EFEITO DE DIFERENTES SOLUÇÕES IRRIGADORAS SOBRE A RESISTÊNCIA ADESIVA DE PINOS DE FIBRA DE VIDRO COM UTILIZAÇÃO DE CIMENTO AUTOADESIVO / NEGATIVE INFLUENCE OF DIFFERENT IRRIGANTS ON BOND STRENGH OF FIBER POSTS CEMENTED WITH A SELF-ADHESIVE CEMENTSeballos, Vívian Gehm 25 July 2016 (has links)
The purpose of this study is to evaluate the effect of different irrigatins on bond strength of fiber posts cemented with RelyX U200. Eighty single-rooted premolars were sectioned at 14 mm from the apex, prepared with ProTaper Universal system until F3 instrument, and filled with F3 master cone and AH Plus sealer. Root canal filling was partially removed, remaining 4 mm of guta-percha at the apical third. Specimens were randomly divided into 8 groups (n=10), according to the irrigant used during root canal preparation and before fiber post cementation (dentin surface treatment), as described: SS: 0,9% saline solution (control group); CHX: 2% chlorhexidine; 1%NaOCl: 1% sodium hypochlorite; 2,5%NaOCl: 2,5% sodium hypochlorite; 5%NaOCl: 5% sodium hypochlorite; 1%CaOCl: 1% calcium hypochlorite; 2,5%CaOCl: 2,5% calcium hypochlorite; e 5%CaOCl: 5% calcium hypochlorite. For each group, irrigation was performed continuously with 2ml. Exacto N2 glass fiber posts were cemented with RelyX U200. The specimens were sectioned providing 3 slices, one for each root third and the push-out test was performed. Optical microscopy was used to analyze the failure mode. Bond strength means were calculated and ANOVA and Bonferroni tests were used for statistical analysis. SS showed higher mean of bond strength values (11.47MPa), than all NaOCl and CaOCl groups, which showed similar values to CHX (7.56Mpa ± 2:47). Adhesive failures at cement/dentin interface were predominant (58.33%). NaOCl and CaOCl negatively affect the bond strength of fiber posts to root dentine when cemented with sef-adhesive resin cement; however the concentration of NaOCl and CaOCl did not affect this outcome. / Este estudo tem como objetivo avaliar o efeito de diferentes soluções irrigadoras sobre a resistência adesiva de pinos de fibra de vidro, cimentados com cimento autoadesivo RelyX U200. Foram utilizados 80 pré-molares inferiores humanos tiveram a coroa seccionada, padronizando-se o comprimento da raiz em 14 mm. Os condutos foram instrumentados com o sistema rotatório ProTaper até o instrumento F3, obturados com cimento endodôntico AH Plus e cones de guta-percha F3 do mesmo sistema, pela técnica do cone único. Os condutos foram desobturados até 10mm de profundidade, mantendo-se os 4mm apicais da obturação. As raízes foram aleatoriamente distribuídas em 8 grupos (n=10), de acordo com a solução irrigadora utilizada previamente à cimentação dos pinos: SS: solução salina 0,9% (grupo controle); CHX: clorexidina 2%; 1%NaOCl: hipoclorito de sódio 1%; 2,5%NaOCl: hipoclorito de sódio 2,5%; 5%NaOCl: hipoclorito de sódio 5%; 1%CaOCl: hipoclorito de cálcio 1%; 2,5%CaOCl: hipoclorito de cálcio 2,5%; e 5%CaOCl: hipoclorito de cálcio 5%. Para cada espécime, a irrigação foi realizada com 2ml da solução a cada troca de instrumento. Os pinos de fibra de vidro do Sistema Exacto Translúcido n02 foram silanizados e cimentados com o cimento resinoso autoadesivo RelyX U200. As raízes foram seccionadas na máquina de corte, de forma a obter 3 slices por espécime, sendo 1 slice para cada terço radicular. A seguir, os corpos de prova foram submetidos ao teste de push-out na máquina de ensaio universal EMIC. Para análise do padrão de falha, os espécimes foram analisados com microscopia óptica. A média de resistência adesiva de cada espécime foi calculada. Testes ANOVA e Bonferroni foram utilizados para analisar as diferenças entre os grupos. O grupo SS demonstrou a maior média de resistência adesiva, sendo superior aos grupos NaOCl e CaOCl (P <0.05), nos quais apresentaram valores semelhantes ao grupo CHX (7.56Mpa ± 2.47). As falhas adesivas cimento/dentina foram predominantes (58.33%). Concluímos que SS parece ser a solução mais adequada para limpeza do canal radicular previamente à cimentação de pinos de fibra cimentados com cimento autoadesivo RelyX U200. NaOCl e CaOCl diminuíram os valores de resistência adesiva dos pinos de fibra à dentina radicular e suas diferentes concentrações não afetaram este resultado.
