Conselho Nacional de Desenvolvimento Científico e Tecnológico / The aim of the present research was to evaluate the physical and mechanical properties of LVL reinforced with fiberglass with two types of resins. Pinus elliottii veneers with 1,5 mm thickness were used to manufacture of the LVL panels. The panels were manufactured in two steps. The first one was the assembling of the LVL panels with nine layers of wood veneer glued with phenol-formaldehyde resin. The second step consisted into reinforcing the LVL with fiberglass impregnated with epoxy resin (E) or isophthalic resin (I). The treatments were: panels without reinforcement (T), panels reinforced with one fiberglass layer (E T1 e I T1), panels reinforced with two fiberglass layers (E T2 e I T2) and panels reinforced with four fiberglass layers (E T3 e I T3). The size of panel was 45 cm x 34 cm x 1,08 cm. The physical properties tested were density and moisture content. The mechanical properties tested were: static bending in flatwise and edgewise position, modulus of elasticity (MOE) and modulus of rupture (MOR); glueline shear strength by compression loading; hardness test; and non-destructive test by ultrasound method. The epoxy and the isophthalic resin showed similar mechanical performance among the different treatments.The resistence and stiffness of the panels were influenced by the reinforcement. The MOE in flatwise position was influenced by one reinforcement layer and the MOR was influenced by two reinforcement layers. In the edgewise position the MOE and the MOR values remained constant among the treatments with two fiberglass reinforcement layers. The MOE in nondestructive test had higher values when compared with the destructive method, however these values remained stable with two layers of reinforcement. Two layers of reinforcement on the tensile and compression side had higher values in hardness test. The epoxy resin presented higher glueline resistence and higher percentage of wood failure. Isophthalic and phenolic resin presented similar values of glueline strenght, however the isophthalic resin had lower percentage of wood failure. Thus, the reinforcement with one layer of fiberglass imprenated with epoxy resin on the tensile side would be enough to promote the mechanical qualities of LVL. / O objetivo desta pesquisa foi avaliar as propriedades físico-mecânicas de painéis de lâminas paralelas (LVL) reforçadas com camadas de fibra de vidro inpregnadas com dois tipos de matrizes. Lâminas de madeira de Pinus ellliottii com espessura de 1,5 mm foram utilizadas na fabricação dos painéis. A montagem dos painéis foi realizada em duas etapas. A primeira consistiu na fabricação dos painéis LVL com nove camadas de lâminas de madeira unidas com resina à base de fenol-formaldeído na gramatura de 190 g/m2 em linha simples. E a segunda etapa consistiu na aplicação do reforço de fibra de vidro impregnado com resinas epóxi (E) ou poliéster isoftálica com NPG (I). Os tratamentos utilizados foram: painéis sem reforços (T), painéis com uma camada de fibra de vidro (E T1 e I T1), painéis com duas camadas de fibra de vidro, sendo uma camada no lado de compressão e uma camada no lado de tração (E T2 e I T2) e painéis com quatro camadas de fibra de vidro, duas camadas do lado de compressão e duas camadas no lado de tração separados por uma lâmina de madeira (E T3 e I T3). Foram realizadas três repetições por tratamento, totalizando 21 painéis. As dimensões finais dos painéis foram 45 cm x 34 cm x 1,08 cm. Para determinar a qualidade dos painéis LVL foram avaliadas as propriedades físicas (massa específica e teor de umidade) e a resistência mecânica (flexão estática na posição flatwise e egdewise, resistência ao cisalhamento, dureza Janka e teste não destrutivo utilizando ultrassom). A resina epóxi e a resina isoftálica apresentaram as mesmas qualidades mecânicas nos diferentes tratamentos. A aplicação do reforço influenciou na resistência e na rigidez do painel. Na flexão estática na posição flatwise o módulo de elasticidade (MOE) foi influenciado por uma camada de reforço e o módulo de ruptura (MOR) por duas camadas de reforço. Na posição edgewise os valores de MOE e do MOR se mantiveram estáveis com a aplicação de duas camadas de reforços de fibra de vidro. O MOE pelo método ultrassônico apresentou valores maiores quando comparado com o método estático; em ambos os métodos os valores mantiveram-se estáveis com a aplicação de duas camadas de reforço. A dureza Janka foi maior para as painéis com mais camadas de fibra de vidro na posição de tração e compressão. A resina epóxi apresentou maior resistência ao cisalhamento e maior percentual de falhas na madeira, enquanto que a resina isoftálica, apesar de apresentar valores de resistência similares à fenólica, não apresentou boa adesão à madeira, representada pelo baixo percentual de falhas na madeira. A aplicação de uma camada de reforço de fibra de vidro com resina epóxi na posição de tração seria o suficiente para melhorar as qualidades mecânicas dos painéis LVL fabricados com lâminas de madeira de pinus unidas com fenol-formaldeído.

