Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The restoration of endodontically treated teeth have been a challenge for restorative dentistry because usually the amount of remaining coronal dentin of these teeth are not enough to retain the restorative material, requiring the use of intra-radicular posts to provide retention for the core and restorative crown. This study aimed to evaluate the effect of rehabilitation protocols of endodontically treated teeth for the comparison of in vivo and simultaneous in vitro tests, employing mechanical tests and computational by finite element method; also aims to validate the computational and experimental testing laboratory through comparative analysis with clinical parameters. This study was divided into four specific objectives; specific objective 1: to evaluate the influence of the surface treatments of fiberglass posts on bond strength to root dentin using push-out test; specific objective 2: to develop protocol and validate the generation of three-dimensional patient specific model of anterior central incisors with different ferrule design restored with glass fiber post and CAD- CAM all-ceramic restoration using cone-beam computed tomography and specific software combination for finite elements analysis; specific objective 3: to evaluate the strain before and after thermo-mechanical fatigue aging, the fracture resistance and fracture mode of endodontically treated incisors restored using a fiberglass post and CAD/CAM all ceramic crown with and without ferrule; specific objective 4: generate manuscript that summarize the main findings of specific objective 1, 2 and 3 designated to Brazilian clinical fulfilling the social function of knowledge generation. After analyzing the results it can be concluded that the post surface treatment with 24% hydrogen peroxide for 1 min yielded significantly higher bond strength on the fiberglass posts cementation. The definition of protocol of individualized models provided the sequence necessary for the application of the methodology on patient, the stress distribution on evaluated teeth showed that stresses on left incisor, which had no-uniform ferrule were higher compared with the right incisor, regardless of the loading method. The maintenance of uniform ferrule was more relevant than localized higher ferrule. The ferrule presence prevented the post detaching maintain the root dentin strain after thermal-mechanical aging. The no ferrule group showed increase root dentin strain after aging process. The ferrule group had higher fracture resistance, lower stress concentration on root dentin and 14 less catastrophic fractures. The use of glass fiber post associated to the all ceramic crown allowed the restoration of biomechanics aesthetics and functionality of endodontically treated tooth with periodontal intervention in order to achieve a favorable condition for the restorative procedures. / A restauração de dentes tratados endodonticamente têm sido grande desafio para a odontologia restauradora. Geralmente, estes dentes apresentam estrutura coronária insuficiente para reter o material restaurador, sendo necessária a utilização de retentores intrarradiculares para viabilizar a reconstituição coronária. Este trabalho tem como objetivo geral analisar o efeito do protocolo restaurador de dente tratado endodonticamente por meio de avaliação comparativa in vivo e simultânea in vitro, empregando ensaios mecânicos e computacionais pelo método de elementos finitos. Visa ainda validar os ensaios computacionais e ensaios experimentais laboratoriais por meio de análise comparativa com parâmetros clínicos. Este estudo foi dividido em quatro objetivos específicos; objetivo específico 1: avaliar a influência do tratamento de superfície de pinos pré-fabricados na resistência de união de pino ao canal radicular, por meio de teste de micropush-out; objetivo específico 2: desenvolver e validar a geração de modelos tridimensionais específicos de paciente com incisivos centrais anteriores com diferente tamanho de férula, restaurados com pino de fibra de vidro e coroa em cerâmica pura CAD/CAM usando tomografia computadorizada Cone-beam (CT) e combinação de softwares específicos de elementos finitos; objetivo específico 3: avaliar a deformação antes e após ciclagem térmica e mecânica, resistência à fratura e padrão de falha de incisivos tratados endodonticamente restaurados com pino de fibra de vidro e coroa total em cerâmica pura CAD/CAM com e sem férula; objetivo específico 4: gerar síntese dos achados dos objetivos específicos 1, 2 e 3 compilados em um artigo de comunicação aos clínicos brasileiros cumprindo a função social da geração do conhecimento. Após análise dos resultados pode-se concluir que o tratamento de superfície com 24% de peróxido de hidrogênio por 1 minuto resultou em significativamente maior resistência de união na cimentação de pinos de fibra de vidro. A definição do protocolo de modelagem individualizada forneceu as etapas necessárias para a aplicação da metodologia em paciente. A distribuição de tensões mostrou que as tensões geradas no incisivo que não possui férula uniforme, foram maiores em comparação a incisivo com maior extensão de férula independentemente do método de carregamento. A manutenção de férula uniforme foi mais relevante do que maior extensão da férula em uma 11 região específica do preparo. A presença de férula evitou o descolamento do pino de fibra da dentina radicular após fadiga térmica e mecânica. O grupo sem férula apresentou maior deformação radicular após processo de envelhecimento. O grupo com férula apresentou maiores valores de resistência à fratura, baixa concentração de tensões na dentina radicular e menor índice de fraturas catastróficas. O uso de pino de fibra de vidro associado à coroa em cerâmica pura permitiu o restabelecimento da estética e funcionalidade biomecânica do dente tratado endodonticamente com intervenção periodontal voltada aos tecidos de revestimento que possibilitou um recontorno gengival adequado para realização dos procedimentos restauradores. / Doutor em Odontologia