|
82 |
Influência do intemperismo no mecanismo da fratura de compósitos soldados PEI/fibra de vidro /Marques, Luís Felipe Barbosa January 2020 (has links)
Orientador: Michelli Leali Costa / Resumo: Dentre os setores de aplicações comerciais de materiais compósitos avançados, destaca-se o setor aeroespacial com larga aplicação desses materiais. Entre as técnicas de união aplicadas aos compósitos termoplásticos está a soldagem com grandes vantagens em relação aos outros processos de uniões tais como, redução de custo, agilidade de processamento, redução de elementos acumuladores de tensão, preparações mais simplórias das superfícies a serem soldadas. Mesmo com essas vantagens e, embora o processo já seja utilizado nos setores industriais, a soldagem de compósitos tem como desafio a melhoria de sua resistência, a aplicação do processo para reparos ou processamentos em campo, além da necessidade de avaliação dos efeitos das condições climáticas em juntas soldadas, as quais podem estar submetidas quando em operação em uma aeronave, por exemplo. Mediante a isso, esse trabalho visa produzir e estudar juntas soldadas por resistência elétrica e por tocha acetilênica em compósito PEI/fibra de vidro. Os compósitos obtidos foram submetidos ao condicionamento higrotérmico seguido de ensaios mecânicos de LSS (Lap Shear Strength) e ENF (End-Notched Flexure). O mecanismo de fratura das juntas soldadas foi avaliado por microscopia. A partir das análises e dos resultados obtidos, foi observado que os valores de resistência ao cisalhamento em modo II dos compósitos soldados por resistência elétrica (3270,9 J/m²) são similares aos descritos na literatura para os compósitos PEI/fibra de vid... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Among the commercial application sectors of advanced composite materials, the aerospace sector with wide application of these materials stands out. Among the joining techniques applied to thermoplastic composites is welding with great advantages over other joining processes such as cost reduction, processing agility, reduction of stress accumulators, little or no preparation required of the surface to be processed. Even with these advantages, and although the process is already used in the industrial sectors, composite welding has the challenge of improving its resistance, the application of the process for field repairs or processing, and the need to evaluate the effects of weather conditions. welded joints, which may be subjected when operating in an aircraft, for example. Therefore, this work aims to produce and study joints welded by electric resistance and acetylene torch in PEI / fiberglass composite. The composites obtained were subjected to hygrothermal conditioning followed by mechanical tests of LSS (Lap Shear Strength) and ENF (End-Notched Flexure). The fracture mechanism of the welded joints was evaluated by microscopy. From the analyzes and results obtained, it was observed that the shear strength values in mode II of the composites welded by electric resistance (3270.9 J / m²) are similar to those described in the literature for PEI / fiberglass composites. However, for the composites welded by the oxyacetylene process, a reduction of approximately 20% in the va... (Complete abstract click electronic access below) / Mestre
|
83 |
[en] ANALYSIS OF THE HYGRO-THERMO-MECHANICAL BEHAVIOR OF PULTRUDED GLASS-FIBER REINFORCED POLYMER COMPOSITES / [pt] ANÁLISE DO COMPORTAMENTO HIGRO-TERMO-MECÂNICO DE MATERIAIS COMPÓSITOS PULTRUDADOS POLIMÉRICOS REFORÇADOS COM FIBRA DE VIDROPRISCILLA SHIMBA CARNEIRO VIEIRA 04 July 2023 (has links)
[pt] Materiais compósitos pultrudados poliméricos reforçados com fibra de
vidro (PRFV) são aplicados em diversos setores da indústria por apresentarem boas
resistências mecânicas, baixo peso específico e alta resistência à corrosão. A
exposição a ambientes agressivos tais como imersão em água, condicionamento sob
alta umidade relativa, temperatura baixa e elevada, ciclos térmicos e úmidos, bem
como a combinação desses efeitos, tornou-se cada vez mais objeto de estudo para
esses tipos de materiais. A compreensão dos efeitos das condições ambientais no
comportamento do material é essencial para avaliar seu desempenho e, desta forma,
garantir a segurança necessária ao projeto estrutural. Com o objetivo de
compreender melhor a influência de diferentes condições ambientais nas
propriedades do material compósito PRFV, foram estudados os efeitos da
temperatura e umidade, além da ação combinada dessas duas condições, nas suas
propriedades físicas, químicas, térmicas e mecânicas. Neste estudo, foram levados
em conta aspectos importantes que influenciam o comportamento do material,
como a resina utilizada, o grau de cura, e características químicas e físicas do
material. Os ensaios experimentais foram conduzidos em quatro condições
ambientais: (i) exposição a temperaturas moderadas/elevadas (70 graus C à 330 graus C), (ii)
imersão em água deionizada (25 graus C, 55 graus C e 70 graus C), (iii) exposição à névoa salina
em câmaras de envelhecimento higrotérmico (35 graus C, 55 graus C e 70 graus C), e (iv) exposição
a ambiente externo real. Além disso, foram aplicados modelos teóricos para
avaliação dos resultados. Foi observado que a temperatura, o tempo de
condicionamento e a umidade são fatores preponderantes no comportamento do
material. Adicionalmente, uma questão importante para o estudo de pultrudados
reside na compreensão das propriedades interlaminares do material. Nesse
contexto, a fratura interlaminar, associada às fissuras no plano longitudinal entre as
camadas do material, é uma das principais causas de falha em compósitos
pultrudados. Consequentemente, a análise da fratura em modo II, que avalia o
mecanismo da propagação da fissura no plano interlaminar, vem ganhando espaço
no estudo de materiais compósitos. A análise de fratura em modo II não é trivial ou
normatizada para compósitos pultrudados PRFV, de forma que poucos dados e
conclusões efetivas foram obtidos até o momento a esse respeito. Com o objetivo
de suprir essa lacuna, realizou-se uma extensa investigação experimental,
culminando na proposição de uma nova metodologia para avaliação da fratura em
modo II em materiais compósitos poliméricos pultrudados reforçados com fibra de
vidro (PRFV). / [en] Pultruded glass-fiber reinforced polymer (GFRP) composites are applied in
various industrial sectors due to their good mechanical strength, low specific
weight, and high resistance to corrosion. Exposure to aggressive environments has
become an increasingly studied topic for these materials, such as immersion in
water, conditioning under high relative humidity, low and high temperatures,
thermal and humid cycles, as well as the combination of these effects.
