Made available in DSpace on 2016-12-08T17:19:39Z (GMT). No. of bitstreams: 1 Dissertacao Adilson - capa - p 20.pdf: 346950 bytes, checksum: a3100709576cd968b71593cb9c01e214 (MD5) Previous issue date: 2011-07-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study aims to evaluate the effect of incorporation of particles of fired clay brick waste (CBW) in the physical and mechanical properties and their relation to the microstructure of concrete with Portland cement. The mixtures were obtained using the technique of fractional factorial design 33-1 for the design and analysis of experiments. For each factor, three levels were selected: CBW content (10, 20 and 30 wt. % of cement), water-to-cement ratio of 0.37, 0.45 and 0.55, and aggregate-to-cement ratio of 2.36, 3.64 and 4.70. The waste was characterized to evaluate their potential as a pozzolana. Fresh properties (consistency) and hardened (compressive strength at various ages, voids index, water absorption and density) were measured. Characterizations of microstructure and thermal using SEM / EDS and DTA / TG were performed to correlate the effect of waste content on the microstructure and properties of the hardened concrete. The waste presents properties adequate to be used as a pozzolan material. Consistency index decreases with the incorporation of the CBW, but is still possible to obtain concrete with adequate workability. For properties in the hardened concrete, the results show that the compressive strength increases with the increase of CBW content as an addition for concretes of Portland cement. Microstructural characterization reveals that the waste contributes to develop a more homogeneous microstructure with fewer pores and cracks when compared to concretes without waste. There is evidences that metakaolin contained in the waste contributes with the hydration reactions, consuming calcium hydroxide and producing more calcium silicate gel and hydrated phases, which keeps the aggregates more cohesive in the concrete microstructure. These microstructural characteristics improve the mechanical properties and durability of concrete. / Este trabalho tem como objetivo avaliar o efeito da incorporação de rejeitos particulados de tijolos (RPT) nas propriedades físicas e mecânicas e sua relação com a microestrutura de concretos de cimento Portland. Os traços foram formulados utilizando a técnica de planejamento fatorial fracionado 33-1 para o projeto e análise de experimentos. Para cada fator, três níveis foram selecionados: teor de RTP incorporado (10, 20 e 30 % em relação ao cimento), relações água-cimento de 0,37, 0,45 e 0,55, e relações agregado-cimento de 2,36, 3,64 e 4,70. O rejeito foi caracterizado para avaliar seu potencial quanto à pozolanicidade. Propriedades no estado fresco (consistência) e endurecido (resistênca à compressão em várias idades, índice de vazios, absorção de água e densidade) foram medidas. Caracterizações de microestrutura e térmica usando MEV/EDS e ADT/TG foram realizadas para correlacionar o efeito do teor de rejeito na microestrutura e propriedades no concreto endurecido. O rejeito apresenta características que possibilitam seu uso como material pozolânico. Para o índice de consistência observa-se que o mesmo diminue com a incorporação do RPT, porém ainda é possíviel obter concretos com adequada trabalhabilidade. Para as propriedades no concreto endurecido, os resultados mostram que a resistência à compressão aumenta com o aumento da porcentagem de RPT em adição ao concreto de cimento Portland. A caracterização microestrutural revela que o rejeito contribui para desenvolver uma microestrutura mais homogênea, com menos trincas e poros, quando comparadas às misturas sem o rejeito. Há indícios de que a metacaulinita contida no rejeito participa das reações de hidratação, consumindo hidróxido de cálcio e produzindo mais silicato de cálcio gel e fases hidratadas, as quais contribuem para manter os agregados mais coesos no corpo cerâmico. Estas características microestruturais melhoram as propriedades mecânicas e durabilidade dos concretos.

