Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The magnetoimpedance effect (MI) in sandwiched thin films of the FeCuNbSiB/Cu produced by Magnetron Sputtering is studied using HP4396B impedance analyzer in the frequency range 100kHz-1,8GHz. The samples were produced with an alloy with composition of Fe73.5Cu1Nb3Si13.5B9 as the ferromagnetic and Cu on the normal metal. single and multilayer thin films were studied as well as sandwiched films using Cu as the central conductor. This configuration of samples exhibited high magnetoimpedance ratios The results were compatible with the theoretical prediction (for the effects of the increase of the conductivity due to the multilayer use for the samples sandwiched) MI ratios of 300% in the multilayer sample and 200% for the sandwiched samples are obtained, showing that the single multilayer sample is more suitable for MI sensors than sandwiched films. / Neste trabalho foi estudado o efeito magnetoimpedância (MI) em multicamadas e sanduíches de filmes finos produzidos por magnetron sputtering . Para isto foi utilizado um analisador de impedância HP4396B, que possibilita uma análise de freqüências na faixa de 100KHz-1.8GHz. Os estudos foram desenvolvidos utilizando-se uma liga a base de ferro com a composição de Fe73. 5Cu1Nb3Si13.5B9 como elemento ferromagnético e Cu com metal normal. Foram produzidos filmes mono e multicamadas de filmes finos, além de filmes na forma de sanduíches utilizando-se o Cu como elemento central simulando um fio condutor sanduichado com filmes ferromagnéticos. Esta configuração de amostra permite altas variações no efeito magnetoimpedância devido, principalmente, ao efeito magnetoindutivo. Os resultados mostraram-se compatíveis com as previsões teóricas (se considerado os efeitos dos aumentos da condutividade devido ao uso de multicamadas para as amostras sanduichadas), resultando variações percentuais da ordem de 300% para a MI nas multicamadas e 200% para os filmes sanduichados utilizando-se multicamadas como elemento ferromagnético. Com isto, provou-se que sensores baseados em multicamadas simples são mais adequados do que sensores baseados em sanduíches F/M/F.

Submitted by Fernanda Rodrigues de Lima (fernanda.rlima@ufpe.br) on 2018-09-25T21:59:02Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Sostynis José de Albuquerque Silva.pdf: 2081022 bytes, checksum: feffc4559b38c5ac02f7373f7833972d (MD5) / Approved for entry into archive by Alice Araujo (alice.caraujo@ufpe.br) on 2018-09-27T22:42:25Z (GMT) No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Sostynis José de Albuquerque Silva.pdf: 2081022 bytes, checksum: feffc4559b38c5ac02f7373f7833972d (MD5) / Made available in DSpace on 2018-09-27T22:42:25Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Sostynis José de Albuquerque Silva.pdf: 2081022 bytes, checksum: feffc4559b38c5ac02f7373f7833972d (MD5) Previous issue date: 2016-09-27 / CAPES / A obesidade é uma doença multifatorial de prevalência crescente e vem adquirindo proporções epidêmicas em todo o mundo, sendo um dos principais problemas da saúde pública modernos. O sistema respiratório é particularmente acometido, desenvolvendo uma síndrome restritiva com a diminuição da expansibilidade pulmonar devido a resistência da parede torácica e elevação diafragmática, levando a redução nos volumes pulmonares, especialmente o VRE. Constitui-se consenso que a abordagem clínica geralmente é ineficaz e a cirurgia bariátrica se apresenta como melhor opção de tratamento. A cirurgia bariátrica é atualmente a única modalidade terapêutica a oferecer perda de peso maciça e mantida ao longo do tempo a pacientes obesos mórbidos. Esta dissertação apresenta dois artigos originais. O primeiro foi um estudo transversal que teve como objetivo avaliar o efeito da obesidade na função e ventilação pulmonar regional de mulheres obesas mórbidas avaliadas através tomografia de impedância elétrica, tivemos como resultado que indivíduos obesos apresentam espirometria e FMR próximas à de individuos eutróficos e que o ΔZ é reduzida nos obesos, sendo a distribuição do ventilação pulmonar semelhante ao indivíduo eutrófico com maior contribuição da região direita no indivíduo obeso. O segundo foi um estudo quase experimental que teve como objetivo avaliar o impacto da cirurgia bariátrica na função e ventilação pulmonar regional de obesos mórbidos através da espirometria e tomografia de impedância elétrica. Encontramos como resultados que a cirurgia bariátrica traz prejuízos à função pulmonar e à PIMax, e parece não exercer influência sobre a Ventilação pulmonar total e regional (ΔZ e VC) e a PEMáx de obesos mórbidos, e que a distribuição da ventilação pulmonar apresenta-se semelhante no período pré e pós operatório. Constituem-se como um dos primeiros trabalhos desenvolvidos buscando elucidar o comportamento da ventilação pulmonar do obeso, afim de guiar adequadamente