Understanding the effects of environment condition on material behavior is
essential to evaluate its performance and ensure the necessary safety for structural
design. In order to better understand the influence of environmental conditions on
the properties of GFRPs, the effects of temperature and humidity, as well as the
combined action of these two effects, on their physical, chemical, thermal, and
mechanical properties were studied. Important aspects that influence the material s
behavior were considered, such as the resin used, the degree of curing, and the
chemical and physical characteristics of the material. Experimental tests were
conducted under four environmental conditions: (i) exposure to moderate/high
temperatures (70 degrees C to 330 degrees C), (ii) immersion in deionized water (25 degrees C, 55 degrees C,
and 70 degrees C), (iii) exposure to salt spray in hygrothermal aging chambers (35 degrees C, 55
degrees C, and 70 degrees C), and (iv) exposure to real outdoor environment. In addition,
theoretical models were applied to evaluate the results. It was observed that
temperature, conditioning time, and moisture are predominant factors in material
behavior. Additionally, a important issue for the study of pultruded composites lies
in understanding the interlaminar properties of the material. In this context,
interlaminar fracture, associated with longitudinal cracks between the layers of the
material, is one of the main causes of failure in pultruded composites.
Consequently, mode II fracture analysis, which evaluates the mechanism of crack
propagation in the interlaminar plane, has been gaining ground in the study of
composite materials. Mode II fracture analysis is not trivial or standardized for
pultruded GFRP composites, so few data and effective conclusions have been
obtained in this regard so far. In order to fill this gap, an extensive experimental
investigation was carried out, culminating in the proposal of a new methodology
for evaluating mode II fracture in pultruded GFRPs.
|
84 |
[pt] COMPORTAMENTO MECÂNICO DE UMA TUBULAÇÃO COMPÓSITA REFORÇADA COM FIBRA DE VIDRO E CARBONO SOB EFEITO DE ENVELHECIMENTO TÉRMICO / [en] MECHANICAL BEHAVIOR OF COMPOSITE PIPELINE REINFORCED WITH FIBERGLASS AND CARBON FIBERS DUE TO EXPOSURE TO THERMAL AGINGLEONARDO MEIRA OTTOLINI 01 October 2019 (has links)
[pt] Tubulações compósitas têm sido empregadas na indústria para substituir as tubulações fabricadas com os materiais convencionais de engenharia, como o aço. O baixo peso específico, elevada resistência química e mecânica, bem como o menor custo de instalação e manutenção são vantagens que justificam o uso e aprimoramento desses materiais. Os materiais compósitos mais empregados para a fabricação de tubulações são os compósitos de matriz polimérica reforçados com fibras. Durante o tempo de serviço, as tubulações compósitas que são utilizadas no setor de óleo e gás estão sujeitas a ambientes agressivos e intempéries, como exposição a altas temperaturas, umidade e diversos produtos químicos. A temperatura e a absorção de fluidos são as principais causas da degradação das propriedades físicas e químicas desses materiais, reduzindo a resistência mecânica e, consequentemente, a vida útil das tubulações em serviço. Portanto, este trabalho teve o objetivo de avaliar durante o período de 12 meses o efeito dos agentes de degradação em uma tubulação compósita de resina epóxi reforçada com fibras de vidro e carbono. Para tal, amostras da tubulação foram submetidas à temperatura, água, óleo lubrificante e pressão hidrostática. O comportamento mecânico foi avaliado a partir do ensaio de achatamento sob placas paralelas, ensaio sonoro, ensaio colorimétrico, análise de absorção de fluidos, análise térmica e microestrutural. Ao final do experimento foi constatado que todas as condições de envelhecimento causaram degradação similar, com redução das propriedades mecânicas e térmicas, bem como a plastificação da matriz polimérica. / [en] Composite pipes has been used in the industry to replace conventional pipes commonly manufactured with steel. The lower specific weight, high chemical and mechanical resistance, as well as the low cost of installation and maintenance are the advantages that warrant the use of this materials and their development. The most common composite materials used for the manufacture of pipes are the polymer matrix composites reinforced with fiber. During their lifetime, the composite pipes used in the oil and gas facilities are subject to aggressive environments, such as exposure to high temperatures, moisture and various chemical products. Temperature and fluid absorption are the principal causes of degradation of physical and chemical properties of these materials, reducing their mechanical resistance and, consequently, the lifetime of the pipes in service. Therefore, the main objective of this work was to evaluate the effect of degradation agents on an epoxy composite pipe reinforced with fiberglass and carbon fibers for a period of 12 months. To achieve this objective, samples of the composite pipe were submitted to temperature, tap water, lubricant oil and hydrostatical pressure. The mechanical behavior was evaluated using parallel-plate test, sound test, colorimetric test, fluid absorption analysis, thermal and microstructural analysis. At the end of the experimental procedure it was verified that all the aging conditions caused similar degradation, with reduction of the mechanical and thermal properties, as well as the plasticization of the polymeric matrix.