Made available in DSpace on 2016-12-08T17:19:14Z (GMT). No. of bitstreams: 1 Parte 1.pdf: 442291 bytes, checksum: f948228d7caa220f7398d3b07a84b8cc (MD5) Previous issue date: 2011-10-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Graphite is the cheapest and the most abundant source to obtain graphene. For a large scale production of graphene and its application in nanocomposites, reduction of graphite oxide (GO) method has been currently used. The graphite oxidation causes an introduction of functional groups which leads to an increase in graphite interlayer distance, producing GO. The GO can be reduced either by chemical or thermal methods. Several polymer matrices have been utilized to produce graphene nanocomposites, one of them is the epoxy resin. One of the challenges to produce polymer nanocomposites is the total dispersion of the nanofillers into the matrix and a strong matrix/nanofillers interfacial adhesion to obtain enhanced final properties. The aim of this work was the production of reinforcements for application in epoxy matrix nanocomposites. From natural graphite, some reinforcements were produced, such as sonicated graphite (SG), exfoliated graphite by supercritical fluid of carbon dioxide (GE-scCO2), GO, expanded GO (EGO) and chemical reduced GO (RGO). Among these, only the SG, GO and EGO were utilized in nanocomposites production at concentrations of 0.025, 0.05, 0.075 e 0.1 wt% in epoxy resin based on diglycidyl ether of bisphenol-A (DGBEA). The results showed the graphite oxidation method was efficient to produce GO and both, chemical and thermal reduction methods, increases the thermal stability of the material, indicating high reduction level which was also verified by X-ray diffraction. The graphite exfoliation by scCO2 demonstrated to be a promising method for graphene production, although it had a low production rate. The results did not show significant changes in thermal stability and electrical conductivity of the nanocomposites, indicating an absence of a threshold percolation with the amounts of reinforcements studied. The most promising system to enhance mechanical properties of epoxy resin nanocomposites is that one with EGO, since it showed a tenacity increase and an improvement of ~70% in tensile strength, although the Young s modulus decreased. The results showed the reinforcements produced from the natural graphite have a great potential to be applied in structural nanocomposites, however to get more significant results on the properties evaluated, higher amounts of reinforcements and different dispersion methods should be studied further. / O grafite é a fonte mais abundante e de baixo custo para obtenção de grafeno. Para uma produção em larga escala de grafeno e sua aplicação em nanocompósitos, o método de redução do óxido de grafite (OG) tem sido o mais utilizado. Com a oxidação do grafite, grupos funcionais, são introduzidos na sua estrutura e causam o afastamento dos planos cristalinos do grafite, produzindo o OG. Sua redução pode ser realizada tanto por métodos químicos quanto térmicos. Várias matrizes poliméricas estão sendo utilizadas na produção de nanocompósitos com grafeno, dentre elas a resina epoxídica. Um dos desafios é proporcionar a dispersão total do nanoreforço na matriz e promover uma forte adesão interfacial matriz/nanoreforço para se obter melhores propriedades finais. Sendo assim, o objetivo desse trabalho foi produzir reforços a partir do grafite natural para aplicação em nanocompósitos poliméricos de matriz epoxídica. A partir do grafite natural, foram produzidos alguns reforços, como o grafite sonificado (GS), grafite esfoliado por fluido supercrítico de CO2 (GE-scCO2), OG, OG expandido (OGE) e OG reduzido quimicamente (OGR). Dentre estes, apenas o GS, OG e OGE foram utilizados na produção dos nanocompósitos, utilizando as concentrações de 0,025, 0,05, 0,075 e 0,1% m/m do reforço em matriz de resina epoxídica à base de éter diglicidílico do bisfenol A (DGEBA). Os resultados indicaram que o método de oxidação do grafite foi eficaz na produção de OG e que tanto a redução química quanto a térmica aumentou a estabilidade térmica do material, evidenciando alto grau de redução, comprovado também por difratografia de raios-X. A esfoliação do grafite por scCO2 se mostrou um método promissor na obtenção de grafeno, embora os resultados obtidos indicaram baixo rendimento de produção. Não foram observadas alterações significativas na estabilidade térmica e na condutividade térmica dos nanocompósitos, indicando que não se formaram redes de percolação nas concentrações estudadas. Os sistemas contendo OGE mostraram ser os mais promissores na melhoria das propriedades mecânicas, pois apresentou maior tenacidade e um incremento de até ~70% na resistência à tração, embora o módulo de Young tenha sido reduzido. Com base nestes dados, pode-se dizer que os reforços produzidos a partir do grafite natural possuem grande potencial para aplicação em nanocompósitos estruturais, porém para se obter resultados mais significativos a respeito das propriedades avaliadas, maiores concentrações de reforço e diferentes técnicas de dispersão devem ser estudadas.

