Submitted by Ricardo Cedraz Duque Moliterno (ricardo.moliterno@uefs.br) on 2015-09-10T00:55:01Z No. of bitstreams: 1 Nilton C N Santos Tese Geno Cito Endo 10 ago 20h.pdf: 2096544 bytes, checksum: fd3a63f3f5235dae758262d72d8a3bb2 (MD5) / Made available in DSpace on 2015-09-10T00:55:01Z (GMT). No. of bitstreams: 1 Nilton C N Santos Tese Geno Cito Endo 10 ago 20h.pdf: 2096544 bytes, checksum: fd3a63f3f5235dae758262d72d8a3bb2 (MD5) Previous issue date: 2015-06-29 / Pulp therapy for deciduous teeth is the last resort for preventing tooth loss, but among the products used for this, i.e. so-called filling pastes, none is considered to be ideal. The objective of this study, using the micronucleus test on the bone marrow of mice and the comet assay on human lymphocytes, was to evaluate the genotoxic and cytotoxic effects of four filling pastes that are used in this therapy: zinc oxide, calcium hydroxide P.A., mineral trioxide aggregate and an iodoform paste (Guedes-Pinto paste). To perform the micronucleus test, male Swiss mice (Mus musculus) were divided into groups of ten animals each: four groups were each exposed to one of the filling pastes, administered intraperitoneally at dilutions of 1/10, 1/50, 1/500 and 1/1000. Cyclophosphamide was used as the positive control. The negative controls used were the dilution vehicles: dimethylsulfoxide (DMSO) for the Guedes paste and zinc oxide; and phosphate-buffered saline solution (PBS) for the calcium hydroxide P.A. and mineral trioxide aggregate. The animals were sacrificed 24 h and 48 h after the treatment. The bone marrow was extracted, in order to calculate the micronucleus occurrence rate in 1000 polychromatic erythrocytes (PCE) in each of the animals, under an optical microscope (1000 X), in a blinded test. Cytotoxicity was evaluated by determining the PCE/NCE (normochromatic erythrocyte) ratio in 200 erythrocytes/animal. For the comet assay, human lymphocytes were cultured in different dilutions of each of the filling pastes (1:500, 1:750, 1:1000 and 1:2000), for 3 h at 37 ?C, under an atmosphere containing 5% CO2. Two positive controls were used: methyl-methanesulfonate (0.4 ?M) for the calcium hydroxide P.A. and mineral trioxide aggregate; and doxorubicin (0.6 ?M) for the Guedes paste and zinc oxide. Two negative controls were also used here: distilled water for the calcium hydroxide P.A. and mineral trioxide aggregate; and DMSO for the Guedes paste and zinc oxide. Comets were identified by means of fluorescence microscopy (400 X), and 100 of them were counted on each of the three slides that were analyzed for each drug test. The statistical analysis on the results from the micronucleus test was performed using the conditional test for comparing proportions in situations of rare events. Analysis of variance, followed by the Tukey test, was used to assess the PCE/NCE ratio obtained from the different treatments and also to compare the means from the DNA damage indices that were obtained through the comet test, using the Prisma software, version 4.0. The micronucleus occurrence rate was significantly higher among the animals treated with Guedes paste, at all the dilutions tested and at both sacrifice times and also among the animals treated with zinc oxide and sacrificed 48 h after treatment at the dilutions of 1:50, 1:500 and 1:1000. Cytotoxic effects from these pastes were detected in the animals sacrificed at both times. Calcium hydroxide P.A. and mineral trioxide aggregate did not present any cytotoxic or genotoxic effects. The results obtained from the comet assay also showed that zinc oxide and Guedes paste presented genotoxicity, whereas calcium hydroxide P.A. and mineral trioxide aggregate did not. These results show that there is a need to reassess the use of zinc oxide and Guedes paste and provide encouragement for conducting additional studies to evaluate the genotoxicity and cytotoxicity of these pastes. / A terapia pulpar de dentes dec?duos se constitui no ?ltimo recurso de preven??o da perda dent?ria, mas, dentre os produtos empregados para tal, as denominadas pastas obturadoras, nenhum ? considerado como ideal. O objetivo deste trabalho foi avaliar, com o uso do teste de micron?cleo em medula ?ssea de camundongo e do ensaio cometa em linf?citos humanos, os efeitos citot?xicos e genot?xicos de quatro pastas obturadoras utilizadas nesta terapia: ?xido de zinco, hidr?xido de c?lcio P.A., agregado tri?xido mineral e uma pasta iodoformada (pasta Guedes-Pinto). Para realiza??o do teste de micron?cleo, camundongos Swiss (Mus musculus), machos, foram divididos em grupos de dez animais, que foram expostos ?s pastas obturadoras, administradas via intraperitoneal nas dilui??es de 1/10, 1/50, 1/500 e 1/1000. Ciclofosfamida foi utilizada como controle positivo. Os controles negativos foram: dimetilsulf?xido (DMSO) para a pasta Guedes-Pinto e ?xido de zinco; e solu??o salina tamponada (PBS) para o hidr?xico de c?lcio P.A. e agregado trioxido mineral. Os animais foram sacrificados 24h e 48h ap?s tratamento, a medula ?ssea foi extra?da e foram analisados 1000 eritr?citos policrom?ticos (PCE) de cada um dos animais, sob microscopia ?ptica (1000X) e em teste cego. A citotoxicidade foi avaliada pela rela??o PCE (eritr?cito policrom?tico) / NCE (eritr?cito