Propriedades tribomec?nicas de superf?cies de tit?nio carbonitretadas por plasmaRocha, Ricardo Cesar da Silva 02 March 2012 (has links)
Made available in DSpace on 2014-12-17T14:07:03Z (GMT). No. of bitstreams: 1
RicardoCSR_DISSERT.pdf: 2528884 bytes, checksum: 9966cb710cbaa37dcf31b5576ecca1d8 (MD5)
Previous issue date: 2012-03-02 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Interstitial compounds of titanium have been mainly studied due to the large range of
properties acquired when C, N, O and H atoms are added. In this work, surfaces of TiCxNy
were produced by thermochemical treatments assisted by plasma with different proportions of
Ar + N2 + CH4 gas mixture. The Ar gas flow was fixed in 4 sccm, varying only N2 and CH4
gas flows. During the thermochemical treatment, the plasma was monitored by Optical
Emission Spectroscopy (OES) for the investigation of the influence of active species. After
treatments, C and N concentration profile, crystalline and amorphous phases were analyzed
by Nuclear Reaction (NRA). Besides tribomechanical properties of the Ti surface were
studied through the nanohardness measurements and friction coefficient determination. The
worn areas were evaluated by profilometry and Scanning Electronic Microscope (SEM) in
order to verify the wear mechanism present in each material. It has been seen which the
properties like nanohardness and friction coefficient have strong relation with luminous
intensity of species of the plasma, suggesting a using of this characteristic as a parameter of
process / Compostos intersticiais de tit?nio t?m sido extensivamente estudados devido ? larga
faixa de propriedades adquiridas quando ?tomos de C, N, O e H s?o adicionados. Neste
trabalho, superf?cies de TiCxNy foram produzidas por tratamento termoqu?mico auxiliado por
plasma de diferentes misturas de N2 + Ar + CH4. Foi fixado o fluxo de Ar em 4 sccm
variando-se os fluxos de N2 e CH4. Durante o tratamento termoqu?mico, o plasma foi
monitorado por EEO para investiga??o da influ?ncia das esp?cies ativas. Ap?s o tratamento,
as superf?cies das amostras foram analisadas quanto ao perfil de concentra??o de C e N, fases
cristalinas e fases amorfas. Tamb?m foram analisadas suas propriedades tribomec?nicas
atrav?s da medida de nanodureza e da determina??o do coeficiente de atrito. As ?reas
desgastadas foram avaliadas por perfilometria e microscopia eletr?nica de varredura (MEV)
com o intuito de verificar os mecanismos de desgastes presentes em cada material. Verificouse
que propriedades como dureza e coeficiente de atrito variavam com a intensidade das
esp?cies, sugerindo o uso da mesma como par?metro de processos a plasma
|
12 |
An?lise da estabilidade gen?tica de c?lulas-tronco mesenquimais humanasCorn?lio, D?borah Afonso 13 April 2012 (has links)
Made available in DSpace on 2014-12-17T14:05:20Z (GMT). No. of bitstreams: 1
DeborahAC_TESE.pdf: 2567069 bytes, checksum: 17be3c292d241e19b0a9d1323613899f (MD5)
Previous issue date: 2012-04-13 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Human multipotent mesenchymal stromal cells (MSCs), also known as mesenchymal stem cells, have become an important and attractive therapeutic tool since they are easily isolated and cultured, have in vitro expansion potential, substantial plasticity and secrete bioactive molecules that exert trophic effects. The human umbilical cord as a cell source for cell therapy will help to avoid several ethical, political, religious and technical issues. One of the main issues with SC lines from different sources, mainly those of embryonic origin, is the possibility of chromosomal alterations and genomic instability during in vitro expansion. Cells isolated from one umbilical cord exhibited a rare balanced paracentric inversion, likely a cytogenetic constitutional alteration, karyotype: 46,XY,inv(3)(p13p25~26). Important genes related to cancer predisposition and others involved in DNA repair are located in 3p25~26. Titanium is an excellent biomaterial for bone-implant integration; however, the use can result in the generation of particulate debris that can accumulate in the tissues adjacent to the prosthesis, in the local bone marrow, in the lymph nodes, liver and