The aim of this study was to evaluate in vivo, using beagle dog model, the effect of incorporation of biossilicato (highly bioactive glass) on the process of osteogenesis through the bone-implant contact and evaluate in vitro using model cell culture, the influence of the incorporation of biossilicato the rough surface on titanium discs adhesion and cell viability. The implants used for the in vivo study (n = 32) were 10 mm long and 3.5 mm in diameter and having surface treated with double etching. Half of these implants (n = 16) received the incorporation of biossilicato on its surface roughened (Group AA + BIO), while the other half only with rough surfaces (n = 16) was used as control group (group AA). The in vitro assays used commercially pure titanium disks grade IV 8.0 mm diameter by 4.0 mm in height with the same characteristics of implants used in in vivo tests. The assessment from scanning electron microscopy revealed that about 25% of the implant surface was covered by highly bioactive glass so homogeneous. Surface double etching associated biossilicato (AA + BIO) also showed a lower contact angle (α10s = 5.3 ± 1.7 °) compared with the AA surface. The adhesion test used to verify the stability of highly bioactive glass particles embedded on both disks as implants, demonstrate adequate stability, with no disruption of the interface bond between the particle and the surface of titanium. The results of in vitro through cell culture, showed that the percentage of viable cells adhered to the roughened surface covered with biossilicato (AA + BIO) was significantly lower (p <0.001) than the group with surface - AA (P = 0.004). The cell viability test showed that there were no statistically significant differences between groups AA and AA + BIO in any of the periods analyzed. The histomorphological results suggest that the initial repair is not affected by surface AA + BIO compared with the surface only with double etching. / O objetivo deste estudo foi avaliar in vivo, utilizando modelo de implantação em mandíbula de cães, o efeito da incorporação de biossilicato (vidro bioativo) sobre o processo de neosteogênese por meio do contato osso-implante e, avaliar in vitro, utilizando modelo de cultura de células, a influência da incorporação do biossilicato na superfície rugosa de discos de titânio sobre a adesão e viabilidade celular. Os implantes usados para o estudo in vivo (n=32) eram de 10 mm de comprimento e 3,5 mm de diâmetro e conexão cone Morse apresentando superfície tratada com duplo ataque ácido. Metade desses implantes (n=16) recebeu a incorporação de biossilicato em sua superfície rugosa (Grupo AA+BIO), enquanto a outra metade apenas com superfícies rugosa (n=16) foi utilizada como grupo controle (Grupo AA). As análises in vitro utilizaram discos de titânio comercialmente puro grau IV de 8,0 mm de diâmetro por 4,0 mm de altura com as mesmas características dos implantes utilizados nos testes in vivo. A avaliação a partir de microscopia eletrônica de varredura revelou que cerca de aproximadamente 25% da superfície dos implantes foi coberta pelo vidro bioativo de forma homogenea. Superfície com duplo ataque ácido associado ao biossilicato (AA+BIO) também apresentou um menor ângulo de contato (α10s=5,3±1,7º) quando comparada com a superfície AA. Os testes de adesão utilizados para verificar a estabilidade das partículas do vidro altamente bioativo incorporado tanto aos discos quanto aos implantes, demostraram uma adequada estabilidade, não havendo rompimento da interface de união entre a partícula e a superfície de titânio. Os resultados in vitro, por meio de cultura de células, demostraram que a percentagem de células viáveis aderidas à superfície rugosa coberta com biossilicato (AA+BIO) foi significativamente menor (p <0,001) do que o grupo com superfície - AA (P = 0,004). O teste de viabilidade celular demonstrou que não houve diferenças estatisticamente significativas entre os grupos AA e AA+BIO em nenhum dos períodos analisados. Os resultados histomorfológicos sugerem que a fase inicial do reparo não é afetada pela superfície com AA+BIO quando comparada com a superfície apenas com duplo ataque ácido. / Mestre em Odontologia

A ausência do perfeito ajuste e o assentamento passivo dos pilares sobre implantes podem provocar tensões inadequadas na interface de osseointegração, possibilitando problemas mecânicos e biológicos. A fotoelasticidade é uma técnica experimental para análise de tensões capaz de produzir resultados confiáveis e fiéis aos parâmetros clínicos. Assim, este estudo teve como objetivos avaliar por meio de microscopia ótica a adaptação marginal entre pilares intermediários tipo mini pilar cônico e a estrutura metálica com desenho geométrico em viga I fundida com liga de cobalto-cromo (CoCr). Analisaram-se, também, por meio de fotoelasticidade, as tensões geradas ao redor dos implantes por essa mesma estrutura metálica quando submetida a cargas estáticas em função da variação do número de pilares (4 ou 5) e da inclinação dos implantes distais (para o modelo