Orientador: Guilherme Elias Pessanha Henriques / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:52:52Z (GMT). No. of bitstreams: 1 Torres_JoseWalterMurta_M.pdf: 1252099 bytes, checksum: 8a9ecb06692b975d77a7808edbe5eeec (MD5) Previous issue date: 2005 / Resumo: Padrões de fundição de restaurações protéticas metálicas são usualmente confeccionados em cera. Todavia, especula-se que possa haver aumento nos valores de desajuste marginal, causado por alterações dimensionais ocorridas quando da remoção dos padrões previamente à inclusão em revestimento. Assim, a resina acrílica quimicamente ativada tornou-se uma opção e seu uso rotineiro em laboratórios comerciais. O titânio possui propriedades como biocompatibilidade, baixa condutividade térmica, baixo custo e alta resistência mecânica, tornando-se o material preferido para implantes e o foco de inúmeros estudos visando seu uso em restaurações e coroas protéticas. Visando o menor desajuste marginal possível é recomendado pelo fabricante do sistema de fundição de titânio o uso de cera para a confecção dos padrões, não havendo avaliações do uso de resina acrílica para este fim. Foi propósito deste estudo comparar o desajuste marginal de coroas unitárias fundidas em titânio comercialmente puro (Ti CP - Tritan; Dentaurum, Alemanha), utilizando-se cera (como controle) e as resinas acrílicas Duralay (Reliance Dental Mfg, Co., EUA) e Pattern Resin (GC America Inc., EUA) na confecção dos padrões. Dez dentes bovinos foram preparados para restaurações tipo coroa total, moldados com silicone e replicados em gesso tipo IV. Dez padrões de fundição com 0,7 mm de espessura foram confeccionados para cada grupo (n=10). As coroas foram fundidas em titânio comercialmente puro em máquina de fundição por plasma e vácuo. Após a fundição, as coroas foram removidas do revestimento e ajustadas nos troquéis e nos dentes correspondentes. Para a leitura dos desajustes marginais foi utilizado um microscópio de medição com precisão de 0,5µm, sendo efetuadas 3 leituras em cada conjunto padrão/dente preparado. Os valores obtidos foram tabulados e submetidos à análise de variância e ao teste de Tukey ao nível de 5% de probabilidade. Foram verificados desajustes de 151µm para as coroas fundidas a partir dos padrões em cera, de 153µm para os padrões obtidos em resina Duralay e de 165µm para as fundições obtidas por padrões em resina Pattern. Não foram verificadas diferenças significativas entre os grupos avaliados, estando estes dentro de valores próximos a 150µm / Abstract: Patterns for casting metallic restorations are usually obtained from wax. However, it is speculated that increased marginal misfits could be created caused by dimensional changes during the removal of the pattern from the cast. Therefore, chemically activated acrylic resin is a routinely option in dental commercial laboratories. The characteristics of titanium include biocompatibility, low thermal conductivity, low cost and high mechanical resistance becoming the material of choice for implants and the focus of innumerous studies in prosthetic field such as crowns. To obtain the lowest marginal misfit in crowns, it is recommended that titanium appliances should be cast using wax as pattern, with no evaluation on the use of acrylic resin for this purpose. The aim of this study was to compare the marginal adjustment of crowns cast in commercially pure titanium (CP Ti - Tritan; Dentaurum, Germany)using wax (control), and the acrylic resins Duralay (Reliance Dental, Mfg Co., USA) and Pattern Resin (GC America Inc., USA) as patterns. Ten bovine teeth were prepared for full crown restorations. Impressions were made in silicone material and replicated in type IV dental stone. Ten 0.7 mm-casting patterns were made for each groups. The crowns were cast in CP Ti in a plasma-vacuum casting machine. After casting, the crowns were removed from the investment and adjusted on the respective preparation. For the marginal misfit readings, a 0.5µm-traveling microscope was used. Three readings were taken from each crown-preparation interface. The means were calculated and submitted to analysis of variance and Tukey test at 5% probability lever. Misfits of 151µm were obtained for the crowns cast using wax as patterns; 153µm when Duralay was used; and, 165µm for the crowns made from Pattern Resin. No significant differences were seen among the groups, and the values about 150µm / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Frederico Andrade e Silva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T12:24:23Z (GMT). No. of bitstreams: 1 Figueiro_Claudio_D.pdf: 2289324 bytes, checksum: a3194128299d48f7fd83c7c0526aa845 (MD5) Previous issue date: 2001 / Resumo: Este estudo avaliou a influência da convergência axial e do alivio interno na adaptação