The R2PdSi3 (R = heavy rare earth) have been synthesized first in 1990 in the search for materials with unusual electronic properties. The availability of single crystals was the starting point for several investigations of the magneto-crystalline anisotropy, also in applied magnetic fields. The results of the observed properties in resistivity, magnetization and susceptibility lead to the summary that these compounds range from interesting to exotic and that their magnetic properties are low dimensional, spin-glass like and altogether “novel”. The focus of this thesis is the careful analysis of the magnetic properties and magnetic structures of single crystalline R2PdSi3 (R = Gd, Tb, Dy, Ho, Er, Tm). The investigation of macroscopic properties uses magnetization and ac-susceptibility measurements. Resulting from these investigations are magnetic phase diagrams. Neutron and resonant X-ray diffraction measurements elucidate the magnetic structure for the investigated compounds. The phase diagram of Tb2PdSi3 is the starting point of a detailed neutron diffraction study in applied magnetic fields up to 6.5 T and in the temperature range from 0.05 K to 100 K on this compound. Key to the understanding of the R2PdSi3 is the strong coupling of crystallographic structure to the magnetic properties. Thus the established framework of exchange interaction and magneto-crystalline anisotropy allows a collective description instead of a “novel” behavior. / Die R2PdSi3 (R = schwere seltene Erde) sind erstmals 1990, im Rahmen der Suche nach Materialien mit ungewöhnlichen elektronischen Eigenschaften, synthetisiert worden. Die Verfügbarkeit von Einkristallen war der Startpunkt für eine Vielzahl von Untersuchungen, auch in angelegten Magnetfeldern, der magneto-kristallinen Anisotropie. Das Ergebnis der untersuchten Eigenschaften Widerstand, Magnetisierung und Suszeptibilität führte zu dem Schluss, dass diese Verbindungen interessant bis exotisch und das ihre magnetischen Eigenschaften niedrig dimensional, spin-glas ähnlich und insgesamt “neuartig“ sind. Der Schwerpunkt dieser Dissertation ist die genaue Analyse der magnetischen Eigenschaften und Magnetischen Strukturen von einkristallinen R2PdSi3 (R = Gd, Tb, Dy, Ho, Er, Tm). Magnetisierungs- und Suszeptibilitäts-Messungen werden zur Untersuchung der makroskopischen Eigenschaften benutzt. Resultat dieser Untersuchungen sind magnetische Phasendiagramme. Neutronen und resonante Röntgendiffraktrometrie klären die magnetische Struktur der untersuchten Verbindungen auf. Das Phasendiagramm von Tb2PdSi3 ist der Startpunkt einer detaillierten Neutronendiffraktionsuntersuchung dieser Verbindung in Magnetfeldern bis 6.5 T und im Temperaturbereich von 0.05 K und 100 K. Der Schlüssel zum Verständnis der R2PdSi3 ist die starke Kopplung der kristallografischen Struktur und der magnetischen Eigenschaften. Dadurch erlaubt das etablierte System aus Austauschwechselwirkung und magneto-kristalliner Anisotropie eine gemeinsame Beschreibung anstatt „neuartigem“ Verhalten.