de 5 implantes). As análises foram feitas antes e após o seccionamento das barras e soldagem a laser. Foram obtidas dez infraestruturas em viga I, fundidas em monobloco, utilizando-se liga de cobalto cromo. A análise da adaptação marginal foi realizada em estereomicroscópio sob aumento de 20X. Modelos fotoelásticos para 4 ou 5 implantes foram confeccionados e realizada a mensuração da tensão ao redor dos implantes. As barras foram seccionadas e soldadas por laser e novas medidas de adaptação marginal foram realizadas, bem como foram confeccionados novos modelos fotoelásticos para as estruturas soldadas. A análise da passividade das vigas I em monobloco não se mostrou estatisticamente significante (p&le;0,05), a passividade no pilar oposto foi sempre menor que a do pilar parafusado antes e após a soldagem a laser, não houve diferença estatística no desajuste vertical entre as vigas I para quatro e cinco implantes, antes e após a soldagem a laser. A soldagem a laser gerou maior passividade e menor desajuste vertical nas vigas I. A análise fotoelástica mostrou que a soldagem a laser ocasionou menor tensão nos implantes quando não há aplicação de carga na viga I para quatro implantes, mas aumentou a tensão em viga I para cinco implantes. Assim, pode-se concluir que a soldagem a laser gerou maior passividade e menor desajuste vertical entre os pilares e o implante, e menor tensão ao redor dos implantes em vigas I de quatro implantes, e maior tensão em viga I para cinco implantes. / The absence of perfect fit and passivity on implants can cause stress on the osseointegration interface, enabling biomechanical problems. Photoelasticity is an experimental technique for stress analysis can produce reliable results and faithful to clinical parameters. Thus, the aim of this study was to assess by light microscopy the marginal adaptation of mini pillar intermediate and superstructure with geometric design I beam with cast cobalt-chromium (CoCr). It was analyzed also by means of photoelasticity, the tensions generated around the implants by the same metal superstructure when subjected to static loads due to the variation in the number of implants (4 or 5) and tilting the distal (for model 5 implants). Analyses were made before and after sectioning of the bars and laser welding. It was obtained ten I-beam superstructure I, cast in cobalt chromium alloy. The analysis of marginal adaptation was performed in a stereomicroscope under magnification 20X. Photoelastic models for 4 or 5 implants were made and carried out the measurement of the tension surrounding the implants. The bars were cut and welded by laser and marginal adaptation of new measures were taken and new photoelastic models were made for welded structures. The analysis of the passivity of the I-beams in a single block was not statistically significant (p&le;0.05), passivity on the pillar opposite was always less than the abutment screws before and after laser welding, there was no statistical difference in the vertical misfit between I-beams for four and five implants before and after laser welding. The laser welding has generated greater passivity and lower beams in vertical misfit I. The photoelastic analysis showed that laser welding caused less stress on the implants when there is no application of load over four implants, but increased the tension for five implants. Thus, it can be concluded that laser welding generated more passivity and less vertical fit between the pillars and the implant, and less tension around the implants in four implants, and higher stress for five implants.

Este estudo tem como objetivo apresentar uma análise retrospectiva de dados contidos em prontuários de atendimento, sobre a evolução clínica de 129 implantes zigomáticos colocados no seio maxilar de 37 pacientes com maxila desdentada severamente reabsorvida (total ou parcialmente), os quais foram reabilitados através da instalação de implantes zigomáticos pela equipe de Cirurgia e Traumatologia Buco-Maxilo-Facial da Faculdade de Odontologia de Ribeirão Preto (FROP-USP), durante o período março/2007 à novembro/2014. Todos os pacientes incluídos no estudo foram tratados usando o mesmo protocolo cirúrgico, técnica ´´sinus slot´´ modificado por Stella. A análise foi direcionada a registro de dados relativos as seguintes variáveis: gênero, idade, raça, história médica, etiologia, vícios, grau de atrofia óssea, tipo e tamanho dos implantes zigomáticos, número de implantes colocados, reabilitação protética, a taxa de sobrevivência e de sucesso dos implantes, além das complicações. Os indivíduos foram acompanhados por meio de exames clínicos e de tomográficos padronizados. O critério de inclusão dos prontuários na amostra foram de pacientes submetidos a esse tipo de tratamento, com preenchimento completo de informações e de possuírem o Termo de Consentimento Livre e Esclarecido. Os dados coletados por um único examinador foram transportados para uma planilha eletrônica utilizando o programa Microsoft Excel, sendo realizada neste momento uma análise descritiva