normocrom?tico) em 200 eritr?citos/animal. Para o ensaio cometa, linf?citos humanos foram cultivados nas dilui??es de 1:500, 1:750, 1:1000 e 1:2000 das pastas obturadoras, durante 3h, a 37?C, em atmosfera de 5% de CO2. Foram utilizados dois controles positivos: metil-metanosulfonato (0,4?M) para o hidr?xido de c?lcio P.A. e agregado tri?xido mineral, e doxorrubicina (0,6 ?M) para a pasta Guedes-Pinto e ?xido de zinco. Foram tamb?m dois os controles negativos utilizados: ?gua destilada para o hidr?xido de c?lcio P.A. e agregado tri?xido mineral, e DMSO para pasta Guedes-Pinto e ?xido de zinco. A identifica??o do cometa foi realizada sob microscopia de fluoresc?ncia (400X), sendo computados 100 deles em cada uma das tr?s l?minas analisadas para cada droga teste. A an?lise estat?stica dos resultados do teste de micron?cleo foi realizada com o uso do teste condicional para compara??o de propor??es em situa??o de eventos raros. An?lise de vari?ncia, seguida do teste de Tukey, foram utilizados para avalia??o da rela??o PCE/NCE obtida com os diferentes tratamentos e tamb?m para compara??o das m?dias dos ?ndices de danos ao DNA obtidos no ensaio cometa com o software Prisma vers?o 4.0. A ocorr?ncia de micron?cleos foi significativamente maior nos animais tratados com a pasta Guedes-Pinto em todas as dilui??es testadas, nos dois tempos de sacrif?cio e tamb?m para os animais tratados com ?xido de zinco e sacrificados 48h ap?s tratamento, nas dilui??es 1:50; 1:500 e 1:1000. Efeitos citot?xicos destas pastas foram detectados nos animais sacrificados nos dois tempos. O hidr?xido de c?lcio P.A. e o agregado tri?xido mineral n?o apresentaram efeitos citot?xicos nem genot?xicos. Os resultados obtidos com o ensaio cometa tamb?m apontaram para a genotoxicidade do ?xido de zinco e pasta Guedes-Pinto, e n?o do hidr?xido de c?lcio P.A. e agregado tri?xido mineral. Estes resultados mostram a necessidade de reavalia??o do uso do ?xido de zinco e pasta Guedes-Pinto e suscitam a realiza??o de estudos adicionais avaliando a genotoxicidade e citotoxicidade destas pastas.

Made available in DSpace on 2014-12-17T14:06:52Z (GMT). No. of bitstreams: 1 AbimaelLM.pdf: 1998740 bytes, checksum: 3bd1ad1da777ebc532ac1fcc9b0a96f4 (MD5) Previous issue date: 2009-03-20 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The low tenacity presented by the Portland cement pastes used in the oil wells cementation has been motivating several researches with attention focused on alternative materials. Additives have been developed to generate flexible pastes with mechanical resistance capable to support the expansions and retractions of the metallic covering of the wells that submit to the steam injection, technique very used to increase the recovery factor in oil reservoirs with high viscosity. A fresh paste with inadequate rheological behavior may commit the cementation process seriously, involving flaws that affect the performance of the paste substantially in the hardened state. This work proposes the elaboration and the rheological analysis of Portland cement pastes with addition of residues of rubber tire in several proportions, with the aim of minimizing the damages provoked in the hem cementing of these wells. By thermogravimetric analysis, the particles of eraser that go by the sieve of 0,5mm (35 mesh) opening and treated superficially with NaOH solution of 1 mol/L presented appropriate thermal resistance for wells that submit to thermal cyclic. The evaluation of the study based on the results of the rheological analysis of the pastes, complemented by the mechanical analysis, thickening, stability, tenor of free water and filtrate loss, being used as parameter a paste reference, without rubber addition. The results showed satisfactory rheology, passive of few corrections; considerable loss of mechanical resistance (traction and compression), compensated by earnings of tenacity, however with established limits for its application in oil wells; satisfactory stability, free water and thickening time / A baixa tenacidade apresentada pelas pastas de cimentos Portland utilizadas na cimenta??o de po?os de petr?leo tem motivado v?rias pesquisas voltadas para materiais alternativos. Aditivos t?m sido desenvolvidos para gerar pastas flex?veis e com resist?ncia mec?nica capaz de suportar as expans?es e retra??es do revestimento met?lico dos po?os que se sujeitam ? inje??o de vapor, t?cnica muito utilizada para aumentar o fator de recupera??o em reservat?rios de ?leo com alta viscosidade. Uma pasta fresca com comportamento reol?gico inadequado pode comprometer seriamente o processo de cimenta??o, implicando em falhas que afetam substancialmente o desempenho da pasta no estado endurecido. Este trabalho prop?e a elabora??o e a an?lise reol?gica de pastas de cimento Portland com adi??o de res?duos de borracha de pneu em diversas propor??es, com o objetivo de minimizar os estragos provocados na bainha cimentante destes po?os. Por an?lise termogravim?trica, as part?culas de borracha passantes na peneira de abertura 0,5 mm (35 mesh) e tratadas superficialmente com solu??o 1 mol/L de NaOH, apresentaram resist?ncia t?rmica adequada para po?os sujeitos ? ciclagem t?rmica. A avalia??o do estudo baseou-se nos resultados da an?lise reol?gica das pastas, complementadas pela an?lise mec?nica, espessamento, estabilidade, teor de ?gua livre e perda de filtrado, utilizando-se como par?metro uma pasta refer?ncia, sem adi??o de borracha. Os resultados mostraram reologia satisfat?ria, passiva de poucas corre??es; consider?vel perda de resist?ncia mec?nica (tra??o e compress?o), compensada por ganho de tenacidade, por?m dentro dos limites estabelecidos para sua aplica??o em po?os de petr?leo; satisfat?ria estabilidade, ?gua livre e tempo de espessamento

