Made available in DSpace on 2017-07-24T19:22:07Z (GMT). No. of bitstreams: 1 Eugenio Jose Garcia.pdf: 2279716 bytes, checksum: bcc5c4e011f01920817473d9a60779e1 (MD5) Previous issue date: 2008-02-28 / The objective of this study was to evaluate the bond strength of three adhesives systems to superficial and deep dentine using microtensile test. Thirty human third molars were cleaned of gross debris and the occlusal enamel was removed to expose a flat surface of superficial or deep dentin. In order to create a standardized smear layer dentinal surfaces were wet-abraded with 600-grit silicon carbide paper for 60 seconds. For each type of surface, the test specimens were randomly divided into three groups which underwent the application of a conventional two-step adhesive system [Adper Single Bond (SB), 3M/ESPE] as control group (n=10), a twobottle self-etching system [One Coat SE Bond (OCSE), Coltène/Whaledent] (n=10) and a one bottle one-step system [Clearfil S3 Bond (CFS3), Kuraray Co.] (n=10). After each adhesive was utilized according to the manufacturer´s instructions, a 5-mm high resin “crown” was built-up with resin composite Filtek Z-250 (3M/ESPE). The bonded test specimens were stored in distilled water for twenty-four hours before been longitudinally sectioned to obtain stick-shaped specimens with a cross-sectional area of 0,7 mm², which were submitted to bond strength test (0,5mm/min). After, some fractured specimens for each adhesive were randomly selected and the dentin side was gently abraded with a 1200-grit SiC paper, etched with acid phosphoric 35% for 15 s and air dried. SEM micrographs at 70X and 2400X magnification were taken to permit calculation of area of tubular dentin (ATD) and tubular density (TD) at the site of fracture. ANOVA two-ways (dentin depth-adhesive) and linear regression were performed to correlate ATD and TD with bond strength. OCSE (29,20±2,68) and CFS3 (32,27±3,78) presented similar bond strength, nevertheless the values were significantly lower than SB (54,53±1,66), irrespective of dentin depth. Linear regression showed significantly relationship between bond strength and area of intertubular dentin for SB (p=0,004), and a significant inverse relationship between tubular density and bond strength for CFS3 (p=0,009). OCSE presented a tendency similar to SB and conversely to CFS3, but it was not statistically significant. It was demonstrated that the bond strength of the conventional two-step adhesive system was significantly higher than self-etching adhesives. The use of digital image analysis facilitate the manipulation of data and a better interpretation of new adhesive systems behavior. / O objetivo deste estudo foi analisar a resistência adesiva de três sistemas adesivos aplicados sobre dentina superficial e profunda através do teste de microtração. Após limpeza, o esmalte oclusal de trinta terceiros molares humanos foi eliminado para obtenção de superfícies dentinárias superficiais ou profundas. A camada de esfregaço foi padronizada com lixas de carbeto de silício de granulação 600 aplicadas durante 1 minuto. Os espécimes foram divididos aleatoriamente segundo o tipo de superfície em três grupos experimentais correspondentes a cada adesivo: Adper Single Bond (SB) (3M/ESPE), sistema convencional de dois passos utilizado como controle (n=10); e dois sistemas autocondicionantes, o One Coat SE Bond (OCSE) (Coltène/Whaledent) (n=10) e o Clearfil S3 Bond (CFS3) (Kuraray Co.) (n=10). Os adesivos foram aplicados segundo as indicações dos fabricantes e as porções coronárias foram restauradas com a resina composta Filtek Z-250 3M/ESPE. Após 24 horas de armazenamento, os dentes foram seccionados com três cortes perpendiculares entre si para obter espécimes com formato de palito com uma área de seção transversal de aproximadamente 0,7 ± 0,1 mm2 os quais foram submetidos ao teste de microtração a uma velocidade de 0,5 mm/min. Depois de fraturados alguns espécimes foram selecionados e a porção correspondente à dentina foi levemente desgastada na face adesiva com lixa de carbeto de silício de granulação #1200, condicionada com ácido fosfórico 35% por 15 segundos e secada ao ar. Foram realizadas fotomicrografias no MEV em aumentos de 70X e 2400X para realizar o cálculo da área de dentina tubular (ADT) e densidade tubular (DT). O teste ANOVA dois critérios (profundidade dentinária-adesivo) mostrou que OCSE (29,20±2,68) e CFS3 (32,27±3,78) apresentaram uma resistência de união semelhante e significativamente inferior ao SB (54,53±1,66), independentemente da profundidade da dentina. O teste de regressão linear mostrou uma relação significativa entre a resistência adesiva e a área de dentina intertubular para SB (p=0,004), e uma relação inversa significativa entre a densidade tubular e a resistência adesiva para CFS3 (p=0,009). OCSE apresentou um comportamento similar a SB e contrário a CFS3, porém não estatisticamente significativo. Os resultados mostraram uma resistência adesiva significativamente superior para o adesivo convencional de dois passos em comparação com os autocondicionantes. Os novos métodos de tratamento de imagens facilitam a manipulação de dados e permitem uma melhor interpretação do comportamento dos sistemas adesivos.

