Made available in DSpace on 2014-06-12T18:06:31Z (GMT). No. of bitstreams: 2 arquivo7834_1.pdf: 2874536 bytes, checksum: 09c88c82dbe6dea8237fc3a68565894d (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2007 / As blendas poliméricas compostas por polímeros sintéticos e naturais, como o amido, vêm merecendo destaque na área de desenvolvimento de novos materiais por apresentarem propriedades similares aos polímeros sintéticos, e maior facilidade de se degradar na exposição aos microrganismos presentes no meio ambiente, quando são descartadas. O presente trabalho teve por objetivo avaliar a capacidade biodegradadora de uma cultura mista de fungos Phanerochaete chrysosporium e Talaromyces wortmannii, durante 90 dias de exposição, através do teste de Sturm, pela produção de CO2, numa blenda composta por polietileno de baixa densidade (PEBD) e amido, quando estas foram previamente esterilizadas através da radiação gama. Também se avaliou o efeito da exposição à luz ultravioleta nos tempos de 6, 24, 48, 60 e 72 horas, nas blendas poliméricas. A capacidade da fotodegradação, biodegradação e radiação gama foram avaliadas por ensaios mecânicos, microscopia eletrônica de varredura (MEV), espectroscopia no infravermelho com Transformada de Fourier (FTIR), difração de raios-X e variação de massa. Os resultados obtidos comprovaram a degradação das blendas pelas radiações gama e ultravioleta, através da formação de grupos carbonila e vinila na sua estrutura química, e perda de propriedades mecânicas. O consumo crescente e gradativo da blenda pela cultura de fungos, como fonte alternativa de carbono, ficou evidente no acompanhamento da produção de CO2. O efeito combinado da radiação gama e a exposição à cultura de fungos nas blendas poliméricas, foi favorecido quando comparadas às blendas que sofreram apenas a exposição aos fungos

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016. / Made available in DSpace on 2016-09-20T04:19:19Z (GMT). No. of bitstreams: 1 341816.pdf: 3448482 bytes, checksum: 841d2e0c211966364ad139b24e564fd5 (MD5) Previous issue date: 2016 / O cateterismo urinário é um procedimento amplamente utilizado na prática clínica devido a necessidade de controlar o débito urinário de pacientes com comprometimento desse sistema. Contudo, se trata de um procedimento invasivo, sua inserção pode ocasionar trauma mecânico e dor, bem como sua manutenção por longos períodos propiciar infecções bacterianas. Existem muitos estudos envolvendo o desenvolvimento de cateteres associados a agentes antimicrobianos, a fim de reduzir os índices de infecções do trato urinário associadas ao cateter. Entretanto, esse procedimento também gera um desconforto físico ao paciente, causando dor e podendo resultar na inflamação devido ao trauma de inserção. Nesse sentido, esse trabalho explorou a fabricação de estruturas tubulares através do método de extrusão, compostas por Polietileno de Alta Densidade (PEAD) e um anti-inflamatório, Ibuprofeno. As amostras foram desenvolvidas utilizando variáveis de processo como a temperatura de extrusão (150 e 160 °C) e velocidade de rotação da rosca (25 e 35rpm), ainda variando na adição de 0 e 10% de fármaco no sistema. Foram obtidos tubos com dimensões satisfatórias à aplicação proposta, a presença de fármaco provocou alterações na densificação da matriz. Para a condição de processamento de 160 °C houve uma maior fração de fármaco localizado na superfície dos tubos. A temperatura e presença do fármaco foram os fatores mais significativos nas alterações observadas para a cristalinidade. Nos ensaios mecânicos as amostras fabricadas com polímero puro apresentaram rigidez proporcional ao aumento de sua cristalinidade, para aquelas contendo Ibuprofeno, a distribuição do fármaco na matriz exerceu a maior influência na determinação do módulo de flexão e relaxações de cadeias observadas pela análise dinâmico mecânica. Avaliada a cinética de liberação do Ibuprofeno a partir dos tubos, se confirmou que parte do fármaco teve a tendência de se localizar nas áreas mais superficiais dos tubos. Fato que gerou uma rápida liberação inicial, sendo essa ainda determinada pela temperatura de processamento, quanto maior a temperatura aplicada maior a fração de fármaco localizada na superfície.