The R2PdSi3 (R = heavy rare earth) have been synthesized first in 1990 in the search for materials with unusual electronic properties. The availability of single crystals was the starting point for several investigations of the magneto-crystalline anisotropy, also in applied magnetic fields. The results of the observed properties in resistivity, magnetization and susceptibility lead to the summary that these compounds range from interesting to exotic and that their magnetic properties are low dimensional, spin-glass like and altogether “novel”. The focus of this thesis is the careful analysis of the magnetic properties and magnetic structures of single crystalline R2PdSi3 (R = Gd, Tb, Dy, Ho, Er, Tm). The investigation of macroscopic properties uses magnetization and ac-susceptibility measurements. Resulting from these investigations are magnetic phase diagrams. Neutron and resonant X-ray diffraction measurements elucidate the magnetic structure for the investigated compounds. The phase diagram of Tb2PdSi3 is the starting point of a detailed neutron diffraction study in applied magnetic fields up to 6.5 T and in the temperature range from 0.05 K to 100 K on this compound. Key to the understanding of the R2PdSi3 is the strong coupling of crystallographic structure to the magnetic properties. Thus the established framework of exchange interaction and magneto-crystalline anisotropy allows a collective description instead of a “novel” behavior. / Die R2PdSi3 (R = schwere seltene Erde) sind erstmals 1990, im Rahmen der Suche nach Materialien mit ungewöhnlichen elektronischen Eigenschaften, synthetisiert worden. Die Verfügbarkeit von Einkristallen war der Startpunkt für eine Vielzahl von Untersuchungen, auch in angelegten Magnetfeldern, der magneto-kristallinen Anisotropie. Das Ergebnis der untersuchten Eigenschaften Widerstand, Magnetisierung und Suszeptibilität führte zu dem Schluss, dass diese Verbindungen interessant bis exotisch und das ihre magnetischen Eigenschaften niedrig dimensional, spin-glas ähnlich und insgesamt “neuartig“ sind. Der Schwerpunkt dieser Dissertation ist die genaue Analyse der magnetischen Eigenschaften und Magnetischen Strukturen von einkristallinen R2PdSi3 (R = Gd, Tb, Dy, Ho, Er, Tm). Magnetisierungs- und Suszeptibilitäts-Messungen werden zur Untersuchung der makroskopischen Eigenschaften benutzt. Resultat dieser Untersuchungen sind magnetische Phasendiagramme. Neutronen und resonante Röntgendiffraktrometrie klären die magnetische Struktur der untersuchten Verbindungen auf. Das Phasendiagramm von Tb2PdSi3 ist der Startpunkt einer detaillierten Neutronendiffraktionsuntersuchung dieser Verbindung in Magnetfeldern bis 6.5 T und im Temperaturbereich von 0.05 K und 100 K. Der Schlüssel zum Verständnis der R2PdSi3 ist die starke Kopplung der kristallografischen Struktur und der magnetischen Eigenschaften. Dadurch erlaubt das etablierte System aus Austauschwechselwirkung und magneto-kristalliner Anisotropie eine gemeinsame Beschreibung anstatt „neuartigem“ Verhalten.

Previous studies on the family of inter-metallic rare-earth compounds R2PdSi3 revealed multifaceted magnetic properties, for instance, spin-glass like behavior. Experimental observations include: Signs of a crystallographic superstructure, complicated magnetic structures both in zero field and in applied magnetic fields as well as a generic phase in applied fields for compounds in the series with the heavy rare-earths R = Gd, Tb, Dy, Ho, Er and Tm. This thesis expands the studies on the magnetic properties of R2PdSi3 employing mainly neutron scattering on single crystals with the focus on the compounds with R = Ho, Er and Tm. A detailed analysis of the crystallographic superstructure using modulation wave approach and group theory is presented. The resulting structure implies the existence of two different rare-earth sites with reduced symmetry and an arrangement of the different sites according to sequences as determined by the superstructure. It will be shown that the reduced symmetry of the rare-earth sites is explicitly observed in the energy spectra of inelastic neutron scattering. The results on the magnetic structures and excitations are shown and discussed in the framework of the superstructure model. Specifically the generic phase in applied fields is interpreted as a direct consequence of the crystallographic superstructure. It is rather unusual that a crystallographic superstructure is playing such a decisive, and through the field dependence also tunable role in determining the magnetic properties as observed in R2PdSi3. The mediating interactions between the crystallographic part and the magnetic part of the system will be discussed. / Frühere Untersuchungen der Familie der intermetallischen Selten-Erd Verbindungen R2PdSi3 zeigten vielfältige magnetische Eigenschaften, zum Beispiel ein Spin-glas ähnliches Verhalten. Die experimentellen