Submitted by Caroline Xavier (caroline.xavier@pucrs.br) on 2017-05-05T17:20:11Z No. of bitstreams: 1 TES_FERNANDO_JOSE_FAVERO_PARCIAL.pdf: 219648 bytes, checksum: c82c65601bd3d6d321aa7ab11b1a88c2 (MD5) / Made available in DSpace on 2017-05-05T17:20:11Z (GMT). No. of bitstreams: 1 TES_FERNANDO_JOSE_FAVERO_PARCIAL.pdf: 219648 bytes, checksum: c82c65601bd3d6d321aa7ab11b1a88c2 (MD5) Previous issue date: 2017-01-20 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Objetivos: 1) Avaliar ? resist?ncia ? fratura de molares endodonticamente tratados com preparos cavit?rios MOD e restaurados com Riva light cure (RLC) ou Riva Silver (RS) com e sem a presen?a de pino de fibra de vidro transfixado associado ? resina Bulk Fill Flow; 2) Avaliar o padr?o de fratura ap?s o ensaio mec?nico. Materiais e M?todos: Cinquenta terceiros molares supeiores extra?dos foram divididos em 5 grupos (n=10 por grupo): H?gidos (H); Preparo MOD (MOD) + Tratamento endod?ntico (TE) + cimento de ion?mero de vidro Riva Light Cure (GI); MOD + TE + cimento de ion?mero de vidro Riva Silver (GIS); MOD + TE + resina Bulk Fill Flowable (BFF) + pino de fibra de vidro horizontal (TFP) + RLC (GIP); MOD + TE + BFF + TFP + RS (GISP). Os preparos cavit?rios MOD e os tratamentos endod?nticos foram realizados em todos os grupos, exceto os h?gidos. A face vestibular e palatina dos grupos (GIP) e (GSIP) receberam a transfixa??o horizontal do pino de fibra de vidro seguido da inser??o da resina composta Bulk Fill Flow, Riva light cure ou Riva Silver de acordo com os grupos de estudo. Os dentes foram submetidos ao teste de resist?ncia ? fratura em uma m?quina de ensaio universal. O tipo de fratura ap?s o ensaio foi classificado em: fratura em assoalho pulpar (condenados) ou em c?spide (recuper?vel). Resultados: M?dias em Newtons(N) seguidas de mesma letra n?o apresentam diferen?a estat?stica para ANOVA e Tukey (P<0,05%): H 3955,6NA; GI 1215,6NB; GIS 1195,8NB; GIP 2064,6NC GISP 2386,5NC. O padr?o de fratura foi similar entre os grupos testados com 54% de fraturas recuper?veis e 46% para dentes condenados. Conclus?es: A associa??o do pino de fibra de vidro, resina Bulk Fill flow, Riva light cure (GIP) ou Riva Silver (GISP) recuperou, respectivamente 52,19%, e 60,23% da resist?ncia ? fratura de um dente h?gido, sendo, em m?dia, 2x maior que os resultados dos grupos (GI) e (GIS). / Objetivos: 1) Avaliar a resist?ncia ? fratura de terceiros molares com preparos cavit?rios MOD tratados endodonticamente e restaurados com resina composta de forma direta, cimento de ion?mero de vidro modificado por resina ou cimento de ion?mero de vidro tipo silver com e sem a presen?a de pino de fibra de vidro transfixado horizontalmente em molares endodonticamente tratados; 2) Avaliar o padr?o de fratura dos dentes ap?s o ensaio de resist?ncia ? fratura. Materiais e M?todos: Setenta molares h?gidos extra?dos foram embutidos em resina acr?lica e divididos em 7 grupos (n=10 por grupo): H?gidos (H); preparo cavit?rio (MOD) + Tratamento endod?ntico (TE) + restaura??o com resina composta Z250 (RC); MOD + TE + cimento de ion?mero de vidro Riva Light Cure (GI); MOD + TE + Cimento de ion?mero de vidro Riva Silver (GIS); MOD + TE + pino de fibra de vidro transfixado (TFP) + RC (RCP); GI + TFP (GIP); GIS + TFP (GISP). Os preparos cavit?rios MOD foram padronizados com largura 2/3 da dist?ncia vest?bulo-lingual, tendo como refer?ncia a ponta das respectivas c?spides, e profundidade ocluso-gengival de 4mm permanecendo 2mm acima do limite amelo-cement?rio. Foram realizados tratamentos endod?nticos em todos os grupos, exceto para o grupo dos dentes h?gidos. Os grupos (RCP), (GIP) e (GSIP) receberam pinos de fibra de vidro transfixados horizontalmente e ap?s foram restaurados com Z250, Riva Light Cure ou Riva Silver, respectivamente. Ap?s, os dentes foram submetidos ao ensaio de resist?ncia ? fratura em uma m?quina de ensaio universal. Ap?s realiza??o dos ensaios, os dentes foram inspecionados quanto ao tipo de fratura e classificados em: Fratura em assoalho pulpar (N?o recuper?vel) ou C?spide (Recuper?vel). Resultados: M?dias seguidas de mesma letra n?o apresentam diferen?a estat?stica para ANOVA e Tukey (p>0,05): (H) 3901NA; (RC) 1232NB; (GI) 1251NB; (GIS) 1259NB; (GISP) 2168NC; (RCP) 2230NC; (GIP) 2292NC. O padr?o predominante de fratura foi em c?spide. Conclus?es: A utiliza??o do pino de fibra de vidro restaurado com resina composta (RCP), Riva Light Cure (GIP) e Riva Silver (GISP) recuperou, respectivamente, 57,16%, 58,75% e 55,56% da resist?ncia ? fratura de um dente h?gido, enquanto os dentes restaurados sem pino recuperaram para os grupos (RC), (GI) e (GIS), 31,53%, 32,07% e 34,84%. O progn?stico predominante foi recuper?vel para todos os grupos, exceto (GIS). / Objectives: 1) To assess the fracture strength of third molars with endodontically treated MOD cavity preparations and restored with direct composit resin, resin modified glass ionomer cement or silver glass ionomer cement with and without the presence of fiberglass post transfixed horizontally in endodontically treated molars; 2) To assess the fracture pattern of the teeth after the fracture resistance test. Materials and Methods: Seventy extracted healthy third molars were embedded in acrylic resin and divided into 7 groups (n = 10 per group): Healthy (H); Cavity preparation (MOD) + Endodontic treatment (ET) + restoration with Z250 composit resin (RC); MOD + TE + glass ionomer cement Riva Light Cure (GI); MOD + TE + Riva Silver glass ionomer cement (GIS); MOD + TE + transfixed fiberglass post (TFP) + RC (RCP); GI + TFP (GIP); GIS + TFP (GISP); MOD cavity preparations were standardized with a width of 2/3 fo the