e resistência à tração de coroas totais cimentadas com o cimento resinoso Scothbond (3M) e com o cimento Enforce com Flúor (Dentsply). Foram realizados preparos padronizados do tipo coroa total em 160 dentes incisivos bovinos, nos quais foram confeccionadas coroas metálicas em NiCr. Foram formados oito grupos de acordo com: convergência axial (24° e 32°), utilização de alívio e agente cimentante utilizado. As coroas foram cimentadas seguindo as orientações dosífabricantes, utilizando uma carga estática de 9 Kgf durante 2 minutos. Os corpos-de-prova receberam uma ciclagem térmica (1500 ciclos nas temperaturas de 5°C ± 2°C e 550C ± 2°C). Metade das coroas foram seccionadas longitudinalmente utilizando um disco diamantado, no seu terço médio no sentido vestíbulo-lingual. As faces obtidas foram incluídas em resina acrílica autopolimerizável, sendo posteriormente realizado polimento com lixas d'água em uma politriz de bancada. A adaptação das coroas foi medida em um microscópio comparador (Leitz) com o aumento de 40X, e a resistência à tração foi medida em uma máquina de testes Universal (Instron). Os resultados foram agrupados e submetidos à uma análise de variância. O resultado da análise de variância mostrou-se significante ao nível de 5%, sendo realizado o teste de Tukey para a comparação das médias. Conforme a metodologia adotada concluiu-se que: 1) o aumento da convergência axial de 24° para 32°, melhorou a adaptação das coroas totais; 2) a utilização de alívio interno nas coroas totais melhorou a adaptação cervical; 3) o cimento resinoso Scotchbond proporcionou uma melhor adaptação cervical nas coroas totais quando comparado com o cimento Enforce; 4) o aumento da convergência axial de 24° para 32°, diminuiu a resistência à tração do cimento Scotchbond; 5) a utilização de alivio interno nas coroas totais diminuiu à resistência à tração das mesmas; 6) na convergência de 24°, o cimento Scotchbond apresentou maior resistência à tração quando comparado com o cimento Enforce / Abstract: The objective of this study was to evaluate the influence of axial convergence and relief on the marginal adaptation and retention of cemented complete crowns with Scothbond resin cement (3M) and Enforce resin cement (Dentsply). Sixteen hundred recently extracted bovine incisors were prepared to receive full cast crows, standardized preparations were made and the crows were made in a Ni-Cr alloy. Eight groups were formed according to: axial convergence (24° and 32°), relief and luting agent. The crowns were cemented according to the manufacturer's instructions, utilizing a 9 Kg static 1000 for two minutes. The specimens were thermocycled for 1500 cycles (5°C:t 2°C e 55°C ± 2°C). The crowns were sectioned with a diamond disk and polished. The marginal aptation was measured using a microscope with 40X of magnification (Leitz). The results were submitted to the ana1ysis of variance (ANOV A). The results of analysis were significant at the 5% leveI, and the Tukey multiple comparisons test was applied at the 5% leveI of significance. We concluded: 1) the crown adaptation was improved with the increase ofthe convergence ofthe 24° to 32°; 2) the crown adaptation was improved with the relief; 3) the crown adaptation was improved with scotchbond resin cement when it was comparable to enforce resin cement; 4) the increase of the convergence ofthe 24° to 32° decreased the crown retention to scotchbond resin cement; 5) The relief decreased the crown retention; 6) the crown retention was improved on axial convercence of24° to scotchbond resin cement when comparable to enforce resin cement / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T16:28:47Z (GMT). No. of bitstreams: 1 Milan_FabioMachado_D.pdf: 3799523 bytes, checksum: 960ea09ac8d14a32a84c0b7a5b037d32 (MD5) Previous issue date: 1999 / Resumo: Considerando as dificuldades técnicas existentes na confecção de restaurações fundidas, onde o mínimo desajuste acarreta sérios problemas clínicos futuros, este trabalho visou analisar o ajuste cervical e interno de coroas totais metálicas sem e com alívio interno (espaçador de troquei, ataque químico com ácido nítrico e jateamento com partículas de óxido de alumínio), confeccionadas com liga de paládio/prata (Pors-on 4), com três diferentes tipos de término cervical: ombro reto, ombro biselado em 20° e chanfro reto em 45°. Para fusão da liga foram utilizadas duas fontes de calor de fundição: gás-oxigênio e resistência elétrica. Após a fundição, as coroas foram assentadas sobre seus respectivos troquéis, sob carga estática de 9 kg. As leituras do desajuste cervical e da interface troquei-coroa das secções transversais foram realizadas em microscópio metrológico (Carl Zeiss), provido de um relógio comparador digital, série 543 IDF (Mitutoyo). Os resultados foram submetidos à análise de variância e ao teste de Tukey (5%) e demonstraram que: os melhores ajustes cervical e interno foram obtidos com a fonte de calor de fundição gás-oxigênio; independente de todos fatores analisados, o término cervical em chanfro reto de 45° apresentou os melhores ajustes, tanto cervical como interno; e, o melhor alívio interno foi o realizado na pós-fundição com jateamento com óxido de alumínio / Abstract: Regarding the existenting difficulties in making casting restorations, where the minimal cervical discrepancy lead to a future serious clinical problems, this research will analyse the cervical and internal fits of