Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-07Bitstream added on 2014-06-13T18:35:10Z : No. of bitstreams: 1 barca_dc_me_sjc.pdf: 4808947 bytes, checksum: 238892d410325de1d23eb76694cb9763 (MD5) / Este estudo avaliou a influência da espessura da cerâmica, do tempo e tipo de fotopolimerização do cimento resinoso na resistência da união entre uma cerâmica vítrea e a dentina coronária humana. A hipótese é a de que o tipo e o tempo de fotopolimerização do agente cimentante e a espessura da cerâmica influenciem na resistência de união entre cimento e dentina. Foram selecionados cento e doze dentes molares humanos hígidos que foram incluídos em resina acrílica e tiveram a superfície oclusal cortadas em máquina Labcut, expondo a dentina planificada. Dois grupos foram tiveram a dentina condicionada com ácido fosfórico 37% lavada e aplicado adesivo (Excite, Ivoclar) fotopolimerizando por 20s. No grupo controle (n=16), utilizou-se cimento auto-adesivo. Foram confeccionados cento e doze blocos (6 x 6 mm) de cerâmica feldspática (Vita PM9) com três espessuras: 1, 2 e 3 mm que tiveram a superfície de cimentação tratad a com ácido fluorídrico 10%, lavada, seca e silanizada. Os blocos cerâmicos foram cimentados, de acordo com o grupo experimental: Variolink II (Ivoclar Vivadent); e fotopolimerizados com LED por 40 ou 80 segundos de fotopolimerização ou cimento Multilink II (no grupo controle). Assim, formaram-se sete grupos (n=16). Os espécimes foram armazenados em água destilada (37°C) por 24 horas e seccionados em dois eixos, X e Y, para a obtenção dos espécimes. Cada grupo (N=16) foi subdividido em 2 (n=8) onde um grupo foi termociclado e o outro submetido ao ensaio de microtração 24 horas após a cimentação. Esse palito (cerâmica/dente) foi fixado no dispositivo de microtração Erios, levado à máquina de ensaio universal e testado com velocidade de 1 mm/min. Os valores médios obtidos (MPa) foram à análise de Variáveis ANOVA 3- fatores, teste de Dunnett e ao teste de Tukey (5%). A resistência adesiva foi significantemente influenciada pelos fatores... / This study evaluated the influence of the thickness of the ceramic, time and type of light curing resin cement on bond strength between a ceramic and glass human dentin. The hypothesis is that the type and time of curing luting agent and the thickness of the ceramic bearing on the bond strength between cement and dentin. We selected one hundred and twelve healthy human molar teeth were embedded in acrylic resin and were cut in the occlusal surface Labcut machine, exposing the dentin. Two groups have had to dentin conditioned with 37% phosphoric acid washed applied adhesive (Excite, Ivoclar) light cured for 20s. In the control group (n = 16), we used self-adhesive cement. We made one hundred and twelve blocks (6 x 6 mm) ceramic feldspathic (Vita PM9) with three thicknesses: 1, 2 and 3 mm that had cement surface treated with hydrofluoric acid 10%, washed, dried, and silanized. The ceramic blocks were cemented according to the experimental group: Variolink II (Ivoclar Vivadent) and cured with LED for 40 or 80 seconds of curing cement Multilink or II (control group). Thus, they formed seven groups (N = 16). The specimens were stored in distilled water (37 ° C) for 24 hours and sectioned in two axes, X and Y, to obtain the specimens. Each group (N = 16) was subdivided into two (n = 8) where a group was thermocycled and another test by microtensile 24 hours after cementation. This toothpick (ceramic / tooth) was mounted in microtensile Erios, led to a universal testing machine and tested at a speed of 1 mm / min. The average values (MPa) were the ANOVA analysis of three variables - factors, Dunnett test and Tukey test (5%). The bond strength was significantly influenced by light irradiation time, thickness of the ceramic thermal cycling

Submitted by LUCAS TEIXEIRA FRANCO null (teixeira_90@hotmail.com) on 2016-02-03T22:56:21Z No. of bitstreams: 1 Dissertação final.pdf: 2325492 bytes, checksum: 36f8ac7caa1da3a9ee584908b80cac74 (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-02-05T11:58:03Z (GMT) No. of bitstreams: 1 franco_lt_me_sjc.pdf: 2325492 bytes, checksum: 36f8ac7caa1da3a9ee584908b80cac74 (MD5) / Made available in DSpace on 2016-02-05T11:58:03Z (GMT). No. of bitstreams: 1 franco_lt_me_sjc.pdf: 2325492 bytes, checksum: 36f8ac7caa1da3a9ee584908b80cac74 (MD5) Previous issue date: 2016-01-18 / O tratamento com plasma não térmico pode modificar a superfície da dentina e melhorar a ligação entre os dentes e resinas compostas. O objetivo deste estudo foi avaliar a influência do tratamento do plasma não térmico (PNT) na resistência adesiva de um sistema adesivo autocondicionante aplicado em diferentes espessuras de dentina humana, bem como observar mudanças na micromorfologia das interfaces dentina/resina em MEV. Molares humanos foram divididos em dois grupos (n = 30) de acordo com a espessura da camada de dentina: superficial (S) (2 mm de espessura) e profunda (P) (1 mm de espessura). Cada grupo foi dividido em três subgrupos (n = 10) de acordo com o tratamento de superfície da dentina: grupo SPA (2 mm dentina + plasma + adesivo); Grupo SAP (2 mm dentina + adesivo + plasma); Grupo SA (2mm de dentina + adesivo); PPA (1 mm dentina + plasma + adesivo); Grupo PAP (1 mm dentina + adesivo + plasma) e grupo PA (1 mm dentina + adesivo). Foi confeccionada uma