The current study aimed to evaluate the effect of irrigating and chelating solutions on bond strength of fiber glass posts cemented with RelyX U200. 60 single-rooted premolars were sectioned at 14 mm from the apex, prepared with ProTaper Universal system until F3 instrument and filled with F3 master cone and AH Plus sealer. Root canal filling was partially removed, remaining 4 mm of guta-percha at the apical third. Specimens were randomly divided into 5 experimental groups (n=12), according to the solution used before fiber post cementation (dentin surface treatment), as described: EDTA 17% (EDTA); QMix (QM); SmearClear (SC); NaOCl 2.5% (NaOCl) and saline solution as control group (SS). Ultrasonic activation was performed three times, during 20 seconds each and root canals were dried with paper points. Exacto N2 glass fiber posts were cemented with RelyX U200. Rhodamine B dye was mixed to RelyX U200 in one specimen per group, in order to provide fluorescence for confocal laser scanning microscopy (CLSM) assessment. A cutting machine was used for root s sectioning, providing 3 slices, one for each root third. Next, push-out test was performed. Stereomicroscope and CLSM were used to analyze the failure mode and to illustrate the pattern of distribution of RelyX U200 inside dentinal tubules, respectively. Bond strength mean were calculated and ANOVA and Bonferroni tests were used for statistical analysis. SS showed the higher mean of bond strength values, superior to QM, SC (P < .05). NaOCl presented intermediary bond strength values, similar to EDTA and SS (P > .05). QM and SC showed the lowest mean of bond strength (P < .05). In conclusion, SS and NaOCl associated to ultrasonic activation seems to be adequate solutions for root canal cleaning before fiber post cementation with RelyX U200, while chelating solutions, such as EDTA, QMix and SmearClear, should not be used for dentin pre-treatment when cementing with RelyX U200. / O presente estudo tem por objetivo avaliar o efeito de diferentes soluções irrigantes e quelantes na resistência adesiva de pinos de fibra de vidro cimentados com cimento autoadesivo RelyX U200. 60 pré-molares inferiores extraídos de humanos, padronizados em 14 mm, foram preparados com o sistema ProTaper Universal até o instrumento F3, obturados com cimento AH Plus e cones F3 do mesmo sistema. Os espécimes foram desobturados parcialmente, restando 4 mm apicais de material obturador e realocados em quatro grupos experimentais e um controle (n=12), de acordo com a solução de tratamento de superfície dentinária prévia à cimentação dos pinos: EDTA 17% (EDTA), QMix (QM), SmearClear (SC), Soro Fisiológico (SS) e NaOCl 2,5% (NaOCl). As soluções foram ativadas por ultrassom em três etapas, durante 20 segundos cada e os canais foram secos com pontas de papel absorventes. Os pinos de fibra de vidro do Sistema Exacto Translúcido N2 foram cimentados com RelyX U200. Em um espécime por grupo foi incorporada Rodamina B ao cimento autoadesivo como marcador fluorescente para análise em Microscopia Confocal à laser (MECL). Foram seccionados 3slices por espécime, sendo 1 slice por terço radicular, e submetidos ao teste de push-out na máquina de ensaio universal EMIC. Estereomicroscópio e MECL foram utilizados para analisar o padrão de falha dos espécimes e o padrão de penetração do cimento autoadesivo nos túbulos dentinários, respectivamente. A média de resistência adesiva de cada espécime foi calculada. Testes ANOVA e Bonferroni foram utilizados para analisar as diferenças entre os grupos. SS demonstrou a maior média de resistência adesiva, sendo superior aos grupos QM, SC (P <.05). NaOCl apresentou valores intermediários de resistência adesiva, similares ao EDTA e SS (P > .05). QM e SC apresentaram as menores médias de resistência adesiva (P < .05). Pode-se concluir que o uso de SS e NaOCl parece ser adequado para lavagem do canal prévia à cimentação de pinos de fibra de vidro, com uso de cimento resinoso autoadesivo RelyX U200. O uso de soluções quelantes como EDTA, QM e SC parece interferir negativamente nos valores de resistência adesiva.

Orientador: Josimeri Hebling / Banca: Mário Alexandre Coelho Sinhoreti / Banca: Regina Maria Pupin-Rontani / Banca: Luiz Geraldo Vaz / Banca: Elisa Maria Aparecida Giro / Resumo: A influência de diferentes métodos de remoção da dentina artificialmente cariada sobre a resistência de união de um sistema adesivo convencional simplificado e de um autocondicionante foi avaliada por meio de ensaio mecânico de microtração. Trinta e dois terceiros molares humanos foram aleatoriamente distribuídos em 8 grupos experimentais, de acordo com o tipo de material (sistema adesivo) e o substrato dentinário. O grupo controle para cada sistema adesivo foi representado por sua aplicação sobre a dentina hígida. Foram avaliados os sistemas adesivos Adper Single Bond (SB) e Clearfil SE Bond (CSE), e quatro tipos de substrato dentinário: a) hígido e afetado por cárie após diferentes métodos de remoção de tecido infectado, b) método mecânico manual; c) método mecânico rotatório; e d) método químicomecânico representado pelo Carisolv™. Superfícies planas de dentina foram submetidas ao desenvolvimento artificial de cárie pela exposição a Streptococcus mutans. Os sistemas adesivos foram aplicados sobre a superfície dentinária resultante após a utilização dos diferentes métodos para remoção da cárie artificial ou sobre a dentina hígida, recebendo em seguida restauração de resina composta Z250. Os dentes restaurados foram mantidos por 24 horas à 37º C, seccionados em forma de "palitos", com área de superfície aderida medindo aproximadamente 0,49mm2 e submetidos ao ensaio mecânico de microtração. Quando os sistemas adesivos foram aplicados em dentina hígida, ambos resultaram em resistência de união não diferente entre si e superior à observada para os grupos onde tinham sido aplicados em dentina cariada, independente do método de remoção de tecido cariado utilizado. Para CSE, a remoção com cureta resultou nos menores valores de resistência de união, estatisticamente inferior aos demais grupos onde foi utilizado. A resistência de... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The purpose of this investigation was to evaluate the influence of different removal methods of artificially carious dentin on the bond strength of a one-step etch and rinse and a two-step self-etching primer bonding agent to caries-affected dentin. Thirty-two human third molars were randomly distributed into 8 groups, according to the bonding agent and the dentin substrartes. The control group was represented by the application of the bonding agents to sound dentin. The bonding agents evaluated were, Adper Single Bond (SB) and Clearfil SE Bond (CSE) and the dentin substrates were: a) sound dentin; b) dentin resulting from hand excavation, c) bur excavation and d) Carisolv™ gel excavation of the carious tissue. Flat dentin surfaces were submitted to an in vitro cariogenic bacterial model to create caries-like lesions. After caries removal, the bonding agents were applied on the caries-affected dentin according to the manufacturers' directions. Composite build-ups were constructed and the teeth were stored in water at 37°C for 24 hrs. Then they were sectioned in the x-y directions to produce beams with a crosssectional area of 0.49 mm2. The specimens were subjected to the microtensile test at a cross-head speed of 0.5 mm/min until failure. For both dentin bonding agents, the highest bond strength was produced in sound dentin when compared to caries159 affected dentin, irrespective of the method of caries removal. For CSE, caries removal using spoon excavators produced the lowest bond strengths (p<0.05) while the adhesive performance of SB was not affected by the caries removal method, although a trend towards lower values was observed when Carisolv was used. For all groups, the predominant mode of failure was adhesive. In conclusion, for both dentin bonding agents evaluated, bond strength to caries-affected dentin was significantly lower than to sound dentin. Caries removal using spoon... (Complete abstract, click electronic address below). / Doutor

O objetivo deste estudo foi avaliar a influência do tipo de sistema de cimentação (condicionamento ácido total ou autoadesivo), do modo de ativação (autoativado ou dual), do terço do conduto radicular (cervical, médio ou apical) e da espessura do filme de cimento sobre a resistência de união de pinos de fibra de vidro cimentados em dentes humanos. Quarenta raízes foram incluídas em resina epóxi, submetidas a tratamento endodôntico e obturadas com guta percha e cimento endodôntico sem eugenol. Decorridos sete dias, os condutos foram preparados a uma profundidade de 10mm com brocas padronizadas do sistema dos pinos de fibra (WhitePost DC #2) e aleatoriamente divididos em 4 grupos, conforme o sistema de cimentação e o modo de ativação: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (condicionamento ácido total), ativação dual, (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, autoativado, (G3) RelyX U100 (autoadesivo), dual e (G4) RelyX U100, autoativado. Após uma semana, cada raiz foi seccionada em máquina de corte, originando 6 fatias de 1 mm de espessura (n=60). Antes do ensaio de push-out cada fatia foi fotografada em ambas as faces, para determinação do raio dos pinos e da espessura do filme de cimento. Após o ensaio mecânico, novas imagens foram capturadas para determinação do modo de falha. Para automatizar a determinação da espessura de cimento, foi desenvolvida uma macro no software KS 400. Os dados foram estatisticamente analisados com ANOVA 3 fatores (resistência de união) e teste de Kruskall-Wallis (espessura do cimento). Comparações múltiplas foram realizadas com o teste Student-Newman-Keuls. Análise de regressão, modelo linear, foi empregada para verificar a correlação entre espessura do cimento e resistência de união. Todos os testes foram aplicados com &#945; = 0,05. O fator cimento exerceu influência significativa para a resistência de união (p = 0,0402): o RelyX U100 apresentou a maior média. A ativação dual elevou os valores de resistência de união em comparação ao modo quimicamente ativado (p < 0,0001). Houve diferenças significantes entre os grupos, sendo G1 (22,4 4,0 MPa) > G3 (20,4 3,6 MPa) > G4 (17,8 5,2 MPa) > G2 (13,5 4,3 MPa). O terço do conduto não exerceu influência significativa sobre a resistência adesiva (p = 0,4749). As espessuras dos filmes de cimento foram estatisticamente diferentes nos diferentes terços: cervical (102 45 m) > médio (75 29 m) > apical (52 28m). Não foi observada forte correlação entre os valores de espessura e os de resistência ao push-out (r = - 0,2016, p = 0,0033). O tipo de falha predominante foi a mista, exceto para o G2, que apresentou 74% das falhas na interface cimento-pino. Dessa forma, o cimento autoadesivo apresentou melhor desempenho que o convencional, e ambos os sistemas duais, sobretudo o RelyX ARC, apresentaram dependência da fotoativação para atingirem maiores valores de resistência de união. / The aim of this study was to evaluate the influence of adhesive cementation system approach (total-etch or self-adhesive), activation mode (self-cure or dual-cure), canal third (cervical, middle or apical) and cement thickness on push-out bond strength of glass fiber post bonded on human roots. Forty roots were embebed in epoxy resin and endodontically treated (filled with guta percha and non-eugenol endodontic sealer). Following 7 days, the post spaces were prepared with low-speed post drills provided by the manufacturer (WhitePost DC #2, FGM) at a depth of 10 mm and the roots were randomly divided in 4 groups, according to cementation system and activations mode: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (total-etch), dual-cure (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, self-cure, (G3) RelyX U100 (self-adhesive), dual-cure and (G4) RelyX U100, self-cure. After 7 days, each root was sectioned with water-cooled diamond blade, generating six 1-mm thickness slices (n=60). Before push-out bond strength test, digital images of both sides of the slices were captured with digital camera, in order to measure the post radius and the cement thickness. After mechanical test, new images were captured to evaluate the failure mode. A macro was developed in KS 400 software to speed and standardize the evaluation of cement thickness. Results were analyzed using three-way ANOVA (push-out) and Kruskall-Wallis test (cement thickness). Post-hoc multiple comparisons were performed using the Student-Newman-Keuls test. The correlation between resin cement thickness and bond strength was evaluated with regression analysis, linear model. All tests were performed with significance level set at 0.05. Push-out bond strength was significantly influenced by cement type (p= 0.0402): the RelyX U100 cement presented higher mean value. The dual-activated mode increased the bond strength in comparison to self-activated mode (p < 0.0001). Statically differences were observed between groups: G1 (22.4 4.0 MPa) > G3 (20.4 3.6 MPa) > G4 (17.8 5.2 MPa) > G2 (13.5 4.3 MPa). Bond strength was not affected by post space depth (p = 0,4749). The resin cement thicknesses were significantly different in root thirds: cervical (102 45 m) > middle (75 29 m) > apical (52 28m). No strong correlation between cement thickness and push-out bond strength was observed (r = - 0.2016, p = 0.0033). The main failure mode was mixed, except for G2 (74% adhesive failures at post-cement interface). It was concluded tha the self-adhesive cement showed a better performance than the conventional one, and both dual resin systems, specially the RelyX ARC, presented photo-activation dependence to attain greater adhesive bond strength.