Made available in DSpace on 2017-07-24T19:22:20Z (GMT). No. of bitstreams: 1 VivianeHass.pdf: 12753582 bytes, checksum: 375b79db14124179b45aa6f1e68d193e (MD5) Previous issue date: 2012-02-24 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study evaluated the effect of prolonged exposure times on immediate (IM) and 6-month (6M) adhesive properties: degree of conversion within hybrid layer (DC), silver nitrate uptake (SNU) and resin-dentin bond strenght (μTBS) for three one-step self-etch adhesive systems (Adper Easy Bond [EB], Clearfil S3 Bond [CS3] and Go [GO]).Ninety caries-free extracted molars were included in this study being 45 for μTBS and SNU (n=5) and 45 for DC (n=5). The dentin surfaces were bonded according to the manufacturer’s instructions, but they were light-cured for 10, 20, and 40 s at 600mW/cm2. Bonded teeth for the μTBS test were sectioned in order to obtain stick-like specimens (0.8mm2) and tested under tensile stress 0.5mm/min). Two bonded sticks from each tooth were analyzed by scanning electron microscopy for SNU. The DC within the hybrid layer were evaluated with micro-Raman spectroscopy. All tests were performed IM and at 6M. Data were analyzed by a threeway repeated measures ANOVA and Tukey´s test (alpha=0.05).The prolonged exposure times increased the DC () [10s- 67.3±19.5; 20s- 84.6 ± 12.3 e 40s- 82.9 ±13.1] for all adhesives and decreased the SNU ()[10s- 24.8 ± 13.2; 20s- 13.3 ± 7.5 e 40s- 13.5 ± 9.3] significantly for all adhesives; however significant improvements in the μTBS (MPa) [10s- 17.3 ± 3.7; 20s- 31.9 ± 4.9 e 40s- 25.0 ± 3.7] and stable bond strengths after water storage [IM- 25.2 ± 7.3; 6M- 24.2 ± 7.2] were observed only for CS3. EB [IM- 35.9 ± 4.7; 6M- 28.0 ± 6.0] and GO [IM- 25.6 ± 5.0; 6M- 14,3 ± 3,7] decreased the μTBS after 6 months. The prolonged exposure times improved the DC within the hybrid layer and reduced the SNU for all adhesives, however this did not prevent the degradation of the adhesive interface. / Este estudo avaliou o efeito dafotoativação prolongadaem tempo imediato (IM) e após 6 meses de armazenamento em água (6M) nas propriedades adesivas: grau de conversão no interior da camada híbrida (GC), nanoinfiltração (NI) e na resistência de união (RU) à dentina de três sistemas adesivos autocondicionantes simplificados (AdperEasyOne [EO], Clearfil S3 Bond [CS3] e Go [GO]).As superfícies dentinárias de 90 molares humanos foram expostas e os adesivos aplicados conforme recomendações dos fabricantes, porém a fotoativação realizada nos tempos10, 20 e 40 s a 600 mW/cm2 depois restaurados com resina composta. Para RU e NI, os dentes restaurados foram seccionados para obtenção de corpos-deprova (cps) na forma de “palitos” (0,8 mm2) e testados por microtração a 0,5 mm/min. Dois cps de cada dente em cada condição experimental foram analisados por microscopia eletrônica de varredura. Para análise do GC, foram realizadas secções longitudinais em cada dente para obtenção de cps em formato de fatias e análise em espectroscopia micro-Raman. Os dados de RU, NI e GC de cada adesivo foram analisados por ANOVA de 3 fatores de medidas repetidas (adesivo vs. tempo de ativação vs. tempo de armazenagem) e teste de Tukey (α = 0,05).A fotoativação prolongada aumentou o GC() [10s- 67,3±19,5; 20s- 84,6 ± 12,3e 40s- 82,9 ± 13,1] para todos os adesivos e diminuiu a NI [10s- 24,8 ± 13,2; 20s- 13,3 ± 7,5e 40s- 13,5 ± 9,3] significativamente para todos os adesivos; contudo melhora significante na RU (MPa) [10s- 17,3 ± 3,7; 20s- 31,9 ± 4,9e 40s-25,0 ± 3,7] e estabilidade da adesão após 6 meses de armazenamento em água [IM- 25,2±7,3; 6M- 24,2 ± 7,2] foi observado somente para CS3. EO [IM- 35,9 ± 4,7; 6M- 28,0 ± 6,0] e GO [IM- 25,6 ± 5,0; 6M- 14,3 ± 3,7] reduziram os valores de RU após 6 meses. A fotoativação prolongada aumentou o GC dentro da camada híbrida e diminuiu a NI para todos os adesivos, porém não preveniu a degradação da interface adesiva.

O objetivo deste estudo foi avaliar a resistência à microtração de adesivos autocondicionantes em dentina desmineralizada de dentes decíduos após a irradiação com laser de Er: YAG. Oitenta e dois molares decíduos tiveram a porção oclusal seccionada transversalmente e os espécimes foram desgastados com lixas de carbeto de silício de granulações 360 e 600 até expor a dentina. Os 60 espécimes utilizados no teste de microtração foram preenchidos com resina composta fotopolimerizável na região correspondente à câmara pulpar, isolados com esmalte cosmético mantendo a superfície dentinária exposta e, em seguida imersos em solução desmineralizante por seis dias em estufa a 37° C para indução de lesão de cárie artificial em dentina. Após a desmineralização, os espécimes foram preparados com laser de Er: YAG (n=30) com os parâmetros de 260 mJ, 3 Hz, 47 J/cm2, 0,81W e com broca de aço esférica em baixa rotação (n=30). Sobre as superfícies preparadas foram aplicados três sistemas adesivos autocondicionantes Clearfil SE Bond (Kuraray); Adper™ Easy One (3M ESPE) e Adper™ SE Plus (3M ESPE) e, em seguida foram confeccionados platôs de resina composta Z 250. Após termociclagem (500 ciclos), os corpos de prova foram seccionados produzindo palitos de aproximadamente 1 mm2 de área transversal, que foram submetidos ao teste de microtração e os valores obtidos foram analisados estatisticamente através de ANOVA e teste de Duncan (5%). A análise qualitativa dos tipos de fraturas foi realizada por meio de lupa estereoscópica (aumento de 40X) e da interface adesiva por meio de MEV. Para a análise química da dentina através de espectroscopia no infravermelho por transformada de Fourier (FTIR), foram utilizados discos de dentina após o preparo superficial com a broca (n=5) e com o laser (n=5), e comparadas com as análises de tecido dentinário sadio e desmineralizado obtidas dos mesmos espécimes. Os resultados foram submetidos ao teste estatístico t−Student (5%). O teste de microtração demonstrou que houve diferença significativa entre os adesivos, sendo que o grupo controle (Clearfil e broca) obteve o melhor desempenho comparativamente a todos os grupos avaliados. O preparo com laser de Er: YAG afetou adversamente a adesão para os sistemas adesivos Clearfil SE Bond e Adper™ Easy One em comparação com os grupos preparados com broca. Nos grupos irradiados com laser, o sistema adesivo Clearfil SE Bond foi o que proporcionou o maior valor médio de microtração. Os resultados da FTIR demonstraram que, com a irradiação da dentina desmineralizada, houve um decréscimo na quantidade de matéria orgânica e de carbonato em relação ao grupo da dentina sadia. No substrato preparado com broca, observouse aumento da matéria orgânica e redução de carbonato. Concluise que, em relação aos sistemas adesivos, o Clearfil SE Bond teve o melhor desempenho no teste de resistência à microtração em dentina de dentes decíduos. A irradiação com laser de Er: YAG afetou