spleen. Subsequently may elicit important biological responses that aren?t well studied. In this work, we have studied the genetic stability of MSC isolated from the umbilical cord vein during in vitro expansion, after the cryopreservation, and under different concentrations and time of exposition to titanium microparticles. Cells were isolated, in vitro expanded, demonstrated capacity for osteogenic, adipogenic and chondrogenic differentiation and were evaluated using flow cytometry, so they met the minimum requirements for characterization as MSCs. The cells were expanded under different concentrations and time of exposition to titanium microparticles. The genetic stability of MSCs was assessed by cytogenetic analysis, fluorescence in situ hybridization (FISH) and analysis of micronucleus and other nuclear alterations (CBMN). The cells were able to internalize the titanium microparticles, but MSCs preserve their morphology, differentiation capacity and surface marker expression profiles. Furthermore, there was an increase in the genomic instability after long time of in vitro expansion, and this instability was greater when cells were exposed to high doses of titanium microparticles that induced oxidative stress. It is necessary always assess the risks/ benefits of using titanium in tissue therapy involving MSCs, considering the biosafety of the use of bone regeneration using titanium and MSCs. Even without using titanium, it is important that the therapeutic use of such cells is based on analyzes that ensure quality, security and cellular stability, with the standardization of quality control programs appropriate. In conclusion, it is suggested that cytogenetic analysis, FISH analysis and the micronucleus and other nuclear alterations are carried out in CTMH before implanting in a patient / C?lulas mesenquimais estromais multipotentes, tamb?m conhecidas como c?lulas-tronco mesenquimais humanas (CTMH), s?o c?lulas multipotentes utilizadas em v?rias pesquisas de terapia celular, pois apresentam a capacidade de se diferenciar em m?ltiplas e diferentes linhagens, t?m grande capacidade de autorrenova??o e de expans?o in vitro, excelentes propriedades imunossupressoras e s?o capazes de secretar mol?culas bioativas que exercem efeitos tr?ficos. O cord?o umbilical ? uma fonte de CTMH cuja extra??o n?o necessita de um procedimento invasivo, al?m de n?o envolver controv?rsias ?ticas, pol?ticas e religiosas. Um dos problemas que envolvem linhagens de CTMH de diferentes fontes ? a possibilidade de ocorr?ncia de altera??es cromoss?micas e instabilidade gen?tica, que podem aparecer durante a expans?o in vitro. Al?m disso, as CTMH de um dos cord?es apresentaram uma altera??o cromoss?mica constitucional: invers?o parac?ntrica no bra?o curto do cromossomo 3, cari?tipo: 46,XY,inv(3)(p13p25~26). Em 3p25-26, est?o localizados v?rios genes de grande import?ncia biol?gica, como genes envolvidos com o reparo de DNA e outros respons?veis pelo desenvolvimento de tumores. O tit?nio ? um dos materiais mais utilizado para fabrica??o de implantes ortop?dicos e dent?rios, e ? considerado um excelente biomaterial, entretanto, as part?culas derivadas de pr?teses acumulam-se nos tecidos periprost?ticos e na medula ?ssea local, disseminam-se para linfonodos, f?gado e ba?o. As implica??es biol?gicas em longo prazo da dissemina??o sist?mica de part?culas de metais e seus efeitos cito e genot?xicos n?o est?o bem caracterizados. Neste trabalho investigamos a estabilidade gen?tica de CTMH isoladas da veia do cord?o umbilical durante a expans?o in vitro, ap?s a criopreserva??o, e em diferentes condi??es de cultivo, na presen?a e na aus?ncia de tit?nio, antes e ap?s o aparecimento de c?lulas senescentes no cultivo. As c?lulas foram isoladas, expandidas, diferenciadas em osteoblastos, adip?citos e condroblastos e analisadas com citometria de fluxo para comprovar que s?o c?lulas-tronco mesenquimais. As CTMH foram tratadas com diferentes doses/ tempo de exposi??o ? micropart?culas de tit?nio. A avalia??o da estabilidade gen?tica das CTMH foi realizada atrav?s da an?lise do cari?tipo, de hibrida??o in situ por fluoresc?ncia (FISH) e da an?lise do micron?cleo e outras altera??es nucleares (CBMN).