restauração em resina composta e as amostras armazenadas (48 h). Palitos de dentina/resina com área adesiva de aproximadamente 1 mm² foram obtidos e submetidos ao teste de microtração. O padrão de fraturas foi analisado por microscopia óptica. Os dados de resistência foram analisados pelos testes estatísticos ANOVA dois fatores e Tukey (5%). As análises das interfaces adesivas em MEV foram realizadas em amostras selecionadas. Os resultados mostraram uma diferença significativa na resistência adesiva entre a dentina superficial e profunda; independentemente do tratamento de superfície, a dentina superficial apresentou maiores valores de resistência adesiva. Entre os grupos tratados com e sem plasma, a resistência adesiva foi maior quando o plasma foi aplicado na superfície da dentina; no entanto a aplicação de plasma antes ou depois do o adesivo não foi estatisticamente diferente. O PNT aumentou a resistência adesiva da dentina humana S e P. / Treatment with non-thermal plasma can modify dentin surface and improve bond between teeth and composite resin. The objective of this study was to evaluate the influence of non-thermal plasma (NTP) treatment on dentin bond strength of a self-etching adhesive system to different thicknesses of human dentin as well as to observe SEM micromorphology changes of the resin/dentin interfaces. Human molars were divided into two groups (n = 30) according to dentin layer thickness: superficial (S) (2 mm thick) and deep (D) (1 mm thick). Each group was divided into three subgroups (n = 10) according to dentin surface treatment: SPA group (2 mm dentin + plasma + adhesive); SAP group (2 mm dentin + adhesive + plasma); Group SA (2 mm dentin + adhesive); PPA (1 mm dentin + plasma + adhesive); PAP group (1 mm dentin + adhesive + plasma) and PA group (1 mm dentin + adhesive). A composite resin restoration was built up and specimens stored (48 h). Teeth sticks with adhesive area of approximately 1 mm² were obtained and submitted to microtensile test. The pattern of fractures was analyzed with optical microscopy. Bond strength data was analyzed by two-way ANOVA and Tukey (5%) statistical tests. Resin/dentin interfaces SEM analysis was conducted on selected specimens. The results showed a significant difference in bond strength between superficial and deep dentin; regardless surface treatment superficial dentin showed higher bond strength. Among the groups treated with and without plasma, bond strength was higher when plasma was applied on dentin surface; however plasma application before or after the adhesive was not statistically different. NTP increased the bond strength of S and D human dentin.

Orientador: José Roberto Rodrigues / Banca: Carlos Augusto Pavanelli / Banca: José Claudio Martins Segalla / Resumo: O objetivo do trabalho foi analisar in vitro a eficiência de adesão através de ensaio de microtração, de um cimento autocondicionante (self-adhesive), sobre esmalte e dentina, com e sem tratamento prévio da superfície dental, antes e após termociclagem. Foram utilizados 56 terceiros molares, 28 para esmalte e 28 para dentina, divididos em 6 grupos experimentais e 2 controle. O cimento resinoso autocondicionante selecionado para os grupos experimentais foi: Rely-X Unicem (3M ESPE/ St. Paul, MN, EUA), e para os grupos controle o Variolink II (Ivoclar Vivadent, AG, Schaan, Liechtenstein) (VR), cimento de cura dual não autocondicionante. Os dentes dos grupos experimentais foram subdivididos quanto à aplicação direta do cimento sobre a superfície dental (R), com o condicionamento ácido (RAC) e com condicionamento ácido e aplicação de sistema adesivo (RACAS). Blocos de resina composta previamente polimerizados foram cimentados à superfície dental. Os conjuntos dente-cimento-bloco receberam cortes paralelos ao longo eixo dos dentes para a confecção dos palitos. O ensaio de microtração com aparelho de ensaio universal (EMIC) foi utilizado para analisar a resistência adesiva dos cimentos avaliados. Os corpos de prova após o ensaio foram analisados mediante microscópio óptico para analise do modo de fratura. Para a análise estatística do μTBST, foi utilizado ANOVA 3 fatores com teste de comparação múltipla de Tukey a 5%, considerando os fatores cimento resinoso, região e armazenagem. Os resultados mostraram diferença estatística existente entre R aplicado diretamente sobre a superfície dental e os demais grupos. Os grupos RACAS e VR apresentaram maiores médias de resistência adesiva para os grupos dentina, respectivamente antes e após termociclagem e o cimento RAC para os grupos esmalte. A termociclagem não diminuiu significativamente os valores de resistência... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this research was to analyze in vitro , the adhesive efficiency of a self - etching cement trough microtensile test , over enamel and dentine , with and with out previous treatment of dental surface , before and after thermocycling. Were used 56 third molars, 28 for enamel and 28 for dentine, divided in 06 experimental groups and 02 control groups. The resin cement self - etching selected for the experimental groups was: Rely X Unicem (3M ESPE/ St. Paul, MN, EUA), and for the control groups: Variolink II (Ivoclar Vivadent, AG, Schaan , Liechtenstein) (VR), dual healing cement not self etching. The teeth of the experimental groups were subdivided in groups as the direct application of cement over the dental surface (R) without previous treatment (RAC), with the acid etching and with acid etching and application of adhesive system (RACAS) e (VR). Composed resin blocks polymerized previously were cemented on dental surface. The sets tooth- cement-block received parallel cuts in long axis of the teeth to make the tooth picks. The micro tensile test was done with the universal apparatus (EMIC) to analyze the resistance efficiency of the evaluated cements. The specimens were analyzed after the test by optical microscope to analyze the mode fracture. For the statistics analyses of μTBST, were used ANOVA 3 factors with multiple comparison test of Tukey 5%, considering the factors resin cement, region and storage. The results showed present statistics difference between R applied directly on dental surface and the other groups. The groups RACAS and VR presented superior average of adhesive resistance for dentine groups before and after thermocycling, and the RAC cement for the enamel groups before and after thermocycling. The thermocycling did not low significantly the adhesive resistance values, just for the RACAS group. By the results we can conclude that the self etching... (Complete abstract click electronic access below) / Mestre

O objetivo desse trabalho foi avaliar a influência da resistência de união de sistemas adesivos à dentina irrigada com substâncias endondônticas, após a degradação da interface adesiva e análise morfológica da interface adesiva por meio de microscopia eletrônica de varredura (MEV). Foram selecionados sessenta terceiros molares, que tiveram a porção oclusal removida e planificada expondo a dentina profunda. Os espécimes foram irrigados com hipoclorito de sódio a 2,5% por 30 minutos e em seguida em EDTA 17% por 5 minutos. Após a irrigação da superfície detinária os dentes foram divididos aleatoriamente em seis grupos (n = 10) de acordo com o sistema adesivo empregado: G1 e G2 - Clearfil (Kuraray); G3 e G4 - Single Bond 2 (3M) e G5 e G6 - XP Bond (Dentsply). Após a aplicação do sistema adesivo, foi confeccionado um platô de resina composta Z100 (3M). A degradação da interface adesiva foi realizada por meio de estocagem em água deionizada/ciclagem térmica: 24 horas de estocagem em água deionizada/nenhum ciclo (grupos G1, G3 e G5) e 6 meses de estocagem em água deionizada/12.000 ciclos (grupos G2, G4 e G6). Após os períodos pré-estabelecidos em cada grupo, os conjuntos dente/resina foram seccionados de forma a se obter 4 palitos de aproximadamente de 1mm2, que foram submetidos ao teste de microtração. A análise morfológica da interface foi realizada por meio de MEV. Os dados obtidos foram submetidos a ANOVA e teste de Tukey ao nível de 5%. Verificou-se que houve diferença significativa entre os adesivos (p<0,01). A durabilidade da adesão da resina composta a dentina irrigada com solução endodôntica não foi afetada após 6 meses de estocagem em água e 12.000 ciclos térmicos (p<0,05). A análise da interface adesiva evidenciou que os sistemas adesivos não alteraram o padrão de união mesmo após 6 meses de ciclagem térmica e degradação em água, exceto para o sistema adesivo XP Bond. Pode-se concluir que a dentina irrigada com NaOCl e EDTA apresentou menor resistência a microtração quando do emprego do sistema adesivo XP Bond. A degradação da interface por meio do armazenamento em água e ciclagem térmica não influenciou na resistência de união, independente do sistema adesivo empregado. / The aim of the present study was to survey the influence of endodontic irrigants on the adhesion resistance of adhesive systems to human dentin, after the degradation of adhesive interface and morphologic analysis of adhesive interface for Scanning Electronic Microscopy SEM. Sixty molar thirds were selected. The deep dentin was exposed removing and ground the oclusal portion. The specimens were irrigated with sodium hypochlorite 2,5% for 30 minutes followed by EDTA 17% for 5 minutes. Subsequently, teeth were divided randomly in six groups (n=10) accordingly to adhesive system applied: G1 and G2 Clearfil (Kuraray); G3 e G4 - Single Bond 2 (3M) e G5 e G6 - XP Bond (Dentsply). After adhesive system application, a composite resin Z100 (3M) was built up created. The degradation of the adhesive interface was realized by storage the specimens in deionized water and thermocycling: 24 hours of deionized water storage/no cycle (groups G1, G3 and G5) and 6 months storage in deionized water/12.000 cycles (groups G2, G4 and G6). After pre-established periods of each group, the systems tooth/resin were sectioned in order to obtain 4 sticks of approximately 1mm2, which were subjected to microtensile bond strength test. The morphologic analysis of interface was performed for SEM. Results were analyzed with ANOVA and Tukey test to level 5%. Significant difference between adhesives was verified (p<0,01). The water storage (6 months) coupled with thermocycling (12.000 cycles) did not affected significantly the resistance to microtensile bond strength of the dentin (p<0,05). The conclusion is that dentin irrigated with NaOCl and EDTA presented less resistance to microtensile bond strength when XP Bond Adhesive system was utilized. The interface degradation through water storage and thermocycling had no effect on the resistance of the dentin bond, independently of the adhesive system applied.