a terapêutica no pré e pós operatório de cirurgia bariátrica a fim de melhorar a funcionalidade do sistema respiratório desses pacientes. / This study aimed to compare the function and regional lung ventilation with obese women and eutrophic individuals by spirometry and electrical impedance tomography and to evaluate the impact of bariatric surgery in the distribution of ventilation before and after surgery. METHODS: This is a cross-sectional study in which were included 10 morbidly obese women (BMI ≥ 40 kg/m²) and 11 eutrophic women (BMI between 18.5 -24.9 kg/m²) matched by age. This is an almost experimental study was to assess the forced spirometry and monitoring a quiet breathing with the Electrical Impedance Tomography (EIT) in the pre and 1 day after bariatric surgery. Another study was experimental study to assess the forced spirometry and monitoring a quiet breathing with the Electrical Impedance Tomography (EIT) in the pre and 1 day after bariatric surgery. Statistical analysis was performed using SigmaPlot software, and applied the Shapiro-Wilk test for normality, the t test for parametric data and the Mann-Whitney test for nonparametric, was adopted as statistically significant p-value < 0.05. RESULTS: We observed reductions in the total impedance variations (ΔZ total) and regional (ΔZ left and ΔZ lower) of the obese group compared to the eutrophic. Significant reductions were found between the groups for the contribution (%) of right and left (p<0,01) regions. Despite the right region further contribute to ventilation in both groups, it was observed that in obese this contribution is even greater when compared to eutrophic with consequent reduction in the left region contribution for these individuals. CONCLUSION: It was observed that the obese women do not show differences in spirometry and RMS compared to eutrophic ones and that the ventilation of obese women is reduced, being the distribution of ventilation more contributed by the right lung, as well as in eutrophic women. It follows that bariatric laparoscopic surgery causes significant reduction in pulmonary function but with maintenance of baseline ventilation and that the distribution of ventilation is greater in the right lung in relation to the left and greater in the posterior region compared to the anterior region preoperatively and postoperatively.

Orientador: Amauri Garcia / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-09-11T21:03:40Z (GMT). No. of bitstreams: 1 Osorio_WisleiRiuperRamos_D.pdf: 6123422 bytes, checksum: 9209146531c11f89f1f12e7d688505b1 (MD5) Previous issue date: 2004 / Doutorado

Submitted by Fernanda Rodrigues de Lima (fernanda.rlima@ufpe.br) on 2018-10-08T21:28:27Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) / Approved for entry into archive by Alice Araujo (alice.caraujo@ufpe.br) on 2018-11-22T17:28:36Z (GMT) No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) / Made available in DSpace on 2018-11-22T17:28:36Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Macário Granja Gonçalves.pdf: 12281899 bytes, checksum: d3655d47934222f30676882c61c7544a (MD5) Previous issue date: 2015-03-19 / CNPq / A utilização de semicondutores orgânicos como materiais ativos em dispositivos optoeletrônicos é uma área de intensa pesquisa e inovação nos dias de hoje. Células solares baseadas em blendas de polímeros condutores ganharam muita atenção devido a suas características mecânicas e bom rendimento, ao que se combina um baixo custo de fabricação. Neste trabalho, investigamos a influência de aspectos óticos e estruturais dos materiais utilizados sobre o transporte eletrônico em dispositivos fotovoltaicos moleculares à base de polihexiltiofeno (P3HT) e 5-(2-etil-hehilóxi)-1,4-fenileno vinileno (MEHPPV) associados com fulerenos funcionalizados (PCBO), e de nanopartículas de ouro recobertas com polianilina (PANI-AuNPs). Os filmes de P3HT e MEH:PPV foram depositados a partir das soluções coloidais por meio da técnica de spin-coating, sendo cada um dos polímeros solubilizado em clorobenzeno. Através de medidas de corrente-tensão realizadas sob luz "solar simulada", e tendo a temperatura, a tensão aplicada e a área ativa dos dispositivos como parâmetros de controle, estimamos a eficiência de conversão de energia. Vale ressaltar que normalmente as técnicas convencionais utilizadas para medir mobilidade elétrica se utilizam de arranjos elétricos e ópticos acoplados, como é o caso das medidas de Tempo de Voo (TOF). Neste trabalho, como método alternativo, nos baseamos em medidas de espectroscopia de impedância elétrica na ausência de luz e com varredura na frequência para estimar a mobilidade dos portadores de carga negativos no interior dos dispositivos. Além disso, avaliamos o efeito de fatores da preparação (velocidade de rotação, temperatura de annealing e concentração de PANI-AuNPs) dos diferentes dispositivos