vestibular-lingual distance, with reference to the tip of the respective cusps, and occlusal-gingival depth of 4mm remaining 2mm above the cemento-enamel junction. Endodontic treatments were performed in all groups, except for the healthy teeth group. The groups (RCP), (GIP) and (GISP) received horizontally transfixed fiberglass posts and afterwards were restored with Z250, Riva Light Cure or Riva Silver, respectively. Afterwards, the teeth were submitted to the fracture strength test in a universal test machine. After the tests were performed, the theeth were inspected for the type of fracture and classified as: Fracture in the pulpal floor (Not-recoverable) or cusps (Recoverable) Results: Averages followed by the same letter did not present statistical difference for ANOVA and Tukey (p>0,05): (H) 3901NA; (RC) 1232NB; (GI) 1251NB; (GIS) 1259NB; (GISP) 2168NC; (RCP) 2230NC; (GIP) 2292NC. The predominant pattern of fracture was cusps. Conclusions: The use of the fiberglass post restored with composite resin (RCP), Riva Light Cure (GIP) and Riva Silver (GISP) recovered, respectively 57.16%, 58.75% and 55.56% of resistance to the fracture of a healthy tooth, whereas the restored teeth without post recovered for the groups (CR), (GI) and (GIS), 31.35%, 32.07% and 34.84%. The predominant prognosis was recoverable for all groups, except (GIS). / Objetivos: 1) To assess the fracture strength of endodontically treated molars with MOD cavity preparations and restored with Riva Light Cure (RLC) ou Riva Silver (RS) with and without the presence of transfixed fiberglass post associated with Bulk Fill Flow resin; 2) To assess the fracture pattern after the mechanical test. Materials and Methods: Fifty third molars extracted were divided into 5 groups (n = 10 per group): Healthy (H); Preparation MOD (MOD) + Endodontic Treatment (TE) + glass ionomer cement Riva Light Cure (GI); MOD + TE + Riva Silver glass ionomer cement (GIS); MOD + TE + BulkFill Flowable resin (BFF) + horizontal fiberglass post (TFP) + RLC (GIP); MOD + TE + BFF + RS (GISP). MOD cavity preparations and endodontic treatments were performed in all groups, except for the healthy ones. The vestibular and palatine face of the (GIP) and (GISP) groups received the horizontal transfixation of the fiberglass post followed by the insertion of the composite resin Bulk Fill Flow, Riva Light Cure or Riva Silver according to the study groups. The teeth were submitted to the fracture strength test in a universal test machine. The type of fracture after the test was classified as: pulpal floor fracture (condemned) or cuspal fracture(recoverable). Results: Averages in Newtons (N) followed by the same letter did not present statistical difference for ANOVA and Tukey (P<0,05%): H 3955,6NA; GI 1215,6NB; GIS 1195,8NB; GIP 2064,6NC GISP 2386,5NC. The fracture pattern was similar between the groups tested with 54% of recoverable fractures and 46% for condemned teeth. Conclusions: The association of fiberglass post, BulkFill Flowable resin, Riva Light Cure (GIP) ou Riva Silver (GISP) recovered respectively 52.19% and 60.23% of the fracture resistance of a healthy tooth, being, on overage, 2x greater than the results of the groups (GI) and (GIS).

Submitted by Caroline Xavier (caroline.xavier@pucrs.br) on 2017-06-26T14:53:16Z No. of bitstreams: 1 TES_DIMAS_JOAO_RODRIGUES_NETO_PARCIAL.pdf: 405454 bytes, checksum: d48967a61777e3e773d5a2112997ee13 (MD5) / Made available in DSpace on 2017-06-26T14:53:16Z (GMT). No. of bitstreams: 1 TES_DIMAS_JOAO_RODRIGUES_NETO_PARCIAL.pdf: 405454 bytes, checksum: d48967a61777e3e773d5a2112997ee13 (MD5) Previous issue date: 2017-01-19 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / For a satisfactory clinical performance, pre-fabricated Co-Cr cylinders must have metallurgical compatibility to Co-Cr based cast alloys. A uniform interface with adequate union and resistance, with absence of interfacial reaction and porosities must be obtained. The present in vitro study aimed to evaluate the metallurgical compatibility at the interface between pre-fabricated Co-Cr cylinders and alloys for Co-Cr compound casting applying different casting techniques. In manuscript 2 the metallurgical compatibility and the interface between implant and alloy cylinders were evaluated for Co-Cr casting with different melting temperatures. Methodology: Three pre-fabricated Co-Cr prosthetic implant cylinders (Neodent, Pi-Br?nemark, Dentium) were subjected to casting with Co-Cr alloy using different casting techniques (Flame Torch, Induction / Centrifugation, Induction / Vacuum). Optical microscopy and Scanning Electron Microscopy (SEM) were used to characterize the obtained microstructures. The elementary composition of the cylinders and diffusion characteristics in the interfacial region between molten alloy and cylinder were determined by dispersive energy spectroscopy (EDS). Vickers microhardness was measured at interface, cylinder and cast alloy. The ANOVA and Tukey test were used to evaluate microhardness values. In the manuscript 2 cylinders based on Co-Cr were overfused with alloys with different melting temperatures and all microstructural analysis and microhardness tests were performed. Results: In the manuscript 1 a union between pre-fabricated cylinders and Co-Cr based alloys was observed microstructurally. An ideal interface was obtained with absence of interfacial reaction or significant porosities with the casting with the induction techniques (centrifugation and vacuum), but excess of porosities and failures were observed with the Torch casting technique. In manuscript 2 a microstructural bond was observed between the alloys and the