Mechanical pulps are used in paper products such as magazine or news grade printing papers or paperboard. Mechanical pulping gives a high yield; nearly everything in the tree except the bark is used in the paper. This means that mechanical pulping consumes much less wood than chemical pulping, especially to produce a unit area of printing surface. A drawback of mechanical pulp production is the high amounts of electrical energy needed to separate and refine the fibers to a given fiber quality. Mechanical pulps are often produced from slow growing spruce trees of forests in the northern hemisphere resulting in long, slender fibers that are well suited for mechanical pulp products. These fibers have large varieties in geometry, mainly wall thickness and width, depending on seasonal variations and growth conditions. Earlywood fibers typically have thin walls and latewood fibers thick. The background to this study was that a more detailed fiber characterization involving evaluations of distributions of fiber characteristics, may give improved possibilities to optimize the mechanical pulping process and thereby reduce the total electric energy needed to reach a given quality of the pulp and final product. This would result in improved competitiveness as well as less environmental impact. This study evaluated the relation between fiber characteristics in three types of mechanical pulps made from Norway spruce (Picea abies), thermomechanical pulp(TMP), stone groundwood pulp (SGW) and chemithermomechanical pulp (CTMP). In addition, the influence of fibers from these pulp types on sheet characteristics, mainly tensile index, was studied. A comparatively rapid method was presented on how to evaluate the propensity of each fiber to form sheets of high tensile index, by the use of raw data from a commercially available fiber analyzer (FiberLabTM). The developed method gives novel opportunities of evaluating the effect on the fibers of each stage in the mechanical pulping process and has a potential to be applied also on‐line to steer the refining and pulping process by the characteristics of the final pulp and the quality of the final paper. The long fiber fraction is important for the properties of the whole pulp. It was found that fiber wall thickness and external fibrillation were the fibercharacteristics that contributed the most to tensile index of the long fiber fractions in five mechanical pulps (three TMPs, one SGW, one CTMP). The tensile index of handsheets of the long fiber fractions could be predicted by linear regressions using a combination of fiber wall thickness and degree of external fibrillation. The predicted tensile index was denoted BIN, short for Bonding ability INfluence. This resulted in the same linear correlation between BIN and tensile index for 52 samples of the five mechanical pulps studied, each fractionated into five streams(plus feed) in full size hydrocyclones. The Bauer McNett P16/R30 (passed 16 meshwire, retained on a 30 mesh wire) and P30/R50 fractions of each stream were used for the evaluation. The fibers of the SGW had thicker walls and a higher degree of external fibrillation than the TMPs and CTMP, which resulted in a correlation between BIN and tensile index on a different level for the P30/R50 fraction of SGW than the other pulp samples. A BIN model based on averages weighted by each fiber´s wall volume instead of arithmetic averages, took the fiber wall thickness of the SGW into account, and gave one uniform correlation between BIN and tensile index for all pulp samples (12 samples for constructing the model, 46 for validatingit). If the BIN model is used for predicting averages of the tensile index of a sheet, a model based on wall volume weighted data is recommended. To be able to produce BIN distributions where the influence of the length or wall volume of each fiber is taken into account, the BIN model is currently based on arithmetic averages of fiber wall thickness and fibrillation. Fiber width used as a single factor reduced the accuracy of the BIN model. Wall volume weighted averages of fiber width also resulted in a completely changed ranking of the five hydrocyclone streams compared to arithmetic, for two of thefive pulps. This was not seen when fiber width was combined with fiber wallthickness into the factor “collapse resistance index”. In order to avoid too high influence of fiber wall thickness and until the influence of fiber width on BIN and the measurement of fiber width is further evaluated, it is recommended to use length weighted or arithmetic distributions of BIN and other fiber characteristics. A comparably fast method to evaluate the distribution of fiber wall thickness and degree of external fibrillation with high resolution showed that the fiber wallthickness of the latewood fibers was reduced by increasing the refining energy in adouble disc refiner operated at four levels of specific energy input in a commercial TMP production line. This was expected but could not be seen by the use of average values, it was concluded that fiber characteristics in many cases should be evaluated as distributions and not only as averages. BIN distributions of various types of mechanical pulps from Norway spruce showed results that were expected based on knowledge of the particular pulps and processes. Measurements of mixtures of a news‐ and a SC (super calendered) gradeTMP, showed a gradual increase in high‐BIN fibers with higher amounts of SCgrade TMP. The BIN distributions also revealed differences between the pulps that were not seen from average fiber values, for example that the shape of the BINdistributions was similar for two pulps that originated from conical disc refiners, a news grade TMP and the board grade CTMP, although the distributions were on different BIN levels. The SC grade TMP and the SC grade SGW had similar levels of tensile index, but the SGW contained some fibers of very low BIN values which may influence the characteristics of the final paper, for example strength, surface and structure. This shows that the BIN model has the potential of being applied on either the whole or parts of a papermaking process based on mechanical or chemimechanical pulping; the evaluation of distributions of fiber characteristics can contribute to increased knowledge about the process and opportunities to optimize it.