fotovoltaicos sobre a eficiência e a mobilidade eletrônica, de modo a estabelecer a dinâmica de condução nas diferentes células solares orgânicas nanoestruturadas investigadas. / The use of organic semiconductors as active materials in optoelectronic devices is nowadays an area of intense research and innovation. Solar cells based on blends of conductive polymers have deserved a lot of attention due to their mechanical characteristics and good efficiency, which could be attained with low manufacturing costs. In this study, we investigated the influence of optical and structural aspects of the material used for the electron transport in molecular-based photovoltaic devices polihe-xiltiofeno (P3HT) and 5-(2-ethylhehiloxi)-1,4-phenylene vinylene (MEH-PPV) associated with functionalized fullerenes (PCBO) and gold nanoparticles coated with polyaniline (PANI-AuNPs). The P3HT films and MEH:PPV were deposited from colloidal solutions through the spin-coating technique, where in each case the corresponding polymer was previously solubilized in chlorobenzene. Through current-voltage measurements performed under "simulated sunlight", and taking the temperature, the applied voltage and the active area of the devices as control parameters, we were able to estimate the corresponding energy conversion efficiency. It is noteworthy that usually the conventional techniques used to measure electric mobility involve the use of coupled electrical and optical arrangements, such as is the case of the flight time (TOF) method. In this work, based on electrical impedance spectroscopic methods, in the absence of both incident light and scanning frequency, we were able to estimate the mobility of negative charge carriers within the device. Furthermore, we evaluated the effect of the preparation factors (rotation speed, temperature and annealing concentration of PANI-AuNPs) of different photovoltaic devices on the efficiency and electron mobility in order to establish different driving dynamics in organic solar cells nanostructured investigated.

Orientador: Fabricio Guimarães Baptista / Coorientador: Francesco Ciampa / Banca: André Luiz Andreoli / Banca: Paulo Roberto de Aguiar / Banca: Rosemar Batista da Silva / Banca: Breno Ortega Fernandez / Resumo: Os sistemas de monitoramento de estruturas aeroespaciais, civis e navais, também conhecidos como sistemas de SHM ("Structural Health Monitoring"), têm como objetivo a detecção de danos estruturais em estágio inicial e, desta forma, se garantir a segurança dos usuários e reduzir os custos com manutenção. Entre as várias técnicas existentes para a detecção de danos, a técnica da impedância eletromecânica (E/M) se destaca pela sua metodologia simples e por utilizar transdutores piezelétricos de baixo custo. Basicamente, o diagnóstico de falhas estruturais se dá pela extração da impedância elétrica de um transdutor acoplado em uma estrutura hospedeira, e o diagnóstico estrutural é realizado pela aplicação de índices estatísticos como o desvio da raiz média quadrática - root mean square deviation (RMSD) - que é baseado na norma Euclidiana e o desvio do coeficiente de correlação - correlation coefficient deviation metric (CCDM) - baseado no coeficiente de correlação. Apesar de ser uma técnica promissora e eficaz, as pesquisas envolvendo a técnica da impedância eletromecânica são realizadas em laboratórios sob condições ideais. Todavia, na prática, durante a medição de impedância, é inevitável a contaminação dos sinais por ruído, o que pode influenciar e prejudicar significativamente o diagnóstico de danos estruturais, limitando a aplicabilidade da técnica E/M. Tomando como base essa questão, o objetivo deste trabalho é explorar novas técnicas de processamento de sinais oriundos das... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Structural Health Monitoring (SHM) systems aim to avoid and detect structural damages at the initial stage in order to promote human safety and reduction of maintenance costs. Among numerous SHM methods for damage detection, the electromechanical impedance (EMI) technique stands out to be a simple methodology that uses low-cost piezoelectric transducers. Basically, the structural damage diagnosis is achieved by extracting the electrical impedance of a transducer attached to a host structure and the failure quantification is accomplished by traditional statistical indices such as the root mean square deviation (RMSD) and the correlation coefficient deviation metric (CCDM). Although the EMI stands out to be an effective and promising SHM technique, research involving the electromechanical impedance is commonly performed in laboratories under ideal conditions. However, in practical applications, during the impedance measurements, it's inevitable the signal contamination by noise, which can significantly influence and impair the diagnosis of structural condition, limiting the applicability of the EMI. Based on this issue, the objective of this work is to explore new signal processing techniques from impedance measurements of piezoelectric transducers, aiming to expand the applicability of this promising SHM approach for low signal-to-noise ratio inspections conditions. Experimental tests were carried out on a carbon fiber reinforced plate and an aluminum component, which are wide... (Complete abstract click electronic access below) / Doutor