|
85 |
Efeito do tipo de cimento de fixação e configurações de retentores intra-radiculares na adesão à dentina radicular em diferentes profundidadesPereira, Janaina Carla 21 August 2007 (has links)
Fundação de Amparo a Pesquisa do Estado de Minas Gerais / This study evaluated the effect of different types of luting cement and post
configuration on the bonding to intra-radicular dentin in different depths. One
hundred and twenty roots received endodontic treatment and were post space
preparation for fixation of glass fiber post in the configurations: serrated/parallel
Reforpost X-Ray (S); and smooth/conical Exato Cônico (L). The posts were fixed
with cements: RelyX ARC (ARC), RelyX Luting 2 (LU), RelyX Unicem (UN),
Maxicem (MAX) and Cement-Post (CP). The roots were sectioned transversally,
getting two disks of 1mm of thickness for third of the root portion: cervical (C),
medium (M) and apical (A), and submitted to the micropush-out test with speed of
0.5mm/min. The bond strength values (MPa) were submitted to the analysis of
variance in scheme of subdivided parcel and Tukey test (p0.05). There was
significant difference among the cements types (p<0.0001), among the
localizations (p<0.0001) and the interaction cement x localization was significant
(p<0.0001). The post configuration did not influence the bond strength values. The
cements LU and UN presented the highest values of bonding in all extension of
root dentin. The cements ARC and CP presented similar bonding values in cervical
third, however, the bond strength decreased in the crown-apex direction for the
ARC. The cement MAX presented the lowest values of bonding. / Este estudo avaliou o efeito do tipo de cimento de fixação e da configuração de
retentores intra-radiculares na adesão à dentina intra-radicular em diferentes
profundidades. Cento e vinte raízes receberam tratamento endodôntico e foram
aliviadas para fixação de retentores intra-radiculares de fibra de vidro nas
configurações: serrilhado/paralelo Reforpost X-Ray (S); e liso/cônico Exato Cônico
(L). Os pinos foram fixados com cimentos: RelyX ARC (ARC), RelyX Luting 2 (LU),
RelyX Unicem (UN), Maxicem (MAX) e Cement-Post (CP). As raízes foram
seccionadas transversalmente, obtendo-se 2 discos de 1mm de espessura por
terço da porção radicular aliviada: cervical (C), médio (M) e apical (A), e
submetidos ao teste de micropush-out com velocidade de 0,5mm/min. Os valores
de resistência adesiva (MPa) foram submetidos à análise de variância em
esquema de parcela subdividida e teste de Tukey (p<0,05). Houve diferença
significativa entre os tipos de cimentos (p<0,0001), entre as localizações
(p<0,0001) e a interação cimento x localização foi significativa (p<0,0001). A
configuração do pino não influenciou nos valores de resistência adesiva. Os
cimentos LU e UN apresentaram os maiores valores de adesão em toda extensão
da dentina radicular. Os cimentos ARC e CP apresentaram valores de adesão no
terço cervical semelhantes, contudo, a resistência adesiva decresceu no sentido
coroa-ápice para o ARC. O cimento MAX apresentou os menores valores de
adesão. / Mestre em Odontologia
|
86 |
Efeito do número de pinos de fibra de vidro na resistência à fratura, deformação estrutural e distribuição de tensão em molares tratados endodonticamenteBarcelos, Luciana Mendes 12 February 2016 (has links)
Conselho Nacional de Desenvolvimento Científico e Tecnológico / The aim of this study was to evaluate the biomechanical effect of the presence
and number of fibreglass post in endodontically treated molars restored with
composite resin. 45 human molars were selected, included in polystyrene resin
cylinders with simulation of the periodontal ligament and endodontically treated.
These teeth were randomized into three groups (n = 15): Wfgp, without
fibreglass post and restored with Filtek Z350 XT; 1fgp, 1 fiberglass post Exact
#2 cemented in the distal root with RelyX U200 and restored with Z350XT; and
2fgp, 2 fiberglass posts cemented with RelyX U200, one in the distal root and
the other in the mesiobuccal root, restored with Z350XT. The specimens were
submitted to mechanical fatigue with axial load of 50N. The tooth remaining
deformation was measured using extensometers (n = 10) during occlusal
loading of 100N and then until fracture. The other teeth (n = 5) were used to
calculate the modulus of elasticity (GPa) and Vickers hardness (VH, N/mm2) of
the enamel, dentin composite resin and fiberglass post in two positions:
parallelly and transversally to the long axis of the post. The stress distribution
was analyzed using three dimensional finite elements model, generated from
micro-CT image of an intact tooth with its geometry similar of those used in the
in vitro study. The calculated mechanical properties were used to characterize
models of finite element analysis. The data of deformation and fracture
resistance were tested for normality (Shapiro-Wilk) and equivalence of
variances (test Levene), followed by parametric statistical tests appropriated for
each test. One way Anova was performed for the axial compressive strength
values, tooth remaining deformation and fracture resistance. Multiple
comparisons were performed using Tukey test. The mean fracture data were
submitted to the Chi-square test. Factorial analysis of variance on two factors
was carried out considering as factors in study: the tooth surface deformation (B
and L) and rehabilitation technique. All tests done had significance level α =
0.05 and all analyses were performed with the statistical program Sigma Plot
version 13.1 (Systat Software, San Jose, CA, USA). The use of two fiber glass
posts resulted in lower fracture resistance than the groups without fiber glass
- 22 -
post and with one fiber glass post. During occlusal loading of 100N lingual
surface of the remaining tooth showed higher deformation for all groups. The
absence of fiber glass post resulted in significantly higher values of stress in the
root and more irreparable fracture modes than the other groups. The use of a
fiber glass post resulted in better ratio deformation/fracture resistance. The
concentration of stress in the furcation area was slightly reduced with use of
fiber glass post. It is concluded that the use of one fiber glass post to
rehabilitated molars with direct composite resin showed higher resistance to
fracture than the use of two fiberglass posts, lower tooth remaining
deformation, better stress distribution and failure pat more repairable when