Ficou estabelecido que as CTMH foram capazes de internalizar as micropart?culas de tit?nio, mas as c?lulas mant?m sua capacidade de prolifera??o, diferencia??o e preservam os mesmos marcadores de membrana. Al?m disso, demonstrou-se que existe um aumento na instabilidade gen?tica com o decorrer do tempo de expans?o in vitro, e esta instabilidade foi maior na presen?a de grande concentra??o de micropart?culas de tit?nio que induzem estresse oxidativo. ? necess?rio sempre avaliar os riscos/ benef?cios da utiliza??o do tit?nio na terapia tecidual envolvendo CTMH, considerando a biosseguran?a da utiliza??o da regenera??o ?ssea guiada que utiliza CTMH e tit?nio. Mesmo n?o se utilizando o tit?nio, ? importante que o uso terap?utico de tais c?lulas seja baseado em an?lises que garantam a qualidade, seguran?a e estabilidade celular, com a padroniza??o de programas de controle de qualidade adequados. Como conclus?o, sugere-se que a an?lise citogen?tica, FISH e a an?lise do micron?cleo e outras altera??es nucleares sejam realizadas nas CTMH antes de implantar num paciente, sejam elas cultivadas por longo tempo ou n?o
|
13 |
Produ??o de estrutura com gradiente de porosidade a partir da sinteriza??o por plasma da mistura de p?s Ti-Nb-SnSilva, Hugo Fernandes Medeiros da 20 June 2014 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2015-12-02T22:57:03Z
No. of bitstreams: 1
HugoFernandesMedeirosDaSilva_DISSERT.pdf: 30197183 bytes, checksum: aff97f351eb1c274b3b803536423bba1 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2015-12-09T20:00:17Z (GMT) No. of bitstreams: 1
HugoFernandesMedeirosDaSilva_DISSERT.pdf: 30197183 bytes, checksum: aff97f351eb1c274b3b803536423bba1 (MD5) / Made available in DSpace on 2015-12-09T20:00:18Z (GMT). No. of bitstreams: 1
HugoFernandesMedeirosDaSilva_DISSERT.pdf: 30197183 bytes, checksum: aff97f351eb1c274b3b803536423bba1 (MD5)
Previous issue date: 2014-06-20 / Estruturas porosas est?o sendo amplamente investigadas para uso em implantes biom?dicos, com objetivo de integrar o implante de forma mec?nica e funcional no interior do tecido ?sseo. Al?m disso, esta estrutura tamb?m ? importante para que f?rmacos possam se armazenados podendo induzir e acelerar o processo de osseointegra??o. Com o intuito de investigar esse efeito, p?s met?licos de Ti, 35Nb e 4Sn foram sinterizados por plasma usando descarga por c?todo oco. As sinteriza??es foram realizadas em plasma de arg?nio, press?o fixada em 4 mbar e temperaturas de 500?C, 600?C e 700?C. Tamb?m foram sinterizadas amostras em forno ? resit?ncia el?trica ? 1200?C, afim de comparar a sinteriza??o a plasma com um met?do convencional. Verificou-se que amostras sinterizadas por plasma na configura??o de c?todo oco apresentaram gradiente de porosidade, enquanto as amostras sinterizadas em forno resistivo n?o apresentaram. Al?m disso, encontrou-se diferen?as na micro-estrutura onde obteve-se uma superfic?e mais porosa e o n?cleo mais denso, em diferentes temperaturas. Assim como per?l de percola??o de ?gua destilada, e a compara??o da composi??o qu?mica das camadas porosas das amostras tratadas por plasma foram os pricipais resultados obtidos. Diante dos resultados obtidos, pode-se concluir que essa estrutura ? particularmente importante para aplica??o na ?rea biom?dica tais como arcabou?os para libera??o de f?rmacos e implantes.
