artificial saliva. This procedure was repeated 4 times a day, for 5 days. Toothbrushing was performed with a slurry of a standard dentifrice (Colgate Total 12 Mint Clean; 1450 ppm F, as NaF), for 15 s (2 min total exposure time to the slurry), 2 times a day, 30 min after the first and last erosive challenges. At the end of cycling, enamel, dentin and restorative material surface loss (in ?m) were determined by optical profilometry. Data were analyzed by the Kruskal-Wallis and Tukey tests. The level of significance was 5%. In the erosion model, for enamel, both ionomeric cements presented lower surface loss than the Z350, although Fuji II LC did not differ significantly from Beautifil and DCPD30% groups. The other groups were no different from Z350 and from each other. For dentin, none of the groups were different from Z350, except for DCPD60%, which presented the highest surface loss. Both ionomeric cements presented lower loss than DCPD30%, Beautifil and DCPD60%. Regarding the restoration, the materials Z350, Beautifil, VB, DCPD30% showed minimal surface loss, with no differences between them. The ionomeric cements had the highest loss values, not differing from DCPD60%. In the erosion-abrasion model, for enamel, the lowest loss was observed for Fuji II LC, with no difference to Beautifil. The other groups showed no difference among them and from Beautifil. For dentin, the groups DCPD60%, Beautifil, Fuji II LC, Z350 and Fuji IX were no significant different and presented lower loss than VB. These five groups were also no different from DCPD30%, except Fuji IX. Regarding the restoration, the highest loss was observed for Fuji IX, with no difference from Fuji II LC and Beautifil. DCPD30%, Z350, VB and DCPD60% presented minimum values of surface loss, without differences between them. It was concluded that Fuji II LC ionomeric cement was the only material able to protect the enamel adjacent to the restoration against erosive and erosive/abrasive challenges, although it was one of the materials that was most susceptible to be wear off by both challenges. For dentin, no material exhibited a significant protective effect.

O objetivo desse trabalho foi avaliar in vitro a diferença da força de cisalhamento da dentina quando submetida a ação de algumas substâncias utilizadas como clareadores dentais e posteriormente restaurados com cimento de ionômero de vidro e resina composta. Utilizou-se 152 terceiros molares superiores hígidos que tiveram suas superfícies palatinas desgastadas e preparadas para receber os materiais restauradores após o tratamento com os agentes clareadores.Os dentes foram divididos aleatoriamente em 12 grupos de acordo com as condições em teste a saber: G1: Soro+Resina, G2: Soro+Ionônero de vidro, G3: Perborato de Sódio+Soro+Resina, G4: Perborato de Sódio+Soro+Ionônero de vidro, G5: Perborato de Sódio+Peróxido de hidrogênio 6%+Resina, G6: Perborato de Sódio+Peróxido de hidrogênio 6%+ Ionônero de vidro, G7: Perborato de Sódio+ Peróxido de hidrogênio 35%+Resina, G8: Perborato de Sódio+Peróxido de hidrogênio 35%+ Ionônero de vidro, G9: Peróxido de hidrogênio 6%+Resina, G10: Peróxido de hidrogênio 6%+ Ionônero de vidro, G11: Peróxido de hidrogênio 35%+Resina, G12: Peróxido de hidrogênio 35%+ Ionônero de vidro.Ao término das restaurações os corpos de prova foram levados à máquina de ensaio universal (EMIC) e os resultados obtidos foram analisados através do teste de ANOVA a um critério e Tukey para comprovação de possíveis diferenças estatísticas .Por essas análises podemos concluir que os materiais restauradores tiveram um comportamento equivalente em todos os grupos e as diferenças significantes ocorreram mais por conta do agente clareador, sendo os grupos G1 e G2 aqueles que tiveram melhores resultados ao teste de adesividade, onde podese observar resultados significantes do grupo G1,em relação aos G5, G9, G10 e G11.O peróxido de hidrogênio a 6% ou 35% gerou os piores resultados de adesividade, melhorados com a associação ao perborato de sódio, revelando significância estatística do grupo G7 em relação aos grupos G9, G10 e G11. / The aim of this study was to evaluate \"in vitro the difference of shear bond strength of dentin when subjected to action of some substances used as dental bleaching and then restored with glass-ionomer cements and composite resin. We used 152 healthy third molars that had their palatal surfaces worn and ready to receive the restorative materials after treatment with bleaching agents. The teeth were randomly divided into 12 