The wall thickness of pulp fibers plays a major role in the paper industry, but it is currently not possible to measure this property without manual laboratory work. In 2007, researcher Ho Fan Jang patented a technique to automatically measure fiber wall thickness, combining the unique optical properties of pulp fibers with image analysis. In short, the method creates images through the use of an optical system resulting in color values which demonstrate the retardation of a particular wave length instead of the intensity. A device based on this patent has since been developed by Eurocon Analyzer. This thesis investigates the software aspects of this technique, using sample images generated by the Eurocon Analyzer prototype. The software developed in this thesis has been subdivided into three groups for independent consideration. First being the problem of solving wall thickness for colors in the images. Secondly, the image analysis process of identifying fibers and good points for measuring them. Lastly, it is investigated how statistical analysis can be applied to improve results and derive other useful properties such as fiber coarseness. With the use of this technique there are several problems which need to be overcome. One such problem is that it may be difficult to disambiguate the colors produced by fibers of different thickness. This complication may be reduced by using image analysis and statistical analysis. Another challenge can be that theoretical values often differ greatly from the observed values which makes the computational aspect of the method problematic. The results of this thesis show that the effects of these problems can be greatly reduced and that the method offers promising results. The results clearly distinguish between and show the expected characteristics of different pulp samples, but more qualitative reference measurements are needed in order to draw conclusions on the correctness of the results.

Pulmonary TNFa concentration and wall thickness after on- versus off pump cardiac surgery

’African Bamboo PLC’ has the vision to become the first and the leading bamboo-based floorboard producer in Africa with export markets in Europe and America. African alpine bamboo (Yushania alpina), common in the highlands of Ethiopia, was used to develop woven strand board (WSB) products. Research on thermal modification was part of the product development. Samples were mainly collected in Tetechia (6°33‘ 34‘‘ N 38°32‘25‘‘ W, 2,650-2,700 m a.s.l.), located in the Sidama region. Three culms each of two, three, four and five years of age were harvested. Samples were taken from the middle of each internode to determine the moisture content and density. Samples used to assess the effects of thermal modification were cut next to them. Further test specimens from different areas and other species such as the lowland bamboo (Oxytenanthera abyssinica) were also investigated. The thermal treatment was applied in a kiln with steam as an inert blanket to reduce oxidative processes. Eight modifications were performed at temperatures of 160 °C, 180 °C, 200 °C and 220 °C, at durations of three or five hours each. Mass loss, sorption behaviour, impact resistance, resistance to indentation and contents of chemical components were analysed for the modified and unmodified samples. Yushania alpina is a thin-walled bamboo with a maximum diameter of 6 cm, moisture content of up to 150 % and densities of between 0.5 g/cm² and 0.8 g/cm². Moisture content, diameter and wall thickness decreased from the bottom to the top of the culms, whereas density increased. Two year old bamboo had the lowest and three year the highest density. The mass loss followed an exponential trend, with about 2 % loss at 160 °C and 16 % at 220 °C. This mainly reflected the degradation of hemicellulose, which was fully removed at 220 °C. Extractive contents, at less than 5 %, fluctuated. Lignin amounted to 30 % and increased appreciably. Cellulose reached contents of about 45 % and decreased slightly at high temperatures. The chemical change, which was based more on the temperature than on the duration of treatment, influenced the sorption behaviour and mechanical properties most of all. The