total metal crowns with or not internal relief (die-spacing, acid conditioning and sandblaster with aluminiun oxide), making with palladium-silver alloy (Pors-on 4), with three different marginal configurations: shoulder, 20-degree bevel shoulder and 45-degree chamfered, on the stainless steel dies. To cast the alloys, two heat sources have been used: gas-oxygen and eletric resistance. After the casting, the specimens were seated on the dies, with a static load of 9 kg. The reading of the cervical fit and die/crown interface was made on a metric microscope (Carl Zeiss), using a digital micrometer (Mitutoyo). The results were submitted to analysis of variance and Tukey's test (5%), indicated that the better cervical and internal fits were obtained with the heat source gas-oxigen; the marginal configuration 45-degree chamfer showed the highest fit cervical and internal; and, the better internal relief was sandblaster with aluminium oxide / Doutorado / Doutor em Materiais Dentários

Orientador : Luis Alexandre Maffei Sartini Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T23:36:23Z (GMT). No. of bitstreams: 1 CarliniJunior_Bruno_D.pdf: 4989185 bytes, checksum: 746f907f11f3e05fc033d327df974b66 (MD5) Previous issue date: 2001 / Resumo: O objetivo deste trabalho foi avaliar o padrão e a resistência à fratura de dentes bovinos tratados endodonticamente e restaurados através de coroas unitárias metálicas nas seguintes condições experimentais: presença ou não de remanescente dental coronário com 2 mm de comprimento; término gengival em ombro-biselado, chanfrado e ombro; e dois métodos de retenção intra-coronária, núcleo metálico fundido e pino metálico pré-fabricado paralelo rosqueado. Cento e vinte raízes bovinas receberem tratamento endodôntico e foram fixadas em cilindros de resina acrílica por meio de ligamento periodontal artificial para serem submetidas ao carregamento tangencial de compressão a 0,5 mm/min e 135°, até ocorrer a fratura. Os resultados (ANOVAI DMMQ a=0,05) demonstraram que houve diferença estatística para as condições término gengival (ombro biselado >=chanfrado> ombro), retenção intra-radicular (pino pré-fabricado> núcleo metálico fundido) e presença de remanescente coronário (com remanescente> sem remanescente); bem como para as interações remanescente x pino e remanescente x término, em que os grupos com remanescente apresentaram valores superiores aos grupos sem remanescente, com diferença estatística significativa. Foi possível concluir que a resistência mecânica de raízes reconstruídas proteticamente tem relação com a quantidade de remanescente coronário, método de retenção intra-radicular e formato de término gengival / Abstract: The aim of this study was to evaluate both the pattern and the fracture strength of bovine teeth endodontically treated through metallic unitary crowns under the following experimental conditions: presence or not of dental coronal structure with 2mm in length; cervical beveled shoulder, chamfered and shoulder; and two methods of intraradicular retention, cast post and core and parallel threaded prefabricated metallic posts. Endodontically treated 120 bovine dental roots were fixed to acrylic resin cylinders by means of artificial periodontal ligament, and then submitted to the compressive strength, at 1350 and 0,5 mm/min, until reaching the fracture. The results (ANOVA/ DMMQ a=0,05) showed statistical significance for the following conditions: cervical prosthetic design (beveled sholder >=chanfer > sholder), intraradicular retention (prefabricated posts > cast post and core) and coronal structure (with 2 mm of coronal structure > without dental structure); It was possible to conclude that the mechanical resistance of the restored roots is correlated with the amount of coronary dental structure, the intra-radicular retention method, and the prosthetic gingival shape / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Wilkens Aurelio Buarque e Silva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T18:40:10Z (GMT). No. of bitstreams: 1 Lameira_DeborahPacheco_D.pdf: 11244410 bytes, checksum: 54506eb4da406d4e27116632cc014de5 (MD5) Previous issue date: 2014 / Resumo: O objetivo deste estudo foi avaliar a resistência à fratura de coroas monolíticas e bicamada a base de zircônia, após envelhecimento artificial. Para este estudo, foram utilizados 32 incisivos bovinos onde foram feitos preparos de coroa total. Estes foram escaneados para a confecção de coroas a base de a zircônia tetragonal parcialmente estabilizada por ítrio (yttrium partially stabilized tetragonal zirconia polycrystalline Y-TZP), por um sistema CAD/CAM (computer-aided design and computer-aided manufacturing). As coroas foram fabricadas de acordo com os grupos experimentais (n=10/grupo): Coroa monolítica de zircônia polida PM (1.5mm de espessura); Coroa monolítica de zircônia com aplicação de glaze GM (1.5mm de espessura); Coroa bicamada com coping de zircônia BL (0.8mm de espessura) com cerâmica de cobertura (0.7mm de espessura). As coroas foram cimentadas nos respectivos preparos com cimento resinoso (RelyX Unicem-2, 3M-ESPE). Após a cimentação, as amostras foram submetidas ao envelhecimento artificial em uma simuladora de mastigação (2,5 milhões de ciclos/3Hz de frequência/8kg) em saliva artificial a 37°C, em seguida foi efetuado o teste de resistência à fratura em maquina Instron, com velocidade de 0,5 mm/min. Duas coroas remanescentes referente