groups according to the conditions in testing are: G1: Serum + resin, G2: Serum + glass ionomer , G3: sodium perborate + Serum + Resin, G4: sodium perborate + Serum + glass ionomer , G5: sodium perborate + Hydrogen Peroxide 6% + Resin, G6: perborate of Sodium Hydrogen peroxide 6 +% + glass ionomer , G7: sodium perborate + 35% hydrogen peroxide + Resin, G8: sodium perborate + 35% hydrogen peroxide + glass ionomer, G9: Hydrogen peroxide 6% + Resin , G10: Hydrogen peroxide 6% + glass ionomer , G11: Hydrogen peroxide 35% + Resin, G12: Hydrogen peroxide 35% + glass ionomer .Finely finish the restorations of the bodies of evidence were brought to universal testing machine (EMIC) and results obtained and the results were analyzed using the Anova test and a Tukey test for evidence of possible statistical differences. For this analysis we can conclude that the restorative materials had an equivalent behavior in all groups, significant differences occurred due to the bleaching agent, and the G1 and G2 who fared better adhesion to the test, we can observe results significant in the G1, for the G5, G9, G10 and G11.The hydrogen peroxide 6% or 35% yielded the worst results of adhesiveness, enhanced with the combination of sodium perborate, showing statistical significance in the G7 the groups G9, G10 and G11.

O objetivo principal foi investigar se o osso cortical apresenta comportamento bimodular, ou seja, se os valores de módulo de elasticidade (E) dependem do tipo de carregamento que o método utiliza. Para alcançá-lo foi preciso: (1) \"calibrar\" os diferentes métodos em um material conhecidamente unimodular, para afastar a possibilidade de erros ligados à execução de um método. (2) Depurar os métodos já calibrados para torná-los exequíveis em osso cortical. O que foi feito em espécimes de resina composta, que é um material unimodular e com E parecido com o do osso cortical. Foi investigado se o método de medida interfere no valor do E obtido neste material (pois, pelas informações da literatura, existia uma dúvida consistente). Finalmente, (3) foi avaliado se o método de medida, a região anatômica e o indivíduo interferem nos valores de E em espécimes de osso cortical. Adicionalmente, (4) verificou-se a possibilidade de se encontrar e validar uma correlação entre E e dureza Knoop (KH), para medir o E de resinas compostas indiretamente. Espécimes de latão (n = 5) tiveram o seu E calculado por quatro métodos estáticos diferentes (flexão em três pontos; tração; compressão e método de Marshall), que foram calibrados até que todos medissem o valor esperado; os valores de cada método foram comparados por análise de variância de medidas repetidas (o método foi o fator vinculado e o nível de significância foi de 5%). Espécimes (n = 4) de cinco marcas diferentes de resina composta, também foram submetidos aos quatro métodos, fazendo as adaptações pertinentes (depuração), e tiveram o seu E calculado. Estes valores foram submetidos à análise de variância de medidas repetidas (o método foi o fator vinculado e o nível de significância foi de 5 %). Espécimes (n = 48) obtidos em diferentes regiões (periósteo, endósteo e \"transversal\") de fêmures de quatro bois diferentes tiveram seu E calculado através dos métodos devidamente depurados (flexão em três pontos, tração indireta e compressão). Os valores de E foram submetidos a análises de variâncias (nível de significância de 5 %) para avaliar a influência do método, da região e do indivíduo (bois diferentes) sobre os valores de E. O método experimental de tração não foi utilizado para analisar o comportamento bimodular, porque durantes os ensaios com osso cortical, ele apresentou valores com viés. Por isso, os valores de tração foram calculados de forma indireta (Eti) através de uma equação e dos valores experimentais de flexão em três pontos (Eb) e compressão (Ec). Para validar o uso de valores de Eti, eles foram comparados com os respectivos valores de tração experimental (Et) calculados previamente nos espécimes de resinas compostas por análise de variância de medidas repetidas, e não foram achadas diferenças significantes (p > 0,05). Para encontrar e validar a correlação entre E e KH, os valores médios de E em cada espécime de resina (média do E obtido nos 4 métodos em cada espécime) foram submetidos ao teste de correlação de Pearson (nível de significância de 5%) com os respectivos valores experimentais de dureza Knoop (KH) e foi obtida uma equação de regressão linear. Para validar a equação foi confeccionado um segundo grupo de