Orientador : Altair Antoninha Del Bel Cury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T09:04:32Z (GMT). No. of bitstreams: 1 Moura_JulianaSilva_M.pdf: 7300692 bytes, checksum: aa5035309d6d97fc7ccaf1024cf40319 (MD5) Previous issue date: 2003 / Mestrado

Orientadores: Luis Alexandre Maffei Sartini Paulillo, Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T10:14:17Z (GMT). No. of bitstreams: 1 Souza_GraceMendoncaDiasde_M.pdf: 2850330 bytes, checksum: 6274f4312fb8638abfeedf84da268f79 (MD5) Previous issue date: 2003 / Resumo: Quando se utilizam pinos de fibra de vidro, a porção coronária deve ser reconstruída empregando materiais estéticos como resina composta, resina modificada por poliácido, ionômero de vidro convencional ou modificado por resina, para dar proteção e estabilidade à coroa protética. Assim, o propósito deste estudo foi avaliar a resistência à fratura de raízes bovinas restauradas com pino de fibra de vidro associado a quatro materiais estéticos para núcleo, indicados para restaurações estéticas, e coroa total em resina composta indireta. Quarenta raízes bovinas tratadas endodonticamente foram inseridas em cilindros de resina poliestirênica, simulando-se o espaço do ligamento periodontal. Pinos de fibra de vidro foram cimentados com agente para cimentação resinoso e as raízes separadas em quatro grupos experimentais com dez unidades cada, de acordo com o tipo de material empregado para a confecção de núcleo: resina composta (RC), resina modificada por poliácido (RM), ionômero de vidro convencional (IV) e ionômero modificado por resina (1M). Coroas livres de metal confeccionadas em resina composta indireta - Solidex ¿ foram cimentadas sobre os núcleos sem o abraçamento radicular. As amostras foram submetidas ao carregamento tangencial de compressão após o período de sete dias de armazenamento em estufa a 37° C e 100% de umidade relativa. Os resultados obtidos foram levados à Análise de Variância (ANOVA) e ao Teste de Tukey. A ANOVA revelou haver pelo menos uma diferença estatística significativa entre as médias obtidas e o Teste de Tukey (p>0,05) mostrou que os melhores resultados de resistência à fratura foram obtidos para os núcleos em resina composta (RC - 71,97kgf - a), que não diferiram dos núcleos confeccionados em ionômero de vidro modificado por resina (IM - 62,15kgf - ab). Entretanto, este não apresentou diferença estatística do ionômero convencional (IV - 51,99kgf - b) e da resina modificada por poliácido (RM - 50,21kgf - b). A análise do padrão de fratura evidenciou que em nenhuma amostra houve fratura radicular, todas as amostras fraturaram na interface pino/núcleo / Abstract: When glass fiber posts are used, the coronary portion should be reconstructed using esthetic materials such as composite resin, polyacid-modified composite resin, conventional glass ionomer cement or resin-modified glass ionomer, in order to protect and stabilize the prosthetic crown. Therefore, the purpose of this study was to evaluate the fracture resistance of bovine roots restored with glass fiber posts associated to four core esthetic materials indicated for esthetic restorations and total crowns in indirect composite resin. Forty endodontically treated roots were inserted in polyestyrene resin cylinders, simulating periodontal ligaments space. Glass fiber posts were cemented with resin cement and the roots divided in four experimental groups with ten specimens each, according to the core material: composite resin (CR), polyacid-modified composite resin (MR), conventional glass ionomer (GI) and resin-modified glass ionomer (MI). Metal free crowns made of indirect composite resin - Solidex - were cemented onto the cores without using ferrule. The tangential load was applied to samples after a seven-day storage at 100% relative humidity and 37° C. The obtained data were subject to Analysis of Variance (ANOVA) and Tukey Test. The ANOVA results revealed that there was at least one significant statistical difference among the obtained means, while the Tukey Test (p>0.05) showed that the best results for resistance to fracture were obtained for the composite resin cores (CR - 71.97kgf - a), which did not differ from the resin-modified glass ionomer ones (MI - 62.15kgF - ab). However, there was no statistical difference among the resin-modified glass ionomer, the conventional glass ionomer (GI - 51.99kgF - b) and the polyacid-modified composite resin (MR - 50.21kgF- b). The analysis of the fracture pattems evidenced a complete absence of root fractures in the samples. On the other hand, all samples were fractured in the core/post interface / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:09:00Z (GMT). No. of bitstreams: 1 Duarte_RosangelaMarques_D.pdf: 3969669 bytes, checksum: 5d104042597bd78c90263b5527023ba8 (MD5) Previous issue date: 2003 / Resumo: O objetivo deste estudo foi avaliar a resistência da união à tração de sistemas adesivos autocondicionantes em combinação com o compósito para cimentação Panavia F (PF) sobre dentina recém cortada e após forramento com o compósito de baixa viscosidade Protect Liner F (PL). Superfícies dentinárias planas foram preparadas nas faces vestibulares de 60 incisivos inferiores bovinos. Para a delimitação da área de união foi utilizada fita adesiva contendo orifício de 4,0 mm de diâmetro. Nos grupos A I, A II e A m foi aplicado o sistema adesivo autocondicionante ED Primer componente do sistema de cimentação adesiva PF. Nos grupo B I, B II e B m foi aplicado o sistema adesivo autocondicionante Clearfil Liner Bond 2V (CLB2V), seguido da aplicação de camada de compósito de baixa viscosidade PL. Em seguida, o compósito para cimentação PF foi aplicado, o cilindro de compósito (Z100) posicionado sobre a área de união delimitada e o compósito fotoativado por 20 segundos em três pontos da interface de união, totalizando 60 segundos. O ensaio de tração foi realizado em máquina de ensaio universal Instron, com velocidade de 0,5 mm/minuto e conduzido após 1O minutos da união para os grupos A I e B I, 24 horas da união para os grupos A II e B II e após 12 meses de armazenagem para os grupos A m e B 111. O tipo de fratura foi observado e classificado em Microscopia Eletrônica de Varredura. Os resultados foram submetidos à análise de variância e_ ao teste de Tukey (p<0,05). Os resultados do ensaio de tração expressos em MPa foram: Grupo A 1 - 9,32 :i: 2,39ab; Grupo A II - 10,16 :i: 1,22a; Grupo A m - 8,47:i: 1,52b; Grupo B 1- 10,58 :t 2,19ab; Grupo B II - 11,31 :t 2,06a; Grupo B m - 9,74:t 1,61b. Não houve diferença estatística significativa entre 10 minutos e 24 horas (p>O,OS) para os grupos testados. Entre 24 horas e 12 meses os valores médios de resistência de união à tração foram estatisticamente inferiores (p<O,OS) para os grupos A li e B li. Os grupos que utilizaram o sistema de cimentação PF sobre a dentina forrada com o compósito de baixa viscosidade PL foram estatisticamente superiores aos grupos do PF sobre dentina para todos os períodos (p<O,O5). A fratura com predominância estatística para os grupos A I, A TI e A TIl foi coesiva no adesivo/camada híbrida e para os grupos B I, B II e B III foi coesiva no compósito. A técnica do uso do compósito de baixa viscosidade PL, "resin coating", proporcionou a proteção do complexo hibridizado, mantendo o se lamento dos túbulos dentinários durante o período de 12 meses de armazenagem em água / Abstract: The purpose of this study was to evaluate the tensile bond strength (TBS) of self-etehing primers, ED Primer (ED) and Clearfil Liner Bond 2V (CLB2V), assoeiated with Panavia F (PF) resin eement on dentin and resin eoated dentin at 10 minute, 24h and 12 months afier euring. Flat dentin surfaees were prepared on labial surfaee of 60 bovine ineisor teeth and a 4.0-mm-diameter bonding area was demarcated on eaeh prepared surfaee with adhesive vinyl tape. On the dentin surfaee of the A I, A 11 and A 111 Groups (Gs) were applied ED and in the B I, B 11 and B 111 Gs was applied CLB2V followed by Proteet Liner F (PLF) and PF. A resin eomposite rod was positioned on the bonding area and eured for 20s at the three points of the interfaee to perform the TBS test using an Instron maehine (0.5 mm/min) at 10 minute to AI and BI Gs and 24h afier euring to Ali and BII Gs. A 111 and B 111 Gs were submitted to TBS