Orientador: Prof. Dr. Daniel Zanetti de Florio / Dissertação (mestrado) - Universidade Federal do ABC, Programa de Pós-Graduação em Nanociências e Materiais Avançados, 2014. / Motores a combustão flexíveis foram desenvolvidos para diversificar a utilização de combustíveis para a indústria da mobilidade, com o intuito de trazer benefícios econômicos, ganho em sustentabilidade e redução do impacto ambiental. Tal diversificação tem proporcionado o desenvolvimento de linhas de pesquisa que aperfeiçoem essa utilização, através de incentivo fiscal do governo, bem como injeção de recursos da indústria nas universidades como, por exemplo, o programa Inovar Auto. Dentre os novos combustíveis está o etanol que devido às suas características físico-químicas, como a sua pressão de vapor traz vantagens como ganho de torque e potência e desvantagens como aumento de desgaste e corrosão dos componentes metálicos a ele expostos. As bronzinas são partes de base metálica que promovem a redução do contato metal-metal entre as principais peças de um motor como bloco, virabrequim e biela, além de permitirem uma melhor hidrodinâmica do óleo lubrificante, aumentando a vida útil do motor. Significativamente expostas ao ambiente etanol, óleo, gases e água, as mesmas são suscetíveis ao fenômeno de corrosão. Análise de corrosão por espectroscopia de impedância eletroquímica é um método conhecido na literatura e motivou a caracterização eletroquímica de componentes cíclicos metálicos de motores, através da obtenção de espectros de impedância para três diferentes recobrimentos em bronzinas, expostos sistematicamente a condicionamentos e envelhecimentos, variando-se temperatura, tempo de exposição em mistura óleo e etanol comuns. Dentre os três recobrimentos está uma proposta cerâmica a partir de óxido de boro depositado por uma técnica comum denominada slurry, apresentada na literatura aeroespacial com vantagens tribológicas. As medições foram feitas em solução aquosa de cloreto de sódio a 0,1 M, utlizando-se um eletrodo de referência de prata e cloreto de prata, um eletrodo de medição de platina como contra eletrodo e um eletrodo de trabalho com amostras de aço embutidas e recobertas com três diferentes superfícies; metálica (VW1), polimérica (P1) e cerâmica (C1), dispostos em uma célula ligada a um impedancímetro e a um potenciostato de marca Solartron. A intersecção do semicírculo do espectro com o eixo das abcissas ou parte real da impedância, Z¿ é conhecida como resistência de polarização Rp. Da literatura sabe-se que esta grandeza é proporcional ao inverso da corrente e taxa de corrosão da superfície do eletrodo de trabalho. A obtenção desta variável pode ser feita através de aproximações, com modelos de circuitos equivalentes RC, que calculam as resistências e capacitâncias destes circuitos. A partir do tratamento dos dados acima descritos, foi possível estabelecer três diferentes tendências de comportamento da taxa de corrosão ao longo do tempo de exposição ao meio etanol mais óleo, a saber: amostra de superfície metálica tipo VW1 apresentou corrosão dinâmica e controlada com taxa de corrosão decrescente ao longo do tempo; amostra polimérica tipo P1 apresentou também redução da taxa de corrosão por passivação ao longo do tempo após penetração da camada polimérica e; amostra cerâmica de óxido de boro tipo C1 apresentou maior redução da taxa de corrosão ao longo do envelhecimento em óleo e etanol. / Flex fuel combustion engines were developed to diversify the use of fuels for the mobility industry, in order to bring economic benefits gain in sustainability and environment impact reduction. Such diversification has permitted the research line development which optimizes this use through government incentive as well as fund injection in universities such as Inovar Auto program. Ethanol is among the new fuels, which due to its physical-chemical characteristics (vapor pressure) presents advantages as power and torque and disadvantages, as waste increase and corrosion of the exposed metal components. The bearings are parts made of metal that promote the metal-metal contact reduction among the main engine parts like cylinder block, cranckshaft and connecting rods. Besides, they allow better hydrodynamics of the lubrication oil increasing the duration of a flex combustion engine. Exposed to the ethanol, oil, gases and water environment these bearings are prone to corrosion