adversamente a adesão dos sistemas adesivos Clearfil SE Bond e Adper™ Easy One. A irradiação com laser de Er:YAG decresceu de maneira significativa a quantidade de matéria orgânica presente na dentina de dentes decíduos. / The purpose of this study was to evaluate the microtensile bond strength of three selfetch adhesives systems to demineralized dentin of primary teeth after irradiation with Er: YAG laser. Eighty two primary molars had the occlusal enamel sectioned and the specimens were grounded with silicon carbide sandpaper grits of 360 and 600 to expose the dentin. The 60 specimens used in the microtensile test were filled with composite resin in the region corresponding to the pulp chamber, insulated with nail varnish keeping the exposed dentin surface and then immersed in demineralizing solution for six days in a stove at 37 Celsius degrees in order to produce artificial carieslike lesions in dentin. After demineralization, the specimens were prepared with Er: YAG (n = 30) using as parameters 260 mJ, 3 Hz, 47 J/cm2, 0.81 W and a round steel drill at low speed (n = 30 ). On the prepared surfaces were applied three self−etch adhesives systems Clearfil SE Bond (Kuraray); Adper™ Easy One (3M ESPE) and AdperTM SE Plus (3M ESPE) and then plateaus of composite resin Z 250 were built up. After thermocycling (500 cycles), specimens were sectioned to produce multiple sticks of approximately 1 mm2 crosssectional area, which were subjected to microtensile test and the data were analyzed with ANOVA and Duncan test at a significance level of 0.05. The qualitative analysis of the types of fractures was performed using a stereomicroscope (X40 magnification) and the morphological analyses of adhesive interfaces were performed by scanning electron microscopy (SEM). Chemical analysis of the dentin by Fourier transform infrared spectroscopy (FTIR) were performed in dentin discs after surface preparation with the steel drill (n = 5) and laser (n = 5) and compared with the values previously obtained from the analysis of sound and demineralized dentin tissue in the same specimens. The results were analyzed by Student\'s t−test at a significance level of 0.05. Regarding the microtensile bond strength there was a significant difference between the adhesive systems, and the control group (Clearfil and steel drill) had the best performance compared to all groups. Er: YAG laser irradiation adversely affected bond strength to the Clearfil SE Bond and Adper™ Easy One compared with the groups prepared with steel drill. In the laser groups Clearfil SE Bond reached the highest average bond strength. Results of FTIR analysis showed that the hydration of dentin remained normal after both preparations. With laser irradiation of demineralized dentin there was a decrease in the amount of organic matter and carbonate in relation to the group of sound dentin. The analyses of substrate prepared with steel drill showed an increase in organic matter and reduction of carbonate. The conclusion in relation to adhesive systems was that Clearfil SE Bond had the best performance in microtensile bond strength in primary teeth dentin. Laser irradiation adversely affected the bond strength of Clearfil SE Bond and Adper™ Easy One selfetch adhesive systems. Laser irradiation had significantly reduced the organic matter content in dentin of deciduous teeth.

Este estudo objetivou investigar a influência da redução do tempo de condicionamento na união de sistemas adesivos à dentina hígida e afetada por cárie de dentes decíduos, por meio de testes de microtração, nanoinfiltração e avaliação micromorfológica da interface adesiva. A superfície dentinária de 48 segundos molares decíduos foi exposta e os dentes divididos aleatoriamente em 8 grupos experimentais de acordo com o substrato (dentina hígida e afetada por cárie ciclagem de pH por 14 dias), sistema adesivo (Adper Single Bond 2 adesivo convencional de dois passos e Clearfil SE Bond - sistema autocondicionante de dois passos) e tempo de condicionamento (recomendado pelo fabricante e metade do tempo). Desta forma, o adesivo Adper Single Bond 2 foi aplicado à dentina após condicionamento com ácido fosfórico a 35% por 15 ou 7 segundos e o agente de união do Clearfil SE Bond após 20 ou 10 segundos de aplicação do primer. Blocos de resina composta (Filtek Z250) foram confeccionados e, após 24 horas de armazenamento em água destilada, os dentes foram seccionados para obtenção de espécimes com área de secção transversal de aproximadamente 0,8 mm2. Metade dos espécimes foi submetida imediatamente ao teste de microtração e a outra metade após 12 meses de armazenamento em água destilada. O padrão de fratura foi avaliado em estereomicroscópio com aumento de 400x. Dois espécimes de cada dente nos respectivos períodos de armazenamento foram imersos em nitrato de prata amoniacal por 24 horas e revelados (8 horas) para avaliação da nanoinfiltração em microscopia eletrônica de varredura. Adicionalmente, dois dentes para cada grupo experimental (n=16) foram preparados como descrito para o teste de microtração e seccionados perpendicularmente à interface adesiva, após 24 horas, para análise da micromorfologia e espessura da camada híbrida. Os valores de resistência de união, expressos em megapascal (MPa), foram submetidos à Análise de Variância (ANOVA) e teste de Tukey ( = 0,05). As demais avaliações foram descritivas. Os sistemas adesivos apresentaram valores similares de resistência de união imediata. Decréscimo dos valores de resistência de união ocorreu após 12 meses de armazenamento em água, exceto para o adesivo Clearfil SE Bond em substrato hígido. A adesão à dentina afetada foi menor em comparação à dentina hígida. A nanoinfiltração também foi mais pronunciada neste substrato. O tempo de condicionamento influenciou apenas a adesão do sistema adesivo Adper Single Bond 2. Maiores valores de resistência de união e menor infiltração de nitrato de prata na interface adesiva foram observados quando o tempo de condicionamento ácido foi reduzido pela metade, independente do substrato. Camadas híbridas mais finas foram produzidas quando a dentina decídua foi condicionada por 7 segundos, especialmente em dentina afetada. Predomínio de fratura adesiva/mista foi observado para todos os grupos experimentais. Em conclusão, o efeito da redução no tempo de condicionamento é material dependente e resulta em maior estabilidade da união de sistema adesivo convencional de dois passos à dentina hígida e afetada de dentes decíduos. / This study aimed to investigate the influence of shortening the etching time on bond of adhesive systems to sound and caries-affected dentin of primary teeth by microtensile and nanoleakage tests, and micromorphological evaluation of the adhesive interface. The dentinal surface of 48 second primary molars was exposed and the teeth were randomly assigned to 8 experimental groups