Made available in DSpace on 2014-12-17T14:07:02Z (GMT). No. of bitstreams: 1 MarcosASA_capa_ate_cap5.pdf: 2919360 bytes, checksum: 8bb04eb85df77f75f3f1de37bbecc19d (MD5) Previous issue date: 2009-04-02 / The Potiguar basin has large fields of viscous oil where the used method for recovering is based on vapor injection; this operation is carried out by injecting vapor in the oilwell directly, without the protection of a revetment through thermal insulation, what causes its dilation and, consequently, cracks in the cement placed on the annular, and lost of hydraulic insulation; this crack is occasioned by the phenomenon of retrogression of the compressive resistance due to the conversion of the hydrated calcium silicate in phases calcium-rich, caused by the high temperatures in the wells, subjected to thermal recuperation. This work has evaluated the application of composite pastes with addition of residue of biomass of ground sugar-cane bagasse as anti-retrogression mineral admixture for cementation of oil-wells subjected to thermal recuperation. The addition of the mineral residue was carried out considering a relative amount of 10, 20, 30, 40 and 59% in relation to cement mass, trying to improve the microstructure of the paste, still being developed a reference paste only with cement and a paste with addition of 40% of silica flour - renowned material in the oil industry as anti-retrogression additive. Pozzolanic activity of the ash was evaluated through XRD, TG/DTG, as the resistance to compression, and it was also determined the physical and mechanical behavior of the pastes when submitted to cure at low temperatures (22 and 38? C); besides it was evaluated the behavior of the pastes when submitted to two cycles of cure at high temperature (280?C) and pressure (7 MPa). It was verified that the ash of the sugar-cane biomass presents pozzolanic reaction and has great efficiency in decrease the permeability of the paste by filler effect, as well as that addition of ash in a relative amount of 10, 20 e 30% increases cured compressive resistance at low temperatures. It was also showed that the ash in a relative amount of 40% and 59% has very significant efficiency as anti-retrogression additive, since it prevents the decrease of compressive resistance and forms hydrated calcium silicate type xenotlita and tobermorita which have more resistance and stability in high temperatures / A bacia Potiguar tem grandes campos de ?leo viscoso, onde o m?todo de recupera??o utilizado ? a inje??o de vapor; essa opera??o ? realizada injetando-se vapor diretamente no po?o, sem a prote??o do revestimento atrav?s de isolamento t?rmico, o que provoca a dilata??o do mesmo, provocando assim falhas no cimento colocado no anular, e conseq?entemente, perda do isolamento hidr?ulico, esta falha tem origem no fen?meno de retrogress?o da resist?ncia ? compress?o devido a convers?o do silicato de c?lcio hidratado em fases ricas em c?lcio, provocada pelas elevadas temperaturas nos po?os, sujeitos ? recupera??o t?rmica. O presente trabalho avaliou a aplica??o de pastas comp?sitas com adi??o de res?duos de biomassa do baga?o da cana-de-a??car mo?das como aditivo mineral anti-retrogress?o para cimenta??o de po?os petrol?feros sujeitos a recupera??o t?rmica. A adi??o do res?duo mineral foi realizada teores de 10, 20, 30, 40 e 59% em rela??o a massa do cimento, visando melhorar a microestrutura da pasta, sendo ainda produzidas uma pasta de refer?ncia, apenas com cimento e uma pasta com adi??o de 40% de silica flour material consagrado na ind?stria de petr?leo como aditivo antiretrogress?o. Foram avaliados a atividade pozol?nica da cinza atrav?s de DRX, TG/DTG e resist?ncia ? compress?o, determinando-se tamb?m o comportamento f?sico e mec?nico das pastas submetidas a cura com baixas temperaturas (22 e 38?C), al?m da avalia??o do comportamento das pastas submetidas a dois ciclos de cura a alta temperatura (280?C) e press?o (7 MPa). Verificou-se que a cinza de biomassa da cana apresenta rea??o pozol?nica, tendo grande efici?ncia na diminui??o da permeabilidade da pasta por efeito filler, e que as adi??es de cinza em teores de 10, 20 e 30% aumentam a resist?ncia ? compress?o das pastas curadas a baixas temperaturas. Constatou-se ainda que a cinza em teores de 40% e 59% tem ?tima efici?ncia como aditivo antiretrogress?o, pois evitam a diminui??o da resist?ncia ? compress?o e formam silicato de c?lcio hidratado do tipo xenotlita e tobermorita que se apresentam mais resistentes e est?veis as altas temperaturas