cylinder, evidencing that both high melt alloy and low melt alloy presented compatibility with the Co-Cr cylinder. Microhardness values, both in manuscript 1 and in manuscript 2 also proved to form a satisfactory interface. Conclusions: It was concluded from manuscript 1 and 2 that both high and low melt temperature Co-Cr have metallurgical compatibility to pre-fabricated Co-Cr cylinders, showing an ideal interface. However, the technique of casting applied is relevant, and the torch technique has been shown to be less indicated due to the lack of standardization of the obtained results. / Para um bom desempenho clinico, cilindros de pilares pr? fabricados de Co-Cr devem apresentar compatibilidade metal?rgica a ligas de sobrefundi??o a base de Co-Cr. Uma interface uniforme com adequada uni?o e resist?ncia, com aus?ncia de rea??o interfacial e porosidades devem ser obtidas. O presente estudo, in vitro, objetivou atrav?s do manuscrito 1 avaliar a compatibilidade metal?rgica na interface entre cilindros pr? fabricados de Co-Cr e ligas para sobrefundi??o de Co-Cr com diferentes t?cnicas de fundi??o. No manuscrito 2, foi avaliado a compatibilidade metal?rgica e a interface entre cilindro de implante e ligas para sobrefundi??o de Co-Cr com diferentes temperaturas de fus?o. Metodologia: Tr?s cilindros pr?-fabricados para pr?tese sobre implantes em Co-Cr (Neodent, Pi-Br?nemark, Dentium) foram sorefundidos com liga de Co-Cr com diferentes t?cnicas de fundi??o (Ma?arico, Indu??o/centrifuga??o, Indu??o/v?cuo). Microscopia ?ptica e Microscopia eletr?nica de varredura (MEV) foram usadas para caracteriza??o das microestruturas. A composi??o elemental dos cilindros e caracter?sticas de difus?o na regi?o interfacial entre liga fundida e cilindro foram determinadas atrav?s de espectroscopia por energia dispersiva (EDS). Microdureza de Vickers foi aplicada na interface, cilindro e liga fundida. Foi aplicado o teste de ANOVA e Tukey para avalia??o dos valores microdureza. No manuscrito 2, cilindros a base de Co-Cr foram sobrefundidos com ligas com diferentes temperaturas de fus?o e foi realizada toda analise microestrutural e testes de microdureza. Resultados: No manuscrito 1 observou-se microestruturalmente uma uni?o entre cilindros pr? fabricados e ligas a base de Co-Cr. Foi obtida uma interface ideal com aus?ncia de rea??o interfacial ou porosidades significantes com a fundi??o com as t?cnicas por indu??o (centrifuga??o e v?cuo), por?m excesso de porosidades e falhas foram observados com a t?cnica de fundi??o ? ma?arico. No manuscrito 2 observou-se uma uni?o microestrutural entre as ligas e o cilindro avaliado, evidenciando que tanto liga de alta fus?o, quanto de baixa fus?o apresentam compatibilidade ao cilindro de Co-Cr. Valores de microdureza, tanto no manuscrito 1 como no manuscrito 2 tamb?m comprovaram a forma??o de uma interface satisfat?ria. Conclus?es: Concluiu-se atrav?s do manuscrito 1 e 2 que ligas de alta e baixa temperatura de fus?o a base de Co-Cr apresentam compatibilidade metalurgica a cilindros pr? fabricados de Co-Cr apresentando uma interface ideal. Por?m, a t?cnica de fundi??o aplicada ? relevante, sendo que a t?cnica ? ma?arico se mostra a menos indicada devido a falta de padroniza??o dos resultados obtidos.

Submitted by Jadson Francisco de Jesus SILVA (jadson@uefs.br) on 2018-07-10T22:51:13Z No. of bitstreams: 1 Santos, Cristiane Brand?o.pdf: 1618648 bytes, checksum: 207f755363fb3b9a7dca89df5c0b2fbc (MD5) / Made available in DSpace on 2018-07-10T22:51:13Z (GMT). No. of bitstreams: 1 Santos, Cristiane Brand?o.pdf: 1618648 bytes, checksum: 207f755363fb3b9a7dca89df5c0b2fbc (MD5) Previous issue date: 2017-06-02 / Funda??o de Amparo ? Pesquisa do Estado da Bahia - FAPEB / Introduction: Dental fluorosis is an alteration in dental enamel mineralization, related to fluoride (F?) intake. Objectives: To investigate the impact of F? addition in toothpaste on the prevalence of dental fluorosis and to compare methods for F? determination in samples of diet and toothpaste. Methods: Two studies were developed: 1) systematic review of the literature, with meta-analysis, performed by two reviewers independently searching the four electronic databases (MEDLINE / PubMed; MEDLINE / Ovid; Bireme and Web of Science). The quality of articles eligible for Strengthening the Reporting of Observational Studies in Epidemiology (STROBE), and by the classification modified by Irani (2013); 2) a laboratory study that determined the F? concentration in the diet and dentifrice samples using two extraction methods: HMDS facilitated microdiffusion and hydrolysis in 0.01M HCl at times 30, 60 and 120 min of incubation. For analysis of the data, the one-way ANOVA test was applied. Results: 1) In the systematic review, eleven articles were eligible, and, when STROBE was applied, the number of items included ranged from 14 and 19, with an average of 16.3 and a standard deviation of 4.03; in the analysis of the classification modified by Irani (2013), two articles were classified as high quality and the rest of intermediate quality; 2) the method of extraction using 0.01M HCl, in the time 30 min, resulted in similar values to that expected by inactivation of 50% of the dentifrice?s F?. And in time 120 min resulted in similar values to HMDS facilitated microdiffusion. Conclusion: The majority of eligible articles in the systematic review found an association between the age of fluoride toothpaste use and dental fluorosis, but the prevalent severity of fluorosis was very mild, ie it does not imply dental fluorosis as a public health problem. It's the method of F? extraction using 0.01M HCl, in the experimental study, was promising to be