The focus of this study is aimed at the traditional building material; clay, together withsheep’s wool to act as reinforcement. The combination of the two materials created thebasis for an alternative board material. Soil-based building materials were used to alarge extent in the past. The oldest clay houses found were built as early as 8000 yearsBC. During the Middle Ages in Central Europe, soil and clay were used as fillers in timberframe structures. As new building materials evolved, clay based building methodshave suffered a more secluded position in the western world. New building materialshave caused the characteristics of traditional building materials to be forgotten. Sheep’swool, unlike clay, has previously not been classified as a building material, but ismostly used for textiles. Sheep are bred generally for two purposes; meat productionand wool production. The wool that comes from sheep that are in the meat productionbecomes a by-product that is usually reckoned as waste.The study presented below involves a product development of a board material containingclay and sheep’s wool. Nine different compositions were made in different series.Focus on the three different series was places on variety of sheep’s wool, amountof sheep’s wool and the viscosity of the clay. The manufacturing of the product wasmade by hand with own thought out and manufactured aids.The lack of aggregated material properties complicates the use of clay and sheep’swool. A performance based declaration and the CE marking of a product are requiredfor a building material to become an accepted product in the construction market.Building engineering research was carried out in the laboratory environment, and basedon standardized methods calculations were made on the Clay-wool board such as flexuralstrength, vapour permeability, thermal conductivity, fire resistance and practicaluse.The result shows that the Clay-wool board is comparable to other board materials. Thetechnical characteristics of the Clay-wool board regarding flexural strength reportedvalues between 118 N and 550 N, depending on the composition of clay and wool. Allthe boards showed that the point of breaking was viscous, since the wool held the clayslabs together. When calculation vapour permeability, the result showed values between2,289 x 106 m2/s and 3,571 x 106 m2/s.The thermal conductivity was measured on one single board, the one containing thelargest amount of wool, where the value was established to 0,218 W/m*K. It was noticedthat the thermal conductivity increased when wool was clay–dipped. / Denna studie fokuserar på det traditionella byggmaterialet lera tillsammans medfårull som ska agera som armering. Kombinationen av de två materialen skapadegrunden för ett alternativt skivmaterial. Jordbaserade byggmaterial användes förri tiden i stor utsträckning. De äldsta lerhusen som hittats är byggda så tidigt sompå 8000 – talet f.Kr. I medeltidens Centraleuropa användes jord och lera till utfackningari ramverkskonstruktioner av trä. I takt med att nya byggmaterial utvecklatsfick lerbaserade byggmetoder en undanskymd ställning i västvärlden.Nya byggmaterial har gjort att det traditionella byggmaterialets egenskaper generellthar glömts bort. Fårull har tidigare inte klassats som ett byggmaterial, liktlera, utan används till största del till textilier. Får avlas generellt för två syften;köttproduktion och ull produktion. Ullen som kommer från får i köttproduktionenblir en biprodukt som vanligen räknas som avfall.Studien som presenteras omfattar en produktutveckling av ett skivmaterial innehållandelera och fårull. Nio olika kompositioner gjordes i tre olika serier. Fokuspå de tre olika serier lades på fårullssort, ullmängd och lerviskositet. Tillverkningav lerullsskivorna gjordes för hand med egna uttänkta och tillverkade hjälpmedel.Bristen på sammanställda materialegenskaper komplicerar användningen av leraoch fårull. Det krävs en prestandadeklaration och CE-märkning av en vara för attett byggmaterial ska bli en accepterad produkt på byggmarknaden. Byggnadstekniskforskning gjordes i laboratorisk miljö och utifrån standardiserade metoderhar beräkningar gjorts på lerullskivorna gällande, böjhållfasthet, ånggenomsläpplighet,värmekonduktivitet, brandtålighet samt praktisk användning.Resultatet visar på att lerullsskivan är jämförbar med andra skivmaterial. Lerullsskivornastekniska egenskaper gällande böjhållfasthet redovisade värden mellan118 N och 550 N, beroende på komposition av lerullsskiva. Alla skivor visade påsega brott, eftersom ullen höll ihop lerullsskivorna. Vid beräkning av ångpermeabilitetvisade resultaten på värden mellan 2,289 x 106 m2/s och 3,571 x 106m2/s. Värmeledningsförmågan beräknades endast på lerullsskivan med störstmängd ull, där värdet blev 0,218 W/m*K. Det uppdagades att värmeledningsförmåganökade när ullen dränktes i lervälling.

O objetivo deste estudo foi avaliar pinos pré-fabricados de fibra de vidro (White Post DC/FGM) submetidos à customização por desgaste da porção apical. Experimento 1: 5 pinos n. 4 foram divididos em 5 grupos (G) de acordo com o instrumento de desgaste: GA - sem desgaste, GB- mini torno industrial (Dentsply), GC - ponta diamantada n. 3195F (KG Sorensen), GD - disco de lixa de granulação média (Sof-Lex/3M/ESPE), GE- alicate (Tramontina). Observou-se a micromorfologia dos pinos em microscópio eletrônico de varredura (ZEISS/DSM 960). Experimento 2: 60 pinos de diferentes diâmetros foram divididos em 6 grupos: G0 - pinos n. 0,5, G1 - pinos n. 1, G2 - pinos n. 2, G3 - pinos n. 3, G4 - pinos n.4, G5 - pinos n. 4 com terço apical desgastado com discos de lixa até o equivalente ao terço apical dos pinos n. 2. Os pinos foram submetidos ao teste de flexão de 3 pontos na máquina de ensaios universal (Instron 5500 R), conforme ISO 10477. Experimento 3: 20 caninos humanos permanentes sofreram tratamento endodôntico e remoção