according to substrate (sound and caries-affected dentin - pH-cycling for 14 days), adhesive system (Adper Single Bond 2 two-step etch-and-rinse adhesive system and Clearfil SE Bond two step self-etch adhesive system) and etching time (recommend by manufacturers and half-reduced time). Thus, the adhesive Adper Single Bond 2 was applied to dentin after 35% phosphoric acid etching for 15 or 7 seconds, and the bond of Clearfil SE Bond after 20 or 10 seconds of primer application. Composite resin blocks (Filtek Z250) were built and, after 24 hours of storage in distilled water, the teeth were sectioned to obtain specimens with cross-sectional area of approximately 0.8 mm2. Half of the specimens were immediately subjected to microtensile test and the other half after 12 months of storage in distilled water. The fracture pattern was evaluated with a stereomicroscope at 400x magnification. Two specimens from each tooth in the respective storage periods were immersed in ammoniacal silver nitrate for 24 hours and revealed (8 hours) to evaluate the nanoleakage in scanning electron microscope. Additionally, two teeth for each experimental group (n=16) were prepared as described for the microtensile test and perpendicularly sectioned to the adhesive interface, after 24 hours, for analysis of micromorphology and thickness of the hybrid layer. Bond strength values, expressed in megapascal (MPa), were submitted to Analysis of Variance (ANOVA) and Tukeys tests ( = 0.05). Other evaluations were descriptive. The adhesive systems presented similar immediate bond strength values. A decrease in bond strength values occurred after 12 months of water storage, except for Clearfil SE Bond in sound substrate. Bonding to caries-affected dentin was lower compared to sound dentin. The nanoleakage was also more pronounced in this substrate. Etching time only influenced the bonding of the adhesive system Adper Single Bond 2. Higher bond strength values and lower infiltration of silver nitrate into adhesive interface were observed when the etching time was half-reduced, irrespective of the substrate. Thinner hybrid layers were produced when the primary dentin was acid etched for 7 seconds, especially in caries-affected dentin. Predominance of adhesive/mixed fracture was observed for all experimental groups. In conclusion, the effect of shortening the etching time is material dependent and results in higher bond stability of two-step etch-and-rinse adhesive system to sound and caries-affected dentin of primary teeth.

O objetivo deste estudo foi avaliar a influência do substrato dentinário sadio e afetado em dentes decíduos, após restaurações realizadas com diferentes materiais, na resistência de união e nanoinfiltração. Setenta e dois segundos molares receberam preparos padronizados na superfície oclusal e foram divididos aleatoriamente em dois grupos. Um grupo foi denominado dentina sadia [DS] (n=36), e o outro foi submetido ao desafio cariogênico artificial (ciclagem de pH) denominado dentina afetada [DA] (n=36). Posteriormente, os dentes foram restaurados (n=6) com os seguintes materiais: cimento de ionômero de vidro modificado por resina (CIVMR) com nanopartículas - KetacTM N100 [KN100], CIVMR - Vitremer [VI], cimento de ionômero de vidro de alta viscosidade (CIVAV) - KetacTM Molar Easy Mix [KME], Sistema Adesivo autocondicionante de passo único AdperTM Easy One Self-Etch Adhesive [EASY], sistema adesivo autocondicionante de dois passos - AdperTM SE Plus [SE], sistema adesivo com condicionamento ácido total - AdperTM Single Bond 2 [SB]. Os grupos dos sistemas adesivos receberam restauração com resina composta (Filtek Z250). Após 24 horas de armazenagem em água destilada (37ºC), os dentes foram seccionados no sentido vestíbulo-lingual e novos cortes no sentido mésiodistal de forma a obter palitos com secção transversal de 1 mm2 de área. Os espécimes foram submetidos ao teste de microtração (1,0 mm/min) e o modo de falha foi determinado utilizando um microscópio óptico (400x). Um espécime de cada dente foi imerso 24 h em uma solução de nitrato de prata 50% por peso e posteriormente imersos em solução reveladora sob luz fluorescente, por 8 horas. A quantidade de penetração foi avaliada por único examinador, cego em relação aos grupos, por meio de imagens em microscópio eletrônico de varredura em modo de elétrons retroespalhados, sendo adotado escore de 0 a 3. A concordância intraexaminador foi de 0,87. A média dos valores de resistência de união de cada material foi submetida à análise de variância de dois fatores e complementado pelo teste de Tukey. Para os dados da nanoinfiltração foram utilizados o teste de Kruskal Wallis e Mann-Whitney. O nível de significância adotado foi de 5%. A média (±desvio padrão) de cada material, em dentina sadia foi: KN100: 35,2 (±9,4); VI: 29,2 (±7,8); KME: 18,8 (±2,7); EASY: 27,12 (±2,42); SE: 18,77 (±7,23); SB: 37,32 (±3,95). Para dentina afetada: KN100: 35,8 (±6,7); VI: 24,9 (±5,7); KME: 14,5 (±0,7); EASY: 14,32 (±5,79); SE: 13,29 (±3,43); SB: 19,36 (±4,06). O tipo de falha mais freqüente independente do tipo de substrato foi coesiva para o CIVAV e adesiva para os sistemas adesivos e CIVMR. O fator substrato dentinário não influenciou significativamente a infiltração de prata na interface. Pode-se concluir que os CIVs não sofrem influência na resistência adesiva em relação ao substrato. Entretanto, os sistemas adesivos autocondicionante de passo único e condicionamento prévio são influenciados pelo substrato afetado por lesão de cárie. / The aim of this study was to evaluate the influence of sound and caries-affected dentin of primary teeth restored with different materials, regarding bond strength and nanoleakage. Seventy two primary second molars received standardized occlusal preparations were randomly assigned in two groups. One group was nominated as sound dentin [SD] (n=36), and the other was submitted to artificial caries challenge (pH cycling), called caries affected dentin [CAD] (n=36). Six teeth in each group were restored according to dental material: resin modified GIC with nanoparticles Ketac TM Nano [KN100], a resin modified GIC - Vitremer [VI], high viscosity glass ionomer cement KetacTM Molar Easy Mix [KME], one-step self-etch adhesive system AdperTM Easy One Self-Etch Adhesive [EASY], two-step self-etch adhesive system - AdperTM SE Plus [SE], total-etching adhesive system - AdperTM Single Bond 2 [SB]. The adhesive systems groups were restored with composite resin (Filtek Z250). After storage in distilled water (37ºC) for 24 hours, the teeth were sectioned in buccallingual direction and then in the mesial-distal to obtain bonded sticks (1 mm2). The specimens were subjected to microtensile test (1.0 mm/min) and the failure mode was determined using an optical microscope (400x). One dentin-material stick from each tooth was immersed in silver nitrate solution 50% weight