. / Porous structures are being widely investigated for use in biomedical implants, aiming to
mechanically integrate and functionally the implant inside the bone tissue. Moreover, this
structure is also important for drugs that can be stored and can induce and accelerate the
process of osseointegration. With the purpose to investigate this effect, Ti, Nb and Sn
metal powders, were sintered by plasma using a hollow cathode discharge. Sintering was
performed in argon plasma set at 4 mbar pressure and temperatures of 500 ? C, 600 ? C and
700 ? C. Samples were also sintered in the electrical resistance furnace at 1200 ? C in order
to compare plasma sintering with the conventional method. It was observed that plasma
samples sintered with the hollow cathode configuration showed a gradient in porosity,
while the samples sintered in the resistive furnace did not. Furthermore, differences in the
microstructure of the samples were found, were a surface with higher porosity and ales
porous core were obtained at different temperatures. The percolation profile of distilled
water and the chemical compositions of the porous layers of the plasma treated samples
were the main results obtained. Based on these results, we can conclude that this structure
is particularly important for application in the biomedical field such as scaffolds for drug
delivery and implants
|
14 |
Compara??o entre t?cnicas de nitreta??o em c?todo oco e gaiola cat?dica na deposi??o de TiNMedeiros, Thiago Victor Rodrigues de 20 November 2014 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-01-26T17:36:30Z
No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-01-27T21:54:39Z (GMT) No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5) / Made available in DSpace on 2016-01-27T21:54:39Z (GMT). No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5)
Previous issue date: 2014-11-20 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico - CNPq / A nitreta??o por plasma vem sendo utilizada nas aplica??es industriais e
tecnol?gicas em larga escala por apresentar uma melhora nas propriedades mec?nicas,
tribol?gicas, dentre outras. A fim de solucionar problemas decorrentes na nitreta??o
convencional, como por exemplo, os an?is de restri??o (efeito de borda), foram
desenvolvidos t?cnicas com catodos diferenciados. No presente trabalho, estudou-se
superf?cies de tit?nio comercialmente puro (Grau II), modificadas por tratamento de
nitreta??o a plasma atrav?s de diferentes configura??es de c?todos (catodo oco, gaiola
cat?dica com uma gaiola e gaiola cat?dica com duas gaiolas) variando a temperatura em
350, 400 e 430oC, com o objetivo de obter uma otimiza??o da superf?cie para aplica??es
tecnol?gicas, avaliando de forma geral qual o tratamento mostrou melhores resultados
no substrato. As amostras foram caracterizadas atrav?s das t?cnicas de ensaios de
Microscopia de For?a At?mica (AFM), Espectroscopia Raman, Microdureza, Difra??o
de Raios-X (DRX), al?m de uma an?lise macrosc?pica. Desta forma, puderam-se
avaliar propriedades do tratamento como rugosidade, topografia, presen?a de elementos
intersticiais, dureza, homogeneidade, uniformidade e espessura da camada nitretada.
Observou-se que todas as amostras expostas a nitreta??o foram modificadas em rela??o
? amostra padr?o (sem tratamento), logo, apresentando aumento da dureza superficial,
presen?a de TiN constatadas tanto por DRX como por Raman, e uma altera??o
significativa na rugosidade das amostras tratadas. Constatou-se que o tratamento em
c?todo oco, apesar de apresentar o menor valor de microdureza entre as amostras
tratadas, foi o que apresentou a menor rugosidade superficial, apesar de nessa
configura??o as amostras sofrerem uma agressividade f?sica maior do tratamento. / The plasma nitriding has been used in industrial and technological applications
for large-scale show an improvement in the mechanical, tribological, among others. In
order to solve problems arising in the conventional nitriding, for example, rings
constraint (edge effect) techniques have been developed with different cathodes. In this
work, we studied surfaces of commercially pure titanium (Grade II), modified by
plasma nitriding treatment through different settings cathodes (hollow cathode, cathodic