a PM e GM foram submetidas a análise estrutural Electron probe microanalysis (EPMA), para medir o nível de ítrio após o envelhecimento. Os resultados foram submetidos a Análise de Variância e teste de Tukey (p=0.05). O modo de fratura foi avaliado por meio de Microscopia Eletrônica de Varredura (MEV). As coroas de zircônia monolíticas apresentaram resultados semelhantes de resistência à fratura (PM = 3476,2N ± 791,7; GM = 3561,5N ± 991,6), que foram maiores (p=0,02) do que os resultados para as coroas bicamada (BL = 2060,4N ± 810,6). Não houve diferença significativa na quantidade de ítrio entre as superfícies oclusais desgastas (PM, GM), e na superfície não desgastada de PM. Destes modo, a resistência à fratura de coroas monolíticas foi maior do que de coroas na configuração bicamada / Abstract: The purpose of this study was to evaluate the fracture strength and failure mode of zirconia crowns in monolithic or bi-layer configuration after artificial aging. Thirty-two bovine incisors received crown preparation and were scanned for the manufacturing of Y-TZP crowns using CAD/CAM technique. Crowns were fabricated according to the following groups (n=10/group): PM polished monolithic zirconia crowns of 1.5mm uniform thickness; GM glazed monolithic zirconia crowns of 1.5mm uniform thickness; BL bi-layer crowns with 0.8mm zirconia core and 0.7mm of veneered porcelain. All crowns were cemented on each respective tooth with resin cement (RelyX Unicem-2, 3M-ESPE). After the cementation, specimens were submitted to artificial aging in a chewing simulator (2.5 million cycles/ 3Hz frequency/8kg) in artificial saliva at 37°C, then the samples were submitted to fracture strength test (Instron) at a crosshead speed of 0.5mm/min. Two remaining crowns referring to PM and GM were submitted to Electron probe microanalysis (EPMA), to measure the yttrium levels after aging. One-way ANOVA and Tukey¿s test (p=0.05) were employed for analysis of the results. The fracture mode was evaluated with Scanning Electron Microscope (SEM). Monolithic zirconia crowns presented similar fracture strength results (PM= 3476.2N ± 791.7; GM= 3561.5N ± 991.6), which were higher (p=0.02) than the results for the bi-layer crowns (BL= 2060.4N ± 810.6). There was no significant difference in the yttrium content among worn occlusal surfaces (PM, GM) and undamaged surface in PM. Thus, the fracture strength of monolithic zirconia crowns was higher than bi-layer configuration / Doutorado / Protese Dental / Doutora em Clínica Odontológica

Orientador: Rafael Leonardo Xediek Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T03:25:43Z (GMT). No. of bitstreams: 1 Carvalho_BrenoCarnevalliFrancode_D.pdf: 2254429 bytes, checksum: 0864903c9e5a5e409b843fd792284ecc (MD5) Previous issue date: 2013 / Resumo: Implantes curtos são utilizados em situações clínicas quando a altura e/ou a espessura óssea são insuficientes. A proposta neste estudo foi verificar por meio da análise de tensão fotoelástica a influência exercida pela altura e largura da coroa protética na força transmitida aos implantes curto (7 mm) e longo (13 mm) quando o carregamento foi efetuado no centro ou na extremidade das coroas. As dimensões da altura e da largura da coroa simulada foram estabelecidas com base nas dimensões de dentes pré-molar e molar inferiores humanos e a espessura estabelecida em 6 mm. O corpo-de-prova de resina fotoelástica foi feito com o sistema bi componente à base de resina epóxi modificada e endurecedor. Os carregamentos foram de 0,4 kgf no centro e de 0,3 kgf numa das extremidade da coroa. A análise fotoelástica avaliando as ordens de franjas ao redor dos implantes foi feita com polariscópio de transmissão. Cada fotografia foi analisada três vezes no programa Fringes para ordens de franja de 0 a 4, considerando as médias da ordem das franjas e da tensão cisalhante para cada ponto estabelecido no modelo. Os dados foram submetidos à ANOVA dois fatores e diferenças estatísticas comparadas pelo teste t de Student em nível de significância de 5%. Os resultados mostraram que não houve diferença entre os níveis de tensões gerados pela altura e largura das coroas protéticas sobre os implantes curto e longo, quando os carregamentos foram feitos tanto no centro como na extremidade das coroas. Concluiu-se que as tensões geradas sobre os implantes curto e longo foram similares qualquer que fosse o tamanho e o local dos carregamentos aplicados sobre as coroas; houve diferença na magnitude da tensão exercida sobre os implantes curto e longo, sendo maior para o implante curto / Abstract: Short implants are used in clinical situations when the mass of bone is deficient in height and/or thickness. The purpose of this study was to verify the height and width crown influence in the stress transmission in short (7mm) and long (13mm) implants when loaded at center and edge of the crown. The simulated crown dimensions were established using a natural premolar and molar crown dimensions and the thickness was 6 mm. The photoelastic models were made using a dual system based on modified epoxi resin and catalyser. The crowns were loaded with 0,4 kgf at the center and 0,3 kgf at the edge. The photoelastic analysis for fringe order around the implants was made using a transmission polariscope. The maximum shear stress and the fringe values from 0 to 4 were determined in each photography measured three times using Fringes software. Two-way ANOVA and t