Beobachtungen beinhalten: Zeichen für eine kristallographische Überstruktur, komplizierte magnetische Strukturen, sowohl im Nullfeld als auch in angelegten Magnetfeldern und darüberhinaus eine generische Phase in Magnetfeldern in den untersuchten Verbindungen mit den schweren Selten-Erden R = Gd, Tb, Dy, Ho, Er und Tm. Diese Dissertation erweitert die Untersuchungen der magnetischen Eigenschaften von R2PdSi3, hauptsächlich durch Verwendung von Neutronenstreuung an Einkristallen, mit dem Schwerpunkt auf den Verbindungen mit R = Ho, Er und Tm. Eine genaue Analyse der kristallographischen Überstruktur mittels Modulationswellenansatz und Gruppentheorie wird präsentiert. Das resultierende Strukturmodell impliziert die Existenz zweier unterschiedlicher Selten-Erd Lagen mit reduzierter Symmetrie in einer Anordnung entsprechend der durch die Überstruktur festgelegten Sequenzen. Es wird gezeigt, dass die reduzierte Symmetrie der Selten-Erd Lagen durch Beobachtungen der inelastischen Neutronenstreuung explizit bestätigt wird. Die Ergebnisse der magnetischen Strukturen und Anregungen werden im Rahmen des Überstrukturmodels diskutiert. Speziell die generische Phase folgt als direkte Konsequenz aus der Überstruktur. Es ist eher ungewöhnlich, dass eine kristallographische Überstruktur eine solch bestimmende und bei Magnetfeldvariation auch “tunebare” Rolle spielt, wie dies in den R2 PdSi3 Verbindungen beobachtet wird. Die vermittelnden Wechselwirkungen zwischen Struktur und Magnetismus werden diskutiert.

Previous studies on the family of inter-metallic rare-earth compounds R2PdSi3 revealed multifaceted magnetic properties, for instance, spin-glass like behavior. Experimental observations include: Signs of a crystallographic superstructure, complicated magnetic structures both in zero field and in applied magnetic fields as well as a generic phase in applied fields for compounds in the series with the heavy rare-earths R = Gd, Tb, Dy, Ho, Er and Tm. This thesis expands the studies on the magnetic properties of R2PdSi3 employing mainly neutron scattering on single crystals with the focus on the compounds with R = Ho, Er and Tm. A detailed analysis of the crystallographic superstructure using modulation wave approach and group theory is presented. The resulting structure implies the existence of two different rare-earth sites with reduced symmetry and an arrangement of the different sites according to sequences as determined by the superstructure. It will be shown that the reduced symmetry of the rare-earth sites is explicitly observed in the energy spectra of inelastic neutron scattering. The results on the magnetic structures and excitations are shown and discussed in the framework of the superstructure model. Specifically the generic phase in applied fields is interpreted as a direct consequence of the crystallographic superstructure. It is rather unusual that a crystallographic superstructure is playing such a decisive, and through the field dependence also tunable role in determining the magnetic properties as observed in R2PdSi3. The mediating interactions between the crystallographic part and the magnetic part of the system will be discussed. / Frühere Untersuchungen der Familie der intermetallischen Selten-Erd Verbindungen R2PdSi3 zeigten vielfältige magnetische Eigenschaften, zum Beispiel ein Spin-glas ähnliches Verhalten. Die experimentellen Beobachtungen beinhalten: Zeichen für eine kristallographische Überstruktur, komplizierte magnetische Strukturen, sowohl im Nullfeld als auch in angelegten Magnetfeldern und darüberhinaus eine generische Phase in Magnetfeldern in den untersuchten Verbindungen mit den schweren Selten-Erden R = Gd, Tb, Dy, Ho, Er und Tm. Diese Dissertation erweitert die Untersuchungen der magnetischen Eigenschaften von R2PdSi3, hauptsächlich durch Verwendung von Neutronenstreuung an Einkristallen, mit dem Schwerpunkt auf den Verbindungen mit R = Ho, Er und Tm. Eine genaue Analyse der kristallographischen Überstruktur mittels Modulationswellenansatz und Gruppentheorie wird präsentiert. Das resultierende Strukturmodell impliziert die Existenz zweier unterschiedlicher Selten-Erd Lagen mit reduzierter Symmetrie in einer Anordnung entsprechend der durch die Überstruktur festgelegten Sequenzen. Es wird gezeigt, dass die reduzierte Symmetrie der Selten-Erd Lagen durch Beobachtungen der inelastischen Neutronenstreuung explizit bestätigt wird. Die Ergebnisse der magnetischen Strukturen und Anregungen werden im Rahmen des Überstrukturmodels diskutiert. Speziell die generische Phase folgt als direkte Konsequenz aus der Überstruktur. Es ist eher ungewöhnlich, dass eine kristallographische Überstruktur eine solch bestimmende und bei Magnetfeldvariation auch “tunebare” Rolle spielt, wie dies in den R2 PdSi3 Verbindungen beobachtet wird. Die vermittelnden Wechselwirkungen zwischen Struktur und Magnetismus werden diskutiert.