cage with a cage and cathodic cage with two cages) varying the temperature 350, 400
and 430oC, with the goal of obtaining a surface optimization for technological
applications, evaluating which treatment generally showed better results under the
substrate. The samples were characterized by the techniques of testing for Atomic Force
Microscopy (AFM), Raman spectroscopy, microhardness, X-ray diffraction (XRD), and
a macroscopic analysis. Thus, we were able to evaluate the processing properties, such
as roughness, topography, the presence of interstitial elements, hardness, homogeneity,
uniformity and thickness of the nitrided layer. It was observed that all samples were
exposed to nitriding modified relative to the control sample (no treatment) thus having
increased surface hardness, the presence of TiN observed by XRD as per both Raman
and a significant change in the roughness of the treated samples . It was found that
treatment in hollow cathode, despite having the lowest value of microhardness between
treated samples, was presented the lowest surface roughness, although this
configuration samples suffer greater physical aggressiveness of treatment
|
15 |
Influ?ncia da superf?cie do tit?nio nitretado a plasma em diferentes atmosferas na ativa??o de plaquetas sangu?neasVitoriano, Jussier de Oliveira 09 January 2015 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-01-26T19:01:21Z
No. of bitstreams: 1
JussierDeOliveiraVitoriano_DISSERT.pdf: 29322891 bytes, checksum: 0c0254774bc22cc8cdd1189f3829e271 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-01-28T21:34:07Z (GMT) No. of bitstreams: 1
JussierDeOliveiraVitoriano_DISSERT.pdf: 29322891 bytes, checksum: 0c0254774bc22cc8cdd1189f3829e271 (MD5) / Made available in DSpace on 2016-01-28T21:34:07Z (GMT). No. of bitstreams: 1
JussierDeOliveiraVitoriano_DISSERT.pdf: 29322891 bytes, checksum: 0c0254774bc22cc8cdd1189f3829e271 (MD5)
Previous issue date: 2015-01-09 / O presente trabalho teve como objetivo analisar a resposta biol?gica em superf?cies de tit?nio
modificadas por plasma de Ar+N2+H2. Discos de tit?nio grau II receberam diferentes tratamentos
de superf?cie com plasma de Ar+N2+H2, constituindo sete grupos experimentais incluindo
amostras apenas polidas utilizadas como padr?o. Antes e ap?s o tratamento as amostras foram
caracterizadas quanto ? topografia, estrutura cristalina e molhabilidade, usando microscopia
de for?a at?mica, difra??o de raios-X, espectroscopia Raman e ensaio da gota s?ssil,
respectivamente. Plasma sangu?neo rico em plaquetas (PRP) foi aplicado sobre as superf?cies
modificadas em placas de cultivo. Imagens obtidas por microscopia eletr?nica das plaquetas
aderidas foram analisadas a fim de verificar o comportamento das plaquetas nas diferentes
condi??es experimentais. Verificou-se que a adi??o de H2 na atmosfera do plasma resultou em
superf?cies mais rugosas, com picos arredondados. Essas superf?cies, ao contr?rio daquelas
tratadas com atmosfera de alta concentra??o de N2, s?o menos propensas ? agrega??o
plaquet?ria e, consequentemente, ? forma??o de trombos quando aplicadas em dispositivos
biom?dicos. / This study aimed to analyze the biological response of titanium surfaces modified by plasma Ar + N2
+ H2. Titanium disks grade II received different surface treatments Ar + N2 + H2 plasma, constituting
seven groups including only polished samples used as standard. Before and after treatment the samples
were evaluated in terms of topography, crystal structure and wettability, using atomic force
microscopy, X-ray diffraction, Raman spectroscopy and testing of the sessile drop, respectively. Rich
plasma (PRP) was applied to the surfaces modified in culture plates. Images obtained by scanning
electron microscopy of the adhered platelets were analyzed to verify the behavior of platelets in the
different experimental conditions. We verified that the adition of H2 on plasma atmosphere resulted in
more rough surfaces, with round tops. These surfaces, in contrast to that surfaces treated with high
concentration of N2, are less propense to platelet aggregation and, consequently, to the formation of
thrombus when applied in biomedical devices.