test afier 12 months storage. The results were analyzed by ANOVA and Tukey's test (p< 0.05). Fracture modes and interfaee adhesive-dentin were observed at SEM. The TBS results in MPa were: A I - 9.32 :t 2.39; AlI - 10.16:t 1.22; A m - 8.47:t 1.52; B I-10.58:t 2.19; B 11 -11.31 :t 2.06; B m - 9.74:t 1.61. There was no statistically significant differenee (p<0.05) among eaeh themselves Gs at 10 minute and 24 h. A m and B m Gs showed the lowest TBS values (p<0.05) afier 12 months storage. PF resin eement on resin eoated dentin (PLF) showed the highest TBS and was statistically different (p<0.05) than PF on dentin at 10 min, 24 h and 12 months. The fracture pattem was cohesive on the adhesivelhybrid layer for A I, A 11 and A 111 Gs and cohesive on eomposite resin for B I, B 11 and B m. The coneept of coating the prepared dentin with adhesive system and low viscosity composite resin showed a protection of the hybridized complex with a dentin seal during the 12 months storage period / Doutorado / Doutor em Materiais Dentários

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T20:20:51Z (GMT). No. of bitstreams: 1 Piva_Evandro_D.pdf: 1188327 bytes, checksum: eb2cbf397b40bbaac42c421a193afd42 (MD5) Previous issue date: 2004 / Doutorado

Orientador: Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T00:35:36Z (GMT). No. of bitstreams: 1 Cordeiro_NaraPereirad'Abreu_M.pdf: 3160661 bytes, checksum: 26a276349e045dff73e7e7af7e8e90fa (MD5) Previous issue date: 1999 / Resumo: O objetivo deste estudo foi avaliar a influência dos sistemas de cimentação na resistência à fratura de in/ays em porcelana. Preparos MOD padronizados foram confeccionados em cinqüenta molares inferiores hígidos, divididos em cinco grupos de dez dentes cada. In/ays em porcelana foram confeccionados e fixados aos dentes preparados com os seguintes sistemas cimentantes: Grupo A- in/ays não cimentados, Grupo B- Fosfato de Zinco, Grupo C- Prime & Bond 2.1 e Enforce, Grupo D- Scotchbond Multi Uso Plus e Resin Cement, Grupo E- Scotchbond Multi Uso Plus e Opal. Os dentes restaurados foram submetidos a um carregamento axial, por uma esfera de 4.0mm de diâmetro posicionada na região central da caixa oclusal, com velocidade de 1.0mm/min até a fratura. Os valores médios de resistência obtidos foram 8,9 Kgf, 143,1 Kgf, 243,1. Kgf, 206,7 Kgf, 201,2 Kgf para os grupos A, S, C, D e E, respectivamente. A análise estatística revelou que os grupos C, D e E demonstraram maior resistência à fratura, não havendo diferenças estatisticamente significantes entre eles. Concluiu-se neste estudo laboratorial que a resistência à fratura de i nlays em porcelana está diretamente relacionada ao sistema de cimentação utilizado, sendo os sistemas resinosos os mais indicados para este fim / Abstract: The aim of this study was to investigate the effect of differing bonding and luting systems on the fracture resistance of dentin-bonded-ceramic inlays. Sound, unrestored, lower molar teeth received standardized preparations and were randomly divided into five groups of ten teeth each: Group A: Received no luting system application; Group B: Zinc Phosphate Cement; Group C: Prime & Bond 2.1 and Enforce; Group D: Scotchbond Multi Uso Plus and Resin Cement; Group E: Scotchbond Multi Uso Plus and Opal. The restored teeth were loaded in compression at 1.0mm/min.. Mean fracture loads of 8.9Kgf, 143.1Kgf, 243.1Kgf, 206.7Kgf, 201.2Kgf were recorded for groups A, B, C, D and E , respective/y. The mean fracture resistance of the inlays was significantly greater (P <0.05) for groups C, D and E, fol/owed by groups B and A, respectively. No statistical differences were observed among groups 'c, D, and E. It was concluded th9t the fracture resistance of ceramic inlays used inthis laboratory study was dependent on the luting system used and it was enhanced by resin /uting ones / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Mario Fernandes de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T05:40:23Z (GMT). No. of bitstreams: 1 Chaves_Eclerion_M.pdf: 4587910 bytes, checksum: 6cb346293d96a9f05897c809edb43ee1 (MD5) Previous issue date: 1999 / Resumo: o objetivo deste estudo foi