Obwohl ultrahohe Magnetfelder jenseits von 100 T mittels spezieller Methoden experimentell nutzbar wurden, sind Magnetisierungsmessungen in diesen Feldern noch immer sehr kompliziert. Magnetfelder im Megagauß-Bereich lassen sich heute allein durch die semidestruktive Single-Turn-Coil (STC)-Methode und durch die vollständig destruktive Flußkompression erzeugen. In beiden Fällen sind die gepulsten Felder auf eine Dauer von wenigen Mikrosekunden und ein nutzbares Feldvolumen von wenigen Kubikzentimetern beschränkt. Dadurch bedingt sind nur solche Methoden für Magnetisierungsmessungen anwendbar, die sich an diese ungünstigen Randbedingungen anpassen lassen. Die Faraday-Rotation kann für optisch transparente Proben sinnvoll sein, jedoch ist die induktive Messung mittels kompensierter Pick-up-Spulen die einzige direkte Methode. Die vorliegende Arbeit beschreibt die Entwicklung und Anwendung eines solchen Meßsystems in einem STC-Feldgenerator. Im Hinblick auf das Meßsystem hat sich die sehr gute geometrische Kompensation der Pick-up-Spulen als wesentlich herausgestellt. Wichtig sind daneben aber auch eine hohe Bandbreite bzw. eine unverzerrte Sprungantwort. Als äußerst effektiv hat sich insbesondere die umfassende elektromagnetische Abschirmung des Meßsystems erwiesen, so daß die vom STC-Generator ausgehenden Störungen weitgehend unterdrückt werden. Besondere, für Magnetisierungsmessungen ungünstige Eigenschaften des STC-Systems, werden dargestellt und diskutiert. Magnetisierungsmessungen bei tiefen Temperaturen an den van Vleck-Paramagneten TmPO4 und TmPO4 ergaben Anomalien bei rund 30 T bzw. 50 T für ein Feld parallel zur tetragonalen Achse. Dieser Effekt resultiert aus einer Überkreuzung der beiden niedrigsten Energieniveaus in starken Magnetfeldern und führt zu einem scharfen Sprung in der Magnetisierung. Temperaturabhängige Messungen belegen den wesentlichen Einfluß des magnetokalorischen Effekts in kurzen gepulsten Feldern. Pulverproben der intermetallischen Verbindungen RMn2Ge2 (R = Gd, Tb, Dy, Ho, Er, Y) wurden bei Helium-Temperaturen in Feldern bis zu 150 T untersucht. Abhängig vom Selten-Erd-Ion wurden in allen Verbindungen ein oder mehrere feldinduzierte metamagnetische Phasenübergänge beobachtet. Sie können auf eine Änderung der magnetischen Struktur des Mn-Untersystems zurückgeführt werden. Die kritischen Felder für den Übergang zur ferromagnetischen Phase betragen zwischen 90 T und 118 T (YMn2Ge2: 55 T). Detaillierte Rechnungen werden im Rahmen eines erweiterten Molekularfeld-Modells durchgeführt. / Although ultrahigh magnetic fields in excess of 100 T have become available by specialized techniques, magnetization measurements in these fields are still a challenging task. Nowadays, magnetic fields in the megagauss range can be produced only by the semidestructive single-turn coil (STC) technique and by the fully destructive flux compression. In both cases these pulsed fields are limited to microsecond pulse duration and a usable field volume of not more than a few cubic centimeters. As a result, only those methods can be used for magnetization measurements, which can be adapted to these difficult boundary conditions. The Faraday rotation can be suitable for optically transparent samples, but the only direct technique is the induction method based on compensated pick-up coils. The present work deals with the development of such a measurement system and its application to various materials in fields up to 150 T produced by the STC. Regarding the measurement system, geometrically very well compensated pick-up coils turned out to be absolutely necessary as well as a large bandwidth and an appropriate transient response. In particular a comprehensive electromagnetic shielding, which