Student test at 5% significance were perfomed. The results showed no difference in the stress levels produced by different height and width crown over the short and long implants when loaded both center and edge of the crowns. In conclusion, the results showed similar stress on the short and long implants regardless the size and the loaded crown area; however, there was statistical difference in the stress level on the implants being higher for the short implant / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T17:46:05Z (GMT). No. of bitstreams: 1 Sicoli_EliseuAugusto_D.pdf: 4658696 bytes, checksum: ce260af08392da02937030d7837080d4 (MD5) Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar o efeito do condicionamento com ácido hidrofluorídrico ( 5 e 10%) e ciclagem térmica na resistência ao microcisalhamento da interface cimento resinoso RelyX ARC - IPS E.max Press. Foram confeccionadas 20 amostras com cerâmica IPS E.max Press de acordo com a recomendação do fabricante. As amostras foram incluídas em tubos de PVC com resina epóxi e divididas em 4 grupos (n=40). Todas as amostras após o condicionamento ácido por 20 segundos foram silanizadas e a confecção dos corpos-de-prova seguiu o mesmo procedimento padrão para a cimentação com RelyX ARC. Os grupos foram separados em: 1- Cerâmica condicionada com ácido hidrofluorídrico a 10%; 2 - Cerâmica condicionada com ácido hidrofluorídrico a 10% e termociclada com 3000 ciclos; 3 - Cerâmica condicionada com ácido hidrofluorídrico a 5% e 4 -Cerâmica condicionada com ácido hidrofluorídrico a 5% e depois termociclada com 3000 ciclos. Após tratamento da superfície da cerâmica foi realizada aplicação de silano RelyX Ceramic Primer. Matrizes de silicone por adição com quatro perfurações de 1 mm de altura por 1 mm de diâmetro foram posicionadas sobre a cerâmica e preenchidas com o cimento RelyX ARC conforme os grupos citados. A fotoativação foi realizada com o aparelho LED UltraLume 5 com 1100 mW/cm2 de irradiância por 40 segundos. As amostras foram mantidas em 100% de umidade relativa a 37°C por 24 horas e levadas a máquina de ensaios Instron para o teste de microcisalhamento com velocidade de 0,5 mm/minuto. Os resultados em MPa (G1: 35,34±5,03; G2: 21,80±6,39; G3: 33,28±7,57; G4: 19,39±5,06) foram submetidos a análise de variância e as médias ao teste de Tukey (p<0,05). A análise estatística mostrou valor de resistência de união ao microcisalhamento significativamente superior para os grupos 1 e 3 (sem ciclagem térmica). Houve diferença estatisticamente significante em relação à concentração do ácido hidrofluorídrico com menor resistência ao microcisalhamento na concentração 5%. Não houve diferença estatística na interação entre os grupos. A análise do padrão de fratura mostrou predominância de fraturas adesivas em todos os grupos; embora os grupos 1 e 3 apresentassem fraturas do tipo coesiva no cimento em maior porcentagem quando comparados aos grupos 2 e 4. Assim concluiu-se que a ciclagem térmica diminuiu a resistência ao microcisalhamento da união adesiva, independentemente da concentração do ácido hidrofluorídrico e as falhas foram predominantemente adesivas / Abstract: The aim of this study was to evaluate the resistence to microshear bond strength from the bonding of cement ceramic IPS E.max Press with resin cement Rely X ARC under etching surface effect with hydrofluoridric acid in concentrations of 5% and 10%. The problems faced in the groups were also analysed. Twenty samples of ceramic were produced according to the manufacturer recommendation. The samples were included in PVC tubes with epoxi resin and separated in 4 groups (n=40). After the etching with acid for 20 seconds, the samples were silanized and the same cementing procedure was done with Rely X ARC. The groups were separated in: 1- Ceramic conditioned with hydrofluoridric acid in 10%; 2- Ceramic conditioned with hydrofluoridric acid in 10%, thermocycled in 3000 cycles with temperature between 5°C and 55°C and baths of 30s in each temperature; 3- Ceramic conditioned with hydrofluoridric acid in 5% and 4- Ceramic conditioned with hydrofluoridric acid in 10%, thermocycled in 3000 cycles with temperature between 5°C and 55°C and baths of 30s in each temperature. After the ceramic surface etching it was applied silane RelyX Ceramic Primer using microbrush. Silicone rubber matrices with four perfurations, 1 mm of thickness by 1 mm of diameter each, were put on the ceramic and fulfilled with Rely X ARC cement. The light activation was done using LED UltraLume 5 with 1100 mW/cm2 irradiation acting for 40 seconds. The samples were stored in environment with 100% relative humidity and 37°C for 24 hours. After this period they were submitted to the resistence test of microshear bond strength in the Instron equipament under 0,5 mm/minute of speed. The results in MPa (G1: 35.34±5.03; G2: 21.80±6.39; G3: 33.28±7.57; G4: 19.39±5.06) were submitted to analysis of variance and Tukey's test (p<0,05). The microshear bond strength resistence was significantly bigger for groups 1 and 3 (without thermocycling). There was statistically significant difference as to hydrofluoridric acid concentration. The concentration with 5% presented lower resistence to the microshear bond strength. The standard fracture analysis showed predominance of adhesive problems in all groups although groups 1 and 3 showed cohesive fractures in the cement with the biggest percentage when compared to