per volume (24 h) and immersed in revealing solution under fluorescent light, for 8 hours. One examiner, blinded regarding groups, evaluated the images using scanning electron microscope adopting scores ranging from 0 to 3. The intra-examiner agreement was 0.87. The values of bond strength from each material were analyzed by two-way ANOVA and Tukey post hoc test. For the nanoleakage data, Kruskal-Wallis and Mann-Whitney tests were used, with level of significance set on 5%. The mean (and standard deviations) for each material, in sound dentin were: KN100: 35.2 (±9.4); VI: 29.2 (±7.8); KME: 18.8 (±2.7); EASY: 27.12 (±2.42); SE: 18.77 (±7.23); SB: 37.32 (±3.95). For caries-affected dentin: KN100: 35.8 (±6.7); VI: 24.9 (±5.7); KME: 14.5 (±0.7); EASY: 14.32 (±5.79); SE: 13.29 (±3.43); SB: 19.36 (±4.06). The most frequent type of failure regardless of substrate was cohesive, for KME, and adhesive, for the adhesive systems and RMGICs. Sound or caries-affected dentin did not significantly affect the infiltration of silver nitrate into the interface. It can be concluded that the bond strength of GICs are not influenced by the substrate, however, the one-step self-etch adhesive system and total-etching are influenced by caries-affected dentin.

O objetivo deste estudo foi avaliar a influência do tipo de sistema de cimentação (condicionamento ácido total ou autoadesivo), do modo de ativação (autoativado ou dual), do terço do conduto radicular (cervical, médio ou apical) e da espessura do filme de cimento sobre a resistência de união de pinos de fibra de vidro cimentados em dentes humanos. Quarenta raízes foram incluídas em resina epóxi, submetidas a tratamento endodôntico e obturadas com guta percha e cimento endodôntico sem eugenol. Decorridos sete dias, os condutos foram preparados a uma profundidade de 10mm com brocas padronizadas do sistema dos pinos de fibra (WhitePost DC #2) e aleatoriamente divididos em 4 grupos, conforme o sistema de cimentação e o modo de ativação: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (condicionamento ácido total), ativação dual, (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, autoativado, (G3) RelyX U100 (autoadesivo), dual e (G4) RelyX U100, autoativado. Após uma semana, cada raiz foi seccionada em máquina de corte, originando 6 fatias de 1 mm de espessura (n=60). Antes do ensaio de push-out cada fatia foi fotografada em ambas as faces, para determinação do raio dos pinos e da espessura do filme de cimento. Após o ensaio mecânico, novas imagens foram capturadas para determinação do modo de falha. Para automatizar a determinação da espessura de cimento, foi desenvolvida uma macro no software KS 400. Os dados foram estatisticamente analisados com ANOVA 3 fatores (resistência de união) e teste de Kruskall-Wallis (espessura do cimento). Comparações múltiplas foram realizadas com o teste Student-Newman-Keuls. Análise de regressão, modelo linear, foi empregada para verificar a correlação entre espessura do cimento e resistência de união. Todos os testes foram aplicados com &#945; = 0,05. O fator cimento exerceu influência significativa para a resistência de união (p = 0,0402): o RelyX U100 apresentou a maior média. A ativação dual elevou os valores de resistência de união em comparação ao modo quimicamente ativado (p < 0,0001). Houve diferenças significantes entre os grupos, sendo G1 (22,4 4,0 MPa) > G3 (20,4 3,6 MPa) > G4 (17,8 5,2 MPa) > G2 (13,5 4,3 MPa). O terço do conduto não exerceu influência significativa sobre a resistência adesiva (p = 0,4749). As espessuras dos filmes de cimento foram estatisticamente diferentes nos diferentes terços: cervical (102 45 m) > médio (75 29 m) > apical (52 28m). Não foi observada forte correlação entre os valores de espessura e os de resistência ao push-out (r = - 0,2016, p = 0,0033). O tipo de falha predominante foi a mista, exceto para o G2, que apresentou 74% das falhas na interface cimento-pino. Dessa forma, o cimento autoadesivo apresentou melhor desempenho que o convencional, e ambos os sistemas duais, sobretudo o RelyX ARC, apresentaram dependência da fotoativação para atingirem maiores valores de resistência de união. / The aim of this study was to evaluate the influence of adhesive cementation system approach (total-etch or self-adhesive), activation mode (self-cure or dual-cure), canal third (cervical, middle or apical) and cement thickness on push-out bond strength of glass fiber post bonded on human roots. Forty roots were embebed in epoxy resin and endodontically treated (filled with guta percha and non-eugenol endodontic sealer). Following 7 days, the post spaces were prepared with low-speed post drills provided by the manufacturer (WhitePost DC #2, FGM) at a depth of 10 mm and the roots were randomly divided in 4 groups, according to cementation system and activations mode: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (total-etch), dual-cure (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, self-cure, (G3) RelyX U100 (self-adhesive), dual-cure and (G4) RelyX U100, self-cure. After 7 days, each root was sectioned with water-cooled diamond blade, generating six 1-mm thickness slices (n=60). Before push-out bond strength test, digital images of both sides of the slices were captured with digital camera, in order to measure the post radius and the cement thickness. After mechanical test, new images were captured to evaluate the failure mode. A macro was developed in KS 400 software to speed and standardize the evaluation of cement thickness. Results were analyzed using three-way ANOVA (push-out) and Kruskall-Wallis test (cement thickness). Post-hoc multiple comparisons were performed using the Student-Newman-Keuls test. The correlation between resin cement thickness and bond strength was evaluated with regression analysis, linear model. All tests were performed with significance level set at 0.05. Push-out bond strength was significantly influenced by cement type (p= 0.0402): the RelyX U100 cement presented higher mean value. The dual-activated mode increased the bond strength in comparison to self-activated mode (p < 0.0001). Statically differences were observed between groups: G1 (22.4 4.0 MPa) > G3 (20.4 3.6 MPa) > G4 (17.8 5.2 MPa) > G2 (13.5 4.3 MPa). Bond strength was not affected by post space depth (p = 0,4749). The resin cement thicknesses were significantly different in root thirds: cervical (102 45 m) > middle (75 29 m) > apical (52 28m). No strong correlation between cement thickness and push-out bond strength was observed (r = - 0.2016, p = 0.0033). The main failure mode was mixed, except for G2 (74% adhesive failures at post-cement interface). It was concluded tha the self-adhesive cement showed a better performance than the conventional one, and both dual resin systems, specially the RelyX ARC, presented photo-activation dependence to attain greater adhesive bond strength.