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-05-27Bitstream added on 2014-06-13T20:51:27Z : No. of bitstreams: 1 fernandesjunior_vvb_me_sjc.pdf: 534033 bytes, checksum: dc3fecf909acf51fb45b0235288dbddc (MD5) / O objetivo do trabalho foi analisar in vitro a eficiência de adesão através de ensaio de microtração, de um cimento autocondicionante (self-adhesive), sobre esmalte e dentina, com e sem tratamento prévio da superfície dental, antes e após termociclagem. Foram utilizados 56 terceiros molares, 28 para esmalte e 28 para dentina, divididos em 6 grupos experimentais e 2 controle. O cimento resinoso autocondicionante selecionado para os grupos experimentais foi: Rely-X Unicem (3M ESPE/ St. Paul, MN, EUA), e para os grupos controle o Variolink II (Ivoclar Vivadent, AG, Schaan, Liechtenstein) (VR), cimento de cura dual não autocondicionante. Os dentes dos grupos experimentais foram subdivididos quanto à aplicação direta do cimento sobre a superfície dental (R), com o condicionamento ácido (RAC) e com condicionamento ácido e aplicação de sistema adesivo (RACAS). Blocos de resina composta previamente polimerizados foram cimentados à superfície dental. Os conjuntos dente-cimento-bloco receberam cortes paralelos ao longo eixo dos dentes para a confecção dos palitos. O ensaio de microtração com aparelho de ensaio universal (EMIC) foi utilizado para analisar a resistência adesiva dos cimentos avaliados. Os corpos de prova após o ensaio foram analisados mediante microscópio óptico para analise do modo de fratura. Para a análise estatística do μTBST, foi utilizado ANOVA 3 fatores com teste de comparação múltipla de Tukey a 5%, considerando os fatores cimento resinoso, região e armazenagem. Os resultados mostraram diferença estatística existente entre R aplicado diretamente sobre a superfície dental e os demais grupos. Os grupos RACAS e VR apresentaram maiores médias de resistência adesiva para os grupos dentina, respectivamente antes e após termociclagem e o cimento RAC para os grupos esmalte. A termociclagem não diminuiu significativamente os valores de resistência... / The objective of this research was to analyze in vitro , the adhesive efficiency of a self - etching cement trough microtensile test , over enamel and dentine , with and with out previous treatment of dental surface , before and after thermocycling. Were used 56 third molars, 28 for enamel and 28 for dentine, divided in 06 experimental groups and 02 control groups. The resin cement self - etching selected for the experimental groups was: Rely X Unicem (3M ESPE/ St. Paul, MN, EUA), and for the control groups: Variolink II (Ivoclar Vivadent, AG, Schaan , Liechtenstein) (VR), dual healing cement not self etching. The teeth of the experimental groups were subdivided in groups as the direct application of cement over the dental surface (R) without previous treatment (RAC), with the acid etching and with acid etching and application of adhesive system (RACAS) e (VR). Composed resin blocks polymerized previously were cemented on dental surface. The sets tooth- cement-block received parallel cuts in long axis of the teeth to make the tooth picks. The micro tensile test was done with the universal apparatus (EMIC) to analyze the resistance efficiency of the evaluated cements. The specimens were analyzed after the test by optical microscope to analyze the mode fracture. For the statistics analyses of μTBST, were used ANOVA 3 factors with multiple comparison test of Tukey 5%, considering the factors resin cement, region and storage. The results showed present statistics difference between R applied directly on dental surface and the other groups. The groups RACAS and VR presented superior average of adhesive resistance for dentine groups before and after thermocycling, and the RAC cement for the enamel groups before and after thermocycling. The thermocycling did not low significantly the adhesive resistance values, just for the RACAS group. By the results we can conclude that the self etching... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-02-27Bitstream added on 2014-06-13T20:51:31Z : No. of bitstreams: 1 freitas_crb_me_arafo.pdf: 1243419 bytes, checksum: 9b17396cab68dbc46f7018d3bc8aec44 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi avaliar o procedimento de hibridização imediata em restaurações indiretas de resina composta. A hipótese nula foi duplicada: os resultados dos adesivos de condicionamento total e auto-condicionante são similares; e a hibridização imediata produz microinfiltração e resistência adesiva similares à cimentação convencional. Foram selecionados 20 terceiros molares humanos recém extraídos e isentos de cárie, nos quais foram realizados preparos cavitários MOD, padronizados para restaurações indiretas. Os dentes foram divididos aleatoriamente em 4 grupos experimentais: (G1) hibridização com adesivo de condicionamento total (SB, Single Bond, 3M ESPE) imediatamente após o preparo cavitário e antes da cimentação, (G2) hibridização com adesivo de condicionamento total antes da cimentação (SB), (G3) hibridização com adesivo auto-condicionante (AP, Adper Prompt, 3M ESPE) imediatamente após o preparo cavitário e antes da cimentação, (G4) hibridização com adesivo auto-condicionante (AP) antes 157 da cimentação. Os espécimes foram restaurados com inlays de Targis (Ivoclar/Vivadent), cimentados com cimento resinoso Rely X ARC (3M ESPE). Todos produtos foram manipulados de acordo com as instruções do fabricante. Após termociclagem, os espécimes foram imersos em solução de nitrato de prata 50%, seccionados para avaliação da microinfiltração com escores pré-determinados de 0 a 3. Em seguida, os espécimes foram novamente seccionados com 0,8mm x 0,8mm para realização dos testes de microtração. Os resultados obtidos foram submetidos à análise estatística (p<0,05). Os escores da microinfiltração foram submetidos ao teste de Mann-Whitney indicando nenhuma diferença na técnica de hibridização (p>0,05). Os resultados da microtração foram submetidos à análise de variância que revelou... . / An analysis was carried out to determine the behavior of immediate hybridization on indirect composite resin restorations. The null hypothesis was two fold: were whether total etch or self-etch (SEA) adhesives result in similar; and whether immediate hybridization produces similar microleakage and æTBS than conventional cementation. Twenty sound extracted teeth were selected and 20 standardized MOD inlay preparations were made. The prepared teeth were randomly assigned in four experimental groups: (G1) hybridization with total-etch adhesive (SB, Single Bond, 3M ESPE) immediately after preparation and prior cementation, (G2) hybridization with total-etch adhesive prior cementation (SB), (G3) hybridization with SEA (AP, Adper Prompt, 3M ESPE) immediately after preparation and prior cementation; and (G4) hybridization with SEA (AP) prior cementation. The specimens were restored with Targis (Ivoclar/Vivadent) inlays, cemented with composite resin cement (RelyX ARC, 3M ESPE). All products were used according with manufacturer's instructions. The specimens were 160 thermocycled and immersed in 50%w/w silver nitrate. The specimens were sectioned and the microleakage evaluated with predetermined scores (0-3). Then, the specimens were sectioned in 0,8mm x 0,8mm and æTBS tested in a MTS-810 machine. The obtained data were submmited to statistical analysis (p< .05). The microleakage scores were submmited to Mann-Whitney non-parametric test showing no statistical differences among the adhesives and technique (p> .05). The æTBS results submitted to ANOVA parametric test reveled that G1 performed better than G2, and G3 superior to G4. The null hypotheses were partially rejected. None of the adhesives eliminate microleakage. Hybridization immediately after the preparation is done and before cementation improved the bond strengths with... (Complete abstract, click electronic address below).