dos resultados. Trinta e sete pacientes consecutivos (25 mulheres, 12 homens; média de idade de 55,64 anos [variação: 40-77 anos]) foram tratados. Todos estavam em necessidade de reabilitação bucal e tinham atrofia maxilar severa com indicação para a colocação de implantes zigomáticos. Cento e vinte e nove implantes zigomáticos foram colocados nesses 37 pacientes. Dois dos 129 implantes falharam, resultando em uma taxa de sucesso de 98,44%, com esses dados de acompanhamento. Sinusite do seio maxilar foi a ocorrência mais comum (21,62%) entre as complicações encontradas. No entanto, entre os implantes que falharam, nenhum foi relacionado com sinusite ou fumo. Concluímos que tratamento com implantes zigomáticos representa uma opção previsível para reabilitação da maxila atrófica desdentada. No entanto, mais estudos são necessários para se relacionar diretamente esses implantes com a sinusite, que apresenta uma elevada prevalência nestes casos. / This study aims to present a retrospective analysis of data contained in patient records on the clinical course of 129 zygomatic implants placed in the maxillary sinus of 37 patients with severely resorbed edentulous maxilla (fully or partially), which were rehabilitated by installing of zygomatic implants by staff of Surgery and Traumatology Oral and Maxillofacial Ribeirão Preto Dental School (FROP-USP), during the period from March/2007 to November/2014. All patients included in the study were treated using the same surgical protocol, \'\'sinus slot\'\' modified by Stella technique. The analysis was aimed at data record the following variables: gender, age, race, medical history, etiology, addictions, degree of bone atrophy, type and size of zygomatic implants, number of placed implants, prosthetic rehabilitation, the survival rate and success of the implant, in addition to complications. The subjects were followed through clinical and standardized CT. The criterion for inclusion of the records in the sample were patients undergoing this type of treatment, with complete filling of information and possess the Informed Consent and Informed. The data collected by a single examiner were transported to a spreadsheet using Microsoft Excel program, being carried out at present a descriptive analysis of the results. Thirty-seven consecutive patients (25 women, 12 men; mean age of 55.64 years [range, 40-77 years]) were treated. All were in need of oral rehabilitation and had severe jaw atrophy indicated for the placement of zygomatic implants. One hundred and twenty-nine zygomatic implants were placed in these 37 patients. Two of the 129 implants fail, resulting in a success rate of 98.44%, with these tracking data. Maxillary sinus sinusitis was the most common event (21.62%) among the complications found. However, between implants that have failed, none has been associated with sinusitis or smoke. We conclude that treatment with zygomatic implants is a predictable option for rehabilitation of edentulous atrophic maxilla. However, more studies are needed to relate directly with these implants sinusitis, which has a high prevalence in these cases.

Orientador: Mauro Antonio de Arruda Nobilo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T22:47:57Z (GMT). No. of bitstreams: 1 Damaceno_AlessandraReginaDerogis_D.pdf: 2207812 bytes, checksum: bee72ab72dd5b1ab3d0126a21f181256 (MD5) Previous issue date: 2007 / Resumo: Este estudo avaliou comparativamente a influência de diferentes intermediários protéticos na indução de tensões em infra-estruturas implanto-suportadas soldadas a laser através da análise fotoelástica. Para isso, foram confeccionadas três infra-estruturas metálicas em monobloco, fundidas em titânio, sobre uma matriz metálica com forma e dimensões similares ao arco mandibular, sendo: 1- infra-estrutura confeccionada com pilares Ucla; 2- infra-estrutura confeccionada sobre pilares Esteticone e 3- infra-estrutura confeccionada sobre pilares Microunit. Após avaliação da interface de adaptação em microscopia óptica e análise de passividade em polariscópio circular, as peças foram seccionadas e submetidas à soldagem vertical a laser. As peças foram novamente avaliadas em relação à adaptação e posteriormente submetidas à análise fotoelástica para comparação do padrão de tensões. Os resultados mostraram a eficiência da soldagem a laser na redução de tensões induzidas pelas infra-estruturas. O método ainda permitiu formação de diferentes padrões de comportamento para os diferentes pilares. Os maiores valores de ordem de franja foram encontrados para a infra-estrutura confeccionada sobre pilares Ucla, seguida daquela sobre pilares Esteticone e por último daquela sobre pilares Microunit. No entanto, a distribuição de tensões ao redor dos implantes foi mais homogênea quando os pilares Esteticone e Microunit foram utilizados. Os valores de desadaptação vertical após soldagem laser encontrados para os diferentes pilares foram de 147.9µm, 389µm e 179.4µm respectivamente para os pilares Ucla, Esteticone e Microunit. Concluiu-se que a técnica de soldagem