das coroas clínicas padronizando 15 mm de remanescente radicular. Os dentes foram incluídos em resina acrílica com simulação do ligamento periodontal, receberam férula de 2 mm e foram divididos em 2 grupos: GI - pinos n. 4 cimentados em condutos preparados com broca equivalente ao pino (FGM), GII - pinos n. 4 customizados no terço apical cimentados em condutos preparados com brocas (FGM) equivalentes aos pinos n. 2 em 10 mm e n. 4 em 5 mm. Os pinos foram cimentados com cimento resinoso (Rely X U100/3M/ESPE), os corpos de prova receberam coroas diretas de resina composta (Enforce Core/Dentsply) padronizadas com coras de policarbonato (TDV) e foram submetidos ao teste de resistência à fratura na Instron a 45da ferramenta cilíndrica, com força de 500 N aplicada a 2 mm da incisal na face palatina/lingual, com velocidade de 0,5 mm/min até falha. O padrão de fratura foi classificado em favorável ou desfavorável. Os resultados foram tratados estatisticamente por teste de análise de variância (ANOVA, p<0,05). Os resultados dos testes de flexão e fratura foram respectivamente: G0 - 58,406,40; G1 - 83,959,43; G2- 103,4219,17; G3 - 160,7817,30; G4 - 170,4711,28; G5 - 106,3521,96; GI - 303,0262,21 e GII - 402,81131,97. O padrão de fratura foi tratado por Mann-Whitney que observou semelhança estatística entre os grupos. Concluiu-se que o desgaste de pinos de fibra de vidro com pontas diamantadas ou discos de lixa produz alterações micromorfológicas aceitáveis. O corte com alicate deve ser evitado. A customização por desgaste da porção apical de pinos de fibra de vidro diminui a resistência à flexão a valores aceitáveis. Dentes restaurados com pinos de fibra de vidro customizados por desgaste possuem resistência à fratura superior a dentes restaurados com pinos intactos. A customização por desgaste facilita a adaptação do pino ao conduto radicular e preserva a estrutura dental. / The purpose of this study was to evaluate fibre posts (White Post DC/FGM) submitted to customization of the apical portion. Experiment 1: 5 #4 posts were divided into five groups (G) and submitted to different custom adaptation treatments: GA no surface treatment, GB- industrial shaping tool (Dentsply), GC- #3195 fine diamond bur (KG Sorensen), GD- medium-grain paper discs (Sof-Lex/3M/ESPE), GE pliers (Tramontina). The micromorphology of the posts was observed in a scanning electron microscope (ZEISS/DSM 960). Experiment 2: 60 posts of different diameters were divided into six groups: G0 #0.5 posts, G1 #1 posts, G2 #2 posts, G3 - #3 posts; G4 - #4 posts and G5 #4 posts submitted to custom adaptation of the apical portion with paper discs until the diameter was equivalent to #2 posts. The posts were submitted to a 3 point bending test in a universal testing machine (Instron/5500 R), according to ISO 10477. Experiment 3: 20 freshly extracted permanent healthy human canines with similar size were endodontically treated and the crowns were removed, leaving a remaining root length of 15 mm. The teeth were embedded in acrylic resin with simulation of the periodontal ligament, received a 2 mm ferule and were divided into two groups: G1- 10 #4 posts were cemented into post spaces prepared with #4 drill (FGM) at 10 mm, G2 - 10 #4 customized posts were cemented into root spaces prepared with #2 drill (FGM) at 10 mm and #4 drill (FGM) at 5 mm. The posts were cemented with resin cement (Rely X U100/3M/ESPE), and the teeth received direct crowns of composite resin (Enforce Core/Dentsply), standardized with polycarbonate crowns (TDV). The fracture strength was measured on an Instron, at 45 degrees to the long axis of the tooth, until fracture. The 500 N cylindrical load was applied to the buccal/lingual axis 2 mm below the incisal line, at crosshead speed of 0.5 mm/min. The fracture pattern was observed and classified as favorable or unfavorable. The results were submitted to ANOVA (p<0.05). Flexural strength and resistance to fracture data were, respectively: G0 58.40+6.40; G1 83.95+9.43; G2 103.42+19.17; G3 160.78+17.30; G4- 170.47+11.28; G5 106.35+21.96;GI 303.02+62.21 and GII 402.81+131.97. Fracture patterns were statistically similar according to Mann-Whitney test. It was concluded that customization of fibre posts with diamond burs or paper discs produces acceptable micromorphological changes. The cut of the post with pliers should be avoided. Grounding of the apical portion of fibre posts reduces the flexural strength to acceptable values. Teeth restored with grounded fiber posts have grater fracture strength than teeth restored with intact posts. Grounding of the post facilitates adaptation to root walls and preserves tooth structure.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-23Bitstream added on 2014-06-13T20:25:49Z : No. of bitstreams: 1 michida_sma_dr_sjc.pdf: 2344259 bytes, checksum: b8cbeae3d13fd34243d34d756ed1ce82 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Neste estudo avaliou-se a influência do tratamento de superfície para cimentação na resistência à flexão de 4 pontos de zircônia tetragonal policristalina estabilizada por óxido de ítrio (Y-TZP). Por meio de blocos pré-sinterizados de Y-TZP (InCeram 2000 YZ Cubes, Vita Zahnfabrik) foram confeccionadas 120 barras (20mm x 4mm x 1,2mm) de acordo com a norma ISO 6872:2008 e aleatoriamente divididas em 4 grupos: Grupo 1: silicatização (Cojet 30 μm) (n=29); Grupo 2: jateamento com óxido de alumínio (44 μm) (n=29); Grupo 3: ponta diamantada de granulação extra-fina (30 μm) (n=27); Grupo 4: (controle) sem tratamento de superfície (n=29). Em seguida, todas as amostras foram submetidas ao ensaio de flexão de 4 pontos (imersos em água destilada à 370C) em máquina de ensaio universal com velocidade de 0,5 mm/min até o rompimento das mesmas. A análise de difração de raios-X foi utilizada para determinar a transformação de fase. A microestrutura da Y-TZP e o padrão de