phenomenon. The corrosion analysis by impedance spectroscopy corrosion is a method known in the literature and has motivated the electrochemical characterization of metal cyclic components by obtaining impedance spectra for three different recovering in bearings. The third type of recovering was developed through bore oxide produced by slurry coating techniques, which was presented on a aerospacial research publication with tribologic gain. These are systematically exposed to conditionings and aging while varying temperature, exposure time and rotation of oil and ethanol common mixtures. The measurements were made on aquous solution of NaCl 0,1 M through a reference silver and silver cloride eletrode, a platine counter eletrode and the work eletrode with samples of the three different bearings surface, metallic (VW1), polymeric (P1) and ceramic (C1) all assembled in a eletrochemistry cell, switched to a potenciostat and an impedancimeter, both by Solartron. The intersection of the semicircle spectra with "X" axle or real part of the impedance Z¿ is known as polarization resistance Rp. From the bibliography review it is known that this resistance is proportional to the inverse of corrosion rate on the surface of the working electrodes. The obtention of this variable could be done through approximation of RC circuit models, which calculate the resistances and the capacitances. Through data treatment it was possible to establish three different tendencies of corrosion rate behavior during ethanol and oil exposure time: Metallic surface sample type VW1 presented dynamic controlled with descending corrosion rate during the aging processes. Polymeric recovery sample type P1 also presented reduction of corrosion rate after penetration of the polymeric recovering e less during the aging processes. Ceramic recovery sample type C1 presented major reduction of corrosion during the aging on oil plus ethanol.

Orientador: Fabricio Guimarães Baptista / Banca: Luiz Gonçalves Junior / Banca: Mário Anderson de Oliveira / Resumo: A técnica da impedância eletromecânica (E/M) tem sido amplamente estudada nas últimas décadas como um método não destrutivo para detectar danos estruturais em aplicações de monitoramento de integridade estrutural (SHM - structural health monitoring) usando transdutores piezelétricos de baixo custo. Esses transdutores operam simultaneamente como sensor e atuador e são fixados à estrutura monitorada utilizando um adesivo a base de cianoacrilato. Embora muitos estudos tenham relatado a eficácia desse método de detecção, inúmeros problemas práticos têm sido reportados, como os efeitos de ruído e vibração, que precisam ser considerados para permitir o uso eficaz desse método em aplicações reais. Portanto, esta dissertação de mestrado apresenta uma análise experimental dos efeitos do ruído e das vibrações na detecção de danos estruturais em sistemas de SHM baseados na técnica da impedância eletromecânica. Os experimentos foram realizados em uma barra de alumínio usando dois diafragmas piezelétricos, sendo que um deles foi usado para obter as assinaturas de impedância elétrica e o outro foi usado como atuador para introduzir ruído e vibração controlada. Para a simulação de dano foi utilizada uma pequena massa metálica fixada na estrutura com uso de adesivo a base de cianoacrilato. Os efeitos do ruído e da vibração sobre as assinaturas de impedância foram avaliados por meio do cálculo da função de coerência e de índices básicos de dano. Os resultados indicam que a vibração e o ruído ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The electromechanical impedance (EMI) technique has been extensively studied in recent decades as a non-destructive method for detecting structural damage in structural health monitoring (SHM) applications using low-cost piezoelectric transducers. These transducers operate simultaneously as actuator and sensor and they are fixed to the structure using cyanoacrylate-based glue. Although many studies have reported the effectiveness of this detection method, a lot of practical problems shown up, such as the noise effects and vibration, that need to be addressed to enable this method's effective use in real applications. Therefore, this master's thesis presents an experimental analysis of noise and vibration effects on the structural damage detection in impedance-based SHM systems. The experiments were performed on an aluminum bar using two piezoelectric diaphragms, where one was used to measure the electrical impedance signatures and the other was used as an actuator to introduce noise and controlled vibration. To simulate damage, a small metal mass was fixed to the structure using cyanoacrylate glue. The effects of noise and vibration on the impedance signatures were evaluated by computing the coherence function and basic damage indices. The results indicate that vibration and noise significantly affect the threshold of the lowest detectable damage, which can be compensated by increasing the excitation signal of the piezoelectric transducer that measure the electrical impedance... (Complete abstract click electronic access below) / Mestre