a laser de infra-estruturas implanto-suportadas reduz significativamente a indução de tensões aos implantes, e que a utilização de pilares intermediários, apesar de permitir maior desajuste marginal das peças, distribui melhor o padrão de formação destas tensões geradas ao redor dos mesmos, com maiores (Esteticone) ou menores (Microunit) valores de ordem de franja / Abstract: This study evaluated the influence of different abutments on stress formation by implant-supported frameworks submitted to laser welding through photoelastic analysis. Three titanium frameworks were cast in-one-piece in a metallic master cast with shape and dimension of mandibular arch: I ¿framework fabricated with Ucla abutments, II ¿framework fabricated over Esteticone abutment and III- framework cast over Microunit abutment. After fit optical microscopy evaluation and non passive analysis in circular polariscopy, the frameworks were sectioned and submitted to vertical laser welded to posterior optical and stress formations analysis to compares the abutments tested. Results showed the laser weld efficiency in the implanted-supported framework stress reduction although had allowed different stress formation patterns among the abutments. The higher franje order number was attributed to the framework cast with Ucla abutments, followed by that cast over Esteticone and Microunit abutments respectively. However the distribution of stress pattern around implants was better with esteticone and microunit abutments utilization. After laser welding the vertical marginal fit found were 147.9µm, 389µm and 179.4µm to Ucla, Esteticone and Microunit abutments, respectively. This study concluded that the laser welding technique reduced significantly the stress formation in the implanted-supported frameworks and although the use of abutments increase the marginal fit of frameworks it allowed the better stress pattern distribution around the implants with higher (Esteticone) and lower (Microunit) franje order number values. Keywords: fixed implant prosthesis, passivity, photoelastic analysis / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: José Ricardo de Albergaria-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T16:30:04Z (GMT). No. of bitstreams: 1 Moraes_PauloHemersonde_M.pdf: 14156681 bytes, checksum: ca90b60d99caa756d6b1104881f6bf54 (MD5) Previous issue date: 2011 / Resumo: Com o avanço da implantodontia, as maxilas edêntulas atróficas que anteriormente eram indicações de enxertos ósseos para viabilizar a reabilitação com implantes dentais, atualmente é possível contornar a maioria destes quadros clínicos sem a necesidade de enxertos ósseos utilizando técnicas como implantes zigomáticos. No entanto, visando a manutenção destes tratamentos aplicados, torna-se essencial o conhecimento do comportamento biomecânico destas modalidades de tratamentos. Diante do exposto, a presente pesquisa apresenta 3 estudos biomecânicos ¿in vitro¿ descritos nos capítulos a seguir. CAPÍTULO I: O objetivo deste estudo foi analisar as tensões mecânicas ao redor dos implantes e ossos adjacentes por meio de análise fotoelástica simulando três combinações de reabilitações com implantes zigomáticos. Cargas oclusais na região do primeiro molar foram simuladas, e a distribuição de tensões sobres os implantes e ossos adjacentes foram examinados. A distribuição das cargas foi observada predominantemente nas regiões de corpo e processo frontal do osso zigomático para ambos os modelos analisados. A distribuição de tensões analisadas pela análise fotoelástica concentrou-se no corpo e processo frontal do osso zigomático. No modelo 1 (2 implantes zigomáticos + 2 implantes convencionais), maiores concentrações foram encontradas ao redor dos implantes e osso adjacente. Diante dos testes realizados, a reabilitação com 2 implantes zigomáticos com 4 implantes convencionais (Modelo 2) são mais favoráveis mecanicamente. CAPÍTULO II: O objetivo deste estudo foi analisar a distribuição de tensões em estruturas craniofaciais e regiões adjacentes aos implantes de dois tipos de reabilitação com conceito All-on- Four utilizando implantes zigomáticos. Os testes fotoelásticos mostraram concentração de carga no corpo e processo frontal do osso zigomático. A partir das análises obtidas, ambos os modelos apresentam satisfatório comportamento mecânico / Abstract: With the advancement of implantology, atrophic edentulous jaws that previously were indications of bone grafts to enable rehabilitation with dental implants, actually is possible to circumvent most of these clinical situations without the need for bone grafts using techniques such as the zygomatic implants. However, for the maintenance of these treatments, becomes essential knowledge of the biomechanical behavior of these treatment modalities. Given the above, this research presents three biomechanical studies in vitro described in the following chapters. CHAPTER I: The aim of this study was to analyze the mechanical stresses around the implants and surrounding bone by photoelastic analysis simulating