O objetivo deste estudo foi realizar uma avaliação tridimensional da rugosidade superficial em 3 tipos de pinos de fibra - DT LightPost, FRC Postec Plus e Transluma Post - submetidos a diferentes tratamentos de superfície e avaliar os efeitos dos pré-tratamentos na resistência adesiva a um compósito de presa dual Biscore. Os tratamentos de superfície foram: imersão em ácido hidrofluorídrico, jateamento com óxido de alumínio a 50m, imersão em peróxido de hidrogênio, jateamento com óxido de alumínio a 50m seguido de imersão em ácido hidrofluorídrico e jateamento com óxido de alumínio a 50m seguido de imersão em peróxido de hidrogênio. No experimento 1, 75 pinos foram divididos em 3 grupos (n = 25), de acordo com seu fabricante e subdivididos em cinco subgrupos. A rugosidade superficial foi medida usando um rugosímetro tridimensional e analisada com o software de análise 3D. Os valores de rugosidade foram obtidos antes e após diferentes tratamentos de superfície na área dos mesmos corpos-de-prova. Para o experimento 2, foram utilizados os mesmos corpos-de-prova, os mesmos grupos e subgrupos do experimento 1, tendo sido adicionado o subgrupo de controle (n=90) e a resistência adesiva a um compósito presa dual Biscore foi mensurada através de um teste push-out. A resistência adesiva foi medida em uma máquina universal de ensaios, com uma célula de carga tipo SLBL-5kN em uma velocidade de 0,5 mm / min. Os resultados do experimento 1 foram analisados através de um teste estatístico t-Student. Jateamento e jateamento seguido de imersão em ácido hidrofluorídrico produziram um aumento estatisticamente significante na rugosidade, contudo somente o tratamento por jateamento proporcionou um aumento significativo nos valores de rugosidade. Os resultados do experimento 2 foram obtidos através de um um teste t-unilateral de hipótese com variância desconhecida. Concluiu-se que o jateamento com óxido de alumínio a 50&#956;m em uma distância de 30 mm a 2,5 bar de pressão por 5 segundos foi suficiente para modificar a topografia dos pinos de fibra de vidro e quartzo e que o jateamento com partículas de 50 &#956; alumina a distância de 30 mm a 2,5 bar de pressão por 5 segundos foi o único tratamento de superfície que aumentou a resistência adesiva do compósito Biscore aos pinos DT Light Post e Transluma Post. Os pinos FRC Postec Plus não demostraram um aumento estatisticamente significante na resistência adesiva em nenhum grupo. / The aim of this study was to perform a tridimensional surface roughness test evaluation of different surface treatments to 3 types of fiber posts - DT LightPost, FRC Postec Plus e Transluma Post - and evaluate the effects of the different pretreatments on the bond strength of a dual-cure resin core material Biscore. The different surface treatments were: immersion in hydrofluoric acid, sandblasting abrasion with 50 alumina particles, immersion in hydrogen peroxide, sandblasting abrasion with 50 alumina particles followed by immersion in hydrofluoric acid and sandblasting abrasion with 50 alumina particles followed by immersion in hydrogen peroxide. In the first experiment seventy five fiber posts were divided into 3 groups (n = 25), according to their manufacturer and subdivided into 5 subgroups. Surface roughness was measured using a tridimensional surface roughness test and analyzed with 3D analysis software. Surface roughness was obtained before and after the different surface treatments at the same post area. In the second experiment the same samples divided in groups and subgroups were used, but a control group (no treatment) was added (n = 90) and the bond strength to a composite resin core material Biscore was measured using a push-out design. The interfacial push-out bond strength was measured in a universal testing machine, with a load cell type SLBL-5kN at a crosshead speed of 0.5 mm/min. Results in experiment 1 were statistically analyzed using Students t-Test. Sandblasting and sandblasting followed by immersion in hydrofluoric acid produced a significant increase in roughness, but the sandblasting treatment was able to provide a significant roughness increase. Results in experiment 2 were statistically analysed using one-sided t-Test of Hypothesis with unknown variance. It was concluded that sandblasting airborne-particle abrasion with alumina 50 at a distance of 30 mm at 2.5 bars pressure for 5 seconds was sufficient to modify the surface topography of glass and quartz fiber posts and the sandblasting abrasion with 50 alumina particles at a distance of 30 mm at 2.5 bars pressure for 5 seconds was the only surface treatment in DT Light Post and Transluma Post that increased the bond strength to dual cure resin composite cores. FRC Postec Plus post did not shown an increase in bond strength in any group.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Significant technological advances in dental materials and chemicals have occurred in recent decades, contributing to increased longevity of adhesive restorations. The aim of this study was to evaluate the influence of the chlorhexidine concentration, time and storage condition on the microtensile bond strength of adhesive systems. The study was conducted in two stages; for the first analysis of this study, thirty noncarious human molars were sectioned to expose middle-coronal dentin, which was etched with 37% phosphoric acid. Specimens were randomly assigned to the following treatments with chlorhexidine digluconate (CHX) (n=10): group C (control), not treatment was done; group 0.12Chx, aqueous solutions of 0.12% Chx; group 2CHX, aqueous solutions of 2% CHX. Each group was subdivided in accordance with adhesive systems (n=5): SC, Adper Scothbond Multi-Purpose; and XP, XP Bond. All were restored with resin composite Filtek Z350 XT. Resin-dentin sticks with cross-sectional area approximately of ±1.0mm2 were submitted to microtensile bond strength (&#956;TBS) test immediately (T0) and after 4 months of storage in artificial saliva (T4). For the second analysis this study, a flat middle dentin surface was prepared on 15 extracted human molars and was etched with 37% phosphoric acid. Specimens were