Made available in DSpace on 2014-12-17T14:07:06Z (GMT). No. of bitstreams: 1 BrunoLSC_DISSERT.pdf: 3848053 bytes, checksum: 28828821b0f45645fb6dc741dc2505bf (MD5) Previous issue date: 2013-09-28 / One of the great challenges at present time related with the materials area concerns of products and processes for use in petroleum industry, more precisely related to the Pre-salt area. Progresses were reached in the last years allowing the drilling of the salt layer, with the time reduction for drilling and larger success at the end. For the oil wells companies the preponderant factor is the technology, however, in spite of the progress, a series of challenges is still susceptible to solutions and one of them refers to the slurries preparation for cementing in those areas. Inside of this context, this study had for objective to analyze the influence of the salts NaCl, KCl, CaSO4 and MgSO4 in strength and chemical structure of the hydrated products. As methodology, they were prepared and analyzed cement slurries with varied concentrations of these salts that are commonly found in the saline formations. The salts concentrations used in formulations of the slurries were of 5%, 15% and 30%. The slurries were formulated with specific weight of 15,8 lb / gal and the cement used was Class G. Strength tests were accomplished in samples cured by 24 hours and 28 days. Also were realized crystallographic characterization (XRD) and morphologic (SEM). In agreement with the presented results, it is observed that the largest resistance values are attributed to the slurries with concentration of 15%. There was reduction of the strength values of the slurries formulated with concentration of 30%. Through the characterization microstructural it was possible to note the salts influence in the main cement hydrated products / Um dos grandes desafios da atualidade relacionado com a ?rea de materiais diz respeito ? produ??o de produtos e processos para uso na ind?stria do petr?leo, mais precisamente relacionado ? ?rea do Pr?-sal. Avan?os foram alcan?ados nos ?ltimos anos permitindo a perfura??o da camada de sal, com a redu??o do tempo para perfura??o dos po?os e maior ?xito ao final da opera??o. Apesar dos avan?os, uma s?rie de desafios ainda ? pass?vel de solu??es e um deles refere-se ? prepara??o de pastas para a cimenta??o de po?os nessas zonas com camadas evapor?ticas. Dentro deste contexto, este estudo teve por objetivo analisar a influ?ncia dos sais NaCl, KCl, CaSO4 e MgSO4 no comportamento mec?nico e estrutura qu?mica dos produtos hidratados. Como metodologia, foram preparadas e analisadas pastas de cimento com concentra??es variadas destes sais que s?o comumente encontrados nas forma??es salinas do reservat?rio do Pr?-sal. As concentra??es dos sais empregadas nas formula??es das pastas foram de 5%, 15% e 30%. As pastas foram formuladas com peso espec?fico de 15,8 lb/gal e o cimento utilizado na prepara??o das pastas foi o do tipo Portland Classe G. Foram realizados ensaios de resist?ncia ? compress?o em corpos de prova curados por 24 horas e 28 dias. Tamb?m foram realizados ensaios de caracteriza??o cristalogr?fica (DRX) e morfol?gica (MEV). De acordo com os resultados apresentados, observa-se que os maiores valores de resist?ncia s?o atribu?dos ?s pastas com concentra??o de 15 % para todos os sais. Houve, tamb?m, redu??o dos valores de resist?ncia das pastas formuladas com concentra??o de 30 % para todos os sais. Atrav?s das an?lises de caracteriza??o micro estrutural foi poss?vel observar a influ?ncia dos sais nos principais produtos hidratados do cimento Portland

Made available in DSpace on 2014-06-11T19:24:46Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-07-08Bitstream added on 2014-06-13T19:11:27Z : No. of bitstreams: 1 martinelli_l_me_sjrp.pdf: 1675808 bytes, checksum: cfe68f960177993855a48c3037727299 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Neste trabalho foi construído e desenvolvido um secador de leito pulso-fluidizado que utilizou partículas inertes para a secagem de pastas e polpas de frutas. O sistema permitia o controle da vazão do ar de fluidização e de sua temperatura, da pulsação do ar e da vazão de injeção de pasta. Foram determinadas as curvas de fluidização de partículas de vidro e teflon no leito pulso-fluidizado sob diferentes configurações, bem como suas velocidades de mínima fluidização, as quais demonstraram-se próximas às curvas de um secador fluidizado convencional. Experimentos para a avaliação da agitação das partículas foram realizados para que fossem encontradas as melhores condições, determinando-se a existência ou não de pontos mortos no leito. Foi visto que as partículas pertenciam ao grupo D, segundo a classificação de Geldart (1973). Pasta de gesso foi seca no secador pulso-fluidizado para avaliação da produção de pó e do hold-up das esferas nas diferentes condições de operação, as quais tiveram como variáveis os períodos de injeção (fase ativa e inativa), ângulo da válvula borboleta que dava acesso do ar ao leito, temperatura do ar de secagem, velocidade do ar e vazão de pasta no leito. Foi observado que todas as variáveis testadas apresentaram influência na produção de pó e na quantidade de material aderido às partículas inertes. O secador pulsofluidizado foi testado também na secagem de suco e pastas de limão, maltodextrina e tomate, mostrando problemas de adesividade e, no caso de derivados de limão, aglomeração das partículas e colapso do leito. O secador foi utilizado ainda como