Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2014. / Made available in DSpace on 2015-02-05T20:46:19Z (GMT). No. of bitstreams: 1 327728.pdf: 1775198 bytes, checksum: 71fd40fde69664480e569ccd87e6e444 (MD5) Previous issue date: 2014 / Este estudo teve como objetivo avaliar a resistência de união adesiva sob teste de microtração à dentina humana, comparando um sistema adesivo universal e suas diferentes técnicas de aplicação com um sistema adesivo convencional. Vinte terceiros molares foram divididos aleatoriamente em 4 grupos, variando o sistema adesivo e a técnica de acordo com o fabricante, seguido da reconstrução da porção coronal com resina composta Filtek Z350: G1- Adper Single Bond, com condicionamento ácido; G2- Single Bond Universal, modo autocondicionante; G3- Single Bond Universal, modo condicionamento ácido (dentina úmida); G4-Single Bond Universal, modo condicionamento ácido (dentina ressecada). Para a análise estatística dos dados, foi empregada análise de variância (Anova) (p=0,05). As comparações individuais foram realizadas com teste de diferença significativa de Tukey (HSD) (p=0,05). Os resultados revelaram que não houve diferenças estatísticas entre os grupos avaliados em relação aos valores de microtração. Pode-se concluir que o adesivo Single Bond Universal apresentou resultados estatisticamente semelhantes ao adesivo Adper Single Bond, independentemente do modo utilizado.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015. / Made available in DSpace on 2015-09-15T04:08:55Z (GMT). No. of bitstreams: 1 334082.pdf: 92171527 bytes, checksum: b6b890346747e7db61aa0b01bb699dc0 (MD5) Previous issue date: 2015 / Este estudo in vitro avaliou o comportamento de materiais restauradores resinosos de diferentes composições frente a degradação química e mecânica, a influência do tempo de espera para escovação após os desafios e o potencial erosivo das soluções utilizadas. Quarenta amostras foram confeccionadas para cada uma das resinas e, aleatoriamente, divididas entre 5 grupos de acordo com o tratamento recebido: imersão em saliva artificial; imersão em ácido hidroclorídrico seguido de abrasão (imediata e tardia); imersão em Coca-Cola seguido de abrasão (imediata e tardia). As amostras foram imersas nas soluções por 2 min, seguido do desafio abrasivo imediato (5 min depois) ou tardio (60 min depois) por um período de 2 min. Este ciclo se repetiu 3 vezes ao dia para cada amostra. As amostras foram mantidas em saliva artificial entre os ciclos erosivos. A rugosidade superficial foi mensurada através da utilização de um perfilômetro de contato. Uma amostra de cada resina composta foi aleatoriamente selecionada entre todos os grupos para análise em MEV. Os dados foram analisados através dos testes de Kruskal-Wallis, Pos-Hoc Dunn-Bonferroni e Wilcoxon. Considerando as soluções de imersão e os tempos entre erosão e escovação, nenhuma diferença estatística significativa foi encontrada (p>0,05). Não houve diferença na rugosidade inicial e final para o grupo controle (p>0,05), entretanto, nos grupos teste, houve um aumento da rugosidade superficial ao final dos desafios. O maior valor de rugosidade foi para a resina Charisma e o menor para Filtek Z350. Concluiu-se que, a composição das resinas influencia na rugosidade superficial pós degradação química e mecânica, independente da solução e do tempo de espera para escovação.

