Made available in DSpace on 2015-04-14T13:58:46Z (GMT). No. of bitstreams: 1 436434.pdf: 2324920 bytes, checksum: cdf79816569d7d9b352a5a2d9b93437f (MD5) Previous issue date: 2012-01-25 / The search for materials that can replace or restore damaged tissues is due to the search for better life quality of the population. Considering that cardiovascular diseases are the main causes of death in Brazil (Banco de Sa?de, 2010), needs some devices that have efficacy in cardiac regeneration, addressing about issues of long-term safety and promoting the healing of vascular vessels (PR Newswire, 2010). In this sense, this paper developed the synthesis of biostable polyurethanes from the reaction of polycaprolactone diol (PCL) with different diisocyanates (HDI and H12MDI), characterizing them by morphological analysis (MEV), thermal (TGA and DSC), mechanical (DMA) and structural (IV), but also evaluating their in vitro cytotoxicity, by testing for the evaluation of cell viability (MTT and VN test) and cell proliferation (Trypan Blue test) using NIH-3T3 fibroblast cells, comparing them with commercial materials, Dacron and PTFE. The obtained results showed that the synthesized polyurethanes had average molar weight (Mw) ranging between 30000 and 263000 g/mol, as well as a plasticity depended of polyol used. The mechanical behavior of polyurethanes showed similar or greater than the commercial material, Dacron and PTFE. The biostability tests showed that there was mass loss below 20% of the materials exposed to hydrolytic degradation in the period of 270 days and below 5% in the enzymatic degradation in the period of 30 days. The cell viability of polyurethanes was superior to 80%, considered non-cytotoxic. Polyurethanes in this study showed favorable results for its possible use as biomaterial in cardiac applications / A procura por materiais que possam substituir ou restaurar tecidos danificados deve-se ? busca por melhor qualidade de vida da popula??o. Levando em considera??o que doen?as cardiovasculares s?o as principais causas de mortes no Brasil (Banco de Sa?de, 2010), necessita-se de dispositivos que possuam efic?cia na regenera??o card?aca, abordando quest?es de seguran?a ? longo prazo e promovendo a cicatriza??o de vasos vasculares (PR Newswire, 2010). Neste sentido, o presente trabalho desenvolveu a s?ntese de poliuretanos bioest?veis a partir da rea??o de policaprolactona diol (PCL) com diferentes diisocianatos (HDI e H12MDI), caracterizando-os por meio de an?lise morfol?gica (MEV), t?rmica (TGA e DSC), mec?nica (DMA) e estrutural (IV), como tamb?m, avaliando sua citotoxicidade in vitro, atrav?s de testes para a avalia??o da viabilidade celular (teste VN e MTT) e prolifera??o celular (teste Azul de Tripan) utilizando c?lulas fibrobl?sticas NIH-3T3, comparando-os com materiais comerciais, Dacron e PTFE. Os resultados obtidos mostraram que os poliuretanos sintetizados apresentaram massa molar ponderal m?dia (Mw) variando entre 30000 e 263000 g/mol, bem como, uma plasticidade dependente do poliol utilizado. O comportamento mec?nico destes poliuretanos mostrou-se semelhante ou superior aos materiais comerciais, Dacron e PTFE. Os testes de bioestabilidade mostraram que houve perda de massa abaixo de 20% dos materiais expostos ? degrada??o hidrol?tica no periodo de 270 dias e abaixo de 5% na degrada??o enzim?tica no periodo de 30 dias. A viabilidade celular dos poliuretanos mostrou-se superior a 80%, consideradas n?o citot?xicas. Os poliuretanos avaliados neste estudo apresentaram resultados favor?veis para seu uso como biomaterial em poss?veis aplica??es cardiol?gicas

