Submitted by Rodrigo Diniz do Prado null (rodrigodiniz.prado@hotmail.com) on 2017-02-09T13:48:10Z No. of bitstreams: 1 Dissert.Mestrado.Rodrigo.Diniz.pdf: 2142391 bytes, checksum: 98314a8816d0ae481af3108941d7a2c2 (MD5) / Approved for entry into archive by LUIZA DE MENEZES ROMANETTO (luizamenezes@reitoria.unesp.br) on 2017-02-14T15:59:08Z (GMT) No. of bitstreams: 1 prado_rd_me_sjc.pdf: 2142391 bytes, checksum: 98314a8816d0ae481af3108941d7a2c2 (MD5) / Made available in DSpace on 2017-02-14T15:59:08Z (GMT). No. of bitstreams: 1 prado_rd_me_sjc.pdf: 2142391 bytes, checksum: 98314a8816d0ae481af3108941d7a2c2 (MD5) Previous issue date: 2016-12-09 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi avaliar o efeito do desgaste com broca diamantada, o envelhecimento (degradação em baixa temperatura) e espessura do material cerâmico no comportamento mecânico de uma cerâmica Y-TZP. Para este estudo, 240 espécimes foram fabricados em formato de disco, de acordo com a norma ISO 6872: 2008 para resistência à flexão biaxial de amostras de cerâmica (N = 120, com dimensões de 0,5 mm de espessura x 15 mm de diâmetro; N = 120 com a dimensão 1,0 milímetros de espessura x diâmetro 15 mm). Os espécimes foram divididos aleatoriamente em 8 grupos (n = 30), de acordo com três fatores em estudo: 'desgaste' em 2 níveis (com e sem desgaste com broca diamantada), o envelhecimento em 2 níveis (com e sem envelhecimento) e da espessura da cerâmica também em 2 níveis (0,5 a 1,0 mm). O desgaste foi realizado com uma broca diamantada montada em um motor de baixa rotação associado a um contra-ângulo multiplicador de velocidade (T2 REVOR R170, Sirona, Bensheim, Alemanha), sob constante irrigação de água. O envelhecimento foi simulado em uma autoclave à temperatura de 134 °C, durante um período de 20 horas, sob pressão de 2 bar. Após o desgaste e envelhecimento, análises de rugosidade e topográficas foram realizadas e análises de transformação de fase por difração de raios-X. Os dados coletados foram submetidos à análise de Weibull. O desgaste promoveu um aumento da rugosidade, enquanto que o envelhecimento em autoclave não afetou estatisticamente a rugosidade da superfície. Além disso, tanto o desgaste quanto o envelhecimento aumentaram a quantidade fase monoclínica, embora, o desgaste levou a uma diminuição da susceptibilidade do material a uma nova transformação de fase durante o envelhecimento (resultando em maior percentual de fase m para a condição controle após envelhecimento em comparação a condição desgaste após envelhecimento). Independente da espessura de zircônia, o envelhecimento em autoclave e o desgaste levaram a um aumento da resistência característica. Dentro dos limites do presente estudo, observou-se que o desgaste e o envelhecimento não promovem efeitos deletério no comportamento mecânico da cerâmica Y-TZP, para ambas espessuras (0,5 mm e 1,0 mm). / The goals of this investigation were to evaluate the effects of grinding with diamond bur and aging (low temperature degradation) on the mechanical behavior of a full-contour Y-TZP ceramic with two thicknesses. Y-TZP shaped-disc specimens (Zirlux FC, Ardent Dental) were manufactured with thickness of 0.5 mm and 1.0 mm (both with 15 mm in diameter). The specimens from every thickness were randomly assigned into 4 groups, according to two factors: ‘grinding’ on 2 levels (with and without grinding with diamond bur), aging in 2 levels (with and without aging). Grinding was performed with a diamond bur mounted in a slow speed rotation motor associated with a counter-angle speed multiplier hand-piece, under constant water-cooling. Low temperature aging was performed in an autoclave at 134°C temperature, for a period of 20h, under 2 bar of pressure. After grinding and aging, roughness analyzes were performed on a surface roughness tester and 3D digital optical profilometer; topographic analysis were made in a scanning electron microscope; phase transformation analysis by X-ray diffraction. Biaxial flexural strength tests were performed in the universal testing machine. Specific statistical analyses were carried out (Weibull analysis for the strength data). Grinding promoted an increase in roughness, while aging in autoclave did not affect statistically the surface roughness. Also, grinding and aging lead to higher values of m-phase content, although, grinding lead to a decrease in the material susceptibility to a new phase transformations during aging (after aging, as-sintered condition resulted in higher m-phase content compared with ground). Independent on the zirconia’s thickness, aging in autoclave and grinding led to an increase in characteristic strengths. Within the limits of this study, it was observed that: grinding and low temperature aging in autoclave do not damage the mechanical behavior of the tested Y-TZP ceramic, for both thicknesses (0.5 mm and 1 mm). Despite those conditions led to high m-phase content, a thinner thickness of 0.5 mm presented similar or higher characteristic strength compared with the 1.0 mm thickness both before and after grinding and aging.