<br> / Abstract : Urinary catheterization is a procedure widely used in clinical practice due to the need to monitor urine output in patients with system impairment. However, this is an invasive procedure; its inclusion can cause mechanical trauma and pain, as well as the maintenance for long periods can propitiate bacterial infections. There are many studies involving the development of catheters associated to antimicrobials agents in order to reduce infection rates associated to the urinary tract catheter. However, this procedure also generates physical discomfort to the patient, causing pain and it may result in inflammation due to insertion trauma. Thus, this study explored the manufacture of tubular structures by the extrusion method, consisting of High Density Polyethylene (HDPE) and an anti-inflammatory, Ibuprofen. The samples were developed using the process variables as the extrusion temperature (150 and 160 °C) and screw speed (25 and 35rpm), ranging in addition from 0 and 10% drug in the system. Tubes with satisfying dimensions to the proposed application were obtained. The presence of drug caused changes in matrix densification. Where for the processing condition of 160 ° C, it was noticed a larger fraction of the drug located on the pipe surface. Factors temperature and presence of drug were more significant in the changes observed for crystallinity. For mechanical testing, the samples manufactured from pure polymer had higher stiffness as greater was the crystallinity for the samples containing ibuprofen, the presence of the drug in the inner regions of the device exerted greater influence to the degree of crystallinity in determining the flexural modulus and relaxations chain observed by dynamic mechanical analysis. Ibuprofen release kinetics from the tubes was evaluated, this confirmed that part of the drug tended to be located in the most surface areas of the tubes. Which leads to a rapid initial release, this being also determined by the processing temperature, where the higher the temperature the greater the drug fraction located on the surface.

Ingeniero Civil Industrial / El presente trabajo muestra la evaluación de factibilidad técnico económica realizada para un proyecto de carácter ecológico que contempla la producción de perfiles plásticos a partir de desechos de polietileno de baja densidad provenientes de la industria salmonera de la región de Los Lagos. El estudio, que comprende la creación de una unidad estratégica de negocios, fue elaborado para la empresa Novapack Ltda., ubicada en la ciudad de Puerto Montt. El análisis técnico contempló el estudio de las propiedades del polietileno, las formas en la que es posible reciclarlo y la identificación de los tipos de madera plástica. También se analizó la materia prima y la maquinaria e infraestructura necesarias para la elaboración del producto final. Además de esto, se realizó un estudio del mercado nacional de la madera plástica, identificando las empresas participantes y sus respectivos precios. Por último, se hizo una evaluación económica por medio de un flujo de caja, determinando el VAN y TIR del proyecto, como también un análisis de escenarios y un análisis de sensibilidad. Los resultados de la evaluación técnica realizada permiten concluir que Novapack posee con las condiciones necesarias para llevar a cabo un plan de esta naturaleza, contando con infraestructura propia y parte importante de la maquinaria necesaria para la producción de los perfiles, debiendo únicamente realizar la adquisición de una máquina extrusora para la confección de las tablas de plastic lumber. La evaluación económica se realizó utilizando un horizonte de evaluación de 10 años y una tasa de descuento del 12%. Con una inversión inicial que alcanza los $45.000.000, se obtuvo como resultado para el proyecto puro un VAN de $85.047.425 (3.265,82 U.F.), una TIR de 20,85% y un período de recuperación de capital de 7 años. Posteriormente, al analizar el escenario con financiamiento bancario por un monto igual al 78% de la inversión, la rentabilidad del proyecto mejoró ostensiblemente, obteniéndose un VAN de $123.880.419 (4.757,01 U.F.) y una TIR de 29,66%. Producto de lo anterior, se recomienda a Novapack llevar a cabo este proyecto de inversión utilizando financiamiento bancario, puesto que es una alternativa rentable que potencia su imagen de empresa verde , utilizando maquinaria que actualmente se encuentra subutilizada y que le permitiría expandirse a un nuevo mercado, diferente a la industria salmonera. / 22/8/2021

Magíster en Ciencias de la Ingeniería, Mención Química / Ingeniera Civil Química / Las poliolefi nas son uno de los plásticos de mayor producción y es por esto que representan un gran porcentaje de los desechos plásticos. Lo anterior, junto con las exigencias de las normativas medioambientales, hace que el tema del reciclaje de estos desechos sea un tema relevante. Dentro de los tipos de reciclaje de desechos se destaca el reciclaje químico donde uno de los procesos más utilizados es la pirólisis, la cual puede realizarse en presencia de un catalizador obteniendo una mayor selectividad y productos de mayor valor comercial. El objetivo de esta tesis es estudiar las variables de operación de la pirólisis catalítica de polietileno y, de este modo, controlar la selectividad hacia gases o condensables (ceras y