FRANCO, Juliana de Melo. Avaliação da eficácia do LED na fotoativação de diferentes resinas compostas. 2007. 78 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2007. / Submitted by denise santos (denise.santos@ufc.br) on 2011-12-14T12:29:44Z No. of bitstreams: 1 2007_dis_jmfranco.pdf: 607134 bytes, checksum: 8cd824f7e1c0190b10ac08822b778924 (MD5) / Approved for entry into archive by Eliene Nascimento(elienegvn@hotmail.com) on 2012-02-01T12:51:50Z (GMT) No. of bitstreams: 1 2007_dis_jmfranco.pdf: 607134 bytes, checksum: 8cd824f7e1c0190b10ac08822b778924 (MD5) / Made available in DSpace on 2012-02-01T12:51:50Z (GMT). No. of bitstreams: 1 2007_dis_jmfranco.pdf: 607134 bytes, checksum: 8cd824f7e1c0190b10ac08822b778924 (MD5) Previous issue date: 2007 / The aim of this study was to evaluate, in vitro, the efficiency of the light-curing unit LED Elipar Freelight 2 (3M ESPE) on the light-curing composites resin Filtek® Z350, Z100® e Filtek® P60 (3M ESPE), using the halogen lamp (Ultralux – Dabi Atlante) as a control. The degree of conversion of the used resin was achieved through FT-Raman spectroscopy and through microhardness test Vickers. A cilidrical aluminum mold with diameter of 5mm and a depth of 10mm was used to build the samples, which were photoactivated only once for 40s (LH) and 20s (LED) and submitted to the scrap method, according to ISO 4049:2000. Three samples were built for each group (n=3). The samples were introduced to the epoxy resine and polished with a sequence of different grades of sandpaper to be able to the microhardness test Vickers. The test was done in 48 hours (imediate) and 6 days (mediate), after the photactivation the samples were kept in an ambient temperature and lack of light. Five indentations were made in the centre and the edge of the sample, from the top to the bottom loaded with 490,3mN for 15s. The direct analysis of the degree of conversion was done with a FT-Raman spectroscopy (Bruker, model RFS 100/S, pumped by a laser Nd:YAG in 1064nm) compared with relative intensities between C=C aromatic (1610cm-1) and C=C methacrylate (1640cm-1) on the surfaces of the top and bottom of the sample. The statistic analisys tests (ANOVA, Student-Newman-Keuls, t–Student and Bonferroni) was done to determinate the possible differences, considering the factors: resin, light source, evaluation moment and surface. Comparing the intragroup (LED x LH) of microhardness Vickers in 48h, only Group 2 (Z100) showed statistics difference with a higher ammount of hardness of the LH (85,51Kg/mm2 ). In the 6 days evaluation, all the groups showed statistics difference, comparing intragroup between two light sources, which the highest ammount of microhardness (94,39Kg/mm2) was from Group 2 (Z100) when LH was applied. There was not statistics differences of the ammount of microhardness of the surfaces on the top and on the bottom, in groups 2 (Z100) e 3 (P60) when LED was applied. The ammounts of the degree of conversion of the top surface were statistically different of the bottom surfaces. All of the studied groups, although, didn´t show statistics diference between the bottom surfaces. There was not statistics difference about the degree of conversion of the groups, between the two light sources. Although, Group I (Z350) showed the lower degree of conversion (53,30Kg/mm2) on the top surface, when LH was applied comparing to the Group II (Z100) e III (P60). Based on these results, it is concluded that the increments of the composite resin of until 2.4mm of thickness is ideal to obtain ammounts of suitable microhardness in all the composites resin analysed; and the LED Elipar Freelight 2 is an alternative light source wich substitutes the halogen lamp, able to produce suitable degree of conversion in different composites resin. / O objetivo deste trabalho foi avaliar in vitro a eficácia do aparelho fotoativador LED Elipar Freelight 2 (3M ESPE) na fotoativação das resinas compostas Filtek® Z350, Z100® e Filtek® P60 (3M ESPE), empregando a luz halógena (Ultralux – Dabi Atlante) como controle. O grau de conversão das resinas utilizadas foi obtido por meio da espectroscopia FT-Raman e por testes de microdureza Vickers. Uma matriz metálica com orifício central de 5mm de diâmetro e 10mm de