makes use of a wire metal, proved to be very effective in suppressing disturbances produced by the STC system. Besides, some inherent characteristics and limitations of the STC generator with respect to magnetization measurements are revealed and discussed. Magnetization measurements were performed on the van Vleck paramagnets TmPO4 and PrVO4, and anomalies were found at about 30 T and 50 T, respectively, at low temperatures for a field along the tetragonal axis. This effect is due to a crossing of the lowest energy levels in high magnetic fields and results in a sharp jump in magnetization. Temperature dependent measurements provide evidence that the magnetocaloric effect plays an essential role in short pulse fields produced by the STC. Powder samples of the intermetallic compounds RMn2Ge2 (R = Gd, Tb, Dy, Ho, Er, Y) have been investigated at liquid helium temperature up to 150 T. Depending on the rare-earth ion one or more field-induced metamagnetic phase transitions have been observed in all compounds, and they are found to be associated with a change in the magnetic structure of the Mn subsystem. The phase transitions to the ferromagnetic phase occur between 90 T and 118 T (YMn2Ge2: 55 T). Detailed calculations are performed using an extended molecular field model.

This thesis describes the syntheses, the crystal structures, and the physical properties of some new ternary and quaternary rare-earth coinage metal arsenides, selenides and oxides. All ternary compounds LnCu1+[delta]As2 (Ln = Y, La, Ce, Nd, Sm, Gd - Lu), LnAg1+[delta]As2 (Ln = La - Nd, Sm), and LnAuAs2 (Ln = Pr, Sm, Gd, Tb) adopt structures closely related to the HfCuSi2 type consisting of PbO-like layers of T and As atoms, square layers of As atoms and layers of Ln atoms separating the former two building units. All copper compounds of this series contain regular square nets of As atoms, whereas the respective nets in the silver and gold compounds are distorted. Two principally different patterns of distortion have been found: [As] zigzag chains in LnAgAs2 (Ln = Pr, Nd, Sm) and [As] cis-trans chains in LaAg1.01(1)As2, CeAgAs2, and PrAuAs2. Both patterns can undergo a further reduction of symmetry to end up with a pattern of As2 dumb-bells as can be seen in SmAuAs2, GdAuAs2, and TbAuAs2. Stoichiometric samples LnCuAs2 (Ln = Y, Pr, Nd, Sm, Gd, Tb, Dy, Er) have been used for measurements of the conductivity [rho], magnetic susceptibility [chi] and heat capacity cp. All investigated compounds exhibit metallic conductivity and, except for Y, order antiferromagnetically at temperatures below 10 K. In contrast to LnCuAs2 compounds, the silver compound CeAgAs2 shows semiconducting behavior throughout the temperature range from 4 to 350 K, whereas in PrAgAs2 metallic conductivity is preserved. The crystal structure of Sm2CuAs3O contains two different PbO-like layers formed either by Sm and O or Cu and As atoms. Both PbO-type layers are separated by sheets of Sm and distorted square nets of As atoms. The As atoms are arranged in planar zigzag chains, like those found in NdAgAs2. Sm2CuAs3O is thus the first quaternary rare-earth pnictide oxide with a distorted As net. The quaternary potassium rare-earth copper selenides KGd2CuSe4, KLn2Cu3Se5 (Ln = Ho, Er, Tm), and K2Ln4Cu4Se9 (Ln = Dy, Y) extend three series of previously described sulfide and selenide compounds. All three series adopt a three-dimensional tunnel structure built up by [LnSe6] octahedra and [CuSe4] tetrahedra. The K atoms reside in the tunnels with a bicapped trigonal prismatic coordination of eight Se atoms for KGd2CuSe4 and KLn2Cu3Se5 (Ln = Ho, Er, Tm), while for K2Ln4Cu4Se9 (Ln = Dy, Y), the K atoms are coordinated by seven Se atoms in monocappped trigonal prisms.