espécimes de resina (de marcas diferentes das utilizadas anteriormente) que teve seu E calculado pelo ensaio de flexão (Eb) e pela equação de regressão proposta previamente (Er); verificou-se então se a correlação entre estes valores (Eb x Er) era significante (nível de significância de 5 %), e se a nova reta de regressão apresentava coeficiente angular não diferente de 1, e coeficiente constante não diferente de zero (critérios de validação). A análise de variância não apontou diferença significante (p > 0,05) entre os valores de E calculados para o metal pelos 4 métodos, e os valores obtidos não diferiram do E conhecido do latão (ao redor de 100 GPa). As depurações necessárias foram realizadas e com elas os diferentes métodos calcularam o E dos espécimes de resina composta de modo consistente: a análise de variância encontrou diferenças significantes (p < 0,05) entre marcas (cujos E médios cobriram a faixa entre 3 e 20 GPa) e não significantes entre os 4 métodos (p > 0,05). Nos espécimes de osso cortical o valor de E foi significantemente dependente (p < 0,05) do método de obtenção (Eti > Eb > Ec). O E dos espécimes obtidos na região \"transversal\" foi menor que o E dos espécimes obtidos na região do endósteo (p < 0,05); no entanto, não houve diferença significante (p > 0,05) entre o E dos espécimes obtidos nas regiões do endósteo e periósteo e entre o E dos espécimes obtidos nas regiões do periósteo e \"transversal\". Ao considerar somente os valores obtidos no ensaio de compressão (Ec), um dos indivíduos apresentou valores de E maiores que os demais (p < 0,05). As médias de E (dos quatro métodos) em cada espécime de resina apresentaram correlação significante com os respectivos valores de KH (p < 0,05) e a equação de regressão linear: E = 0,1602 KH. Também foi significante (p < 0,05) a correlação dos valores de Eb com os respectivos valores de Er (calculados pela regressão E = 0,1602 KH); além disso, a reta de regressão linear desta nova correlação (Eb = 1,0088Er + 0,0475) apresentou coeficiente angular não diferente de 1 e coeficiente constante não diferente de zero. Pode-se concluir que: (1) Quatro métodos de medir o E apresentaram resultados semelhantes em um material metálico. (2) Estes mesmos métodos foram depurados com sucesso para sua utilização em espécimes de osso cortical ao constatar que também não interferiram no valor do E obtido em espécimes semelhantes aos de osso, confeccionados com resinas compostas. (3) Os valores de E de osso cortical dependem do método de medida, o que demonstra seu comportamento bimodular. A região anatômica e o indivíduo também afetam os valores de E dos espécimes de osso cortical (o indivíduo só foi um fator significante ao considerar somente os valores obtidos no ensaio de compressão). (4) Foi encontrada e validada uma correlação entre E e KH em resinas compostas, que permite calcular o E deste material através da regressão E = 0,1602 KH. / The main objective was to investigate whether the cortical bone has a bimodular behavior, that is, if the values of elastic modulus (E) depend on the load type used by the method. To achieve this, it was necessary: (1) \"calibrate\" the different methods in a material with well-known unimodular behavior, for excluding the possibility of systematic errors in the execution of the methods. (2) Depurate the calibrated methods to make them executable in cortical bone. This was made on specimens of composite resin, which is a unimodular material and has an E similar to that of cortical bone. It was also investigated if the method of measuring the E influences the obtained value in this material (because there was a consistent doubt in the literature). Finally (3), we assessed whether the E values in cortical bone are influenced by the measurement method, by the anatomical region and by the individual. Additionally, (4) it was verified if it would be possible suggesting and validating a correlation between E and Knoop hardness (KH), to indirectly measure the E of composite resins. Brass specimens (n = 5) had their E calculated by four different static methods (three point bending, tensile, compression and Marshall\'s method), which were calibrated until all the methods were capable of measuring the expected value; the E values of each method were compared by analysis of variance of repeated measures (the method was the linked factor and the significance level was 5%). Specimens (n = 4) of five different composite resins were also subjected to the four methods, making the relevant adjustments (depuration), and had their E calculated. These values were subjected to analysis of variance of repeated measures (the method was the linked factor and the significance level was 5%); Specimens (n = 48) obtained in different regions (periosteum, endosteum and \"transverse\") of bovine femurs from four different individual had their E calculated using the depurated methods (three point bending, indirect tensile and compression). The E values were subjected to analyzes of variance (significance level of 5%) to evaluate the influence of the method, of the region and of the individual (different cattle) in the E values. The experimental tensile method was not used to analyze the bimodular behavior because during tests on cortical bone, this method showed values with bias. Therefore, the tensile values were indirectly calculated (Eti) by a formula and by the experimental values of E calculated by three point bending (Eb) and compression (Ec). To validate the use of Eti values, they were compared with the corresponding tensile experimental values (Et) previously measured in the composite resins specimens by analysis of variance (repeated measures), and no significant difference was found (p > 0.05). For suggesting and validating the correlation between E and KH, the average values of E of each composite specimen (mean of E obtained considering the values of the four methods in each specimen) were submitted to the Pearson\'s correlation test (significance level of 5 %) with the corresponding experimental KH values and it was obtained the linear regression equation. To validate this equation, it was made a second group of composite resins specimens (with different brands of the previously used) in which the E was calculated by three point bending test (Eb) and by regression equation previously proposed (Er); then it was checked whether the correlation between these values (Eb x Er) was significant (significance level of 5 %), and if the new regression line showed angular coefficient no different from one, and constant coefficient no different from zero (validation criteria). The analysis of variance showed no significant difference (p > 0.05) among the E values calculated for the metal specimens by the four methods; the obtained values did not differ from the known E of the brass (about 100 GPa). The necessary adjustments (depuration) were made and then the different methods calculated the E of the composite resin specimens consistently: the analysis of variance found significant difference (p < 0.05) between composite brands (whose E mean covered the range between 3 and 20 GPa) and no significant difference among the four methods (p> 0.05). In the specimens of cortical bone, the E values were significantly dependent (p < 0.05) of the obtainment method (Eti > Eb> Ec). The E values of the \"transversal\" specimens were lower than the endosteum specimens (p < 0.05); but there was no significant difference (p > 0.05) between the E of endosteum specimens and periosteum specimens and between the E of periosteum specimens and \"transversal\" specimens. When considering just E values of the compression method, one cattle showed higher E values than the others (p < 0.05). The mean of the four methods for each specimen composite resin exhibited a significant correlation with the respective KH values (p < 0.05) and the linear regression equation: E = 0.1602 KH. It was also significant (p < 0.05) the correlation between Eb and the respective Er values (calculated by the regression E = 0.1602 KH); furthermore, the linear regression of this new correlation (Eb = 1.0088Er + 0.0475) presented angular coefficient no different from 1, and constant coefficient no different from zero. It can be concluded that: (1) Four methods of E measuring showed similar results in a metallic material. (2) The same methods were successfully depurated for their execution in cortical bone specimens, since the measurement method did not affect the obtained E value in resin composites (that is a material with E value similar to cortical bone); (3) The E values of cortical bone depend on the measurement method, which demonstrates its bimodular behavior. The anatomical region and the individual also affect the E values of the cortical bone specimens (the individual was a significant factor only when considering just the E values obtained in the compression test). A correlation between E and KH that allows the E estimation by the regression E = 0.1602 KH was suggested and validated in composite resins.