combinations of three rehabilitations with zygomatic implants. Occlusal loads in first molar region were simulated, and the stress distribution on the implants and surrounding bone were examined. The load distribution was observed predominantly in the body and frontal process of zygomatic bone for both models analyzed. The stress distribution analyzed by photoelastic analysis concentrated on the body and frontal process of zygomatic bone. Model 1 (2 + 2 zygomatic implants conventional implants), higher concentrations were found around the implants and surrounding bone. Before the tests, rehabilitation with two zygomatic implants with conventional implants 4 (Model 2) are better mechanically. CHAPTER II: The aim of this study was to analyze the stress distribution in craniofacial structures and regions adjacent to implants of two types of rehabilitation with All-on-Four concept using zygomatic implants. The photoelastic tests showed load concentration in the body and frontal process of zygomatic bone. From the analysis obtained, both models have satisfactory mechanical properties. / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica

Orientadores: Cecília Amélia de Carvalho Zavaglia, Vanessa Petrilli Bavaresco / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-18T02:53:41Z (GMT). No. of bitstreams: 1 Santos_FernandaHenriquesdos_M.pdf: 2590038 bytes, checksum: 807936f77ee66231cc661475d6643f25 (MD5) Previous issue date: 2011 / Resumo: Na área médica, para se desenvolver um dispositivo que funcione como implante, deve-se utilizar materiais que sejam compatíveis para funções específicas do corpo humano, e esses são classificados como biomateriais. Neste trabalho, foram determinados os parâmetros que serão aplicados ao laser de infravermelho (condutividade térmica do material, densidade do material e comprimento de onda do laser) utilizado na máquina de prototipagem rápida, a qual será usada para a fabricação do implante. Este implante será composto por um biomaterial polimérico a base de Polivinilalcool (PVAl) e, terá como objetivo a substituição da cartilagem articular mandibular. Estudos já avaliaram as propriedades mecânicas de hidrogéis poliméricos de PVAl mostrando sua aplicabilidade como reparadores da cartilagem articular em articulação de quadril, porém a articulação mandibular é submetida à aplicações de cargas superiores havendo a necessidade de melhoria de suas propriedades mecânica. A mistura física de dois ou mais polímeros é denominada blenda polimérica e seu objetivo é aperfeiçoar ou modificar as propriedades dos materiais adequando-as para uma aplicação específica. A literatura relata que PVAl e Polivinilpirrolidona (PVP) são polímeros miscíveis entre si e, quando não reticulados são solúveis em água. O PVP é um polímero amorfo e autolubrificante, e por isso, foi escolhido para melhorar as propriedades mecânicas do PVAl. Blendas nas composições de 90:10 de PVAl e PVP respectivamente, reticuladas via laser infravermelho utilizando concentração de 2,5% de termoiniciador cianovalérico foram caracterizadas via Espectroscopia do Infravermelho Médio, Calorimetria Exploratória Diferencial (DSC), Microscopia Eletrônica de Varredura (MEV) e Extração sol-gel. Através desses experimentos foram determinados os parâmetros do laser para posterior utilização na máquina de prototipagem rápida. Foi possível também realizar a cura do material através do laser de infravermelho. A cura foi confirmada através dos outros ensaios realizados / Abstract: In the medical area to develop a device that functions as an implant, one should use materials that are compatible for specific functions of the human body, and these are classified as biomaterials. In this study, we determined the laser parameters that will be applied to the infrared laser (thermal conductivity, material density and wavelength of the laser) in rapid prototyping machine, which will be used to manufacture the implant. This implant is a polymeric biomaterial based on polyvinylalcool (PVAl) and will aim to replace the articular cartilage of the mandible. Studies have evaluated the mechanical properties of polymeric hydrogels PVAl showing its applicability as repairing articular cartilage in hip joint, but the mandibular joint is subjected to loads greater than applications having the need to improve their mechanical properties. The physical mixture of two or more polymers is called polymer blend and its goal is to improve or modify the properties of materials making them suitable for a specific application. The literature reports that PVAl and PVP polymers are miscible and, when not crosslinked, are soluble in water. PVP is an amorphous polymer and selflubricating, and therefore was chosen to improve the mechanical properties of PVAl. Blends in the compositions of 90:10 PVAl and PVP respectively, crosslinked using infrared concentration of 2.5% termoiniciador cianovaléric were characterized by mid-infrared spectroscopy, Differential Scanning Calorimetry (DSC), Scanning Electron Microscopy (SEM) and sol-gel fraction. Through