compared to molars restored without use of fiber-glass post / O objetivo deste trabalho foi avaliar o efeito biomecânico da presença e do
número de pinos de fibra de vidro em molares tratados endodonticamente e
restaurados de forma direta com resina composta. Quarenta e cinco molares
humanos foram selecionados, incluídos em cilindros de resina de poliestireno
com simulação do ligamento periodontal e tratados endodonticamente. Estes
dentes foram randomizados em três grupos (n=15): Spfv, sem pino de fibra de
vidro, restaurado com Filtek Z350XT; 1pfv, 1 pino de fibra de vidro Exacto Nº 2
cimentado no canal distal com RelyX U200 restaurado com Z350XT; e 2pfv, 2
pinos de fibra de vidro Exacto Nº 2 cimentados com RelyX U200, um no canal
distal e o outro no mesio-vestibular restaurado com Z350XT. As amostras
foram submetidas à fadiga mecânica com carregamento axial de 50N. A
deformação do remanescente foi mensurada usando extensômetros (n=10)
durante o carregamento oclusal de 100N e em seguida até o momento de
fratura. Os demais dentes (n=5) foram usados para calcular o módulo de
elasticidade (E, GPa) e dureza Vickers (VH, N/mm2) do esmalte, dentina, resina
composta e pino de fibra de vidro em duas posições: paralelamente e
transversalmente ao longo eixo do pino. A distribuição de tensões foi analisada
usando modelo tridimensional de elementos finitos gerado a partir de imagem
de micro-CT de um dente hígido com medidas e geometrias representativo das
amostras usadas na etapa experimental. Às propriedades mecânicas
calculadas foram utilizadas para caracterizar os modelos da análise por
elementos finitos. Os dados de deformação e resistência à fratura foram
submetidos à teste de normalidade (Shapiro-Wilk) e equivalência de variâncias
(teste de Levene), seguido por testes estatísticos paramétricos adequados para
cada tipo de ensaio. Análise de variância em fator único foi realizada para os
valores de resistência à compressão axial, deformação do remanescente e
resistência à fratura. Comparações múltiplas foram realizadas usando teste de
Tukey. Os dados de padrão de fratura foram submetidos ao teste Quiquadrado.
Análise de variância fatorial em dois fatores foi realizada
considerando como fatores em estudo: deformação da superfície do
remanescente (V e L) e a técnica de reabilitação. Todos os testes empregados
- 19 -
tiveram nível de significância α=0,05 e todas as análises foram realizadas com
o programa estatístico Sigma Plot versão 13.1 (Systat Software Ins, San Jose,
CA, USA). O uso de dois pinos de fibra de vidro resultou em menor resistência
à fratura que os grupos sem pino de fibra de vidro e com um pino de fibra de
vidro. Durante o carregamento oclusal de 100N a superfície lingual do
remanescente demonstrou maior deformação para todos os grupos. A
ausência de pino de fibra de vidro resultou em valores significativamente mais
elevados de tensões na dentina radicular e modos de fratura irreparáveis
significativamente maiores que os outros grupos. O uso de um pino de fibra de
vidro resultou em melhor razão deformação/resistência fratura. A concentração
de tensão na área de furca foi ligeiramente reduzida com uso de pino de fibra
de vidro. Conclui-se que o uso de um pino de fibra de vidro para reabilitar
molares inferiores com resina composta direta mostrou maior resistência à
fratura que o uso de dois pinos de fibra de vidro, menor deformação do
remanescente, melhor distribuição de tensões e padrão de falha com maior
número de fraturas reparáveis quando comparado a molares restaurados sem
uso de pino de fibra de vidro / Mestre em Odontologia
|
87 |
Substituição do alumínio pelo compósito de poliamida no suporte do coxim motorSilva, Leandro Cardoso da 27 January 2014 (has links)
Made available in DSpace on 2016-03-15T19:36:41Z (GMT). No. of bitstreams: 1
Leandro Cardoso da Silva.pdf: 4262718 bytes, checksum: ac43795cdc56049895a5038a95097702 (MD5)
Previous issue date: 2014-01-27 / Mounts are considered structural parts. Generally, mounts utilize metals such as aluminum and steel. These metals have high fatigue strength and its degradation temperature transmitted
by the engines is very small. This work aimed to study the replacement of the aluminum mounts engine by glass fiber reinforced polyamide composite in order to reduce the mass.
Polyamide reinforced with fiberglass is the choice that offers the best compromise of a recyclable material, with adequate thermal and fatigue resistance. The composite used was the commercial polyamide PA66 with 0%, 30%, 35%, 50% glass fiber. This study will focus mainly on the fatigue properties of the composite at temperatures of engine operation. The fatigue tests of the composite with glass fiber additions were performed on flexure specimens at 120°C. The fatigue behavior of the composite was analyzed using the staircase method. The results obtained in fatigue tests showed that the polyamide with 50% glass fiber has the lowest deflection. The observations of the fracture surfaces of the tested specimens were made by Scanning Electron Microscopy (SEM). These observations by SEM showed an excellent adhesion of glass fiber in the polyamide. Analyzes will also be conducted by simulation using the Finite Element Method (FEM) from fatigue results and the conditions of use of the component. The comparison by the FEM of the mounts manufactured of glass fiber reinforced polyamide composite and of aluminum alloy indicated similar results with respect to stress
levels. The fatigue tests results and of the simulation by finite element method showed a good possibility of substitution of the aluminum alloy by glass fiber reinforced polyamide composite in the mounts, with a reduction in weight of 0.2 kg (32%). / Os coxins são considerados dentro das classificações automobilísticas como peças estruturais. Geralmente, os coxins utilizam metais como o alumínio e o aço em seus suportes. Esses
metais oferecem grande resistência à fadiga e sua degradação na temperatura transmitida pelos motores é muito pequena. Devido à necessidade de diminuir a massa e reduzir o custo,
este trabalho teve como objetivo estudar a substituição do suporte de alumínio do coxim do motor pelo compósito de poliamida reforçado com fibra de vidro. O compósito de poliamida é a escolha que melhor oferece o compromisso de um material reciclável, com resistência térmica e à fadiga, devido às suas propriedades mecânicas serem comparáveis às do alumínio.