O objetivo deste estudo foi avaliar, in vitro, o comportamento citotóxico e a produção de citocinas induzidos pelos materiais restauradores resinosos contendo novos monômeros KaloreTM (GC FUJI) e FiltekTMSilorane (3M ESPE) em comparação com as resinas compostas convencionais Charisma® (Heraeus-Kulzer) e FiltekTM Z250 (3M ESPE), em cultura de fibroblastos L929 e macrófagos RAW 264.7 de camundongos. As células foram estimuladas com as resinas compostas, fotopolimerizadas ou não, a partir da colocação em contato indireto ou pela extração de seus componentes durante 15, 45 e 120 dias. Após a incubação por 6, 12 e 24 horas, a viabilidade celular foi avaliada pelo Ensaio MTT e a produção de citocinas foi investigada pelo ensaio imunoenzimático (ELISA). Os dados obtidos foram analisados utilizando-se análise de variância de uma via (One-way ANOVA) e pós-teste de Tukey (&alpha;=0,05). A produção de TNF-&alpha; e IL-6 não foi detectada em fibroblastos da linhagem L929, após 6, 12 e 24 horas de contato indireto com as resinas compostas KaloreTM e FiltekTM Silorane. Por outro lado, a produção de TNF-&alpha; foi detectada em macrófagos da linhagem RAW 264.7, mas não foi influenciada pelo contato indireto com as resinas compostas, com exceção da resina FiltekTM Silorane que inibiu a produção de TNF-&alpha;, após 12 horas de incubação. Os extratos obtidos das resinas compostas KaloreTM e FiltekTM Silorane incubadas por 15 dias, se mostraram mais citotóxicos do que os extratos incubados por 45 e 120 dias. A citotoxicidade da resina composta KaloreTMnão foi influenciada pela fotopolimerização enquanto a citotoxicidade da resina FiltekTM Silorane foi maior no grupo não fotopolimerizado. Os extratos das resinas compostas Charisma® e FiltekTM Z250, obtidos aos 15, 45 e 120 dias de incubação, não foram citotóxicos 24 horas após a estimulação das células. Ainda, a resina FiltekTM Silorane, fotopolimerizada ou não, estimulou a produção de IL-6 no período de 45 dias de extração. A resina KaloreTM, diferentemente da resina FiltekTM Silorane, estimulou a produção de IL-10, aos 15 dias de extração. Entretanto, no período de 45 de extração, a resina KaloreTM fotopolimerizada inibiu a produção de IL-10, após 12 horas de incubação, e aos 120 dias de extração não houve produção detectável de IL-10 em nenhum dos grupos avaliados. / The aim of this study was to evaluate in vitro the cytotoxicity and the production of cytokines induced by resin-based restorative materials containing new monomers KaloreTM (GC FUJI) and FiltekTM Silorane (3M ESPE) compared with conventional composite resins Charisma® (Heraeus-Kulzer) and FiltekTM Z250 (3M ESPE), in mice L929 fibroblast and RAW 264.7 macrophages culture. Cells were stimulated with the composite resins, light-cured or not, by indirect contact or extraction during 15, 45, and 120 days. After incubation for 6, 12, and 24 hours, cell viability was assessed by MTT assay and production of cytokines was investigated by enzyme-linked immunosorbent assay (ELISA). Data obtained were analyzed using oneway analysis of variance (ANOVA) and Tukey post-test ( &alpha; = 0.05). Production of TNF-&alpha; and IL-6 was not detected in L929 fibroblasts either 6, 12 or 24 hours following indirect contact with the KaloreTM and FiltekTM Silorane composite resins. On the other hand, the production of TNF-&alpha; was detected in RAW 264.7 macrophages, but was not influenced by indirect contact with composite resins, with the exception of the FiltekTM Silorane resin that inhibited the production of TNF-&alpha;, after 12 hours of incubation. The extracts