these experiments were determined laser parameters for subsequent use in rapid prototyping machine. It was also possible to realize the cure of material through the infrared laser. The cure was confirmed by other tests / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Orientador: Jose Ricardo de Albergaria Barbosa / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T22:50:05Z (GMT). No. of bitstreams: 1 Perez_MiguelAngelJaimes_D.pdf: 10680088 bytes, checksum: c91b56bc63db2e1197b0228d1fc609d5 (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi analisar qualitativa e quantitativamente a distribuição das tensões geradas em modelos fotoelásticos após a aplicação de cargas verticais de 150N, em implantes osseointegráveis de diferentes desenhos. Foram selecionados 3 implantes: I.) Serson Implant 3,75 x 13 mm, Hexágono Externo; II.) Colosso RC 4,0 x 13 mm, Hexágono Interno; III.) Kopp 4,0 x 13 mm, Cone Morse. Para a análise da distribuição de tensões foram confeccionadas 3 hemimandibulas em resina fotoelástica a partir da duplicação de três réplicas de hemimandibulas humanas de poliuretano. Cada implante foi posicionado e fixado no interior da hemimandibula fotoelástica na região do segundo pré-molar ausente. Através do polariscópio circular pertencente ao laboratório de Materiais Dentários da Faculdade de Odontologia de Piracicaba FOP-UNICAMP, foi possível visualizar as franjas isocromáticas nos modelos. Na análise qualitativa foi observado o início da primeira franja e a distribuição das tensões quando aplicado 150N de carga. A análise quantitativa foi obtida através da formula da lei ótica das tensões, conhecendo a respectiva ordem de franja no ponto de interesse, a constante ótica do material e a espessura do modelo. Este cálculo permitiu conhecer a tensão cisalhante de cada implante. O implante cilíndrico Serson, H.E apresentou distribuição das tensões na região cervical, apical e média do implante com maior tensão cisalhante na região cervical, seguido pela região media e apical. O implante Colosso RC com H.I apresentou distribuição das tensões na região apical, cervical e média do implante com um padrão uniforme de tensões nas três regiões. O implante Kopp, com desenho cônico e C.M apresentou distribuição das tensões na região cervical, apical, e média do implante com maior concentração de tensão cisalhante na região apical, seguido pela região cervical e media conjuntamente. Baseado nos resultados e na metodologia empregada neste estudo conclui-se que os três desenhos de implantes apresentaram padrões diferentes de distribuição de tensões, observando-se menor concentração de tensões nos implantes cônicos com conexões internas H.I e C.M. O implante cilíndrico com H.E apresentou maior concentração de tensão / Abstract: This study qualitatively and quantitatively analyze the distribution of tensions generated in fotoelastic models after the application of vertical loads of 150N in osseointegrables implants of different designs. We selected 3 implants: I.) Serson Implant 3.75 x 13 mm, External Hexagon II.) Colosso RC 4.0 x 13 mm, Internal Hexagon, III.) Kopp 4.0 x 13 mm, Morse Cone. For the analysis of the distribution of tensions, 3 hemimandibles using fotoelastic resin from the duplication of three replics of human hemimandibles of polyurethane were made. Each implant was placed and fixed inside the fotoelastic hemimandibles in the region where the second pre-molar was absent. Through a circular polariscope belonging to the Dental Materials, School of Dentistry of Piracicaba (FOP - UNICAMP) laboratory was able to see the isochromatics fringes in the models. In the qualitative analysis was observed the beginning of the first fringe and the distribution of the tensions when was applied a load of 150N. A quantitative analysis was obtained through the optical formula law of the tensions, knowing the order of fringe at the point of interest, an optical constant of the material and the thickness of the model. This calculation allowed to know the cisalhante shear of each implant. The cylindrical implant Serson HE showed distribution of the tensions in the cervical, middle and apical region of the implant with great tension shear in the cervical, followed by middle and apical region. The implant Colosso RC with HI showed distribution of the tensions in the apical, cervical and middle region of the implant with a uniform pattern of the tensions in these three regions. The implant Kopp with conic design and CM showed distribution of the tensions in the cervical, apical, and middle region of the implant with great concentration of the tension shear in the apical region, followed by cervical and middle together. Based on the results and methodology used in this study, we concluded that the three designs of implants showed different patterns of distribution of the tensions, with less concentration of the tensions in the conical implants with internal connections HI and CM. The cylindrical implant with HE showed higher concentration of the tension / Doutorado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Doutor em Clínica Odontológica

