Made available in DSpace on 2011-12-27T14:14:22Z (GMT). No. of bitstreams: 2 000422268-0.pdf: 14833302 bytes, checksum: 1b71642b280aa5b7984729b688fbd92e (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study examines histologically the effect of cement Calcium Phosphate (CFC) reinforced with nylon fibers, polypropylene and carbon used as implant supra-cortical femur of rats. We used 20 male Wistar rats, approximately 300g each. Being prepared plates CFC with fibers, on the size of 2mm thick and 6 mm in diameter, which were tightened in the femur of animals. These were euthanized at 30, 60, 90 and 120 days after the implant. These pieces were removed and subjected to a routine process for preparing slides slides, stained with Hematoxilyn and Eosin. The biocompatibility, the degree material’s resorption anda its ability to osteoconduction were evaluated at the different times. At all diferents times studied, the histological sections showed formation of dense tissue, few cellularized, showing slightly vascularized and discrete mononuclear infiltration. In the area around the implant, there are discrete reabsorption areas, and hyalinization induction of collagen fibers peripheral. The tissue includes the material of the implant. After 120 days, may be observed a formation of osteoid material. The degree of bone reabsorption in the periphery of the implant was less, and without statistical significance. Can be concluded that: The CFC with fiber is biocompatible promotes bone conduction and bone neoformation rounding the cement. CFC with fibers in the form of prefabricated plates is suitable for use as implants and bone substitute, within the parameters of this experiment. / Este estudo analisa histologicamente o efeito do Cimento de Fosfato de Cálcio (CFC) reforçado com fibras de náilon, carbono e polipropileno utilizado como implante supra-cortical em fêmur de ratos. Foram utilizados 20 ratos Wistar, machos, com cerca de 300g cada. Sendo confeccionadas placas de CFC com fibras, no tamanho de 2 mm de espessura por 6 mm de diâmetro, os quais foram aparafusados no fêmur dos animais. E estes foram eutanasiados em 30, 60, 90 e 120 dias após o implante sendo as peças removidas e submetidas ao processo de rotina para confecção de lâminas, coradas com Hematoxilina e Eosina. Foram avaliados nos diferentes tempos a biocompatibilidade, o grau de reabsorção do material e a sua capacidade de osteocondução. Em todos os tempos estudados os cortes histológicos revelam formação de tecido conjuntivo denso, pouco celularizado, apresentando discretamente vascularizado e discreto infiltrado inflamatório mononuclear. No entorno do implante, observam-se discretas áreas de reabsorção, e indução de hialinização das fibras colágenas periféricas. O tecido apresenta inclusão do material do implante. Aos 120 dias chama a atenção a formação de material osteóide, O grau de reabsorção óssea na periferia do implante foi menor não apresentando significância estatística. Podendo-se concluir que: O CFC com fibras é biocompatível, promove a osteocondução e neoformação óssea contornando o cimento. O CFC com fibras, na forma de placas pré-fabricadas é adequado para ser utilizado como implante e substituto ósseo, dentro dos parâmetros deste experimento.

Made available in DSpace on 2011-12-27T14:14:24Z (GMT). No. of bitstreams: 2 000435511-0.pdf: 4163986 bytes, checksum: 37629882e85d83ed66d26ed9bed14b82 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / In order to accelerate and improve the quality of the osseointegration process has recently been given emphasis to growth factors. Thus, this thesis was aimed to evaluate the use of growth hormone (GH) on osseointegration of titanium implants. This thesis is composed of two papers, the first chapter is a review of literature on the use of growth factors, and, in particular GH in the process of bone repair. The second chapter is an experimental study to evaluate the topical use of rhGH in the osseointegration of nanotexturized titanium implants inserted in the tibia of rabbits. We used 14 animals randomly divided into rhGH-treated group and control group. In the rhGH-treated group was administered 1 IU of rhGH in surgical defect immediately before the placement of each implant. In the control group was not used rhGH. Each animal received two implants in the left tibia. The animals were sacrificed at 14 and 42 days after surgery. The peri-implant regions were avaluated by transmission and reflection on optical microscopy (OM), to pull out biomechanical testing of implants and scanning electron microscopy (SEM). In all analyzes the rhGH-treated groups showed better performance than the control groups, especially at 14 days. MO at 14 days in the rhGH-treated group have histological characteristics of proliferative repair phase with new bone formation and also marked cortical reaction from the endosteum and periosteum and at 42 days, the bone tissue has a lamellar appearance.The control group at 14 days also has characteristics of the inflammatory and moderate proliferative new bone formation, and with 42 days the new bone does not have lamellar characteristics. In the pull-out testing of the rhGH-treated group showed tension of 59. 26N/cm2 and 29. 69 N/cm2 at 14 and 42 days respectively. The control group showed tension of 33. 88 N/cm2 and 25. 