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Esta pesquisa estudou a influência de diferentes velocidades de corte e marcas de discos diamantados nos valores de resistência adesiva, durante a preparação dos espécimes a serem submetidos à microtração, e na integridade das amostras por meio do microscópio eletrônico de varredura (MEV). Vinte blocos da cerâmica à base de dissilicato de lítio (IPS e.max Press) foram unidos com cimento resinoso (Rely X ARC) a blocos de compósito (Z100), construídos incrementalmente. Foram seguidas as recomendações dos fabricantes no tratamento da superfície da cerâmica e aplicação do cimento resinoso. Após 24 horas em água destilada a 37C, os espécimes foram divididos em dois grupos de discos: marcas Buehler e Extec e subdivididos nas velocidades de 200rpm e 400rpm (B2; E2; B4 e E4, respectivamente). Cada espécime foi cortado em dois eixos perpendiculares para obtenção de palitos com área adesiva de 1,0mm. Para cada condição experimental, os palitos foram separados, aleatoriamente, 15 palitos para análise ao MEV e 30 palitos para serem submetidos à força de tração. As médias de resistência adesiva em MPa foram E4=20,312 ; B4= 24,2 11,3 ; B2= 25,2 9,0 e E2= 28,6 10,4. Na análise estatística, observou-se que os valores de resistência adesiva na velocidade de 200rpm foram significativamente maiores comparados a velocidade de 400rpm, independente do disco empregado. Ao MEV, observou-se melhor integridade dos palitos na velocidade de 200rpm com presença de trincas menos extensas nas bordas externas. Constatou-se também que o disco Extec na velocidade de 400rpm apresentou movimentos excêntricos ao corte e obteve-se maior número de perdas prematuras, uma diminuição significante na média da área total de união (p<0,05), além de diferença significativa nos valores de resistência comparada a velocidade de 200rpm. Concluiu-se que a utilização de diferentes velocidades e sua interação com o disco empregado interfere na integridade dos espécimes e nos valores de resistência adesiva, sendo mais acentuada ao se utilizar o disco da marca Extec. / The aim of this research was to verify the influence of different cutting speeds and brand of diamond saws during microtensile specimen preparation on the bonding strength values and on the samples microscopy integrity (SEM). Twenty lithium disilicate glass-ceramic blocks (IPS e.max Press) were bonded with dual-cure resin cement (Rely X ARCTM) to composite (Z100TM) blocks, built incrementally. The manufacturers recommendations were followed for ceramic treatment surface and placement on the resin cement, as well. After storage for 24 hours in distillated water at 37C, the specimens were divided in two groups of diamond saws, Buehler and Extec brands, which were further subdivided using 200rpm and 400rpm speeds (B2; E2; B4 and E4 respectively), and they were sectioned into two perpendicular axes obtaining sticks shaped specimens with cross-sectional area of 1.0mm. For each experimental situation the sticks were randomly separated; 15 for the analysis to the SEM and 30 to be submitted to tensile strength. Mean bond strength values (MPa) were: E4 = 20.3 12; B4 = 24.2 11.3; B2 = 25.2 9.0; and E2 = 28.6 10.4. The statistical analysis of data showed that the values of bond strength at 200 rpm speed were significantly higher as compared to 400 rpm speed, regardless of saw employed. In SEM, it was noted better integrity of sticks at 200 rpm speed with presence of less extensive cracks in external edges. It was also found that the Extec saw at 400 rpm showed eccentric movement to cutting and achieved higher number of premature losses, a significant decreased mean total area of bond (p<0.05), in addition to significant difference in strength values compared with 200 rpm speed. It was concluded that using different speeds and their interaction with the used saw interfere with the integrity of specimens and the bond strength values, being more pronounced when using the Extec saw.

Hipótese do estudo: A presente pesquisa hipotetiza que a técnica de cimentação está diretamente ligada a resistência adesiva de restaurações indiretas. Objetivos: O presente estudo experimental verificou se o selamento imediato da dentina, com diferentes sistemas adesivos, apresentaram melhores resultados de resistência de união junto a cimentação resinosa de restaurações indiretas. Métodos: Foram utilizados 48 terceiros molares humanos, divididos em seis grupos de acordo com as técnicas de cimentação testadas: grupo 1) Sistema Variolink II (Ivoclar Vivadent); grupo 2) Clearfill SE (Kuraray) + Variolink II; grupo 3) Selamento com Clearfill SE + Sistema Variolink II após 24h; grupo 4) Selamento com Exite DSC (Ivoclar Vivadent) + Sistema Variolink II; grupo 5) Selamento com Clearfill + Tetric Evo Flow (Ivoclar Vivadent) + Sistema Variolink II após 24h; Grupo 6) selamento com