líquidos) en un reactor de lecho fi jo, utilizando diferentes catalizadores tanto comerciales como otros desarrollados en el laboratorio. Los productos gaseosos y condensables obtenidos fueron analizados en cromatógrafos de gas para comparar su composición. Se logró establecer que las condiciones de operación adecuadas fueron 450 °C y 50% en peso de carga de catalizador y no se observaron efectos al utilizar distintos tipos de polietileno. Al usar un catalizador se disminuyó la temperatura de degradación notando un aumentó del porcentaje de gases entre un 83 %-51% con respecto a una pirólisis térmica, donde solo se producen entre un 0,8 %-1 %. Con los catalizadores desarrollados en el laboratorio se obtuvo un mayor porcentaje de condensables (28 %-48 %) comparado con lo obtenido con los comerciales (11 %-29 %) y esto se debe principalmente a las propiedades ácidas y estructurales de ellos. En general, los catalizadores mostraron que aumentaban la cantidad de C4 presentes en los gases. Por otra parte, los productos condensables al ser caracterizados mostraron un alto porcentaje de hidrocarburos del rango diésel, observando un especial aumento de estos en los catalizadores desarrollados en el laboratorio. Además, se realizaron pirólisis con mezclas de poliolefi nas, demostrando que se disminuye la cantidad de gases y se favorece la producción de condensables. Luego se estudió la desactivación de los diferentes catalizadores, observando que los desarrollados en el laboratorio se desactivan más rápidamente, sin embargo, estos pueden ser regenerados logrando resultados similares a uno comercial. Por otra parte, se comprobó que en un lecho fijo se pueden predecir bien los resultados obtenidos en reactores tipo industriales. Finalmente, se realizó una evaluación de prefactiblidad económica con uno de los catalizadores desarrollados en el laboratorio, obteniendo un VAN positivo. Gracias al estudio realizado se comprobó que con los catalizadores desarrollados en el laboratorio se pueden obtener combustibles de buena calidad. Se espera en el futuro que este tipo de catalizadores ayuden a que la pirólisis sea una alternativa rentable para disminuir la cantidad de desechos plásticos.

Orientador: Antonio Jose de A. Meirelles / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-07-19T15:23:35Z (GMT). No. of bitstreams: 1 Silva_LuizaHelenaMellerda_M.pdf: 2160286 bytes, checksum: e34718444cf6f9d7ede0182fec206e6b (MD5) Previous issue date: 1994 / Resumo: Tendo em vista a falta de dados experimentais na literatura, para sistemas aquosos bifásicos compostos' por um polímero e um sal e, com o intuito de fornecer um suporte maior ao estudo da partição de biomoléculas nestes sistemas, apresentamos neste trabalho dados de equilíbrio para os sistemas polietileno glicol 8000/fosfato de potássio/água e polietileno glicol 1000/fosfato de potássio/água a diferentes valores de temperatura e pH. Os métodos analíticos utilizados foram: titulação potenciométrica para a determinação da concentração do sal e umidade em estufa a vácuo a 600e por 24h para a determinação da concentração da água; a concentração do polímero obtida por diferença. O pH, variado em função da equação de Henderson Hasselbach e a temperatura mantida no interior da célula por um banho termostático garantindo uma variação não superior a 0,1° C. Os resultados obtidos permitem observar que um aumento na região de separação é causado com a elevação da temperatura e do pH, obtendo-se deste modo uma maior diferença na .concentração do polímero entre as duas fases. Deve-se destacar que o coeficiente de partição de biomoléculas é 'significativamente dependente desta diferença de concentração (comprimento da "tié line"). Verificou-se que a temperatura influencia o equilíbrio de fases de duas formas, mudando a inclinação das linhas de amarração e deslocando a linha binodal, aumentando ou diminuindo a região de separação. Se a temperatura é aumentada, aumenta também a região de separação e as linhas de amarração tendem a ter um grau de inclinação maior se diminuída o efeito é inverso. No caso de partição de proteínas a temperatura é de fundamental importância, pois seu manuseio (variação) pode causar desde mudanças de estrutura à desnaturação. Além disso, verificou-se também que o efeito da temperatura é maior na região entre 40° C e 25°C, do que de 25° C para 40°C, apesar do gradiente ser praticamente o mesmo. Com respeito ao pH, observa-se que a medida que ele aumenta, aumenta também a região de separação e varia a inclinação das linhas de amarração, como a temperatura. Porém o efeito de inclinação nas linhas de amarração é maior. Nos experimentos, observou-Se que em temperaturas menores a separação se torna mais difícil e se o pH for diminuído causa a formação de três fases. Pouco se conhece na literatura