randomly divided according to the treatments with CHX (n=10): Np, no pretreatment; 0.12CHX, aqueous solutions of 0.12% CHX; 2CHX, aqueous solutions of 2% CHX. All specimens were bonded with Adper Scothbond Multi-Purpose and restored with resin composite Filtek Z350 XT. Resin-dentin sticks with cross-sectional area of approximately ±1.0mm2 were submitted to microtensile bond strength test immediately (T0) and after 4 months of storage (T4) in mineral oil. The results of this second analysis were compared with the results of the groups that used the Adper Scothbond Multi- Purpose adhesive system of the first evaluation. The data were submitted to statistical analysis by 3-way analysis of variance (ANOVA) and the Tukey Honestly Significant Difference (HSD) test (&#945;=.05). Results of first evaluation showed statistically significant differences on bond strength values to aging factor (p<.001) and adhesive factor (p<.001). The failure mode was analyzed by Fisher s Exact Test, which demonstrated significant differences within the groups; prevalence of mixed in T0 and adhesive failure after aging to SC groups, except the groups treated with 2% CHX; and XP groups had a prevalence of adhesive failures at T0 and mixed failures in T4, except the groups treated with 2% chlorhexidine. For the second evaluation, was found statistically significant differences between the bond strength of storage media (p < .001) and between aging versus the storage media (p<.001). Fisher s Exact Test demonstrated significant differences between the failure mode within the groups; prevalence of mixed and adhesive failure. Therefore, the use of chlorhexidine did not influenced the bond strength values of the adhesive systems tested, however of 2% CHX showed influence in the dental structure. Differences in adhesives systems were detected, which 3-step etch-and-rinse adhesive presented higher bond strength values than 2-step etch-and-rinse adhesive; and after 4 months of aging, the bond strength values were lower, regardless of the adhesive system tested. Specimens stored in artificial saliva long-term showed interface degradation by hydrolysis and reduction on bond strength, unobserved characteristics in mineral oil storage. / Significantes avanços tecnológicos e químicos de materiais odontológicos ocorreram nas últimas décadas, contribuindo para aumento da longevidade de restaurações adesivas. O objetivo deste estudo foi avaliar a influência da concentração de clorexidina, tempo e diferentes meios de armazenagem na resistência de união de sistemas adesivos à dentina, por meio de ensaio mecânico de microtração. O estudo foi realizado em duas etapas; na primeira etapa 30 terceiros molares humanos íntegros foram selecionados. O esmalte oclusal foi seccionado, expondo dentina média, a qual foi condicionada com ácido fosfórico 37%. Os espécimes foram divididos em três grupos (n=10) de acordo com o tratamento da dentina com diferentes concentrações de digluconato clorexidina (CHX), sendo: grupo C (controle), não recebeu tratamento com clorexidina; grupo 0,12Chx, aplicação de CHX a 0,12% durante 60 s; e grupo 2Chx, aplicação de CHX 2% por 60 s. Posteriormente, cada grupo foi subdividido em dois grupos (n=5) de acordo com o sistema adesivo utilizado: SC, Adper Scothbond Multi-Purpose, e XP, XP Bond. Todos os espécimes foram restaurados com resina composta Filtek Z350 XT; e seccionados em palitos de área de seção de ±1 mm2. Estes foram submetidos ao ensaio de microtração imediatamente (T0) e após 4 meses de armazenagem (T4) em saliva artificial. Para segunda análise deste estudo, 15 terceiros molares humanos íntegros tiveram a superfície oclusal seccionada e condicionada com ácido fosfórico 37%. Os dentes foram divididos em três grupos (n=5) de acordo com o tratamento da dentina com clorexidina: Np (controle), não recebeu tratamento com clorexidina; 0,12CHX, tratamento dentinário com solução de clorexidina a 0,12% durante 60 s; e 2CHX, tratamento com clorexidina a 2% por 60 s. Os espécimes receberam aplicação de sistema adesivo Adper Scothbond Multi-Purpose e foram restaurados com resina composta Filtek Z350 XT. Palitos de resina/dentina de ±1 mm2 foram seccionados e submetidos ao ensaio de microtração imediatamente (T0) e após 4 meses de armazenagem (T4) em óleo mineral a 37ºC. Os resultados desta segunda análise foram comparados com os resultados dos grupos em que foi utilizado o sistema adesivo Adper Scothbond Multi-Purpose da primeira análise. Os dados obtidos foram estatisticamente analisados pela análise de variância fatorial e teste de Tukey (&#945; = 0,05). Os resultados da primeira análise mostraram diferença estatisticamente significante nos valores de resistência de união para o fator envelhecimento (p<0,001) e fator adesivo (p<0,001). O padrão de falha foi analisado pelo Teste Exato de Fisher, o qual mostrou diferença estatística dentro dos grupos; prevalecendo falha mista em T0 e falha adesiva após envelhecimento para os grupos SC, exceto os grupos tratados com CHX a 2%; e os grupos XP apresentaram prevalência de falhas adesivas em T0 e falhas mistas em T4, exceto os grupos tratados com clorexidina 2%. Na segunda análise deste estudo foi encontrada diferença estatisticamente significante para o meio de armazenagem (p<0,001), e entre envelhecimento e meio de armazenagem (p<0,001). Teste Exato de Fisher mostrou diferença significante no padrão de falha dentro de cada grupo; e prevalência de falhas mistas e adesivas. Portanto, o uso de clorexidina não influenciou nos valores de resistência de união dos sistemas adesivos testados, no entanto a CHX 2% mostrou ter influência no padrão de fratura. Diferença na resistência de união dos sistemas adesivos foi detectada, sendo que o adesivo de 3 passos apresentou maiores valores. E espécimes armazenados em saliva artificial apresentaram degradação da interface resina/dentina e redução na resistência de união, características não encontradas nos grupos armazenados em óleo mineral. / Mestre em Odontologia