|
16 |
An?lise do potencial genot?xico da superf?cie de tit?nio modificada por plasmaTavares, Joana Cristina Medeiros 26 March 2008 (has links)
Made available in DSpace on 2014-12-17T15:18:07Z (GMT). No. of bitstreams: 1
JoanaCMT.pdf: 30865 bytes, checksum: 27f51c3cbcadb5a4ec7e07d9182ea1aa (MD5)
Previous issue date: 2008-03-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / O Tit?nio (Ti) ? atualmente o material mais utilizado para fabrica??o de implantes ortop?dicos e dentais. Altera??es na superf?cie de tit?nio comercial puro (TiCP) podem determinar a reposta funcional das c?lulas, sendo um fator cr?tico para o sucesso do implante. Entretanto, a genotoxicidade de superf?cies de tit?nio tem sido pouco estudada. Deste modo, o objetivo deste trabalho foi avaliar o potencial genot?xico de uma nova superf?cie de tit?nio porosa desenvolvida por plasma comparada com uma superf?cie somente polida. Para tanto, foram realizados os ensaios cometa, aberra??es cromoss?micas (CAs) e micron?cleo (MN), utilizando c?lulas CHO-K1 (c?lulas do ov?rio de hamster Chin?s). Nossos resultados revelaram que a superf?cie de tit?nio polida foi capaz de induzir um aumento significativo dos danos no DNA, no n?mero das CAs, na tetraploidia e na freq??ncia de micron?cleos comparada ao controle. A superf?cie tratada por plasma, n?o promoveu efeito genot?xico significativo para todos os ensaios realizados. Estes resultados sugerem que a nova superf?cie de tit?nio tratada por plasma pode ser um material biologicamente seguro para sua utiliza??o em implantes ou futura aplica??o na terapia de regenera??o ?ssea-guiada, ao menos no que se refere ? sua genotoxicidade
|
17 |
Avalia??o do crescimento ?sseo em implantes de tit?nio revestidos por plasma spraying com diferentes interfaces metal-filmeCunha, Alexandre 22 April 2008 (has links)
Made available in DSpace on 2015-04-14T13:58:25Z (GMT). No. of bitstreams: 1
400633.pdf: 244771 bytes, checksum: 929e01919e85f7195f849c8c0c09bddc (MD5)
Previous issue date: 2008-04-22 / Tit?nio e suas ligas s?o amplamente aplicados como materiais de implantes ortop?dicos e odontol?gicos devido a sua excelente biocompatibilidade, baixo m?dulo de elasticidade e alta resist?ncia ao desgaste e ? corros?o. Os fatores que influenciam decisivamente a adequada funcionalidade de um biomaterial s?o o crescimento do tecido ?sseo e a sua ades?o ? superf?cie do implante. Pesquisas recentes indicam que o processo de ades?o entre o implante e o tecido vivo depende da rugosidade superficial, devido ? modifica??o da sua superf?cie, e do crescimento ?sseo nesta regi?o. Essas modifica??es s?o alcan?adas principalmente com a deposi??o de revestimentos porosos por aspers?o t?rmica, a aplica??o de jateamentos com particulados cer?micos, ataques ?cidos e eletroqu?micos, entre outros. O objetivo espec?fico desta pesquisa ? estimar a osseointegra??o de filmes porosos de tit?nio em contato com a cortical ?ssea de ovinos, bem como avaliar o comportamento do processo de osseocondu??o desses filmes. O segundo objetivo ? avaliar a ades?o destes filmes porosos de tit?nio depositados sobre superf?cies modificadas de discos de tit?nio. As t?cnicas de fluoresc?ncia de raios X e espectroscopia por energia dispersiva de raios X foram aplicadas para verificar a composi??o qu?mica dos implantes, filme de tit?nio e implantes osseointegrados. A Microscopia Eletr?nica de Varredura foi usada para caracterizar a morfologia dos discos de Ti, filme de tit?nio e a interface tecido ?sseo/filme de tit?nio/metal-base. Testes de tra??o foram aplicados para avaliar a osseointegra??o dos filmes de tit?nio e a ades?o destes aos discos. Os valores de tens?o de ruptura estimados para os filmes de tit?nio s?o superiores aos verificados em discos sem revestimento poroso de tit?nio (RENZ, 2007), principalmente no per?odo de 30 dias p?s-operat?rio. Os filmes de tit?nio atacados com ?cido fluor?drico apresentaram os maiores valores de tens?o de ruptura da interface osso-filme quando comparados aos filmes somente depositados, indicando aumento da osseointegra??o. Os valores de ades?o dos filmes de tit?nio para as superf?cies modificadas s?o maiores que os valores de ades?o na superf?cie somente usinada.