profundidade foi utilizada para confecção dos espécimes, os quais foram fotoativados uma única vez por 40s (LH) e 20s (LED) e submetidos ao método da raspagem, conforme ISO 4049:2000. Três corpos-de-prova foram confeccionados para cada grupo (n=3). Para realização da microdureza Vickers, os espécimes foram embutidos em resina epóxica e submetidos a um polimento seqüencial com lixas de granulações diferentes. O ensaio de microdureza foi realizado com 48 horas (imediato) e 6 dias (mediato) após a fotoativação e os espécimes armazenados a temperatura ambiente e ao abrigo da luz. Cinco indentações foram realizadas no centro e na periferia do corpo de prova, da superfície de topo para a base, com uma carga de 490,3mN por 15s. A análise direta do grau de conversão foi realizada com um espectrofotômetro FT-Raman (Bruker, modelo RFS 100/S, excitado com um laser Nd:YAG em 1064nm) por meio da comparação das intensidades relativas entre C=C aromática (1610cm-1) e C=C alifática (1640cm-1) nas superfícies de topo e base dos corpos-de-prova. A análise estatística (ANOVA, testes Student-Newman-Keuls, t–Student e Bonferroni) foi realizada para determinar as possíveis diferenças em função dos fatores resina, fonte de luz, momento da avaliação e superfície analisada. Na comparação intragrupo (LED x LH) da microdureza Vickers em 48h, somente o Grupo 2 (Z100) apresentou diferença estatística com maior valor de dureza para a LH (85,51Kg/mm2). Na avaliação de 6 dias, todos os grupos apresentaram diferença estatística na comparação intragrupo entre as duas fontes de luz, cujo maior valor de dureza (94,39Kg/mm2) foi do Grupo 2 (Z100) quando a LH foi empregada. Não houve diferença estatística nos valores de microdureza das superfícies de topo e base, nos Grupos 2 (Z100) e 3 (P60), quando o LED foi empregado. Os valores do grau de conversão da superfície de topo foram estatisticamente diferentes dos da base. Porém, todos os grupos estudados não apresentaram diferença estatística entre as superfícies base. Na comparação entre as duas fontes de luz, não houve diferença estatística quanto ao grau de conversão entre os grupos. Entretanto, o Grupo I (Z350) apresentou o menor grau de conversão (53,30 Kg/mm2 ) na superfície de topo, quando a LH foi empregada em relação aos Grupos II (Z100) e III (P60). Com base nesses resultados, conclui-se que incrementos de resina composta de até 2,4 mm de espessura são ideais para se obter valores de microdureza adequados em todas as resinas compostas estudadas; e o LED Elipar Freelight 2 é uma fonte de luz alternativa à luz halógena capaz de promover adequado grau de conversão de variadas resinas compostas.

A rotomoldagem é a forma de transformação do polietileno que mais cresce no Brasil e por ser relativamente nova, ainda tem muito para se desenvolver tecnicamente. Esse processo é capaz de produzir peças ocas de grandes dimensões e formas que são inviáveis por processos como sopro, injeção, entre outros. Os moldes e as máquinas estão avançando no sentido de melhor qualidade de acabamento, fechamento, controle do processo, eficiência nos fornos, novas técnicas de resfriamento etc. Com isso, os fabricantes de resina precisam acompanhar a evolução e projetar resinas com características que atendam plenamente os crescentes requisitos por ciclos mais rápidos, menor empenamento, acabamento superficial e propriedades mecânicas da peça final. O polietileno (PE) figura como a principal matéria-prima empregada na rotomoldagem (~90%). Devido à relevância do PE nessa aplicação, é de fundamental importância o conhecimento da relação entre a sua estrutura e o desempenho no ciclo de processamento, que é basicamente dividido em quatro etapas: carregamento, aquecimento, resfriamento e desmoldagem. A sinterização ocorre dentro da etapa de aquecimento, onde se dá a formação da peça e, consequentemente, é determinante no tempo de ciclo de processamento, bem como nas propriedades mecânicas que a peça pode alcançar. A proposta deste trabalho foi correlacionar a estrutura do polietileno com o seu desempenho na sinterização, através da comparação entre três resinas de PE que deveriam apresentar desempenho semelhante visto que possuem propriedades básicas (Índice de fluidez e densidade) similares. Outro objetivo