Orientador: William Dias Belangero / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Ciencias Medicas / Made available in DSpace on 2018-08-09T02:25:23Z (GMT). No. of bitstreams: 1 Garrido_LuizFernando_M.pdf: 3331524 bytes, checksum: 50f44c5fff048c0f9e4c220b4f7e52f4 (MD5) Previous issue date: 2007 / Resumo: Este estudo teve como objetivo avaliar o desempenho in vivo, de implantes cilíndricos com altura e diâmetro de 5mm formados por cerâmica ß-tricálcio fosfato (ß-TCP) ou polietileno de ultra-alto peso molecular (PEUAPM) todos recobertos com hidrogel de poli (2-hidroxi etil metacrilato) - poli(metacrilato de metila-co-ácido acrílico) (75:25) (pHEMA/poli (MMA-co-AA)) para preencher defeitos osteocondrais nos joelhos direito e esquerdo de cães. Foram operados treze cães machos com peso entre 15 e 25 kg fornecidos pelo Canil do Centro Multi Institucional de Bioterismo da Unicamp, sem raça definida, em bom estado de nutrição, vacinados após período prévio de quarentena. Cinco cães foram utilizados como controle e oito foram seguidos por nove meses após a colocação dos implantes. Os implantes de cerâmica foram colocados no sulco troclear do joelho direito e os de polietileno no joelho esquerdo. Foram realizadas análises da superfície do implante macroscópica (in vivo e in vitro), mecânica e microscópica, com a finalidade de avaliar a formação de tecido sobre o implante, o seu desgaste, o se desempenho viscoelástico e a interface formada entre o implante e o tecido ósseo. Os implantes de cerâmica apresentaram desempenho inferior ao polimérico, em todos os critérios avaliados. Embora não tenha havido desgaste significativo na superfície do hidrogel os dois implantes estudados produziram abrasão na superfície da patela / Abstract: This study had the purpose of evaluating ¿in vivo¿ the performance of ß-TCP ceramic or extreme high molecular weight polyethylene cylindrical implants, with height and diameter of 5mm, all covered with poly(2-HEMA) ¿ poly(methyl methacrilate-co-acrilic acid) hydro gel (polyHEMA/poly(MMA-co-AA) (75:25) in order to fill in bone defects in both the right and left knees of dogs. Thirteen male dogs weighting between 15 and 25kg, supplied by UNICAMP¿s Centro Multi Institucional de Bioterismo, were operated. All the dogs were well nourished, vaccinated and the operation took place after a previous quarantine period. Five dogs were used as control and eight were followed for nine months after putting the implants. The ceramic implants were placed in the right knees and the polyethylene ones in the left knees. Macroscopic, mechanic and microscopic analyses of the implant surface, (both in vivo and in vitro) were performed, in order to evaluate the tissue formation on the implant, the wearing off of the implant, the viscoelastic performance and the interface between the implant and the bone tissue. The ceramic implants presented an inferior performance when compared to the polymeric ones, in all of the evaluated aspects. Although there was no significant degradation on the hydro gel surface, both studied implants produced erosion on the kneecap surface / Mestrado / Cirurgia / Mestre em Cirurgia

Orientador: Vitor Baranauskas / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Eletrica / Made available in DSpace on 2018-08-09T14:59:50Z (GMT). No. of bitstreams: 1 Rodrigues_AnaAmelia_M.pdf: 19209454 bytes, checksum: 1a2efefc090d27e2715b48aad097989d (MD5) Previous issue date: 2006 / Resumo: O desenvolvimento de novos materiais para a produção de implantes ortopédicos tem sido uma busca constante, devido principalmente ao aumento das aplicações clínicas e à necessidade de se alcançar maior durabilidade, diminuindo assim as cirurgias de revisão. O diamante CVD obtido por deposição química da fase vapor é um novo material com grande potencial de uso devido às suas excelentes propriedades físico-químicas. Dentre elas pode-se destacar a inércia química, extrema dureza e baixo coeficiente de atrito, características importantes para materiais que necessitam resistir ao desgaste e à corrosão produzida pelos fluídos do corpo humano. O objetivo deste estudo foi avaliar pela análise ¿in vitro¿ e ¿in vivo¿ a biocompatibilidade de tubos de diamante microcristalino e diamante nanocristalino produzidos pela deposição química de vapor em filamento quente (CVD). Palavras Chave: diamante CVD, biomateriais, implantes, próteses / Abstract: The development of new materials for orthopedic implants has been a quest due to the increasing number of clinical applications and necessity of achieving larger durability for lessening the need for revision surgeries. Diamond CVD (Chemical Vapour Deposition) is a new material with larger potential of future use due its excellent physico-chemical properties like for instance, high chemical inertness, extreme hardness and low friction coefficient. The aim of this study is to evaluate by ¿in vitro¿ and ¿in vivo¿ assays the biocompatibility of microcrystalline and nanocrystalline diamond self-sustaining tubes produced by hot-filament chemical vapor deposition (CVD). Key Words: chemical-vapor-deposited diamond, biomaterials, implants, prosthesis / Mestrado / Engenharia de Computação / Mestre em Engenharia Elétrica