tratamento de superfície foram analisados por meio de perfilometria óptica e microscopia eletrônica de varredura. Os dados de resistência à flexão foram estatisticamente analisados por meio de ANOVA 1-fator, teste de Tukey HSD (α=0,05) e Weibull (m=módulo; σ0=resistência característica). As médias±desvio-padrão (MPa) foram os seguintes: G1:1207,1±229,7a; G2: 1369,7±272,3a; G3: 874,4±365,4b e G4: 1196,2±284,2a. Os valores de (m) e (σ0) foram: G1: 6,0 e 1300,28; G2: 5,9 e 1477,88; G3: 2,6 e 985,901 e G4: 4,5 e 1308,12. Concluiu-se que a utilização de pontas diamantadas de granulação extra-fina deve ser evitada nos procedimentos prévios à cimentação resinosa de Y-TZP / This study evaluated the influence of surface treatment on 4-point bending test of yttrium stabilized policristaline tetragonal zirconia (Y-TZP). From Y-TZP blocks (InCeram 2000 YZ Cubes, Vita Zahnfabrik) were obtained 120 bars (20mm×4mm×1.2mm) according to norm ISO 6872:2008 and randomly divided in 4 groups: Group 1: silicatization (Cojet 30 μm) (n=29); Group 2: sandblasting with aluminium oxide (44 μm) (n=29); Group 3: fine coarse diamond bur (30 μm) (n=27); Group 4: (control) without surface treatment (n=29). As follow, all samples were submitted to the 4-point bending test (immersed in distilled water at 370C) in an universal testing machine with cross-head speed of 0.5 mm/min until the rupture of the samples. X-ray diffraction analysis was utilized to quantify the monoclinic phase. The microstructure of Y-TZP and pattern of surface treatment were analyzed by optic profilometer and scanning electron microscopy. The data of flexural strength (σ4p) were statistically analyzed by 1-factor ANOVA, Tukey HSD (α= 0.05) and Weibull (m= modulus, σ0 = characteristic strength). The mean±standard deviation (MPa) were the following: G1:1207.1±229.7a; G2: 1369.7±272.3a; G3: 874.4±365.4b and G4: 1196.2±284.2a. The values of (m) and (σ0) were: G1: 6.0 and 1300.28; G2: 5.9 and 1477.88; G3: 2.6 and 985.901 and G4: 4.5 and 1308.12. It was concluded that silicatization and sandblasting increased the flexural strength of Y-TZP, diminished the roughness of surface and present higher reliability for cementation of Y-TZP restorations

Placas oclusais são dispositivos intraorais utilizados no manejo de pacientes que apresentam desordens do sono, migrânia do tipo tensional e outros. No entanto são os cirurgiões dentistas que predominantemente utilizam as placas oclusais como tratamento do equilíbrio das arcadas dentárias nas disfunções temporomandibulares, prevenção de desgaste dental em pacientes com hábitos parafuncionais e na prevenção de traumas em atletas. Vários métodos têm sido empregados para reforçar resinas acrílicas, como reforço metálico e atualmente a incorporação de diferentes tipos de fibras tais como: carbono, polietileno e vidro. Contudo a adição de fibras de vidro com partículas menores em algumas propriedades mecânicas ainda permanecem desconhecidas. Objetivo: O objetivo desse estudo foi avaliar algumas propriedades mecânicas como a rugosidade de superfície, microdureza, módulo de elasticidade e resistência flexural em resinas acrílicas após a incorporação de fibras de vidro particuladas pré silanizadas. Material e método: Para avaliação das propriedades foram confeccionados vinte e quatro corpos de prova (65 x 10 x 3 mm) de cada marca comercial de resina acrílica, utilizadas para confecção de placas oclusais, Vipi Flash (autopolimerizável), Vipi Wave (termopolimerizável por calor de microondas), Vipi Crill, Lucitone e QC-20 (termopolimerizáveis por calor de banho de água), sendo doze corpos-de-prova controles, e doze experimentais, com adição de 10% em peso de fibras de vidro particuladas (Reforplás S/A, São Paulo, SP, Brasil). Após a realização do acabamento superficial dos corpos de prova com lixas de carborundum e feltros era realizada a avaliação da rugosidade superficial em rugosímetro (Mitutoyo®) com três leituras ao longo dos corpos-de-prova, a microdureza Vickers era analisada em um microdurômetro (Micro Hardness Tester, Shimadzu, Japan) com cinco mensurações em cada corpo-de-prova, e para avaliar os ensaios de resistência flexural e módulo de elasticidade os corpos-de-prova foram avaliados por meio uma máquina de ensaios universal (Emic DL 2000®, Emic, São José dos Pinhais, PR, Brasil), com velocidade de 5mm/min. Os dados foram analisados estatisticamente, usando testes paramétricos e não paramétricos, de acordo com a distribuição da amostra. Resultados: As médias e desvios padrões do teste de rugosidade superficial em Ra foram Vipi Flash sem fibra (0,10 ± 0,03); Vipi Flash com fibra (0,12 ± 0,01); Vipi Wave sem fibra (0,16 ± 0,02); Vipi Wave com fibra (0,13 ± 0,02); Vipi Cril sem fibra (0,12 ± 0,03); Vipi Crill com fibra (0,15 ± 0,03); Lucitone sem fibra (0,10 ± 0,02); Lucitone com fibra (0,09 ± 0,04); QC-20 sem fibra (0,11 ± 0,02) e QC-20 com fibra (0,18 ± 0,03). As médias e desvios-padrão ao teste de microdureza Knoop com relação às marcas comerciais foram: Vipi Flash sem fibra (15,35 ± 0,3); Vipi Flash com fibra (15,51 ± 0,4); Vipi Wave sem fibra (16,60 ± 0,8); Vipi Wave com fibra (17,25 ± 0,9); Vipi Cril sem fibra (17,78 ± 2,27); Vipi Crill com fibra (18,02 ± 1,0); Lucitone sem fibra (15,72 ± 0,3); Lucitone com fibra (16,69 ± 0,6); QC-20 sem fibra (15,91 ± 0,4) e QC-20 com fibra (15,63 ± 0,2). As médias e desvios-padrão ao teste de módulo de elasticidade foram: Vipi Flash sem fibra (2952,76 ± 292,12); Vipi Flash com fibra (3373,49 ± 403,76); Vipi Wave sem fibra (2511,69 ± 304,09); Vipi Wave com fibra (3225,01 ± 248,66); Vipi Cril sem fibra (2745,61± 288,86); Vipi Crill com fibra (3671,67 ± 329,91); Lucitone sem fibra (1904,53 ± 149,05); Lucitone com fibra (3056,87 ± 126,11); QC-20 sem fibra (1913,86 ± 147,80) e QC-20 com fibra (2858,32 ± 185,26). As médias e desvios-padrão ao teste de resistência flexural foram Vipi Flash sem