Made available in DSpace on 2016-12-08T17:19:16Z (GMT). No. of bitstreams: 1 Parte 1.pdf: 86993 bytes, checksum: 84f9ef5ca3d5e4b6abc44c72fe430745 (MD5) Previous issue date: 2012-02-24 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Epoxy resin / carbon nanotubes (CN) composites are widely used due to the versatile matrix phase and the excellent properties of the reinforcing phase. However, the development of polymer nanocomposites still faces three important challenges: interfacial interaction, dispersion and orientation of the reinforcing phase. This work studied the orientation process of NC by electric field of 100 V/cm, and how this phenomenon changes the properties of these materials. The in situ polymerization method was used to fabricate nanocomposites with multi-walled carbon nanotubes and epoxy resin. We made three sets of nanocomposites, each set contained five concentrations of CN: 0.00, 0.04, 0.08, 0.20 and 0.30 (v/v). In the manufacture of the first set, the samples were not subjected to an electric field during curing, while the second set of samples was prepared under an electric field of 100 V/cm at a frequency of 1 kHz during curing. The third set was prepared under an electric field of 100 V/cm at 60 Hz during curing. Viscosimetry techniques, optical microscopy, scanning electron microscopy, differential scanning calorimetry (DSC) and impedance spectroscopy were used to characterize the dispersion and orientation of carbon nanotubes. The viscosimetry shows that the nanocomposites exhibit a shear thinning behavior for all concentrations studied. However, the viscosity of the material increased considerably with CN concentration, ca. 50% for 0.30% (v/v) NC, difficulting the processing of samples. Optical and electronic microscopies showed that the manufacturing method used to disperse the CN did not provide a homogeneous dispersion. Using the impedance spectroscopy technique it was possible to characterize the orientation of the CN, since the electrical conductivity of all samples submitted to the electric field during curing showed an increase of 2.8 orders of magnitude compared to the set that was not subjected to the electric field. The orientation of the CN decreased the percolation threshold of the samples. Nanocomposite samples not subjected to the electric field during curing (ER) showed a percolation threshold of (0.06 ± 0.02) (v/v), while the set of samples subjected to the electric field (EA) had a percolation threshold (0,010 ± 0,005) (v/v). In these systems the direction of CN showed no dependence on the frequency of the applied electric field during curing, as the electrical conductivity of the samples prepared under the electric field oscillating at 1 kHz and that of the samples prepared at 60 Hz showed similar values. / Compósitos de resinas epoxídicas e nanotubos de carbono (NC) são materiais amplamente estudados para potenciais aplicações funcionais e estruturais, pois a fase matriz polimérica é versátil e a fase reforço apresenta excelentes propriedades. Porém, o desenvolvimento destes nanocompósitos poliméricos ainda enfrenta três desafios para que as propriedades da fase reforço sejam transferidas à matriz: a interação interfacial, a dispersão e a orientação da fase reforço. Nesse trabalho foi estudado o processo de orientação de NC por campo elétrico de 100 V/cm e como esse fenômeno altera as propriedades desses materiais. O método de polimerização ��in situ�� foi usado para fabricar nanocompósitos com nanotubos de carbono de paredes múltiplas e resina epóxi baseada no éter diglicidílico do bisfenol A (DGEBA), tendo em vista o estudo das suas propriedades elétricas. Foram fabricados três conjuntos de nanocompósitos, cada conjunto continha cinco concentrações de NC: 0,00; 0,04; 0,08; 0,20 e 0,30 % (v/v). Na fabricação do primeiro conjunto as amostras não foram submetidas ao campo elétrico durante a cura. Na fabricação do segundo conjunto as amostras foram submetidas a um campo elétrico de 100 V/cm com frequências de 1 kHz durante a cura. Na fabricação do terceiro conjunto as amostras foram submetidas a um campo elétrico de 100 V/cm com frequências de 60 Hz durante a cura. As técnicas de viscosimetria, microscopia ótica, microscopia eletrônica de varredura, calorimetria diferencial de varredura (DSC) e espectroscopia de impedância foram usadas para caracterizar a dispersão e orientação dos nanotubos de carbono. A viscosimetria mostrou que os nanocompósitos apresentam um comportamento pseudoplástico para todas as concentrações estudadas. Contudo, o aumento da concentração de NC aumentou também a viscosidade do material, em cerca de 150 % para 0,30 %(v/v) de NC, dificultando o processamento das amostras. As técnicas de microscopia ótica e eletrônica mostraram que o método de fabricação usado para dispersar os NC não proporcionou uma dispersão homogênea em escala nanométrica. Já com a técnica de espectroscopia de impedância foi possível caracterizar a orientação dos NC, pois a condutividade elétrica do conjunto de amostras submetidas ao campo elétrico durante a cura apresentou um incremento de 2,8 ordens de grandeza quando comparado ao conjunto não submetido ao campo elétrico. A orientação dos NC diminuiu o limiar de percolação das amostras, pois o conjunto de amostras de nanocompósitos não submetidas ao campo elétrico durante a cura apresentou um limiar de percolação de (0,06 ± 0,02) % (v/v). Já o conjunto de amostras de nanocompósitos submetidas ao campo elétrico apresentou um limiar de percolação de (0,010 ± 0,005) % (v/v). Nesse sistema a orientação dos NC não apresentou dependência à frequência do campo elétrico aplicado durante a cura, pois a condutividade elétrica das amostras submetidas ao campo elétrico oscilando a 1 kHz e das amostras submetidas ao campo elétrico oscilando a 60 Hz apresentaram valores similares.

