Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2013. / Made available in DSpace on 2015-03-18T20:51:44Z (GMT). No. of bitstreams: 1 328563.pdf: 1266696 bytes, checksum: f4214c6feea1ed227e92defc2319ce0d (MD5) Previous issue date: 2013 / O objetivo deste estudo foi avaliar os efeitos dos diferentes pré-tratamentos do canal radicular na resistência de união de um pino de fibra de vidro cimentado à dentina. Quarenta e oito pré-molares unirradiculares inferiores foram tratados endodonticamente e preparados para receber os pinos de fibra Whitepost # 2 (FGM/Dentscare, Joinville, Brasil). Após o preparo do espaço para o pino, os dentes foram divididos em quatro grupos (n=12). As paredes das raízes foram submetidas ao não tratamento (grupo controle-G1) ou a um dos três tratamentos de superfície: irrigação com 10 mL de hipoclorito de sódio 5%, durante 3 minutos (G2); irrigação com 10 mL de ácido etilenodiaminotetracético (EDTA) 17%, durante 3 minutos e associado com 10 mL de hipoclorito de sódio 5%, durante 3 minutos (G3) ou a irrigação com 10 mL de EDTA 17%, durante 3 minutos (G4). Os pinos de fibra foram cimentados com o cimento autoadesivo RelyX U100 (3M ESPE, Seefeld, Alemanha). O teste de resistência de união push-out foi realizado por uma máquina de testes universal a uma velocidade de 0,5 mm/min. Os dados obtidos foram registrados e expressos em Mpa, além de serem analisados estatisticamente com uma análise simples de variância (ANOVA) e com o teste de Tukey. O Grupo 3 apresentou os maiores valores de resistência de união, entretanto mostrou-se estatisticamente similar ao grupo controle. Os Grupos 2 e 4 apresentaram diminuição na resistência de união quando comparados ao grupo controle. O Grupo 4 apresentou resistência de união significativamente menor quando comparado aos demais grupos.<br> / Abstract: The aim of this study was to evaluate the effects of different pretreatment of root canal on the bond strength of a fiber post luted to dentin. Fourty-eight single-rooted mandibular premolars were endodontically treated and post spaces were prepared to receive Whitepost fiber posts #2 (FGM/Dentscare, Joinville, Brazil). After post space preparation, the teeth were assigned to four groups of 12 teeth each (n=12). The walls of the roots were subjected to either none (control - G1) or one of three surface pretreatments: irrigation with10ml of 5% sodium hypochlorite for 3 minutes (G2), irrigation with 10ml of 17% ethylenediaminetetracetic acid (EDTA) for 3 minutesassociated with 10ml of 5% sodium hypochlorite for 3 minutes (G3) or irrigation with 10ml of 17%EDTA alone for 3 minutes (G4). The fiber posts were bonded with self-adhesive cement RelyX U100 (3M - ESPE, Seefeld, Germany). A push-out bond strength test was performed by a universal testing machine at a crosshead speed of 0.5 mm/min. The bond strength data were recorded and expressed in Mpa. Data were analysed with a one-way analysis of variance (ANOVA) and Tukey test. The irrigation of 17% EDTA associated with 5% sodium hypochlorite showed increased in the bond strength, but was statistically similar when compared with control group. The groups 2 and 4 showed decrease in the bond strength when compared with control group. The group 4 showed bond strength significantly lower when compared with all groups.

Tese (doutorado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2015. / Submitted by Fernanda Percia França (fernandafranca@bce.unb.br) on 2016-02-16T11:51:40Z No. of bitstreams: 1 2015_MaitêCevallosMijanKessler.pdf: 13377430 bytes, checksum: 3606ad0c7d151d47306c37ca3223a62c (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2016-02-19T12:04:46Z (GMT) No. of bitstreams: 1 2015_MaitêCevallosMijanKessler.pdf: 13377430 bytes, checksum: 3606ad0c7d151d47306c37ca3223a62c (MD5) / Made available in DSpace on 2016-02-19T12:04:46Z (GMT). No. of bitstreams: 1 2015_MaitêCevallosMijanKessler.pdf: 13377430 bytes, checksum: 3606ad0c7d151d47306c37ca3223a62c (MD5) / De acordo com a Organização Mundial de Saúde, 72% e 95% das lesões de cárie cavitadas em dentina de dentes decíduos não são tratadas em países de alta e de baixa renda, respectivamente, comprovando a falta de acesso à saúde bucal e a ineficiência dos tratamentos restauradores convencionais. A busca por novas alternativas de manejo da cárie dentária introduziu abordagens como o ART e o UCT. Em 2009 um estudo clínico controlado quasi-randomizado foi iniciado no Paranoá, DF-Brazil, comparando três protocolos no manejo de cárie dentária cavitadas em dentina em molares decíduos: CRT – remoção de cárie por instrumentos rotatórios e restauração com amálgama; ART – remoção de cárie por instrumentos manuais e restauração com cimento de ionômero de vidro e; UCT – combinação de ART para cavidades pequenas e controle de biofilme para cavidades médias e grandes. Este estudo avaliou clinicamente ao longo de 3,5 anos a taxa de sobrevida e a taxa de