Submitted by Sandro Basso Bitencourt null (sandrodonto@gmail.com) on 2017-03-23T13:07:44Z No. of bitstreams: 1 Dissertação final - revisado pela biblioteca.pdf: 1890741 bytes, checksum: 67162843354d597f4f93a297398b42fc (MD5) / Approved for entry into archive by Luiz Galeffi (luizgaleffi@gmail.com) on 2017-03-23T16:14:48Z (GMT) No. of bitstreams: 1 bitencourt_sb_me_araca.pdf: 1890741 bytes, checksum: 67162843354d597f4f93a297398b42fc (MD5) / Made available in DSpace on 2017-03-23T16:14:48Z (GMT). No. of bitstreams: 1 bitencourt_sb_me_araca.pdf: 1890741 bytes, checksum: 67162843354d597f4f93a297398b42fc (MD5) Previous issue date: 2017-02-24 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / A obtenção de uma união duradoura da interface zircônia/cerâmica de cobertura é uma preocupação para sucesso clínico de restaurações livres de metal e ainda não existem evidências que indiquem uma técnica de tratamento dessa zircônia com melhor previsibilidade e durabilidade. Assim, o objetivo desse estudo foi desenvolver e caracterizar fisico-quimicamente um novo filme por vapor químico melhorado por plasma (plasma enhanced chemical vapor deposition – PECVD) na superfície da zircônia tetragonal policristalina estabilizada por óxido de ítrio (Y-TZP) para melhorar sua resistência de união com cerâmica de cobertura. Para isso, um total de 192 amostras de Y-TZP (13×5,4×5 mm) foram divididas em 6 grupos, de acordo com o tratamento de superfície: controle – sem tratamento (C), jateamento com partículas de óxido de alumínio de 27 µm (Al27), jateamento com partículas de óxido de alumínio de 110 µm (Al110), jateamento com partículas de óxido de alumínio de 250 µm (Al250), aplicação de liner para zircônia (L) e o filme por PECVD (P). A superfície da Y-TZP foi caracterizada por meio da microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EED), microscopia de força atômica (MFA), perfilometria e energia livre de superfície. A resistência de união entre a Y-TZP e uma cerâmica de cobertura foi testada antes e após fadiga térmica (20.000 ciclos de 5 e 55 °C). Os dados foram submetidos à análise de variância e teste Tukey HSD (α=0,05). Como resultados, foi encontrado que o grupo P não alterou a rugosidade de superfície da Y-TZP (P>0,05 vs controle), enquanto os grupos Al110, Al250 e L apresentaram os maiores valores (P<0,05). Todos os tratamentos melhoraram a energia livre de superfície da Y-TZP, exceto o Al27. O grupo P mostrou os maiores valores de resistência ao cisalhamento (P<0,05), sendo semelhante apenas ao grupo Al27 (P=0,107). Os demais grupos foram similares ao controle (P>0,05). A fadiga térmica não afetou a interface Y-TZP/cerâmica de cobertura. Filmes produzidos pela deposição por plasma não promovem alterações estruturais na Y-TZP e são promissores para melhorar a interface de união Y-TZP/cerâmica de cobertura. / The obtainment of a durable zirconia/veneer ceramic interface bond is a preoccupation for clinical success of metal-free restorations and did not exist evidence indicates that the technique with the best predictability and durability. Thus, the aim of this study was to develop and to physico-chemically characterize a novel film formed after plasma enhanced chemical vapor deposition (PECVD) on the yttria stabilized tetragonal zirconia (Y-TZP) surface aiming to improve its bond strength to the veneer ceramic. For this, a total of 192 YTZP samples (13×5.4×5 mm) were divided in 6 groups, according the surface treatment: control – no treatment (C), airborne-particle with 27 µm aluminum oxide (Al27), airborneparticle with 110 µm aluminum oxide (Al110), airborne-particle with 250 µm aluminum oxide (Al250), zirconia liner (L) and the film by PECVD (P). The Y-TZP surface was characterized through scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), atomic force microscopy (AFM), surface roughness and surface free energy. The bond strength between Y-TZP and veneer ceramic was tested before and after thermal fatigue (20,000 cycles of 5 and 55ºC). The data were submitted to analysis of variance and Tukey HSD test (α=0.05). The results were that the roughness of Y-TZP surface was not