|
18 |
Avalia??o da osseointegra??o de implantes de tit?nio submetidos a diferentes tratamentos de superf?ciesRenz, Renata Pedrolli 14 December 2008 (has links)
Made available in DSpace on 2015-04-14T13:58:27Z (GMT). No. of bitstreams: 1
402797.pdf: 6535759 bytes, checksum: d71c96f436ffa7b29f0ee38a5038a7f7 (MD5)
Previous issue date: 2008-12-14 / O processo de osseointegra??o est? fortemente ligado com as propriedades f?sicoqu?micas superficiais dos materiais utilizados em implantes. Pesquisas recentes indicam que o desenvolvimento de superf?cies texturizadas aumenta a efici?ncia deste processo, influenciando diretamente na resposta inicial das c?lulas na interface osso/implante, na taxa e na qualidade da forma??o do tecido ?sseo formado. Por?m, n?o foi verificada a melhor rela??o entre os diversos tipos de tratamentos de superf?cies e a ades?o ?ssea ao implante. O objetivo deste trabalho foi avaliar a osseointegra??o in vivo de implantes de tit?nio cil?ndricos, submetidos a diferentes tratamentos de superf?cie, atrav?s de ensaio mec?nico do tipo pull out, de acordo com a norma ASTM C 633. A morfologia superficial dos implantes foi caracterizada pelas t?cnicas de MEV e rugosimetria. A composi??o qu?mica foi avaliada pelas t?cnicas de EDS e XRF, de acordo com a norma NBR ISO 5832-2, enquanto que, para avaliar a resist?ncia ? corros?o, foi utilizada a t?cnica de Polariza??o Linear, segundo as recomenda??es da ASTM F 746. Os resultados indicaram que a composi??o qu?mica dos grupos de amostras, com exce??o do escovado, atende aos limites estipulados quanto ao teor de contaminantes presentes. Os valores de densidade de corrente indicam comportamento de passiva??o, significativamente abaixo do valor m?ximo permitido pela norma. Os testes de pull out mostraram que 30 dias de cicatriza??o foram insuficientes para se obter crescimento ?sseo satisfat?rio. De modo geral, pode-se dizer que os resultados obtidos para o grupo de 60 dias indicaram que os valores de rugosidade superficial influenciaram os valores de tens?o m?xima.
|
19 |
Produ??o e caracteriza??o de implantes nanotexturizados de tit?nio associado a libera??o gradual de f?rmacosVeleda, Paula Pr? 30 August 2012 (has links)
Made available in DSpace on 2015-04-14T13:58:55Z (GMT). No. of bitstreams: 1
443419.pdf: 4259691 bytes, checksum: 3fbe554be4dac8a49f70f55d940079dd (MD5)
Previous issue date: 2012-08-30 / The aim of this study was to assess, in vivo, the effect of two different surface treatments of titanium implants - plasma-spray (PSA) and nano-textured plasma-spray (PSA-nano) - at the bone-to-implant interface (osseointegration), associated or not to the recombinant human growth hormone (rhGH). Twenty-four prototypes of pure titanium implants, 6-mm long and 2-mm wide, were especially fabricated in a cylindrical shape and placed in 12 New Zealand rabbit s tibiae. The implants were divided into four groups: 1) PSA implants without rhGH, 2) PSA implants with rhGH, 3) PSA-nano implants without rhGH and, lastly, 4) PSA-nano implants with rhGH. The animals were sacrificed 14 and 42 after the surgeries. Samples were collected and analysed by optical microscopy (OM), scanning electronic microscopy (SEM) and infrared microscopy (μ-FTIR), besides the pull-out mechanical test. The results showed that in the early stage of osseointegration, the recombinant human growth hormone has favored new bone formation, regardless the surface treatment. Howev-er, in the later stage, the nano-textured surface, even without the hormone, has made a positive influence on the new bone formation, when compared to its use with hormone. In this stage, only the plasma-spray surface (PSA) has been favored by the growth hormone / O objetivo deste trabalho foi avaliar, in vivo, o efeito de dois diferentes trata-mentos de superf?cie de implantes de tit?nio - plasma-spray (PSA) e plasma-spray nanotexturizado (PSA-nano) - na interface osso-implante (osseointegra??o), associ-ados ou n?o ao horm?nio do crescimento humano recombinante (rhGH). Vinte e quatro prot?tipos de implantes de tit?nio puro, medindo 6 mm de comprimento por 2 mm de di?metro, foram especialmente confeccionados em uma forma cil?ndrica e colocados na t?bia de 12 coelhos da ra?a New Zealand. Os implantes foram dividi-dos em quatro grupos: 1) implantes PSA sem rhGH, 2) implantes PSA com rhGH, 3) implantes PSA-nano sem rhGH e, por ?ltimo, 4) implantes PSA-nano com rhGH. Os animais foram sacrificados 14 e 42 dias ap?s as cirurgias. As amostras foram cole-tadas e analisadas por microscopia ?ptica (MO), microscopia eletr?nica de varredura (MEV) e microscopia de infravermelho (μ-FTIR), al?m do teste mec?nico de pull-out. Os resultados mostraram que no est?gio inicial da cicatriza??o, o horm?nio do cres-cimento recombinante humano favoreceu a neoforma??o ?ssea, independente do tipo de superf?cie. Por?m, no est?gio tardio, a nanotexturiza??o, sem a presen?a do horm?nio, exerceu uma influ?ncia positiva na neoforma??o ?ssea, quando compa-rada ao seu emprego com o horm?nio. Neste est?gio, apenas a superf?cie de plas-ma-spray (PSA) foi favorecida pelo horm?nio do crescimento
|
20 |
Aplica??o de filmes finos de tit?nio em componentes acetabulares de uhmwpe para prote??o contra oxida??o devido a exposi??o ? radia??o XVasconcellos, Let?cia Ara?jo 17 July 2006 (has links)
Made available in DSpace on 2015-04-14T13:59:17Z (GMT). No. of bitstreams: 1
383160.pdf: 3194550 bytes, checksum: cc6dcfdfc93d7782e5f949d40152d488 (MD5)
Previous issue date: 2006-07-17 / Os implantes de quadril s?o constitu?dos de uma cabe?a esf?rica met?lica que e. g., ? de a?o inoxid?vel 316-L ou ligas de Cr-Co, al?m de um componente polim?rico (UHMWPE). A aplica??o da radia??o gama usada no processo de esteriliza??o e dos raios X de diagn?stico utilizados no controle cl?nico da pr?tese podem contribuir na degrada??o prematura da superf?cie do UHMWPE resultando numa diminui??o do seu tempo de vida ?til. Neste trabalho, foi estudado o grau de prote??o de revestimentos tipo filme fino de tit?nio sobre o componente polim?rico (UHMWPE) em fun??o da exposi??o aos raios X de diagn?stico, comparando-os com os pol?meros n?o revestidos que tamb?m foram expostos ao mesmo tipo de radia??o. Parte destas amostras foram submersas em uma solu??o de HBSS (Hank s Balanced Salt Solution), a qual ? freq?entemente utilizada em culturas de c?lulas, pois simula o meio fisiol?gico do organismo humano. As amostras foram analisadas por diversas t?cnicas de caracteriza??o, dentre elas, a t?cnica de nanodureza para uma an?lise das propriedades mec?nicas do pol?mero, microscopia eletr?nica de varredura (MEV) para observa??o da qualidade superficial do UHMWPE e infravermelho por transformada de Fourier (FTIR) para avalia??o das modifica??es na composi??o qu?mica do pol?mero. Ap?s serem irradiadas, as amostras utilizadas na primeira parte do trabalho, os resultados dos testes de nanodureza levaram a concluir que as propriedades mec?nicas do UHMWPE variam de lote para lote. As an?lises de MEV indicaram dois fatos claros: primeiramente que as amostras revestidas apresentavam uma qualidade superficial com menos danos que as amostras revestidas em concord?ncia com as an?lises de nanodureza e FTIR. Desta forma, com base nos resultados obtidos, podemos concluir que nossa hip?tese inicial, de que uma fina camada de tit?nio pode diminuir a oxida??o superficial do UHMWPE, ? verdadeira.
|