foi o desenvolvimento de um método para medir o processo de sinterização e prever o comportamento prático das resinas. Os resultados mostraram que este método apresenta boa correlação com resultados práticos. Em relação às questões estruturais, a distribuição de comonômero homogeneamente ao longo das cadeias de diferentes tamanhos mostrou-se como fator determinante no desempenho de sinterização. A mesma impacta na cristalinidade e consequentemente reduz a temperatura de fusão, possibilitando que a sinterização inicie em temperatura menor. Além disso, observa-se também uma relação com o módulo de relaxação, também afetado pela distribuição de comonômero. / The rotational molding is the polyethylene processing with the biggest growth rate in Brazil and due to its youth, has a lot to be technically developed. This processing is capable to produce big hollow parts with shapes unviable by processing like blown molding, injection molding, and others. Molds and machines are advancing in the direction of better finishing quality, joints, process control, oven efficiency, new cooling techniques etc... With it, resin producers have to follow this evolution and design resins that fully meet growing requirements for faster cycle times, less warpage, finishing and mechanical properties of the final part. Polyethylene (PE) represents the main raw material used for rotational molding (~90%). Due to this PE relevance, it is of fundamental importance the knowledge of the relation between its structure and the performance in the processing cycle, that is basically divided in four steps: charging, heating, cooling and demolding. Sintering happens within heating step, where the part is formed, and consequently are determinant for the cycle time, as well as the mechanical properties that the final part can achieve. The proposal of this work was correlate the structure of PE with its performance on sintering, throw the comparison of three PE resins that should present similar behavior considering its basic properties (melt flow rate and density). Another objective was the development of method to measure and predict practical performance of the resins. Results showed that the developed method presents good relation with practical results. Regarding structural matters, the homogeneity of comonomer distribution along different chain sizes has shown itself to be a determinant factor in the sintering performance. It impacts crystallinity and consequently reduces melting temperature, allowing the sintering to start at lower temperatures. Besides that, its seen a relation with the relaxation modulus, that is impacted by the comonomer distribution too.

Trabajo de Investigación Requisito para optar al Título de Cirujano Dentista / El objetivo de este estudio fue determinar si existen diferencias estadísticamente significativas en los valores de adhesión, medidos a través de la resistencia al cizallamiento, al reparar un sustrato de resina compuesta de nanotecnología con tres tipos de composite. Los grupos experimentales estuvieron formados por 75 cilindros de RC de nanotecnología que fueron madurados en agua destilada a 37ºC por 24 horas. La superficie a reparar fue asperizada con un disco abrasivo, grabada con ácido fosfórico, silanizada y tratada con adhesivo. Sobre esta superficie se adherieron nuevos cilindros de RC microhíbrida, de micropartículas y de nanotecnología. Los grupos control estuvieron constituídos por 75 cilindros de RC de nanotecnología, sobre los cuales se adhirieron inmediatamente nuevos cilindros de los mismos tres tipos de composite. Luego todas las muestras fueron maduradas en agua destilada a 37ºC por 24 horas y se incluyeron en acrílico de autopolimerización. La prueba de resistencia al cizallamiento se realizó en una máquina de Ensayo Universal Instron y los resultados obtenidos fueron analizados estadísticamente. Se encontraron diferencias estadísticamente significativas al reparar un sustrato de RC de nanotecnología con composites de distinto tipo de relleno. La mayor resistencia se obtuvo al reparar con un material de nanotecnología y los menores valores al hacerlo con uno de micropartículas. 64 El tipo de RC influye en la Adhesión que se obtiene en la reparación de RC de nanotecnología.