Made available in DSpace on 2016-12-08T17:19:22Z (GMT). No. of bitstreams: 1 Renata Hack.pdf: 4507234 bytes, checksum: a9a47eaf8a6524ae5f448abca5062a08 (MD5) Previous issue date: 2014-02-07 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O grafite natural é uma fonte de baixo custo e é abundante para obtenção de grafeno. O método que se mostrou mais eficiente para a produção de grafeno em larga escala é o método Hummers modificado, que consiste na oxidação do grafite. Com isso, o objetivo principal deste trabalho foi produzir grafeno a partir do grafite natural pelo método de Hummers modificado, além de produzir nanocompósitos de matriz epoxídica reforçada com o grafeno produzido (GP) e o grafeno comercial (GC). Para a produção dos nanocompósitos foi utilizado à resina epoxídica à base de éter diglicidílico do bisfenol A (DGEBA). Foram obtidos nanocompósitos em concentrações de 0,75; 1,00 e 2,00% m/m de GC e GP, com e sem a utilização de solvente THF no processo de preparação. Os resultados obtidos indicaram um alto grau de oxidação do grafite, comprovando assim que o processo foi eficiente. As análises de Raman e FTIR realizadas no GC e GP mostraram que o GP possui as mesmas características do GC. A adição do GC e GP com e sem adição de THF elevou a estabilidade térmica dos nanocompósitos. A alta concentração de nanoreforços e a não utilização de solvente THF em alguns sistemas pode ter contribuído para a formação de aglomerados nestes nanocompósitos, decorrendo assim em uma diminuição do módulo de Young. Através da análise de impedância foi possível verificar que apenas os nanocompósitos com 2%m/m de GP sem THF apresentou percolação dielétrica. Verifica-se que a produção do grafeno a partir do grafite natural possui potencial para aplicação em nanocompósitos estruturais.

Orientador: Newton Luiz Dias Filho / Banca: Devaney Ribeiro do Carmo / Banca: Wagner Luiz Polito / Resumo: Polímeros epoxídicos são um dos mais importantes tipos de polímeros termorrígidos, extensivamente usados como adesivos e estruturas. Em reações epoxídicas são convertidos em um sistema termorrígido pela ação de agentes de cura. Tais reações químicas provocam uma mudança no estado físico do material, partindo de um líquido viscoso para um gel e se transformando em um material vitrificado. Os termorrígidos apresentam excelentes propriedades, tais como: alta tensão de ruptura e módulo de Young, fácil processamento, resistência térmica e química, e estabilidade dimensional. Entretanto, são quebradiços e possuem baixa resistência a propagação de trincas. Para superar estes inconvenientes, muitos tipos de compósitos de polímero com reforço foram desenvolvidos, em que as resinas epoxídicas são reforçadas com agentes modificadores, tais como enchimentos, oligômeros poliédricos de silsesquioxanos, dendrímeros, etc. Oligômeros poliédricos de silsesquioxanos (POSS), (RSiO1.5)n com n = 4, 6, 8, 10..., são nanoplataformas organo-funcionalizadas com 1 a 8 grupos reativos ou não reativos (R) ligados aos oito vértices possíveis do silsesquioxano cúbico. POSS octaédrico (n = 8) são os membros mais importantes desta família. No POSS, o núcleo cúbico de silicato é "uma partícula rígida" com 0,53 nm de diâmetro e um raio esférico de 1-3 nm, incluindo unidades orgânicas periféricas. Neste trabalho, um oligômero poliédrico de silsesquioxano contendo oito grupos epoxídicos por molécula (OG) foi incorporado ao sistema epoxídica DGEBA/DETA, como objetivo de avaliar a influência de um modificador reativo suas propriedades mecânicas e térmicas. Por meio de ensaios mecânicos foi observado um decréscimo de 30-50% na resistência à fratura (K1C)... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Epoxy resins are one of the most important kind of thermosetting polymers, extensively used for adhesives and structural applications. On cure, linear epoxy resins are undergoes in a thermoset system for the action of cure agents. Such chemical reactions cause a change into the physical state, from a viscous liquid to a gel and eventually to a vitrified material. They show various desirable properties such as high tensile strength and modulus, easy processing, good thermal and chemical resistance and dimensional stability, but they are brittle and have poor resistance to crack propagation. To overcome these drawbacks, many types of polymer-filler composites have been developed, in which the epoxy resins are reinforced with modifying agents, such as fillers, polyhedral oligosilsesquioxanes, dendrimers, etc. Polyhedral oligomeric silsesquioxanes (POSS), (RSiO1.5)n with n = 