Made available in DSpace on 2016-12-08T17:19:39Z (GMT). No. of bitstreams: 1 Resumo.pdf: 35261 bytes, checksum: 5c14dd5939481fe398edfb044903a091 (MD5) Previous issue date: 2011-07-26 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This paper presents a study on the linear thermal expansion of foundry sands used as aggregates in foundry cores with resin phenolic-urethane/Cold Box. The work examines the correlation between thermal expansion of the sand and hot deformation tendency of the core during the casting process. The hot deformation tendency has important technological significance, because it affects the dimensional quality of the casting. It was tested three silica sands, one chromite sand, two types of based aluminum silicates sands and two types of blended minerals. The sands were characterized for particle size distribution, loss on ignition, AFS clay content, density, permeability, pH, acid demand, specific surface area, coefficient of angularity, chemical analysis, XRD, shape and surface of the grains and linear thermal expansion. The dilatometer test was done with loose unbonded sands. The sand was placed into an alumina sample holder and inserted into the dilatometer. The hot deformation tendency of the core was performed with two tests: first, using an experimental iron casting and second a hot distortion laboratory test, in which the test specimen was subjected to heating by a flame. It was verified that the hot deformation tendency is directly correlated to the thermal expansion of the sand. The higher the thermal expansion of the sand used to make cores the more susceptible it is to hot deformation. / O presente trabalho apresenta um estudo sobre a influência da expansão térmica linear das areias de fundição utilizadas para a confecção de machos com resina fenólicauretânica/ Cold Box sobre a tendência à deformação a quente dos machos durante o processo de fundição das peças. A tendência à deformação a quente dos machos tem grande importância tecnológica, porque isto afeta diretamente a qualidade dimensional das peças fundidas. Foram ensaiadas três areias de sílica, uma areia de cromita, duas areias à base de silicato de alumínio, dois compostos de minerais. As areias foram caracterizadas quanto à distribuição granulométrica, perda ao fogo, teor de argila AFS, densidades solta e relativa, permeabilidade, pH, demanda ácida, superfície específica, coeficiente de angularidade, análise química, difratometria de raios-X, formato e superfície dos grãos e expansão térmica linear. O ensaio de dilatometria das areias foi realizado em corpos de provas não ligados com aglomerantes, ou seja, a areia foi acondicionada em um porta-amostra de alumina e este foi inserido no dilatômetro. Foram executados dois ensaios de tendência à deformação a quente dos machos: o ensaio de corpo de prova fundido e o ensaio de distorção a quente em laboratório, onde o corpo de prova (macho) é submetido a um aquecimento por chama. Verificou-se que a tendência à deformação a quente dos machos tem correlação direta com a expansão térmica da areia. Quanto maior a expansão térmica da areia utilizada para a confecção do macho mais suscetível ele estará à deformação a quente.

Made available in DSpace on 2014-12-17T14:08:46Z (GMT). No. of bitstreams: 1 LarissaCLA_DISSERT.pdf: 2411784 bytes, checksum: bc6175bf8ed881abf12e8c0d17d59264 (MD5) Previous issue date: 2011-07-04 / Biodiesel is an alternative fuel, renewable, biodegradable and nontoxic. The transesterification of vegetable oils or animal fat with alcohol is most common form of production of this fuel. The procedure for production of biodiesel occurs most commonly through the transesterification reaction in which catalysts are used to accelerate and increase their income and may be basic, acid or enzyme. The use of homogeneous catalysis requires specific conditions and purification steps of the reaction products (alkyl ester and glycerol) and removal of the catalyst at the end of the reaction. As an alternative to improve the yield of the transesterification reaction, minimize the cost of production is that many studies are being conducted with the application of heterogeneous catalysis. The use of nano-structured materials as catalysts in the production of biodiesel is a biofuel alternative for a similar to mineral diesel. Although slower, can esterify transesterified triglycerides and free fatty acids and suffer little influence of water, which may be present in the raw material. This study aimed at the synthesis, characterization and application of nano-structured materials as catalysts in the transesterification reaction of soybean oil to produce biodiesel by ethylic route. The type material containing SBA-15 mesoporous lanthanum embedded within rightly