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study evaluated the effect of thermally deposited siloxane-methacrylate coating on bond strength glass-fiber post to core materials. Furthermore, evaluated mechanical properties of flexural strength, flexural modulus and stiffness. For bond strength, two types of GFP (Exacto, Angelus and White Post DC, FGM) were divided into eight groups (n = 13): S (control): pre-hydrolyzable silane (Prosil, FGM) was applied on the post surface; SA: silane was applied followed by one layer of adhesive (Scothbond, 3M Espe); HS: etching with 35% H2O2 (Whiteness HP Max, FGM) for one minute followed by silane; HSA: etching with H2O2 followed by silane and adhesive; Si: deposited siloxane-methacrylate coating (Si-O) by means of immersion of post in experimental solutions of5% MPTS fowled by heating at 120°C for one hour; SiS: silane application after Si-O; SiA: application adhesive after Si-O; SiSA: silane and adhesive application after Si-O. The composite resin restorations (AllCem Core, FGM) were simulated using translucent silicone molds. After 24 hours water storage at 37 °C, the post/resin assembly was serially sectioned in beams that were subjected to a microtensile bond strength test. For analysis of mechanical properties, eighteen White Post DC and eighteen Exact were used (n = 6). Post without surface treatment, etched with H2O2 and coated with siloxane methacrylate after thermally deposition had their mechanical properties evaluated skin test flexural strength of three points. The data presented normal and homogeneous distribution and subjected to two-way ANOVA and Tukey test. The results showed that the surface treatment only affected the bond strength in Exacto post (P<0.001), while for the White Post DC all groups were statistically equal to the control (22.5 ± 5.1). The highest bond strength values were obtained in SiS (40.4 ± 6.9) and SiSA (38.8 ± 5.3) groups. The etching with H2O2 (HS: 22.9 ± 2.5 and HSA: 25.5 ± 4.5) promoted increased bond strength when compared to control (15.8 ± 4.1), however, had lower values than the thermally deposition siloxane. The mechanical proprieties were not affected by surface treatment, only by the type of post, wherein Exacto post showed highest means of flexural strength, flexural modulus and lower stiffness. Thus, it is concluded that the thermally deposited siloxane-methacrylate coating is a viable option for increasing the bond strength to the core pins without alterations completion of its mechanical properties. / O objetivo desses estudo foi avaliar o efeito do revestimento de pinos de fibra com siloxano-metacrilato, após deposição térmica, na resistência de união ao núcleo de preenchimento em resina composta. Além disso, avaliou a influência deste tratamento nas propriedades mecânicas de resistência flexural, modulo de flexão e rigidez. Para avaliar a resistência de união dois tipos de pinos (White Post DC3, FGM, Produtos Odontológicos e Exacto 3, Ângelus) foram divididos aleatoriamente em oito grupos (n=13): S (controle): uma camada de silano (Prosil, FMG) foi aplicado sobre a superfície do pino; SA: aplicação de uma camada de silano, seguido do adesivo (Scothbond, 3M Espe); HS: condicionamento com H2O2 35% (Whiteness HP Max, FGM) por um minuto seguido da aplicação de silano; HSA: aplicação de H2O2 seguido da aplicação de silano e adesivo; Si: revestimento com siloxano-metacrilato após deposição térmica (Si-O), por meio da imersão em solução experimental de MTPS a 5% seguido de aquecimento a 120°C por 1 hora. SiS: aplicação de silano após Si-O; SiA: aplicação de adesivo após Si-O; SiSA: aplicação de silano e adesivo após Si-O. As restaurações em resina composta (AllCem Core, FGM) foram simuladas utilizando moldes de silicones translúcidos. Após 24h de armazenagem em água a 37ºC, as amostras foram submetidas a cortes seriados, perpendiculares ao longo eixo do pino, obtendo amostras com dimensões de aproximadamente 1x1mm, com formato de palito. As amostras foram submetidas ao ensaio mecânico de microtração à velocidade de 0,7 mm/min até o rompimento dos espécimes. Para análise das propriedades mecânicas, dezoito White Post DC e dezoito Exacto foram utilizados (n=6). Pinos sem tratamento de superfície, condicionados com H2O2 e revestidos com siloxano-metacrilato após deposição térmica tiveram suas propriedades avaliadas pelo ensaio mecânico de resistência flexural de três pontos. Os dados obtidos apresentaram distribuição normal e homogênea e foram submetidos a análise de variância fatorial de dois fatores e teste de Tukey. Os resultados demostraram que o tratamento de superfície só afetou a resistência de união no pino Exacto (P<0,001), enquanto para o White Post DC todos os grupos foram estatisticamente iguais ao controle (22,5 ± 5,1). Os maiores valores de resistência de união foram obtidos nos grupos SiS (40,4 ± 6,9) e SiSA (38,8 ± 5,3). O condicionamento com H2O2 (HS: 22,9 ± 2,5 e HSA: 25,5 ± 4,5) promoveu o aumento da resistência de união quando comparado com o controle (15,8 ± 4,1), no entanto, obteve valores menores que a deposição térmica de siloxano. As propriedade mecânicas não foram afetadas pelo tratamento de superfície, apenas pelo tipo de pino, sendo que o Exacto apresentou maiores valores de resistência flexural, modulo de flexão e menor rigidez. Dessa forma, conclui-se que a deposição térmica com siloxano-metacrilato é uma opção viável para o aumento da resistência de união dos pinos ao núcleo de preenchimento, sem alterações da suas propriedades mecânicas. / Mestre em Odontologia