O presente estudo objetivou testar experimentalmente a existência da possível correlação entre a penetração de cimento nos túbulos dentinários e a qualidade do selamento. Foram utilizados 60 incisivos centrais superiores humanos que formaram um único grupo experimental. Após a eliminação das porções coronárias, as raízes foram padronizadas em 13 mm de comprimento. A instrumentação dos canais foi realizada no sentido coroa-ápice, e o comprimento de trabalho estabelecido a 1 mm aquém do forame apical. Como solução irrigadora foi empregado o NaOCl a 5,25% e ao final, EDTA a 17%. Em seguida, todos os canais foram obturados com guta-percha e cimento AH Plus marcado com um corante fluorescente. Para determinar a qualidade do selamento das obturações endodônticas, as amostras foram submetidas ao modelo de infiltração de glicose sob pressão. As raízes foram montadas em um dispositivo de dupla-câmara selada para permitir a infiltração da glicose. Como controle negativo foram utilizados 4 dentes hígidos, e como controle positivo, 2 dentes instrumentados porém, não obturados. Foram utilizados 0,75 mL de solução de glicose a 1 mol/L na câmara superior e 0,75 mL de água deionizada na câmara inferior. Os dispositivos foram conectados a um sistema de distribuição de pressão desenvolvido com o objetivo de permitir a infiltração de 32 amostras em uma mesma etapa. A solução de glicose foi forçada apicalmente sob uma pressão de 15 psi durante 1 hora. Uma alíquota de 50 L foi coletada da câmara inferior para quantificar a glicose infiltrada. A concentração de glicose foi determinada através de um método enzimático com o auxílio do Kit Glucose HK e de um espectrofotômetro em um comprimento de onda de 340 nm. Na sequência, as amostras foram desacopladas dos corpos de prova, embutidas em resina epóxi e cortadas em 3 secções transversais. Uma sequência de preparação metalográfica padrão foi realizada para permitir a observação da penetração de cimento nos túbulos dentinários por meio de microscopia confocal e óptica. Os dados obtidos nos 2 experimentos foram cruzados pelo teste de correlação de Spearman, o qual revelou a inexistência de qualquer possibilidade de correlação (r = 0,12). Com base nesses resultados, o presente trabalho concluiu que, dentro das condições experimentais usadas, a quantidade de cimento presente dentro dos túbulos dentinários não teve relação com a qualidade do selamento produzido. / The purpose of the present study was to experimentally test the potential correlation between tubular dentin sealer penetration and sealability. Sixty human maxillary central incisors were selected in order to compose a single experimental group. After removing of crowns, the roots were standardized at 13 mm in length. A crown-down root canal instrumentation was performed 1mm short of the apical foramen (working length). How irrigating solution was used 5.25% NaOCl and final, 17% EDTA. Then, all root canals were filled with gutta percha and AH Plus sealer labeled with a fluorescent dye. To determine the sealability pattern, samples were submitted to glucose leakage model under pressure. Four intact teeth were used as negative control while further 2 instrumented but nonfilled teeth was used as positive control. The roots were mounted in a double-chamber apparatus where 0,75 mL of 1 mol/L glucose solution was placed into the superior chamber and 0,75 mL of deionized water was placed into the inferior chamber. The devices were connected to a pressure distribution system that was developed in order to allow testing 32 specimens at the same experimental stage. The glucose solution was forced apically under a pressure of 15 psi during 1 hour. A sample of 50 L was taken from the inferior chamber and the glucose concentration was measured following an enzymatic reaction using a Glucose HK Kit readed under spectrophotometry (wave-length of 340 nm). After that, the samples were removed from the apparatus, embedded in epoxy resin and cut into 3 sections. Standard metallographic preparation was performed prior the observation of the sealer penetration into dentinal tubules by confocal and optical microscopy. Data provided by the evaluations were submitted to Spearman correlation test which revealed a lack of correlation between the two variables (r = 0.12). Therefore, the present study concluded that there was no correlation between tubular sealer penetration and sealability in non-bonding conventional root-fillings.