Si / La = 50 was used catalyst. Solid samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, nitrogen adsorption and desorption. For the transesterification process, we used a molar ratio of 20:1 alcohol and oil with 0.250 g of catalyst at 60?C and times of 6 hours of reaction. It was determined the content of ethyl esters by H-NMR analysis and gas chromatography. It was found that the variable of conversion obtained was 80%, showing a good catalytic activity LaSBA-15 in the transesterification of vegetable oils via ethylic route / O biodiesel ? um combust?vel alternativo, renov?vel, biodegrad?vel e n?o t?xico. A transesterifica??o dos ?leos vegetais ou gordura animal com ?lcool ? a forma mais usual de produ??o desse combust?vel. O procedimento de produ??o de biodiesel ocorre mais comumente atrav?s da rea??o de transesterifica??o, na qual se utiliza catalisadores para acelerar e aumentar seu rendimento, podendo ser b?sico, ?cido ou enzim?tico. O uso da cat?lise homog?nea requer condi??es e etapas espec?ficas de purifica??o dos produtos da rea??o (?ster alqu?licos e glicerol) e remo??o do catalisador ao t?rmino da rea??o. Como alternativa para melhorar o rendimento da rea??o de transesterifica??o, minimizar os custos com a produ??o ? que muitos estudos est?o sendo realizados com aplica??o de cat?lise heterog?nea. O uso de materiais nano-estruturados como catalisadores na produ??o de biodiesel ? uma alternativa para obter um biocombust?vel semelhante ao diesel mineral. Mesmo sendo mais lentos, conseguem transesterificar os triglicer?deos e esterificar os ?cidos graxos livres, al?m de sofrerem pouca influ?ncia da ?gua, que possa estar presente na mat?riaprima. Este trabalho teve como objetivo a s?ntese, caracteriza??o e aplica??o de materiais nano-estruturados como catalisadores na rea??o de transesterifica??o de ?leo de soja, para obten??o de biodiesel pela rota et?lica. O material do tipo SBA-15 contendo lant?nio incorporado na estrutura mesoporosa, com raz?o Si/La=50, foi utilizado como catalisador. As amostras s?lidas foram caracterizadas por difra??o de raios-X, an?lise termogravim?trica, espectroscopia na regi?o do infravermelho, adsor??o e dessor??o de nitrog?nio. Para o processo de transesterifica??o, utilizou-se uma raz?o molar entre ?lcool e ?leo de 20:1 com 0,250 g de catalisador, temperatura de 60?C e tempos de 6 horas de rea??o. Determinou-se o teor de ?steres et?licos pela an?lise de H-RMN e cromatografia a g?s. Foi verificado que a vari?vel de convers?o obtida foi de 80%, mostrando uma boa atividade catal?tica do LaSBA- 15 na transesterifica??o do ?leo de soja via rota et?lica

Made available in DSpace on 2014-12-17T14:08:46Z (GMT). No. of bitstreams: 1 PedroTPA_DISSERT.pdf: 2026522 bytes, checksum: 77beea38c42704a86dbc6a2648061f42 (MD5) Previous issue date: 2011-07-04 / Stimulation operations have with main objective restore or improve the productivity or injectivity rate in wells. Acidizing is one of the most important operations of well stimulation, consist in inject acid solutions in the formation under fracture formation pressure. Acidizing have like main purpose remove near wellbore damage, caused by drilling or workover operations, can be use in sandstones and in carbonate formations. A critical step in acidizing operation is the control of acid-formation reaction. The high kinetic rate of this reaction, promotes the consumed of the acid in region near well, causing that the acid treatment not achive the desired distance. In this way, the damage zone can not be bypassed. The main objective of this work was obtain stable systems resistant to the different conditions found in field application, evaluate the kinetic of calcite dissolution in microemulsion systems and simulate the injection of this systems by performing experiments in plugs. The systems were obtained from two non ionic surfactants, Unitol L90 and Renex 110, with sec-butanol and n-butanol like cosurfactants. The oily component of the microemlsion was xilene and kerosene. The acqueous component was a solution of HCl 15-26,1%. The results shown that the microemulsion systems obtained were stable to temperature until 100?C, high calcium concentrations, salinity until 35000 ppm and HCl concentrations until 25%. The time for calcite dissolution in microemulsion media was 14 times slower than in aqueous HCl 15%. The simulation in plugs showed that microemulsion systems promote a distributed flux and promoted longer channels. The permeability enhancement was between 177 - 890%. The results showed that the microemulsion systems obtained have potential to be applied in matrix acidizing / As opera??es de estimula??o s?o opera??es realizadas com a finalidade de restaurar ou melhorar o ?ndice de produ??o ou inje??o dos