modified in the P group (P>0.05 vs control), while the Al110, Al250 and L groups showed higher roughness values (P<0.05). All the treatments improved the surface free energy of Y-TZP, except for the Al27 group. The P group showed higher shear bond strength (P<0.05), similar only to the Al27 group (P=0.107). The other groups were similar to control (P>0.05). The thermal fatigue did not affect the Y-TZP/veneer ceramic interface. Films produced by the PECVD deposition did not promote structural changes on the Y-TZP and are promising to improve the bond interface Y-TZP/veneer ceramic. / FAPESP: 2015/10826-9 / FAPESP: 2015/11412-3

Orientador: José Maurício dos Santos Nunes Reis / Banca: Ligia Antunes Pereira Pinelli / Banca: Paulo Francisco Cesar / Resumo: O objetivo desteestudofoi avaliar o efeito do desgaste, seguido ou não por ressinterização, sobre o limite de fadiga flexural da cerâmica LavaTM Y-TZP (3M ESPE). Cento e vinte espécimes em forma de barra foram obtidos: 20×4,0×1,2mm (n=40) e 20×4,0×1,5mm (n=80). Metade dos mais finos constituiu o grupo controle (C), enquanto que os mais grossos foram desgastados com ponta diamantada (4ZR, Komet-Brasseler) sob refrigeração constante (DI) ou não (D). A outra metade das amostras mais finas, e das desgastadas foram ressinterizadas (1000ºC, 30 min), resultando nos grupos CR, DIR e DR. As amostras foram avaliadas pelo método de escada, de Dixon e Mood, com o nível de estresse inicial a 60 % da resistência à flexão monotônica. Os espécimes foram montados em dispositivo de quatro pontos de flexão em saliva artificial a 37±1ºC, e submetidos a 500.000 ciclos a 10 Hz. MEV (500X) a partir do lado de tração de amostras não fraturadas (n=3), e do controle não fadigado (n=3) foi utilizada para avaliar a topografia da superfície. Além disso, MEV (30X e 100X) foi realizada em amostras fraturadas de cada grupo experimental (n=3) para determinar a origem das falhas. Dados de testes de fadiga foram analisados estatisticamente por ANOVA a dois fatores e teste de Tukey (α=0,05). Desgaste, com refrigeração ou não, aumentou o limite de fadiga dos grupos não ressinterizados. Não houve diferença significativa entre os grupos ressinterizados. Ressinterização aumentou significativamente o limite de fadiga do grupo C. Ciclagem e ressinterização não alteraram a topografia da superfície da zircônia. Desgaste criou sulcos aparentes na superfície. Independentemente dos grupos experimentais, as falhas iniciaram no lado de tração. O desgaste aumentou o limite de fadiga por flexão da Y-TZP, enquanto a ressinterização não forneceu aumento significativo do limite de fadiga das amostras desgastadas / Abstract: The purpose of this study was evaluate the effect of grinding protocols, followed or not by resintering, on the flexural fatigue limit of the LavaTM Y-TZP (3M ESPE) ceramic. One hundred and twenty bar-shaped specimens were obtained: 20×4.0×1.2mm (n=40) and 20×4.0×1.5mm (n=80). Half of the thinner specimens constituted the as-sintered (control) group (AS), while the thicker ones were ground with diamond burs (4ZR, Komet-Brasseler) under constant irrigation (WG) or not (G). The other half of the thinner specimens, and half of the ground ones were resintered (1000ºC for 30 min), resulting in the ASR, WGR and GR groups. The samples were evaluated by the staircase method, proposed by Dixon and Mood, with the initial stress level set at 60 % of the monotonic flexural strength. Specimens were mounted in a four-point flexural fixture in artificial saliva bath at 37±1ºC, and subjected to 500,000 cycles at 10 Hz. SEM (×500) images from the tensile side of non-fractured specimens (n=3), and of non-fatigued as-sintered ones (n=3) were used to evaluate the surface topography. In addition, SEM analyses (×30 and ×100) were performed in fractured specimens of each experimental group (n=3) to determine the origin of the failures. Data from fatigue testing were statistically analyzed by 2-way ANOVA and Tukey tests (α=.05). Grinding, performed with irrigation or not, increased the fatigue limit of the non-resintered groups. There was no significant difference among the resintered groups. Resintering significantly increased the fatigue limit of AS group. Cyclic loading and resintering did not change the surface topography of zirconia. Grinding created apparent grooves on the zirconia surface. Regardless of the experimental groups, failures initiated at the tensile side of the specimens. Grinding increased the flexural fatigue limit of LavaTM Y-TZP, while resintering did not provide a significant increase in the fatigue limit of the ground specimens. / Mestre