Exite DSC + Tetric Evo Flow + Sistema Variolink II após 24h. Oito amostras de cada grupo foram para máquina de cortes seriados (Isomet 1000) para obtenção de palitos com 1mm2 de área. Os palitos de cada grupo foram submetidos ao teste de microtração. O teste de microtração foi utilizado após 24h da cimentação. Os dados foram estatisticamente analisados pelo teste de Kruskal-Wallis e o teste de Dunn (5%). Diferenças significativas foram detectadas (p=0,0074). Resultados: Os grupos 1 e 2 apresentaram mediana de resistência de união intermediária, sendo estatisticamente semelhantes aos demais grupos. O grupo 6 apresentou mediana significativamente mais alta que os grupos 3, 4 e 5, os quais foram semelhantes entre si. Adicionalmente os tipos de fratura foram analisados com auxílio de lupa estereoscópica, em todos os grupos a porcentagem de fraturascoresivas em dentina ou mistas foi menor em comparação as fraturas adesivas e coesivas em cerômeros. Conclusão: O selamento imediato da dentina com adesivo de condicionamento total junto a resina flow demonstrou maior resistência adesiva. / Hypothesis of the study: This study hypothesizes that the cementation technique is directly related to the bond strength of indirect restorations. Objectives: The present experimental study examined whether the immediate dentin sealing with different bonding systems, the best-performing bond strength in the resin cementation of indirect restorations. Methods: A total of 48 human third molars was divided into six groups according to the techniques of tested: group 1) Variolink System II (Ivoclar Vivadent), group 2) Clearfill SE (Kuraray) + Variolink II, Group 3) with Seal Clearfill SE + System Variolink II after 24h, group 4) Sealing successfully DSC (Ivoclar Vivadent) + Variolink System II, Group 5) Sealing with Clearfill + Tetric Evo Flow (Ivoclar Vivadent) + System Variolink II after 24h, Group 6) sealing successfully DSC + + Tetric Evo Flow System Variolink II after 24h. Eight samples of each group were machine serial sections (Isomet 1000) to obtain sticks with 1 mm2 in size. The sticks of each group were subjected to microtensile testing. The microtensile test was performed used after 24h of cementation. The data were statistically analyzed by Kruskal- Wallis test and Dunn (5%). Significant differences were detected (p = 0.0074). Results: Groups 1 and 2 had a median of intermediate bond strength, being statistically similar to other groups. The sixth group median significantly higher than groups 3, 4 and 5, which were similar. Besides the types of fracture were analyzed with the aid of a stereomicroscope. Conclusions: The immediate detin sealing with total etch adhesive and the flowable resin showed higher bond strength.

Made available in DSpace on 2015-04-11T13:55:49Z (GMT). No. of bitstreams: 1 Thiago Mendes de Lima.pdf: 1095985 bytes, checksum: af3d342d9c71734320c0b651931b5083 (MD5) Previous issue date: 2014-02-21 / Fundação de Amparo à Pesquisa do Estado do Amazonas / A utilização de agentes antioxidantes tem sido proposta para melhorar a resistência adesiva após clareamento dental. O presente estudo in vitro avaliou o efeito do hidrogel de ascorbato de sódio a 10% (AS), aplicado após o clareamento com peróxido de hidrogênio a 35% (PH), na resistência adesiva em esmalte de uma resina composta (RC). Foram selecionados 50 dentes bovinos e aleatoriamente divididos em cinco grupos experimentais (n=10) subdividindo-os em grupos testados tardiamente (7 dias) e após envelhecimento (3 meses): Grupo 1 (G1: 7 dias/ G1A: 3 meses) - sem clareamento (grupo controle) + RC; G2/G2A PH + RC; G3/G3A PH + 14 dias + RC; G4/G4A PH 35% + AS 10% (30 min) + RC; G5/G5A PH + 14 dias + AS (30 min) + RC. Foram obtidos palitos de resina-adesivo-esmalte (1mm x1mm) e submetidos ao tese de resistência à microtração em uma máquina de ensaio universal EMIC DL2000 (100N a 0,5mm/min). Os tipos de falhas foram analisados em microscopia digital (40x) e eletrônica de varredura, classificado-as como coesiva, adesiva, mista. Os valores (Mpa) de resistência adesiva à microtração foram avaliados estatisticamente através da Análise de Variância a dois critérios (ANOVA) e do teste de Tukey para comparações das médias, com significância 1%. Os resultados foram: G1: 20,09Aab ± 5,33 / G1A: 24,09Abc ± 5,12; G2: 17,14Aa ± 4,94 / G2A: 20,84Aab ± 5,21; G3: 20,36Aab ± 5,30 / G3A: 22,76Abc ± 5,40; G4: 22,18Aabc ± 5,30 / G4A: 30,22Ad ± 8,05; G5: 21,92Aab ± 5,90 / G5A: 27,25Ac ± 7,12. Pode-se concluir que, o uso do ascorbato de sódio a 10% interfere positivamente na resistência adesiva de restaurações envelhecidas em 3 meses, aumentando os valores de resistência adesiva.