esfoliação dos molares decíduos submetidos aos três protocolos terapêuticos e avaliou, em um estudo ex vivo, as microfraturas marginais de dentes restaurados com amálgama (CRT) e restaurados com CIV (ART e UCT). O método Kaplan-Meier estimou as curvas de sobrevida e o de PHERG estimou as curvas de esfoliação. A análise de microfraturas marginais em dentes com restaurações classificadas como bem-sucedidas foi realizada pela quantificação de microfendas por microscopia eletrônica de varredura e por microinfiltração com solução aquosa de nitrato de prata a 50%. Neste experimento, a diferença entre grupos e a relação com variáveis independentes foram aferidas pelos Teste de Fischer, teste t e ANOVA. Após 3,5 anos, a taxa de sobrevida cumulativa e erro padrão para todos os molares tratados foi de 90,9 ± 2,0% para CRT, 90,4 ± 2,4% para ART e 88,6 ± 1,9% para UCT (p=0,13). Apenas um efeito do tipo de superfície foi observado – a taxa de sobrevida para dentes com cavidade envolvendo única superfície foi maior que aquela observada para dentes com múltiplas superfícies. Por sua vez, após o mesmo período, não houve diferença na taxa de esfoliação dos molares decíduos: 51% (CRT), 48,7% (ART) e 48,1% (UCT) (p=0,37). Dentes com envolvimento de múltiplas superfícies esfoliaram em maior proporção que os com única superfície para todos os grupos de tratamento (p=0,04). Não houve diferença nas taxas de microinfiltração (p=0.20) e no tamanho das microfendas (p=0,83) observadas nos dentes restaurados por amálgama e por CIV pela técnica ART. Dentes com envolvimento de múltiplas superfícies apresentaram maior infiltração de nitrato de prata que os dentes com única superfície (p=0,02). Os resultados demonstram que a restauração de cavidades pela técnica ART associada à manutenção das cavidades de molares decíduos sob controle de biofilme dental, como empregado no protocolo UCT, pode se tornar uma alternativa adequada para o manejo de cárie na dentição decídua frente aos tratamentos restauradores convencionais, uma vez que introduz componentes de prevenção da doença e promoção de saúde bucal. / According to World Health Organization, 72% and 95% of dentin cavitated carious lesions in primary teeth are untreated in high- and low-income countries, respectively, proving the lack of access to oral health and the inefficiency of the conventional restorative treatment options. The search for new approaches in the management of dental caries introduced ART and UCT in recent years. In 2009, a controlled, quasi-randomized, clinical trial was carried out in Paranoá, DF-Brazil with the aim to compare three treatment protocols for dentin cavitated dental caries in primary molars: CRT - caries removal with rotary instruments and amalgam restoration; ART - caries removal with hand instruments and glass-ionomer cement restoration and; UCT - combination of ART for small cavities and biofilm control for medium and large cavities. The present study evaluated clinically the survival and the exfoliation rates of the deciduous molars submitted to the three therapeutic protocols over a period of 3.5-years, and assessed in an ex vivo study, the marginal microleakage of the teeth restored with amalgam (CRT) and restored with GIC (ART and UCT). The Kaplan-Meier method estimated survival curves and the PHERG estimated the exfoliation curves. The marginal microleakage analysis was performed by quantification of the gap size by scanning electron microscopy and microinfiltration with a silver nitrate solution 50%. In this experiment, the difference between groups and the relationship with independent variables were estimated by Fischer’s test, t-test and ANOVA. After 3.5 years, the cumulative survival rate and standard error for all molars treated was 90.9 ± 2.0% for CRT, 90.4 ± 2.4% for ART and 88.6 ± 1.9% for UCT (p = 0.13). Only a type of surface effect was observed: the survival rate for molars were higher for single- than for multiple-surface cavities. In turn, there was no difference in the exfoliation rate of primary molars: 51% (CRT), 48.7% (ART) and 48.1% (UCT) (p = 0:37) had exfoliated after 3.5-years. Teeth with multiple surfaces cavities exfoliated in a higher proportion than those with single surface for all treatment groups (p = 0.04). There was no difference in microleakage rates (p = 0.20), and gap size (p = 0.83) observed in teeth restored with amalgam and GIC according to the ART technique. Teeth with multiple-surfaces cavities showed greater infiltration of silver nitrate than those with single-surface (P = 0.02). Taken together, the results show that restoring cavities according to the ART technique and maintaining opened cavities through biofilm control, as in the UCT protocol, can become a suitable alternative for caries management in primary dentition, compared to the to conventional restorative treatments once disease prevention and promotion of oral health are introduced.