O objetivo deste trabalho foi estudar a ação sobre a dentina humana (in vitro) de vários tratamentos de superfície: Lixa, IADR-GM, CVDt e CVDi e de alguns adesivos dentais: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL) avaliando: rugosidade e resistência adesiva por micro-cisalhamento. Foram utilizados 72 terceiros molares hígidos que foram divididos ao meio. As superfícies oclusais das 144 metades dentais foram removidas e padronizadas com Lixa #600. Após receberem os tratamentos de superfície citados, foi avaliada a rugosidade média superficial (Ra) da dentina. Em seguida realizou-se a hibridização e a confecção dos cilindros de resina composta (RC) para finalizar o preparo dos corpos de prova (cps). Após armazenagem de 24h em água destilada a 370C realizou-se o teste de micro-cisalhamento com velocidade de deslocamento de 1mm/min. Os resultados foram submetidos a testes de analise estatística (ANOVA) onde foi comprovado que a menor Ra foi encontrada nas superfícies instrumentadas com Lixa #600 seguida pelo CVDi, IADR-GM que apresentaram rugosidade intermediaria e se igualaram e pelo CVDt que produziram as superfícies mais rugosas. Já para o tratamento de superfície, o CVDi foi que apontou os piores valores de resistência de adesão que com Lixa e IADR-GM. Nos resultados para os adesivos, o PL apresentou valores de resistência à união inferiores ao SB e CF que se igualaram. Já para a interação entre os tratamentos de superfície e os adesivos não houve diferenças estatisticamente significantes entre os grupos tratados com Lixa #600, IADR-GM e CVDt e hibridizados com SB ou CF. Concluiu-se: que a Ra produzida em dentina pelo CVD variou de acordo com o tipo de movimento (CVDt produz maior rugosidade que o CVDi); que não foi possível estabelecer uma correlação entre Ra e valores de resistência adesiva; que o PL apresentou valores de resistência à adesão inferiores aos obtidos pelos adesivos SB e CF; que a interação dos tratamentos Lixa, IADR-GM e CVDt com os três adesivos (SB, CF, PL) mostrou valores mais altos para o SB e CF que se igualaram e menores para o PL; que o fator tratamento não produziu diferença de resistência adesiva para o adesivo CF e o mesmo ocorreu com o PL. / The aim of this in vitro study was to evaluate the micro-shear bond strength and the roughness to human dentin using different instrumentations (SiC #600, diamond rotary bur, CVDt and CVDi) and three dentin adhesive/composite resin systems: Adper Sigle Bond 2 (SB), Clearfil SE Bond (CF) e Adper Prompt L-Pop (PL). Seventy-two third molars were split in the middle. The oclusal third from the one hundred and forty and four halves were removed and standardized using the SiC #600. After the prepared surfaces, which were analyzed the roughness average (Ra) with a surface perfilometer and hybridization. The specimens were then stored in distillated water for 24 hours at 370C. The specimens were then were attached to a micro-shear apparatus and subjected to a micro-shear strength test at a crosshead speed of 1mm/min until failure occurred. The two-way ANOVA indicated that there was significant differences in average roughness between the instrumentations which SiC #600 was the smoothest surface. No differences were detected between dentin surface prepared with diamond bur and CVDi (intermediate in the roughness assessment) and the CVDt gave the roughest surface. The bond strengths varied slightly, though dentin instrumentations with CVDi showed the lowest values than the surfaces prepared with SiC #600 and diamond bur. The bond strengths varied slightly, though adhesives, PL showed lower micro-shear bond strength than SB and CF, which were no significant relevance. The interaction of SiC #600, diamond bur and CVDt using SB and CF showed no significant difference in micro-shear bond strength and higher than PL. The instrumentation showed no significant differences in micro-shear bond strength using CF and PL.

Este estudo avaliou, in vitro, a influência da radioterapia na resistência de união (RU) e na interface adesiva entre diferentes cimentos resinosos e dentina radicular. Sessenta caninos superiores foram distribuídos em 2 grupos (n=30) de acordo com a irradiação: não irradiados e irradiados. Os dentes do grupo irradiado foram submetidos à radioterapia com raios-X de 6 MV em frações de 2 Gy, com 30 ciclos, perfazendo 60 Gy. Os dentes foram seccionados para obtenção de raízes com 16 mm de comprimento, sendo realizado em seguida o preparo biomecânico com instrumento Reciproc R50 e obturação pela técnica de condensação lateral com cimento a base resina epóxica. Cada grupo foi subdividido de acordo com o cimento resinoso utilizado para a cimentação dos pinos de fibra de vidro (n=10): RelyX U200; Panavia F 2.0; RelyX ARC. Os pinos foram submetidos a tratamento de superfície com ácido fluorídrico 10% e cimentados de acordo com as recomendações de cada fabricante. Após a cimentação dos pinos, os dentes foram seccionados transversalmente em slices de 1 mm de espessura, obtendo-se 3 slices de cada terço da raiz. Os slices mais cervicais de cada terço foram utilizados para avaliar a RU, por meio do teste de push-out com velocidade de 0,5 mm/min, e posterior análise do padrão de falha em estereomicroscópio. Os slices mais apicais de cada terço foram selecionados para análise da interface cimento/dentina em MEV com aumentos de 100, 1000, 2000 e 4000X. Os dados de RU e adaptação da interface cimento/dentina foram submetidos à análise estatística pelos testes de ANOVA e Tukey, e Kruskal-Wallis e Duns, respectivamente. Os espécimes irradiados apresentaram menores valores de RU (8,23&plusmn;4,26) comparados aos dentes não irradiados (11,88&plusmn;6,42) (p<0,00001). Quanto aos cimentos resinosos, o RelyX U200 apresentou maiores valores na RU (15,17&plusmn;5,89) comparado aos cimentos RelyX ARC (7,68&plusmn;4,22) (p<0,0001) e Panavia F 2.0 (7,32&plusmn;2,71) (p<0,0001). O terço cervical apresentou maiores valores de RU (13,08&plusmn;6,10) comparado aos terços médio (9,72&plusmn;5,03) e apical (7,38&plusmn;4,53) (p<0,0001). O padrão de falhas mostrou ocorrência de falhas coesivas na dentina para os espécimes irradiados. Na análise da interface cimendo/dentina por MEV, observou-se maior desadaptação nos dentes submetidos à radioterapia. Em relação aos cimentos resinosos, foi observada maior adaptação com RelyX U200 e RelyX ARC comparados à Panavia F 2.0. Na análise qualitativa em MEV observou-se presença de fraturas e microfraturas na dentina radicular e menor presença de fibras colágenas em dentes irradiados. Para o cimento resinoso RelyX U200 e Panavia F 2.0 observou-se interface justaposta do cimento com a dentina radicular em dentes irradiados e não irradiados, sendo que para o cimento resinoso RelyX ARC foi observada formação de camada híbrida e tags de maneira similar para dentes irradiados e não irradiados. Concluiu-se que a radioterapia resultou na redução da resistência de união e na maior desadaptação da interface cimento resinoso/dentina radicular e que o cimento resinoso autoadesivo se apresentou como melhor alternativa para cimentação de pinos de fibra de vidro em dentes irradiados. / This in vitro study, evaluated the influency of radiotherapy on bond strength (BS) and adhesive interface between different resin cements and root dentin. Sixty maxillary canines were selected and distributed into two groups (n = 30) according to the irradiation protocol: non-irradiated and irradiated. The irradiated group were submitted to X-ray radiotherapy of 6 MV in fractions of 2 Gy, with 30 cycles, until complete 60 Gy. The teeth were sectioned to obtain 16 mm of root length, followed by biomechanical preparation with R50 reciproc instrument and obturation using the lateral condensation technique with epoxy resin-based sealer. Then, each group was subdivided according to the resin cement used for the glass fiber post cementation (n = 10): RelyX U200, Panavia F 2.0 and RelyX ARC. The posts were submitted to surface treatment with 10% hydrofluoric acid, and then cemented according to the manufacturer instructions. After the posts cementation, the teeth were sectioned transversely into 1 mm thick slices, and 3 slices were obtained from each root third. The most cervical slice of each third was used to evaluate the BS by the push-out test at 0.5 mm/min of velocity and the failure pattern was analyzed using stereomicroscopy. The most apical slice of each third was selected for SEM analysis, which were prepared and metalized. The dentin/cement interface analysis was performed at the following magnification: 100, 1000, 2000 and 4000X. The BS data and dentin/cement interface adaptation were submitted to statistical analysis by ANOVA, Tukey and Kruskal-Wallis, and Duns tests respectively. The irradiated specimens had lower BS values (8.23 &plusmn; 4.26) compared to non-irradiated group (11.88 &plusmn; 6.42) (p <0.00001). Regarding the resin cements, the RelyX U200 showed the higher values in BS (15.17 &plusmn; 5.89) compared to RelyX ARC (7.68 &plusmn; 4.22) and Panavia F 2.0 (7 , 32 &plusmn; 2.71) (p <0.0001). In addition, the cervical third presented higher BS values (13.08 &plusmn; 6.10) when compared to the middle (9.72 &plusmn; 5.03) and apical (7.38 &plusmn; 4.53) thirds (p <0.0001). The failure pattern showed cohesive failures in root dentin of the irradiated specimens. In the SEM dentin/cement interface analysis, a greater misadaptation was observed for the teeth submitted to radiotherapy. Regarding the resin cements, a better adaptation was observed for the RelyX U200 and RelyX ARC compared to the Panavia F 2.0. In the SEM qualitative analysis of the irradiated teeth, was possible to observe the presence of fractures and microfractures in the root dentin and a small number of collagen fibers. The resin cements RelyX U200 and Panavia F 2.0 showed a juxtaposed interface of the cement with the root dentin in irradiated and non-irradiated teeth, being that for the RelyX ARC cement the presence of hybrid layer and tags was similar for irradiated and non-irradiated groups. It was concluded that the radiotherapy promoted reduction of the bond strength and increase the gaps in the dentin/resin cement interface and the self-adhesive resin cement is the best alternative for glass fiber posts cementation in irradiated teeth.

A presente pesquisa se propôs a avaliar a influência de cinco tratamentos dentinários na resistência de união à dentina de quatro cimentos de ionômero de vidro modificados por resina (CIVRMs). O ensaio experimental foi realizado in vitro, fazendo uso de 200 incisivos bovinos. Destes, foram obtidos 200 fragmentos de dentina, que foram distribuídos aleatoriamente em 20 grupos (n=10), segundo os fatores de variação que compreendem cinco tratamentos dentinários (Grupo controle, ou seja, sem tratamento; Ácido Poliacrílico a 20%, Clearfil SE Bond; Single Bond Universal e Primer do Vitremer) e quatro cimentos ionoméricos (GC Fuji II LC® CAPSULE; GC Fuji LINING® LC (Paste Pak); Vitrebond® e Vitremer). Após a confecção dos corpos de prova e 24h de armazenamento em estufa à 37oC, foi realizado o teste de microcisalhamento na máquina de ensaios universal (Instron 5942 - Canton, MA, EUA) com velocidade de 1mm/min, seguido da análise do padrão de fratura em microscópio digital. A análise estatística dos 400 resultados obtidos foi feita por meio do teste paramétrico ANOVA para dois fatores de variação (cimento e tratamento) (p<0,05%) e pelo teste auxiliar de Tukey (p<0,05%). Os testes estatísticos demonstraram haver diferença estatística tanto entre os tratamentos, como entre os cimentos e na interação de ambos (p<0,0001). Os sistemas adesivos Clearfil SE (X?=18,26 ± 2,78) e SingleBond (X?=17,28 ± 2,49) promoveram os valores de resistência adesiva mais elevados em comparação aos demais tratamentos, mas sem apresentarem diferença estatística entre si, o que representou um aumento na resistência de união de 121% para o Clearfil SE e 109,2% para o Single Bond Universal em relação ao Grupo Controle. O uso do Ácido Poliacrílico (X?=9,94 ± 3,55) alcançou valores intermediários, correspondendo a um aumento de 20% na resistência adesiva em relação ao Grupo Controle. Esse tratamento se diferenciou estatisticamente dos maiores valores, porém não apresentou diferença frente ao Primer do Vitremer (X?=8,91 ± 2,97). O grupo controle (X?