99 N/cm2 respectively. The implants analyzed in the SEM showed in the rhGH-treated group at 14 days greater amount of bone attached, but at 42 days there were no differences between groups. The findings in this experiment corroborate the literature, which observed that rhGH increases the speed and amount of newly peri-implanted bone, especially in the early stages of bone repair. Thus, this thesis concludes that topical application of rhGH in the region peri-implant area induces new bone formation. / Com o intuito de acelerar e melhorar a qualidade do processo de osseointegração, recentemente tem sido dado ênfase aos fatores de crescimento. Logo, foi objetivo dessa Tese avaliar o emprego do hormônio do crescimento (GH) na osseointegração de implantes de titânio. Esse trabalho é composto de dois artigos, o primeiro artigo é uma revisão de literatura sobre o emprego dos fatores de crescimento, e, em especial o GH, no processo de reparo do tecido ósseo. O segundo artigo é um estudo experimental no qual se avaliou o uso tópico do rhGH no processo de osseointegração de implantes de titânio nanotexturizados inseridos na tíbia de coelhos. Foram utilizados 14 animais divididos aleatoriamente em grupo teste e controle. No grupo teste foi aplicado 1 IU de rhGH no defeito cirúrgico imediatamente antes da colocação de cada implante. No grupo controle não foi aplicado o rhGH. Cada animal recebeu 2 implantes na tíbia esquerda. Os animais foram sacrificados em 14 e 42 dias depois da cirurgia. As regiões periimplantares foram submetidas à microscopia óptica (MO) de transmissão e de reflexão, e os implantes ao ensaio biomecânico de pull out e a microscopia eletrônica de varredura (MEV). Em todas as análises realizadas o grupo teste apresentou desempenho superior ao controle, principalmente aos 14 dias. Na MO aos 14 dias o grupo teste possuía características histológicas da fase proliferativa do reparo com acentuada neoformação óssea e também a formação de uma espécie de calo ósseo sobre a cortical óssea externa, e aos 42 dias o tecido ósseo possuía aspecto lamelar.O grupo controle aos 14 dias possuía ainda características da fase inflamatória e proliferativa com moderada neoformação óssea, e aos 42 dias o tecido ósseo neoformado ainda não possuía características lamelares. No ensaio de pull-out o grupo teste apresentou tensão de 59,26 N/cm2 e 29,69 N/cm2 aos 14 e 42 dias respectivamente, enquanto o grupo controle apresentou tensão de 33,88 N/cm2 e 25,99 N/cm2 aos 14 e 42 dias, respectivamente. Os implantes analisados no MEV demonstraram no grupo teste aos 14 dias maior quantidade de tecido ósseo aderido, porém aos 42 dias não se observaram diferenças entre os grupos. Os achados no experimento corroboram com a literatura, em que se observa que o rhGH aumenta a velocidade e quantidade de osso periimplantar neoformado, principalmente em estágios iniciais do reparo ósseo. Com base na revisão de literatura pesquisada e com os resultados do presente experimento, conclue-se que a aplicação tópica de rhGH na região periimplantar acelera o processo de neoformação óssea.

Made available in DSpace on 2011-12-27T14:14:31Z (GMT). No. of bitstreams: 2 000399356-0.pdf: 4105847 bytes, checksum: 0c59a09fa1073f779a885d9635fec74e (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This research in vivo blind-controlled was to investigate post mortem, through the histomorphometrical analysis, the influence of the low power laser in bone formation on machined and roughened titanium dental implants inserted in rabbits tibia-bones. The animals were subjected or not to the GaAlAs irradiation laser device, with a length of wave of 830nm, in a continuous form during 10 seconds, with a power output of 100mW. A total of six white New Zealand rabbits were equally and randomly divided into two groups, irradiated and controlled groups, where four implants were placed in each animal. Two machined were implanted in the right tibia and two roughened in the left tibia. The experimental group received irradiation through the skin in three points around the implants, during 15 days, every 48 hours. The first application was performed in the same day of the surgery, with a total of eight days of irradiation and total dose of 24J/cm2 in each tibia (3 points x 1J x 8 applications = 24J). The control group were submitted to the same routine of the irradiated animals, however with the laser equipment turned off. After 30 days all animals suffered euthanasia, and histological sections were obtained. The sections were then stained with toluidine blue. Each section was reduced to a final thickness of about 10 to 19μm. The bone-to-implant contact measurements in percentage were performed by using two central sections from each sample, blinded form, were photomicrographed on optical microscope connected to an image analyzer digital program. The averages obtained from the two sections of each implant right after the blinding belittled were compared in general form between laser and control groups and among the four sub-groups were performed by using Student’s t-test. There was no statistically significant difference (p> 0,05) in the percentage of bone-to-implant contact between the laser (77,048 % ± 10,173) and control groups (69,516 % ± 19,284) in a general form, not even between the sub-groups roughened with laser (81,530 % ± 10,155), roughened control (72,190 % ± 16,778), machined with laser (72,565 % ± 8,737) and machined control (66,842 % ± 22,791). In the present research, results suggest that the low power laser, with the irradiated protocol, did not significantly contribute for increasing the percentage of bone-to-implant contact. Nevertheless, new formed bone undergone to the with GaAlAs irradiation laser device during the period of osseointegration, it seems to present a bigger vasculature and lamellar organization compared to the control group, suggesting bone maturation improvement. However, further research is necessary to better explain the biological mechanisms of low power laser action on the mediation of necessary process for titanium implants osseintegration as well as dosimetric parameters for getting bone biostimulation. / Este trabalho in vivo controlado e com cegamento avaliou post mortem, através da análise histomorfométrica, a influência do laser de baixa potência na formação óssea em implantes lisos e texturizados inseridos em tíbias de coelhos, submetidos ou não à irradiação com laser de GaAlAs com comprimento de onda de 830nm, de