po?os. Dentre as opera??es de estimula??o, destaca-se a opera??o de acidifica??o, que consiste na inje??o de solu??es ?cidas na forma??o, com press?o abaixo da press?o de fratura da forma??o. A acidifica??o tem como principal objetivo remover danos causados nas etapas de perfura??o e/ou workover, podendo ser realizada tanto em arenitos quanto em carbonatos. Um dos pontos mais cr?ticos da opera??o de acidifica??o ? o controle da rea??o ?cido-rocha, pois a elevada velocidade da rea??o faz com que o ?cido seja todo consumido na regi?o pr?xima ao po?o, fazendo com que o tratamento ?cido n?o atinja a dist?ncia desejada. Dessa maneira, as regi?es com dano podem n?o ser ultrapassadas. Este trabalho teve como objetivo obter sistemas microemulsionados est?veis ?s diferentes condi??es encontradas no campo de aplica??o, avaliar a cin?tica de dissolu??o da calcita nesses sistemas, bem como, simular a inje??o desses sistemas realizando ensaios em plugues. Utilizaram-se sistemas microemulsionados obtidos a partir dos tensoativos Renex 110, Unitol L90 e o OMS (?leo de mamona saponificado). Foram utilizandos o sec-butanol e o n-butanol como cotensoativos. Como componentes org?nicos foram utilizados o xileno e o querosene e como componente aquoso foram utilizadas solu??es de HCl variando-se a concentra??o de 15-26,1%. Os resultados mostraram que os sistemas microemulsionados foram est?veis ? temperaturas de at? 100?C, ? concentra??es elevadas de c?lcio, ? salinidade de at? 35000 ppm e a concentra??es de HCl de at? 25%. A cin?tica de dissolu??o da calcita, ao utilizar os sistemas microemulsionados ?cidos, foi at? 14 vezes mais lenta quando comparada com a solu??o de HCl 15%. Os resultados da inje??o dos sistemas ?cidos mostraram que as microemuls?es favorecem um fluxo mais distribu?do com rela??o ao HCl 15%, bem como, formam canais mais longos, promovendo incrementos na permeabilidade dos plugues de 177 - 890%. Os resultados mostraram que os sistemas microemulsionados possuem potencial para aplica??o em opera??es de acidifica??o de po?os

Made available in DSpace on 2014-12-17T14:08:46Z (GMT). No. of bitstreams: 1 AllisonARS_DISSERT_Parcial.pdf: 268843 bytes, checksum: ccc10add424035b8ef9b1b3a87699d4f (MD5) Previous issue date: 2011-06-27 / With the increasing of demand for natural gas and the consequent growth of the pipeline networks, besides the importance of transport and transfer of oil products by pipeline, and when it comes to product quality and integrity of the pipeline there is an important role regarding to the monitoring internal corrosion of the pipe. This study aims to assess corrosion in three pipeline that operate with different products, using gravimetric techniques and electrical resistance. Chemical analysis of residues originated in the pipeline helps to identify the mechanism corrosive process. The internal monitoring of the corrosion in the pipelines was carried out between 2009 and 2010 using coupon weight loss and electrical resistance probe. Physico-chemical techniques of diffraction and fluorescence X-rays were used to characterize the products of corrosion of the pipelines. The corrosion rate by weight loss was analyzed for every pipeline, only those ones that has revealed corrosive attack were analyzed located corrosion rate. The corrosion potential was classified as low to pipeline gas and ranged from low to severe for oil pipelines and the pipeline derivatives. Corrosion products were identified as iron carbonate, iron oxide and iron sulfide / Com o aumento da demanda de g?s natural e consequente crescimento da malha dutovi?ria, al?m da import?ncia do transporte e transfer?ncia de petr?leo e derivados por dutos, e em se tratando da qualidade do produto e da integridade do duto h? um importante papel no que diz respeito ao monitoramento da corros?o interna da tubula??o. O objetivo deste trabalho ? avaliar a corros?o em 3 (tr?s) dutos que operam com diferentes produtos, utilizando t?cnicas gravim?trica e de resist?ncia el?trica. An?lises qu?micas dos res?duos gerados nos dutos ajudam a identificar o mecanismo do processo corrosivo. Monitoramento da corros?o interna em dutos foi realizado no per?odo de 2009 a 2010 utilizando cupom de perda de massa e sonda de resist?ncia el?trica. T?cnicas f?sico-qu?micas de difra??o e fluoresc?ncia de Raios-X foram utilizadas na caracteriza??o dos produtos de corros?o dos dutos. A taxa de corros?o por perda de massa foi analisada para todos os dutos, apenas aqueles que apresentaram ataque corrosivo localizado foram analisados a taxa de corros?o localizada. O potencial de corros?o foi classificado como baixo para duto de transporte de g?s e variou de baixo a severa para dutos de petr?leo e para o duto de derivado. Foram identificados produtos de corros?o como carbonato de ferro, ?xido de ferro e sulfeto de ferro / 2020-01-01