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2016-03-22T17:35:14Z No. of bitstreams: 1 ronaldoluisalmeidadecarvalho.pdf: 1029602 bytes, checksum: cc60051c61c4c956fd0881bb40822c3c (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2016-04-24T02:26:37Z (GMT) No. of bitstreams: 1 ronaldoluisalmeidadecarvalho.pdf: 1029602 bytes, checksum: cc60051c61c4c956fd0881bb40822c3c (MD5) / Made available in DSpace on 2016-04-24T02:26:37Z (GMT). No. of bitstreams: 1 ronaldoluisalmeidadecarvalho.pdf: 1029602 bytes, checksum: cc60051c61c4c956fd0881bb40822c3c (MD5) Previous issue date: 2013-01-24 / O objetivo do presente estudo foi avaliar três hipóteses: H0- O tratamento térmico do silano e o tipo de cimento resinoso não influencia na resistência de união entre cimentos resinosos e uma cerâmica feldspática; H1- O tratamento térmico do silano influencia na resistência de união entre cimentos resinosos e uma cerâmica feldspática; H2- O cimento resinoso influencia na resistência de união de uma cerâmica feldspática. Foram confeccionados 30 blocos cerâmicos (VITA Mark II, Zahnfabrik), os quais foram duplicados em resina composta (W3D Master, Wilcos). Os blocos foram divididos em 6 grupos (n=5) de acordo com os seguintes tratamentos de superfície: ASCp- Ácido fluorídrico 10% + silano + Panavia F; ASTCp- Ácido fluorídrico 10% + silano + tratamento térmico (forno) + Panavia F; STCp- Silano + tratamento térmico (forno) + Panavia F; ASCr- Ácido fluorídrico 10% + silano + RelyX ARC; ASTCr- Ácido fluorídrico 10% + silano + tratamento térmico (forno) + RelyX ARC; STCr- Silano + tratamento térmico (forno) + RelyX ARC. Para realização do tratamento térmico do silano foi utilizado forno sob temperatura de 100 ºC durante 2 minutos. Cada bloco cerâmico já condicionado foi unido ao seu correspondente em resina composta, utilizando o cimento resinoso respectivo ao seu grupo, sob a carga constante de 750g. Cada conjunto cerâmica/cimento/resina composta foi seccionado e os corpos de prova foram analisados por meio do teste mecânico de microtração. Os valores de resistência de união e os desvios-padrão (MPa) para os grupos foram: ASCp (25,47 ± 9,34a); ASTCp (33,04 ± 10,65b); STCp (13,76 ± 8,82c); ASCr (24,80 ± 7,99a); ASTCr (23,84 ± 7,16a); STCr (11,41 ± 11,71c). Os testes ANOVA e Post Hoc foram aplicados. Com os resultados deste estudo, pode-se concluir: A hipótese H0 foi rejeitada; A hipótese H1 foi parcialmente aceita, pois o tratamento térmico do silano proporcionou maiores valores médios de resistência de união desde que seja realizado em associação com o condicionamento com ácido fluorídrico a 10%, independente do cimento resinoso testado; A hipótese H2 foi parcialmente aceita, pois o cimento com MDP apresentou valor médio de resistência de união estatisticamente superior ao cimento convencional, quando foi realizado o condicionamento com ácido fluorídrico a 10% previamente ao tratamento térmico do silano. / The aim of this study was to evaluate three hypotheses: H0- Heat treatment of silane and resin cement type does not influence the bond strength of resin cements and a feldspathic ceramic;H1- Heat treatment of silane influences the bond strength between cements resin and a feldspathic ceramic; H2- The resin cement influences the bond strength of a feldspathic ceramic. Thirty blocks were fabricated using a ceramic (VITA Mark II, Zahnfabrik), which were duplicated in composite resin (W3D Master, Wilcos). The blocks were divided into 6 groups (n = 5) in accordance with the following surface treatments: ASCp- Hydrofluoric acid 10% + silane + Panavia F; ASTCp- Hydrofluoric acid 10% + silane + heat treatment (furnace) + Panavia F; STCp- Silane + heat treatment (furnace) + Panavia F; ASCr- Hydrofluoric acid 10% + silane + RelyX ARC; ASTCr- Hydrofluoric acid 10% + silane + heat treatment (furnace) + RelyX ARC; STCr- Silane + heat treatment (furnace) + RelyX ARC. To perform the heat treatment silane was used furnace under temperature of 100 ° C for 2 minutes. Then each ceramic block conditioning was already attached to its corresponding composite resin, using a resin cement to its respective group, under the constant load of 750g. Each set ceramic / cement / composite resin was sectioned and the specimens were analyzed by microtensile mechanical test. The bond strength values and standard deviations (MPa) for the groups were: ASCp (25.47 ± 9.34a); ASTCp (33.04 ± 10.65b); STCp (13.76 ± 8.82c); ASCr (24.80 ± 7.99a); ASTCr (23.84 ± 7.16a); STCr (11.41 ± 11.71c). ANOVA and Post Hoc were applied. With the results of this study, we can conclude: The hypothesis H0 was rejected; H1 hypothesis was partially accepted because the heat treatment of the silane led to the highest average bond strength provided it is conducted in association with the hydrofluoric acid etching 10%, independent of the resin cement tested; H2 hypothesis was partially accepted because the cement with MDP averaged bond strength statistically superior to conventional cement when the conditioning was conducted with 10% hydrofluoric acid prior to the heat treatment of silane.