Orientador: Paulo Henrique dos Santos / Banca: Ana Flávia Sanches Borges / Banca: Wirley Gonçalves Assunção / Resumo: O propósito deste estudo foi avaliar as técnicas de cimentação adesiva de pinos de fibra de vidro nos diferentes terços da dentina intrarradicular, através da resistência de união e avaliação de propriedades mecânicas da interface adesiva. Quarenta dentes humanos unirradiculares foram utilizados neste estudo. Após obturação endodôntica e preparo mecânico dos condutos radiculares, os dentes foram divididos em cinco grupos experimentais (n=8), de acordo com a técnica adesiva adotada para cimentação de pinos de fibra de vidro: Grupo 1: adesivo fotoativado Single Bond 2 + cimento resinoso RelyX ARC; Grupo 2: adesivo dual Excite DSC + RelyX ARC; Grupo 3: adesivo autocondicionante Adper SE Plus + RelyX ARC; Grupo 4: cimento resinoso autoadesivo RelyX Unicem; Grupo 5: cimento resinoso autoadesivo Set. As propriedades mecânicas de dureza e módulo de elasticidade foram mensuradas nas estruturas da interface adesiva em ultramicrodurômetro digital DUH-211. A resistência de união foi mensurada pelo teste de push-out em máquina de ensaio universal nos diferentes terços da dentina intrarradicular (cervical, médio e apical). Os dados de resistência de união e propriedades mecânicas foram submetidos a testes estatísticos de normalidade e analisados pela ANOVA e teste de Fisher ( = 0,05). Os resultados mostraram que as propriedades mecânicas de dureza Martens e módulo de elasticidade dos materiais adesivos e do substrato dentinário são influenciados pela interação dos materiais resinosos utilizados, bem como pela profundidade intrarradicular. O mesmo fenômeno foi observado no teste de resistência de união. Para os materiais resinosos, houve uma tendência de o terço apical apresentar os menores valores das propriedades analisadas, o que poderia conduzir à realização de preparos intrarradiculares mais conservativos / Abstract: The purpose of this study was to evaluate techniques for adhesive cementation of glass fiber posts in different thirds of intra-root dentin, through the bond strength and evaluation of mechanical properties of the adhesive interface components. Forty extracted single-rooted human teeth were used in this study. After endodontic filling and mechanical preparation of root canal, teeth were divided into five groups (n=8), according to the technique adopted for adhesive cementation of glass fiber posts: Group 1: Single Bond 2 light-cured adhesive + RelyX ARC resin cement; Group 2: Excite DSC dual adhesive + RelyX ARC; Group 3: Adper SE Plus self-etch adhesive + RelyX ARC; Group 4: RelyX Unicem self-adhesive resin cement; Group 5: Set selfadhesive resin cement. The mechanical properties of Martens hardness and elastic modulus were measured in the structures of the adhesive interface in a DUH-211 digital ultramicro hardness tester (Shimadzu). Push-out bond strength was measured in a universal testing machine (Emic DL 3000) in different areas of intra-root dentin (cervical, middle and apical). The data of bond strength and mechanical properties were subjected to statistical tests of normality and analyzed by ANOVA and Fisher's test ( =0.05). The results showed that the mechanical properties of Martens hardness and elastic modulus of the adhesive materials and dentin substrate can be influenced by the interaction of the materials, as well as the depth of intraradicular dentin. The same phenomenon was observed in the push-out bonding strength test. There was a tendency of the apical region show the least values of mechanical properties, which could stimulate the use of more conservative intraradicular preparation / Mestre

Orientador: Eduardo Passos Rocha / Banca: Paulo Francisco Cesar / Banca: Paulo Henrique dos Santos. / Resumo: Introdução: Fragmentos cerâmicos têm sido utilizados como opção restauradora em dentes anteriores com necessidade de pequenas correções de contorno e forma. A espessura da camada de cimento resinoso e a variação da temperatura intra-bucal são fatores influentes no sucesso das restaurações cerâmicas convencionais como inlays, onlays, coroas e laminados. Entretanto, a literatura não apresenta dados sobre a influência destes dois fatores no comportamento mecânico do fragmento cerâmico que geralmente apresenta dimensões não uniformes, principalmente nos limites da restauração. Proposição: O objetivo do presente estudo é analisar, através do método dos elementos finitos tridimensional (EF 3-D), o comportamento da camada de cimento resinoso e da cerâmica, variando a espessura da camada de cimento e a temperatura intra-bucal. Materiais e Métodos: Após a obtenção do conjunto de imagens microtomográficas de um incisivo central maxilar, o modelo sólido do dente será elaborado no programa Mimics. A partir deste modelo inicial (M), 5 modelos serão elaborados no programa SolidWorks, simulando a restauração do ângulo disto-incisal com o uso de um fragmento cerâmico colado ao substrato dental, variando a espessura da camada de cimento resinoso: M1 - 0 μm de espessura; M2 - 50 μm em toda... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Introduction: Ceramics fragments have been used for dental/aesthetic restorative purposes in the anterior dentition. The cement layer thickness and temperature variation play an important role for the adequate biomechanical behavior of the ceramics in case of inlays, onlays, total crown and laminate veneers. However, those aspects has not been evaluated in case of ceramics fragments that usually shows non-uniform dimension and shape which might have negative influence in the behavior of dental ceramics fragments. Purpose: The aim of this study was evaluated by 3-D finite element analysis the mechanical behavior of the cement layer and ceramic fragment varying the cement layer thickness and the temperature. Materials and Methods: After obtaining the microtomography data set of a maxillary central incisor, the solid model was rebuild using Mimics program. The model was exported to the Solidworks program for the simulation of a defect at the distal/incisal edge. This defect was restored with a ceramic fragment bonded to the enamel surface. From this restored model (M), 5 different models were tested: M1 - cement layer (CL) showing 0 μm of thickness; M2 - CL with an uniform thickness of 50 μm; M3 - CL with 50 μm at the margin of ceramics and 100 μm in the inner area; M4 - CL with 50 μm at the margin of ceramics and 200 μm in the inner area; and M5 - CL with 100 μm at the margin of ceramics and 200 μm in the inner area. In all models, the environment temperature changed from 5ºC to 50ºC in 4 increments. The finite element (FE) mesh was refined drove by convergence of analysis. The numerical approach was performed using Ansys Workbench FE program. Results: The maximum principal stress... (Complete abstract click electronic access below) / Mestre

Orientador: Renato Herman Sundfeld / Banca: Ticiane Cestari Fagundes / Banca: Anderson Catelan / Banca: André Luiz Fraga Briso / Banca: Márcio Grama Hoeppner / Resumo: O objetivo desse estudo foi avaliar através das análises clínica e clínica/digital o comportamento de 90 restaurações, realizadas em lesões cervicais não cariosas, após 12 e 24 meses de suas realizações. Foram formados 3 grupos de estudo com 30 dentes cada, de acordo com os materiais e técnicas empregadas. Os dentes pertencentes ao grupo I receberam, após o condicionamento com ácido fosfórico 35% em esmalte e dentina, o sistema adesivo convencional Peak LC Bond (Ultradent Products, Inc., South Jordan, USA); os do grupo II receberam a aplicação do sistema adesivo autocondicionante Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão); os do grupo III, previamente à aplicação do sistema adesivo autocondicionante Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão), receberam o condicionamento com ácido fosfórico apenas em esmalte. Todos os dentes foram restaurados com a resina composta Amelogen Plus (Ultradent Products, Inc., South Jordan, USA). Após o acabamento e polimento, bem como aos 12 e 24 meses, as restaurações foram fotografadas para posterior análise clínica/digital em computador de alta resolução. De acordo com critérios previamente estabelecidos, dois examinadores devidamente calibrados realizaram as análises clínica e clínica/digital das restaurações, nos tempos inicial, 12 e 24 meses de suas realizações. Para a análise clínica das restaurações foram considerados as variáveis retenção, adaptação marginal, descoloração marginal, presença de lesão de cárie e sensibilidade, enquanto que para a clínica/digital, retenção e descoloração marginal. Para análise estatística foram aplicados os testes de Kruskal-Wallis, de Wilcoxon, de Friedman e de Dunn. Aos 12 e 24 meses de análise clínica e clínica/digital não foram observadas diferenças estatisticamente significativas para as variáveis analisadas ... / Abstract: The aim of this study was to evaluate the performance of 90 restorations performed in noncarious cervical lesions through clinical and clinica/digital analysis after 12 and 24 months. Three groups were obtained with 30 teeth each, according to the materials and techniques. The teeth of group I received, after etching with 35% phosphoric acid on enamel and dentin, the total-etch adhesive system Peak LC Bond (Ultradent Products, Inc., South Jordan, USA); the teeth of group II received the self-etching adhesive system Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão), and the teeth of group III, prior to application of the self-etching adhesive system Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão), received the phosphoric acid etching only in enamel. All teeth were restored with composite resin Amelogen Plus (Ultradent Products, Inc., South Jordan, USA). Two calibrated examiners performed the clinical and clinical/digital