Submitted by Edileide Reis (leyde-landy@hotmail.com) on 2015-04-15T02:42:59Z No. of bitstreams: 1 MATHEUS RIBEIRO GUERRA.pdf: 807469 bytes, checksum: 8ed4d1e53b540383a2ac166cf918bf26 (MD5) / Made available in DSpace on 2015-04-15T02:42:59Z (GMT). No. of bitstreams: 1 MATHEUS RIBEIRO GUERRA.pdf: 807469 bytes, checksum: 8ed4d1e53b540383a2ac166cf918bf26 (MD5) Previous issue date: 2013 / As evoluções constantes sofridas pelos materiais dentários ocorrem como resultado da busca pelo chamado “material ideal”. O desenvolvimento de um material não termina na finalização da sua composição pelo fabricante, e sim, após este ter sido submetido a diversas condições que simulem a sua futura aplicabilidade clínica. É importante identificar um material que forneça propriedades semelhantes às estruturas dentárias que serão substituídas e que promova longevidade ao procedimento restaurador. Este trabalho teve como objetivo revisar a literatura acerca dos testes utilizados para avaliação das propriedades físicas das resinas compostas. Testes como abrasão, polimento, rugosidade, contração volumétrica e os diversos ensaios de resistência são indispensáveis ao estudo dos materiais dentários e estes, somados, sugerem a sua eficiência clínica. Uma das maiores dificuldades em testes ou ensaios de um modo geral está na construção de uma metodologia para que seja possível a difusão da confiabilidade do estudo e que permita sua reprodução. A escolha de um material, ou mesmo de uma técnica associada a ele, pode ser facilitada pela divulgação das propriedades necessárias para que este seja compatível mecânica, biológica e esteticamente, e que, principalmente, facilite a sua aplicação na clínica diária. Diante desta revisão de literatura os testes mais frequentemente utilizados para avaliação das propriedades físicas são a resistência flexional, resistência à fratura, resistência à compressão, microdureza e rugosidade superficial. Importante ressaltar que não é possível correlacionar diretamente os resultados in vitro com a aplicabilidade clínica.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015. / Made available in DSpace on 2016-04-19T04:21:15Z (GMT). No. of bitstreams: 1 338273.pdf: 1080261 bytes, checksum: acf293b5b565486ac04c1be84e427afb (MD5) Previous issue date: 2015 / Objetivos: Avaliar a fluência por microindentação de materiais restauradores à base de polímeros como, resina composta para uso direto e resina composta para uso indireto. Material e Método: Discos de resinas compostas foram confeccionados em uma matriz metálica, de forma circular com 1mm de altura e 16mm de diâmetro. Estes espécimes foram divididos em quatro grupos de acordo com o material utilizado: Grupo I ( Empress Direct, Esmalte A2); Grupo II (Filtek Z350 XT, Esmalte A2); Grupo III (Signum Ceramis, Esmalte A2); Grupo IV (SR Adoro, A2) e subdivididos em dois grupos (n=20) de acordo com a armazenagem e controle de umidade, temperatura e tempo: SG I: armazenagem em água destilada 23oC; SG II: armazenagem à seco 23oC, controlado por ar-condicionado; Os períodos de avaliação foram após 24h, 1, 3, e 6 meses de armazenagem. Após o polimento, a lisura, a planificação e o paralelismo entre as superfícies dos discos de resinas compostas foram analisados, para garantir a planificação e o paralelismo entre as faces superior e inferior do disco de resina composta, foram levados ao microdurômetro e submetidos ao teste de fluência em um microdurômetro HMV-2, Micro Hardness Tester, (Shimadzu). Foram realizadas duas endentações, uma inicial e outra final. A carga de endentação utilizada foi de 100gf. O tempo de cada endentação foi 30s e o tempo de relaxação entre cada endentação também de 30s. Os períodos de avaliação foram 24h, 1 mês, 3 meses e 6 meses após a confecção dos espécimes. Para cada espécime foi realizado cinco leituras, uma no centro e em cada quadrante do disco, e então realizada uma média entre esse valores. Resultados; As resinas compostas indiretas apresentarem menos valores de deformação por fluência que as resinas compostas diretas, sendo que todas apresentaram deformação permanente maior quando armezenadas em água e por período de 6 meses., diminuindo a cada período. Conclusão: As resinas compostas indiretas são mais resistentes à fluência que as resinas compostas diretas, a armazenagem em água diminui a resistência de todos os materiais aqui testados, assim como o tempo de armazenagem.