used in evaluation of F? in dietary intake and dentifrices. / Introdu??o: Fluorose dent?ria ? uma altera??o na mineraliza??o do esmalte dental relacionada ? ingest?o de fluoreto (F?). Objetivos: Investigar o impacto da adi??o de F? aos dentifr?cios na preval?ncia de fluorose dent?ria e comparar metodologias para a determina??o da concentra??o de F? em amostras de dieta e dentifr?cio. M?todos: Dois estudos foram desenvolvidos: 1) revis?o sistem?tica da literatura, realizada por dois revisores que buscaram, de forma independente, os estudos em quatro bases de dados eletr?nicas (MEDLINE/PubMed; MEDLINE/Ovid; Bireme e Web of Science). Avaliou-se a qualidade dos artigos eleg?veis pelo Strengthening the Reporting of Observational Studies in Epidemiology (STROBE) e pela classifica??o modificada por Irani (2013); 2) experimento laboratorial que determinou a concentra??o de F- nas amostras de dieta e dentifr?cio utilizando-se dois m?todos de extra??o: microdifus?o facilitada por HMDS e hidr?lise em HCl 0,01M com tempos 30, 60 e 120 minutos de incuba??o. Para an?lise dos dados foi aplicada o teste ANOVA um crit?rio. Resultados: 1) Na revis?o sistem?tica, onze artigos foram eleg?veis, e quando aplicado o STROBE o n?mero de itens inclu?dos variou entre 14 e 19, com m?dia de 16,3 e desvio padr?o 4,03; na an?lise da classifica??o modificada por Irani (2013), dois artigos foram classificados como de alta qualidade e o restante de qualidade intermedi?ria. 2) A t?cnica de extra??o em HCl 0,01M no tempo 30 minutos resultou em valores semelhantes ao esperado pela inativa??o de 50% do F? do dentifr?cio. E o tempo de 120 minutos resultou em resultados semelhantes ? t?cnica de microdifus?o facilitada por HMDS. Conclus?o: A maoiria dos artigos eleg?veis da revis?o sistem?tica encontraram associa??o entre idade do uso do dentifr?cio fluoretado e fluorose dental, por?m a severidade prevalente da flurose foi o grau muito leve, ou seja, n?o implica considerar fluorose dental como um problema de sa?de p?blica. E o estudo laboratorial sugere que o m?todo de extra??o de F? em HCl 0,01M ? promissor para ser utilizado em trabalhos de avalia??o da ingest?o de F? pela dieta e dentifr?cios.

Made available in DSpace on 2015-04-14T14:49:57Z (GMT). No. of bitstreams: 1 445318.pdf: 1162939 bytes, checksum: bc5afbd6b0e554990f5c89cef7859875 (MD5) Previous issue date: 2012-08-10 / The occlusal plane is an imaginary plane that passes between the upper and lower dental arches and is used as reference for assessments in several kinds of dental treatment. The correct orientation of this plan is important for a successful treatment because it is from this orientation, for example, that a surgery can be planned. The treatment planning is often done, using virtual or physical models (plaster) to replicate the dental arches and the patient's teeth. This replication, however, reach the problem of how to register the patient?s occlusal plane orientation and transport it to the model. Motivated by this problem this paper has developed a process to obtain both an anthropometric reference, as the angles relating the occlusal plane to this reference. The process presented in this work is based on the application of computer vision techniques on two images of the patient's head, one from the front and another from the profile. It also presents a method to transport this information to a plaster model and virtual / O plano oclusal ? um plano imagin?rio que passa entre as arcadas dent?rias inferior e superior e ? utilizado como refer?ncia para avalia??es em diversos tipos de tratamentos odontol?gicos. A correta orienta??o deste plano ? importante para o sucesso do tratamento pois ? a partir deste, por exemplo, que uma cirurgia pode ser planejada. O planejamento dos tratamentos ? feito, com muita frequ?ncia, utilizando-se modelos f?sicos (de gesso) ou virtuais que replicam as arcadas dent?rias e os dentes do paciente. Esta replica??o, entretanto, esbarra no problema de como registrar no paciente a orienta??o do plano oclusal e transport?-la para o modelo. Motivado por este problema o presente trabalho desenvolveu um processo para obter tanto uma refer?ncia antropom?trica, quanto os ?ngulos que relacionam o plano oclusal ? esta refer?ncia. O processo apresentado neste trabalho ? baseado na aplica??o de t?cnicas de vis?o computacional sobre duas imagens fotogr?ficas da cabe?a do paciente, uma de frente e outra de perfil. Tamb?m ? apresentado um m?todo para o transporte destas informa??es para um modelo de gesso e virtual

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2015-04-28T17:12:45Z No. of bitstreams: 1 467675.pdf: 1437644 bytes, checksum: dbcd8d581c9d8dc4da7301e5b4e3ac75 (MD5) / Made available in DSpace on 2015-04-28T17:12:45Z (GMT). No. of bitstreams: 1 467675.pdf: 1437644 bytes, checksum: dbcd8d581c9d8dc4da7301e5b4e3ac75 (MD5) Previous issue date: 2015-01-22 / The objectives of the study were to evaluate the influence of the depth of cement, the cement type and mechanical cycling through the pullout bond strength of direct anatomical post in fragile bovine roots and assess the thickness of resin cements in different root thirds of direct anatomical post and fiber post in human single-rooted. Eighty bovine roots were obtained for the bond strength by pullout. The canals were endodontically treated and extended with diamond burs. The roots were divided in two groups: G1 - direct anatomical posts cemented with RelyX ARC; G2 - direct anatomical posts cemented with RelyX U200. Both groups were divided in two subgroups, each subgroup (n = 10) cemented with a depth of 5 mm or 10 mm. Half of the specimens of each depth was submitted to mechanical cycling. The specimens were submitted to pullout test in a universal testing machine. The results were analyzed by ANOVA three factors (?