analysis of the restorations at baseline, 12 and 24 months. For clinical analysis were considered the factors: retention, marginal adaptation, marginal discoloration, presence of caries and sensitivity; while for the clinical/digital analysis only retention and marginal discoloration. At 12 and 24 months of clinical and clinical/digital analysis, there were no statistically significant differences for the variables analyzed among the study groups, as well as within a group in said analysis time. The dental sensitivity significantly decreased and was totally eliminated after 12 and 24 months of clinical analysis, respectively. In the statistical analysis were applied the Kruskal-Wallis, Wilcoxon, Friedman and Dunn tests. We conclude according the clinical and clinical/digital analysis that non-carious cervical lesions restorations, performed with total-etch and self-etching adhesive systems, showed satisfactory and similar clinical performance at 12 and 24 months of analysis. / Doutor

Orientador: Rosehelene Marotta de Araújo / Banca: Emilio Carlos Zanatta / Banca: Margareth Oda / Banca: José Roberto Rodrigues / Banca: Henrique Cerveira Netto / RESUMO: A finalidade deste trabalho foi verificar a possível infiltração marginal, em cavidades de Classe V, restauradas com resina composta e dois sistemas adesivos, variando-se o tipo de metodologia: estudo in vivo e in vitro. No estudo in vitro,foram realizados dois testes laboratoriais: 1) termociclagem, empregando-se 300 ciclos de trinta segundos cada em banhos entre 5"a 55" C e, 2)utilizando-se termociclagemmais carga de 33kgf/cem ciclos. Foram utilizadas 60 pré-molares humanoshigidos, onde foram confeccionados preparos cavitários de Classe V com dimensões de aproximadamente 2mm de largura X 2mm de altura X 1,5rnmde profundidade. Os dentes para os testes in vitroforam aleatoriamente divididosem quatro grupos de dez dentes cada: grupo 1 - aplicação de carga etermociclagem com o emprego do adesivo Single Bond; grupo 2 - aplicação decarga e termociclagem com o emprego do adesivo Prime & Bond NT; grupo 3 -aplicação de termociclagem com o emprego do adesivo Single Bond; grupo 4 -aplicação de termociclagem com o emprego do adesivo Prime & Bond NT. Osdentes foram pintados com esmalte de unha, respeitando-se a distancia de 1 mm darestauração, ficaram imersos em solução de nitrato de prata a 50% por 24 horas,lavados e secos e expostos a luz fluorescente por oito horas em solução reveladora Kodak. Apos esse período, os dentes receberam duas secções no sentido oclusogengival, para verificar a infiltração em estereomicroscópio. Para os estudos invivo, formaram-se dois grupos: grupo 5 - aplicação do sistema adesivo SingleBond; grupo 6 - aplicação do sistema adesivo Prime & Bond NT. Apos os vinte edois dentes terem sido restaurados e permanecidos em função por sessenta dias, osmesmos foram extraídos, limpos e pintados com esmalte de unha, respeitando-se a distancia de 1 mm da restauração, ficaram imersos em solução de nitrato de prata a50% por 24 horas, lavados e secos e ... / ABSTRACT: The purpose of this study was to verify the marginal infiltration, in restorations of Class V, restored with composed resin and two adhesive systems, being varied the methodology type: study in vivo and in vitro. In the study in vitro, two tests was accomplished: I) thermocycling, with 300 cycles of thirty seconds each in bathing among 5ºtu 55º C and2) study in vitro being used thermocycling more load of 33kgf/100 cycles. 60 higidhuman bicuspids were used, where cavity of Class Vwere made with dimensionsof approximately 3mm of widthX 2mm of height X2mmof depth. The teeth for the tests in vitro were handomlydivided in four groups of ten teeth each: a) group 1- load application and thermocycling with the employment of adhesive Single Bond; b) group 2- load application and thermocyclingwith the employment of the Pime&Bond NT; c) group 3- thermocyclingapplication with the employment of adhesive Single Bond; d) group4 - thermocycIingapplication with the employment of the Prime &Bond NT. Theteeth were colored with fingernail enamel, being respected distances if of 1mm of the restoration, they were immerged in solution of silver nitrate at 50% for 24 hours, washed and dryand exposed to the fluorescent light by eight hows indeveloping solution Kodak. After that period, the teeth received two cuts in oclusogengival sense, to verify the infiltration in stereomicroscopy. For the studies in vivo, they were formed twogroups: e) group 5 - application of the adhesive system Single Bond; f) group 6 - applicationof the adhesive systemPrime &Bond NT. After the restorations complete, the twenty teeth stayed in function by sixty days. They were extracted, clean and painted with fingernail enamel, being respected distances it of 1mm ofthe restoration, they were immerged in solution of silver nitrate at 50% for 24hours, washed and dry and exposed to the fluorescentlight by eight hours in developing solution Koda... / Doutor