forma contínua por 10 segundos, com potência de 100mW. Para tanto foram utilizados seis coelhos da raça Nova Zelândia, distribuídos igualmente de forma aleatória em grupo irradiado e grupo controle, onde cada coelho recebeu quatro implantes, sendo dois lisos na tíbia direita e dois texturizados na tíbia esquerda. Os animais do grupo experimental receberam irradiação transcutaneamente em três pontos ao redor dos implantes, durante 15 dias a cada 48 horas, sendo a primeira aplicação no dia da cirurgia, com total de oito dias de irradiação e dose total de 24J/cm2 em cada tíbia (3 pontos x 1J x 8 aplicações = 24J).Os animais do grupo controle foram submetidos à mesma rotina dos animais irradiados, porém com equipamento laser desligado. Após 30 dias todos os animais sofreram eutanásia para obtenção de lâminas histológicas coradas com azul de toluidina a partir de cortes das tíbias com os implantes inseridos numa espessura final de 10 a 19μm. Para avaliação do percentual de contato osso-implante os dois cortes mais centrais de cada amostra, de forma cegada, foram fotomicrografados em microscópio óptico e analisados através de um programa digital de processamento de imagens. As médias obtidas a partir dos dois cortes de cada implante, após desfeito o cegamento, foram comparadas de forma geral e dentro dos grupos utilizando-se o teste t-student. Não houve diferença estatisticamente significativa (p>0,05) no percentual de contato osso-implante entre os grupos laser (77,048% ± 10,173) e controle (69,516% ± 19,284) de forma geral, nem entre os subgrupos texturizado com laser (81,530% ± 10,155), texturizado controle (72,190% ± 16,778), liso com laser (72,565% ± 8,737) e liso controle (66,842% ± 22,791).Estes resultados sugerem que o laser de baixa potência, com o protocolo de irradiação utilizado neste modelo animal, não contribuiu significativamente para o aumento do percentual de contato osso-implante. Não obstante, o osso novo formado submetido à irradiação com laser de GaAlAs durante o período de ossoeintegração, parece apresentar uma maior vascularização e organização lamelar que o grupo controle, sugerindo uma maior maturação. Porém, são necessárias novas pesquisas de modo a preencher as lacunas ainda existentes quanto ao entendimento dos mecanismos biológicos da ação do laser de baixa potência na mediação dos processos necessários à osseointegração de implantes de titânio, bem como dos parâmetros dosimétricos para obtenção da bioestimulação óssea.

Made available in DSpace on 2011-12-27T14:14:32Z (GMT). No. of bitstreams: 2 000430369-0.pdf: 669885 bytes, checksum: 002b0553e91e6ef0df52888b901e3907 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study is evaluate 3 implant surfaces in dogs at early times of ossointegration. Forty eight implants (Ti-6Al4V) were used: Resorbable Blasted Media Acid Etched (RBMa), Alumina Blasted Acid Etched (AB/AE) as control group and Alumina Blasted Acid Etched + Resorbable Blasted Media Acid Etched (AB/AE + RBMa). Tree implants per group were utilized for fisico/chemical characterization (SEM, AFM and XPS). For the animal procedure 3 implants were placed on proximal tibiae bilaterally and remained for 2 weeks in vivo (8 dogs, 16 per surface, 6 per dog). Following euthanasia half of implants were torque to interface failure and other half for non-dehydrated histological processing to final sections of ≈30μm for bone to implant contact (%BIC) and bone arial fraction ocuppied (BAFO). The GLM ANOVA at 95% of significance and Dunn’s post-hoc were used for statistical analysis. AB/AE group presented higher values of Sa e Sq than groups RBMa and AB/AE + RBMa. Ti, Al, O, C, N, Ca and P were observed in groups RBMa and AB/AE + RBMa, for AB/AE group Ti, Al, O, C, N and V were observed. No statistical difference was observed for histomorfometric parameters (%BIC and BAFO) among groups. All surfaces are biocompatible and osseoconductive, newly formed woven bone was observed in proximity with all surfaces. / O objetivo deste estudo é determinar em cães, a influência dos tratamentos de superfície através de jateamento com biocerâmicas nos períodos iniciais de osseointegração. Quarenta e oito implantes (Ti-6Al-4V) tratados com jateamento com biocerâmica seguido de ataque ácido (RBMa), jateamento com alumina e ataque ácido (AB/AE) usado como controle, jateamento com alumina e ataque ácido com subsequente jateamento com biocerâmica e ataque ácido (AB/AE + RBMa). Três implantes de cada grupo foram destinados a caracterização físico/química por microscopia eletrônica de varredura (SEM), microscopia de força atômica (AFM) e Espectroscopia Fotoelétrica de Raios X (XPS). O estudo animal compreendeu a colocação de 48 implantes na porção proximal da tíbia (8 cães, 16 por superfície, 6 por cão) os quais permaneceram por 2 semanas in vivo. Após a eutanásia, metade dos espécimes foram destinados ao teste de torque de remoção e a outra metade foram processadas para obtençao de lâminas não descalcificadas de aproximadamente 30μm de espessura onde foram realizadas análises histomorfológica e histomorfométrica de contato osso/implante (%BIC) e fração arial de osso formado (BAFO). O teste GLM ANOVA com 95% de significância foi utilizados para análise estatística com post-hoc de Dunn. A AFM demonstrou valores de rugosidade (Sa e Sq) significante maiores do grupo AB/AE em relação aos grupos RBMa e AB/AE + RBMa. O XPS demonstrou presença de Ti, Al, O, C, N, Ca e P para os grupos RBMa e AB/AE + RBMa, os mesmos elementos foram em contrados no grupo AB/AE, juntamente com o V, exceto Ca e P. Não foram encontradas diferenças estetísticas para %COI e BAFO. Todos os grupos demonstraram bicompatibilidade com osso imaturo observado em íntimo contato com as superficies.