sobre o comportamento desta variável / Abstract: This work presents experimental equilibrium data. for two-phase polymer-salt aqueous systems. This is an important contribution to the study of partition of biomolecules. It is important to remind the lack of such data in the literature. The systems studied covers polyethilene glycol 8000 and 1000 plus potassium phosphate in water at a range of temperature and pH. Methods of analysis were:. potentiometric tritation for salt concentration and water content in a vacuum oven at 60° during 24 hours. Equation of Henderson-Haselbach was used for pH while temperature was maintained within +/- 0,1ºC. Results indicate an increase in the separation region caused by elevation of temperature and pH thus giving an higher difference in polymer concentration between phases. It must be enphasized that biomolecules parti tion coefficient is highly dependent on this concentration difference (tie line lenght). It was demonstrated that temperature affects phase equilibrium by changing the gradient of tie lines and moving the binodal curve thus affecting the separation region. the elevation of temperature increases the separation region and tie lines tend to higher gradients; the opposite is also verified. For proteins separation temperature is of paramount importance 'due to structure changes and denaturation. It was seen that temperature importance is higher in the 4°c - 25° C region as compared to 25°C - 40°C. Increasing the pH it was observed an increase both in the separation region and gradient of tie lines but little is known or reported in the literature about this topic. It was observed that at lower values of both temperature and pH a third phase (a solid one) was produced / Mestrado / Engenharia de Alimentos / Mestre em Engenharia de Alimentos

Orientadores : Maria Isabel Felisberti, Marco-Aurelio De Paoli / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-07-20T03:05:36Z (GMT). No. of bitstreams: 1 Silva_MarciaAparecidada_M.pdf: 3081971 bytes, checksum: a912680981aca4ac6b7f93d486f49161 (MD5) Previous issue date: 1995 / Mestrado

Memoria para optar al título de Ingeniero Civil Químico / La cantidad de alimentos que se pierden por factores asociados al envasado y la creciente industria frutícola en Chile, han motivado una creciente investigación en el área de envasado activo. Es por ello que, en la presente memoria, se prepararon nanopartículas de grafeno oxidado (GO) con diferente exfoliación, GO sin sonicar, GO sonicado y GO sonicado de alta oxidación, para ser utilizados como relleno en nanocompósitos de polietileno lineal de baja densidad, como potenciales envases activos. El objetivo fue estudiar el efecto de la incorporación de diferentes concentraciones de estas nanopartículas en las propiedades de barrera, mecánicas, térmicas, y antimicrobiales. En las propiedades de barrera al oxígeno, el GO sonicado y el GO de alta oxidación tuvieron efectos positivos en la permeabilidad, disminuyéndola hasta en un 25% para los dos tipos, y aumentándola para el GO sin sonicado. Lo primero se debió al aumento en la tortuosidad, que disminuye la difusión del gas en el del material, y lo segundo a la formación de volúmenes libres. La permeabilidad al vapor de agua de los nanocompósitos presentó mejoras, con una reducción del 28% para el GO sonicado y GO de alta oxidación. Esto fue debido a la tortuosidad generada por el GO, que en parte fue anulada por el carácter hidrofílico del GO, que aumentó la solubilidad de la matriz al agua. El ángulo de contacto de las muestras preparadas no mostró diferencias significativas respecto al blanco, debido al poco impacto superficial del GO. Las propiedades mecánicas también se vieron beneficiadas con la adición de GO, logrando un aumento de hasta un 20% en las muestras con GO sonicado y de alta oxidación con una concentración de 5%, sin disminuir la elongación a la rotura. Esto se debió al grado de dispersión de los GO con mayor exfoliación, que restringió el movimiento de las cadenas poliméricas. La resistencia térmica de los nanocompósitos tuvo leves mejorías debido a la presencia del GO. Sin embargo, estas mejoras no estuvieron relacionadas con el nivel de exfoliación del GO, ya que todas las muestras tuvieron una resistencia en promedio 10 [°C] mayor a la muestra blanca. Las muestras mostraron actividad antimicrobial debido a su capacidad de aplastar y oxidar las células, pero sin mostrar tendencia entre los GO. Como conclusión general se tuvo que el GO mejora las propiedades del polietileno de baja densidad lineal como para poder ser utilizado en envasado de alimentos, siempre y cuando se encuentre exfoliado, oxidado y bien disperso en la matriz polimérica, siendo capaz de presentar mejoras en propiedades de barrera, mecánicas, térmicas y antimicrobiales.