obtained from incubation for 15 days with composite resins KaloreTM and FiltekTM Silorane were more cytotoxic than extracts incubated for 45 and 120 days. Cytotoxicity of composite KaloreTM was not influenced by light curing while cytotoxicity of FiltekTM Silorane resin was higher in the group that not received light-cure. Extracts of Charisma® and FiltekTM Z250 composite resins, obtained at 15, 45, and 120 days of incubation, were not cytotoxic 24 hours after stimulation of the cells. Also, FiltekTM Silorane, light-cured or not, stimulated the production of IL-6 following 45 days of incubation. KaloreTM resin extract for 15 days, unlike FiltekTM Silorane resin, stimulated the production of IL-10. However, during periods of 45 days of extraction, KaloreTM resin, light-cured, inhibited the production of IL-10, after 12 hours of incubation, and 120 days of extraction there was no detectable production of IL-10 in any of the groups.

O objetivo do estudo foi avaliar ex vivo a influência da aplicação do laser de Er:YAG na parede dentinária de raízes fragilizadas, reforçadas com resina composta. Cinquenta caninos superiores tiveram suas coroas removidas próximo da junção amelo-cementária e incluídas em bloco de resina acrílica. Após tratamento endodôntico foi realizada a fragilização das raízes. Os espécimes foram distribuídos aleatoriamente em 5 grupos (n=10),: Grupo I - não irradiado, tratado com ácido fosfórico 37%; Grupo II - irradiado com laser Er:YAG, 300mJ - 10 Hz; Grupo III - irradiado com laser Er:YAG, 300mJ - 10 Hz e tratado com ácido fosfórico 37% ;Grupo IV - irradiado com laser Er:YAG, 500mJ - 10 Hz; Grupo V - irradiado com laser Er:YAG, 500mJ - 10 Hz e tratado com ácido fosfórico 37%. Todos os espécimes receberem reforço intra-radicular com resina composta, foto-polimerizada por meio de pino foto-transmissor. No espaço promovido por este pino foi cimentado o pino metálico pré-fabricado, com cimento resinoso auto-adesivo de dupla polimerização. Os espécimes foram submetidos ao teste de Tração na Máquina Universal de Ensaios - INSTRON 4444. Os maiores valores para o deslocamento foram atribuídos ao Grupo I, estatisticamente semelhante ao Grupo III. Entretanto o Grupo III ocupa uma posição intermediária, podendo pertencer também aos GruposIV e V que foram estatisticamente semelhantes entre si e ao grupo II. / The aim of this study was to assess ex vivo the effects of Er:YAG laser as dentin treatment of weakened root canal reinforced with composite resin. Fifty upper canines were decoronated at cementoenamel junction and the roots were embedded in acrylic resin. After the endodontic treatment the roots were weakened and the specimens were randomly assigned to five groups (n=10): Group I - unirradiated, treated with phosphoric acid 37%; Group II - Er:YAG laser 300mJ - 10Hz; Group III - Er:YAG laser 300mJ - 10 Hz, treated with phosphoric acid 37%; Group IV - Er:YAG laser 500mJ - 10 Hz; Group V - Er:YAG laser 500mJ - 10 Hz, treated with phosphoric acid 37%. The intraradicular reinforcement was made in all specimens with composite resin using photo-transmitter post, which creates a space for the insertion of prefabricated metal post. The metal posts were inserted using a resin cement self-adhesive dual-cured. The tensile bond strength of specimens was tested in a universal testing machine - INSTRON 4444. The results showed that Group I was statistically similar to the Group III and presented the highest bond strength values. Group III also showed statistical similarity with Group IV and V, which were similar among them and the Group II.