Made available in DSpace on 2014-12-17T14:08:46Z (GMT). No. of bitstreams: 1 AnelieseLF_DISSERT.pdf: 3198107 bytes, checksum: 808e93eb6952cb8e374d91afa53cabe1 (MD5) Previous issue date: 2011-07-01 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / This master thesis aims at developing a new methodology for thermochemical degradation of dry coconut fiber (dp = 0.25mm) using laboratory rotating cylinder reactor with the goal of producing bio-oil. The biomass was characterized by infrared spectroscopy with Fourier transform FTIR, thermogravimetric analysis TG, with evaluation of activation energy the in non-isothermal regime with heating rates of 5 and 10 ?C/min, differential themogravimetric analysis DTG, sweeping electron microscopy SEM, higher heating value - HHV, immediate analysis such as evaluated all the amounts of its main constituents, i.e., lignin, cellulose and hemicelluloses. In the process, it was evaluated: reaction temperature (450, 500 and 550oC), carrier gas flow rate (50 and 100 cm?/min) and spin speed (20 and 25 Hz) to condensate the bio-oil. The feed rate of biomass (540 g/h), the rotation of the rotating cylinder (33.7 rpm) and reaction time (30 33 min) were constant. The phases obtained from the process of pyrolysis of dry coconut fiber were bio-oil, char and the gas phase non-condensed. A macroscopic mass balance was applied based on the weight of each phase to evaluate their yield. The highest yield of 20% was obtained from the following conditions: temperature of 500oC, inert gas flow of 100 cm?/min and spin speed of 20 Hz. In that condition, the yield in char was 24.3%, non-condensable gas phase was 37.6% and losses of approximately 22.6%. The following physicochemical properties: density, viscosity, pH, higher heating value, char content, FTIR and CHN analysis were evaluated. The sample obtained in the best operational condition was subjected to a qualitative chromatographic analysis aiming to know the constituents of the produced bio-oil, which were: phenol followed by sirigol, acetovanilona and vinyl guaiacol. The solid phase (char) was characterized through an immediate analysis (evaluation of moisture, volatiles, ashes and fixed carbon), higher heating value and FTIR. The non-condensing gas phase presented as main constituents CO2, CO and H2. The results were compared to the ones mentioned by the literature. / O presente trabalho tem como objetivo o desenvolvimento de uma metodologia de degrada??o termoqu?mica da fibra do coco seco (dp = 0,25 mm) utilizando reator de cilindro rotativo em escala de laborat?rio, visando a produ??o de bio-?leo. A biomassa foi caracterizada por an?lise elementar (C, H, N), espectroscopia no infravermelho com transformada de Fourier - IVTF, an?lise termogravim?trica ATG, com avalia??o da energia de ativa??o no regime n?o isot?rmico com taxas de aquecimento de 5 e 10 oC/min, an?lise diferencial termogravim?trica - DTG, microscopia eletr?nica de varredura - MEV, poder calor?fico superior - PCS, an?lise imediata (avalia??o da umidade, materiais vol?teis, cinzas e carbono fixo) bem como avalia??o dos teores dos principais constituintes, ou seja, lignina, celulose e hemicelulose. No processo de pir?lise os seguintes par?metros foram estudados: temperatura da rea??o (450, 500 e 550 ?C), vaz?o do g?s de arraste (50 e 100 cm?/min) e velocidade de centrifuga??o para condensa??o do bio-?leo (20 e 25 Hz). O fluxo de alimenta??o da biomassa (540 g/h), a rota??o do cilindro rotativo (33,7 rpm) e o tempo de rea??o (30 33 min) foram mantidos constantes. Os produtos obtidos no processo da pir?lise da fibra do coco seco foram o bio-?leo, os finos de carv?o e a fase gasosa n?o condensada. Um balan?o de massa macrosc?pico aplicado tendo como base o peso de cada produto permitiu obter o rendimento dessas fases. O melhor rendimento de 18,1 % em bio-?leo foi obtido nas seguintes condi??es: temperatura de 500 ?C, vaz?o de g?s inerte 100 cm?/min e velocidade de centrifuga??o de 20 Hz. Nessas condi??es, o rendimento em finos de carv?o foi de 21,7 %, fase gasosa n?o condens?vel 37,6 % e perdas da ordem de 22,6 %. Algumas propriedades f?sicas do bio-?leo foram avaliadas, a saber, a densidade, viscosidade, pH, poder calor?fico superior, teor de finos de carv?o, an?lise por IVTF e CHN. A an?lise cromatogr?fica do bio-?leo mostrou que os principais constituintes de sua composi??o foram o fenol seguido do sirigol, aceto vanilona e vinil guaiacol. A fase s?lida (finos de carv?o) obtida foi caracterizada por an?lise imediata, poder calor?fico superior e IVTF. A fase gasosa n?o condensada apresentou como principais constituintes o CO2, CO e H2. Os resultados foram comparados com dados da literatura.