Orientador: João Eduardo Gomes Filho / Banca: Edilson Ervolino / Banca: Sandra Helena Penha de Oliveira / Banca: Marco Antonio Húngaro Duarte / Banca: Rodrigo Ricci Vivan / Resumo: O objetivo deste estudo foi analisar as propriedades biológicas do MTA em condição normal e hiperglicêmica. Para tanto, esse trabalho foi dividido em duas partes, sendo que a primeira teve como objetivo avaliar o efeito do MTA no processo de reparo do Ligamento Periodontal (PDL) e na diferenciação de células mesenquimais progenitoras do PDL (PDSCs) e da Medula Óssea (BMSCc) após injuria dental. Uma perfuração na região de furca do primeiro molar superior de camundongos transgênicos (αSMACreERT2/Ai9/Col2.3GFP) foi realizada e os efeitos do MTA após 2, 17 e 30 dias de lesão, foram examinados e comparados com resina composta (AS) utilizando análise histológica e epifluorescência. Além disso, BMSCs e PDSCs desses camundongos foram isoladas, cultivadas e os efeitos do MTA na proliferação celular e diferenciação osteogênica foram avaliados. Os resultados indicaram que o MTA promoveu a regeneração do PDL e do osso alveolar na área da injuria dental. No entanto, demonstrou efeitos negativos na diferenciação osteogênica de PDSCs e BMSCc. A segunda parte, teve como objetivo avaliar a influência da Diabetes Mellitus na proliferação celular, produção de citocinas, resposta tecidual, capacidade de mineralização e na expressão local e sistêmica de marcadores ósseos. Para alcançar esses objetivos, células de linhagem fibroblásticas L929 foram cultivadas em alta concentração de glicose e a influência do MTA na proliferação celular e na produção de citocinas das IL-1β, IL-6 e TNF-α foram obse... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The a im of this study was to analyze the biological properties of MTA in normal and hyperglycemic conditions . Therefore, this study were divided into two parts; the first part aim was to evaluate MTA effect on healing of periodontal ligament (PDL) and dif ferentiation of mesenchymal progenitor cells in PDL (PDSCs) and bone marrow stromal cells (BMSC c ) following dental injury. Perforation on the pulp floor in the furcation area in the first maxillary molars of transgenic mice ( α SMACreERT2/Ai9/Col2.3GFP ) were performed and the effects of MTA after 2, 17, 30 days of injury, were examined and compared to AS using histological and epifluorescence analysis. Additionally, BMSCs and PDSCs from these mice were isolated, cultured and the effects of MTA on cell prolife ration and osteogenic differentiation were evaluated. The results indicated that MTA promoted regeneration of injured PDL and alveolar bone in the area of dental injury. However, it has demonstrated negative effects on the osteogenic differentiation of PDS Cs and BMSCs. The aim of second part was to evaluate the influenc e of Diabetes Mellitus on cell proliferation, cytokine production, tissue response, mineralization ability and local and systemic expression of bone markers. To achieve these goals, L929 fibr oblasts cell line were cultured under high glucose concentration and the influence of MTA on cell proliferation and production of cytokine IL - 1 β, IL - 6 and TNF - α were observed at 6, 24, 48 and 72 hours; polyethylene tubes were implanted in the subcutaneous tissue of normal and diabetic rats (induced by Alloxan) and the influence of MTA on tissue response, cytokines production and mineralization...(Complete abstract click electronic access below) / Doutor

Orientador: Carlos Rocha Gomes Torres / Banca: Taciana Marco Ferraz Caneppele / Banca: Alessandra Bühler Borges / Banca: Ricardo Amore / Banca: Carlos Eduardo Francci / Resumo: O objetivo deste estudo foi avaliar a influência da viscosidade das resinas compostas e do tipo de cura dos sistemas adesivos, na resistência adesiva de resinas diretas submetidas a envelhecimento artificial. Foram utilizados 240 dentes incisivos bovinos, os quais tiveram a face vestibular desgastada para exposição da dentina. Os espécimes foram incluídos em resina acrílica autopolimerizável e a smear layer foi padronizada com lixa P600. Os espécimes foram divididos em 2 grupos de acordo com viscosidade da resina utilizada: Grupo GC: Grandio SO, alta viscosidade e Grupo GF: Grandio SO Heavy Flow, baixa viscosidade. Esses grupos foram subdivididos em 6 subgrupos de acordo com o sistema adesivo autocondicionante utilizado: FM: Futurabond M - fotopolimerizado, FDCQ: Futurabond Dual Cure Quimicamente ativado, FDCF: Futurabond Dual Cure Fotoativado, CS3: Clearfil S3 fotopolimerizado, CDCQ: Clearfil Dual Cure Quimicamente ativado e CDCF: Clearfil Dual Cure Fotoativado. Sobre a superfície dentinária foram construídos blocos de resina com auxílio de matriz de silicone. Os espécimes foram armazenados em água deionizada em estufa a 37 ºC, por um período de 24 h, e cada grupo foi subdividido em dois, sendo