O sucesso do tratamento com implantes dentários depende do conhecimento teórico-prático do profissional, condições biológicas do paciente, e das propriedades mecânicas dos seus componentes. Dois testes de fadiga podem avaliar as propriedades mecânicas destes materiais: ensaios monotônicos unidirecionais e testes de flexão rotacional. A vantagem do dispositivo de flexão rotacional é o ensaio mais rápido que fornece dados relevantes e uma previsão mais realista da longevidade clínica. Oliveira-Neto (2011) avaliou o dispositivo de flexão rotacional desenvolvido por Ferreira (2010), e mostrou que componentes do dispositivo necessitavam ser revistos para assegurar melhor fixação do implante, controle de temperatura, frequência e permitir modificação do momento de força aplicado aos espécimes. O objetivo deste trabalho foi confeccionar e avaliar novos componentes para o dispositivo de flexão rotacional de Ferreira (2010) e avaliar seus efeitos em sistemas de implante de hexágono externo e interno. Os grupos testados foram: Aimplantes Hexagono Externo (HE) com munhão (UCLA); B- implantes HE com Pilar Cônico; C- implantes Hexagono Interno (HI) com munhão (UCLA); D- implantes HI com Pilar Cônico. O novo método consistiu em modificações no: porta implante, porta rolamento, centralizador do implante, material de fixação (resina acrílica). As amostras foram submetidas a ciclagem em torno do seu eixo longitudinal enquanto uma extremidade estava fixada em um mandril à 45o e a outra extremidade recebia a carga. O objetivo foi determinar o nível de carga em que 50% dos espécimes sobreviveram e 50% fraturaram antes de 106 ciclos girando a 16Hz. Assim, a resistência a fadiga (F50) foi determinada através da técnica staircase analysis. Após a ciclagem, os componentes que não apresentaram falhas tiveram o destorque de remoção mensurado eletronicamente, e todas as amostras foram analisadas através de microscópio eletrônico de varredura, radiografia e fotografia digital. Os resultados mostraram que os grupos UCLA têm maior resistência à fadiga. O sistema de HI-UCLA mostrou um desempenho mais estável, com uma resistência igual ao HE. Os grupos com Pilar Cônico apresentaram falhas clinicamente melhor, permitindo a substituição de componentes protéticos. Os danos mais graves ocorreram em ambos os grupos HE, com danos aos implantes. O método de desinclusão do implante da resina precisa ser revisto visando a obtenção de imagens sem artefatos. O dispositivo de Ferreira (2010) associado às modificações propostas por Oliveira-Neto permitiu a execução do ensaio de flexão rotativa em sistema de implantes com variadas configurações, produzindo resultados clinicamente relevantes. / Implant success depends on professional ability, patient biological conditions and also mechanical properties. Two fatigue tests can study implant mechanical properties: unidirectional bend-release fatigue testing and rotational fatigue testing. Advantages of rotational bending devices include faster tests that can generate relevant data and provide more realistic prediction of clinical performance. Oliveira- Neto (2011) evaluated a rotational bending device developed by Ferreira (2010), and showed its components need to be revised to ensure better implant fixation, temperature control, frequency and also enable to increase force moment. The aim of this study was fabricate and evaluate new components to Ferreiras device and it evaluate it effects in external and internal hexagon implant systems.Following groups were tested: A-external hex (EH) implants with UCLA abutment, B- EH implants with Conical Abutment, C- internal hex (HI) implants with UCLA abutment, D- IH implants with Conical Abutment. The new methodology consisted in changes on implant holder, bearing case, implant centralizer and bone material simulator (acrylic resin). Samples were spun around their long axes while being clamped into a 45o revolving collet on one end and loaded normal to their long axis on the other end. The aim was to determine the load level at which 50% of the specimens survived- and 50% fractured before 106 cycles at 16Hz. Fatigue resistance (F50) were determined using the staircase procedure. After cycling, torque of survival components were measured electronically, and all samples were analyzed by scanning electron microscopy, x-ray and digital photography. Results showed that UCLA groups have higher fatigue resistence. The IH-UCLA system showed more stable performance, with equal resistance to EH. Conical Abutment groups failure clinically better, allowing replacement of prosthetic components. The most severe damage occurred in both EH groups, with implant damages. Ferreiras device with Oliveira-Neto changes enabled to perform a rotating bending test on implant system in numerous configurations, producing clinically relevant results.