fibra (81,62 ± 4,82); Vipi Flash com fibra (83,98 ± 4,98); Vipi Wave sem fibra (83,52 ± 8,79); Vipi Wave com fibra (88,98± 8,47); Vipi Cril sem fibra (64,17± 5,46); Vipi Crill com fibra (93,37 ± 9,97); Lucitone sem fibra (74,71± 9,43); Lucitone com fibra (87,29 ± 4,73); QC-20 sem fibra (75,80 ± 8,82) e QC-20 com fibra (81,67± 12,97). Conclusão: Conclui-se que a incorporação de fibras provocou alterações em praticamente todas as propriedades analisadas, sendo, portanto facilmente utilizável como um reforço adicional às resinas acrílicas. Com relação à dureza superficial as resinas acrílicas termopolimerizável por banho de água e termopolimerizável por calor de microondas apresentaram maiores valores quando comparados com a resina acrílica autopolimerizável. Além disso, a adição de fibras de vidro particuladas aumentou os valores de rugosidade de algumas resinas acrílicas Vipi Crill, Vipi Flash e Vipi Wave e se manteve constante nas resinas Lucitone e QC-20. A adição de fibra de vidro não aumentou significantemente a microdureza Knoop nos grupos em estudo. Com relação à resistência flexural as fibras de vidro particuladas aumentaram significantemente todos os valores, assim como o módulo de elasticidade das resinas acrílicas reforçadas pela adição de fibras de vidro. / Intraoral Occlusal splints are devices used in the management of patients with sleep disorders, migraine type tension and others. But dentists who are predominantly using the plates as a treatment of occlusal balance of the dental arches in temporomandibular disorders, prevention of tooth wear in patients with habits and prevention of injuries in athletes. Several methods have been used to strengthen acrylic resins, such as metal reinforcement and are currently incorporating different types of fibers such as carbon, polyethylene and glass. However the addition of glass fibers with smaller particles on mechanical properties are still unknown. Objective: The objective of this study was to evaluate some mechanical properties such as surface roughness, hardness, elastic modulus and flexural strength in acrylic resins after the incorporation of glass fiber particulate pre silanized. Methods: To evaluate the properties were made twenty-four specimens (65 x 10 x 3 mm) of each brand of acrylic resin, used for fabrication of occlusal splints, Vipi Flash (self-curing), Vipi Wave (by thermo microwave heat), Vipi CRILL, Lucitone and QC-20 (thermo heat water bath), with twelve specimes controls, and twelve experimental, with the addition of 10 wt% glass fiber particulate (Reforplás S / A, São Paulo, Brazil). After completion of the roughness of the specimens with grit carborundum and felt it was evaluated the surface roughness on roughness tester (Mitutoyo ®) with three readings over the specimes, the microhardness was examined with a hardness ( Micro Hardness Tester, Shimadzu, Japan) with five measurements in each specime, and evaluate the tests for flexural strength and modulus of elasticity of the specimes was evaluated using a universal testing machine (Emic DL 2000 ®, Emic, São José dos Pinhais, PR, Brazil), with speed 5mm/min. The data were statistically analyzed using parametric and nonparametric tests, according to the sample distribution. Results: The mean and standard deviation of the test surface roughness were Vipi Flash without fiber (0.10 ± 0.03); Flash Vipi with fiber (0.12 ± 0.01); Vipi Wave without fiber (0, 16 ± 0.02); Vipi Wave with fiber (0.13 ± 0.02); Vipi Cril without fiber (0.12 ± 0.03); Vipi CRILL with fiber (0.15 ± 0.03); Lucitone without fiber (0.10 ± 0.02); Lucitone with fiber (0.09 ± 0.04), QC-20 fiber without (0.11 ± 0.02) and QC-20 with fiber (0.18 ± 0.03). Means and standard deviations for Knoop microhardness test with respect to trademarks were Vipi Flash without fiber (15.35 ± 0.3); Flash Vipi with fiber (15.51 ± 0.4); Vipi Wave without fiber (16.60 ± 0.8); Vipi Wave with fiber (17.25 ± 0.9); Vipi Cril without fiber (17.78 ± 2.27); Vipi CRILL with fiber (18.02 ± 1.0 ); Lucitone without fiber (15.72 ± 0.3); Lucitone with fiber (16.69 ± 0.6), QC-20 without fiber (15.91 ± 0.4) and QC-20 with fiber (15 , 63 ± 0.2). Means and standard deviations to test elastic modulus were Vipi Flash without fiber (2952.76 ± 292.12); Flash Vipi with fiber (3373.49 ± 403.76); Vipi Wave without fiber (2511.69 ± 304.09); Vipi Wave with fiber (3225.01 ± 248.66); Vipi Cril without fiber (2745.61 ± 288.86); Vipi CRILL with fiber (3671.67 ± 329.91); Lucitone without fiber (1904.53 ± 149.05); Lucitone with fiber (3056.87 ± 126.11), QC-20 without fiber (1913.86 ± 147.80) and QC-20 with fiber (2858.32 ± 185 26). Means and standard deviations for flexural strength were Vipi Flash without fiber (81.62 ± 4.82); Flash Vipi with fiber (83.98 ± 4.98); Vipi Wave without fiber (83.52 ± 8 , 79); Vipi Wave with fiber (88.98 ± 8.47); Vipi Cril without fiber (64.17 ± 5.46); Vipi CRILL with fiber (93.37 ± 9.97); Lucitone without fiber ( 74.71 ± 9.43); Lucitone with fiber (87.29 ± 4.73), QC-20 without fiber (75.80 ± 8.82) and QC-20 with fiber (81.67 ± 12.97). Conclusion: the conclusion is that the incorporation of fibers resulted in changes in almost all properties examined, and thus easily used as an additional reinforcement for acrylic resins. With respect to the surface roughness of acrylic resins by thermo water bath and microwave thermo heat showed higher values when compared with acrylic resin. Moreover, the addition of glass fiber particulate increased the roughness values of some acrylic resins Vipi CRILL, Vipi Flash and Vipi Wave and remained constant in the resins Lucitone and QC-20. The addition of glass fiber does not increase significantly the microhardness in the groups. With respect to flexural strength glass fiber particulate significantly increased all values, as well as the modulus of acrylic resin reinforced by the addition of glass fibers.