avaliar o efeito da aplicação do si/ano na resistência a tração de três cimentos resinosos. Foram confeccionados 168 discos de porcelana (Duceram). Os discos de porcelana foram embutidos, desgastadas com lixas de granulação 220 e 600 e limpos em ultra-som. Os discos cerâmicos foram divididos em 3 grupos contendo 56 amostras. No Grupo I foi usado o Cimento Enforce; Grupo 11, Cimento Variolink 1/; Grupo 111, Cimento Opal. Metade das amostras de cada grupo foi tratada com o respectivo agente de silanização de cada cimento resinoso usado de acordo com as instruções de cada fabricante, seguido da aplicação do adesivo e cimento resinoso. A outra metade das amostras não recebeu o tratamento com o silano, apenas a aplicação do adesivo e cimento resinoso. A seguir, os discos cerâmicos, aos pares, foram posicionados em uma matriz com a superfície tratada voltada uma para a outra para o procedimento de fixação com o cimento resinoso. Desta forma, a resina foi fotopolimerizada por 160 segundos e os corpos-de-prova armazenados por 24 horas a 37° C e 100% de umidade relativa. A seguir, com o auxílio de uma matriz metálica, corpos-de-prova foram submetidos ao ensaio de tração em uma máquina de ensaio universal INSTRON (modelo 4411) a uma velocidade de 1 mm/min. Os resultados obtidos foram submetidos à análise de variância e ao teste de Tukey. As médias dos resultados obtidos foram as seguintes: Grupo I, sem si/ano = 6,30 MPa; com silano = 7,81 MPa; Grupo 11, sem silano = 3,76 MPa, com silano = 6,11 MPa; Grupo 111, sem silano = 4,46 MPa; com silano = 6,31 MPa. Após o ensaio de resistência a tração, as superfícies das amostras de porcelana foram examinadas em uma lupa estereoscópica Carl Zeiss (Carl Zeiss do Brasil), com 25 aumentos, determinando um predomínio de fraturas coesivas no corpo da porcelana para as amostras do Grupo I e de fraturas adesivas e coesivas no cimento para os grupos 11 e 111. O padrão de fratura foi documentado através de fotomicrografias realizadas com o auxílio de um microscópio eletrônico de varredura (Zeiss DS M 960, Germany). Foi concluído que: (1) Os valores médios de resistência à tração obtidos para os corpos-de-prova tratados com o agente de silanização foram estatisticamente superiores (p<0,05) aos grupos de corpos-de-prova que não receberam o tratamento independente do sistema resinoso. (2) Os valores médios de resistência á tração obtidos para o grupo I (Enforce) foram estatisticamente superiores à aqueles obtidos para os grupos 11 (Variolink) e 111 (Opal) que não apresentaram diferença estatística significante entre si (P>0,05). (3) O padrão de fratura apresentado pelos corpos-de-prova do grupo I (Enforce) foi predominantemente coesivo no corpo da porcelana mesmo nos corpos-de-prova que não foram tratados com o silano. Para o material Variolink /I (Grupo 11), a maioria das amostras que não receberam silano, apresentou padrão de fratura adesivo e o padrão misto (adesivo e coesivo no cimento) foi observado nas amostras silanizadas. No grupo 111 (Opal), o padrão de fratura misto foi predominante .para as amostras que receberam ou não à aplicação do silano / Abstract: The purpose of this study was to evaluate the effects of silane treatment on tensile strength ofresin cements bonded to porcelain. One hundred sixty eight samples (Ouceram) were prepared and separated in three groups. Group I - Enforce resin cement (Oentsply); Group 11 - Variolínk li resin cement (Vivadent) and Group 111 - Opal resin cement (3M Co.). The samples were embedded with chemically cured acrylic resin and the surface of porcelain was smoothed by use of a 220 - 600 grit wet silicon carbide papers and shaped to allow the application of resin cements. Afie r, the samples was cleaned by means of a ultrasonic device and porcelain samples for each group were divided into two subgroups for surface treatment, Le., half of the samples of each group was treated with respective silane agents, and the other half remained untreated. The samples were stored for 24 hours at 37° C and 100% of relative humidity. The tensile strength test was conduct on a universal testing machine (INSTRON - 4411), at a cross speed of 1 