Die vorliegende Arbeit behandelt die Wechselwirkung von Verarbeitung und Gefüge Mn-Al basierter hartmagnetischer Werkstoffe sowie die Auswirkung des Gefüges auf deren Eigenschaften. Dabei wurde das Gefüge der metastabilen tau-Phase im Anschluss an die Phasenbildung aus der Hochtemperaturphase epsilon-MnAl und die Auswirkung einer anschließenden Umformung untersucht. Der Schwerpunkt der Arbeit lag in der Analyse der Evolution verschiedener Gefügebestandteile, wie Grenzflächenverteilung, Versetzungen und Korngröße unter Verwendung von Rasterelektronenmikroskopie und Elektronenrückstreubeugung. Die epsilon-tau Umwandlung kann auf 2 verschiedene Routen erfolgen. In beiden Fällen wird die Bildung von 3 kristallographisch unterschiedlichen zwillingsähnlichen Defekten beobachtet, die als wahre Zwillinge, Ordnungszwillinge und Pseudozwillinge bezeichnet werden. Sie lassen sich als Rotationen um einen kristallographischen {111}-Pol beschreiben. Der Anteil der Zwillingsdefekte nach der Umwandlung, aber auch die Korngröße und Versetzungsdichte sind von der gewählten Umwandlungsroute abhängig. Während die Sättigungspolarisation annähernd gleich ist, reagiert die Koerzitivfeldstärke sensitiv auf den Gefügezustand. Eine niedrige Korngröße und hohe Versetzungsdichte tragen zu ihrer Erhöhung bei. Eine anschließende Kaltumformung erzeugt ein vielfach verzwillingtes Verformungsgefüge mit hoher Koerzitivfeldstärke. Wärmebehandlungen und die Analyse der Schärfe von Kikuchi-Beugungsbildern haben gezeigt, dass nicht die hohe Zwillingsdichte, sondern primär Versetzungen im Verformungsgefüge die Koerzitivfeldstärke steigern. Warmumformung von tau-MnAl führt zur dynamischen Rekristallisation. Die Kinetik der Gefügeneubildung und die resultierende Korngröße sind stark von der Umformtemperatur abhängig. Durch Umformung lässt sich eine kristallographische Texturierung von tau-MnAl erreichen. Die Orientierung der magnetisch leichten [001]-Richtung ist dabei vom gewählten Umformverfahren und gegebenenfalls von der Nachbehandlung abhängig. Statische und dynamische Rekristallisation reduzieren den Anteil der Zwillingsdefekte signifikant und besonders Pseudozwillinge und Ordnungszwillinge werden im Gefüge beseitigt. Das Rekristallisationsgefüge weist gegenüber dem Umwandlungsgefüge einen geringeren Widerstand gegen die mit der Zersetzungsreaktion verbundene Bildung von beta-Mn auf. Die Ursache liegt in einer selektiven beta-Mn-Bildung an allgemeinen Korngrenzen, während die Zwillingsdefekte einen erhöhten Widerstand gegen sie Zersetzung aufweisen.