O objetivo deste estudo foi avaliar pinos pré-fabricados de fibra de vidro (White Post DC/FGM) submetidos à customização por desgaste da porção apical. Experimento 1: 5 pinos n. 4 foram divididos em 5 grupos (G) de acordo com o instrumento de desgaste: GA - sem desgaste, GB- mini torno industrial (Dentsply), GC - ponta diamantada n. 3195F (KG Sorensen), GD - disco de lixa de granulação média (Sof-Lex/3M/ESPE), GE- alicate (Tramontina). Observou-se a micromorfologia dos pinos em microscópio eletrônico de varredura (ZEISS/DSM 960). Experimento 2: 60 pinos de diferentes diâmetros foram divididos em 6 grupos: G0 - pinos n. 0,5, G1 - pinos n. 1, G2 - pinos n. 2, G3 - pinos n. 3, G4 - pinos n.4, G5 - pinos n. 4 com terço apical desgastado com discos de lixa até o equivalente ao terço apical dos pinos n. 2. Os pinos foram submetidos ao teste de flexão de 3 pontos na máquina de ensaios universal (Instron 5500 R), conforme ISO 10477. Experimento 3: 20 caninos humanos permanentes sofreram tratamento endodôntico e remoção das coroas clínicas padronizando 15 mm de remanescente radicular. Os dentes foram incluídos em resina acrílica com simulação do ligamento periodontal, receberam férula de 2 mm e foram divididos em 2 grupos: GI - pinos n. 4 cimentados em condutos preparados com broca equivalente ao pino (FGM), GII - pinos n. 4 customizados no terço apical cimentados em condutos preparados com brocas (FGM) equivalentes aos pinos n. 2 em 10 mm e n. 4 em 5 mm. Os pinos foram cimentados com cimento resinoso (Rely X U100/3M/ESPE), os corpos de prova receberam coroas diretas de resina composta (Enforce Core/Dentsply) padronizadas com coras de policarbonato (TDV) e foram submetidos ao teste de resistência à fratura na Instron a 45da ferramenta cilíndrica, com força de 500 N aplicada a 2 mm da incisal na face palatina/lingual, com velocidade de 0,5 mm/min até falha. O padrão de fratura foi classificado em favorável ou desfavorável. Os resultados foram tratados estatisticamente por teste de análise de variância (ANOVA, p<0,05). Os resultados dos testes de flexão e fratura foram respectivamente: G0 - 58,406,40; G1 - 83,959,43; G2- 103,4219,17; G3 - 160,7817,30; G4 - 170,4711,28; G5 - 106,3521,96; GI - 303,0262,21 e GII - 402,81131,97. O padrão de fratura foi tratado por Mann-Whitney que observou semelhança estatística entre os grupos. Concluiu-se que o desgaste de pinos de fibra de vidro com pontas diamantadas ou discos de lixa produz alterações micromorfológicas aceitáveis. O corte com alicate deve ser evitado. A customização por desgaste da porção apical de pinos de fibra de vidro diminui a resistência à flexão a valores aceitáveis. Dentes restaurados com pinos de fibra de vidro customizados por desgaste possuem resistência à fratura superior a dentes restaurados com pinos intactos. A customização por desgaste facilita a adaptação do pino ao conduto radicular e preserva a estrutura dental. / The purpose of this study was to evaluate fibre posts (White Post DC/FGM) submitted to customization of the apical portion. Experiment 1: 5 #4 posts were divided into five groups (G) and submitted to different custom adaptation treatments: GA no surface treatment, GB- industrial shaping tool (Dentsply), GC- #3195 fine diamond bur (KG Sorensen), GD- medium-grain paper discs (Sof-Lex/3M/ESPE), GE pliers (Tramontina). The micromorphology of the posts was observed in a scanning electron microscope (ZEISS/DSM 960). Experiment 2: 60 posts of different diameters were divided into six groups: G0 #0.5 posts, G1 #1 posts, G2 #2 posts, G3 - #3 posts; G4 - #4 posts and G5 #4 posts submitted to custom adaptation of the apical portion with paper discs until the diameter was equivalent to #2 posts. The posts were submitted to a 3 point bending test in a universal testing machine (Instron/5500 R), according to ISO 10477. Experiment 3: 20 freshly extracted permanent healthy human canines with similar size were endodontically treated and the crowns were removed, leaving a remaining root length of 15 mm. The teeth were embedded in acrylic resin with simulation of the periodontal ligament, received a 2 mm ferule and were divided into two groups: G1- 10 #4 posts were cemented into post spaces prepared with #4 drill (FGM) at 10 mm, G2 - 10 #4 customized posts were cemented into root spaces prepared with #2 drill (FGM) at 10 mm and #4 drill (FGM) at 5 mm. The posts were cemented with resin cement (Rely X U100/3M/ESPE), and the teeth received direct crowns of composite resin (Enforce Core/Dentsply), standardized with polycarbonate crowns (TDV). The fracture strength was measured on an Instron, at 45 degrees to the long axis of the tooth, until fracture. The 500 N cylindrical load was applied to the buccal/lingual axis 2 mm below the incisal line, at crosshead speed of 0.5 mm/min. The fracture pattern was observed and classified as favorable or unfavorable. The results were submitted to ANOVA (p<0.05). Flexural strength and resistance to fracture data were, respectively: G0 58.40+6.40; G1 83.95+9.43; G2 103.42+19.17; G3 160.78+17.30; G4- 170.47+11.28; G5 106.35+21.96;GI 303.02+62.21 and GII 402.81+131.97. Fracture patterns were statistically similar according to Mann-Whitney test. It was concluded that customization of fibre posts with diamond burs or paper discs produces acceptable micromorphological changes. The cut of the post with pliers should be avoided. Grounding of the apical portion of fibre posts reduces the flexural strength to acceptable values. Teeth restored with grounded fiber posts have grater fracture strength than teeth restored with intact posts. Grounding of the post facilitates adaptation to root walls and preserves tooth structure.