mm/min. The mean results were as follows: Group I - no silane treatment = 6,30 MPa, with silane treatment = 7,81 MPa; Group " - no silane = 3,76 MPa, with silane = 6,11 MPa; Group 111 - no silane = 4,46 MPa, with silane = 6,31 MPa. The data was then submitted to ANOVA and Tl.Irkey's test. Afier tensile strength test, the samples surfaces were examined on a glass magnifying (Carl Zeiss), with magnification of 25 times. The fractures pattem was documented through photomicrographs in scanning electronic microscope (Zeiss OS M 960 - Germany). It was concluded: (1) the tensile strength of specimens treated with silane was statistically higher (p<0,05) than the group that did not receive silane. For ali resin cements systems; (2) The mean values of resistance for Group I (Enforce) were statistically higher from Group " (Variolink li) and 111 (Opal) that did not present significant difference to each other (p<0,05) and (3) the fracture pattem presented by the Group I was cohesive fractures in the body of porcelain, while for the Groups 11 and 111 were mixed (adhesive and cohesive in the cement) / Mestrado / Materiais Dentarios / Mestre em Odontologia

Orientador: Regina Maria Puppin-Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:12:27Z (GMT). No. of bitstreams: 1 Borges_AnaFlaviaSanches_M.pdf: 3516462 bytes, checksum: a51b845dc96d230cbc181dac6262187f (MD5) Previous issue date: 2005 / Resumo: As restaurações indiretas de compósito são uma das alternativas na clínica odontopediátrica, pois, proporcionam a redução da duração da sessão clínica, além da possibilidade da diminuição da contração de polimerização inerente ao pequeno volume do agente de fixação resinoso. Em casos de dentes tratados endodonticamente, o desempenho das restaurações ¿adesivas¿ não se encontra bem estabelecido, e estas são de extrema importância uma vez que a falha nas restaurações das coroas de dentes submetidos à terapia pulpar pode significar a perda do tratamento endodôntico. Assim, os objetivos desta dissertação fundamentada em dois artigos foram: (1) avaliar a adaptação marginal inicial de restaurações tipo onlay de compósito em dentes decíduos previamente submetidos ou não à irrigação com hipoclorito de sódio 1% (NaOCl 1%) e cimentados com dois sistemas resinosos para fixação (EnForce e Rely X), (2) avaliar os efeitos do tratamento com NaOCl 1% e dois agentes resinosos de fixação na recuperação da força compressiva de dentes decíduos restaurados com onlays de compósito e analisar os padrões de fratura produzidos quanto ao grau de severidade. No estudo 1, a amostra foi constituída de quarenta molares decíduos hígidos, restaurados com restaurações indiretas tipo onlay de compósito resinoso, divididos em grupos conforme os dois fatores de variação estabelecidos para o estudo: irrigação com (NaOCl 1%) e agentes de fixação resinosos (EnForce e Rely X). Para a análise da adaptação marginal foi aplicada uma solução corante nas margens da restauração, e, as áreas coradas foram consideradas como presença de fendas marginais. O software Image Tool 3.0 foi utilizado para a mensuração linear do comprimento das fendas. No estudo 2, trabalhou-se com a mesma amostra do estudo 1, com o acréscimo do grupo controle composto de dentes hígidos, totalizando cinqüenta dentes. Todos os espécimes foram submetidos ao teste mecânico de compressão, os tipos de fratura foram classificados macroscopicamente quanto aos graus de severidade e os sítios de fratura foram analisados em microscopia eletrônica de varredura a título de ilustração. No estudo 1, não houve diferença estatisticamente significativa quanto à quantidade de fendas encontrada entre os grupos (p>0.05), porém, o risco relativo de ausência de fenda revelou que alguns grupos apresentaram maior chance de ausência de fenda que outros, sendo que o grupo com maior risco relativo foi o grupo tratado com hipoclorito e fixado com EnForce (RR=1.56). No estudo 2, não houve diferença quanto aos valores de força compressiva entre os grupos estudados (p>0.05), consequentemente, os grupos experimentais apresentaram recuperação da resistência à compressão, alcançando valores que não diferiram daqueles do