Made available in DSpace on 2014-12-17T14:08:46Z (GMT). No. of bitstreams: 1 LennedyCS_DISSERT.pdf: 3653783 bytes, checksum: 8a237d13a56a26f3a6ff1bf8c63bdede (MD5) Previous issue date: 2010-03-22 / The several existing methods for oil artificial lifting and the variety of automation equipment for these methods many times lead the supervisory systems to be dedicated to a unique method and/or to a unique manufacturer. To avoid this problem, it has been developed the supervisory system named SISAL, conceived to supervise wells with different lifting methods and different automation equipments. The SISAL system is working in several Brazilian states but, nowadays, it is only supervising rod pump-based wells. The objective of this work is the development of a supervision module to the plunger lift artificial lift method. The module will have the same characteristics of working with automation hardware of many manufacturers. The module will be integrated to the SISAL system, incorporating the capacity to supervise the plunger lift artificial lift method. / Os v?rios m?todos de eleva??o artificial de petr?leo e os diferentes equipamentos de automa??o existentes muitas vezes levam a que os sistemas supervis?rios sejam dedicados a um ?nico m?todo e/ou a um ?nico fabricante de equipamentos. Para contornar este problema, foi desenvolvido o sistema SISAL, capaz de supervisionar po?os com diferentes m?todos de eleva??o e equipamentos de automa??o. Atualmente, o SISAL est? em opera??o em diversos po?os em v?rios estados do Brasil, supervisionando po?os de bombeio mec?nico. O objetivo deste trabalho ? desenvolver um m?dulo de supervis?o para o m?todo de eleva??o artificial plunger lift, com as mesmas caracter?sticas de poder trabalhar com hardwares de automa??o de diferentes fabricantes. O m?dulo desenvolvido ser? integrado ao SISAL, de forma a incorporar ao sistema a capacidade de supervisionar este novo m?todo de eleva??o.

Made available in DSpace on 2014-12-17T14:08:47Z (GMT). No. of bitstreams: 1 MartinhoQAF_DISSERT.pdf: 3517855 bytes, checksum: e2d79876500fdde55b949a6a832b6ff0 (MD5) Previous issue date: 2011-05-27 / Water injection is the most widely used method for supplementary recovery in many oil fields due to various reasons, like the fact that water is an effective displacing agent of low viscosity oils, the water injection projects are relatively simple to establish and the water availability at a relatively low cost. For design of water injection projects is necessary to do reservoir studies in order to define the various parameters needed to increase the effectiveness of the method. For this kind of study can be used several mathematical models classified into two general categories: analytical or numerical. The present work aims to do a comparative analysis between the results presented by flow lines simulator and conventional finite differences simulator; both types of simulators are based on numerical methods designed to model light oil reservoirs subjected to water injection. Therefore, it was defined two reservoir models: the first one was a heterogeneous model whose petrophysical properties vary along the reservoir and the other one was created using average petrophysical properties obtained from the first model. Comparisons were done considering that the results of these two models were always in the same operational conditions. Then some rock and fluid parameters have been changed in both models and again the results were compared. From the factorial design, that was done to study the sensitivity analysis of reservoir parameters, a few cases were chosen to study the role of water injection rate and the vertical position of wells perforations in production forecast. It was observed that the results from the two simulators are quite similar in most of the cases; differences were found only in those cases where there was an increase in gas solubility ratio of the model. Thus, it was concluded that in flow simulation of reservoirs analogous of those now studied, mainly when the gas solubility ratio is low, the conventional finite differences simulator may be replaced by flow lines simulator the production forecast is compatible but the computational processing time is lower. / A inje??o de ?gua ? o m?todo de recupera??o suplementar mais difundido na maioria dos campos de petr?leo, devido a v?rios motivos, como o fato de a ?gua ser um eficiente agente deslocante de ?leos com baixa viscosidade associado ao fato de ser relativamente f?cil de injetar e de existir grande disponibilidade de ?gua a um custo relativamente baixo de se obter. Para o dimensionamento de um projeto de inje??o de ?gua ? necess?rio efetuar um estudo de reservat?rio com o objetivo de se definir os v?rios par?metros necess?rios para aumentar a efic?cia do m?todo. Para este estudo podem ser utilizados v?rios modelos matem?ticos classificados como anal?ticos ou num?ricos. Este trabalho tem como objetivo efetuar uma an?lise comparativa entre os resultados apresentados por um simulador de linhas de fluxo e um simulador convencional por diferen?a finita, que s?o dois tipos de simuladores de