O condutor protônico zirconato de bário dopado com ítrio (BaZr1-xYxO3-&delta;, BZYx) é um material promissor para a aplicação como eletrólito sólido em células a combustível operacional em temperaturas intermediárias (400 a 700 oC). No entanto, sua natureza refratária (ponto de fusão ~ 2600 oC) faz com que para sua densificação, necessária para sua aplicação como eletrólito, sejam necessários altas temperaturas e longos tempos de tratamento térmico (1600 a 1800 °C por 24 a 48 h). Tais condições extremas causam um desvio da estequiometria de bário que afeta a química de defeitos do material e, consequentemente a diminuição da condutividade protônica do BZYx. Portanto, o processamento desse eletrólito sólido em menores temperaturas, preservando sua estequiometria, formando uma microestrutura densa e com baixa resistividade inter-granular são os principais objetivos e desafios da comunidade científica. Visando aumentar a sinterabilidade das partículas, o BZY foi preparado pelo método dos peróxidos oxidantes (OPM). O procedimento experimental original do OPM foi modificado e otimizado para viabilizar a formação do BZYx, com x = 10 a 50 mol% de Y3+. Dentre as modificações, a síntese foi feita com e sem o controle da atmosfera, em câmara de luvas sob atmosfera de nitrogênio e ao ar, respectivamente. As propriedades estruturais, morfológicas, térmicas, termodinâmicas e elétricas das composições de BZYx foram investigadas. As amostras produzidas foram calcinadas em diversas temperaturas e investigadas quanto à sua sinterabilidade e densificação. Os pós de BZYx, com x = 10 a 50 mol% de Y3+, produzidos com controle da atmosfera foram investigados quanto às suas propriedades termodinâmicas. Os valores de entalpia de formação a partir dos óxidos (&Delta;Hf,ox) foram calculados com os dados obtidos por calorimetria de dissolução a alta temperatura. As amostras de BZY10 e BZY20 produzidas com controle da atmosfera atingiram condutividade elétrica total de 1,6 x 10-3 e 1,3 x 10-3 S/cm a 530 oC, respectivamente. A alta resistividade inter-granular contribui para a alta resistividade total das amostras. A análise por espectroscopia Raman e os valores de &Delta;Hf,ox obtidos sugerem que para valores de Y3+ > 20 mol% ocorrem interações defeito-defeito na estrutura cristalina, causando à diminuição de sítios efetivos para a hidratação e a diminuição da mobilidade dos prótons na estrutura e, consequentemente, a diminuição da condutividade protônica total. / The proton conductor oxide yttrium doped barium zirconate (BaZr1-xYxO3-&delta;, BZYx) is a promising solid electrolyte for solid oxide fuel cells (SOFC) operating at intermediate temperatures (400 to 700 oC). However, the BZY refractory nature (MP ~ 2600 oC) inhibits the achievement of the densification needed for application in SOFCs (relative density &ge; 95% T.D.), requiring long dwell times and high temperatures (T &ge; 1600 oC, t &ge; 24 h). Those extreme conditions cause barium stoichiometry deviation, which affects the defect chemistry and the depletion of proton conductivity. Therefore, BZY processing in less aggressive conditions, preserving cation stoichiometry, leading to dense microstructures with low intergranular resistivity are the great challenges of the scientific community nowadays. Aiming to increase particles sinterability, BZYx (x = 10 to 50 mol% of Y3+), solid solutions where synthesized by the Oxidant Peroxide Method (OPM). The original OPM experimental procedure was modified to allow the BZY formation with different dopant content. One of the modifications was to carry out the synthesis under laboratory and nitrogen atmospheres. The study of structural, thermal, morphological, thermochemical and electrical properties of all samples was performed. The samples where calcined at different temperatures and the particles sinterability and densification were also investigated. The thermochemical properties of BZYx solid solutions were investigated by high temperature oxide melt solution calorimetry, for evaluation of the formation enthalpies (&Delta;Hf,ox). The total electrical conductivity of the BZY10 and BZY20 sintered samples synthesized under nitrogen was 1.6 x 10-3 and 1.3 x 10-3 S/cm at 530 oC, respectively. The blocking of charge carriers at interfaces contributes to the low total electrical conductivity. Raman spectroscopy analysis and the evaluated &Delta;Hf,ox values obtained suggest that from 20 mol% Y3+, defect interaction might happen, leading to vacancy clustering. This effect might cause the depletion of mobile oxygen vacancies, affecting the mobility of protons, with a decrease in proton conductivity.