=0.05). To study the thickness of the resin cement, 40 single-rooted human upper anterior teeth were obtained. The teeth were endodontically treated and weakened with drill Largo and diamond burs in a depth of 10 mm.The teeth were randomly divided in four groups (n = 10): Group 1 - fiber post + RelyX ARC; Group 2 - fiber post + RelyX U200 +; Group 3 - anatomical post + RelyX ARC; Group 4 - anatomical post + RelyX U200. The dyes 0.1% Fluorescein and 0.1% Rhodamine B isothiocyanate were added to adhesive system and resin cement, respectively. After cementation, the roots were sectioned in slices and observed by confocal laser scanning microscopy. Datas were analyzed by ANOVA followed by Tukey test (?=0.05). For the pullout test, the resin cement factor (p = 0.0001) and mechanical loading factor (p = 0.0001) were significant. The bond strength of RelyX U200 (6.47 MPa) was statistically superior to RelyX ARC (5.51 MPa). The depth of cementation factor was not significant (p=0.328). However, the interaction between depth and mechanical cycling was significant (p=0.0001). For a depth of 5 mm of cementation, the average bond strength of samples without mechanical cycling (6.98 MPa) was statistically higher to samples with mechanical cycling (4.78 MPa). For the depth of cementation of 10 mm, there was no statistical difference between the samples with and without mechanical cycling.For analysis of the resin cement thickness, post, cement and root thirds influenced the thickness of the resin cement (p <0.001). The thickness of resin cement was significantly lower in anatomical post groups than in fiber post groups, except in the apical third of the canal. There was no significant statistical difference between the cements for the direct anatomical post; for the fiber posts, only the cervical third showed a statistically significant difference between the cements. It was concluded that the direct anatomical posts cemented in the 10 mm depth obtained the best results with RelyX U200, regardless of mechanical cycling. In addition, in weakened roots, the preparation of direct anatomical post allows the better adaptation of post to the channel walls, favoring the formation of a thin and uniform cement film. / Os objetivos do estudo foram avaliar a influ?ncia da profundidade de cimenta??o, do cimento resinoso e da ciclagem mec?nica na resist?ncia ? tra??o por pull out de pinos anat?micos diretos em ra?zes bovinas fragilizadas, assim como avaliar a espessura de cimentos resinosos nos ter?os radiculares de pinos anat?micos diretos e pinos de fibra de vidro em ra?zes unirradiculares humanas. Para o ensaio de pull out, 80 remanescentes radiculares bovinos foram tratados endodonticamente e alargados com pontas diamantadas, sendo divididos em dois grupos: G1 - pinos anat?micos diretos cimentados com RelyX ARC; G2 - pinos anat?micos diretos cimentados com RelyX U200. Ambos os grupos foram divididos em dois subgrupos, sendo cada subgrupo (n=10) cimentado com profundidade de 5 mm e 10 mm. Metade dos corpos de prova de cada profundidade recebeu ciclagem mec?nica. Os corpos de prova foram submetidos ao ensaio de pull out em m?quina de ensaio universal. Os resultados foram analisados pela ANOVA de tr?s fatores (?=0,05). Para o estudo da espessura do cimento resinoso, 40 ra?zes unirradiculares humanas da regi?o ?ntero-superior foram tratadas endodonticamente e fragilizadas com broca Largo e pontas diamantadas na profundidade de 10 mm.Os dentes foram divididos aleatoriamente em quatro grupos (n=10): Grupo 1 - pino de fibra de vidro + RelyX ARC; Grupo 2 - pino de fibra de vidro + RelyX U200; Grupo 3 - pino anat?mico + RelyX ARC; Grupo 4 - pino anat?mico + RelyX U200. Os corantes Fluorosce?na 0,1% e Isotiocianato de Rodamina B 0,1% foram adicionados ao sistema adesivo e ao cimento resinoso, respectivamente. Ap?s cimenta??o, as ra?zes foram seccionadas em fatias e observadas em microscopia confocal de varredura ? laser. Os dados foram analisados pela ANOVA, seguido do teste Tukey (?=0,05). Para o ensaio de pull out, os fatores cimento resinoso (p=0,0001) e ciclagem mec?nica (p=0,0001) foram significativos. A resist?ncia de uni?o do RelyX U200 (6,47 MPa) foi estatisticamente superior ao RelyX ARC (5,51 MPa). O fator profundidade de cimenta??o n?o foi significativo (p=0,328). No entanto, a intera??o entre ciclagem mec?nica e profundidade foi significativa (p=0,0001). Para a profundidade de 5 mm, a m?dia de resist?ncia de uni?o sem ciclagem mec?nica (6,98 MPa) foi estatisticamente superior a com ciclagem mec?nica (4,78 MPa). Para a profundidade de 10 mm, n?o houve diferen?a estat?stica entre as amostras sem e com ciclagem mec?nica.Para a an?lise da espessura de cimento resinoso, o pino, o cimento e os ter?os radiculares influenciaram na espessura do cimento (p<0,001). A espessura de cimento foi significativamente menor nos pinos anat?micos do que nos pinos de fibra de vidro, exceto no ter?o apical do canal. N?o houve diferen?a estat?stica significativa entre os cimentos para pinos anat?micos; para os grupos com pinos de fibra de vidro, apenas o ter?o cervical apresentou diferen?a estat?stica significativa entre os cimentos. Concluiu-se que os pinos anat?micos diretos cimentados em profundidade de 10 mm obtiveram os melhores resultados quando utilizado o RelyX U200, independente da ciclagem mec?nica, e que, em ra?zes fragilizadas, a confec??o de pinos anat?micos diretos permite uma melhor adapta??o dos pinos ?s paredes do canal, favorecendo a forma??o de uma pel?cula de cimento fina e uniforme.