groups 2 and 4. This way in conclusion the thermocycling decrease the resistence to microshear of the Bond union,independent of the hydrofluoridric acid concentration and the adhesive failures was predominant / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientadores: Marcelo Giannini, Pascal Magne / Tese (Doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T22:55:10Z (GMT). No. of bitstreams: 1 Carvalho_AdrianaOliveira_D.pdf: 96375930 bytes, checksum: 98085bf2a4f1941f9510f1ba4c7d0a85 (MD5) Previous issue date: 2013 / Resumo: Objetivos: Comparar a resistência à fadiga (RFAD) e à fratura (RFRA), o modo de falha e o desgaste do antagonista em contato com os diferentes designs de coroas CAD/CAM utilizadas para restaurar molares tratados endodonticamente/TE ou não, fabricadas em cerâmica feldspática/FEL, dissilicato de lítio/DL ou resina nano cerâmica/RNC e fixadas com cimento resinoso auto-adesivo. Materiais e Métodos: Para os capítulos um e dois, 90 molares foram preparados e restaurados com coroas com espessura de 1,5mm ou 0,7mm respectivamente, em FEL, DL ou RNC. Para os capítulos três e quatro, outros 90 molares tiveram a porção coronária removida (nível da junção cemento-esmalte), foram TE e restaurados utilizando três diferentes designs de núcleo de preenchimento em resina composta/NPRC (4-mm de altura, 2-mm ou sem núcleo de preenchimento/endocrown) associados a coroas em RNC ou DL respectivamente. Para o capítulo cinco, grupos dos capítulos um (RNC/1,5mm e DL/1,5mm), três (NPRC de 4-mm de altura/RNC) e quatro (NPRC de 4-mm de altura/DL) foram combinados. Todas as coroas do estudo foram confeccionadas pelo sistema CAD/CAM Cerec 3 e cimentadas com o cimento RelyX Unicem II Automix. As coroas em FEL e DL foram previamente condicionadas com ácido fluorídrico e silanizadas. As coroas em RNC, assim como os dentes preparados foram apenas jateados. Todas as restaurações foram submetidas ao teste de RFAD com um carregamento cíclico isométrico aplicado por uma esfera de resina composta. O carregamento começou com cargas de 200N (5.000x) seguidos por estágios de 400, 600, 800, 1000, 1200 e 1400N a um máximo de 30.000 ciclos cada. Os espécimes foram submetidos ao carregamento até a fratura ou por no máximo 185.000 ciclos. Os espécimes que resistiram a todos os ciclos foram novamente testados axialmente até a falha ou até uma carga máxima de 4.500N. Os espécimes foram classificados quanto ao modo de falha em: catastrófica, possivelmente reparável e reparável. Os grupos foram comparados utilizando uma análise de sobrevida para o teste de RFAD e t-test ou ANOVA para o teste de RFRA. Comparações Post hoc também foram utilizadas para comparar os diferentes grupos. Resultados: A taxa de sobrevida das coroas sobre os molares não TE foram: 80% (RNC/1,5mm), 6,6% (RNC/0,7mm), 93,3% (DL/1,5mm), 13,2% (DL/0,7mm), 6,6% (FEL/1,5mm) e 0% (FEL/0,7mm). A RFRA das coroas com 1,5mm de espessura foi: 3122N-RNC, 3237N-DL e 2500N-FEL. As coroas cimentadas sobre molares TE tiveram taxa de sobrevida e RFRA respectivamente de: 53%/2969N (RNC-4mm de altura), 100%/3181N (DL-4mm de altura), 87%/2794N (RNC-2mm de altura), 93%/3759N (DL-2mm de altura), 87%/2606N (RNC-endocrown) e 100%/3265N (DL-endocrown). No teste de RFAD houve falha catastrófica apenas para as coroas confeccionadas em RNC-4mm. Após o teste de RFRA todos os espécimes falharam catastroficamente. As coroas em RNC induziram menor desgaste aparente ao antagonista. Conclusão: Apenas as coroas FEL-0,7mm não sobreviveram além da máxima força mastigatória humana. Para os dentes não TE, as coroas em DL e RNC com espessuras de 1,5mm tiveram o melhor desempenho mecânico. Para os molares TE, uma maior carga para fratura foi requerida com o uso de coroas em DL-2mm. O tratamento endodontico não teve influência sobre a RFAD de molares restaurados com coroas CAD/CAM de DL, mas diminuiu a performance das RNC / Abstract: Objectives: To evaluate the fatigue resistance, load-to-failure, failure mode and antagonistic wear in contact with different designs of full CAD/CAM crowns made of feldspathic ceramic/FEL, lithium disilicate/LD or resin nano ceramic/RNC. These prosthetic materials were used to restore endodontic treated molars or not, using a simplified cementation process. Materials and Methods: Chapters One and Two used 90 molars, which had a standardization of full crown preparation and teeth were restored using crown made of FEL, LD and RNC with thickness of 1.5mm or 0.7mm, respectively. Chapters Three and Four used 90 molars decoronated at the level of CEJ, endodontically-treated and restored using three different Filtek Z100 adhesive core build-ups designs (4-mm-build-up; 2-mm-build-up; and no buildup/ endocrown preparation) combined to crowns made of RNC and LD, respectively. For Chapter Five, groups of Chapters One (RNC/1,5mm and LD/1,5mm), Three (4-mm-build-up/RNC) and Four (4-mm-build-up/LD) were combined. All molars were restored using the Cerec 3 CAD/CAM system and cemented with RelyX Unicem II Automix cement. FEL and LD restorations were conditioned by hydrofluoric acid etching and silanated. RNC restorations as well as all preparations were treated only with airborne-particle abrasion. All restorations were submitted to cyclic isometric loading applied through a composite resin hemi-sphere. The cyclic loading started with a load of 200N (x5000 cycles), followed by stages of 400, 600, 800, 1000, 1200, and 1400N at a maximum