Cerâmicas à base de zircônia tetragonal estabilizada com ítria (ZrO2(3%Y2O3)) possuem excelentes propriedades mecânicas, devido a uma peculiar transformação de fases que ocorre nos grãos desta cerâmica durante o crescimento de uma trinca. O crescimento da trinca gera tensões compressivas sobre os grãos tetragonais metaestáveis, os quais se transformam em monoclínicos, promovendo uma expansão volumétrica de 3 a 5%, a qual impede que a trinca continue crescendo nas condições de carregamento mecânicos inicialmente utilizados, o que produz aumento da resistência à fratura, e tenacidade deste material. Neste trabalho são apresentados os resultados do estudo da recuperação da fase tetragonal pela utilização de tratamentos térmicos, em zircônia envelhecida por desgaste, durante a preparação de próteses dentárias. Blocos cerâmicos pré-sinterizados à base de ZrO2(3%Y2O3) foram sinterizados em três condições distintas, quais sejam, 1450°C - 0h, 1530°C - 2h e 1600°C - 4h. Cada lote de amostras sinterizado foi submetido análise de densidade relativa, difração de raios X (DRX) e microscopia eletrônica de varredura (MEV). Parte das cerâmicas sinterizada foi fraturada, e a superfície de fratura foi re-examinada por DRX e MEV. Outra parte foi fragmentada visando a transformação martensítica, que gera a fase monoclínica no material, e em seguida caracterizada por DRX. Os resultados da densificação e análise microestrutural indicaram densidade relativa de 94,2%, 99,6% e 99,75%, tamanho médio de grão de 0,28?m, 0,49m e 1,31m, para amostras sinterizadas a 1450°C - 0h, 1530°C - 2h e 1600°C - 4h respectivamente. Após fragmentação, os teores de fase monoclínica medidos foram da ordem de 58%, 43% e 4,5% que correspondem a aproximadamente 65% vol, 50% vol e 6% vol. Tratamentos térmicos realizados a 950°C, 1100°C e 1200°C foram necessárias para recuperação de 100% de fase tetragonal, em amostras sinterizadas a 1450°C - 0h, 1530°C - 2h e 1600°C - 4h, respectivamente. / Tetragonal zirconia-based ceramic stabilized with (ZrO2(3%Y2O3)) have excellent mechanical properties due to a peculiar phase transformation that occurs in this ceramic grains during the growth of a crack. The crack growth generates compressive stresses on the metastable tetragonal grains, which are transformed into monoclinic, promoting a volumetric expansion of 3 to 5% which prevents the crack continues to grow under conditions of mechanical loading initially used, which produces the increased fracture strength and toughness of this material. This paper presents results of the recovery of the tetragonal phase by the use of thermal treatments in zirconia aged for wear during the preparation of dental prostheses. ZrO2(3%Y2O3) pre-sintered ceramic blocks were sintered in three different conditions: 1450°C-0h, 1530°C-2h and 1600°C-4h. Sintered samples were characterized by relative density, X-Ray diffraction (XRD) and Scanning Electron Microscopy (SEM). Part of the sintered samples was fractured and the fracture surface was re-examined by XRD and SEM. Another part was milled aiming generates a martensitic transformation (monoclinic phase), and characterized by XRD. The results of densification and SEM analysis indicates relative density of 94.2%, 99.6% and 99.75%, average grain size of 0.28?m, 0.48m and 1.31m, for samples sintered at 1450°C-0h, 1530°C-2h and 1600°C-4h respectively. After milling, the monoclinic phase content was 58%, 43% e 4,5% corresponding to 65% vol, 50% vol e 6% vol. For samples sintered at 1450°C-0h, 1530°C-2h e 1600°C-4h, heat treatments of 950°C, 1100°C and 1200°C were performed respectively, for recuperation of 100% of tetragonal phase.