vibro-fluidizado, quando o sistema de pulsação foi desligado e um sistema de vibração por eixos excêntricos foi acionado, constatando-se que o mesmo apresentou rendimento inferior ao pulso-fluidizado. Um secador do tipo spray dryer foi usado para a secagem... / For this work, a pulse fluidized bed drier that used inert particles for drying pastes and fruit pulps was constructed and developed. The system allowed for the control of fluidized air flow and its temperature, the air pulses and the paste injection flow. The fluidization curves and minimum velocity of fluidization of glass and Teflon particles were determined in the pulse fluidized bed. Experiments to evaluate the agitation of particles were done to find the best agitation conditions, determining the existence or not of dead spots in the bed. It was seen that the particles belonged to D group, as per Geldart (1973) classification. Plaster paste was dried in the pulse fluidized dryer to evaluate the production of powder and hold-up of the spheres under different operational conditions which were variations of the periods of paste injection (active and inactive phase), angle of the butterfly valve which gave air access to the bed, air drying temperature, air speed and paste flow. All tested variables influenced the powder production and the amount of material adhered to inert particles. The pulse fluidized bed drier was also tested for drying lemon juice and paste, maltodextrina and tomato, showing adhesive problems and, with the lemons, an agglomeration of particles and a collapsed bed. The dryer was also used as a vibro fluidized bed when the pulsation system was turned off and a vibration system with eccentric axles was set in motion, it was seen that the vibro fluidized bed had a lower yield than the pulse fluidized bed. A spray drier was used to dry lemon juice with maltodextrina, and it was found that a minimum of 65% of additional maltodextrina was needed. Physic-chemical testes were done from the powders obtained from the spray drying. These testes were for humidity, flowability, degree of agglomeration, higroscopicity, dispersibility, color determination and water activity... (Complete abstract click electronic access below)

Made available in DSpace on 2014-12-17T15:01:28Z (GMT). No. of bitstreams: 1 RomeroGSAF_DISSERT.pdf: 5251211 bytes, checksum: 91e35eccdc843f543fbc2744a816fb64 (MD5) Previous issue date: 2012-03-16 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / All around the world, naturally occurring hydrocarbon deposits, consisting of oil and gas contained within rocks called reservoir rocks , generally sandstone or carbonate exists. These deposits are in varying conditions of pressure and depth from a few hundred to several thousand meters. In general, shallow reservoirs have greater tendency to fracture, since they have low fracture gradient, ie fractures are formed even with relatively low hydrostatic columns of fluid. These low fracture gradient areas are particularly common in onshore areas, like the Rio Grande do Norte basin. During a well drilling, one of the most favorable phases for the occurrence of fractures is during cementing, since the cement slurry used can have greater densities than the maximum allowed by the rock structure. Furthermore, in areas which are already naturally fractured, the use of regular cement slurries causes fluid loss into the formation, which may give rise to failures cementations and formation damages. Commercially, there are alternatives to the development of lightweight cement slurries, but these fail either because of their enormous cost, or because the cement properties were not good enough for most general applications, being restricted to each transaction for which the cement paste was made, or both reasons. In this work a statistical design was made to determine the influence of three variables, defined as the calcium chloride concentration, vermiculite concentration and nanosilica concentration in the various properties of the cement. The use of vermiculite, a low density ore present in large amounts in northeastern Brazil, as extensor for cementing slurries, enabled the production of stable cements, with high water/cement ratio, excellent rheological properties and low densities, which were set at 12.5 lb / gal, despite the fact that lower densities could be achieved. It is also seen that the calcium chloride is very useful as gelling and thickening agent, and their use in combination with nanosilica has a great effect on gel strength of the cement. Hydrothermal Stability studies showed that the pastes were stable in these conditions, and mechanical resistance tests showed values of the order of up to 10 MPa / Em todo o mundo, ocorrem naturalmente dep?sitos de hidrocarbonetos, constitu?dos de petr?leo e g?s natural, contidos dentro de rochas denominadas "rochas reservat?rio", em geral arenitos ou carbonatos. Esses dep?sitos existem em variadas condi??es de press?o e profundidade, desde poucas centenas at? milhares de metros. Em geral, reservat?rios mais "rasos" t?m a tend?ncia a fraturar mais facilmente, pois possuem baixo gradiente de fratura, ou seja, as fraturas s?o formadas mesmo com colunas hidrost?ticas de fluido relativamente baixas. Essas zonas de baixo gradiente de fratura s?o particularmente mais comuns em zonas onshore, como aqui no Rio Grande do Norte. Um dos momentos mais prop?cios para a ocorr?ncia de fraturas ? durante a cimenta??o do po?o, ao se utilizar uma pasta cimentante de densidade superior ao m?ximo permitido pela estrutura rochosa. Al?m disso, em zonas j? naturalmente fraturadas, o uso de cimentos comuns causa perda de fluido para a forma??o, o que pode dar causa a cimenta??es falhas. Comercialmente, existem alternativas para o desenvolvimento de sistemas de pastas de cimento leves, mas esses falham ou em raz?o de seu elevad?ssimo custo, ou em fun??o das propriedades da pasta obtida n?o serem suficientemente boas para aplica??es mais gen?ricas, ficando restritas a cada opera??o para qual a pasta de cimento foi feita. Nesse trabalho foi realizado um planejamento estat?stico para determinar a influ?ncia de tr?s vari?veis, definidas como a concentra??o de cloreto de c?lcio, concentra??o de vermiculita e concentra??o de nano s?lica, nas v?rias propriedades do cimento. O uso da vermiculita, um min?rio de baixa densidade presente em grandes quantidades no nordeste brasileiro, como extensor para pastas cimentantes, permitiu a produ??o de pastas est?veis, com alta raz?o ?gua/cimento, propriedades reol?gicas excelentes e baixas densidades, que foram fixadas em 12,5 lb/Gal. Viu-se tamb?m que o cloreto de c?lcio ? um poderoso viscosificante e gelificante, e seu uso combinado com a nano s?lica possui grande efeito nas for?as g?is do cimento. Estudos de estabilidade hidrot?rmica mostraram que as pastas foram est?veis nessas condi??es, e os ensaios de resist?ncia mec?nica mostraram valores da ordem de at? 10 MPa

En el presente trabajo de investigación se presentará el estudio de pre factibilidad para la implementación de un planta procesadora de fideos integrales enriquecidos con linaza. / The current research job will describe the pre-feasibility study to implement a whole noodle production plant enriched with linseed. / Trabajo de investigación

[pt] A busca por materiais que não impactem negativamente o meio ambiente tem sido uma das prioridades de engenheiros que trabalham com materiais de construção. A emissão expressiva de CO2 na produção de cimento contribui para tal preocupação. Dentro deste cenário, soluções com emprego de nanotecnologia vêm chamando a atenção em diversas áreas por proporcionar novas soluções. O principal objetivo da presente tese é associar um material proveniente de uma fonte natural com benefícios provenientes da nanotecnologia a fim de modificar propriedades de pastas de cimento considerando seus aspectos químicos, físicos e mecânicos. A nanocelulose se apresenta como material proveniente de fonte renovável que apresenta propriedades atraentes aos materiais cimentícios, sendo assim uma opção a ser utilizada em conjunto com o cimento. Dentre os diversos tipos disponíveis, a celulose nanofibrilada (CNF) foi elencada para ser investigada neste trabalho. A celulose microcristalina (CMM) foi incluída nas investigações para possibilitar uma comparação direta entre as fibrilas da CNF e as partículas de CMM. O uso desses materiais celulósicos pode ser considerado recente e, com isso, existem ainda lacunas no que tange o entendimento dos seus efeitos em materiais cimentícios. Assim, a viabilidade da CNF e da CMM enquanto reforços em pastas de cimento foi avaliada por meio de ensaios de compressão e flexão. Os possíveis mecanismos responsáveis pelo efeito de ambas CMM e CNF foram estudados por meio de análises químicas e físicas. Por fim, foi realizada a caracterização das pastas reforçadas quanto à retração, total e autógena, e à reologia, nos regimes estático e dinâmico. Por conta dos impactos na trabalhabilidade promovidos pela inclusão de CNF, a mistura delas nas pastas de cimento foi facilitada com a adição de superplastificante, especialmente em porcentagens maiores que 0.050 por cento, em peso. A CMM e a CNF se mostraram eficazes em reforçar as pastas de cimento quanto a esforços de flexão e tração, levando ao aumento das respectivas resistências e módulos. Os resultados obtidos mostraram que a água presente no gel da CNF não está totalmente disponível como água de mistura por conta da morfologia e hidroficilidade das fibrilas. Observada uma certa combinação de porcentagem e fator água-cimento, a inclusão de CNF diminuiu a retração autógena das pastas. A inclusão de 0,040 por cento de NFC levou a resultados semelhantes aos da adição de CMM referente ao aumento da tensão de escoamento e da viscosidade. / [en] The seek for low environmental impact materials has become one of the priorities of construction building materials engineers. One of the reasons is the massive growing contribution of cement production industry in worldwide CO2 emissions. In this scenario, the dissemination of nanotechnology into varied areas is drawing attention for enabling new possibilities. The idea of the present thesis is to associate a material provided from a natural source with the potential benefits of nanotechnology to modify conventional cement pastes regarding their chemical, physical and mechanical aspects. Nanocellulose arises as an alternative that meets an eco-friendly source with remarkably properties expected from nanomaterials. There are different