O compósito utilizado foi à poliamida comercial PA 6.6 com 0%, 30%, 35%, 50% de fibra de vidro. Este estudo focará principalmente nas propriedades em fadiga do compósito nas
temperaturas de trabalho e nas análises de simulação decorrentes das propriedades obtidas e das condições de utilização do componente. Os ensaios de fadiga do compósito de poliamida com adições de porcentagens variadas de fibra de vidro foram executados em corpos de prova do tipo de flexão a 120°C. O comportamento em fadiga do compósito foi analisado
utilizando-se o método staircase. As observações das superfícies de fratura dos corpos de prova ensaiados foram feitas por microscopia eletrônica de varredura e evidenciaram a
excelente aderência da poliamida na fibra de vidro. Os resultados obtidos nos ensaios de fadiga, esforços máximos e esforços excepcionais permitiram concluir que o compósito de poliamida com 50% de fibra de vidro apresenta a menor deflexão. A comparação pelo Método de Elementos Finitos do suporte do coxim do motor em compósito de poliamida com reforço
de fibra de vidro e da liga de alumínio indicou, de uma maneira geral, resultados similares com relação aos níveis de tensão. Contudo, os valores de deflexão apresentaram valores
sistematicamente maiores no compósito. Os resultados dos ensaios mostram um bom comportamento do compósito de poliamida, dando indícios sobre a viabilidade de utilização
na substituição da liga de alumínio, com uma redução em massa de 0,2 kg (32%).
|
88 |
Fibra de vidro recoberta com ZnO como suporte para análise de trihalometanos por HS-SPME-CG / Glass fiber recovered with ZnO as suport to trihalomethanes analysis by HS-SPME-CGFavreto, Wagner Alex Jann 28 November 2008 (has links)
Made available in DSpace on 2017-07-10T18:08:12Z (GMT). No. of bitstreams: 1
Wagner Alex Jann Favreto.pdf: 2401353 bytes, checksum: 8e382cf32a6bec4d2e8a69fffdafffff (MD5)
Previous issue date: 2008-11-28 / In the present work we describe the methodology to obtain and modify the surface of glass fibers composed by Li2O - ZrO2 - BaO - SiO2 with zinc oxide.
The glass fibers were obtained by classical fusion followed by the stretch of the vitreous fused mass, where the diameter of the fibers was controlled by the stretching velocity. They were recovered with ZnO by dip-coating and sol-gel processing of deposition, using both inorganic and organic polymeric gel methods, where the zinc acetate dihydrate was the zinc oxide precursor.
The superficial morphology of the fiber was verified by scanning electron microscopy (SEM) and the zinc oxide layer was characterized by mapping of Kα and Lα lines of the zinc by EDX analyses.
The results of the SEM characterization pointed out the deposition of ZnO by inorganic polymeric gel method results in a thick layer of the oxide without apparent porosity, while by the organic polymeric gel method results a dip homogeneous and porous layer of ZnO over the glass fiber surface.
The glass fibers recovered with ZnO by organic polymeric gel were used to develop an analytical methodology to simultaneous determination of trihalomethanes (THM´s) in drinking water using headspace-SPME-Gas Chromatography. The study was based on the selectivity, linearity, accuracy, precision and recovery of the analytical method using the glass fiber/ZnO. The effect of the salt addition, extraction temperature and extraction, desorption and incubated time on the analytical response were evaluated too. Good linear dynamic range was observed from the method quantification limits with correlation coefficients better than 0.9900 for all compounds. The method was accurate with recoveries ranging from 95,00 to 105,00%. and the range of linearity observed was 30 ng/mL to 500 ng/mL to trichloromethane, 20 ng/mL to 250 ng/mL to dichlorobromomethane and dibromochloromethane and 10 ng/mL to 100 ng/mL to tribromethane. The method is also robust and has great potential to be used in a trihalomethane determination. / No presente trabalho encontram-se descritas a metodologia para obtenção, e para a modificação da superfície de fibras de vidro de composição Li2O - ZrO2 - BaO - SiO2 com óxido de zinco.
As fibras de vidro foram obtidas pelo método de fusão clássico, seguido do estiramento da massa vítrea fundida, controlando-se o diâmetro através da velocidade de estiramento. Estas foram recobertas com ZnO, utilizando-se da técnica sol-gel em dip-coating controlado, usando-se os métodos de deposição do gel polimérico inorgânico e do gel polimérico orgânico, onde o acetato de zinco di-hidratado foi empregado como reagente precursor do óxido de zinco.