4, 6, 8, 10 ...., are organofunctional nanoplatforms with 1 to 8 reactive or nonreactive groups (R) connected to the eight possible vertexes of cubic silsesquioxanes. POSS Octahedral (n = 8) are the most important members of this family. In the POSS, the cubic core silica is a "hard particle" rigid with 0.53 nm diameter and a spherical radius of 1-3 nm including peripheral organic units. In this work, a polyhedral oligomeric silsesquioxanes containing eight epoxy groups per molecule (OG) was incorporated to an epoxy system of DGEBA/DETA thermosetting polymers in order to investigate the influence of a reactive modifier over the their mechanical and thermal properties. Through the mechanical tests an decrease of about 30-50% was observed in the fracture toughness (K1C) without or with a very soft decreasing in the module of Young (E)... (Complete abstract, click electronic address below) / Mestre

Neste trabalho experimental, objetivou-se avaliar comparativamente a alteração dimensional de três diferentes materiais utilizados na confecção de troqueis: gesso tipo IV Fuji Rock (GC), resina epóxica industrial Sikadur 32 (Sika) e resina epóxica Tri-Epoxy Die Material (Tri-Dynamics). Foram confeccionados dois modelos-padrão em aço inoxidável. Um desses modelos foi confeccionado de modo a simular um preparo para coroa total em um pré-molar. O outro modelo foi confeccionado 2,0mm maior em todas as dimensões em relação ao primeiro de modo a proporcionar um alívio uniforme para a base leve do material de moldagem. Trinta troquéis foram obtidos a partir de moldes em silicona de adição (Aquasil Dentsply) utilizada com a técnica de dois passos. Os troqueis foram divididos em grupos de dez para cada material. As alterações foram mensuradas através das medições da altura e dos diâmetros da base e do topo dos troqueis obtidos, com o auxílio de um Projetor de Perfis Deltronic DV-114 com leitura em software. As medidas obtidas foram dispostas em tabelas e analisadas estatisticamente. Após avaliação pode-se concluir que houve diferença estatisticamente significante entre todos os grupos testados. Os troquéis de gesso tipo IV Fuji Rock (GC) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições do diâmetro da base, apresentando diferença estatisticamente significativa em todas as comparações com o grupo controle (metal). Os troquéis de resina epóxica Tri-Epoxy (Tri-Dynamics) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições diâmetro da base, apresentando diferença estatisticamente significante somente no diâmetro do topo nas comparações com o grupo controle (metal). Os troquéis de resina epóxica Sikadur 32 (Sika) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições do diâmetro das base, apresentando diferença estatisticamente significante em todas as comparações com o grupo controle (metal). / The aim of this study was to comparatively evaluate the dimensional changes of three different materials used in the production of dies: gypsum type IV - Fuji Rock (CG), industrial epoxy resin - Sikadur 32 (Sika) and epoxy resin - Tri-Epoxy Die Material (Tri-Dynamics). Two standard models of stainless steel have been made. One of these models was prepared to simulate a full crown preparation on a premolar. The other model was prepared 2.0 mm larger in all dimensions compared to the first one so as to provide an uniform relief for impression material mild base. Thirty dies have been made from molds in vinyl polysiloxane (Aquasil - Dentsply) using the two steps technique. Dies were divided into groups of ten for each material. Changes were evaluated by measuring the height and diameter of bottom and top of the dies with the aid of a Deltronic DV-114 Profiles Projector with reading software. The resultant measurements were arranged into tables and statistically analyzed. After evaluation, it was concluded that there was a statistically significant difference among all tested groups. Gypsum Fuji Rock type IV (GC) dies shrank in tops height and diameter measurements, and expanded the bottom diameter measurements, showing statistically significant differences when compared to control group (metal). Epoxy resin Epoxy-Tri (Tri-Dynamics) dies shrank in tops height and diameter and expanded in bottom diameter measurements, showing statistically significant difference only in tops diameter when compared to control group (metal). Epoxy resin Sikadur 32 (Sika) dies shrank in tops height and diameter measurements and expanded in bottoms diameter measurements, showing a statistically significant difference when comparing to control group (metal).