Die vorliegende Arbeit behandelt die Wechselwirkung von Verarbeitung und Gefüge Mn-Al basierter hartmagnetischer Werkstoffe sowie die Auswirkung des Gefüges auf deren Eigenschaften. Dabei wurde das Gefüge der metastabilen tau-Phase im Anschluss an die Phasenbildung aus der Hochtemperaturphase epsilon-MnAl und die Auswirkung einer anschließenden Umformung untersucht. Der Schwerpunkt der Arbeit lag in der Analyse der Evolution verschiedener Gefügebestandteile, wie Grenzflächenverteilung, Versetzungen und Korngröße unter Verwendung von Rasterelektronenmikroskopie und Elektronenrückstreubeugung. Die epsilon-tau Umwandlung kann auf 2 verschiedene Routen erfolgen. In beiden Fällen wird die Bildung von 3 kristallographisch unterschiedlichen zwillingsähnlichen Defekten beobachtet, die als wahre Zwillinge, Ordnungszwillinge und Pseudozwillinge bezeichnet werden. Sie lassen sich als Rotationen um einen kristallographischen {111}-Pol beschreiben. Der Anteil der Zwillingsdefekte nach der Umwandlung, aber auch die Korngröße und Versetzungsdichte sind von der gewählten Umwandlungsroute abhängig. Während die Sättigungspolarisation annähernd gleich ist, reagiert die Koerzitivfeldstärke sensitiv auf den Gefügezustand. Eine niedrige Korngröße und hohe Versetzungsdichte tragen zu ihrer Erhöhung bei. Eine anschließende Kaltumformung erzeugt ein vielfach verzwillingtes Verformungsgefüge mit hoher Koerzitivfeldstärke. Wärmebehandlungen und die Analyse der Schärfe von Kikuchi-Beugungsbildern haben gezeigt, dass nicht die hohe Zwillingsdichte, sondern primär Versetzungen im Verformungsgefüge die Koerzitivfeldstärke steigern. Warmumformung von tau-MnAl führt zur dynamischen Rekristallisation. Die Kinetik der Gefügeneubildung und die resultierende Korngröße sind stark von der Umformtemperatur abhängig. Durch Umformung lässt sich eine kristallographische Texturierung von tau-MnAl erreichen. Die Orientierung der magnetisch leichten [001]-Richtung ist dabei vom gewählten Umformverfahren und gegebenenfalls von der Nachbehandlung abhängig. Statische und dynamische Rekristallisation reduzieren den Anteil der Zwillingsdefekte signifikant und besonders Pseudozwillinge und Ordnungszwillinge werden im Gefüge beseitigt. Das Rekristallisationsgefüge weist gegenüber dem Umwandlungsgefüge einen geringeren Widerstand gegen die mit der Zersetzungsreaktion verbundene Bildung von beta-Mn auf. Die Ursache liegt in einer selektiven beta-Mn-Bildung an allgemeinen Korngrenzen, während die Zwillingsdefekte einen erhöhten Widerstand gegen sie Zersetzung aufweisen.

Im binären Mn-Ga-System wurde für Legierungen mit 55 at.% bis 65 at.% Mangan die Phasenbildung der L10-Phase mit Röntgenbeugung und Differenzialkalorimetrie untersucht. Nach der Herstellung der L10-Phase in allen Legierungen erfolgte eine Untersuchung der intrinsischen magnetischen Eigenschaften. Die Mn55Ga45-Legierung zeigte dabei die höchste Sättigungsmagnetisierung mit µ0Ms = 0,81 T. Für diese Legierung erfolgten deshalb Versuche zur Verbesserung der extrinsischen Eigenschaften. Dazu wurden Pulver gemahlen und die Möglichkeit der Ausrichtung im Magnetfeld untersucht. Dabei konnte ein Texturgrad von 0,45 für Pulver mit einer Partikelgröße kleiner 10 µm erreicht und die Koerzitivfeldstärke um das 7-fache gegenüber der Volumenprobe erhöht werden. Weiterhin konnten die Pulverproben durch Heißkompaktieren bei 400 °C erneut zu einer Volumenprobe gepresst werden. Die dabei erhaltene Probe besitzt eine Koerzitivfeldstärke von 0,16 T und eine leicht reduzierte Sättigungsmagnetisierung auf Grund einer Packungsdichte von 83 %. Im ternären Mn-Al-Ga-System wurden Proben der Sollzusammensetzung Mn55Al45-xGax mit 5,625 < x < 22,5 hergestellt. Für Legierungen mit x >= 11,86 erwies sich eine Wärmebehandlung bei 600°C für 24 Stunden als ausreichend die reine L10-Phase zu