O objetivo desse estudo foi verificar a influência da fotoativação com laser de argônio na tensão de contração (TC), microdureza (M), porcentagem de dureza máxima (PDM), resistência flexural (RF) e módulo de elasticidade (ME) de uma resina composta híbrida. A fotoativação foi realizada com laser de argônio 200mW por 10 segundos (L1), 200mW por 20 segundos (L2), 250mW por 10 segundos (L3) e 250mW por 20 segundos (L4). Como controle foi utilizada a luz hálógena por 20 segundos (H). A TC foi monitorada por 5 minutos em corpos-de-prova com 5mm de diâmetro e 1mm de altura. A M e a PDM foram obtidas em corpos-de-prova com 2mm de espessura após 7 dias a 37°C. Para obtenção da RF e do ME foram confeccionados corpos-de-prova nas dimensões 10 X 2 X 1mm (comprimento, largura e espessura), testados após 24h a 37°C. Os dados obtidos foram analisados por ANOVA/Teste de Tukey (p<0,05). Os valores de TC (MPa) foram estatisticamente mais baixos para o grupo L3 (1,3)c, seguido pelos grupos L1(2,7)b, L4 (3,4)a,b, L2 (3,7)a e H (4,5)a. Para os valores de M não houve diferença estatisticamente significante quando o mesmo tempo de fotoativação foi utilizado, sendo L1= 70,1a, L2= 78,1b, L3= 69,9a, L4= 78,1b e H= 79,9b. Todos os grupos apresentaram uma PDM de no mínimo 80%. Apenas o grupo L1 apresentou diferença estatisticamente significante na RF (MPa) e no ME (GPa), 86,2 e 5,4 respectivamente, sendo inferior. Dentro dos grupos estudados, o L3 apresentou propriedades mecânicas adequadas e mínima tensão de contração, além de possibilitar redução do tempo clínico para fotoativação de restaurações com a resina testada em 50%. / The objective of this study was to verify the influence of photoactivation with the argon ion laser on shrinkage stress (SS), followed by evaluation of Vickers microhardness (VM), percentage of maximum hardness (PMH), flexural strength (FS) and flexural modulus (FM) of a composite resin. Methods: The light curing units used were argon ion laser and halogen light. The groups were: L1- laser at 200mW for 10 seconds; L2- laser at 200mW for 20 seconds; L3- laser at 250mW for 10 seconds; L4- laser at 250mW for 20 seconds; and H- halogen light at 275mW for 20 seconds. The SS was monitored for 5 minutes in samples 5-mm in diameter by 1-mm in height. The VM and PHM were obtained in samples with a thickness of 2-mm after 7 days at 37°C. To FS and FM the samples were prepared using a stainless steel mold 10 x 2 x 1mm (length, width and height) and measured after 24h storage at 37°C. Data were analyzed by ANOVA/Tukey`s test (p<0.05). Results: The values of SS (MPa) were statistically lower for the group L3(1.3)c, followed by groups L1(2.7)b, L4 (3.4)a,b, L2(3.7)a and H(4.5)a. To the values of VM there was no difference when the same time of photo activation was used, being L1= 70.1a, L2=78.1b, L3= 69.9a, L4= 78.1b and H= 79.9b. All groups showed a PMH of at least 80%. Only the group L1 showed difference in FS (MPa) and FM (GPa), 86.2 and 5.4 respectively, being lower. Conclusion: within the studied groups, the L3 group presented adequate mechanical properties and minimum SS, reducing the clinical working time for photo activation of restorations with the tested resin in 50%.

Made available in DSpace on 2014-10-09T12:43:02Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:07:48Z (GMT). No. of bitstreams: 1 06176.pdf: 9306804 bytes, checksum: c8d5e9d8cf888b1ed0725717af3c2309 (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

O objetivo deste estudo foi avaliar o efeito da temperatura de troca iônica (TI) nas propriedades mecânicas da porcelana Ultrapaline ST e o efeito da TI nos parâmetros de crescimento subcrítico de trincas (SCG) (coeficiente de SCG - n, parâmetro escalar - ?f0), de Weibull (resistência característica - ?0, módulo de Weibull - m) e no comportamento de curva R desta porcelana. 250 discos (12 mm diâmetro x 1 mm espessura) foram fabricados de acordo com as instruções do fabricante, usinados em retificadora plana e polidos até 1 ?m. Para determinar o efeito da temperatura de TI na resistência à flexão biaxial (?), dureza (H) e tenacidade à fratura (KIc), 40 discos foram divididos em 4 grupos (n=10): GI (controle) - sem TI; e GII, GIII e GIV submetidos a TI com KNO3 por 15 min a 450°C; 470°C e 490°C, respectivamente. A ? foi determinada por \"pistão sobre três esferas\" em saliva artificial a 37°C a 10 MPa/s. Para dureza e tenacidade à fratura, foram feitas 3 indentações Vickers em cada espécime (2kg, 30s) e as diagonais e trincas radiais foram medidas e os valores de H e KIc calculados. As médias e desvios-padrão para ? (MPa), H (GPa) e KIc (MPa.m1/2) foram: GI: 57,95 ± 8.97, 7,24 ± 0,79 e 1,14 ± 0,14; GII: 125,04 ± 23,58, 5,80 ± 0,14, 2,62 ± 0,14; GIII: 133,00 ± 11,00, 5,88 ± 0,45, 2,54 ± 0,22; GIV: 137,67 ± 12,05, 5,88 ± 0,17, 2,57 ± 0,10, respectivamente. Para determinação dos parâmetros de SCG e de Weibull, 140 espécimes foram divididos em 2 grupos: GC (controle) e GT (submetidos à TI por 15 min a 470°C). Para determinação de n e de ?f0, 50 espécimes de cada grupo foram testados em saliva artificial a 37°C em flexão biaxial em uma das seguintes taxas de tensão: 10-2, 10-1, 100, 101 e 102 MPa/s. Para determinação dos parâmetros de Weibull, mais 20 espécimes de cada grupo foram ensaiados na taxa de 100 MPa/s. Os valores de n, ?f0, m e ?0 foram, respectivamente (valores entre parênteses representam intervalos de confiança de 95%): 24,1 ± 2,5; 58,1 ± 0,01; 13,8 (10,0 a 18,8) e 60,4 (62,2 a 58,5) para GC e 36,7 ± 7,3; 127,9 ± 0,01; 7,4 (5,3 a 10,1) e 136,8 (129,1 a 144,7) para GT. Para determinação do efeito da TI no curva R, 7 espécimes de cada grupo receberam uma indentação Vickers em uma das seguintes cargas de indentação (kg): 0,18; 0,32; 0,56; 1,0; 3,2. Após armazenados ao ar por 24 h os espécimes foram ensaiados a 10 MPa/s em saliva artificial a 37°C. Os parâmetros ?, ?, q foram, respectivamente: 62,57; 0,12 e 0,2857 para GC e 161,50; 0,34 e -0,0074 para GT. Os valores de k variaram de 0,371 a 0,515 para GC e de 1,240 a 0,804 para GT. Não houve diferença nas propriedades mecânicas entre as três temperaturas de TI testadas. A TI promoveu aumento significativo do valor de n, ?f0 e ?0, entretanto resultou em diminuição do valor de m e também suprimiu o comportamento de curva R, presente no material antes da realização da TI. / The objectives of this study were to determine the influence of different ion exchange (IE) temperatures on mechanical properties of a dental porcelain Ultrapaline ST and the effect of IE on slow crack growth (SCG) (coefficient of SCG - n, scale parameter - ?f0) and Weibull parameters (characteristic strength - ?0; Weibull modulus - m) and R-curve behavior of this porcelain. 