Fundação de Amparo à Pesquisa do Estado do Rio de Janeiro / Assim como em outras áreas do conhecimento a construção civil vem evoluindo ao longo dos anos. Grandes investimentos e elevadas taxas de demandas por novos projetos requerem uma maior velocidade na consolidação de obras. Neste cenário, ficam precários os estudos e pesquisas que avaliam a capacidade de novas tecnologias. Na área do concreto e estruturas de concreto armado, depara-se a associação de técnicas consolidadas à métodos inovadores. A utilização de polímeros como material de construção, como é o caso dos aditivos para concreto, dos tubos e conexões, das esquadrias e como adesivos, utilizados em ligações de aduelas de pontes, associados a fibras de vidro ou carbono para reforços estruturais e para fixação de armaduras ou conectores no caso de reparação de estruturas, oferecendo uma solidarização eficiente entre elementos estruturais. O presente trabalho visa avaliar uma pequena parcela de aplicação de materiais poliméricos, principalmente quanto a sua característica de aderência e colagem de barras de aço ao concreto. O desenvolvimento do estudo ocorreu sobre uma perspectiva de ensaios laboratoriais de arrancamento de barras coladas com resina epóxi em blocos de concreto, sendo estes resultados comparados com barras de aço concretadas em blocos de concreto. Desse modo o principal fator de comparação seria a tensão de aderência desenvolvida na área de contato da barra com o substrato. Alguns parâmetros foram inseridos para uma abordagem de maior amplitude, tais como variação do diâmetro da barra (φ = 10,0mm; φ = 12,5mm e φ = 16,0mm), do comprimento de ancoragem (múltiplos do diâmetro, sendo 5φ e 7,5φ) e da espessura da resina (1mm, 2mm e 3mm). De forma complementar procedeu-se ao ensaio de vigas bi-apoiadas submetidas à flexão visando representar o comportamento de uma recuperação/reforço estrutural aplicado em escala. Para avaliar o comportamento destas vigas, foram ensaiados dois espécimes, uma viga padrão concretada de uma única vez e outra submetida a um reparo estrutural, onde possuía a armadura inferior inserida posteriormente à concretagem inicial, colada com resina epóxi nas extremidades da viga. / Just like others fields of knowledge, the civil construction is evolving. Hughes investments and the need for new projects improve the speed and the technology usually applied for basic infrastructures development. These scenarios achieve issues as the miss understanding of the behavior of this technological advances in long terms, caused by the few studies and researches about these subjects. At the concrete structures field, an extremely self consolidate knowledge whose have been replaced for new methods, as the case of the polymeric materials. This kind of material have large scale of applications at construction and projects of structural elements, used as a bond interface for different elements and offering a significant monolithically performance between structural pieces. The current study pretends analyze the behavior of bonded steel bars at the concrete using epoxy resin. The development of the study occur by lab tests where a steel bar is pulled out of a concrete block, named Pull-out-test. This one was adapted for a bond whit epoxy resin, were the results was compared whit the regular ones (concrete bonded bars), in this method the phenomenon of the stress occurred at the bar surface in contact whit the concrete or the resin evaluate. Some parameters were included for a better understanding of the bond behavior, such as: Steel bar diameter (10mm, 12,5mm and 16mm); Length of anchorage (5φ and 7,5φ), and Resin thickness (1mm, 2mm and 3mm). For the same purpose, was molded a concrete beam to represent the bonded situation at a real condition, these beam had two different configuration, one of those were a regular reinforcement beam, and the other one were a recuperated reinforcement beam, whit yours inferior steel bar added post concrete solidification, simulating a intervention at a problematic beam, in this case the steel bars were bonded whit epoxy resin at the edges of the beam.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Neste trabalho foi proposto o monitoramento do processo de cura e fotocura de resinas epóxi através da Espectroscopia Fotoacústica. Nos experimentos, foram utilizados dois tipos de resinas epóxi: A resina Epoxtec 331, com o endurecedor DER 24, e a resina fotocurada EBECRYL 3720-TP25, com o fotoiniciador OMNIRAD 808. Foram utilizados dois modelos de células fotoacústicas: uma baseada na técnica de diferença de fase dos dois feixes (T2F); e outra convencional. São apresentadas as montagens experimentais desenvolvidas para os monitoramentos da cura e fotocura das resinas. O estudo foi realizado monitorando o sinal fotoacústico fazendo varredura em comprimentos de onda. Também foi monitorado o sinal fotoacústico em função do tempo durante as curas e fotocuras. Foi estudado o efeito de luz saturante, não modulada, nos processos de fotocura. Tanto a amplitude quanto a fase do sinal fotoacústico revelaram-se boas ferramentas para o monitoramento proposto. Apesar