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2013-04-17T13:33:15Z No. of bitstreams: 1 447176.pdf: 2750615 bytes, checksum: 6db2237c9889f4756aec07a95d930df2 (MD5) / Made available in DSpace on 2013-04-17T13:33:16Z (GMT). No. of bitstreams: 1 447176.pdf: 2750615 bytes, checksum: 6db2237c9889f4756aec07a95d930df2 (MD5) / Este estudo é parte de um projeto que teve por objetivo avaliar o efeito da terapia com laser de baixa intensidade pós-implante dentário osseointegrável no funcionamento da glândula tireoide e, consequentemente, na regulação do cálcio, através da mensuração dos níveis hormonais de Triiodotironina (T3), Tiroxina (T4) e dos níveis de Cálcio e Albumina no soro sanguíneo de coelhos. Foi avaliado o efeito de 3 doses terapêuticas distintas de LLLT utilizadas para aceleração do processo de osseointegração de implantes dentários. Para tanto, foram utilizados 40 coelhos da ordem Lagomorpha, raça Nova Zelândia, machos, pesando entre 3 e 4 kg, clinicamente sadios, distribuídos aleatoriamente em cinco grupos, com oito animais cada, sendo dois grupos designados como controle: o grupo controle CI (animais não irradiados e não operados) e o grupo controle CII (animais não irradiados); e três grupos designados como experimentais: EI, EII e EIII – animais irradiados com três doses distintas de laser – grupo experimental EI (dose total - 70J/cm²), grupo experimental EII (dose total - 35J/cm²) e grupo experimental EIII (dose total - 140J/cm²). Para padronizar os experimentos, todos os animais dos grupos CII, EI, EII e EIII foram submetidos ao procedimento cirúrgico de exodontia do incisivo inferior esquerdo e colocação imediata de um implante osseointegrável com superfície nanotexturizada (Nanotite® - Biomet 3iTM) no respectivo alvéolo, criando uma condição clínica inicial de igualdade entre os quatro grupos operados. Os animais do grupo controle CI participaram da mesma rotina dos demais; no entanto, não foram submetidos a nenhum dos procedimentos clínicos/cirúrgicos, servindo como controle absoluto nos testes imunológicos para contagem de T3, T4, Cálcio e Albumina. Os animais dos grupos experimentais foram irradiados com o laser de diodo infravermelho com meio ativo GaAlAs (Arseneto de Gálio e Alumínio), com comprimento de onda de 830nm, de forma pontual, com potência de 50mW, no modo de emissão contínua, a cada 48 horas, num total de sete sessões de aplicação, durante o período de 13 dias. O protocolo de irradiação foi iniciado imediatamente após o procedimento cirúrgico. As coletas de sangue para dosagens laboratoriais de T3, T4, Cálcio e Albumina foram realizadas por meio de punção venosa da veia jugular nos cinco grupos em quatro momentos distintos: 72 horas antes do procedimento cirúrgico, imediatamente após a primeira aplicação de laser, 72 horas após a primeira aplicação de laser e 72 horas após a última aplicação de laser. Os resultados obtidos demonstraram diferenças estatisticamente significativas para os valores de T3 e Cálcio entre os grupos estudados e para os valores de T3, T4, Cálcio e Albumina nos diferentes tempos de coleta ao longo do experimento. Conclui-se que a LLLT, no protocolo de irradiação utilizado neste estudo, apesar de ter alterado significativamente os níveis hormonais de T3 e T4 e os níveis de Cálcio e Albumina circulantes no soro de coelhos, não comprometeu definitivamente o funcionamento da glândula tireoide dos mesmos, pois na etapa final do controle hormonal percebe-se o restabelecimento da função glandular. / This study is part of a larger project that sought to assess the effect of lowlevel laser therapy (LLLT) after placement of an osseointegrated dental implant on thyroid gland function – and, consequently, calcium regulation – and its potential interference with the osseointegration process. Toward this end, circulating serum levels of triiodothyronine (T3), thyroxine (T4), calcium, and albumin were measured in rabbits. The effects of three therapeutic doses of LLLT, used to accelerate the dental implant osseointegration process, were assessed. Forty healthy male New Zealand rabbits (order Lagomorpha), weight 3–4 kg, were allocated randomly across five groups of eight each: two control groups, CI (no LLLT, no surgery) and CII (no LLLT), and three experimental groups, EI, EII, EIII, exposed to three different doses of laser radiation (EI, total dose 70 J/cm²; EII, total dose 35 J/cm²; and EIII, total dose 140 J/cm²). For standardization purposes, all animals in groups CII, EI, EII, and EIII underwent surgical extraction of the mandibular left incisor and immediate placement of a nanoparticle-coated osseointegrated implant (NanoTite® – Biomet 3iTM) into the prepared socket, creating a condition of equality between groups at baseline. Animals in group CI were exposed to the same handling conditions, but did not undergo any clinical or surgical procedures, thus serving as an absolute control for T3, T4, calcium, and albumin measurements. Animals in the experimental groups received spot irradiation with a GaAlAs (gallium aluminium arsenide) infrared diode laser, wavelength 830 nm, power 50 mW, in continuous emission mode, over two points, every 48 hours over 13 days, for a total of seven sessions; the irradiation protocol was started immediately after the surgical procedure. Blood was collected for measurement of T3, T4, calcium, and albumin levels, by puncture of the external jugular vein, at four points in time: 72 hours before surgery, immediately after the first LLLT session, 72 hours after the first LLLT session and 72 hours after the last LLLT session. The results showed significant differences in T3 and calcium levels between study groups, as well as significant within-group differences in T3, T4, calcium, and albumin levels over time. We conclude that, despite a significant effect on circulating serum levels of T3, T4, calcium and albumin, the LLLT protocol used in this study did not lead to impairment of thyroid function in a rabbit model, because in the final stage of the hormonal control it is noticed the reestablishment of glandular function.