250 specimens (12 mm diameter x 1 mm height) were fabricated according to the manufacturer\'s instructions, grounded with a surface-grinding device and polished up to 1?m. To determine the effect of IE temperature on biaxial flexural strength (?), hardness (H) and fracture toughness (KIc), 40 specimens were divided in four groups (n=10) as follow: GI - control (no ion exchange); GII, GIII and GIV submitted to IE with KNO3 for 15 min at 450°C; 470°C e 490°C, respectively. The ? was determined using a piston-on-three-balls device, in artificial saliva at 37°C and constant loading rate of 10 MPa/s. For hardness and fracture toughness, 3 Vickers indentations (2kg, 30s) were made on each specimen. The diagonals and radial cracks were measured in order to calculate H and KIc. Mean and standard deviations values of ? (MPa), H (GPa) and KIc (MPa.m1/2) were: I: 57.95 ± 8.97; 7.24 ± 0.79; 1.14 ± 0.14; II: 125.04 ± 23.58; 5.80 ± 0.14; 2.62 ± 0.14; III: 133.00 ± 11.00; 5.88 ± 0.45; 2.54 ± 0.22; IV: 137.67 ± 12.05; 5.88 ± 0.17; 2.57 ± 0.10, respectively. To determine the effect of IE on SCG and Weibull parameters, 140 specimens were divided in 2 groups: GC (control) and GIE (submitted to IE at 470°C for 15 min). To determine the SCG parameters, 10 specimens of each group were tested in biaxial flexural strength in each one of five constant stress rates: 10-2, 10-1, 100, 101 e 102 MPa/s. To determine the Weibull parameters, 20 specimens of each group were tested in the stress rate of 100 MPa/s. The n, ?f0, m and ?0 (values in parenthesis represent the confidence interval) were: 24.1 ± 2.5; 58.1 ± 0.01; 13.8 (10.0 to 18.8) and 60.4 (62.2 to 58.5) for GC and: 36.7 ± 7.3; 127.9 ± 0.01; 7.4 (5.3 to 10.1) and 136.8 (129.1 to 144.7) for GIE, respectively. To determine the effect of IE on R-curve behavior, 7 specimens of each group received a Vickers indentation in one of the following indentation loads (kg): 0.18; 0.32; 0.56; 1.0; 3.2. After stored on air for 24 h, the specimens were tested biaxial flexure strength in artificial saliva at 37°C in a stress rate of 10 MPa/s. The ?, ?, q parameters were, respectively: 62.57; 0.12 and 0.2857 for GC and 161.50; 0.34 and -0.0074 for GIE. The values of k varied from 0.371 to 0.515 for GC and from 0.34 to 0.0074 for GIE. There are no differences on mechanical properties among the three IE temperatures tested. The IE promoted significantly increase of n, ?f0 and ?0 however, decreased the m value and suppressed the R-curve behavior originally present on material before the IE.

Este trabalho avaliou a influência da densidade de energia da pré-cura, e de diferentes tratamentos pós-cura na otimização das propriedades físicas (Resistência à Flexão e Dureza Knoop) de resinas compostas diretas, visando a possibilidade de indicação para restauraçoes indiretas. Foram usadas as resinas diretas Fillmagic, Concept, Glacier, Z100, Masterfill e W3D Master e as indiretas Solidex e Belleglass HP como controle. Para cada resina direta foram confeccionados 60 espécimes em barra (10x2x2mm), 30 irradiados em uma face e 30 nas duas faces (30 espécimes = 10 controle, 10 autoclave e 10 forno de luz). Para as resinas indiretas foram preparados 10 espécimes conforme processamento de seus fabricantes. 380 espécimes foram submetidos ao ensaio de resistência à flexão (Kratos). De cada condição experimental, 10 fragmentos foram usados para ensaio de microdureza Knoop (Shimadzu HMV-2). A análise de variância e o teste de Tukey demonstraram significância para resistência à flexão nos fatores Resina (p<0,001) e Tratamento (p=0,001) e na interação Resina x Tratamento (p=0,001). Para a microdureza Knoop os três fatores e as interações foram significantes: Resina (p=0,001); Face (p=0,001) Tratamento (p=0,017); Resina x Face (p=0,001); Resina x Tratamento (p=0,007); Face x Tratamento (p=0,001) e Resina x Face x Tratamento (p=0,024). A maior média de cada resina direta, independente da condição experimental, foi comparada às médias das resinas indiretas. Os resultados apontam que na resistência à flexão (Z100 = W3D = Fillmagic = Glacier) e (Z100 > Masterfill > Belleglass HP > Concept > Solidex). Na Dureza Knoop (Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill e Solidex). Conclusão: as propriedades físicas (resistência à flexão e dureza Knoop) não são obstáculos na indicação de resinas compostas de uso direto para restaurações indiretas / This study evaluated the influence of pre-cure energy density, and additional post-cure treatments in optimizing the physical properties (Flexural strength and Knoop microhardness) of direct resin composites with the aim at allowing their use for indirect restorations. Direct resin composites evaluated were Fillmagic, Concept, Glacier, Z100, Masterfill and W3D Master; indirect composites were Solidex and Belleglass HP. Sixty bar-shaped specimens (10x2x2mm) were prepared for each material, so that 30 of them were light-cured by one surface and 30 on both surfaces. From the 30 specimens of each group, 10 were control, 10 were submitted to additional autoclave and 10 to light oven treatment. Ten specimens were prepared with each indirect composite following the manufactures’ recommendations. The 380 specimens were submitted to flexural strength test (Kratos universal testing machine), and values obtained at fracture were reported. After that, 10 fragments were chosen for each experimental condition and assessed for Knoop microhardness (Shimadzu HMV-2). Data were submitted to analysis of variance and Tukey’s test at p<0.05. Statistically significant differences were found among flexural strength results regarding composite materials (p<0.001), treatments (p<0.001) and interactions (composite x treatment, p<0.001). Regarding Knoop microhardness, both three factors and their interactions were also significant: composite (p<0.001), surface (p<0.001) and treatment (p<0.017), composite x surface (p<0.001), composite treatment (p<0.001), surface x treatment (p<0.001) and composite x surface x treatment (p<0.024). The highest mean value for each direct composite, regardless of the experimental condition, was compared to the mean values obtained for the indirect materials. With regard to flexural strength, comparisons point out that Z100 = W3D = Fillmagic = Glacier and Z100 > Masterfill > Belleglass HP > Concept > Solidex, whereas for Knoop microhardness Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill and Solidex. Conclusion: considering the physical properties evaluated in this study, they are not an obstacle to the indication of direct composites for indirect restorations