Submitted by PAULO ROBERTO MARÃO DE ANDRADE CARVALHO (DINTER) null (paulo@saolucas.edu.br) on 2017-02-13T19:20:07Z No. of bitstreams: 1 Tese Paulo Roberto Marao de Andrade Carvalho final.pdf: 1677819 bytes, checksum: c20c78af94d169f788debf8565ad1f21 (MD5) / Approved for entry into archive by Juliano Benedito Ferreira (julianoferreira@reitoria.unesp.br) on 2017-02-15T13:33:28Z (GMT) No. of bitstreams: 1 carvalho_prma_dr_araca.pdf: 1677819 bytes, checksum: c20c78af94d169f788debf8565ad1f21 (MD5) / Made available in DSpace on 2017-02-15T13:33:28Z (GMT). No. of bitstreams: 1 carvalho_prma_dr_araca.pdf: 1677819 bytes, checksum: c20c78af94d169f788debf8565ad1f21 (MD5) Previous issue date: 2016-12-19 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Introdução: O objetivo deste estudo clínico controlado, prospectivo, randomizado e com avaliadores cegos foi avaliar o desempenho clínico de restaurações cervicais não cariosas frente às diferentes estratégias de adesão ao substrato dental. Métodos: foram utilizados um sistema restaurador adesivo (Single Bond Universal/Z350XT) com e sem condicionamento seletivo do esmalte e um cimento de ionômero de vidro modificado por resina (Vitremer) com e sem tratamento prévio com EDTA, seguindo as instruções do CONSORT. Um total de 200 restaurações foram realizadas por dois operadores em 50 pacientes voluntários. Previamente à execução das restaurações e em cada tempo de avaliação foram avaliados os índices de sangramento gengival, placa visível e CPOD. Todas as restaurações foram avaliadas por meio do sistema de avaliação do USPHS modificado. Dois examinadores calibrados, cegos e diferentes dos operadores realizaram as avaliações nos seguintes intervalos de tempo: inicial imediato (baseline), 6, 12 e 24 meses. Ao final de 24 meses os dados foram analisados pelos testes estatísticos de Friedman, Qui-quadrado, Kappa, Cochran, Wilcoxon e análise de regressão logística múltipla, adotando-se nível de significância a 5%. Resultados: a amostra foi composta de 34 homens e 16 mulheres com idade média de 61,8 anos. Em relação ao CPOD, houve um aumento gradativo e significante ao longo do tempo, havendo diferença entre os quatro tempos de avaliação (p≤0,001). Não teve diferença entre os tempos para o índice de placa visível (p=0,28). No entanto, houve uma redução significativa do índice de sangramento gengival entre o baseline e os demais tempos (p≤0,001). Não houve diferença estatisticamente significante entre os 4 grupos em cada tempo de avaliação em nenhum dos critérios avaliados (p>0,05), assim como não houve entre os 4 tempos de avaliação para todos os grupos (p>0,05). Em relação à regressão logística, embora não tenha apresentado nenhuma variável isolada como estatisticamente significante, o modelo como um todo apresentou-se estatisticamente significante (p=0,034). Conclusão: As quatro diferentes estratégias de adesão em restaurações cervicais não cariosas apresentaram similar desempenho clínico após 24 meses de acompanhamento. / Introduction: the aim of this study, prospective, randomized controlled clinical trial and with blind evaluators was to evaluate the clinical performance of non-carious cervical restorations to different strategies of adhesion for the dental substrate. Methods: we used a restorative adhesive system (Universal/Z350XT Single Bond) with and without selective etching of enamel and a modified glass ionomer luting cement for resin (Vitremer) with and without previous treatment with EDTA, following the instructions of the CONSORT. 200 in total restorations were performed by two operators in 50 patients. Prior to the execution of the restorations and each time, we evaluated the evaluation indexes of gum bleeding, visibly Board and CPOD. All restorations were evaluated using the evaluation system USPHS modified. Two calibrated examiners, blind and different operators, performed the evaluations in the following time intervals: immediate initial (baseline), 6, 12 e 24 months. At the end of 24 months data were analyzed by statistical tests Friedman, Qui-quadrado, Kappa, Cochran, Wilcoxon and multiple logistic regression analysis, adopting the significance level 5%. Results: the sample was composed of 34 men and 16 women with an average age of 61.8 years. Concerning the CPOD, there was a gradual and significant increase over time, difference between the four evaluation times (p≤0,001). There was no difference between the time the visible card index (p=0,28). However, there was a significant reduction of gingival bleeding index between the baseline and other times (p≤0,001). There was no statistically significant difference among the 4 groups in each time any of the assessment criteria evaluated (p>0,05), just as happened with the 4 times of evaluation for all groups (p>0,05). With regards to the logistic regression, although it has not presented any isolated variable as statistically significant, the model as a whole showed statistically significant (p=0,034). Conclusion: The four different adhesive strategies in non-carious cervical restorations showed similar clinical performance after 24 months of follow-up. / FAPESP: 2014/07086-0

A resistência de união (RU) dos materiais deve ser avaliada após a degradação da interface adesiva, tentando simular um processo que ocorre naturalmente ao longo do tempo na cavidade bucal. O presente estudo avaliou a degradação da interface adesiva em diferentes materiais utilizando o modelo de envelhecimento in vitro e in situ em dentina hígida e cariada. Noventa segundos molares decíduos hígidos e sem defeitos de esmalte, foram aleatoriamente divididos em dois grupos de acordo com o substrato a ser testado (hígido e com lesão de cárie induzida). A seguir, cada um dos grupos foi subdividido aleatoriamente de acordo com o material restaurador (n=15): resina composta associada ao sistema adesivo - RC, cimento de ionômero de vidro modificado por resina - CIVMR e cimento de ionômero de vidro de alta viscosidade - CIVAV. A superfície da dentina foi preparada e com o auxílio de cânulas de polietileno, foram confeccionados os espécimes com os materiais restauradores. Partes de um mesmo dente foram submetidas a cada envelhecimento: in vitro (24 horas e 6 meses) - armazenados em água destilada à 37°C; e in situ (uso de dispositivo intraoral palatino por voluntários em uma fase experimental de 7 dias). Os espécimes foram submetidos ao teste de microcisalhamento (MPa) para avaliação da RU, seguido de análise do padrão de fratura em estereomicroscópio (400X). Os dados foram submetidos a análise de variância de medidas repetidas seguida pelo teste de Bonferroni (? = 5%). De forma geral, o armazenamento por seis meses em água degradou o grupo CIVMR em dentina hígida (<0,001) e RC em dentina cariada (p=0,007), para os outros materiais não houve diferença estatística (p=1,00). O modelo in situ influenciou negativamente os valores de RU nos grupos RC e CIVMR (p<0,001) no substrato hígido e na RC (p<0,001), CIVMR (p=0,001) e CIVAV p=0,020) no substrato cariado. Concluí-se que no modelo in vitro, seis meses em água destilada não foram suficientes para degradar a interface de união dos materiais avaliados e o modelo in situ é uma metodologia rápida que pode ser utilizada para avaliar a degradação da interface de união de materiais restauradores em dentina cariada de dentes decíduo. / Materials bond strength (BS) should be evaluated after degradation of the adhesive interface, simulating the intra-oral enviroment. This study assessed the degradation of the bonding interface of differents materials using in vitro and in situ models of aging in sound and caries - affected primary dentin. Ninety sound second primary molars without enamel defects were randomly assigned into two groups (sound and induced carious) according to the substrate to be tested. Then each group was subdivided according to the restorative material (n=15): composite resin associated with the adhesive system - CR, resin-modified glass ionomer cement - RMGIC or high-viscous glass ionomer cement- HVGIC. Dentin surface was prepared and with the aid of polyethylene tubes specimens of each restorative materials were prepared. Parts of a same tooth were subjected to in vitro and in situ models of aging. For in vitro model, the specimens were stored in distilled water at 37°C during 24 hours per 6 months; and for in situ model an intraoral palatal device was confectioned and used by volunteers in an experimental phase for 7 days. Specimens were submitted to microshear test (MPa) for BS evaluation and then stereomicroscopy (400X) analys of failure mode. Data were analyzed by repeated measures ANOVA for followed by Bonferroni test (? = 5%). In general, the storage for six months in distilled water degraded the RMGIC group in sound dentin (<0.001) and RC group in caries-affect dentin substrate (p = 0.007), for the others materials there was no statistical difference (p = 1.00). The in situ model, adversely, influenced the BS in RC and RMGIC groups (p <0.001) in sound substrate, and in RC (p <0.001), RMGIC (p = 0.001) and HVGIC (p = 0.020) in caries-affected dentin. We can concluded that in in vitro model, using six months distilled water, was not sufficient to degrade the bonded interface of the evaluated materials and in situ model is a faster method to evaluate degradation of the adhesion interface of restorative materials in cariesaffected dentin.