Made available in DSpace on 2013-08-07T18:53:51Z (GMT). No. of bitstreams: 1 000400633-Texto+Parcial-0.pdf: 244771 bytes, checksum: 929e01919e85f7195f849c8c0c09bddc (MD5) Previous issue date: 2008 / Titanium and its alloys are widely applied as orthopedic and dental materials implants because of their excellent biocompatibility, low elastic modulus and high corrosion and wear resistance. The main causes that influence the adequate biomaterial functionality are the bone tissue growth and its adhesion to the implant surface. Recent researches indicated that the adhesion between the living bone tissue and the implant is related to the surface roughness, due to surface modifications, and the increasing of bone ingrowths in this region. These surface modifications are achieved mostly by deposition of porous coating using thermal spraying technique, application of blasting of ceramic particulates and acid and electrochemical etchings. The main goal of this research is to estimate the osseointegration of titanium porous coating in contact with sheep cortical bone, as well as to evaluate the bone conductive behavior of these coatings. The second goal is to evaluate the adhesive strength of the titanium porous coatings deposited on modified surfaces of titanium coin shaped implants. X-ray fluorescence (XRF) and xray dispersive energy spectroscopy (EDS) were applied to verify the chemical composition of the Ti implants, titanium porous coatings and osseointegrated titanium implants. Scanning electron microscope (SEM) was applied to characterize the morphology of titanium coin shaped implants, titanium porous coating and the bone tissue/titanium porous coatings/titanium implants interface. Pull out tests were applied to evaluate the osseointegration and the adhesion of porous coatings on the surface of titanium coin shaped implants. The rupture tension values verified for titanium porous coatings are higher than the values verified for titanium implants without porous coatings (RENZ, 2007), mainly after 30 days of healing. The titanium porous coatings etched with HF showed the highest rupture tension values when compared with titanium porous coatings as deposited. The adhesion values of titanium porous coatings increased for modified surfaces when compared with the adhesion values verified for the machined surfaces. / Titânio e suas ligas são amplamente aplicados como materiais de implantes ortopédicos e odontológicos devido a sua excelente biocompatibilidade, baixo módulo de elasticidade e alta resistência ao desgaste e à corrosão. Os fatores que influenciam decisivamente a adequada funcionalidade de um biomaterial são o crescimento do tecido ósseo e a sua adesão à superfície do implante. Pesquisas recentes indicam que o processo de adesão entre o implante e o tecido vivo depende da rugosidade superficial, devido à modificação da sua superfície, e do crescimento ósseo nesta região. Essas modificações são alcançadas principalmente com a deposição de revestimentos porosos por aspersão térmica, a aplicação de jateamentos com particulados cerâmicos, ataques ácidos e eletroquímicos, entre outros. O objetivo específico desta pesquisa é estimar a osseointegração de filmes porosos de titânio em contato com a cortical óssea de ovinos, bem como avaliar o comportamento do processo de osseocondução desses filmes. O segundo objetivo é avaliar a adesão destes filmes porosos de titânio depositados sobre superfícies modificadas de discos de titânio. As técnicas de fluorescência de raios X e espectroscopia por energia dispersiva de raios X foram aplicadas para verificar a composição química dos implantes, filme de titânio e implantes osseointegrados.A Microscopia Eletrônica de Varredura foi usada para caracterizar a morfologia dos discos de Ti, filme de titânio e a interface tecido ósseo/filme de titânio/metal-base. Testes de tração foram aplicados para avaliar a osseointegração dos filmes de titânio e a adesão destes aos discos. Os valores de tensão de ruptura estimados para os filmes de titânio são superiores aos verificados em discos sem revestimento poroso de titânio (RENZ, 2007), principalmente no período de 30 dias pós-operatório. Os filmes de titânio atacados com ácido fluorídrico apresentaram os maiores valores de tensão de ruptura da interface osso-filme quando comparados aos filmes somente depositados, indicando aumento da osseointegração. Os valores de adesão dos filmes de titânio para as superfícies modificadas são maiores que os valores de adesão na superfície somente usinada.