=8,26 ± 4,17) evidenciou os menores valores, se diferenciando estatisticamente dos sistemas adesivos e do Ácido Poliacrílico, mas com resultados que o equiparou ao tratamento com o Primer do Vitremer. Ao se analisar a interação entre cimento e tratamento, todos os cimentos de ionômero de vidro resinomodificados (CIVRMs) testados neste estudo apresentaram seus maiores resultados quando um dos sistemas adesivos foi utilizado como tratamento dentinário, independente de qual sistema adesivo. Com base nesses resultados, pôde-se concluir que os dois sistemas adesivos autocondicionantes foram capazes de melhorar significativamente a resistência adesiva dos CIVRMs. / This research aims to evaluate the influence of five dentin pretreatments on microshear bond strength of four resin-modified glass ionomer (RMGI). The experiment was performed in vitro, using 200 bovine incisors. From these, there were obtained 200 dentine fragments that were randomly distributed into 20 groups (n = 10) according to the variation factors comprising five dentin treatment (control group, i.e., no treatment; Polyacrylic Acid 20%; Clearfil SE Bond; Single Bond Universal and Vitremer Primer) and four glass ionomer cements (GC Fuji II LC® CAPSULE; GC Fuji LC LINING® (Paste Pak); Vitrebond® and Vitremer). After preparation of the samples and 24h storage at 37 °C, was performed microshear test in a universal testing machine (Instron 5942 - Canton, MA, USA) with speed of 1mm/min, followed by analysis of the pattern fractures in digital microscope. Statistical analysis of the 400 results was performed by ANOVA nonparametric test for two variation factors (cement and treatment) (p <0.05%) and the post-hoc Tukey (p <0.05%). The tests demonstrated there are statistical difference between treatments, cements and between the interaction of both (p <0.0001). The Clearfil SE (X?=18,26 ± 2,78) and SingleBond (X?=17,28 ± 2,49) promoted the highest bond strength values compared to the other treatments, but showing no statistical difference between them, which represented an increase in bond strength of 121% for Clearfil SE and 109.2% for Single Bond Universal compared to control group. The Polyacrylic Acid (X?=9,94 ± 3,55) has reached intermediate values, corresponding to a 20% increase in adhesive strength compared to control group. This treatment differed significantly from the higher values, but showed no difference compared to Primer Vitremer (X?=8,91 ± 2,97). The control group (X?=8,26 ± 4,17) showed the lowest values, statistically differing from the adhesives and polyacrylic acid, but with results that matched to the treatment with Vitremer Primer. When analyzing the interaction between cement and treatment, all cements tested in this study had higher results when one of the adhesive systems was used as dentin treatment, regardless of which adhesive system. Based on these results, it could be concluded that the two adhesive systems were able to significantly improve the adhesive strength of RMGIs.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-01-12T12:51:08Z No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Approved for entry into archive by Diamantino Mayra (mayra.diamantino@ufjf.edu.br) on 2017-01-31T11:16:46Z (GMT) No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Made available in DSpace on 2017-01-31T11:16:46Z (GMT). No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) Previous issue date: 2009-12-10 / O presente estudo teve como objetivo avaliar a influência do tratamento da dentina radicular com clorexidina a 2% e ácido cítrico a 10% na resistência de união de pinos de fibra de vidro cimentados com cimento resinoso RelyX Ultimate (3M ESPE) associado a um adesivo autocondicionante Single Bond Universal (3M ESPE). Quarenta e cinco dentes humanos unirradiculares foram selecionados e seccionados na junção cemento-esmalte, padronizando-os com 14 mm de comprimento. Após tratamento endodôntico, as raízes foram divididas aleatoriamente em 3 grupos (n=15) de acordo com o tratamento prévio do conduto radicular: G1, nenhum tratamento; G2, aplicação de gel de clorexidina a 2% (Rioquímica®) por 60 segundos; G3, aplicação de ácido cítrico a 10% (Idem per Idem Farmácia de Manipulação Ltda) por 60 segundos. Posteriormente, foi aplicado o adesivo nos condutos e nos pinos de fibra de vidro (White Post, FGM) e estes foram cimentados com cimento resinoso (RelyX Ultimate - 3M ESPE), sendo fotopolimerizados por 40 segundos. As raízes foram seccionadas axialmente em discos de 2 mm e os espécimes foram submetidos ao teste de push-out. As médias dos valores obtidos (MPa) foram analisadas por meio dos testes one-way ANOVA e Tukey (α=0,05) e os tipos de falhas analisadas em estereomicroscópio com aumento de 8,0X. Os resultados mostraram que não houve diferença estatisticamente significativa entres os grupos avaliados, assim como quando comparados os terços radiculares em cada grupo (p>0,05), entretanto resultados significantes foram encontrados entre os grupos G1 e G2 na região cervical (p=0,045). Falhas mista e adesiva entre cimento e dentina foram mais prevalentes. Pôde-se concluir que o uso da clorexidina a 2% no conduto radicular pode interferir na resistência de união de pinos de fibra de vidro e que o ácido cítrico não influenciou nos resultados. / The aim of this study was to investigate the influence of root dentine treatment with 2% chlorhexidine and 10% citric acid on bond strength of fiberglass post cemented with self-etching cement. Forty five human single-rooted teeth were selected and sectioned in the cement-enamel junction, standardizing them with 14 mm length. After endodontic treatment the roots were randomly divided in 3 groups (n=15) according to the previous treatment of the root canal: G1, no treatment; G2, application of 2% chlorhexidine (Rioquímica®) for 60s; G3, application of 10% citric acid (Idem per Idem - Farmácia de Manipulação Ltda) for 60s. Subsequently, the self-etching adhesive Single Bond Universal (3M ESPE) was applied in the canals and on the fiberglass post (White Post, FGM) and these ones were cemented with resin cement (RelyX Ultimate - 3M ESPE), and light polymerized for 40s. The roots were sectioned transversely in slides of 2 mm thickness and the push-out test was performed. Data were analyzed by one-way ANOVA and Tukey test (α=0.05) and the types of failures were analyzed under stereomicroscopy (8.0X). The results show that there was no statistically significant difference between the groups, as well as when comparising bond strength in root thirds in each group (p>0.05), however, significant results were found between groups G1 and G2 in the cervical third (p=0.045). Mixed and adhesive failures between cement and dentine were predominant. It can be concluded that the use of 2% chlorhexidine in the root canal can interfere in the fiberglass posts bond strength.