de muitos dos efeitos encontrados, nos estudos realizados, ainda não terem explicação, o presente trabalho mostrou a potencialidade da espectroscopia fotoacústica para esta área de pesquisa. / In this work it was proposed the monitoring of the cure and photocuring of epoxy resins by Photoacoustic Spectroscopy. In the experiments, two types of epoxy resins were used: the resin Epoxtec 331,with the hardener DER 24; and the resin EBECRYL 3720 - TP25, with the photoinitiator 808 OMNIRAD. Two models of Photoacoustic cell were used: one based on two-beam phase-lag technique (T2F); and a conventional one. The developed set-ups for monitoring of cure and photocuring of epoxy resins are presented. The study was carried out with monitoring the photoacoustic signal on the wavelengths scan. Also the photoacoustic signal as a function of time was observed during the cure and photocuring. The effect of unmodulated saturating light was studied in the processes of photocuring. Both the amplitude and the phase of the photoacoustic signal proved to be good tools for the proposed monitoring. Although many of the effects found in these studies have not yet been explained, the present study showed the potential of photoacoustic spectroscopy to this area of research.

As fontes radioativas seladas são usadas na verificação de detectores de câmara de ionização, os quais medem a atividade dos radioisótopos usados nas mais diversas áreas, como na Medicina Nuclear. A medida da atividade dos radioisótopos deve ser feita com exatidão, pois será administrada em um paciente. Para garantir o adequado funcionamento dos detectores de câmara de ionização, são estipulados ensaios normatizados pela Agência Internacional de Energia Atômica (IAEA) e a Comissão Nacional de Energia Nuclear (CNEN) utilizando-se fontes radioativas seladas de Bário-133, Césio-137 e Cobalto-57. Os testes avaliam a exatidão, precisão, reprodutibilidade e linearidade da resposta do equipamento. O foco deste trabalho foi o estudo e o desenvolvimento dessas fontes radioativas padrão de Bário-133, Césio-137 e Cobalto-57, utilizando um polímero, no caso resina epóxi comerciais do tipo éter diglicidílico do bisfenol A e um agente de cura a base de poliamina modificada da dietilenotriamina ,para imobilizar o material radioativo. A matriz polimérica apresenta a função primordial de fixar e imobilizar o conteúdo radioativo não permitindo seu vazamento dentro dos limites técnicos exigidos pelas normas de proteção radiológica no quesito de características de uma fonte selada e, adicionalmente, ter a capacidade de reter a emanação de quaisquer gases que venham a se formar durante o processo de fabricação e do período de vida útil deste artefato. O processo de manufatura de uma fonte selada padrão consiste no envasamento, em um frasco de geometria padronizada, de uma quantidade, em volume fixo, de uma matriz polimérica no interior da qual é adicionada e dispersada homogeneamente uma quantidade precisa e exata em atividade de um material radioativo padrão. Nesse sentido, realizou-se um estudo para a escolha da resina epóxi, analisando suas características e propriedades. Foram realizados estudos e testes, verificando a máxima miscibilidade da resina com a água (solução ácida, simulando as condições da solução radiativa), perdas de propriedades mecânicas e térmicas, bem como o controle de dose radioativa para a completa cura (irradiadores de cobalto).Foram produzidas fontes de césio-137 e bário-133, realizou-se testes para determinação do grau de homogeneidade na dispersão do material radioativo na matriz e testes de imersão das fontes seladas produzidas para verificar a estanqueidade do sistema desenvolvido, obtendo um resultado satisfatório de acordo com as normas. Analisando todos os resultados obtidos, as fontes seladas podem ser confeccionadas em matriz epóxi DGEBA e endurecedor poliamínico DETA modificado, desde que a quantidade de material radioativo, na forma de solução ácida, adicionado à composição não ultrapasse um teor de 20%. A cura da resina epóxi pode ser melhorada em relação a ambiente, com uso da irradiação desde que seja exposta a uma dose ao redor de 33 kGy durante a cura. Nos testes de estanqueidade, verificou-se que as fontes são estanques, as medições da atividade da água utilizada nos testes mostraram um valor inferior a 185 Bq (de acordo com a International Standard Organization- Radiation protection sealed radioactive sources - ISO 9978), comprovando a eficiência da resina epóxi como material para selar o material radioativo. Tendo a finalidade de criar uma tecnologia nacional capaz de suprir a demanda deste produto no mercado interno e atingir excelência em qualidade através da acreditação e certificação do produto junto aos órgãos competentes. / The radioactive sealed sources are used in verification ionization chamber detectors, which measure the activity of radioisotopes used in several areas, such as in nuclear medicine. The measurement of the activity of radioisotopes must be made with accuracy, because it is administered to a patient. To ensure the proper functioning of the ionization chamber