A análise precisa dos resultados da timpanometria é essencial para determinar a condição da orelha média, principalmente em crianças nos primeiros anos de vida. Assim, o objetivo deste estudo foi apresentar um padrão de análise da timpanometria com sonda de 226 Hz para a faixa etária de seis meses a três anos, considerando a pressão do pico de máxima compliância e a compliância estática. Foram analisados prontuários de crianças de seis meses a três anos de idade atendidas no período de outubro de 2012 a fevereiro de 2016 no Centro de Pesquisas Audiológicas - Seção de Implante Coclear do Hospital de Reabilitação de Anomalias Craniofaciais e na Clínica de Audiologia Infantil da Clínica de Fonoaudiologia da Faculdade de Odontologia de Bauru, ambos da Universidade de São Paulo. A casuística foi dividida em dois grupos: grupo sem alteração de orelha média, composto por 224 orelhas, e o grupo com alteração de orelha média, composto por 59 orelhas. Foram considerados para análise os valores de pressão do pico de máxima compliância (daPa) e de compliância estática (ml) obtidos na timpanometria com sonda de 226Hz. No grupo sem alteração, o Teste Correlação Mann Whitney revelou que não houve diferença significante entre os sexos para pressão do pico de máxima compliância (p=0,782) e para a compliância estática (p=0,085). Também não houve correlação dos valores de pressão (p=0,678) e compliância (p=0,079) com a idade, de acordo com o Teste Correlação de Spearman. Considerando o intervalo entre os percentis 2,5 e 97,5 obtidos para a pressão e compliância nos grupos sem e com alteração, observou-se uma faixa de valores comum aos dois grupos, ou seja, os valores contidos nesta faixa não conseguiram classificar a orelha média como normal ou alterada. De acordo com os percentis 2,5 e 97,5, foi possível estabelecer uma faixa de normalidade para a pressão do pico de máxima compliância, de +52 daPa a -100 daPa, e para compliância estática, de 0,20 ml a 0,68 ml. Enquanto que na faixa de alteração, os valores variaram de -259 a 17,52 daPa para pressão e de 0,04 a 0,41 ml para a compliância. Assim, uma faixa de intersecção foi identificada, correspondente ao intervalo de -100 a 17,52 daPa para pressão do pico de máxima compliância e de 0,2 a 0,41 ml para a compliância estática. A análise dos dados demonstrou que a timpanometria com sonda de 226 Hz apresentou alta sensibilidade e baixa especificidade na faixa etária de seis meses a três anos. / Accurate analysis of tympanometry results is essential to determine the condition of the middle ear, especially in children in their first years of life. Thus, this study aimed at presenting a standard analysis of tympanometry with a 226 Hz probe for the age range six months to three years, taking into account the pressure of the peak of maximum compliance and static compliance. The records of 6-month to three-year old children assisted from October 2012 to February 2016 at the Audiology Research Center - Cochlear Implant Section of the Craniofacial Anomalies Rehabilitation Hospital and at the Children\'s Audiology Clinic of the Audiology and Speech-Language Pathology Clinic of the Bauru Dentistry School, both of the University of São Paulo, were analyzed. The sample was divided into two groups: a group with no middle ear alteration comprising 224 ears and the group with middle ear alteration composed of 59 ears. For analysis, the pressure values of the maximum compliance peak (daPa) and static compliance (ml) obtained in the tympanometry with a 226Hz probe were considered. In the group with no alteration, the Mann Whitney Correlation Test showed no significant difference between the genders for the maximum compliance peak pressure (p = 0.782) and for static compliance (p = 0.085). No difference was seen, either, for pressure (p = 0.678) and compliance (p = 0.079) values, according to age, by using the Spearman Correlation Test. Considering the interval between percentiles 2,5 and 97,5 obtained for pressure and compliance in the groups without and with alteration, a range of values common for the two groups was observed, that is, the values contained in this range could not classify the Middle ear as normal or altered. According to percentiles 2,5 and 97,5, it was possible to establish a range of normality for the pressure of the maximum compliance peak, from +52 daPa to -100 daPa, and for static compliance, from 0.20 ml to 0.68 ml, while in the alteration range, values ranged from -259 to 17,52 daPa for pressure and from 0,04 to 0,41 ml for compliance. Thus, an intersection range was identified, corresponding to the interval of -100 to 17,52 daPa for the pressure of the maximum compliance peak and 0,2 to 0,41 ml for the static compliance. Data analysis showed that tympanometry with a 226 Hz probe presented high sensitivity and low specificity in the 6-month to 3-year age range.