grupo controle. Quanto ao grau de severidade das fraturas, os grupos experimentais mostraram os tipos mais severos de fratura, enquanto o grupo controle apresentou os tipos menos severos. Assim, a técnica restauradora indireta de compósitos resinosos em dentes decíduos com preparos cavitários complexos e submetidos à simulação do procedimento de irrigação endodôntica, apresentou adequada adaptação marginal inicial e foi capaz de recuperar a resistência à carga compressiva em relação aos dentes hígidos / Abstract: The indirect restorations are an interesting restoration procedure in the pediatric dentistry clinic, because this leads to a reduced chairside time, besides would decrease polymerization shrinkage due to the resin luting agent lower volume. To endodontically treated teeth, the performance of adhesive restorations has already not been established, and this is extremely important since if restorations upon crowns failures, the pulp therapy can be lost. Then, the objectives presented in the dissertation form based in two articles were: (1) to evaluate the earlier marginal adaptation of onlay composite restorations in primary teeth subjected or not to 1% sodium hypochlorite (1% NaOCl) irrigation and bonded with two types of resin luting agents (EnForce e Rely X); (2) to evaluate the compressive strength of experimental groups studied in the first research and compare them with the sound teeth, besides to evaluate the types of fractures regarding to severity degree. In the first study, the sample was accomplished by forty sound molars restored with indirect onlay composite restorations. The teeth were divided into groups according the two factors of variations established in this study: 1% NaOCl irrigation and resin luting agents (EnForce and Rely X). To analyze the marginal adaptation a dye solution was applied upon restorations margins, and the dyed margins were considered as marginal gaps presence. TheImage Tool 3.0 software was used to measure the linear length. In the second study, the same sample of the study 1 was used with the addition of the control group accomplished the sound teeth, with the total of 50 teeth. All specimens were subjected to compression mechanic test, and the fractures types were macroscopically classified related to the severity degree. In the first study, there were no statistically difference related quantity of gaps among the groups (p>0.05), however, some groups showed the relative risk tendency of no gap higher than others, and the group treated with NaOCl and fixed EnForce (RR=1.56) produced the higher relative risk tendency. In the second study, there were no statistically differences related to compressive force values among any studied groups (p>0.05), consequently, the experimental groups had similar values to sound teeth. Concerning the severity of fractures, the experimental groups showed the most severe types of fractures, while the control group showed the lower severe types. Then, the composite indirect restored technique showed acceptable earlier marginal adaptation and recovery of the compressive strength of teeth with complex prepares and submitted to endodontic irrigation procedure / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientador: Alexandre Augusto Zaia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:22:25Z (GMT). No. of bitstreams: 1 Almeida_JoseFlavioAffonsode_M.pdf: 1181131 bytes, checksum: 0782b1ca6fa876770da95f2cac650895 (MD5) Previous issue date: 2005 / Resumo: Este estudo teve como objetivo avaliar capacidade de escoamento, obturação e selamento marginal contra infiltração de corantes em canais laterais artificialmente produzidos em dentes humanos, utilizando seis diferentes cimentos empregados em Endodontia (Pulp Canal Sealer (EWT), Endométhasone, Target H&D, Sealapex, Sealer 26 e AH Plus). O escoamento dos cimentos foi testado seguindo as normas internacionais n.