of 30,000 cycles each. Specimens were loaded until failure or for a maximum of 185,000 cycles. Survived specimens were axially loaded until failure or to a maximum load of 4,500N. After load tests, the specimens were analyzed for the failure mode: "catastrophic" tooth/root failure, "possibly reparable" failure and "reparable" failure. Groups were compared using the life table survival analysis (fatigue test) and the t-test, one-way or two-way ANOVA for the survived samples loaded to failure. Pairwise post hoc comparisons were used to compare the different groups. Results: The survival rates for the vital teeth were: 80% (RNC - 1.5mm), 6.6% (RNC - 0.7mm), 93.3% (LD - 1.5mm), 13.2% (LD - 0.7mm), 6.6% (FEL - 1.5mm) and 0% (FEL - 0.7mm). Post-fatigue load-to-failure for 1.5mm crowns ranged between 3122N (RNC), 3237N (LD) and 2500N (FEL). The survival rate and post-fatigue load to failure for non-vital teeth were 53% / 2969N (4mm - RNC), 100% / 3181N (4mm - DL), 87% / 2794N (2mm - RNC), 93% / 3759N (2mm - DL), 87% / 2606N (endocrown - RNC) e 100% / 3265N (endocrown - LD), respectively. There were only catastrophic failures for 4mm-build-up RNC during the fatigue test. All of specimens in the load-to-failure test exhibited non-restorable catastrophic fractures. Crowns made of RNC seemed to generate the least amount of antagonistic wear. Conclusions: FEL crowns with 0.7mm of thickness didn't survive beyond the maximum masticatory forces. RNC and LD crowns with 1.5mm thick had the best performance on vital teeth. LD crowns combined with short build-ups (2mm) were associated to highest loads to failure. Endodontic treatment did not influence the fatigue resistance of molars restored with LD CAD/CAM complete crowns but decreased the performance of RNC crowns / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-06-15Bitstream added on 2014-06-13T20:37:57Z : No. of bitstreams: 1 souza_roa_me_sjc.pdf: 815502 bytes, checksum: 2c82a3a91698db3c6e94fda59d746792 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo avaliou a discrepância marginal (DM) e interna (DI) de coroas totais cerâmicas fabricadas pelo sistema CAD/CAM Cerec inLab, frente a três diferentes términos cervicais. A hipótese nula foi que o tipo de término não influencia a DM e DI das coroas. A partir de três troquéis metálicos com distintos términos cervicais, foram fresadas trinta coroas cerâmicas (ProCad/Ivoclar Vivadent) (n=10): CI) chanfro inclinado; CL) chanfro largo e O) ombro arredondado. Para análise da DM, mensurou-se, em 50 pontos, a distância entre a margem externa de cada coroa à margem do término cervical do respectivo troquel metálico. Utilizando a técnica da réplica, avaliou-se a DI de cada coroa em 12 pontos igualmente distribuídos por regiões: término (T), axial (A) e oclusal (Ocl). As mensurações foram realizadas em microscópio óptico (250x). Os dados obtidos ('mü'm) foram submetidos aos testes estatísticos ANOVA e de Tukey (5%). Os resultados demonstraram que grupo O (28,24'mais ou menos'11,42'mü'm) gerou valores de DM significativamente inferiores (p=0,001) aos dos grupos CI (99,92'mais ou menos'18,32'mü'm) e CL (64,71'mais ou menos'25,64'mü'm), os quais diferiram estatisticamente entre si. A análise da DI demonstrou que o grupo CL (183,01'mais ou menos'62,82'müm) apresentou valores inferiores (p=0,0014) aos demais grupos: CI (216,26'mais ou menos'83,23 'mü'm) e O (219,12'mais ou menos'87,24'mü'm), os quais foram semelhantes entre si. Observou-se também que a DI variou entre as regiões mensuradas (p=0,0001). A hipótese nula foi rejeitada. Baseado nos resultados pôde-se concluir que, apesar das diferenças estatísticas observadas entre os grupos, os três términos cervicais geraram coroas com valores de DM e DI aceitáveis clinicamente. / This study evaluated the marginal discrepancy (MD) and internal (ID) of ceramic crowns manufactured by the CAD/CAM system Cerec inLab, varying the finish line. The null hypothesis was that the preparations won't influence the MD and ID of the crowns. From three metallic dies with different finish lines, thirty ceramic crowns (ProCad/Ivoclar Vivadent) were machined (n=10): TC) tilted chamfer; LC) large chamfer and RS) rounded shoulder. For MD analysis, were measured, in 50 points, the distance between each crown extern edge to the edge of the cervical preparation on the respective metallic die. Using the replica technique, it was evaluated the ID of each crown at 12 points equally distributed between the regions: end (E), axial (A) and oclusal (Ocl). The mensurations were done in optical microscope (250x). The data obtained ('mü'm) were submitted to the statistical tests ANOVA and Tukey (5 %). The results demonstrated that the group RS (28,24 'mais ou menos'11,42'mü'm) produced MD values smaller (p=0,001) than the groups TC (99,92'mais ou menos'18,32'mü'm) and LC (64,71'mais ou menos'25,64 'mu'm), which, between them, differed statistically. The analysis of ID demonstrated that the group LC (183,01'mais ou menos'62,82 'mü'm) presented values lower (p=0,0014) than TC (216,26'mais ou menos'83,23'mü'm) and RS (219,12'mais ou menos'87,24 'mü'm), which were similar between them. It was also noticed that ID varied between the measured regions (p=0.0001). The null hypothesis was rejected. It was concluded that, in spite of the statistical differences observed between the groups, the three cervical finish lines produced crowns with MD and ID values clinically acceptance.