A arqueometria é uma área consolidada, com ampla utilização de métodos analíticos nucleares destrutivos e não destrutivos para caracterização, proteção e restauração de peças arqueológicas. O presente projeto teve como objetivo estudar a composição química elementar de amostras de fragmentos cerâmicos encontradas no sítio arqueológico São Paulo II localizado na calha do rio Solimões, próximo ao município de Coari na Amazônia Brasileira. Realizou-se a caracterização das amostras pela determinação de Ce, Co, Cr, Cs, Eu, Fe, Hf, K, La, Lu, Na, Nd, Sb, Sm, Rb, Sc, Ta, Tb, Th, U, Yb and Zn por meio da análise por ativação com nêutrons (NAA). A partir da composição química da cerâmica, foi possível definir o agrupamento de amostras em função da similaridade/dissimilaridade da composição química presente no material cerâmico. O agrupamento foi interpretado por métodos estatísticos multivariados como análise de cluster, análise de componentes principais e análise de discriminante. Foram selecionadas, a partir da formação dos grupos, 7 cerâmicas com o objetivo de elaborar o horizonte temporal do sítio, realizado por termoluminescência (TL) e ressonância paramagnética eletrônica (EPR). A temperatura de queima da cerâmica foi determinada em 6 fragmentos por meio da técnica de EPR. Os resultados apresentados neste trabalho podem contribuir com os estudos arqueológicos sobre a dinâmica da ocupação da Amazônia Central anterior à colonização Brasileira. / Archaeometry is currently a well established field in the archaeological sciences. The nuclear method for analysis of chemical elements is one of the important instruments for the characterization of the archaeological materials and has influences on the preservation and restoration. From the chemical and physical analyses it is possible to infer technical processes in ceramics manufacture and tools used by ancient people. Therefore, it contributes to the typology and to understand the roles of materials available in the archaeological sites, such as clays and lythic sources. Evidently, all the archaeological materials and sites are related to people that lived there a long time ago, and studies, as outlined above, reconstruct at least partially the history of such a population. This project aimed at studying the elementary chemical composition of 70 ceramic fragments samples from São Paulo II archaeological site, located along the Solimões River channel, next to Coari city, in Brazilian Amazon. The characterization of samples was performed by neutron activation analysis (NAA). By the determination of 22 elements in the ceramic fragments ( Ce, Co, Cr, Cs, Eu, Fe, Hf, K, La, Lu, Na, Nd, Sb, Sm, Rb, Sc, Ta, Tb, Th, U, Yb and Zn), it was possible to define groups of samples regarding the similarity/dissimilarity in elementary chemical composition. For such a task, the multivariate statistical methods employed were cluster analysis (CA), principal component analysis (PCA) and discriminant analysis (DA). Afterwards, seven ceramic fragments have been selected to elaborate the site temporal horizon using thermoluminescence (TL) and electron paramagnetic resonance (EPR) dating results. The EPR technique was also used to find the average firing temperature to produce the ceramics. The results of this research may contribute to the study on the occupation dynamics in the pre-colonial Brazilian Amazon.

Submitted by Rosivalda Pereira (mrs.pereira@ufma.br) on 2017-06-23T18:25:33Z No. of bitstreams: 1 KarolineGuimaraes.pdf: 4831145 bytes, checksum: b9a74fa65c7ad6e524149ce87f6c4b8f (MD5) / Made available in DSpace on 2017-06-23T18:25:33Z (GMT). No. of bitstreams: 1 KarolineGuimaraes.pdf: 4831145 bytes, checksum: b9a74fa65c7ad6e524149ce87f6c4b8f (MD5) Previous issue date: 2015-04-28 / Fundação de Amparo à Pesquisa e ao Desenvolvimento Científico e Tecnológico do Maranhão (FAPEMA) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPQ) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / The disposal of solid waste is seen as an environmental problem. A solution presented by the National Plan for Solid Waste the reuse of waste in new production processes, proposal worked in this paper.The use can also be seen as a technological solution because adds functional and aesthetics characteristics of the products. The cattle bones and the fine of ornamental rocks have phtsio-chemical characteristics, which can be incorporated into other materials as in ceramic production. In this paper, hite ceramic compositions were developed with waste additions of bones and rocks which were analyzed in two steps: the first consisted of a quantitative analysis of technological properties such as water absorption, porosity, density, loss to fire, linear shrinkage and the modulus of rupture in bending; and the econd were an qualitative evaluation of the visual appearance of the material. The percentages of the best performing were used in products, for pressing and bonding the slip process, to a new visual analysis. The results show that the compositions of 30%, 35% e 55% of cattle bones and 30%, 35% e 40% of fine of ornamental rocks showed the best results. Furthermore, the material presented a great visual performance in the application of products – like coatings and utilities - by pressing and onding the slip. / O descarte de resíduos sólidos é visto como um problema ambiental. Uma solução apresentada pelo Plano Nacional de Resíduos Sólidos consiste no reaproveitamento de resíduos em novos processos produtivos, proposta trabalhada neste estudo. O reaproveitamento pode ser visto também como uma solução tecnológica, pois agrega características funcionais e estéticas aos produtos. Os ossos bovinos e o fino de rochas ornamentais possuem características fisio-químicas interessantes, passíveis de serem incorporados a outros materiais, como ocorre na produção cerâmica. Neste trabalho, foram desenvolvidas composições de cerâmica branca com adições de resíduos de ossos e de rochas, as quais foram submetidas a análises em duas etapas: a primeira consistiu em uma análise quantitativa de propriedades tecnológicas, tais como a absorção de água, a porosidade, densidade, perda ao fogo, retração linear e o ódulo de ruptura à flexão; e a segunda foi uma avaliação qualitativa do aspecto visual do material. As porcentagens com melhor desempenho foram utilizadas em produtos pelos processos de prensagem e colagem de barbotina, para nova análise visual. Os resultados mostram que as composições de 30%, 35% e 55% de ossos bovinos e de 30%, 35% e 40% de fino de rochas ornamentais apresentaram os melhores resultados. Além disso, o material apresentou ótimo desempenho visual na aplicação em produtos - como revestimentos e utilitários - por prensagem e colagem de barbotina.