types of nano cellulosic materials that may be tailored to achieve desired compatibilities with varied cementitious materials. In this work, nanofibrillated cellulose (NFC) in the form of gel, and microcrystalline cellulose (MCC) particles were investigated, so a comparison could be traced between them. The use of both NFC and MCC in cementitious materials is recent and there are important gaps regarding their effect. For that reason, the feasibility of MCC and NFC to act as reinforcement on cement pastes was evaluated through compressive and flexural tests. Then, the possible mechanisms behind the effect of MCC and NFC on the microstructure of cement pastes were investigated through distinct chemical and physical analyses. Moreover, the total and autogenous shrinkage were characterized, as well as the dynamic and static rheological behaviors. Due to rheological modifications, the mixture of cement pastes with NFC was facilitated by a superplasticizer, especially for percentages higher than 0.050 percent wt. The MCC and NFC promoted the reinforcement of the cement pastes, regarding flexural and tensile stresses, increasing the composite strength and modulus. It was observed that he water present in the NFC gel is not totally available as mixing water due to the morphology and hydrophilicity of the fibrils. If associating certain levels of inclusions and water ratio, the NFC inclusion led to a decrease in autogenous shrinkage. The addition of 0.040 percent of NFC resulted in similar outcomes to 1.000 percent of MCC regarding their ability to increase yield stress and viscosity.

Made available in DSpace on 2014-12-17T14:07:09Z (GMT). No. of bitstreams: 1 Marcus VCB_DISSERT_PARCIAL.pdf: 2643130 bytes, checksum: 5d46e76949be4c4eb0ad9dfdafb24bcb (MD5) Previous issue date: 2013-02-18 / The materials engineering includes processes and products involving several areas of engineering, allowing them to prepare materials that fulfill the needs of various new products. In this case, this work aims to study a system composed of cement paste and geopolymers, which can contribute to solving an engineering problem that directly involves the exploitation of oil wells subject to loss of circulation. To correct it, has been already proposed the use of granular materials, fibers, reducing the drilling fluid or cement paste density and even surface and downhole mixed systems. In this work, we proposed the development of a slurry mixed system, the first was a cement-based slurry and the second a geopolymer-based slurry. The cement-based slurry was formulated with low density and extenders, 12.0 ppg (1.438 g/cm ?), showing great thixotropic characteristics. It was added nano silica at concentrations of 0.5, 1.0 and 1.5 gps (66.88, 133.76 and 200.64 L/m3) and CaCl2 at concentrations of 0.5, 1, 0 and 1.5%. The second system is a geopolymer-based paste formulated from molar ratios of 3.5 (nSiO2/nAl2O3), 0.27 (nK2O/nSiO2), 1.07 (nK2O/nAl2O3) and 13.99 (nH2O/nK2O). Finally, we performed a mixture of these two systems, for their application for correction of circulation lost. To characterize the raw materials, XRD, XRF, FTIR analysis and titration were performed. The both systems were characterized in tests based on API RP10B. Compressive strength tests were conducted after curing for 24 hours, 7 and 28 days at 58 ?C on the cement-based system and the geopolymer-based system. From the mixtures have been performed mixability tests and micro structural characterizations (XRD, SEM and TG). The results showed that the nano silica, when combined with CaCl2 modified the rheological properties of the cement slurry and from the concentration of 1.5 gpc (200.64 L / m?) it was possible to obtain stable systems. The system mixture caused a change in the microstructure of the material by favoring the rate of geopolymer formation to hinder the C3S phase hydration, thus, the production of CSH phases and Portlandite were harmed. Through the mixability tests it can be concluded that the system, due to reduced setting time of the mixture, can be applied to plug lost circulation zones when mixed downhole / A engenharia de materiais abrange processos e produtos envolvendo v?rias ?reas da engenharia, permitindo que sejam preparados materiais que atendam a v?rias necessidades de novos produtos. Neste caso, este trabalho tem por objetivo estudar um sistema de pasta composto por cimento e geopol?meros, que possa contribuir para a resolu??o de um problema de engenharia que envolve diretamente a explora??o de po?os de petr?leo sujeitos ? perda de circula??o. Para corrigi-la, j? foi proposto na literatura o uso de materiais granulares, fibrosos, redu??o da densidade do fluido de perfura??o ou pasta de cimento e at? mesmo sistemas mistos de fluidos misturados na superf?cie ou no fundo do po?o. Neste trabalho, foi proposto o desenvolvimento de um sistema misto de pastas, sendo o primeiro ? base de cimento Portland e o segundo ? base de geopol?mero. A pasta ? base de cimento, foi formulada com baixa massa espec?fica e aditivos extendedores, 12,0 lb/gal (1,438 g/cm?), apresentando grande car?ter tixotr?pico. Essa pasta foi aditivada com nanoss?lica, em concentra??es de 0,5; 1,0 e 1,5 gpc (66,88; 133,76 e 200,64 L/m3) e CaCl2, em concentra??es de 0,5; 1,0 e 1,5 %. A segunda pasta se constitui ? base de geopol?mero, sendo formulada a partir das raz?es molares de 3,5 (nSiO2/nAl2O3); 0,27 (nK2O/nSiO2); 1,07 (nK2O/nAl2O3) e 13,99 (nH2O/nK2O). E por fim, foi realizada a mistura desses dois sistemas, visando sua aplica??o para corre??o de perda de circula??o. Para caracterizar os precursores foram utilizadas as t?cnicas de DRX, FRX, FTIR e titula??o. Foram realizados os ensaios de caracteriza??o baseados na API RP10B para ambas as pastas puras. Ensaios de resist?ncia ? compress?o foram realizados ap?s a cura por 24 horas, 7 e 28 dias ? 