Made available in DSpace on 2013-08-07T18:53:53Z (GMT). No. of bitstreams: 1 000402797-Texto+Completo-0.pdf: 6535759 bytes, checksum: d71c96f436ffa7b29f0ee38a5038a7f7 (MD5) Previous issue date: 2007 / Osseointegration process is strongly related to superficial physical-chemical properties of materials applied as implants. Recent researches indicate that the development of surfaces treatments increases the efficiency of this process, influencing directly on the initial response of the cells in bone/implant interface, on rate and quality of bone tissue formation. However, the best relationship among several surface treatments processes and bone implant bonding remains unknown. The aim of this study was to evaluate in vivo osseointegration of coin shaped titanium surface treatmented implants by pull out assays according to ASTM C 633. The implants superficial morphology was characterized using MEV and rugosimetry techniques. Chemical composition was evaluated by means of EDS and XRF analyses according to NBR ISO 5832-2, while corrosion resistance was verified by Linear Polarization technique, according to ASTM F 746. The results showed that chemical composition of samples groups are in agreement with the limits recommended towards the presence of contaminants, except the brushed group. The current density values indicated passivation behavior, which is significantly lower than the maximum value allowed. The pull out assays showed that 30 days of healing period was insufficient to achieve satisfactory bone healing. The results obtained for the 60 days samples group demonstrated superficial roughness values which influenced maximum tension values. / O processo de osseointegração está fortemente ligado com as propriedades físicoquímicas superficiais dos materiais utilizados em implantes. Pesquisas recentes indicam que o desenvolvimento de superfícies texturizadas aumenta a eficiência deste processo, influenciando diretamente na resposta inicial das células na interface osso/implante, na taxa e na qualidade da formação do tecido ósseo formado. Porém, não foi verificada a melhor relação entre os diversos tipos de tratamentos de superfícies e a adesão óssea ao implante. O objetivo deste trabalho foi avaliar a osseointegração in vivo de implantes de titânio cilíndricos, submetidos a diferentes tratamentos de superfície, através de ensaio mecânico do tipo pull out, de acordo com a norma ASTM C 633. A morfologia superficial dos implantes foi caracterizada pelas técnicas de MEV e rugosimetria. A composição química foi avaliada pelas técnicas de EDS e XRF, de acordo com a norma NBR ISO 5832-2, enquanto que, para avaliar a resistência à corrosão, foi utilizada a técnica de Polarização Linear, segundo as recomendações da ASTM F 746. Os resultados indicaram que a composição química dos grupos de amostras, com exceção do escovado, atende aos limites estipulados quanto ao teor de contaminantes presentes. Os valores de densidade de corrente indicam comportamento de passivação, significativamente abaixo do valor máximo permitido pela norma. Os testes de pull out mostraram que 30 dias de cicatrização foram insuficientes para se obter crescimento ósseo satisfatório. De modo geral, pode-se dizer que os resultados obtidos para o grupo de 60 dias indicaram que os valores de rugosidade superficial influenciaram os valores de tensão máxima.

Made available in DSpace on 2013-08-07T18:54:00Z (GMT). No. of bitstreams: 1 000443419-Texto+Completo-0.pdf: 4259691 bytes, checksum: 3fbe554be4dac8a49f70f55d940079dd (MD5) Previous issue date: 2012 / The aim of this study was to assess, in vivo, the effect of two different surface treatments of titanium implants - plasma-spray (PSA) and nano-textured plasma-spray (PSA-nano) - at the bone-to-implant interface (osseointegration), associated or not to the recombinant human growth hormone (rhGH). Twenty-four prototypes of pure titanium implants, 6-mm long and 2-mm wide, were especially fabricated in a cylindrical shape and placed in 12 New Zealand rabbit’s tibiae. The implants were divided into four groups: 1) PSA implants without rhGH, 2) PSA implants with rhGH, 3) PSA-nano implants without rhGH and, lastly, 4) PSA-nano implants with rhGH. The animals were sacrificed 14 and 42 after the surgeries. Samples were collected and analysed by optical microscopy (OM), scanning electronic microscopy (SEM) and infrared microscopy (μ-FTIR), besides the pull-out mechanical test. The results showed that in the early stage of osseointegration, the recombinant human growth hormone has favored new bone formation, regardless the surface treatment. Howev-er, in the later stage, the nano-textured surface, even without the hormone, has made a positive influence on the new bone formation, when compared to its use with hormone. In this stage, only the plasma-spray surface (PSA) has been favored by the growth hormone. / O objetivo deste trabalho foi avaliar, in vivo, o efeito de dois diferentes tratamentos de superfície de implantes de titânio - plasma-spray (PSA) e plasma-spray nanotexturizado (PSA-nano) - na interface osso-implante (osseointegração), associados ou não ao hormônio do crescimento humano recombinante (rhGH). Vinte e quatro protótipos de implantes de titânio puro, medindo 6 mm de comprimento por 2 mm de diâmetro, foram especialmente confeccionados em uma forma cilíndrica e colocados na tíbia de 12 coelhos da raça New Zealand. Os implantes foram divididos em quatro grupos: 1) implantes PSA sem rhGH, 2) implantes PSA com rhGH, 3) implantes PSA-nano sem rhGH e, por último, 4) implantes PSA-nano com rhGH. Os animais foram sacrificados 14 e 42 dias após as cirurgias. As amostras foram coletadas e analisadas por microscopia óptica (MO), microscopia eletrônica de varredura (MEV) e microscopia de infravermelho (μ-FTIR), além do teste mecânico de pull-out. Os resultados mostraram que no estágio inicial da cicatrização, o hormônio do crescimento recombinante humano favoreceu a neoformação óssea, independente do tipo de superfície. Porém, no estágio tardio, a nanotexturização, sem a presença do hormônio, exerceu uma influência positiva na neoformação óssea, quando comparada ao seu emprego com o hormônio. Neste estágio, apenas a superfície de plasma-spray (PSA) foi favorecida pelo hormônio do crescimento.