equilibrium moisture content was reduced by between 10 % to 40 %, depending on the climate and modification temperature chosen. This reduction stabilised between temperatures of 200 °C and 220 °C. The impact resistance of untreated bamboo was 3.8 J/cm², compared to only 1.4 J/cm² for modified samples. Resistance also differed between samples from the outer and inner part of the culm in the transverse section. The resistance to indentation declined also. Unmodified samples had 47 N/mm², compared to only 20 N/mm² for strongly modified samples. The results of the analysis and the experience gained indicate that temperatures between 180 °C and 200 °C, held for three hours, lead to the best results for woven strand board production using Ethiopian highland bamboo. / ’African Bamboo PLC’ setzt sich zum Ziel, als erstes Unternehmen Holzwerkstoffe aus Bambus nach Europa und Amerika zu exportieren. Afrikanischer Hochgebirgsbambus (Yushania alpina), welcher vor allem im Hochland von Äthiopien vorkommt, wurde dazu verwendet ”woven strand boards” (WSB) zu entwickeln. Untersuchungen zur thermischen Modifizierung waren dabei Bestandteil der Produktentwicklung. Die dafür notwendigen Bambusproben wurden hauptsächlich in Tetechia (6°33‘34‘‘ N 38°32‘25‘‘ W, 2650-2700 m ü. NN), einem Dorf in Sidama, entnommen. Es wurden dazu je drei Bambushalme der Altersklassen zwei, drei, vier und fünf Jahre geerntet. Proben für die Bestimmung von Holzfeuchte und Dichte wurden in der Mitte jedes Internodiums entnommen. Diese spielten als Referenzprobe eine große Rolle. Neben den Referenzprobekörpern wurden die jeweiligen Stücke für die thermische Behandlung heraus gesägt, wobei dies nach einer bestimmten Systematik erfolgte. Neben den Proben aus Tetechia wurden für die Untersuchungen zudem Proben aus anderen Gebieten und von einer anderen Art, dem Tieflandbambus (Oxytenanthera abyssinica), hinzugefügt. Die thermische Modifizierung erfolgte unter Wasserdampf, welcher oxidative Prozesse verhinderte. Insgesamt erfolgten acht Modifizierungen bei Temperaturen von 160 °C, 180 °C, 200 °C und 220 °C und einer jeweiligen Haltezeit von drei oder fünf Stunden. In Anbetracht der unbehandelten und behandelten Proben wurden der Masseverlust, die Bruchschlagarbeit, der Eindruckswiderstand und die chemische Zusammensetzung analysiert. Yushania alpina ist ein dünnwandiger Bambus mit Durchmessern bis zu 6 cm, Holzfeuchten bis 150 % und Dichten zwischen 0,5 g/cm² und 0,8 g/cm². Holzfeuchte, Durchmesser und Wandstärke verringerten sich mit der Halmhöhe, wobei die Dichte hingegen anstieg. Zweijähriger Bambus hatte die geringsten und dreijähriger Bambus die höchsten Dichten. Der Masseverlust folgte einem expontiellem Verlauf mit Werten von 2 % bei 160 °C und 16 % bei 220 °C. Er widerspiegelte den Abbau der Hemicellulose, welche bei 220 °C schon nicht mehr vorhanden war. Exktraktgehalte fluktuierten mit Werten unter 5 %. Der Ligningehalt lag bei ungefähr 30 % und stieg merklich an. Der Cellulosegehalt erreichte Werte von etwa 45 %, wobei die Cellulose bei höheren Temperaturen leicht abgebaut wurde. Die chemischen Veränderungen, welche maßgeblich von der angewandten Temperatur statt der Behandlungsdauer beeinflusst wurden, wirkten sich auf das Sorptionsverhalten und mechanische Eigenschaften aus. Je nach ausgesetztem Klima und erfolgter Modifikation wurde die Ausgleichsfeuchte der Proben um 10 % bis 40 % reduziert. Die Abnahme der Ausgleichsfeuchte stabilisierte sich im Temperaturbereich von 200 °C bis 220 °C. Die Bruchschlagarbeit des unbehandelten Bambus betrug 3,8 J/cm², die des behandelten nur 1,4 J/cm². Die Bruchschlagarbeit variierte unabhängig von der Modifikation zwischen dem inneren und äußeren Abschnittes innerhalb des Halmquerschnitts. Der Eindruckswiderstand nahm mit der thermischen Behandlung ebenfalls ab. Unbehandelte Proben hatten 47 N/mm², während die modifizierten Proben nur noch 20 N/mm² aufwiesen. Anhand der Ergebnisse und erworbenen Erfahrungen lies sich schlussfolgern, dass Temperaturen zwischen 180 °C und 200 °C bei einer Haltezeit von drei Stunden für die thermische Modifizierung von Äthiopischem Hochlandbambus in Bezug auf die Entwicklung von ”woven strand boards” empfehlenswert waren.