58 ?C, para os sistemas de pasta de cimento e geopol?mero, separadamente. A partir das misturas, foi realizado o ensaio de misturabilidade e caracteriza??es microestruturais (DRX, TG e MEV). Os resultados mostraram que a nanoss?lica, quando combinada ao CaCl2 modificou as propriedades reol?gicas da pasta de cimento e a partir da concentra??o de 1,5 gpc (200,64 L/m?) foi poss?vel se obter sistemas est?veis. A mistura dos sistemas ocasionou uma modifica??o da microestrutura do material, atrav?s do favorecimento da rea??o de geopolimeriza??o em detrimento da hidrata??o da fase C3S, com isso, a produ??o das fases Portlandita e C-S-H foram prejudicadas. Atrav?s dos ensaios de misturabilidade, devido ao reduzido tempo de pega das misturas, pode-se concluir que o sistema misturado, pode ser aplicado para tamponar zonas de perda de circula??o quando misturado no fundo do po?o

Cement slurries are used in oil wells to isolate the production area from the rock formation. An important property of these materials is their durability. Due to the interactions of the cement slurries with aggressive media in the oil wells, the durability can be threatened or lost. Cement slurries modified with polymers are promising materials candidates for cementing oil wells. Thus, it is necessary to evaluate new materials in hostile environments. In this work, new cement slurries were prepared with the Epoxy resin and the ethylenediamine hardener in two different media: distilled water and sea water. The new slurries were tested for their mechanical properties and characterized before and after interaction with the following media: production water, hydrochloric acid solution and mud acid solution. After 365 days of contact with the production water, the modified slurries showed greater chemical and mechanical resistance compared to the slurries without the polymer network (Standard slurries). Moreover, for the modified slurries after contact with the production water, a decrease of 9% in the compressive strength occurred, whereas for the slurries without the polymer network, the reduction reached 40%. Kinetic studies, chemical and thermodynamic equilibrium were carried out in the investigation of the interaction of the cement slurries with the solutions of HCl and mud acid. The results have suggested that the interactions between the modified slurries and the acid media are due to surface reactions with preservation of the hydrated compounds of the cement, causing a mass loss around 25%. For the standard slurries, the mechanism is predominantly diffusion, with structural deterioration of these slurries and mass loss of approximately 46%. Thus, the modified slurries with the polymer network Epoxy-EDA presented good characteristics to be used in the oil well procedures. / Pastas de cimento são utilizadas em poços de petróleo para isolar a zona de produção da formação rochosa. Uma propriedade importante desses materiais é sua durabilidade. Devido suas interações com meios agressivos, essa propriedade pode ser ameaçada ou perdida. Pastas de cimento modificadas com polímeros são materiais promissores candidatos à cimentação de poços de petróleo. Assim, é necessário avaliar novos materiais em meios hostis. Neste trabalho, novas pastas de cimento foram preparadas com a resina Epoxy e o endurecedor Etilenodiamina em dois meios distintos: água destilada e água do mar. As novas pastas foram testadas em relação às suas propriedades mecânicas e caracterizadas antes e após a interação com os seguintes meios: água de produção, solução de ácido clorídrico e solução de mud acid. Após 365 dias de contato com a água de produção, as pastas modificadas apresentaram maior resistência química em comparação com as pastas sem a rede polimérica (pastas padrão). Além disso, para as pastas modificadas após o contato com a água de produção, ocorreu uma diminuição de 9% na resistência à compressão, já para as pastas sem a rede polimérica, a redução atingiu 40%. Estudos cinéticos, equilíbrio químico e termodinâmico foram realizados na investigação da interação das pastas de cimento com as soluções de HCl e mud acid. Os resultaram sugerem que as interações entre as pastas modificadas e os meios ácidos são devido a reações superficiais com preservação dos compostos hidratados do cimento, ocasionando uma perda de massa em torno de 25%. Para as pastas padrão, o mecanismo é predominantemente por difusão, com deterioração estrutural dessas pastas e perda de massa de aproximadamente de 46%. Desta forma, as pastas modificadas com a rede polimérica Epoxy-EDA apresentaram boas características para serem utilizadas em ambientes subterrâneos dos poços de petróleo. / São Cristóvão, SE