Os objetivos deste estudo foram: 1) avaliar a resistência à flexão em três pontos de um compósito para uso direto (Filtek Z350 XT, 3M ESPE) e um para uso indireto (Signum, Heraeus, Kulzer) reforçados por uma ou duas camadas de fibras de polietileno (Ribbond -THM, Ribbond®) ou de vidro (Interlig, Ângelus) tratados termicamente (170°C por 10 minutos), comparados com os grupos controle (não reforçados por fibras e/ou não tratados termicamente; 2) avaliar a sorção, a solubilidade e a estabilidade de cor dos compósitos reforçados, após armazenamento em água destilada à 37°C por 14 dias. A estabilidade de cor foi avaliada com auxílio de um espectrofotômetro de contato dental (Vita EasyShade, Vident, CA, USA). Para o ensaio de resistência à flexão, foram confeccionados espécimes retangulares com dimensões de 12 x 2 x 2mm (n=10), com os seguintes fatores de variação: a) compósito (para uso direto ou indireto); b) tipo e número de camadas de fibras (vidro ou polietileno/uma ou duas camadas); c) submetidos ou não a tratamento térmico. O tratamento térmico foi realizado 24 horas após fotoativação em estufa à temperatura de 170°C por 10 minutos. O ensaio foi realizado 24 horas após fotoativação ou tratamento térmico. Para avaliação de sorção/solubilidade e estabilidade de cor, foram confeccionados espécimes em forma de disco com dimensões de 15 x 2mm (n=5), em que foram analisados os seguinte fatores: a) compósito (para uso direto ou indireto); b) tipo de fibra (vidro ou polietileno); c) número de camadas de fibras (uma ou duas). Foi realizada análise dos parâmetros de cor antes e após imersão em água deionizada por 14 dias. Os resultados foram analisados por ANOVA e teste de contraste de Tukey, com nível de significância de 5% e revelaram que a fibra de vidro, quando utilizada em duas camadas, propiciou os maiores valores de resistência à flexão para os dois compósitos testados (165,4 MPa Z350XT e 208,7MPa Signum ). O tratamento térmico não apresentou significância estatística quanto à resistência à flexão do compósito direto. Para o compósito para uso indireto (Signum ) foi encontrada diferença estatisticamente significante para o fator tratamento térmico, que indicou valores de resistência à flexão inferiores para os grupos tratados termicamente. O compósito para uso direto apresentou valor de sorção superior (33,6/cm3) ao do compósito para uso indireto (19,1/cm3). Para solubilidade, foi encontrada interação para os fatores compósito e tipo de fibra, indicando maiores valores para o compósito para uso direto associado à fibra de vidro. A análise de alteração de cor demonstrou maior valor de E para a fibra de polietileno (E =1,5) quando comparado à fibra de vidro (E=1,0). Concluiu-se que: 1) a adição de fibras propicia aumento dos valores de resistência à flexão de compósitos para uso direto e indireto, o aumento da resistência foi observado quando do uso de duas camadas de fibras; 2) o tratamento térmico à 170°C por 10 minutos não indicou melhora nas propriedades mecânicas dos compósitos reforçados; 3) adicionar fibras aos compósitos não aumentou os valores de sorção/solubilidade quando imersos em água; 4) Imersão em água não produziu alterações de cor relevantes para os compósitos reforçados com fibras se comparados aos sem fibras. / The aims of this study were: 1) to evaluate the flexural strength of one composite for direct use (Filtek Z350 XT, 3M ESPE) and one for indirect use (Signum, Heraeus, Kulzer) as a function of the reinforcement by one or two layers of polyethylene (THM-Ribbond, Ribbond ®) or glass fibers (Interlig, Angelus) submitted to heat treatment (170°C for 10 minutes) compared with control groups (not reinforced by fibers and/or not heat-treated; 2) evaluate water sorption, solubility and color stability of the reinforced composites, after storage in distilled water at 37°C for 14 days. Color stability was evaluated using a spectrophotometer (Vita Easyshade, Vident, CA, USA). For three point flexural bending test, rectangular specimens were prepared with dimensions of 12 x 2 x 2 mm (n=10), according to the following variation factors: a) composite (for direct or indirect use); b) type of fibers and number of layers (glass or polyethylene/one or two layers; c) subjected or not to heat treatment. The heat treatment was performed 24 hours after curing, in a furnace, at 170 ° C for 10 minutes. Tests were performed 24 hours after curing or heat treatment. To evaluate the water sorption/solubility and color stability, disc-shaped specimens were prepared with dimensions of 15 x 2 mm (n=5) according to the following variation factors: a) composite (for direct or indirect uses); b) fiber type (glass or polyethylene); c) number of fiber layers (one or two). Color parameters were analyze before and after immersion in deionized water for 14 days. The results were analyzed by ANOVA and Tukeys test with significance level of 5%, and indicated that the glass fiber when used in two layers, showed the highest flexural strength for the two tested composites (165.4 MPa - Z350XT and 208.7 MPa - Signum ). The heat treatment did not significantly affect the flexural strength of the direct composite. For the composite for indirect use (Signum ), a statistical significance for the factor heat treatment was found, indicating lower values of flexural strength for heat-treated groups. The composite for direct use showed higher water sorption value (33.6 /cm3) when compared to the composite for indirect use (19.1 /cm3). For solubility, a significant interaction was found for composite and fiber type, indicating higher values for direct composite and glass fiber. Color stability analysis showed higher color difference value for polyethylene fiber (E =1.5) when compared to glass fiber (E=1.0). It was concluded that: a) adding fibers increased the flexural strength values of the composites for direct or indirect use, the increase in strength was more pronounced when using two fiber layers; 2) heat treatment at 170 ° C for 10 minutes showed no improvement of the mechanical properties of fiber reinforced composites; 3) adding fibers to the composite did not increase the sorption/solubility after water immersion, 4) Immersion in water did not change the color of the fiber reinforced composites when compared with those without fibers.