erzeugen. Bei den Legierungen mit einem geringeren Ga-Anteil war eine zweistufige Wärmebehandlung notwendig, um ausschließlich L10 zu erhalten. Nach der ersten Wärmebehandlung bei 1100 °C entstand ein Phasengemisch aus gamma2 und L10(epsilon). Letzteres wurde aus der epsilon-Hochtemperaturphase gebildet. Durch die anschließende Wärmebehandlung bei 500 °C für 24 Stunden konnte die verbleibende gamma2-Phase in L10(gamma2) umgewandelt werden. Untersuchungen der lokalen Legierungszusammensetzung ergaben einen geringeren Mn-Anteil der L10(gamma2)-Phase im Vergleich zu L10(epsilon). Die Unterschiede in den zwei L10-Phasen konnten weiterhin durch eine Reflexaufspaltung in den Röntgenbeugungsaufnahmen sowie der Existenz zweier Curie-Temperaturen bestätigt werden. Die gemessenen Sättigungsmagnetisierungen ergaben eine Superposition beider Phasen und einen maximalen Wert von µ0Ms = 0,85 T. Untersuchungen der thermischen Stabilität der L10-Phasen bei 700 °C zeigten, dass die L10(gamma2)-Phase thermisch stabil ist und sich die L10(epsilon)-Phase langsam in beta-Mn und gamma2 zersetzt. Bei der Zersetzung war im Vergleich zum binären Mn-Al-System eine starke Steigerung der thermischen Stabilität durch die Substitution geringer Mengen Galliums zu erkennen. Über die zersetzungsbedingte Reduktion der Magnetisierung konnten Abschätzungen der Zersetzungskinetik getroffen werden.

This thesis describes the syntheses, the crystal structures, and the physical properties of some new ternary and quaternary rare-earth coinage metal arsenides, selenides and oxides. All ternary compounds LnCu1+[delta]As2 (Ln = Y, La, Ce, Nd, Sm, Gd - Lu), LnAg1+[delta]As2 (Ln = La - Nd, Sm), and LnAuAs2 (Ln = Pr, Sm, Gd, Tb) adopt structures closely related to the HfCuSi2 type consisting of PbO-like layers of T and As atoms, square layers of As atoms and layers of Ln atoms separating the former two building units. All copper compounds of this series contain regular square nets of As atoms, whereas the respective nets in the silver and gold compounds are distorted. Two principally different patterns of distortion have been found: [As] zigzag chains in LnAgAs2 (Ln = Pr, Nd, Sm) and [As] cis-trans chains in LaAg1.01(1)As2, CeAgAs2, and PrAuAs2. Both patterns can undergo a further reduction of symmetry to end up with a pattern of As2 dumb-bells as can be seen in SmAuAs2, GdAuAs2, and TbAuAs2. Stoichiometric samples LnCuAs2 (Ln = Y, Pr, Nd, Sm, Gd, Tb, Dy, Er) have been used for measurements of the conductivity [rho], magnetic susceptibility [chi] and heat capacity cp. All investigated compounds exhibit metallic conductivity and, except for Y, order antiferromagnetically at temperatures below 10 K. In contrast to LnCuAs2 compounds, the silver compound CeAgAs2 shows semiconducting behavior throughout the temperature range from 4 to 350 K, whereas in PrAgAs2 metallic conductivity is preserved. The crystal structure of Sm2CuAs3O contains two different PbO-like layers formed either by Sm and O or Cu and As atoms. Both PbO-type layers are separated by sheets of Sm and distorted square nets of As atoms. The As atoms are arranged in planar zigzag chains, like those found in NdAgAs2. Sm2CuAs3O is thus the first quaternary rare-earth pnictide oxide with a distorted As net. The quaternary potassium rare-earth copper selenides KGd2CuSe4, KLn2Cu3Se5 (Ln = Ho, Er, Tm), and K2Ln4Cu4Se9 (Ln = Dy, Y) extend three series of previously described sulfide and selenide compounds. All three series adopt a three-dimensional tunnel structure built up by [LnSe6] octahedra and [CuSe4] tetrahedra. The K atoms reside in the tunnels with a bicapped trigonal prismatic coordination of eight Se atoms for KGd2CuSe4 and KLn2Cu3Se5 (Ln = Ho, Er, Tm), while for K2Ln4Cu4Se9 (Ln = Dy, Y), the K atoms are coordinated by seven Se atoms in monocappped trigonal prisms.