Os objetivos deste trabalho foram a implantação e a otimização da técnica de sinterização a laser de corpos cerâmicos, o estudo da cinética do processo e a avaliação de propriedades físicas dos compostos Bi4Ti3O12 e Bi4Ge3O12 sinterizadas a laser, em comparação com as cerâmicas processadas em forno convencional. A escolha dos materiais baseou-se em seu potencial de aplicação: o Bi4Ge3O12 como dispositivo cintilador e o Bi4Ti3O12 como cerâmica eletrônica. A sinterização a laser mostrou-se eficiente para estes materiais, produzindo cerâmicas com densidade superior a 98 % e pequeno tamanho de grão. A combinação de pré-aquecimento e subida gradual da potência do laser evitou gradientes de temperatura e taxas de aquecimento excessivos, e reduziu consideravelmente a incidência de trincas e a porosidade nas cerâmicas. No estudo cinético da sinterização a laser, registraram-se energias de ativação inferiores às observadas no processamento convencional, exceto para o BIT no estágio final de sinterização, e os resultados sugerem um adiantamento no processo de sinterização, provocado por efeito da irradiação a laser. A caracterização física do BIT foi feita por espectroscopia de impedância e medidas de histerese ferroelétrica. Comparado à cerâmica convencional, o corpo cerâmico sinterizado a laser apresentou condutividade elétrica 3 vezes menor na região de bulk, maior permissividade dielétrica acima de 300 °C, com igual perda dielétrica, mesmo campo coercitivo e polarização remanescente 35 % superior. A caracterização física do BGO foi feita por medidas de absorção óptica, radioluminescência e termoluminescência. Os resultados mostraram que a cerâmica de BGO sinterizada a laser possui grau de transparência 50 % maior, densidade de defeitos estruturais 2 vezes menor, eficiência levemente superior e mesmo dano por radiação, se comparada à cerâmica sinterizada em forno elétrico. Os resultados obtidos foram interpretados com base na escala de tempo característica da sinterização a laser, que afeta a formação e distribuição dos defeitos durante o processo, e resulta em cerâmicas com microestrutura diferenciada. / The goals of this work were the implantation and optimization of the laser sintering technique for ceramic bodies, the kinetic study of the process and the evaluation of the physical properties of the laser sintered compounds Bi4Ti3O12 and Bi4Ge3O12, compared to ceramics sintered in conventional furnace. The choice of the materials was based on their potential applications: Bi4Ge3O12 as scintillator device and Bi4Ti3O12 as an electronic ceramic. Laser sintering showed to be efficient for these materials, producing ceramics with density higher than 98 % and small grain sizes. The combination of pre-heating with a gradual rising of the laser power prevented excessive temperature gradient and heating rate, and reduced considerably the incidence of cracks and pores in the ceramics. The kinetic study of the laser sintering revealed lower activation energies than that observed in the conventional processing, except for BIT ceramics during the final stage of sintering. The results suggest that the laser irradiation anticipates the stages of the sintering process. The physical characterization of BIT was done through impedance spectroscopy and ferroelectric hysteresis measurements. Compared to the conventional sample, this material presented bulk electrical conductivity 3 times smaller, higher dielectric permittivity above 300 °C, comparable dielectric loss, the same coercive field and 35 % higher remanent polarization. The physical characterization of BGO was done through optical absorption, radioluminescence and thermoluminescence measurements. The results showed that the transparency of the laser sintered BGO ceramic was 50 % higher than the transparency of the conventional BGO ceramic, the density of structural defects is 2 times lower, the radiation damage levels are comparable and the overall scintillating efficiency is slightly higher. The obtained results were interpreted on the basis of the time scale of the laser sintering, which affects the formation and distribution of defects during the process, and results in a particular microstructure.