fluxo baseados em m?todos num?ricos, para um modelo de um reservat?rio de petr?leo leve submetido ? inje??o de ?gua. Para tanto foram montados dois modelos de reservat?rio, sendo um modelo heterog?neo e outro homog?neo contendo valores m?dios das propriedades de rocha do primeiro modelo. Foram realizadas compara??es dos resultados destes modelos considerando sempre as mesmas condi??es de opera??o. Em seguida foram alterados alguns par?metros de fluido e de rocha em ambos os modelos e efetuadas novamente compara??es de resultados. A partir do planejamento fatorial, realizado para a an?lise de sensibilidade dos par?metros de reservat?rio, foram escolhidos alguns casos para efetuar an?lise da varia??o dos par?metros operacionais escolhidos que foram a vaz?o de inje??o de ?gua e a localiza??o dos canhoneados. Observou-se que os resultados entre os simuladores s?o bastante similares na maioria dos casos estudados, tendo sido encontrado diverg?ncias apenas nos casos em que h? aumento na raz?o de solubilidade de g?s do modelo. Desta maneira foi conclu?do que o simulador convencional por diferen?as finitas pode ser substitu?do por um simulador por linhas de fluxo em reservat?rios semelhantes ao estudado, quando a raz?o de solubilidade possui valores baixos, sem preju?zo aos resultados de produ??o e com menores tempos de processamento computacional. / 2020-01-01

Made available in DSpace on 2014-12-17T14:08:47Z (GMT). No. of bitstreams: 1 LoivaLSB_DISSERT.pdf: 3990836 bytes, checksum: 3537e4304659ead550f1c758b72dbbce (MD5) Previous issue date: 2010-07-19 / Currently, the oil industry is the biggest cause of environmental pollution. The objective was to reduce the concentration of copper and chromium in the water produced by the oil industry. It was used as adsorbent natural sisal fiber Agave sp treated with nitric acid and sodium hydroxide. All vegetable fibers have physical and morphological properties that enablies the adsorption of pollutants. The basic composition of sisal is cellulose, hemicellulose and lignin. The features are typically found in the characterization of vegetable fibers, except the surface area that was practically zero. In the first stage of adsorption, it was evaluated the effect of temperature and time skeeking to optimize the execution of the factorial design. The results showed that the most feasible fiber was the one treated with acid in five hours (30?C). The second phase was a factorial design, using acid and five hours, this time was it determined in the first phase. The tests were conducted following the experimental design and the results were analyzed by statistical methods in order to optimize the main parameters that influence the process: pH, concentration (mol / L) and fiber mass/ metal solution volume. The volume / mass ratio factor showed significant interference in the adsorption process of chromium and copper. The results obtained after optimization showed that the highest percentages of extraction (98%) were obtained on the following operating conditions: pH: 5-6, Concentration: 100 ppm and mass/ volume: 1 gram of fiber/50mL solution. The results showed that the adsorption process was efficient to remove chromium and copper using sisal fibers, however, requiring further studies to optimize the process. / A ind?stria de petr?leo ? atualmente uma das principais causadoras da polui??o ambiental. O objetivo deste trabalho foi reduzir a concentra??o de cobre e cromo na ?gua produzida pela ind?stria petrol?fera. Foi usado como adsorvente a fibra de sisal natural, tratada com ?cido n?trico e hidr?xido de s?dio. Todas as fibras vegetais possuem caracter?sticas f?sicas e morfol?gicas que possibilitam a adsor??o de poluentes. A composi??o b?sica do sisal ? celulose, hemicelulose e lignina. As caracter?sticas encontradas na caracteriza??o s?o t?picas de fibras vegetais, com exce??o da ?rea superficial que foi praticamente zero. Na primeira fase da adsor??o foi realizado um estudo a temperatura (30?C, 45?C e 60?C) e tempo para otimizar a realiza??o do planejamento fatorial. Os resultados mostraram que a fibra mais vi?vel para o estudo ? a fibra tratada com ?cido ? 30?C durante 5 horas. A segunda fase foi a do planejamento fatorial, usando a fibra ?cida e o tempo de cinco horas determinado na primeira fase. Os ensaios foram efetuados seguindo o planejamento Fatorial 2 3. Os resultados obtidos foram analisados, atrav?s de m?todos estat?sticos, visando a otimiza??o dos principais par?metros que influenciam no processo: pH, concentra??o (mol/L) e rela??o massa de fibra (g)/ volume de solu??o (mL). Os resultados do planejamento descrevem, o fator concentra??o e o fator massa/volume apresentam interfer?ncia significativa no processo de adsor??o do cromo e cobre. Os resultados, ap?s a otimiza??o, demonstraram que os maiores percentuais de extra??o (98 %) foram obtidos nas seguintes condi??es operacionais: pH: 5-6, Concentra??o: 100 ppm e a rela??o massa /volume: 1grama de fibra/50mL de solu??o. Observou-se que o processo foi eficiente com rela??o ? adsor??o do cromo e cobre, contudo s?o necess?rios mais estudos para a otimiza??o do processo.