Orientador: Geralda M. F. S. Dalglish (Lalada Dalglish) / Banca: Jean-Jacques Armand Vidal / Banca: Marosil Marini / Banca: Camila da Costa Lima / Banca: Sonia Carbonell Alvares / Resumo: Percebendo uma dinâmica na cerâmica indígena que é fruto de agências e seus efeitos de captura sobre os receptores desta arte, a pesquisa faz uma aproximação às relações socioambientais e cosmologias, andina e amazônica, para compreender as ontologias indígenas e as relações de alteridade com seres míticos como a serpente, que desencadeiam transformações sociais nas aldeias. A atuação do xamanismo na produção de conceitos e de pessoa está inscrita nas produções cerâmicas através de referências à serpente como nos kene Shipibo-Conibo e na iconografia cerâmica andina pré-colombiana, indicando que os saberes cerâmicos indígenas funcionam em rede cosmológica na América do Sul. / Resumen: Percibiendo una dinámica en la cerámica indígena que es fruto de agencias y sus efectos de captura sobre los receptores de esta arte, la investigación hace una aproximación a las relaciones socioambientales y cosmologías, andina y amazónica, para comprender las ontologías indígenas y las relaciones de alteridad con seres míticos como la serpiente, que desencadenan transformaciones sociales en las aldeas. La atuación del xamanismo en la producción de conceptos y de persona está inscrita en las producciones cerámicas a través de referencias a la serpiente, como los kene, el dibujo Shipibo-Conibo, y en la iconografía cerámica andina precolombina, indicando que los saberes cerámicos indígenas funcionan en red cosmológica en América del Sur. / Abstract: Noticing a dynamic in the indigenous ceramics that is the result of agencies and their capture effects on the receptors of this art, the research makes an approximation to the socio-environmental relations and cosmologies, Andean and Amazonian, to understand the indigenous ontologies and the relations of alterity with mythical beings like the serpent that trigger social transformations in the communities. The agency of the xamanism in the production of concepts and of person is inscribed in the ceramic productions through references to the serpent as the kene, drawings Shipibo-Conibo, and prehispanic Andean ceramic iconography, indicating that indigenous ceramic knowledge functions in a cosmological network in South America. / Mestre

Orientador: Margarida Juri Saeki / Banca: Thomaz Augusto Guisard Restivo / Banca: Valber de Albuquerque Pedrosa / Banca: Gustavo Rocha de Castro / Banca: Joelma Perez / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi / Resumo: O presente trabalho teve por objetivo preparar a cerâmica de BaZr0,1Ce0,7Y0,1Yb0,1O3-δ considerando a aplicação como eletrólito de Células a Combustível de Cerâmicas Protônicas (PCFCs). A cerâmica foi preparada pelo Método do EDTA-Citrato e avaliou-se a influência do pH na estrutura, após a calcinação. Avaliou-se também sua influência na densificação, condutividade elétrica e estabilidade química em atmosfera de CO2. Os resultados de caracterização físico-química do material em pó indicaram a formação da fase perovskita sob sistema monoclínico em temperaturas de 700ºC-1000ºC, mas que contem resíduos de carbonatos, independente da faixa de pH da síntese. Em temperaturas de calcinação de maiores que 1200ºC/3h, os materiais sintetizados em 5≤pH≤6 mantiveram sob estrutura cristalina perovskita do sistema monoclínico (menos simétrico), porém, os materiais sintetizados em 8≤pH≤9 organizaram-se sob estrutura cristalina perovskita no sistema ortorrômbico (mais simétrico). Para ambas as faixas de pH de síntese, resíduos de carbonatos estáveis foram encontrados até uma temperatura de 1200ºC. Os materiais obtidos em ambas as faixas de pH apresentaram alto grau de densificação (densidades relativas >97%), requerendo temperaturas de 1450oC. Os resultados de espectroscopia de impedância elétrica na faixa de 400ºC-600ºC mostraram que o material sintetizado em 8≤pH≤9 apresentou altos valores de condutividade protônica (0,601-4,17 mS/cm) em atmosfera de 20%O2/N2 e 20%H2/N2 umidificadas. Os re... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This work aimed to prepare the BaZr0,1Ce0,7Y0,1Yb0,1O3-δ ceramic for the application as electrolyte of Protonic Ceramic Fuel Cell (PCFCs). The ceramic was synthesized by EDTA-Citrate Method and the pH influence (5≤pH≤6 and 8≤pH≤9) was evaluated. After, densification, electrical conductivity and chemical stability (in CO2 10mol% atmosphere) were studied. Concerning to physicochemical characterization results of powder, it was observed the formation of perovskite phase with monoclinic system when treated at 700ºC-1000ºC and it was observed the presence of stable carbonates up to 1200ºC/3h for both pH synthesis conditions. At 1200ºC/3h, the materials synthesized at 5≤pH≤6 range maintained under perovskite monoclinic system (less symmetrical). On the other hand, the materials synthesized at 8≤pH≤9 range structured under perovskite orthorhombic system (more symmetrical). After the densification process at 1450ºC/3h the materials maintained the previous crystalline structures. The materials showed high level of the densification (relatives densities >97%) for the both pH range. The electric impedance spectroscopy analysis of the materials synthesized at 8≤pH≤9 range showed high protonic conductivity (0,601-4,17 mS/cm) at humidified atmosphere of 20%O2/N2 and 20%H2/N2, at 400ºC-600ºC range. The chemical stability results (in CO2 10mol% atmosphere) showed that the material has adequate chemical stability in temperatures of 400-500ºC and that it can be used as PCFCs electrolyte in thi... (Complete abstract click electronic access below) / Doutor

O propósito deste trabalho foi avaliar, in-vitro, a alteração de cor da cerâmica de dissilicato de lítio, após o envelhecimento artificial acelerado (EAA), variando-se os seguintes aspectos: processo de confecção (cerâmica monolítica e com infraestrutura coberta por cerâmica de revestimento), espessuras de 1,5 e 2,0mm e substratos de resina e liga metálica, com e sem cimento. Para isso foram confeccionadas 40 pastilhas de cerâmica IPS e.max Press, que foram divididas em 2 grupos (n=20): LT (cerâmica de baixa translucidez na cor A2) e HO (cerâmica de alta opacidade). Neste grupo as pastilhas foram confeccionadas com 0,5mm de espessura e, posteriormente, revestidas com a cerâmica IPS e.max Ceram na cor A2 e com espessuras de 1,0 e 1,5mm. Foram utilizados substratos em resina composta (n=20) e em liga metálica (cobre-alumínio) (n=20). Para a cimentação foi utilizado o cimento de polimerização dual Variolink II, na cor translúcida. A leitura da cor foi realizada em um espectrofotômetro (Minolta CM2600d), equipado com fonte de luz padrão D65 (luz do dia). A cor determinada no aparelho é expressa em coordenadas CIE L* a* b* e os valores correspondentes foram utilizados para calcular o E. Foram feitas as seguintes comparações: discos de cerâmica antes do EAA vs discos de cerâmica cimentadas sobre os substratos antes do EAA; discos de cerâmica cimentadas sobre os substratos antes do EAA vs discos de cerâmica cimentadas sobre os substratos após o EAA; discos de cerâmica antes do EAA vs discos de cerâmica cimentadas sobre os substratos após o EAA; discos de cerâmica antes do EAA vs discos de cerâmica após o EAA. Os dados foram submetidos a análise estatística (ANOVA) a 3 critérios e (ANOVA) a 2 critérios e testes de Tukey, p<0,05). Os resultados mostraram que: 1. os grupos somente de discos de cerâmica vs discos de cerâmica com 1,5 e 2,0mm de espessuras, cimentadas em substratos de resina e liga metálica, antes do EAA. O menor valor encontrado de E (E=3,6) foi com o grupo de discos da cerâmica HOA2 com 2mm de espessura cimentados em substrato de metal, seguido pelo grupo da mesma cerâmica com 1,5mm de espessura cimentada em substrato de resina. O maior valor encontrado (E=10,0) foi com os discos de cerâmica LTA2 com 1,5 e 2mm de espessuras e cimentados em substrato de metal; 2. os grupos com discos de cerâmicas com 1,5 e 2,0mm de espessuras e cimentados em substratos de resina e liga metálica antes do EAA vs o mesmo grupo após EAA. Os grupos de discos com a cerâmica HOA2 com 2mm de espessura cimentados em substrato de metal teve menor alteração de cor (E=1,1) e a maior alteração de cor ocorreu com o grupo da cerâmica LTA2 com 2mm de espessura cimentada em substrato de metal (E=2,1); 3. os grupos somente com discos de cerâmica antes do EAA vs grupos de cerâmicas com discos de 1,5 e 2,0mm de espessuras e cimentados em substratos de resina e liga metálica após o EAA. O menor valor encontrado (E=3,7) foi com a cerâmica HOA2 com revestimento e 2mm de espessura cimentada em substrato de metal. O maior valor encontrado (E=10,0) foi o da cerâmica LTA2 com 1,5 e 2mm de espessuras cimentadas em substrato de metal; 4. os grupos discos de cerâmica, antes e após o processo de EAA O grupo que teve menor alteração de cor foi o da cerâmica HOA2 com 1,5mm (E=0,6). O grupo que teve maior alteração de cor foi o da cerâmica LTA2 com 2mm (E=2,2). Concluiu-se que o EAA causou alteração na cor