metade dos espécimes levados à cortadeira Labcut para obtenção de palitos dentina/resina medindo aproximadamente 1 X 1mm e a outra metade submetida a ciclagem termomecânica (300.000 ciclos mecânicos e 1000 ciclos térmicos) e sequencialmente cortados para obtenção de palitos. Os palitos foram submetidos a teste de microtração na máquina de ensaios universal DL-200MF (EMIC) e os resultados obtidos foram submetidos à análise estatística empregando-se os testes ANOVA 3 fatores e Tukey (α = 5%). O teste ANOVA mostra que houve diferença estatística somente para os fatores Adesivo (p = 0,0000) e Ciclagem termomecânica (p=0,0001), assim como para a interação entre eles ... / Abstract: The aim of this study was to evaluate the influence of composite resins viscosity and the type of cure of the adhesive systems on the bond strength of direct composite resins submitted to artificial aging. Two hundred forty bovine incisors had the buccal dentin exposed by sandblasting papers and were included in acrylic resin. The smear layer was standardized by sandblasting papers (600 SiC, Fepa-P). The specimens were divided in 2 groups according to the viscosity of the composite resin used: Group GC: Composite Grandio SO, high viscosity and Group GF: Grandio SO Heavy Flow, low viscosity These groups were divided in 6 according to the self-etch adhesive used: FM: Futurabond M - light cured, FDCQ: Futurabond Dual Cure - chemical cured, FDCF: Futurabond Dual Cure - light cured, CS3: Clearfil S3 - light cured, CDCQ: Clearfil Dual Cure - chemical cured and CDCF: Clearfil Dual Cure - light cured. Resin blocks were build up on the dentin surface using a silicon mold. The specimens were stored in deionized water 37°C along 24 h and half of them were cut to obtain resin/dentin sticks (1X1mm) and the other half submitted to thermomechanical aging (300.000 mechanical cycles and 1000 thermal cycles) and lately cut to sticks. The dentin/resin sticks were submitted to microtensile bond strength test (μTBS) in Universal machine DL-200MF (EMIC) and the results were analysed by 3 way ANOVA and Tukey's test (α=5%). ANOVA showed signifficant statistical difference to the parameters: Adhesive (p=0,0000) and Thermomechanical aging (p=0,0001), as well to their interaction (p=0,0062). Tukey's test showed the results: Adhesive: CDCQ: 13,44 (±5,13)a; FM: 14,01 (±2,71)a; CDCF: 14,51 (±4,98)a; FDCQ: 18,66 (±7,13)b; CS3: 18,80 (±6,50)b; FDCF: 19,18 (±7,39)b; Thermomechanical aging: Aged: 14,99 (±6,32)a; Not aged: 17,87 (±5,97)b. The conclusions were: Composite resin viscosities and type of cure... / Doutor

Resumo: Objetivou-se avaliar a resistência à tração (σ) da união de três sistemas de cimentação resinosa de ativação dual (RelyX ARC, RelyX U100 e Panavia F) entre a dentina e uma cerâmica à base de zircônia estabilizada por óxido de ítrio (In-Ceram YZ, Vita Zanhfabrik) com diferentes tratamentos de superfície. A superfície oclusal de 54 terceiros molares humanos hígidos foi exposta e condicionada conforme as instruções de cada cimento. Cinqüenta e quatro blocos cerâmicos foram planificados e sinterizados (6,4 mm x 6,4 mm x 4,8 mm). Após, foram divididos em dois grupos conforme o tipo de tratamento de superfície: jateamento com óxido de alumínio ≤ 50 μm ou silicatização (CoJet, 3M ESPE)(24-28 psi). A cimentação à dentina foi realizada de acordo com as instruções de cada fabricante. Assim, foram constituídos 6 grupos. Os conjuntos foram armazenados em água destilada à 37°C por 24 h e cortados no sentido x e y, 9 corpos de prova (cp) por conjunto foram obtidos em média (área adesiva de ± 1 mm2). Os cp de cada conjunto foram divididos aleatoriamente em 3 condições de armazenagem: ensaio imediato; 60 dias de armazenagem em água destilada (37ºC) e termociclagem (10.000x, 5ºC - 55ºC) (n≥12). O ensaio de resistência adesiva por microtração foi realizado numa máquina de ensaio universal (1 mm/min). Nos grupos imediatos RelyX ARC-silicatização e Panavia Fjateamento apresentaram as médias mais altas de σ (13,9 e 13,0 MPa, respectivamente), seguido do RelyX U100-jateamento (10,2 MPa). Após a termociclagem, o cimento Panavia F-jateamento foi melhor (14,8 MPa) seguido pelo RelyX ARC-silicatização e RelyX U100-jateamento (12,9 e 9,9 MPa, respectivamente). Após a armazenagem por 60 dias, os cimentos se comportaram de forma semelhante, onde os grupos que foram silicatizados demonstraram uma tendência a valores mais elevados de σ (MPa) / Abstract: The aim of this study was to evaluate the bond strength of three dualcured resin cement systems (RelyX ARC, RelyX U100 and Panavia F) to dentin and to an yttria-stabilized zirconia-based ceramic (In-Ceram YZ, Vita Zanhfabrik) after different surface treatments. The occlusal surface of 54 sound human third molars was exposed and conditioned according to the manufacturers' instructions. Fifty-four ceramic blocks were cut (6.4mm x 6.4mm x 4.8mm), flattened and fired. They were