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2015-10-23T11:10:19Z No. of bitstreams: 1 475858 - Texto Completo.pdf: 2068340 bytes, checksum: c21728abeb983dd0a87ba3186541f47a (MD5) / Made available in DSpace on 2015-10-23T11:10:19Z (GMT). No. of bitstreams: 1 475858 - Texto Completo.pdf: 2068340 bytes, checksum: c21728abeb983dd0a87ba3186541f47a (MD5) Previous issue date: 2015-08-13 / The aim of the study was to evaluate the association of different aging methods on bond strength values of composite repair, through the use of shear test. 96 samples of rectangular section were made with the microhybrid composite Point 4 (Kerr) and were divided into 8 groups (n = 12) as follows: (1) immersion in distilled water for 7 days; (2) immersion in distilled water for 30 days; (3) immersion in citric acid for 7 days; (4) immersion in boiling water for 8 hours; (5) immersion in distilled water for 30 days plus immersion in citric acid for 7 days; (6) immersion in distilled water for 30 days plus immersion in boiling water for 8 hours; (7) immersion in citric acid for 7 days plus immersion in boiling water for 8 hours and (8) immersion in distilled water for 30 days plus immersion in citric acid for 7 days plus immersion in boiling water for 8 hours. After going through the designated method of aging the treatment of prerepair was conducted with roughening the surface with sandpaper grain silicon carbide 120 and application of the adhesive system Single Bond 2 (3MESPE) and then made a repair with the same composite resin. The samples were tested in a universal testing machine (EMIC) for the shear bond strength test at a loading speed of 1mm / min. After the failure all samples were evaluated in an increase of 35x stereomicroscope and two samples from each group were evaluated in the SEM as surface after aging and after roughening with sandpaper silicon carbide. The results for evaluation of values in the bond strength test were subjected to statistical test analysis of variance (ANOVA) followed by Tukey test (p <0.05) and no significant differences between the groups tested were found. The evaluation of failure occurred in stereomicroscope were made in a descriptive way, with all samples of all groups presented cohesive failures in the aged resin. Conclusion: The association of different aging methods does not influence the bond strength values of resin repairs made when the roughening method simulating diamond burs coarse-grained is used pre-repair. / O objetivo do estudo foi avaliar a influ?ncia da associa??o de diferentes m?todos de envelhecimento nos valores de resist?ncia de uni?o de reparos de resina composta, atrav?s da utiliza??o de teste de cisalhamento. Foram confeccionadas 96 amostras com a resina composta microh?brida Point 4 (Kerr) de sec??o retangular que foram divididas em 8 grupos (n=12) sendo: (1) imers?o em ?gua destilada por 7 dias; (2) imers?o em ?gua destilada por 30 dias; (3) imers?o em ?cido c?trico por 7 dias; (4) imers?o em ?gua em ebuli??o por 8 horas; (5) imers?o em ?gua destilada por 30 dias mais imers?o em ?cido c?trico por 7 dias; (6) imers?o em ?gua destilada por 30 dias mais imers?o em ?gua em ebuli??o por 8 horas; (7) imers?o em ?cido c?trico por 7 dias mais imers?o em ?gua em ebuli??o por 8 horas e (8) imers?o em ?gua destilada por 30 dias mais imers?o em ?cido c?trico por 7 dias mais imers?o em ?gua em ebuli??o por 8 horas. Ap?s passarem pelo m?todo de envelhecimento designado, foi realizado o tratamento de superf?cie pr?-reparo com asperiza??o com lixa de carbeto de sil?cio de granula??o 120 e aplica??o do sistema adesivo Single Bond 2 (3MESPE) e ent?o, confeccionado um reparo com a mesma resina composta. As amostras foram testadas em uma m?quina de ensaio universal (EMIC) para o teste de cisalhamento a uma velocidade de carregamento de 1mm/min. Ap?s a falha todas as amostras foram avaliadas no estereomicrosc?pio com aumento de 35x e duas amostras de cada grupo foram avaliadas em MEV quanto ? superf?cie ap?s o envelhecimento e ap?s a asperiza??o com lixas de carbeto de sil?cio. Os resultados para avalia??o dos valores no teste de resist?ncia de uni?o foram submetidos ao teste estat?stico de an?lise de vari?ncia (ANOVA) seguido do teste de Tukey (p<0,05) e n?o foram encontradas diferen?as significativas entre os grupos testados. A avalia??o no estereomicrosc?pio das falhas ocorridas foram feitas de forma descritiva, sendo que todas as amostras de todos os grupos apresentaram falhas coesivas na resina envelhecida. Conclus?o: a associa??o de diferentes m?todos de envelhecimento n?o influencia nos valores de resist?ncia de uni?o em reparos de resina composta, quando o m?todo de asperiza??o simulando pontas diamantadas de granula??o grossa ? utilizado pr?-reparo.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2016-04-07T18:38:48Z No. of bitstreams: 1 DIS_CAROLINA_RITTER_BROMBERG_PARCIAL.pdf: 119775 bytes, checksum: 01252fee5f06d6e381692a4123b32401 (MD5) / Made available in DSpace on 2016-04-07T18:38:48Z (GMT). No. of bitstreams: 1 DIS_CAROLINA_RITTER_BROMBERG_PARCIAL.pdf: 119775 bytes, checksum: 01252fee5f06d6e381692a4123b32401 (MD5) Previous issue date: 2016-01-20 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Objectives: The aim of this in vitro study was to compare the maximal load resistance of endodontically treated molars restored with: inlays or onlays of Lava Ultimate, composite resin Z350 XT with or without fiberglass post. Methods: Fifty sound extracted third molars were embedded in acrylic resin and divided into 5 groups (n = 10 per group): H = healthy, ON = onlay, IN = inlay, RC = composite resin, PT = fiberglass post + Z350 XT. The MOD preparations and endodontic treatment were performed. Indirect restorations were made through CAD/CAM CEREC system and cemented with SingleBond Universal and RelyX Ultimate under load of 1 kg. Restorations of RC and PT groups were performed by incremental technique and the two posts in the PT group were horizontally transfixed and bonded with flowable resin. Then, mechanical loading in all samples were performed in 500.000 cycles at 200 N at a frequency of 1 cycle / second and the maximum load test was performed in a universal testing machine at a speed of 1 mm / min. After the mechanical test, the faults were categorized into pulpal floor fracture (irreparable) and cuspal fracture (repairable). Results: Mean values were (means followed by the same letter show no significant difference to ANOVA and Tukey): RC 1680N ? 