final das cerâmicas de dissilicato de lítio, levando-se em conta as variáveis pesquisadas. / The purpose of this in vitro study was to evaluate the color changing of the lithium disilicate ceramic discs after accelerated artificial aging (AAA) varying the following aspects: manufacturing process (monolithic ceramic and infrastructure with ceramic covering), thickness of the ceramic (1.5 and 2.0 mm) and abutment substrate (composite resin and alloy), with and without cement. Forty ceramic discs were fabricated with ceramic IPS e.max Press and divided into two groups (n = 20): LT (low translucency, shade A2) and HO (high opacity). In the HO group, the discs were fabricated with a thickness of 0.5 mm of the IPS e.max Ceram combined with a thickness of 1 or 1.5mm of veneering ceramic, shade A2. The abutments substrates were fabricated with composite resin (n = 20) and metallic alloy (n = 20). The resin cement used was Variolink II translucent color. Color was measured with a spectrophotometer and expressed in CIE L * a * b * coordinates. Color differences (E) were calculated. The data were analyzed with ANOVA and the Tukey HSD test (p <0.05).The results showed that 1.in the groups of ceramic discs vs. ceramic discs with 1.5 and 2.0mm thickness, cemented on resin substrates and metal alloy, before AAA, the lowest value of E (E = 3,6) was obtained for HOA2 ceramic discs with 2mm thickness cemented in metal substrate, followed by ceramic discs with 1.5mm thickness cemented in substrate of resin. The highest value (E = 10.0) was observed for ceramic discs LTA2 with 1.5 and 2mm thickness and cemented in metal substrate; 2. In the groups with ceramic discs with 1.5 and 2.0mm thickness and cemented on resin and metal substrates prior to AAA vs the same group after AAA, the HOA2 ceramic discs with 2mm thickness cemented on a metal substrate had the smallest color change (E = 1,1) and the largest occurred for LTA2 with 2mm thickness and cemented in metallic substrate (E = 2.1); 3. In the groups of ceramic discs before AAA vs groups of ceramic with discs of 1.5 and 2.0mm of thickness and cemented on resin substrates and metal alloy after AAA, the lowest value (E = 3,7) was obtained for HOA2 veneering ceramic 2mm thickness cemented on a metal substrate. The highest value found (E = 10.0) was for LTA2 ceramic with 1.5 and 2mm thickness cemented on a metal substrate; 4. comparing the groups of ceramic discs before and after the AAA process, the lowest color change was obtained for HOA2 ceramic with 1.5mm (E = 0.6) and the greatest color change was fore LTA2 ceramic with 2mm (E = 2.2). It was concluded that the AAA caused alteration in the final color of the lithium disilicate ceramics, taking into account the variables studied.

Orientador: Renata Marques de Melo Marinho / Coorientador: Tiago Moreira Bastos Campos / Banca: Altair Antoninha Del Bel Cury / Banca: Marco Antonio Bottino / Banca: Paulo Francisco César / Banca: Guilherme de Siqueira Ferreira Anzaloni Saavedra / Resumo: O objetivo do estudo foi avaliar os efeitos de diferentes infiltrações de sílica pelo método sol-gel realizado com a presença de catalisadores nas propriedades mecânicas, microestrutura, características de superfície de uma zircônia Y-TZP, e na resistência de união entre a zircônia e um cimento resinoso, bem como avaliar a energia interfacial (tenacidade à fratura) na união de zircônia infiltrada por sílica ou vidro ao cimento resinoso. O estudo foi segmentado em duas partes, na parte A foram confeccionados 210 discos de Zircônia Y-TZP e divididos em 6 grupos, infiltrados por ácido silícico obtido por TEOS, infiltrados por ácido silícico obtido por metassilicato de sódio (Na2SiO3): sem catalisador, com catalisador, com duas e três imersões, e o grupo não infiltrado (controle). Os discos foram caracterizados com DRX, FT-IR e MEV, e depois foram submetidos ao ensaio de resistência à flexão biaxial. Os dados foram analisados com a estatística descritiva, ANOVA 1-fator e Teste de Tukey (95%), e também com a Análise de Weibull para determinar a homogeneidade estrutural. Adicionalmente foram produzidos espécimes retangulares de zircônia, que foram divididos da mesma forma que os grupos citados acima, para a realização do teste de resistência de união. Os espécimes infiltrados foram tratados com ácido fluorídrico 2% por 10 segundos e depois silanizados. Uma matriz de silicone foi adaptada com cera sobre as superfícies tratadas da zircônia e o cimento resinoso foi inserido dentro da ... (Resumo completo, clicar acesso eletrônico abaixo) / Doutor