divided into two groups according to the type of surface treatment: air-abrasion with ≤ 50μm alumina particles or CoJet system (3M ESPE) (14-28 psi). The cementation procedure followed the instructions of each manufacturer. Thus, there were 6 groups. All teeth-cement-ceramic blocks were stored in 37°C distilled water for 24 hours before cutting into non-trimming specimens (adhesive area= 1 mm²). About nine specimens (sp) were obtained per block (n=27). The specimens of each block were randomly assigned to one of the three storage conditions: dry- immediate test, W60- 60 days of storage (37°C water) and TC- thermocycling (10,000x) (n≥12). The microtensile bond strength test was performed using an universal testing machine (crosshead speed: 1 mm/min). Immediate groups of RelyX ARC-Cojet and Panavia F-air-abrasion presented the highest σ average (13.9 and 13.0 MPa, respectively), followed by RelyX U100-airabrasion (10,2 MPa). After TC, Panavia F-air-abrasion was the best (14.8 MPa) followed by RelyX ARC-Cojet and RelyX U100-air-abrasion (12.9 and 9.9 MPa, repectively). After W60, all the cements behaved similarly, when the groups were treated with Cojet system, tended to higher values of σ (MPa) / Orientador: Alvaro Della Bona / Coorientador: Tarcísio José de Arruda Paes Junior / Banca: Estevão Tomomitsu Kimpara / Banca: Mário Alexandre Coelho Sinhoreti / Mestre

Resumo: Este estudo avaliou a resistência de união entre dentina bovina e três sistemas adesivos: um de condicionamento total e dois autocondicionantes, variando-se o tipo de preparo da dentina. Foram utilizados 108 dentes bovinos onde as raízes foram removidas e a dentina coronária vestibular foi exposta. As superfícies foram preparadas com os seguintes métodos: pontas diamantadas de granulação média em turbina de alta rotação, pontas CVD acopladas em aparelho de ultra-som e laser Er:YAG. Os grupos foram subdivididos para aplicação dos seguintes sistemas adesivos de acordo com as recomendações do fabricante: Clearfil SE Bond (Kuraray), Adper SE Plus (3M ESPE), autocondicionantes, e Adper Single Bond 2 (3M ESPE), de condicionamento ácido total. Os espécimes foram restaurados com resina composta Filtek 250 (3M ESPE) com espessura de 4 mm. A resina foi inserida em incrementos de 2 mm e fotopolimerizada por 20 s. Em seguida, os espécimes foram armazenados em água destilada a 37 °C por 24 h e então seccionados em formato de palito com aproximadamente 1mm2 de área na interface adesiva. Foi realizado o teste de microtração em máquina de ensaio universal com velocidade de 1.0 mm/min. Os resultados foram submetidos aos testes estatísticos de análise de variância paramétrica de 2 fatores (ANOVA) e o teste de Tukey empregando um nível de significância de 5% (p<0,05). Espécimes adicionais foram preparados para observação em microscópio eletrônico de varredura. Os resultados mostraram que a ponta CVD obteve menores valores de resistência adesiva, enquanto a ponta diamantada e o laser obtiveram valores semelhantes, porém mais elevados. O sistema adesivo Single Bond obteve valores equivalentes ao Adper SE Plus e significativamente diferentes quando comparados ao sistema adesivo Clearfil SE Bond . O estudo concluiu que o método de preparo e o tipo de sistema adesivo influenciaram na resistência de união / Abstract: The aim of this study was to compare the microtensile bond strength of two self-etching adhesive systems and one total-etching, with different methods of dentin preparation. A hundred and eight bovine teeth, stored in freezer -18ºC, were used. The buccal face dentine was exposed and prepared with three different methods: Diamond tip (DT) with high speed; CVD tip with ultrasound advice (CVD) and Er:YAG laser (LA). Three different adhesive systems were used: Adper Single Bond 2 (SB) (3M ESPE), total etch; Adper SE Plus (AS) (3M ESPE) and Clearfil SE Bond (CS) (Kuraray), both self-etching. After dentin preparation, the adhesives systems were applied according to manufacturer's instructions. Blocks of composite resin (Filtek Z250 - 3M ESPE) with 4 mm high were prepared using the incremental technique. After storage in distilled water for 24h at 37ºC, serial mesio-distal and bucco-lingual cuts were made and stick-like specimens were obtained, with transversal section of 1,0 mm2. The samples were submitted to microtensile test at 1 mm/min and load of 10 kg in a universal testing machine. Data (Mpa) were subjected to ANOVA and Tukey tests (5%). The results showed lower bond strength in groups prepared with CVD tip. LA and DT groups obtained similar values of bond strength and higher than CVD. The adhesive systems SB and AS showed values higher than CS. It was concluded that the method of dentine preparation and adhesive system tested influenced in bond strength / Orientador: Rebéca Di Nicoló / Coorientador: Alessandra Bühler Borges / Banca: Marcelo José Strazzeri Bönecker / Banca: César Rogério Pucci / Mestre