As propriedades de selagem de filmes plásticos são um dos principais gargalos para o aumento de produtividade em processos de empacotamento automático de produtos, em que é necessário otimizar a velocidade do envase, a temperatura de solda e a qualidade da embalagem de forma a garantir a integridade do produto embalado. O objetivo deste trabalho foi determinar as características do polímero que mais influenciam nas propriedades de selagem de filmes de polietileno metalocênico. Foram produzidos nove filmes de 3 camadas por coextrusão em que se variou a composição da camada de selagem com o uso de sete tipos de polietilenos. Seis PEs foram obtidos com catalisadores metalocênicos, sendo que quatro possuem alto teor de comonômero (mPEUBD), além de um PEBD obtido através de polimerização via radical livre em altas pressões. Características intrínsecas de cada polietileno, como tipo e teor de comonômero, distribuição de massa molar, distribuição de composição química e propriedades reológicas foram correlacionadas com as propriedades de selagem, mecânicas e ópticas dos filmes. Verificou-se que quanto maior o teor de comonômeros e quanto mais larga a distribuição de composição química no PE metalocênico utilizado na camada de selagem, maior a sua efetividade em reduzir a temperatura de solda e maior a resistência mecânica da região de selagem do filme. Polietilenos com ramificações longas, apesar de apresentar melhor processabilidade, apresentam pior desempenho na selagem. Em relação às propriedades mecânicas e ópticas, os filmes apresentaram maior resistência ao impacto e à perfuração, maior alongamento no escoamento e maior transparência e brilho com o uso de mPE com maior teor de comonômeros, em detrimento de uma redução na resistência ao rasgo e rigidez. / Sealing properties of plastic films are one of the main bottlenecks to raise productivity in automatic form-fill-seal packaging processes, and it is necessary to optimize speed, sealing temperature and packaging quality to ensure integrity of the packaged product. The objective of this study was determine the polymer characteristics that most influence sealing properties of films produced with metallocene polyethylene. Nine 3-layer films were produced by coextrusion varying the composition of sealing layer by using seven types of polyethylenes. Six PEs were obtained with metallocene catalysts (mPE), where four of them have high comonomer content (mULDPE), and one LDPE obtained by free radical polymerization at high pressures. Intrinsic characteristics of each polyethylene, such as type and content of comonomer, molar mass distribution, chemical composition distribution, thermal behavior and rheological properties were determined and correlated with sealing, mechanical and optical properties of the films. It has been found that the higher the comonomer content and the broader its chemical composition distribution in metallocene PE used in the sealing layer, the greater its effectiveness in reducing the sealing temperature, with improves on mechanical strength of sealing region. Polyethylenes with long chain branches, despite better processability, showed poorer sealing performance. Regarding mechanical and optical properties, films produced with mULDPE presented greater impact and puncture resistance, better transparency and gloss, and poorer stiffness and tearing resistance.