O objetivo deste estudo in vitro foi avaliar o potencial erosivo de suco de fruta amazônica ácida sobre a superfície dentinaria associado ao efeito abrasivo de diversos cremes dentais contendo agentes dessensibilizantes. O trabalho foi dividido em 3 fases distintas: Na fase 1, o valor do pH inicial de diversas frutas amazônicas foi medido utilizando 50 ml de cada suco, obtido de polpa industrializada. Foi utilizado um eletrodo de pH calibrado e a água destilada foi utilizada como controle. Na fase 2, 120 espécimes de dentina bovina foram submetidos a ciclos alternados de desafio abrasivo e erosivo, com a fruta escolhida na fase 1. Os espécimes foram divididos aleatoriamente em Grupo A (Desafio Abrasivo) e Grupo B (Desafio Erosivo e Abrasivo). Cada um destes grupos foram subdivididos em 5 subgrupos: 1: Água Destilada (Controle Negativo), 2: Colgate Tripla Ação (Controle Positivo), e os demais de acordo com o creme dental utilizado 3: Sensodyne Rápido Alívio, 4: Colgate Pró-Alivio e 5: Sensodyne Repair&Protect, (n=9). Na fase 3 foi realizado microscopia eletrônica de varredura para avaliar qualitativamente os espécimes (n=3). - O suco da fruta taperebá (Spondias mombin) apresentou os menores valores de pH, diante disso, foi escolhido como agente erosivo; Os testes de Kruskall Wallis e Teste de Dunn, mostraram que para os grupos nos quais somente a abrasão foi realizada, todos os cremes dentais mostraram comportamentos semelhantes em relação a perfilometria, não havendo diferença estatisticamente significante entre os grupos. Porém, para os grupos nos quais o processo erosivo foi adicionado, observou-se a potencialização do processo abrasivo, sendo que os cremes dentais Sensodyne Rápido Alivio e Colgate Sensitive Pro-Alivio foram os que mostraram menores alterações superficiais no padrão de perfilometria, comparados com o grupo controle negativo. Já os cremes dentais, Colgate Tripla Ação (controle positivo) e Sensodyne Repair&Protect apresentaram-se semelhantes entre si e com uma perda de estrutura dentinaria. mais significante. Conclui-se que o efeito erosivo da fruta amazônica taperebá é fator de grande importância na potencialização do efeito abrasivo, mesmo quando do uso de cremes dentais com agentes dessensibilizantes.. Na análise qualitativa da superfície dentinária em MEV, com exceção do Colgate tripla ação, os demais grupos não apresentaram oclusão tubular após o desafio ácido / The aim of this in vitro study was to evaluate the erosive potential of amazonian fruit juice with or without the abrasive challenge with various toothpastes containing desensitizing agents. The work was divided into three phases: in phase 1, the pH of various Amazonian fruits was evaluated. In step 2 it was performed surface perfilometry of the specimens, and in phase 3 it was evaluated qualitatively the dentin surface. In step 1, the initial pH value of several amazonian fruits was measured using 50 mL of each juice, from industrialized pulp. It was used a calibrated pH electrode, and distilled water was used as control. In step 2, 120 bovine dentin specimens were subjected to alternate cycles of abrasive and erosive challenge, with the fruit chosen in step 1. The specimens were randomly divided into Group A (without erosion) and Group B (with erosion). Each of these groups were divided into 5 groups: 1: Distilled Water, 2: Colgate Tripla Ação, 3: Sensodyne Rápido Alívio, 4: Pro-Alivio, 5: Sensodyne Repair & Protect, (n = 9). In Phase 3 it was conducted scanning electron microscopy to evaluate qualitatively the specimens (n=3). As a result it can be stated that: 1. The juice of the taperebá fruit had the lowest pH values, so it was chosen as the erosive agent; 2. For the groups in which only the abrasion was performed, all toothpastes showed similar behaviors, no statistically significant difference was observed between groups, but for the groups in which the erosion process was added, there was a potentiation of the abrasive process, and the toothpastes showed different profiles. The toothpaste Sensodyne Rapido Alívio Pró-Alívio was the ones that showed lower mineral loss, compared with the negative control group. Colgate Tripla Ação and Sensodyne Repair&Protect were similar among themselves and with a more significant mineral loss. It can be conclude that erosive effect of diet is a factor of great importance in the potentiation of abrasive effect. Clinical studies are essential to determine the dentin hypersensitivity levels after use of toothpaste used.