Made available in DSpace on 2014-12-17T14:08:51Z (GMT). No. of bitstreams: 1 LiaraTV_DISSERT.pdf: 1753803 bytes, checksum: 5e53187cb6e33e84a341ab8ca9fd48da (MD5) Previous issue date: 2011-12-22 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The objective of the thermal recovery is to heat the resevoir and the oil in it to increase its recovery. In the Potiguar river basin there are located several heavy oil reservoirs whose primary recovery energy provides us with a little oil flow, which makes these reservoirs great candidates for application of a method of recovery advanced of the oil, especially the thermal. The steam injection can occur on a cyclical or continuous manner. The continuous steam injection occurs through injection wells, which in its vicinity form a zone of steam that expands itself, having as a consequence the displace of the oil with viscosity and mobility improved towards the producing wells. Another possible mechanism of displacement of oil in reservoirs subjected to continuous injection of steam is the distillation of oil by steam, which at high temperatures; their lighter fractions can be vaporized by changing the composition of the oil produced, of the oil residual or to shatter in the amount of oil produced. In this context, this paper aims to study the influence of compositional models in the continuous injection of steam through in the analysis of some parameters such as flow injection steam and temperature of injection. Were made various leading comparative analysis taking the various models of fluid, varying from a good elementary, with 03 pseudocomponents to a modeling of fluids with increasing numbers of pseudocomponents. A commercial numerical simulator was used for the study from a homogeneous reservoir model with similar features to those found in northeastern Brazil. Some conclusions as the increasing of the simulation time with increasing number of pseudocomponents, the significant influence of flow injection on cumulative production of oil and little influence of the number of pseudocomponents in the flows and cumulative production of oil were found / O objetivo da recupera??o t?rmica ? aquecer o reservat?rio e o ?leo nele existente para aumentar a sua recupera??o. Na Bacia Potiguar existem v?rios reservat?rios de ?leos pesados cuja energia de recupera??o prim?ria nos fornece uma vaz?o de ?leo pequena, o que torna tais reservat?rios ?timos candidatos para aplica??o de um m?todo de recupera??o avan?ada de petr?leo, especialmente o t?rmico. A inje??o de vapor pode ocorrer de forma c?clica ou cont?nua. A inje??o de vapor cont?nua ocorre atrav?s de po?os injetores, pr?ximos aos quais se forma uma zona de vapor que se expande, tendo como conseq??ncia o deslocamento do ?leo com viscosidade e mobilidade melhoradas na dire??o dos po?os produtores. Outro mecanismo poss?vel de deslocamento do ?leo em reservat?rios submetidos ? inje??o cont?nua de vapor ? a destila??o do ?leo por vapor, o qual quando alcan?am altas temperaturas, suas fra??es mais leves podem ser vaporizadas alterando a composi??o do ?leo produzido, do ?leo residual ou impactar na quantidade de ?leo produzida. Nesse contexto, este trabalho objetiva estudar a influ?ncia de modelos composicionais na inje??o cont?nua de vapor atrav?s de uma an?lise de par?metros como vaz?o de inje??o de vapor e temperatura de inje??o. Foram realizadas diversas an?lises comparativas levando os diversos modelos de fluidos, variando de um bem elementar, com 03 pseudocomponentes at? modelagens de fluidos com n?meros crescentes de pseudocomponentes. Foi utilizado um simulador num?rico comercial para o estudo a partir de um modelo de reservat?rio homog?neo com caracter?sticas similares ?s encontradas no Nordeste brasileiro. Algumas conclus?es como o aumento do tempo de simula??o com o aumento do n?mero de pseudocomponentes, a influ?ncia significativa da vaz?o de inje??o na produ??o acumulada de ?leo e a pouca influ?ncia do n?mero de pseudocomponentes nas vaz?es e produ??o acumulada de ?leo foram constatadas