As propriedades de selagem de filmes plásticos são um dos principais gargalos para o aumento de produtividade em processos de empacotamento automático de produtos, em que é necessário otimizar a velocidade do envase, a temperatura de solda e a qualidade da embalagem de forma a garantir a integridade do produto embalado. O objetivo deste trabalho foi determinar as características do polímero que mais influenciam nas propriedades de selagem de filmes de polietileno metalocênico. Foram produzidos nove filmes de 3 camadas por coextrusão em que se variou a composição da camada de selagem com o uso de sete tipos de polietilenos. Seis PEs foram obtidos com catalisadores metalocênicos, sendo que quatro possuem alto teor de comonômero (mPEUBD), além de um PEBD obtido através de polimerização via radical livre em altas pressões. Características intrínsecas de cada polietileno, como tipo e teor de comonômero, distribuição de massa molar, distribuição de composição química e propriedades reológicas foram correlacionadas com as propriedades de selagem, mecânicas e ópticas dos filmes. Verificou-se que quanto maior o teor de comonômeros e quanto mais larga a distribuição de composição química no PE metalocênico utilizado na camada de selagem, maior a sua efetividade em reduzir a temperatura de solda e maior a resistência mecânica da região de selagem do filme. Polietilenos com ramificações longas, apesar de apresentar melhor processabilidade, apresentam pior desempenho na selagem. Em relação às propriedades mecânicas e ópticas, os filmes apresentaram maior resistência ao impacto e à perfuração, maior alongamento no escoamento e maior transparência e brilho com o uso de mPE com maior teor de comonômeros, em detrimento de uma redução na resistência ao rasgo e rigidez. / Sealing properties of plastic films are one of the main bottlenecks to raise productivity in automatic form-fill-seal packaging processes, and it is necessary to optimize speed, sealing temperature and packaging quality to ensure integrity of the packaged product. The objective of this study was determine the polymer characteristics that most influence sealing properties of films produced with metallocene polyethylene. Nine 3-layer films were produced by coextrusion varying the composition of sealing layer by using seven types of polyethylenes. Six PEs were obtained with metallocene catalysts (mPE), where four of them have high comonomer content (mULDPE), and one LDPE obtained by free radical polymerization at high pressures. Intrinsic characteristics of each polyethylene, such as type and content of comonomer, molar mass distribution, chemical composition distribution, thermal behavior and rheological properties were determined and correlated with sealing, mechanical and optical properties of the films. It has been found that the higher the comonomer content and the broader its chemical composition distribution in metallocene PE used in the sealing layer, the greater its effectiveness in reducing the sealing temperature, with improves on mechanical strength of sealing region. Polyethylenes with long chain branches, despite better processability, showed poorer sealing performance. Regarding mechanical and optical properties, films produced with mULDPE presented greater impact and puncture resistance, better transparency and gloss, and poorer stiffness and tearing resistance.

As propriedades de selagem de filmes plásticos são um dos principais gargalos para o aumento de produtividade em processos de empacotamento automático de produtos, em que é necessário otimizar a velocidade do envase, a temperatura de solda e a qualidade da embalagem de forma a garantir a integridade do produto embalado. O objetivo deste trabalho foi determinar as características do polímero que mais influenciam nas propriedades de selagem de filmes de polietileno metalocênico. Foram produzidos nove filmes de 3 camadas por coextrusão em que se variou a composição da camada de selagem com o uso de sete tipos de polietilenos. Seis PEs foram obtidos com catalisadores metalocênicos, sendo que quatro possuem alto teor de comonômero (mPEUBD), além de um PEBD obtido através de polimerização via radical livre em altas pressões. Características intrínsecas de cada polietileno, como tipo e teor de comonômero, distribuição de massa molar, distribuição de composição química e propriedades reológicas foram correlacionadas com as propriedades de selagem, mecânicas e ópticas dos filmes. Verificou-se que quanto maior o teor de comonômeros e quanto mais larga a distribuição de composição química no PE metalocênico utilizado na camada de selagem, maior a sua efetividade em reduzir a temperatura de solda e maior a resistência mecânica da região de selagem do filme. Polietilenos com ramificações longas, apesar de apresentar melhor processabilidade, apresentam pior desempenho na selagem. Em relação às propriedades mecânicas e ópticas, os filmes apresentaram maior resistência ao impacto e à perfuração, maior alongamento no escoamento e maior transparência e brilho com o uso de mPE com maior teor de comonômeros, em detrimento de uma redução na resistência ao rasgo e rigidez. / Sealing properties of plastic films are one of the main bottlenecks to raise productivity in automatic form-fill-seal packaging processes, and it is necessary to optimize speed, sealing temperature and packaging quality to ensure integrity of the packaged product. The objective of this study was determine the polymer characteristics that most influence sealing properties of films produced with metallocene polyethylene. Nine 3-layer films were produced by coextrusion varying the composition of sealing layer by using seven types of polyethylenes. Six PEs were obtained with metallocene catalysts (mPE), where four of them have high comonomer content (mULDPE), and one LDPE obtained by free radical polymerization at high pressures. Intrinsic characteristics of each polyethylene, such as type and content of comonomer, molar mass distribution, chemical composition distribution, thermal behavior and rheological properties were determined and correlated with sealing, mechanical and optical properties of the films. It has been found that the higher the comonomer content and the broader its chemical composition distribution in metallocene PE used in the sealing layer, the greater its effectiveness in reducing the sealing temperature, with improves on mechanical strength of sealing region. Polyethylenes with long chain branches, despite better processability, showed poorer sealing performance. Regarding mechanical and optical properties, films produced with mULDPE presented greater impact and puncture resistance, better transparency and gloss, and poorer stiffness and tearing resistance.