detectors, standardized tests are set by the International Atomic Energy Agency (IAEA) and the National Nuclear Energy Commission using sealed radioactive sources of Barium-133, Cesium-137 and Cobalt-57. The tests assess the accuracy, precision, reproducibility and linearity of response of the equipment. The focus of this work was the study and the development of these radioactive sources with standard Barium-133 and Cesium-137, using a polymer, in case commercial epoxy resin of diglycidyl ether of bisphenol A (DGEBA) and a curing agent based on modified polyamine diethylenetriamine (DETA), to immobilize the radioactive material. The polymeric matrix has the main function of fix and immobilize the radioactive contents not allowing them to leak within the technical limits required by the standards of radiological protection in the category of characteristics of a sealed source and additionally have the ability to retain the emanation of any gases that may be formed during the manufacture process and the useful life of this artifact. The manufacturing process of a sealed source standard consists of the potting ,into bottle standardized geometry, in fixed volume of a quantity of a polymeric matrix within which is added and dispersed homogeneously to need and exact amount in activity of the radioactive materials standards. Accordingly, a study was conducted for the choice of epoxy resin, analyzing its characteristics and properties. Studies and tests were performed, examining the maximum miscibility of the resin with the water (acidic solution, simulating the conditions of radioactive solution), loss of mechanical and thermal properties, as well as the radioactive dose control for complete curing (cobalt irradiators). For this work was produced a sources of barium-133 and cesium -137,tests were conducted to determination the degree of homogeneity in the dispersion of the radioactive material in the matrix and immersion tests of sealed sources produced to verify the leakage (ISO 9978) of the developed system, occurring obtaining a satisfactory result. With the purpose of creating a national technology able to meet the demand of this product in the domestic market and achieve excellence in quality through accreditation and certification of the product by the appropriate bodies.

The epoxy resin has a widespread use in the manufacture of polymer composites to obtain various elements of structural engineering. The overall objective of this research is to evaluate the effect of reinforcing fabric architecture fiber-based Kevlar 49 and glass S on the mechanical performance of composites with epoxy matrix. It was observed that the mechanical performance of the epoxy resin and the composite, after natural aging and in seawater at a temperature of 70 ° C. Three architectures are designed for the production of tissue related to the structural reinforcement of the composite element: only aramid (Kevlar 49), and hybrid Kevlar 49 and glass S; varying the type of yarn and intertwining of the composition (fiber content in percentage) in each frame. The composite plates were made by hand casting process with epoxy matrix reinforced with woven fabrics of Kevlar fiber and Kevlar hybrid/glass, according to an innovative architecture. The mechanical properties of the composites were determined by tensile, bending and impact carried out in parallel and perpendicular to the warp direction. We used scanning electron microscopy to observe the reinforcement and matrix fractures after the mechanical tests. The composites with hybrid structure of Kevlar/glass on reinforcing fabric showed the best results with respect to the specific strength and impact energy. / A resina epóxi possui uma ampla utilização na fabricação de compósitos poliméricos, para obtenção de diversos elementos da engenharia estrutural. O objetivo geral desta Tese é avaliar o efeito da configuração do tecido de reforço à base de fibras de Kevlar 49 e vidro S no desempenho mecânico de compósitos com matriz epoxídica. Observou-se o desempenho mecânico da resina epóxi e do compósito, após envelhecimento natural ao ar livre e na água do mar sob temperatura de 70 ºC. Foram concebidas três configurações para produção do tecido referentes ao elemento de reforço estrutural do compósito: apenas em aramida (Kevlar 49), e híbrido de Kevlar 49 e fibra de vidro S; variando-se o tipo de entrelaçamento dos fios e composição (teor de fibra em percentual) em cada estrutura. Foram fabricadas placas do compósito pelo processo de moldagem manual com matriz epoxídica, reforçadas por tecidos planos em fibra de Kevlar, e híbrido Kevlar/vidro, de acordo com uma configuração inovadora. As propriedades mecânicas dos compósitos foram determinadas por ensaios de tração, flexão e impacto, realizados nas direções paralela e perpendicular ao urdume. Utilizou-se a microscopia eletrônica de varredura para observar as fraturas do reforço e matriz após os ensaios mecânicos. Os compósitos com estrutura híbrida de Kevlar/vidro no tecido de reforço apresentaram os melhores resultados com relação à resistência mecânica específica, bem como energia de impacto.