Utilizou-se a técnica de Microscopia Eletrônica de Varredura (MEV) para avaliar a morfologia das fibras sem recobrimento e das fibras recobertas. O recobrimento com óxido de zinco sobre a superfície das fibras, foi mapeado através das linhas Kα e Lα do zinco, por Microssonda de Energia Dispersiva (EDS), sendo observado uma camada regular de ZnO sobre a superfície do suporte.
Através dos resultados obtidos por MEV, verificou-se que pela técnica de deposição do gel polimérico inorgânico as fibras apresentam recobrimento bastante espesso, mas sem porosidade aparente. Quanto à técnica de deposição do gel polimérico orgânico, obtem-se fibras com um recobrimento mais homogêneo, espesso e poroso.
Desta forma utilizaram-se as fibras recobertas pelo método do gel polimérico orgânico, para o desenvolvimento de metodologia analítica para determinações cromatográficas de trihalometanos (THM s) em solução aquosa. Utilizou-se da técnica de extração em head-space (HS) por Microextração em Fase Sólida (SPME) (HS-SPME) conjugada a Cromatografia Gasosa (CG). O estudo foi baseado na seletividade, linearidades, exatidão, precisão e na recuperação do método analítico usando a fibra de vidro/ZnO. O efeito da adição de sal, temperatura e tempo de extração, tempo de dessorção e o tempo de incubação na resposta analítica. O bom alcance dinâmico linear, foi observado nos limites da quantificação do método com coeficientes de correlação maiores que 0,99 observados para todos os compostos. O método demonstrou-se exato e com a recuperações que variam de 95,00 a 105,00% com escala de linearidades observadas entre 30 ng/mL a 500 ng/mL para o triclorometano, 20 ng/mL a 250 ng/mL ao diclorobromometano e o dibromoclorometano e 10 ng/mL a 100 ng/mL para o tribromometano. O método apresentou-se robusto, e possui grande potencial para ser usado em determinações de trihalometanos.
|
89 |
Desenvolvimento de suportes vítreos e vitrocerâmicos baseados no sistema Li2O-BaO-SiO2 mofificados pelos óxidos Nb2O5, TiO2, V2O5 e ZrO2, para microextração em fase sólida (SPME-CG) / Development of new glass and glass-ceramics supports for solid phase microextraction (SPME-CG)Percio, Maycon Fernando 28 February 2012 (has links)
Made available in DSpace on 2017-07-10T18:08:21Z (GMT). No. of bitstreams: 1
Maycon Fernando Percio.pdf: 4386871 bytes, checksum: fd68bea53c4d4cbfe32a314a01715c6e (MD5)
Previous issue date: 2012-02-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In the present work a vitreous composition based on combination of the oxides BaO-SiO2-Li2O modified by adding of oxides Nb2O5, TiO2, V2O5 and ZrO2 as nucleating agent was evaluated and used in the manufacture of glass and glass-ceramic fibers for use in SPME-CG. The stability of the resulting glasses was accompained by X-ray diffraction (XRD) and differential thermal analysis (DTA). The stability parameters of Weinberg (KW), Hubrÿ (KH), Lu e Liu (KLL), Du and Huang (KDU) and Saad and Poulain (KSP) were obtained by DTA data. By KSP was observed that stability of glassy phases follows the descending order: Composition 5 (ZrO2) > Composition 2 (Nb2O5) > Composition 1 (without nucleant) > Composition 4 (V2O5) > Composition 3 (TiO2). Through these data it was possible to determine the apparent activation energies of the crystallization process by the crystallization peaks of the DTA curves, whereby the decreasing order was obtained: Composition 5 (ZrO2)> Composition 4 (V2O5) > Composition 2 (Nb2O5) > Composition 3 (TiO2) > Composition 1 (without nucleant). It was found, through the Avrami index, a surface crystallization mechanism of the compositions that leads to a correspondent transition to the glass ceramic. From DRX data obtained after thermal treatment at varying time, the TTT diagrams (Time, Temperature and Transformation) of the compositions were constructed, which delimited the conditions for preparation of glass ceramic fibers. The XRD analysis indicated that the main crystalline phases formed after heat treatments are rhombic Li2SiO3 Li2Si2O5. The fibers obtained were further tested in chromatographic analysis by HS-SPME-GC of the methanol in aqueous solution at concentrations of 10 and 100 mgL-1 with satisfactory results. / No presente trabalho, foram estudadas composições vítreas baseada na combinação dos óxidos Li2O-BaO-SiO2 modificadas pelos óxidos Nb2O5, TiO2, V2O5 e ZrO2, utilizados como nucleantes na fabricação de fibras de vidro e vitrocerâmicas para a utilização em SPME-CG. Determinou-se a estabilidade vítrea para cada composição através da difração de raio-X (DRX) e análise térmica diferencial (DTA) sendo observada a estabilidade das fases vítreas na ordem decrescente: Composição 5 (ZrO2) > Composição 2 (Nb2O5) > Composição 1 (sem nucleante) > Composição 4 (V2O5) > Composição 3 (TiO2). Através destes dados foi possível determinar as energias de ativação aparente das fases cristalinas através dos picos de cristalização das curvas de DTA, cuja ordem decrescente obtida foi: Composição 5 (ZrO2) > Composição 4 (V2O5) > Composição 2 (Nb2O5) > Composição 3 (TiO2) > Composição 1 (sem nucleante). Verificou-se através do índice de Avrami que as composições vítreas obtidas apresentaram mecanismo de nucleação de superfície para a formação do vitrocerâmico. Os dados de DTA possibilitaram a obtenção de diagramas de Tempo, Temperatura e Transformação (TTT), que delimitaram as condições de preparo das fibras vitrocerâmicas. Foram fabricados 5 tipos diferentes de fibras vítreas (Fibras A), que após tratamento térmico deram origem a fibras vitrocêramicas parcialmente cristalizadas (Fibras B) e fibras vitrocerâmicas totalmente cristalizadas (Fibras C), resultando um total de 15 espécies de fibras de composições e estruturas cristalinas diferentes. As análises por DRX indicaram que as principais fases cristalinas formadas depois dos tratamentos térmicos são Li2SiO3 e Li2Si2O5 ortorrômbicos. As fibras obtidas foram ainda testadas em análises cromatográficas por Cromatografia Gasosa na extração de metanol em solução aquosa nas concentrações de 10 e 100 mgL-1 com resultados satisfatórios.