454 d; PT 2693N ? 372 bc; ON 2922N ? 774 b; IN 2053N ? 313 cd; H 4514N ? 548 a. The predominant failure pattern for teeth restored with onlays, inlays and direct composite resin with or without post was the irreparable type. Conclusion: Endodontically treated molars restored with transfixed fiberglass post and composite resin have similar fracture resistance to those restored with indirect Lava Ultimate inlay and onlay. Horizontally fiber post restoration has the same efficiency that onlays restoration. / Objetivos: O objetivo deste estudo foi avaliar e comparar in vitro a resist?ncia m?xima ao carregamento de molares tratados endodonticamente e restaurados com: inlays ou onlays de Lava Ultimate, resina composta Z350 XT com ou sem pino de fibra de vidro transfixado. Materiais e m?todos: Cinquenta terceiros molares h?gidos extra?dos foram inclu?dos em acr?lico autopolimeriz?vel e divididos em 5 grupos (n = 10 por grupo): H = h?gido, ON = onlay, IN = inlay, RC = resina composta, PT = pino de fibra de vidro + Z350 XT. Em seguida, foram realizados os preparos MOD e o tratamento endod?ntico. As restaura??es indiretas foram confeccionadas atrav?s do sistema CAD/CAM CEREC e cimentadas com SingleBond Universal e RelyX Ultimate sob carga de 1 Kg. As restaura??es do grupo RC e PT foram realizadas pela t?cnica incremental e os dois pinos no grupo PT foram transfixados horizontalmente e colados com resina flowable. Ap?s, os corpos de prova foram submetidos a 500.000 ciclos de fadiga mec?nica sob carga vertical de 200 N na frequ?ncia de 1 ciclo/segundo. Na sequ?ncia, foi aplicado o teste de carga m?xima de carregamento em m?quina de ensaio universal a uma velocidade de 1 mm/min. Ap?s o ensaio mec?nico, as falhas foram categorizadas em fratura de assoalho pulpar (irrepar?veis) e fraturas de c?spides (repar?veis). Resultados: Os valores m?dios obtidos foram (m?dias seguidas de mesma letra n?o apresentam diferen?a estat?stica para ANOVA e Tukey): RC 1680N ? 454 d; PT 2693N ? 372 bc; ON 2922N ? 774 b; IN 2053N ? 313 cd; H 4514N ? 548 a. O padr?o de falha predominante para dentes restaurados com onlays, inlays e resina composta direta com ou sem pino foi do tipo irrepar?vel. Conclus?o: Molares endodonticamente tratados e restaurados com pinos de fibra de vidro transfixado e resina composta Z350 XT direta apresentam resist?ncia ? fratura similar ?s restaura??es indiretas tipo inlay e onlay de Lava Ultimate. Restaura??es com pino transfixado horizontalmente possuem a mesma efic?cia que as restaura??es onlays.

Made available in DSpace on 2015-04-14T13:29:23Z (GMT). No. of bitstreams: 1 409857.pdf: 3768332 bytes, checksum: 510f89bdc41453b63f0fecf44ffcf27c (MD5) Previous issue date: 2009-01-20 / Este trabalho teve como objetivo verificar, atrav?s da radiografia digital, como se expressam os valores m?dios, em n?veis de cinza, em diferentes s?tios de dentes restaurados com resinas compostas em diversas espessuras e quais as poss?veis justificativas para tais valores encontrados. Para tanto foram selecionados 10 primeiros pr?-molares h?gidos, que tiveram suas ra?zes inclu?das em prismas de base quadrangular, sendo radiografados por t?cnica padronizada utilizando placas ?pticas do sistema digital DenOptix, as quais foram digitalizadas e arquivadas para posterior an?lise. Estas constitu?ram o grupo 1. Cada vez que estes dentes recebessem algum tratamento, que alterasse a sua forma original, se constituiria um novo grupo. Os dentes passaram por preparo cavit?rio padronizado com espessura V-P de 2mm, foram novamente radiografados e as imagens digitais arquivadas, constituindo o grupo 2. As cavidades foram restauradas com resina composta Filtek Z350, os dentes foram novamente radiografados e as imagens digitais arquivadas, constituindo o grupo 3. Essas restaura??es foram destacadas das cavidades e os dentes novamente restaurados com a resina 4Seasons, radiografados e as imagens digitais arquivadas, constituindo grupo 4. Ap?s as restaura??es serem destacadas, essas cavidades foram mais uma vez restauradas, agora com a resina Filtek Z250, repetindo-se as radiografias e o arquivamento das imagens digitais, constituindo o grupo 5. Ap?s a remo??o dessas restaura??es as cavidades foram ampliadas na largura V-P para 3mm, repetindo-se a mesma seq??ncia realizada nos grupos anteriores, constituindo os grupos 6, 7, 8 e 9. Ap?s a remo??o das restaura??es do grupo 9, as cavidades foram ampliadas na largura V-P para 4mm, repetindo-se a seq??ncia realizada nos grupos anteriores, constituindo novos grupos: 10, 11, 12 e 13. Tamb?m foram confeccionadas 30 placas acr?licas nas espessuras de 2, 3 e 4mm, 10 placas em cada uma das espessuras, sendo que as placas continham uma amostra de cada resina. Estas constitu?ram os grupos 14, 15 e 16 que passaram pelo mesmo processo de radiografia e arquivamento das imagens digitais. Amostras