° 57 da American Dental Association (ADA) e 6876 da International Organization for Standardization (ISO). Com auxílio de brocas de 0,1mm de diâmetro, dois canais laterais foram confeccionados em 82 raízes dentais, sendo um no terço médio e outro no terço apical do canal radicular. As raízes foram obturadas com a técnica da condensação lateral e radiografadas digitalmente no sentido vestíbulo-lingual. Após 48h, as raízes foram imersas em tinta nanquim por 24h e diafanizadas. Os testes de escoamento dos cimentos demonstraram que os cimentos Pulp Canal Sealer (EWT), AH Plus e Target H&D foram capazes de cumprir com as recomendações 57 da ADA e 6876 da ISO. Os cimentos Sealapex e Sealer 26 cumpriram com a recomendação da ADA mas não cumpriram com a ISO. O Endométhasone não apresentou o escoamento mínimo exigido pelas duas recomendações. Os preenchimentos dos canais laterais analisados através de radiografia digital, diafanização e infiltração de corantes apresentaram índices estatisticamente semelhantes para todos os cimentos testados. A comparação estatística entre os índices de infiltração de corante dos cimentos demonstrou que os cimentos AH Plus e Sealapex permitiram menos infiltração do que o cimento Pulp Canal Sealer (EWT). A análise radiográfica não foi eficiente em demonstrar a obturação dos canais laterais artificiais em aproximadamente 20% dos casos. As taxas de escoamento requeridas pelas normas 57 da ADA e 6876 da ISO não demonstraram relação direta com a capacidade dos cimentos testados em obturar canais laterais artificiais de 0,1mm de diâmetro / Abstract: The aim of this study was to evaluate the flow rate, the filling and dye leakage in artificial lateral canals using 6 different sealers (Pulp Canal Sealer (EWT), Endométhasone, Target H&D, Sealapex, Sealer 26 e AH Plus). The flow rate was analyzed through 57 American Dental Association (ADA) and 6876 International Organization for Standardization (ISO) specifications. Two lateral canals were produced in the medium and apical third of 82 dental roots with 0,1mm drills. Lateral condensation and the sealers were used to fill the root canals and buccolingual digital radiographs were performed. After 48h the roots were immersed in Indian ink and cleared in methyl salicylate. Pulp Canal Sealer (EWT), AH Plus and Target H&D were able to accomplish with 57 ADA and 6876 ISO specifications. Sealapex and Sealer 26 accomplished with 57 ADA specification but not with 6876 ISO. Endométhasone were not able to accomplish with any specifications. Lateral canal fillings evaluated by radiograph, clearing technique and dye leakage were statistically similar for the 6 sealers tested. The dye leakage demonstrated that AH Plus and Sealapex permitted less leakage than Pulp Canal Sealer (EWT). This data were statistically significant. The radiograph was not able to demonstrate the filling of lateral canal in approximately 20%. There is no correlation of the flow rate required by the 57 ADA and 6876 ISO specifications and the sealers ability to fill 0.1mm artificial lateral canals / Mestrado / Endodontia / Mestre em Clínica Odontológica

Orientador: Milton Carlos Kuga / Resumo: Os objetivos dos estudos foram avaliar os efeitos da cimentação provisória intrarradicular de um pino metálico com cimentos temporários, de composição química diferentes, e analisar a influência da irrigação com agitação ultrassônica passiva (PUI), sobre a resistência de união do cimento resinoso autoadesivo (Relyx U200) na dentina do espaço radicular preparado para pino de fibra de vidro. Noventa raízes unirradiculares de dentes humanos, foram padronizadas com o comprimento de 17,0 mm, a partir do ápice radicular. Os canais radiculares foram instrumentados até o instrumento F5, irrigados a cada troca de instrumento com 5 mL de hipoclorito de sódio a 2,5% e obturados com cimento contendo resina epóxi (AH Plus; Dentsply DeTrey GmbH, Konstanz, GER). Após 7 dias, foi preparado o espaço intrarradicular para pino de fibra de vidro, na extensão de 11mm, a partir da face cervical radicular, com brocas tipo Largo #1 e #2, e dada a conformação final com a broca #2 do sistema White Post DC (FGM, Joinville, SC, BR). No estudo 1, quarenta espécimes foram distribuídos em 4 grupos (n =10), de acordo com o tipo de protocolo de cimentação provisório do pino metálico: G1 (CO), sem a realização prévia da cimentação provisória do pino metálico intrarradicular; G2 (PR), cimentação provisória do pino metálico com o sistema Provy (Dentsply); G3 (RT) cimentação provisória do pino metálico com o sistema Relyx Temp NE (3M) e G4 (TB), cimentação provisória do pino metálico com o sistema Temp Bond NE (... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aims of this study are to evaluate the effects of temporary intraradicular cementation of a metallic pin with temporary cements made from different chemical composition, and to analyze the influence of agitation with passive ultrasonic irrigation (PUI) on the bond strength of the self-adhesive resin cement (Relyx U200) in the root space dentin prepared for fiberglass pin. Ninety one-root human teeth were standardized with a length of 17.0 mm from the radicular apex. The root canals were instrumented up to instrument F5, irrigated at each instrument change with 5 mL of 2.5% sodium hypochlorite and filled with cement containing epoxy resin (AH Plus; Dentsply DeTrey GmbH, Konstanz, GER). After 7 days, the intraradicular space, 11mm in length, was prepared for the fiberglass pin, from the root cervical face with Largo # 1 and # 2 drills, and given the final conformation with the drill # 2 from White Post DC system (FGM, Joinville, SC, BR). In study 1, forty specimens were distributed into 4 groups (n = 10), according to the type of provisional cementation protocol of the metal pin: G1 (CO), without executing beforehand the provisional cementation of the intraradicular metallic pin; G2 (PR), provisional cementation of the metallic pin with Provy system (Dentsply); G3 (RT) temporary cementation of the metallic pin with Relyx Temp NE (3M) and G4 (TB) system, provisional cementing of the metallic pin with Temp Bond NE system (Sybron Kerr). In all groups, with exception of CO, met... (Complete abstract click electronic access below) / Mestre

Orientador: Eduardo Dias de Andrade / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-20T07:25:27Z (GMT). No. of bitstreams: 1 Selber_AndreaCosta_M.pdf: 2436633 bytes, checksum: 14f5679d235d598b8143e5f645e4f6dd (MD5) Previous issue date: 1994 / Resumo: O presente trabalho teve como finalidade avaliar a biocompatibilidade histológica de um cimento cirúrgico fotopolimerizável (Barricaid 'MARCA REGISTRADA') em tecido subcutâneo de ratos, comparando-o com o cimento de óxido de zinco e eugenol e tendo como material controle, a esponja de PVC, implantados subcutaneamente em ratos. Os animais foram distribuídos aleatoriamente em grupos, no dorso dos quais foram introduzidos os materiais citados, denominados de corpos de prova. Nos tempos de: 3, 6 e 14 dias pós-implantação dos corpos de prova, os animais foram sacrificados e, então foram removidos espécimes do tecido contendo o material implantado. As peças foram submetidas ao processamento histológico de rotina e as lâminas assim obtidas, foram examinadas ao microscópio óptico. Os resultados obtidos demonstraram que o Barricaid 'MARCA REGISTRADA') constitui uma alternativa viável para aplicação clínica, já que as reações teciduais por ele causadas foram menos intensas em todos os períodos de tempo analisados, em relação ao cimento a base de óxido de zinco e eugenol / Abstract: This experiment's purpose is to investigate the histological biocompatibility of the visible-light-cure periodontal dressings (Barricaid 'TRADEMARK'), implanted in the subcutaneous tissue of Wistar rats and compare it with zinc oxide-eugenol mixtures, PVC sponge wich were subcutaneously implanted, as well. The last were supposed to be inert and served as control materiais. The animais were randomly grouped, the materiais being introduced in theirs dorsal region, were designated - wounds. Rats were sacrificed on dates 3, 6 and 14 days post implantation, during when the materiais were surgically collected with the surrounding subcutaneous tissue. The specimens were histologicaly processed and examined on the optic microscope. Results showed Barricaid 'TRADEMARK' to be a viable altemative for clinical application as far as foreign body reaction found was less intense than produced by the control material / Mestrado / Farmacologia / Mestre em Odontologia