|
90 |
Restauração de dentes tratados endodonticamente: ensaio clínico randomizado e revisão sistemática com metánalise / Restoration of endodontically treated teeth: a randomized clinical trial and a systematic review with meta-analysisOnofre, Rafael Sarkis 13 December 2012 (has links)
Made available in DSpace on 2014-08-20T14:30:09Z (GMT). No. of bitstreams: 1
Dissertacao_rafael_sarkis_onofre.pdf: 1491340 bytes, checksum: 00453dc2916d638be0bec47f9d29aa11 (MD5)
Previous issue date: 2012-12-13 / The best way to restore endodontically treated teeth has been discussed in the literature because some factors can influence the post selection and the final restoration. Two of the most used intra-radicular posts are cast metal posts and glass fiber posts. Moreover, there is a large variability of in vitro studies that evaluate the use of different resin cement and the alterations of technique and the influence in the bond strength of glass fiber posts. The aims of the study were to compare the survival of two types of dental posts used to restore endodontically treated teeth with great damage of coronal walls and verify through a systematic review if there is difference on bond strength of glass fiber posts to dentin between self-adhesive and regular resin cements. Systematic review: In vitro studies that investigated the bond strength of glass fiber post luted with self-adhesive (RC) and regular (RC) were selected. Global comparison between self-adhesive (RC) and regular resin cement was performed. Two subgroup analyses were performed: self-adhesive resin cement x regular resin cement (etch-and-rinse adhesive), self-adhesive resin cement x regular resin cement (self-etch adhesive). The three analyses performed showed favorable results to self-adhesive resin cement. Clinical trial: The teeth were randomly allocated into two groups depending on the post used: glass fiber or cast metal post. Fifty-four (45 women) patients and 72 teeth were evaluated up to 3 years and the survival probabilities were 97.1% and 91.9% to cast metal posts and glass fiber posts. Four failures were observed, 2 glass fiber posts debonding (premolar and anterior tooth), 1 glass fiber post debonding associate with root fracture and 1 root fracture with a cast metal post. We can conclude that in vitro literature seems to suggest that the use of self-adhesive cement could help to achieve higher bond strength of GFPs to the root canal and after 3 years of follow up, both posts presented the same clinical performance and / A melhor maneira de se restaurar dentes tratados endodonticamente vem sendo muito discutida na literatura principalmente porque alguns fatores como a escolha do pino a ser utilizado pode influenciar o resultado final da restauração. Dois dos retentores intra-radiculares mais utilizados atualmente são os núcleos metálicos fundidos e os pinos de fibra de vidro. Além disso, existe uma grande variabilidade de estudos in vitro que avaliam tanto a utilização de diferentes cimentos resinosos como alterações das técnicas e a influência na resistência de união de pinos de fibra de vidro. O objetivo deste trabalho foi avaliar as taxas de sucesso clínico de dentes tratados endodonticamente sem remanescente coronário e restaurados com de pino de fibra de vidro ou núcleo metálico fundido através de um ensaio clínico randomizado. Além disso, realizar uma revisão sistemática da literatura de ensaios in vitro que comparassem a resistência de união de pinos de fibra de vidro cimentados com cimento resinoso regular e cimento resinoso autoadesivo. Para a revisão sistemática, estudos in vitro que avaliaram a resistência de união de pinos de fibra de vidro cimentados com cimento autoadesivo e cimento regular foram selecionados. As seguintes metánalises foram realizadas: comparação global entre cimento autoadesivo x cimento regular e análises de subgrupo cimento autoadesivo x cimento regular (adesivo etch-and-rinse) e cimento autoadesivo x cimento regular (adesivo self-etch). As três análises mostraram resultados estatisticamente significantes e favorecendo o uso de cimento autoadesivo. No ensaio clínico, os dentes selecionados foram randomizados e alocados em 2 grupos dependendo do pino utilizado. Após 3 anos, 54 pacientes (72 dentes: 35 núcleos metálicos fundidos e 37 pinos de fibra de vidro) foram avaliados. As taxas de sobrevivência foram 97,1% e 91,9% para núcleos metálicos fundidos e pinos de fibra de vidro respectivamente. Quatro falhas foram observadas: duas descimentações de pinos de fibra de vidro (pré-molar e dente anterior), uma descimentação de pino de fibra de vidro associada a fratura radicular (pré-molar) e uma fratura radicular associada ao uso de núcleo metálico fundido (molar). Conclui-se que a literatura sugere que o uso de cimento resinoso autoadesivo poderia ajudar a conseguir maior resistência de pinos de fibra vidro ao canal radicular e que após 3 anos, ambos os pinos apresentaram performance semelhante
|