Orientador: Guilherme Elias Pessanha Henriques / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T09:25:51Z (GMT). No. of bitstreams: 1 Daroz_LuizGustavoDias_M.pdf: 1050394 bytes, checksum: 25c85e7dd89cc812e9e871cdc982a3a1 (MD5) Previous issue date: 2006 / Resumo: A obtenção de uma peça perfeitamente adaptada aos componentes de retenção, mantendo a resistência estrutural a custo acessível é o principal objetivo durante a construção de uma prótese implanto-retida de múltiplos elementos. Além disto, julgar a qualidade da adaptação das peças depende da confiabilidade dos métodos existentes para determinação da passividade. O objetivo deste estudo foi determinar o desajuste marginal de infra-estruturas metálicas implanto-retidas tipo monobloco antes e após o fresamento corretivo destas peças empregando retificador manual. Avaliou-se ainda a hipótese de que os procedimentos de fresamento corretivo podem ter influência sobre a confiabilidade do teste do parafuso único utilizado para averiguação de adaptação marginal de peças múltiplas sobre implantes. Foram confeccionadas 40 infra-estruturas metálicas pela técnica do monobloco, sendo 20 fundidas em titânio comercialmente puro (Ti c.p.) e outras 20 fundidas em liga de cobalto-cromo (Cr-Cr). Para tal, utilizou-se matriz metálica simulando a disposição clínica de implantes osseointegrados na região interforames mentonianos contendo 5 análogos de pilares cônicos para peças múltiplas padrão Branemark (Micro-Unit - Conexão) e cilindros protéticos calcináveis compatíveis. As peças confeccionadas em Ti c.p. e em Co-Cr, foram subdivididas em 2 subgrupos (n=10) de acordo com a seqüência de retificação a que foram impostas: Seqüência A ¿ fresamento corretivo das bordas de adaptação dos cilindros protéticos seguido do fresamento corretivo da base de assentamento da cabeça do parafuso protético ao pilar; e, Seqüência B ¿ fresamento corretivo da base de assentamento da cabeça do parafuso protético ao pilar seguido do fresamento corretivo das bordas de adaptação dos cilindros protéticos. A conduta forneceu um total de 4 grupos experimentais (Titânio A e B; Co-Cr A e B). As leituras de desajuste marginal, realizadas sobre a matriz metálica e com auxílio de um microscópio mensurador, foram baseadas na técnica do parafuso único e realizadas em cada estrutura antes e após cada etapa de retificação corretiva. As médias de desajuste marginal de cada estrutura foram calculadas e consideradas como uma unidade para a análise estatística. O teste de Friedman foi aplicado com nível de significância de 5% para avaliar o efeito dos diferentes passos de retificação sobre o desajuste marginal. Nos Grupos Ti A e B, assim como no Grupo Co-Cr A, não foi observada diferença significativa entre as condições experimentais (Grupo Ti A, p=0,9048; Grupo Ti B, p=0,273 e Grupo Co-Cr A, p=0,4966). Porém, diferenças estatisticamente significativas foram observadas no Grupo Co-Cr B, após a retificação corretiva das bordas dos cilindros fundidos (p=0,0017). Foi concluído que os procedimentos de fresamento corretivo não mostraram efeito significativo sobre a adaptação marginal das pecas de titânio. Contudo, em um grupo de peças fundidas em Co-Cr, a retificação das bordas dos cilindros mostrou efeito adverso sobre a passividade. Os procedimentos de fresamento corretivo parecem não apresentar influência significativa sobre a confiabilidade do teste do parafuso único, porém, devem ser realizados cuidadosamente, necessitando de aperfeiçoamentos para uma utilização segura / Abstract: The fabrication of a passively fitting framework over abutments and fixtures, maintaining its structural integrity and with a low costs, is the ultimate goal of the construction process of a multi-unit implant-support prosthesis. Furthermore, the accuracy and reliability of the passive fit determination methods have a crucial hole on framework misfit analysis. The objective was to evaluate the passive fit by the single-screw test method of cast commercially pure titanium (CP Ti) implantsupported frameworks after the corrective finishing of cast cylinders fitting borders and screw seats. The hypothesis tested was that finishing procedures could affect the single screw test measurements reliability. Were fabricated 40 frameworks by onepiece casting method, being 20 CP Ti frameworks and others 20 Co-Cr frameworks. A metallic index containing 05 Branemark-type multi-unit abutment analogs and respective calcinable cylinders were used to frameworks fabrication. The CP Ti and Co-Cr frames were assembled in 2 sub-groups (n=10) accordingly with the finishing sequence proposed: Group A - corrective finishing of cast cylinder borders followed by corrective finishing of cast cylinder screw seats - and Group B - corrective finishing of cast cylinder screw seats followed by corrective finishing of cast cylinder borders-. This conduct produce 4 experimental groups (CPTi A and B; Co-Cr A and B). The marginal gaps, assessed over the metallic matrix using a traveling microscope, were carried out before and after each corrective finishing step accordingly with one screw test protocol. The marginal misfit means of each framework was considered as a unit to statistical analyses. The Friedman¿s test was used with significance level set as 5% to analyze the effect of the different corrective finishing steps over frameworks passive fit. In the CPTi A and B Groups, and in the Co-Cr A Group, there was no