<br> / Abstract : Objectiv: Evaluate fluency by microindentação of restorative materials to the polymer base as composite resin for direct use and indirect composite resin for use. Methods: composite resin discs were prepared using a metal matrix, circular in shape with 1 mm high and 16mm in diameter. These specimens were divided into four groups according to the material used: Group I (Empress Direct Enamel A2); Group II (Filtek Z350 XT, Enamel A2); Group III (Signum Ceramis, Enamel A2); Group IV (SR Love, A2) and subdivided into two groups (n = 20) in accordance with the storage and humidity control, temperature and time: I GS: storing in distilled water 23 ° C; SG II: dry storage at 23 ° C, controlled air conditioning; The evaluation periods were after 24 hours, 1, 3, and 6 months of storage. After polishing, the smoothness, the planning and the parallelism between the surfaces of the composite resin discs were analyzed to ensure the planning and the parallelism between the upper and lower faces of the composite disc were taken and subjected to the test microhardness fluency in a HMV-2 microdurometer, Micro Hardness Tester (Shimadzu). Two indentations, initial and another final were held. The indentation load was 100gf used. The time of each indentation was 30s and the relaxation time between each indentation also 30s. The evaluation periods were 24, 1 month, 3 months and 6 months after the making of the specimens. For each specimen was performed five readings, one in the center and in each quadrant of the disc, and then held an average of these values. Results; The indirect composite resins exhibiting less creep strain values that direct composites, which all showed higher permanent deformation when armezenadas in water and for a period of 6 months., Decreasing each period. Conclusion: The indirect composite resins are more resistant to creep than the direct composites, storage decreases in water resistance of all materials tested here, as well as the storage time.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências Físicas e Matemáticas. Programa de Pós-Graduação em Química. / Made available in DSpace on 2012-10-20T22:23:19Z (GMT). No. of bitstreams: 1 201623.pdf: 8238389 bytes, checksum: fc85bfbfa9cb140e108839033f6a3d73 (MD5) / Pseudo-redes poliméricas interpenetradas (pseudo-RPIs) foram sintetizadas a partir de resina epóxi, N´, N´ - tetraglicidil - 4,4' - difenil diamina metano, TGDDM, (Araldite, MY - 720), e estireno (S), metacrilato de metila (MMA), acrilato de t-butila (tBA), respectivamente. As sínteses foram realizadas simultaneamente ou seqüencialmente usando como agente de ligação cruzada etilenodiamina, EDA ou trietilenotetramina, TETA e como iniciador, peróxido de benzoíla. A estrutura da resina TGDDM foi confirmada por espectroscopia no infravermelho, análise elementar e espectroscopia de ressonância magnética nuclear (RMN).

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia / Made available in DSpace on 2012-10-21T07:42:12Z (GMT). No. of bitstreams: 1 199925.pdf: 2459501 bytes, checksum: be708c7710f0bccb1f2b20cc84990569 (MD5) / Esta pesquisa avaliou o efeito da unidade de fotoativação (halógena ou Led) no selamento marginal de restaurações de resina composta. Quarenta cavidades de Classe V foram restauradas e aleatoriamente divididas em 4 grupos de acordo com a unidade de fotoativação utilizada (n=10): G1- Optilux 501; G2- Elipar Freelight; G3- Ultra Lume LED 2; G4- L.E.Demetron I. Os espécimes foram então submetidos ao teste de microinfiltração. Não foram observadas diferenças estatísticas entre os grupos tanto para as margens em esmalte (p=0,8806) como para as margens em dentina (p=0,2764). Concluiu-se que a variação da unidade de fotoativação não resultou em diferenças com relação ao selamento marginal de restaurações de Classe V com resina composta.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia. / Made available in DSpace on 2012-10-20T07:55:12Z (GMT). No. of bitstreams: 1 187112.pdf: 388096 bytes, checksum: a36d9533d23dfd65aff908752259e2a3 (MD5) / O objetivo deste estudo foi avaliar a prevalência de contatos abertos em restaurações proximais de resina composta e amálgama executados por dentistas e estudantes de odontologia. Foram examinados pacientes adultos (homens e mulheres) entre 20 e 80 anos de idade, totalizando uma amostra de 200 pacientes (sendo 100 em consultórios particulares e 100 em faculdades). Dentes permanentes posteriores, pré-molares e molares de todos os hemiarcos foram examinados. Para a avaliação dos contatos abertos, fez-se uso de fio dental sem cera, e o contato era considerado aberto quando não fosse encontrado resistência com o uso do mesmo. O total de contatos entre restaurações examinados foi de 792, sendo 339 em consultórios particulares e 453 em faculdades. O total de contatos abertos encontrados foi de 22, sendo 16 em consultórios particulares e 6 em faculdades. Os contatos abertos mais encontrados estavam localizados entre os segundos pré-molares e molares na maxila (36,36%) e entre o primeiro e o segundo molares na mandíbula (27,27%), estando estes contatos abertos localizados entre amálgama e dente hígido (p<0,05).