de cada uma das resinas compostas foram analisadas pelo EDS, para verifica??o dos elementos qu?micos respons?veis pelas caracter?sticas de radiopacidade desses materiais. Ap?s an?lise estat?stica dos dados foi poss?vel concluir que: (1)existiu diferen?a significativa entre os s?tios de leitura. (2)Encontraram-se os menores valores m?dios em n?veis de cinza nos dentes com maiores preparos cavit?rios sem restaura??es (G10 - 4mm). (3)Encontraram-se os maiores valores m?dios, em n?veis de cinza, nos dentes restaurados com a resina 4 Seasons? na maior espessura de restaura??o (4mm - G12). (4)Os dentes cavitados apresentaram valores m?dios, em n?veis de cinza, inferiores aos das estruturas dent?rias h?gidas. (5)Os dentes restaurados apresentaram valores m?dios, em n?veis de cinza, superiores aos das estruturas dent?rias h?gidas, com exce??o da resina Filtek Z350 nos s?tios proximais das restaura??es na espessura de 3mm. (6)Os dentes restaurados apresentaram valores m?dios, em n?veis de cinza, superiores aos dos dentes com preparos cavit?rios sem restaura??es. (7)Houve distin??o entre os valores m?dios, em n?veis de cinza, para as diferentes resinas compostas estudadas quando analisadas individualmente, sem influ?ncia dos tecidos dent?rios (placas) em uma mesma espessura. (8)Para as resinas compostas sem a influ?ncia dos tecidos dent?rios, quanto maior foi a espessura, maior o valor m?dio em n?veis de cinza. (9)Os valores em n?veis de cinza para os dentes restaurados nem sempre alteraram-se conforme as altera??es em n?veis de cinza das resinas compostas analisadas individualmente (placas) na espessura correspondente. (10)A presen?a de maior concentra??o do elemento qu?mico de mais alto n?mero at?mico refletiu-se em maiores valores m?dios, em n?veis de cinza, nas resinas compostas

Made available in DSpace on 2015-04-14T13:29:43Z (GMT). No. of bitstreams: 1 411408.pdf: 3121916 bytes, checksum: d0e7791af851fbf98b39ad1f7dd9ed3f (MD5) Previous issue date: 2009-01-15 / O objetivo desse estudo foi avaliar, in vitro, a resist?ncia de uni?o ? microtra??o de cimentos resinosos auto-adesivos ? dentina, assim como a influ?ncia do pr?-tratamento com ?cido poliacr?lico nessa uni?o. Em terceiros molares humanos extra?dos foi obtida uma superf?cie oclusal plana em dentina, sendo a mesma regularizada com lixas de carbeto de sil?cio de granula??o 320, 400 e 600, respectivamente. Os dentes foram divididos aleatoriamente em cinco grupos: Grupo 1 RelyX ARC (controle); Grupo 2 RelyX Unicem; Grupo 3 Maxcem; Grupo 4 ?cido poliacr?lico 22,5% e RelyX Unicem; Grupo 5: ?cido poliacr?lico e Maxcem. Ap?s a aplica??o dos cimentos resinosos, foram constru?dos blocos de resina composta com 6 mm de altura. As amostras foram armazenadas em ?gua destilada a 37? C por 24 horas. Os conjuntos dente/resina foram cortados paralelamente ao longo eixo do dente, nos sentidos vest?bulo-lingual e m?sio-distal, com sec??o de aproximadamente 0,7 mm. Foram obtidos 20 corpos-de-prova para cada grupo, sendo ent?o submetidos ao teste de resist?ncia ? microtra??o em m?quina de ensaio universal com velocidade de 0,5 mm/min. As falhas foram observadas em microscopia eletr?nica de varredura. De acordo com a An?lise de Vari?ncia e o teste de Tukey (a=0,05), a maior m?dia de resist?ncia ? microtra??o foi para o RelyX ARC (21,38 MPa), n?o diferindo estatisticamente do Maxcem associado ao ?cido poliacr?lico (19,22 MPa) e RelyX Unicem associado ao ?cido poliacr?lico (17,75 MPa) (p>0,05). Estes dois ?ltimos grupos n?o diferiram estatisticamente do RelyX Unicem (16,98 MPa) (p>0,05). A menor m?dia foi obtida para o Maxcem (6,43 MPa), diferindo estatisticamente dos outros grupos (p<0,05). No grupo do Maxcem, sem pr?-tratamento com ?cido poliacr?lico, ocorreram somente falhas adesivas, e nos demais grupos as falhas foram predominantemente mistas.

Made available in DSpace on 2015-04-14T13:29:49Z (GMT). No. of bitstreams: 1 428173.pdf: 3267525 bytes, checksum: 111e79e4715696d409dab4a83d48e6c0 (MD5) Previous issue date: 2010-12-15 / OBJETIVO: Avaliar as altera??es histol?gicas ?sseas superficiais ap?s a inser??o de miniplacas e parafusos com diferentes composi??es met?licas. MATERIAL E METODOS: Dezoito ratos, da linhagem Wistar, foram utilizados. Uma miniplaca e dois parafusos foram inseridos na superf?cie externa do f?mur direito de cada animal. Todos os parafusos foram de 5,0 mm de comprimento e foram inseridos at? as pontas serem projetadas pelo lado endosteal. Os animais foram divididos em tr?s grupos com seis animais cada. Nos primeiros seis animais foram colocados uma placa e dois parafusos de tit?nio, em outros seis animais foram colocados uma placa de tit?nio e dois parafusos de a?o inoxid?vel, e nos animais restantes foram colocados placa e parafuso revestido com Diamond-Like Carbon (DLC). Ap?s 30 dias da realiza??o do procedimento cir?rgico, as miniplacas e os parafusos foram retirados e foram feitas avalia??es histol?gicas na interface placa parafuso no defeito ?sseo, em uma extens?o de 0,5 cm2. RESULTADOS: Na avalia??o histol?gica observou-se um maior processo inflamat?rio no grupo com diferentes composi??es met?licas (Grupo tit?nio-a?o)(p=0,204), como tamb?m uma maior presen?a de lacunas de Howship que indicam uma poss?vel oste?lise em decorr?ncia de um ?nicio de corros?o galv?nica entre o tit?nio e o a?o inoxid?vel (p=0.002). CONCLUS?ES: Os resultados deste estudo indicam que, quando usamos diferentes materiais com diferentes composi??es met?licas, os componentes de implantes de a?o inoxid?vel quando em associa??o com o tit?nio t?m uma maior suscetibilidade ? provocar oste?lise do que quando se utilizam os mesmos componentes como materiais de fixa??o.