significant differences between experimental conditions (Group CPTi A, p=0.9048; Group CPTi B, p=0.273 and Grupo Co-Cr A, p=0.4966). However, in the CPTi B Group, a significant difference was found after cast cylinder fitting borders corrective finishing (p=0.0015). It was concluded that the finishing process does not show any effect over Ti framewoks misfit values. However, to a group of Co-Cr frames, the fitting borders corrective finishing has a deleterious effect over passivity. The corrective finishing procedures seamed do not influence the single-screw test reliability, nevertheless, it should be used carefully and requires further improvements to guarantee a sever usage / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Renato Mazzonetto / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T00:56:48Z (GMT). No. of bitstreams: 1 Maurette_MarvisAllaisde_M.pdf: 1769240 bytes, checksum: 3ddb933e447862c0ef2db5b11338ce9d (MD5) Previous issue date: 2004 / Resumo: Este trabalho teve como objetivo avaliar clínica, radiográfica e subjetivamente a técnica de distração osteogênica alveolar (DOA) na reconstrução de rebordos alveolares atróficos. Foram avaliados 55 pacientes, submetidos a reconstrução alveolar vertical com distração osteogênica, por meio de um distrator justa-ósseo, na Faculdade de Odontologia de Piracicaba, Universidade Estadual de Campinas. Do total dos pacientes, 51% foram operados na região posterior de mandíbula, 40% na região anterior de maxila, 5% na região anterior de mandíbula e 4% na região posterior de maxila. O ganho ósseo vertical médio obtido para cada uma das respectivas regiões foi: 4,49mm; 7,46 mm; 6,09mm e 6,32mm com um ganho médio total de 6,09mm. Em relação às complicações encontradas durante o tratamento, 14 pacientes (25,45%) apresentaram complicações classificadas como menores, ou seja, todas aquelas que não interferiram com o resultado final do tratamento e 6 pacientes (10,90%) apresentaram complicações maiores que causaram a falha da técnica. Os pacientes submetidos ao estudo, foram ainda avaliados por meio de um questionário buscando a percepção dos eventos trans e pós-operatórios. Entre as respostas obtidas dos pacientes temos que 80% acharam que a cirurgia foi suportável, assim como o período pós-operatório (84%), não sentindo dor durante as ativações (88%) descrevendo somente uma sensação de pressão (58%) neste momento, não apresentando, de uma forma geral, dificuldade na ativação do aparelho (74%). Dos pacientes avaliados, 22% responderam que a haste de ativação era desconfortável ou altamente desconfortável, interferindo em algumas funções bucais. Cabe destacar que 78% dos pacientes se submeteriam novamente à cirurgia caso fosse necessário e que quando comparados com outros métodos de reconstrução como enxerto por exemplo, 80% dos pacientes referiram que este último era consideravelmente mais desconfortável. A técnica de DOA, demonstrou ser eficaz na reconstrução de rebordos alveolares atróficos com um sucesso de 89,09%, apresentando pequenas complicações que podem ser solucionadas por meio de uma pronta intervenção por parte do profissional. Apesar de ser uma técnica relativamente traumática, tem uma aceitação alta entre os pacientes submetidos a ela, porém alguns detalhes como a interferência da haste de ativação continua incomodando ao paciente. Cabe destacar que, quando comparada com os enxertos ósseos a aceitação é muito maior / Abstract: The aim of this study was to evaluate clinical, radiographic and subjectively the alveolar distraction osteogenesis technique (ADO) in the reconstruction of atrophy alveolar ridges. Fifty-five patients were submitted to the alveolar reconstruction with distraction osteogenesis, using a extra-alveolar distractor - 51% were operated in the posterior mandible area; 40% in the anterior maxilla; 5% in the anterior mandible region and 4% in the posterior maxilla. The mean real bone gain for each region was 4,49mm ; 7,46 mm; 6,09 mm and 6,32 mm respectively, with a mean of 6,09 mm. Complications presented during the treatment were minor in 14 patients (25,45%), and major complications in 6 patients (10,90%). Patients who were treated with this technique evaluates the perception of trans and postoperative events. The results showed that 80% thought the surgery is bearable, as well as in the postoperative period (84%), they didn't feel pain during the activations (88%) only pressure sensation (58%), and they didn't present difficulty in the activation of the apparel (74%). However 22% of the patients answered that the activation stem was uncomfortable or highly uncomfortable, interfering in some oral functions. 78% of patients would undergo the surgery again and that when compared with other reconstruction methods as bone graft for instance 80% of the patients referred that this was considerably more uncomfortable. The technique of ADO demonstrated to be effective in reconstruction of atrophic alveolar ridges with a success rate of 89,09%, with minor complications that can be solved with an opportune attendance by the professional. To weigh of being a technique relatively traumatic, it has a high acceptance among the patients submitted to it, however some details as the interference of the activation stem continue inconveniencing the patient. It fits to highlight that when compared with the bone grafts the acceptance is very larger / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica