Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-03T17:14:13Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017-1-50.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017-51-111.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Luciana Ferreira (lucgeral@gmail.com), reason: olhe no guia a forma de nomear arquivos divididos on 2017-05-04T11:04:01Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-04T17:04:01Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 1.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 2.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Luciana Ferreira (lucgeral@gmail.com), reason: No guia está registrado: - Quando o arquivo tiver que ser dividido, por ser grande, cada um deve ser renomeado da mesma forma, adicionando a indicação da parte, entre parênteses, no final. Exemplos: “Tese - João Alves da Silva - 2015 (1)”, “Tese - João Alves da Silva - 2015 (2)”. on 2017-05-05T12:44:32Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-05T16:53:52Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 1.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 2.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Erika Demachki (erikademachki@gmail.com), reason: on 2017-05-05T17:13:14Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-05T17:15:42Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-05-08T15:51:39Z (GMT) No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-05-08T15:51:39Z (GMT). No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-03-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The objectives of this work were to evaluate the stress distribution (SD), fracture resistance (RF), adhesive strength (AS) and their respective fracture patterns of weekeaned bovine roots, rehabilitated with customized pins with different resinous materials. In addition, the objective of this study was to evaluate the polymerization depth of the resinous materials by Knoop microhardness method (MH). Eight experimental groups were established (n = 10 for FR and AS; n = 5 for MH), with the factor under study: 1. The post type (industrialized glass fiber post relined (I) and personalized post (P), 2. the relining material only for industrialized glass fiber post (experimental composite (e) and composite resin (R)); 3. the material used only for personalized post (experimental composite (e) and bulk fill resin (b), and 4. the amount of remaining dentin (root embrittlement inner wear, in lengths of 5 mm or 10 mm). One hundred and forty bovine roots of similar size were selected and restored according to the group to which they belonged. For FR, Pperiodontal and alveolar bone were simulated and the specimens were placed in an Instron 5965 machine at a 135 ° angle to the long axis and loaded at a constant velocity of 0.5 mm/min in compression until the fracture. The fracture pattern was classified as: F1- crown; F2- root; F3- crown/root; F4- fracture with displacement of the crown/post. For AS, the specimens were sectioned in slices of 1 mm perpendicular to their long axis. Each specimen was placed in a test machine to received the load in the apical-coronal direction, at a constant velocity of 0.5mm / min, pushing the pin through the largest side of the sample until fracture. The fracture pattern was classified as: F1- cohesive of the pin and/or reline material; F2- cohesive of dentin; F3- adhesive of pin/reline material; F4 - Adhesive bonding cement/ eline material and F5 - mixed. For MH, the specimens were sectioned parallel to their long axis. The tests were performed with a Knoop penetrator under a static charge of 50 grams per 10 seconds. MH was calculated as the average value for each third. Finally, the finite element method was used to analyze the DT. 3D virtual models representative of each experimental group were created and analyzed under von Mises equivalent stresses criterion, simulating loading of 100N at a 45o angle with the long axis. The experimental composite proved to be an alternative for the rehabilitation of weakened roots when used to create personalized posts or when used as a relining material, with FR values similar to the traditional technique, but with more favorable stress distributions. Moreover, it presented excellent adhesive strength to the dentin structure, being comparable to conventional composite resin and bulk fill resin. The bulk fill resin resulted in low values of fracture resistance associated with the fracture and displacement of post/crown. Lower microhardness values were observed in the apical third for bulk fill resin. / Os objetivos deste trabalho foram avaliar a distribuição de tensões (DT), resistência à fratura (RF), resistência adesiva (RA) e seus respectivos padrões de fratura de raízes bovinas fragilizadas, reabilitadas com pinos personalizados com diferentes materiais resinosos. Além disso, objetivou-se avaliar a profundidade de polimerização dos materiais resinosos por meio do método de microdureza Knoop (MD). Oito grupos experimentais foram criados (n=10 para RF e RA; n=5 para MD), tendo como fator em estudo: 1. o tipo de pino utilizado (pino de fibra de vidro industrializado reembasado (I) e pino personalizado (P)); 2. o material de reembasamento apenas para os pinos industrializados (compósito experimental (e) e resina composta (r)); 3. o material utilizado para confecção apenas dos pinos personalizados (compósito experimental (e) e resina bulk fill (b)); e 4. a quantidade de dentina remanescente (fragilização radicular por desgaste interno nos comprimentos de 5 mm ou 10 mm). Cento e quarenta raízes bovinas com dimensões semelhantes foram selecionadas e restauradas de acordo com o grupo ao qual pertenciam. Para RF, ligamento periodontal e osso alveolar foram simulados e os espécimes posicionados em máquina Instron 5965, em um ângulo de 135° em relação ao longo eixo do dente de modo que recebessem carregamento à velocidade constante de 0,5mm/min em compressão até a fratura. Em seguida, o padrão de fratura foi classificado em: F1- coroa; F2- raiz; F3- coroa/raiz; F4- fratura com deslocamento do conjunto coroa/pino. Para RA, os espécimes foram seccionados em fatias 1 mm perpendicularmente ao seu longo eixo. Cada espécime foi posicionado em máquina de ensaio de modo que recebessem a carga no sentido apical-coronal, à velocidade constante de 0,5mm/min, empurrando o pino através do maior lado da amostra até a fratura. O padrão de fratura foi classificado em: F1 - coesiva do pino e/ou material de reembasamento; F2 - coesiva da dentina; F3 - adesiva pino/material de reembasmento; F4 - adesiva material de reembasamento/cimento e F5 – mista. Para MD, os espécimes foram seccionados paralelamente ao seu longo eixo. Os testes foram realizados com um penetrador Knoop sob uma carga estática de 50 gramas por 10 segundos. MD foi calculada como o valor médio para cada terço. E por fim, o método de elementos finitos foi empregado para analisar a DT. Modelos virtuais 3D representativos de cada grupo experimental foram criados e analisados sob critério de tensões equivalentes de von Mises, simulando carregamento de 100N em um ângulo de 45o com o longo eixo. O compósito experimental demostrou ser uma alternativa para a reabilitação de raízes fragilizadas quando utilizado para criar pinos personalizados ou quando utilizado como material de reembasamento de pinos, com valores de resistência à fratura semelhantes à técnica tradicional porém, com distribuição de tensões mais favoráveis. Além disso, apresentou excelente resistência adesiva à estrutura dentinária, sendo comparável à resina composta convencional e à resina bulk fill. Já a resina bulk fill resultou em baixos valores de resistência à fratura associado ao deslocamento do conjunto pino/coroa protética. Valores de microdureza inferiores foram observados no terço apical para a bulk fill.

A lesão não cariosa causada pela dissolução da estrutura dentária sem o envolvimento bacteriano é denominada lesão de erosão dental. Existe ainda a falta de consenso quanto ao tratamento dessas lesões, além de pouco conhecimento quanto ao comportamento delas frente aos procedimentos adesivos. Dentre os mais realizados, tratamentos através de restaurações adesivas têm sido os de melhor resultado. Este trabalho teve como objetivo avaliar a resistência de união (TBS) de restaurações de resina composta realizadas sobre um substrato de dentina erodida simulada, utilizando dois sistemas adesivos diferentes. 40 terceiros molares humanos não irrompidos tiveram o esmalte do terço oclusal completamente removidos, deixando a dentina exposta. Após ter sua superfície dentinária regularizada com lixa de carbeto de silício granulação #600, cada dente foi dividido ao meio, criando assim, 40 amostras pareadas, sendo uma das metades a amostra controle e a outra, experimental. Esta passou por um protocolo de criação de lesão de erosão simulada. Sobre o substrato dentinário de todas as amostras, foram confeccionadas restaurações em resina composta Z350 (3M ESPE). Previamente às restaurações, 20 amostras controle e suas respectivas experimentais foram condicionadas utilizando ácido forfórico 37% e sistema adesivo Adper Single Bond 2 (3M ESPE) (amostras CSB e ESB). As outras 20 amostras receberam o sistema adesivo auto-condicionante Clearfill SE (Kuraray) (amostras CCFe ECF). As amostras produziram palitos de aproximadamente 1,0 mm2 que foram submetidos ao teste de microtração com velocidade média de 0,5 mm/min até a fratura. Resultados estatísticos mostraram haver diferença significativa entre os grupos (usando ANOVA 1 variância, F=4,643). As amostras experimentais tratadas previamente com o adesivo Clearfill SE (ECF) mostraram valores de resistência de união significativamente maios altos quando comparadas com os valores dos outros grupos (m=42.16 ±20.509 Mpa) (p=0,0082). / Non carious lesions caused by dentals structure dissolution without involving bacterial acids are called dental erosion. There is still limited information regarding which treatments should be considered, as well as to how the eroded dentin behaves in adhesive procedures. This study aims to evaluate the effect of different adhesive systems on micro-tensile bond strength (TBS) on eroded dentin and its paired sound substrate sample. 40 non irrupted third human molars had the oclusal enamel removed with a low-speed diamond saw and their exposed superficial dentin surfaces were submitted to polishing with wet # 600-grit silicon carbide sandpaper to remove remaining enamel and plane the surface. Each molar was divided into two equal halves originating 40 paired samples- one control and one experimental. All experimental samples underwent a pH cycling protocol to create a simulated dental erosion lesion. A composite resin Z350 (3M ESPE) restoration was built on each samples surface. Previous to restoration, control group and their respective experimental halves were divided into 2 sub-groups. 20 control + experimental samples were treated with 37% phosphoric acid and Adper Single Bond 2 (3M ESPE) (CSB and ESB); The other 20 control+ experimental samples were treated with Clearfill SE (Kuraray) (CSE and ESE). All 40 restored teeth were cut yielding stick-shapped samples with a cross-sectional area of approximately 1.0 mm2 and were submitted to a micro-tensile force running at a crosshead speed of 0.5 mm/min until fracture. Statistic results showed significant difference among the groups (using the ANOVA test F= 4,643). The eroded dentin samples submitted to surface treatment with Clearfill SE (ECF) prior to restoration showed significantly higher bond strength results when compared to all the other groups (m=42.16 ±20.509 Mpa) (p=0,0082).

Avaliou-se, por meio do teste de microtração, a resistência adesiva da interface pino de fibras de vidro /cimento/ dentina radicular, variando-se cimentos, adesivos dentinários e tempo de armazenamento. Foram utilizados dentes caninos humanos permanentes, extraídos por razões periodontais, que tiveram suas coroas seccionadas e as raízes preparadas para receber pinos de fibras de vidro (Fibrekor). Os dentes foram aleatoriamente divididos em grupos de dez, variando a técnica de cimentação adesiva e o tempo de armazenamento. Os cimentos utilizados foram (1) Panavia F, (2) Variolink II, (3) Enforce, com seus respectivos adesivos. Avaliou-se também a influência da aplicação de uma camada do adesivo hidrofóbico Scotchbond Multi-Purpose Plus [SBMP] com o cimento Panavia F e Enforce. Espécimes cimentados com Variolink II, Panavia F com SBMP e Enforce com SBMP foram armazenados em água destilada por três meses. Após a cimentação, as raízes foram seccionadas (longitudinalmente e horizontalmente) com disco diamantado obtendo-se espécimes de 1mm de espessura, dois por terço da raiz. Os espécimes foram submetidos ao teste de microtração e o modo de fratura analisado em microscópio óptico. Os valores médios de resistência (MPa) foram submetidos aos testes ANOVA e Tukey (p < 0,05). A análise estatística mostrou (1) diferenças significativas na resistência adesiva entre cimentos e terços sendo que na média total dos terços, o cimento Variolink II foi superior aos outros cimentos; (2) na análise por terços, o cimento Variolink II mostrou valores estatisticamente superiores para o terço cervical. Os cimentos Panavia F e Enforce apresentaram valores significativamente menores no terço cervical; (3) diferenças significativas na resistência adesiva, com a aplicação do adesivo hidrofóbico, independente da região avaliada; (4) diminuição significativa na resistência adesiva para os cimentos Variolink II e Enforce, após armazenamento em água; (5) após o armazenamento, o cimento Variolink II apresentou diminuição na resistência adesiva no terço cervical e o cimento Enforce nos terços médio e apical. O cimento Panavia F exibiu aumento significativo da resistência adesiva nos terços cervical e médio, e diminuição no terço apical; (6) em microscopia óptica, um padrão de fraturas predominantemente do tipo adesiva para todos os experimentos. / This study evaluated the microtensile bond strengths of the fiber post-resin / resin cement/ root dentin when were varied the resin cement, dentin bonding system and longterm water storage. Were used for this study, human canines teeth extracted for periodontal reasons. The crown was sectioned and root canals were prepared for fiber post-resin (Fibrekor). The teeth were randomly assigned into experimental groups (n = 10) when were varied the resin luting technique and term water storage. The resin cements were (1) Panavia F, (2) Variolink II, (3) Enforce mediated by their respective adhesives. Experimental groups, using Panavia F and Enforce, were prepared in the same way, except that the additional layer of a low-viscosity bonding resin (Scotchbond Multi-Purpose Plus [SBMP]) was placed on the bonded root dentin surface before luting the fiber post-resin. The teeth were stored for 3 months and subsequently prepared for microtensile bond strength testing. Beams of approximately 1mm2 were tested in tension at 0,5mm/mim in a universal testing machine. Fractured surfaces were examined under X 40 stereomicroscope to determine the mode of fracture. The data were divided into cervical, middle and apical regions and analyzed using ANOVA and Tukey\'s test (p < 0,05). The results of tensile bonding strengths showed (1) significant differences among resin cements and root dentin regions, were presented higher mean bond strength values to Variolink II, when compared with others; (2) the cervical third of Variolink II demonstrated higher values, to Panavia F and Enforce demonstrated lower values for that regions; (3) the application of the additional layer of the hydrophobic adhesive resulted in significant improved in the tensile bonding strength; (4) water storage for 3 months produced bond strengths that were significant lower for Variolink II e Enforce; (5) after storage, the Variolink II reduced bond strengths in the cervical third and Enforce in the middle and apical regions. The cervical and middle third of Panavia F presented higher mean bond strength values and apical regions demonstrated lower values; (6) No cohesive fractures within resin cement, fiber-reinforced composite resin post, or root dentin were identified.

Submitted by Rosangela Silva (rosangela.silva3@unioeste.br) on 2018-05-15T19:35:27Z No. of bitstreams: 2 Saulo Vinicius da Rosa.pdf: 2244692 bytes, checksum: e13fed6b2f75e2fa2861bf064a121ca7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-05-15T19:35:27Z (GMT). No. of bitstreams: 2 Saulo Vinicius da Rosa.pdf: 2244692 bytes, checksum: e13fed6b2f75e2fa2861bf064a121ca7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-03-03 / Bulk fill resins can be used as dentin replacements, requiring coating by another composite resin, such as a nano-hybrid resin, or they can be used without the need for a new composite resin for their protection. The objective of this work was to evaluate the bond strength of repairs made between different composite resins, after aging in different solutions. Five composite resins were used, one conventional and four bulk fill composites. 2x2x5 mm CP were made in silicone mold and aged for 30 days, after which the resins were given the surface treatment and soon after the repair, becoming a CP with 2x2x10mm. All the resins were combined. The mean values obtained for each test specimen were submitted to the Shapiro Kruskall Wallis test, followed by the Dunn test, p <0.05. The results showed that, after aging in distilled water, Aura bulk fill as base showed statistical differences when compared to the composite resins Z350 (1.27 + 0.95) and Tetric Ceram bulk fill (3.72 + 1.74), the composite resin Tetric Ceram bulk fill used as a base showed that there was statistical difference when Filtek bulk fill composite resin 4,81 (+1,20) was used and when Z350 resin (2.22 + 0.63) and Tetric Ceram bulk fill (2.54 + 0.52). After aging in water / ethanol solution, no statistically significant differences were found between all possible combinations. After aging in nitric acid solution, when Aura bulk fill was used as base there were statistical differences between the repair with Tetric Ceram bulk fill (4.02 + 0.82) and Z350 (1.71 + 1.09 ), when Filtek bulk fill used as base there were statistical differences between Z350 (2.30 + 0.62) and Filtek bulk fill 4.02 (+1.85) used for the repair, with Tetric ceram bulk fill as base there were statistical differences when compared to the composite resin Filtek bulk fill 4,04 (+1,07) and Z350 (1,99 + 0,76). According to the results obtained it was possible to verify that, in the majority of the comparisons made among the composite resins evaluated in this study, the composite resins bulk fill obtained better values of bond strength when the composite resins themselves were united bulk fill and the worst values when they received the repair with the composite resin when immersed in acidic solutions and distilled water, it was not possible to observe statistically significant differences when immersing in water / ethane. / As resinas “bulk fill” podem ser utilizadas como substitutas da dentina, necessitando de recobrimento por outra resina composta, como uma resina nano- híbrida, ou ainda podem ser utilizadas sem a necessidade de uma nova resina composta para sua proteção. O objetivo desse trabalho foi avaliar a resistência de união de reparos confeccionados entre diferentes resinas compostas, após envelhecimento em diferentes soluções. Foram utilizadas cinco resinas compostas, sendo uma convencional e quatro resinas compostas “bulk fill”. Foram confeccionados CP de 2x2x5 mm em molde de silicone e envelhecidas por 30 dias, após esse período as resinas receberam o tratamento de superfície e logo após o reparo, tornando-se um CP com 2x2x10mm. Todas as resinas foram combinadas entre si. Os valores médios obtidos para cada corpo de prova foram submetidos ao teste de Shapiro Kruskall Wallis, seguido do pós teste de Dunn, p < 0,05. Os resultados mostraram que após o envelhecimento em água destilada, a Aura bulk fill como base mostrou diferenças estatísticas quando comparadas as resinas compostas Z350 (1,27+0,95) e Tetric Ceram bulk fill (3,72+1,74), a resina composta Tetric Ceram bulk fill utilizada como base mostrou que houve diferença estatística quando utilizada a resina composta Filtek bulk fill 4,81(+1,20) e quando utilizada a resina Z350 (2,22+0,63) e Tetric Ceram bulk fill (2,54+0,52). Após o envelhecimento em solução água/etanol não foram encontradas diferenças estatisticamente significantes entre todas as combinações possíveis. Após o envelhecimento em solução de ácido nítrico, quando a Aura bulk fill foi utilizada como base houve diferenças estatísticas entre o reparo com a Tetric Ceram bulk fill (4,02+0,82) e a Z350 (1,71+1,09), já quando Filtek bulk fill utilizada como base houve diferenças estatísticas entre a Z350 (2,30+0,62) que e a Filtek bulk fill 4,02(+1,85) usadas para o reparo, com a Tetric ceram bulk fill como base houve diferenças estatísticas quando comparadas a resina composta Filtek bulk fill 4,04(+1,07) e a Z350 (1,99+0,76). De acordo com os resultados obtidos foi possível verificar que, na maioria das comparações realizadas entre as resinas compostas avaliadas nesse estudo, as resinas compostas bulk fill obtiveram melhores valores de resistência a união quando unidas as próprias resinas compostas bulk fill e os piores valores quando receberam o reparo com a resina composta quando imersas em soluções ácidas e na água destilada, já na imersão em água/etano não foi possível observar diferenças estatisticamente significantes.

Este trabalho avaliou a influência da densidade de energia da pré-cura, e de diferentes tratamentos pós-cura na otimização das propriedades físicas (Resistência à Flexão e Dureza Knoop) de resinas compostas diretas, visando a possibilidade de indicação para restauraçoes indiretas. Foram usadas as resinas diretas Fillmagic, Concept, Glacier, Z100, Masterfill e W3D Master e as indiretas Solidex e Belleglass HP como controle. Para cada resina direta foram confeccionados 60 espécimes em barra (10x2x2mm), 30 irradiados em uma face e 30 nas duas faces (30 espécimes = 10 controle, 10 autoclave e 10 forno de luz). Para as resinas indiretas foram preparados 10 espécimes conforme processamento de seus fabricantes. 380 espécimes foram submetidos ao ensaio de resistência à flexão (Kratos). De cada condição experimental, 10 fragmentos foram usados para ensaio de microdureza Knoop (Shimadzu HMV-2). A análise de variância e o teste de Tukey demonstraram significância para resistência à flexão nos fatores Resina (p<0,001) e Tratamento (p=0,001) e na interação Resina x Tratamento (p=0,001). Para a microdureza Knoop os três fatores e as interações foram significantes: Resina (p=0,001); Face (p=0,001) Tratamento (p=0,017); Resina x Face (p=0,001); Resina x Tratamento (p=0,007); Face x Tratamento (p=0,001) e Resina x Face x Tratamento (p=0,024). A maior média de cada resina direta, independente da condição experimental, foi comparada às médias das resinas indiretas. Os resultados apontam que na resistência à flexão (Z100 = W3D = Fillmagic = Glacier) e (Z100 > Masterfill > Belleglass HP > Concept > Solidex). Na Dureza Knoop (Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill e Solidex). Conclusão: as propriedades físicas (resistência à flexão e dureza Knoop) não são obstáculos na indicação de resinas compostas de uso direto para restaurações indiretas / This study evaluated the influence of pre-cure energy density, and additional post-cure treatments in optimizing the physical properties (Flexural strength and Knoop microhardness) of direct resin composites with the aim at allowing their use for indirect restorations. Direct resin composites evaluated were Fillmagic, Concept, Glacier, Z100, Masterfill and W3D Master; indirect composites were Solidex and Belleglass HP. Sixty bar-shaped specimens (10x2x2mm) were prepared for each material, so that 30 of them were light-cured by one surface and 30 on both surfaces. From the 30 specimens of each group, 10 were control, 10 were submitted to additional autoclave and 10 to light oven treatment. Ten specimens were prepared with each indirect composite following the manufactures’ recommendations. The 380 specimens were submitted to flexural strength test (Kratos universal testing machine), and values obtained at fracture were reported. After that, 10 fragments were chosen for each experimental condition and assessed for Knoop microhardness (Shimadzu HMV-2). Data were submitted to analysis of variance and Tukey’s test at p<0.05. Statistically significant differences were found among flexural strength results regarding composite materials (p<0.001), treatments (p<0.001) and interactions (composite x treatment, p<0.001). Regarding Knoop microhardness, both three factors and their interactions were also significant: composite (p<0.001), surface (p<0.001) and treatment (p<0.017), composite x surface (p<0.001), composite treatment (p<0.001), surface x treatment (p<0.001) and composite x surface x treatment (p<0.024). The highest mean value for each direct composite, regardless of the experimental condition, was compared to the mean values obtained for the indirect materials. With regard to flexural strength, comparisons point out that Z100 = W3D = Fillmagic = Glacier and Z100 > Masterfill > Belleglass HP > Concept > Solidex, whereas for Knoop microhardness Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill and Solidex. Conclusion: considering the physical properties evaluated in this study, they are not an obstacle to the indication of direct composites for indirect restorations

O presente estudo avaliou in situ a influência de fatores da dieta associado ao uso de clorexidina na cor e na rugosidade superficial de diferentes resinas compostas (Z250® - 3M-ESPE e Filtek Supreme® - 3M-ESPE). Foram confeccionados 112 corpos-de-prova (6,0x2,0mm) que foram polidos com disco abrasivos Super Snap® (Shofu). O estudo foi constituído por duas fases de 5 dias cada, com um período de washout de 9 dias entre elas. Os corpos-de-prova de cada um dos materiais foram divididos entre 14 voluntários e montados em dispositivo palatino, na região dos pré-molares e molares superiores e instalados nos participantes para a realização dos bochechos e da ingestão do chá em cada uma das fases do experimento. De acordo com sorteio aleatório, metade dos voluntários utilizou, na primeira fase do experimento, solução de gluconato de clorexidina 0,12% (S1) e a outra metade dos voluntários realizou os bochechos com uma solução placebo (S2), de mesma composição da solução original, porém sem adição de gluconato de clorexidina 0,12%. Os bochechos foram realizados 2 vezes ao dia, por 1 minuto, durante 5 dias. Todos os voluntários, após o bochecho com gluconato de clorexidina 0,12% ou placebo ingeriram 200 mL de chá em ambas as fases. Na segunda fase do experimento, os corpos-de-prova foram substituídos por outros e os voluntários foram cruzados quanto à solução, de modo que todos usaram ambas às soluções. As leituras de cor, obtidas através de um colorímetro, e a rugosidade superficial, obtida por meio de um rugosímetro, foram realizadas imediatamente antes da fixação do espécime no aparelho intra-bucal e após 24 horas do término do período experimental. Os dados foram submetidos ao teste ANOVA e Tukey (p&le;0,05). Os resultados mostraram que: a) a solução S1obteve maiores médias de alteração de cor (&Delta;E*) que S2 enquanto que para os outros fatores e interações não houve diferença estatisticamente significante para esta variável; b) todos os fatores e respectivas interações, exceto a interação Solução x Material, sofreram variação de luminosidade (L*) significante estatisticamente; c) todos os fatores e respectivas interações, exceto a interação Material x Tempo, sofreram variação do parâmetro a* significantes estatisticamente; d) o fator Solução quando analisado isoladamente e a interação Tempo x Solução não obtiveram resultados estatisticamente diferentes para o parâmetro b* e; e) para a rugosidade superficial (Ra) apenas o fator Tempo foi estatisticamente significante. Conclui-se que: houve uma maior alteração de cor da resina composta quando se utiliza soluções a base de Clorexidina 0,12%; as resinas estudadas não influenciaram no comportamento da cor quando associado à Clorexidina 0,12% e chá preto; para os parâmetros L* a* e b* os fatores Solução, Material e Tempo tiveram efeito significante, exceto o fator Solução para o parâmetro b*; a utilização de Clorexidina durante 5 dias não influenciou na rugosidade superficial dos materiais estudados e; o tempo teve influencia sobre o aumento da rugosidade superficial. / This in situ study evaluated the influence of dietary factors in association with chlorhexidine on the color change (&Delta;E*) of two composites resins (Z250® - 3M-ESPE and Filtek Supreme® - 3M-ESPE). 112 discs (6.0x2.0mm) were fabricated and polished with Super Snap® discs (Shofu). The specimens were divided among 14 volunteers, and fitted onto intraoral devices and placed in the maxillary premolar and molar positions. Palatal intra-oral acrylic resin appliances were made for each volunteers in the experiment. In each appliance, two specimen of each materials was randomly fixed. This study was composed of two phases of 5 days each, with a washout period of 9 days between them. In the first phase, half of the volunteers chosen by random draw, used a 0.12% chlorhexidine solution (S1) and the other half used a placebo solution (S2). The mouthwashes were performed 2 times a day, for 1 min. each, for 5 days. In the second phase of the experiment, the specimens were replaced by others and the volunteers were crossed on the outcome. In both phases, after mouthwashes with S1 or S2, all volunteers ingested 200 mL of black tea for 10 minutes. The color change of all specimens before and after of the experimental period was measured by a colorimeter and the data were analyzed by two-way analysis of variance (ANOVA) and Tukey´s test (&alpha=.05). Subsequently, the surface roughness (Ra) of the specimens was evaluated using a profilometer, and the data were compared by two-way ANOVA followed by a Tukey multiple comparations test (&alpha;=.05). According to ANOVA: a) the S1 solution had the highest means of color change (&Delta;E*) that S2, while for the others factors and interactions no have statistically significant difference for this variable; b) all the factors and their interactions had significant statistically changes in lightness (L*), except for the Solution x Material interaction; c) all the factores and their interactions had significant statistically changes in parameter a*, except for the Material x Time interaction; d) the solution factor and Time x Solution interaction no had statistica different for the parameter b* and; e) for surface roughness (Ra) only the time factor was statistically significant. It was concluded that: there was an increase in color change of composite resin when using Chlorhexidine 0.12%; the resin did not influence on the color when associated with Chlorhexidine 0.12% and black tea; for parameters L * a * b * Solution, Material and Time factors had significant effect, except for the Solution factor for the parameter b *; the use of chlorhexidine for 5 days did not influence the surface roughness of the materials studied; and the time had a significant influence on increased surface roughness.

Made available in DSpace on 2014-08-20T14:30:17Z (GMT). No. of bitstreams: 1 Dissertacao_Daniela_Venturini.pdf: 913438 bytes, checksum: e17fa4ddbe1c025e3411319cac841d1e (MD5) Previous issue date: 2006-06-30 / This study evaluated the effects of immediate and delayed polishing on surface roughness (Ra), microhardness (KHN) and microleakage of a microfilled composite (Filtek A110) and a hybrid composite (Filtek Z250) restorations after one-year storage. Standardized cavities preparations were made in the buccal surface of 256 bovine teeth; half were restored with each composite. Immediately after photo activation finishing was carried out with #280 grit sandpaper. For each composite, the specimens were randomly allocated for two sub-groups. The first group (IM) was immediately polished, using three different systems (n=16): A- Sof-Lex; B- Flexicups; and C- a sequential technique using Flexicups, Jiffy Polishing Brush and Flexibuffs. The specimens were stored in saline solution at 37ºC. The second group (DE) was stored for two weeks and then polished with the same systems. Part of the specimens had their surface properties analyzed at the baseline, and the remaining specimens were stored for one-year in distilled water at 37ºC. Five readings per specimen were taken for each specimen regarding surface roughness and microhardness. After immersion in basic fuchsin, microleakage was evaluated (X40) using standardized scores. Data were analyzed at significance level of 0.05 with analysis of variance and a SNK test (surface roughness and microhardness) or with Mann-Whitney and Kruskal-Wallis (microleakage). For comparison between baseline and one-year Student´s t test (Ra) and Mann-Withney (microleakage) were carried out. After one-year, in general microfilled composite specimens showed lower roughness and hardness. No difference regarding microleakage was observed among different groups, but better sealing was observed in enamel margins. The sequential technique provided the lowest roughness and the Sof-Lex the lowest hardness in the most of the experimental conditions. Aging increased composite roughness. Immediate polishing showed similar or better performance than delayed polishing for microleakage and surface roughness, but this was not observed for microhardness, except in sequential technique groups / Este estudo avaliou os efeitos do polimento imediato e mediato na rugosidade média superficial (Ra), dureza Knoop (KHN) e microinfiltração de um compósito microparticulado (Filtek A110) e um híbrido (Filtek Z250), após um ano de armazenagem dos espécimes. Preparos padronizados de 3mm mesio-distais, 3mm inciso-cervicais e 2mm de profundidade foram realizados na face vestibular de 256 incisivos bovinos, metade destes foi restaurada com cada tipo de compósito. Imediatamente após a fotoativação realizado o acabamento com lixa d água de granulação 280. Os espécimes restaurados com cada compósito foram divididos em dois grupos. O primeiro grupo (IM) foi polido imediatamente após o acabamento, usando três sistemas diferentes (n=16): A- Sof-Lex (3M-ESPE), B- FlexiCups (Cosmedent), C- (técnica seqüencial)- a seqüência de FlexiCups, Jiffy Polishing Brush (Ultradent) e FlexiBuffs (Cosmedent). Os espécimes foram então armazenados em solução salina a 37ºC. O segundo grupo (ME) foi armazenado por duas semanas e então polido com os mesmos sistemas. Parte dos espécimes foi analisada numa primeira etapa do experimento e o restante ficou armazenado por um ano em água destilada a 37ºC. Cinco leituras por espécimes foram realizadas para Ra e KHN. Após imersão em fucsina básica realizou-se o teste de penetração de corante sendo após analisado sob aumento (40x) usando escores padrão. Os dados foram verificados através de Análise de Variância e teste SNK (Ra e KHN). Também foram utilizados os testes de Mann-Whitney ou Kruskal-Wallis (microinfiltração). Para comparação com os dados baseline foram utilizados os testes t de Student (Ra) e Mann-Withney (infiltração marginal). Todos os testes foram executados com significância de 5%. Após um ano de armazenagem os espécimes do compósito A110 apresentaram significativamente menor rugosidade e menor dureza. A técnica seqüencial promoveu a menor rugosidade e os discos Sof-Lex a menor dureza, essas diferenças foram estatisticamente significantes. Os escores de infiltração marginal foram semelhantes entre os grupos. Após um ano de armazenagem os espécimes apresentaram um aumento significativo na rugosidade. O polimento IM mostrou-se igual, ou melhor, que o ME tanto para a infiltração marginal como para a rugosidade superficial para a maioria dos grupos analisados, no entanto tal fato não foi observado quanto à dureza superficial, exceto quando foi utilizada a técnica seqüencial

Este estudo investigou propriedades mecânicas do compósito silorano em dois capítulos. Capítulo A Objetivo: avaliou a resistência de união entre a estrutura dental e um composto à base de silorano, após o clareamento dental. Método: Sessenta incisivos bovinos foram distribuídos aleatoriamente em seis grupos (n=10), de acordo com o período de armazenamento entre o tratamento clareador e a restauração com compósito à base de silorano. O tratamento clareador com peróxido de carbamida à 10% seguiu um protocolo de quatro horas diárias durante duas semanas. Após o período de armazenamento, as cavidades foram preparadas e restauradas com uma resina composta à base de silorano. Resultado: Após o tratamento clareador e os devidos períodos de armazenagem, nenhuma diferença significativa foi observada nos resultados de resistência adesiva (p>0,05). Conclusão: a resistência adesiva entre o compósito à base de silorano e o substrato dental não foi afetada pelo tratamento clareador com 10% de peróxido de carbamida. Capítulo B Objetivo: avaliou a resistência coesiva entre as camadas de resinas compostas à base metacrilato e silorano e a microdureza Knoop (KHN) após ciclos de erosão e abrasão. Método: Para a resistência coesiva, vinte amostras foram feitas com cada compósito, metacrilato (MC) e silorano (SC) (n=10). As amostras foram divididas em quatro grupos, de acordo com tipo e quantidade de incrementos de resina composta. O teste de microtração foi realizado 24h após a confecção das amostras. Para a análise da KHN, após os ciclos de erosão/abrasão, foram produzidas quarenta amostras de cada resina composta testada (MC e SC). As amostras foram distribuídas em oito grupos (n=10) de acordo com tipo de compósito e tipo de bebida envolvida no processo de erosão (controle, suco de laranja, Smirnoff Ice e Gatorade) e abrasão com dentifrício de alta abrasividade. Resultado - não foram observadas diferenças na resistência coesiva entre as camadas incrementais dos compósitos estudados (p> 0,05). Os resultados de KHN dos grupos MC apresentaram menor valor para o Smirnoff Ice (p<0,05), no entanto, para os grupos SC nenhuma diferença foi observada (p>0,05). Conclusão: a resistência coesiva entre as camadas incrementais de ambos compósitos testados não foi afetada pelo oxigênio; as bebidas, em conjunto com a abrasão, não tiveram capacidade de interferir na KHN dos compósitos testados, exceto o Smirnoff Ice para o MC. / This study investigated the mechanical properties of the silorane based composite in two chapter. Chapter A Aim: evaluated the bond strength between the dental structure and a silorane-based composite (SC), after bleaching treatment. Method: Sixty bovine incisors were randomly distributed into six groups (n=10) according to the storage period between the bleaching treatment and the SC restoration. The bleaching treatment followed a protocol of 10% carbamide peroxide with one application during four hours per day during two weeks. After the period of storage, cavities were made and filled with SC. Results: After the periods of bleaching treatment, no significant difference was observed in the results of push out bond strength between the SC and the bleached substrate (p>0.05). Conclusion: the bond strength between the SC and the dental substrate was not affected by the bleaching treatment with 10% carbamide peroxide. Chapter B Aim: evaluated the bond strength between incremental layers of methacrylate and silorane composites and the micro hardness Knoop (KHN) after erosion and abrasion cycles. Method: for the bond strength, twenty samples were made with each composite, methacrylate (MC) and silorane (SC) (n=10). The samples were divided into four groups according composite type and quantity of increments. The microtensile test was performed 24 h after the samples were made. For the KHN test, after erosion/abrasion process, forty samples of each composite tested (MC and SC) were made. The samples were distributed into eight groups (n=10) according composite type and beverage type involved in the erosion process (control, orange juice, Smirnoff Ice and Gatorade) and abrasion with high abrasivity detifrice. Results: no differences were observed in the bond strength between increment layers when the same composite was analyzed (p>0.05). The results of KHN in the MC groups showed smaller value for the Smirnoff Ice (p<0.05), however for the SC groups no differences were found (p>0.05). Conclusion: the bond strength between incremental layers of SC was not affected by the oxygen; the others beverages, jointly with the abrasion, have no capacity to interfere in the KHN of the composites tested.

As lesões cervicais não cariosas (LCNCs) são definidas pela perda de estrutura dental na junção cemento/esmalte que envolve três mecanismos de estresse mecânico (tensão), atrito (fricção) e erosão (degradação química).. Existem tratamentos preventivos e dessensibilizantes para o principal sintoma das LCNCs, a hipersensibilidade dentinária cervical (HDC), porém, em casos que há perda de estrutura dental maior que 1mm é necessário realizar uma intervenção restauradora. Dessa forma, o objetivo deste estudo foi avaliar a resistência de união da dentina erodida e abrasionada modificada com diferentes pré-tratamentos e posteriormente restauradas com resina composta, através do teste de microtração. Para tanto, foram selecionados 40 molares humanos íntegros, que tiveram as porções oclusais seccionadas até exposição da dentina. Os espécimes passaram por desafio erosivo e abrasivo em uma ciclagem de 5 dias. Após os desafios, os espécimes receberam os tratamentos de superfície (n=10): G1: controle sem tratamento; G2: tratamento de superfície com ponta diamantada; G3: jateamento com óxido de alumínio, G4: ciclagem com enxaguatório fluoretado Elmex Erosion. Feito isso os espécimes foram restaurados, seccionados em palitos e submetidos ao teste de microtração em uma máquina universal de ensaios a 0,5mm/min. Para a analise estatística, foi utilizado o teste paramétrico de análise de variância (ANOVA) um fator e o teste auxiliar de Tukey. Foi observado que não houve diferença entre os tratamentos com ponta diamantada, óxido de alumínio e enxaguatório fluoretado. O único grupo a se diferenciar dos demais foi o grupo controle que apresentou valores de resistência de união inferiores. Dentro das limitações de um trabalho in vitro, conclui-se que os tratamentos de superfície estudados são procedimentos indicados para melhorar a adesão dental frente à necessidade de restaurar uma LCNC. / Non-carious cervical lesions (NCCLs) are defined by loss of dental structure at the cement/enamel junction involving three mechanisms of mechanical stress (tension), friction and erosion (chemical degradation). There are preventive and desensitizing treatments for the the main symptom of NCCLs, cervical dentin hypersensitivity (CDH), but in cases where there is loss of tooth structure greater than 1mm, a restorative intervention is necessary. Thus, the objective of this study was to evaluate the bond strength of the eroded and abraded dentin modified with different pre-treatments and later restored with composite resin, through the microtensile test. For this, 40 sound human molars were selected, which had the occlusal portions sectioned until exposure of the dentin. The specimens underwent erosive and abrasive challenge in a 5-day cycling. After the challenges, the specimens received the surface treatments (n = 10): G1: control without treatment; G2: surface treatment with diamond tip; G3: sandblasting with aluminum oxide, G4: cycling with fluoridated rinse Elmex Erosion. After this, the specimens were restored, sectioned on sticks and subjected to the microtensile test in a universal test machine at 0.5mm/min. For statistical analysis, the parametric analysis of variance (ANOVA) one factor and the Tukey auxiliary test were used. It was observed that there was no difference between treatments with diamond tip, aluminum oxide and fluoride. The only group to differentiate from the others was the control group that presented inferior bond strength values. Within the limitations of an in vitro work, it is concluded that the surface treatments studied are procedures indicated to improve dental adhesion in view of the need to restore NCCL.

O presente estudo in vitro analisou o efeito de 3 sucos de fruta com baixo pH (suco de cupuaçu, taperebá e laranja), e saliva artificial (controle) sobre materiais restauradores indicados em lesões cervicais não cariosas: resina composta nanoparticulada (Filtek Z350 XT), cimento de ionômero de vidro resino modificado (Vitremer) e um cimento de ionômero de vidro convencional (Fuji II). Os materiais foram avaliados, quantitativamente, quanto à alteração de: peso, rugosidade superficial e microdureza superficial, e qualitativamente, por microscopia eletrônica de varredura (MEV). Foram confeccionados 144 corpos de prova para cada teste quantitativo (n=12) e 45 para o MEV (n=3), de (8mm de diâmetro x 2mm de altura). Os corpos de prova foram preparados, mantidos em saliva artificial por 24 h à 37º C, receberam acabamento em politriz, e em seguida foram realizadas as leituras iniciais. Durante um período de 10 dias consecutivos, os corpos de prova foram submetidos ao desafio erosivo (nos respectivos sucos de frutas) durante 30 minutos três vezes ao dia, totalizando 90 minutos/dia e mantidos em saliva artificial entre os intervalos. Após o período de ciclagem erosiva, foram realizadas as leituras finais. Os resultados obtidos foram submetidos ao teste t, ANOVA e Tukey. As médias de alteração entre os valores de peso finais e iniciais demonstraram diferença significativa (p<0,01) nos materiais estudados e em todos os sucos estudados, com exceção do Vitremer quando imerso no suco de taperebá (p>0,01). As médias de alteração entre os valores de rugosidade superficial final e inicial demonstraram diferença significativa (p<0,01) para todos os materiais estudados em todos os sucos, exceto a Filtek Z350 XT no grupo controle que não apresentou diferença significativa (p>0,01). A comparação entre os valores de microdureza final e inicial demonstrou diferença significativa (p<0,01) na microdureza dos materiais estudados em todos os meios de imersão, inclusive no grupo controle. De um modo geral o suco de taperebá foi o que provocou a maior alteração na superfície dos materiais restauradores quanto ao peso, rugosidade, microdureza e na microscopia eletrônica de varredura. A resina composta Filtek Z350 XT foi o material restaurador que menos sofreu alterações de superfície. Concluiu-se que os sucos das frutas estudados são capazes de alterar os materiais restauradores, sendo que a resina composta foi o material que sofreu menor alteração. / This in vitro study examined the effects of 3 fruit juices with low pH (cupuaçu, taperebá and orange) and artificial saliva (control) upon restorative materials indicated in noncarious cervical lesions: nanoparticle composite resin (Filtek Z350 XT), resin-modified glass ionomer cement (Vitremer) and a glass ionomer cement (Fuji II). The materials were evaluated quantitatively as for alterations in weight, surface roughness and surface microhardness, and qualitatively by scanning electronic microscopy (SEM). 144 specimens were prepared for each quantitative test (n = 12) and 45 for the SEM (n = 3), of (8mm diameter x 2mm height). The specimens were prepared, stored in artificial saliva for 24 hours at 37º C, were finished in a polishing machine, and then the initial readings were performed. During a period of 10 consecutive days, the specimens were subjected to erosive challenge (in the respective juices) for 30 minutes, three times a day, and totaling 90 minutes/day and kept in artificial saliva between intervals. After the erosive cycling period, the final readings were taken. The data were analyzed using t test, ANOVA and Tukey.Test The average alterations between the values of initial and final weight showed significant difference (p < 0.01) in the material studied and all the juices studied, except for Vitremer when immersed in taperebá juice (p > 0.01). The average alterations between the values of initial and final surface roughness showed a significant difference (p < 0.01) for all materials studied in all juices, except for Filtek Z350 XT, in the control group, that showed no significant differences (p > 0.01). The comparison between the values of initial and final microhardness showed a significant difference (p < 0.01) in microhardness of the materials studied in all immersion means, including the control group. In general, taperebá juice was the one that caused the biggest alterations in the surface of restorative materials with respect to weight, roughness, hardness and scanning electronic microscopy. The composite resin Filtek Z350 XT was the restorative material that suffered less surface alterations. It was concluded that the fruit juices studied are capable of altering the restorative materials, and composite resin was the material that has undergone minor changes.