Made available in DSpace on 2015-04-14T13:59:04Z (GMT). No. of bitstreams: 1 454476.pdf: 17188672 bytes, checksum: b9bae5126e1fa699d075b37bc4ae70fa (MD5) Previous issue date: 2014-03-06 / Searches in nanotechnology allied to studies of biopolymers advances for application in the medical / pharmaceutical field. Micro / nanoparticles (NP) with biodegradable polymer systems are promising for the controlled release of drugs in the form of nanocapsules (NC) or nanospheres (NS), able to protect / release the substance gradually. This work aims to prepare NP polyurethane (Mw = 224,973 g/ mol and Mn = 134 670 g / mol) for the encapsulation by multiple emulsion of the pharmaco α-tocopherol (α-TOC) with and without a?ai oil and different stirring techniques (ultra-turrax (TR) and ultrasound (SM)), as well as the study of controlled release in physiological medium. The average sizes of the obtained NP were between 600 nm and 10 μm using the SM and between 2-15 μm using the TR and all presented spherical morphology and variables distributions depending on the presence or absence of a?ai oil. It was also possible to detect the presence of α-TOC and a?ai oil (when present) in all NP's, as well as the degradation of PU and release of α-TOC through the techniques of UV-Vis, IR and TGA. The encapsulation efficiency of α-TOC was moderate, ranging between 15-34% for NPs obtained by TR and between 18-44% for NPs obtained by SM, due to the affinity of the hydrophobic compound with the PU. The amount of α-TOC initially added in the formulations obtained high rates of recovery ranging from 93-96%. The NPs showed a mass loss of less than 4% when exposed to hydrolytic degradation up to 30 days. The ultraturrax samples without a?ai oil and ultrasound with a?ai oil showed increased release of α-TOC from the 12th day, whereas NP's ultra-turrax with a?ai oil and ultrasound without acai oil showed constant release up to day 30. The results indicate that the presence of oil using the MS showed more efficiency in the formation of NPs / Pesquisas em nanotecnologia aliada aos estudos dos biopol?meros possibilitaram avan?os para aplica??o na ?rea m?dica/farmac?utica. Sistemas de micro/nanopart?culas (NP) com pol?meros biodegrad?veis s?o promissores na libera??o controlada de f?rmacos na forma de nanoc?psulas (NC) ou de nanoesferas (NE), capaz de proteger/liberar a subst?ncia gradativamente. Este trabalho tem como objetivo preparar NP de poliuretano (PU- Mw= 224.973 g/mol e Mn=134.670 g/mol) para o encapsulamento por emuls?o m?ltipla do f?rmaco α-tocoferol (α-TOC) com e sem ?leo de a?a? e com diferentes t?cnicas de agita??o (ultra-turrax (TR) e ultrassom (SM) ), bem como, o estudo de libera??o controlada em meio fisiol?gico. Os tamanhos m?dios das NP obtidas foram entre 600nm e 10 μm utilizando o SM e entre 2-15 μm utilizando o TR e apresentaram morfologia esf?rica e distribui??es vari?veis em fun??o da presen?a ou n?o de ?leo de a?a?. Tamb?m foi poss?vel detectar a presen?a de α-TOC e ?leo de a?a? (quando presente) em todas as NP s, assim como a degrada??o do PU e libera??o do α-TOC atrav?s das t?cnicas de UVVis, TGA e IV. A efici?ncia de encapsulamento do α-TOC foi moderada, variando entre 15 a 34% para as NP s obtidas por TR e entre 18 a 44% para as NP s obtidas por SM, devido ? afinidade deste composto hidrof?bico pelo PU. A quantidade de α- TOC inicialmente adicionada nas formula??es obteve tamb?m elevadas taxas de recupera??o, variando entre 93-96%. As NP s apresentaram uma perda de massa abaixo de 4% quando expostos a degrada??o hidrol?tica at? 30 dias. As amostras TR S/?LEO e SM C/?LEO apresentaram libera??o crescente de α-TOC a partir do 12? dia, enquanto que as NP s TR C/?LEO e SM S/?LEO apresentaram libera??o constante ate 30? dia. Os resultados indicam que a presen?a de ?leo e utiliza??o de SM mostraram-se mais eficiente na forma??o das NP s.

Made available in DSpace on 2015-04-14T13:59:10Z (GMT). No. of bitstreams: 1 462026.pdf: 4874123 bytes, checksum: 1a15895448105e314b1f653aab8461a5 (MD5) Previous issue date: 2014-08-26 / The addition of inorganic fillers in polyurethane resins for use as coating has been of great technological interest because it leads to improvements in the properties and performance of existing materials, besides the possibility of reducing environmental impact and costs. In this context, this work presents the production of ternary composites with addition of commercial inorganics fillers, titanium dioxide (TiO2) and silica (SiO2), in aqueous polyurethane dispersions. These ternary composites were obtained from the addition of 1% of different combinations of proportion of fillers (TiO2: SiO2 = 0:100 25:75 50:50 75:25 to 100:0) in aqueous polyurethane dispersions (PUD) by the in situ polymerization process. The characteristics of the ternary composite were evaluated in the form of polymer dispersion (particle size, pH, viscosity and conductivity) and in the form of films (thermal, mechanical and morphological properties), as well as the study of degradation of these materials. The results show that the synergy resulting from the combination of the two fillers, SiO2 and TiO2, interferes with the formation of micelles in PUD colloidal system, changing the coalescence process in the formation of films and modifying light reflection and refraction in the composite making it opaque and matte. The presence of anatase crystalline phase in TiO2 particles provides better compatibility filler1-filler2-polymer increasing the tensile strength and thermal stability of the ternary composites. The presence of SiO2 retarded the degradation process in the soil of the ternary composites and they did not show biological material on the surface after degradation. / A adi??o de cargas inorg?nicas em resinas de poliuretano para aplica??o como revestimento tem tido grande interesse tecnol?gico, pois conduz a melhorias nas propriedades e no desempenho dos materiais j? existentes, al?m da possibilidade de redu??o de impacto ambiental e de custos. Neste contexto, este trabalho apresenta a produ??o de comp?sitos tern?rios com a adi??o de cargas inorg?nicas comerciais, di?xido de tit?nio (TiO2) e di?xido de sil?cio (SiO2), em dispers?es aquosas de poliuretano. Estes comp?sitos tern?rios foram obtidos a partir da adi??o de 1% de diferentes propor??es das cargas (TiO2:SiO2 = 0:100, 25:75, 50:50, 75:25 e 100:0) em dispers?es aquosas de poliuretano (DPU) pelo processo de polimeriza??o in situ. As caracter?sticas dos comp?sitos tern?rios foram avaliadas na forma de dispers?o polim?rica (tamanho de part?cula, pH, viscosidade e condutividade) e na forma de filmes (propriedades t?rmicas, mec?nicas e morfologia), bem como, o estudo de degrada??o destes materiais. Os resultados mostram que a sinergia resultante da combina??o das duas cargas, SiO2 e TiO2, interfere na forma??o das micelas no sistema coloidal DPU, alterando o processo de coalesc?ncia na forma??o dos filmes e modificando a reflex?o e a refra??o de luz no comp?sito deixando-o opaco e fosco. A presen?a da fase cristalina anatase nas part?culas de TiO2 propicia melhor compatibilidade carga1-carga2-pol?mero aumentando a resist?ncia a tra??o com altos percentuais de deforma??o e a estabilidade t?rmica dos comp?sitos tern?rios. A presen?a de SiO2 retardou o processo de degrada??o em solo dos comp?sitos tern?rios e estes n?o apresentaram material biol?gico na superf?cie depois da degrada??o.

Submitted by PPG Ci?ncias Criminais (ppgccrim@pucrs.br) on 2018-05-15T13:08:39Z No. of bitstreams: 1 Anna Tereza Santos.pdf: 1107028 bytes, checksum: 99b98f2f8d0bf3bfe2ba0523a3a5b3fb (MD5) / Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2018-05-21T11:48:39Z (GMT) No. of bitstreams: 1 Anna Tereza Santos.pdf: 1107028 bytes, checksum: 99b98f2f8d0bf3bfe2ba0523a3a5b3fb (MD5) / Made available in DSpace on 2018-05-21T11:59:29Z (GMT). No. of bitstreams: 1 Anna Tereza Santos.pdf: 1107028 bytes, checksum: 99b98f2f8d0bf3bfe2ba0523a3a5b3fb (MD5) Previous issue date: 2018-03-12 / The medicalization process has been growing over the years in modern society. In general, the concept of medicalization has been used in several studies to deal with a phenomenon that has traditionally had the general sense of reducing social and political problems in private and individual problems. This present aims to analyze the contemporary expressions of medicalization in adolescents in conflict with the law. Taking as a starting point the studies on the biopolitics of the population of Michel Foucault and the reflections of authors like Cristian Dunker and Vladmir Safatle on the expansion of diagnostic categories, these work seeks to understand how the medical and psychiatric discourses are being used by legal knowledge as instrument of normalization, arbitrary social control and management of adolescents who commit an infraction. / O processo de medicaliza??o tem sido uma crescente com o passar dos anos na sociedade moderna. De forma geral, o conceito de medicaliza??o aparece em diversos estudos para tratar de um fen?meno que teve, tradicionalmente, o sentido geral de reduzir problemas sociais e pol?ticos a problemas privados e individuais. O presente trabalho tem como objetivo analisar as express?es contempor?neas da medicaliza??o no ?mbito dos adolescentes em conflito com a lei. Tomando como ponto de partida os estudos sobre a biopol?tica da popula??o, de Michel Foucault, e as reflex?es de autores como Cristian Dunker e Vladmir Safatle sobre a expans?o das categorias diagn?sticas, este trabalho busca perceber como os discursos m?dicos e psiqui?tricos est?o sendo utilizados pelo saber jur?dico como instrumento de normaliza??o, controle social arbitr?rio e gest?o dos adolescentes autores de ato infracional.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2016-07-26T14:16:17Z No. of bitstreams: 1 DIS_MAURICIO_DA_SILVA_HOFFMANN_COMPLETO.pdf: 3702613 bytes, checksum: 3b0ef365d0e0899c33cdef47ae74d886 (MD5) / Made available in DSpace on 2016-07-26T14:16:17Z (GMT). No. of bitstreams: 1 DIS_MAURICIO_DA_SILVA_HOFFMANN_COMPLETO.pdf: 3702613 bytes, checksum: 3b0ef365d0e0899c33cdef47ae74d886 (MD5) Previous issue date: 2016-03-04 / Polyurethanes (PU) are widely used as biomaterials because it has good compatibility, and desirable mechanical properties and branched polyurethanes have shown besides these characteristics, an appreciable stability to hydrolytic and enzymatic degradation. Within this context, this study aimed to synthesize branched polyurethanes from the addition of pentaerythritol and evaluate its potential use as scaffolds in tissue engineering. Polycaprolactone diol (PCL) as polyol and pentaerythritol (PETT) in different amounts (5, 10 and 15% w/w relative to the polyol) as well as the hexamethylene diisocyanate (HDI) were used in the synthesis of the branched PU. These branched PU (PU-PETT) were evaluated for structural, morphological, mechanical, thermal and solubility in various organic solvents and compared to the linear PU (without PETT). Among the branched PU, PU-PETT 5% showed better morphological and tensile strength characteristics, so it was used to prepare membranes leached with the linear PU. The leached membranes were evaluated for their structural, morphological, mechanical, thermal properties, wettability, hydrolytic degradation, calcification and swelling degree. The leached membrane PU-PETT 5% showed high porosity and interconnectivity, greater thermal stability compared to linear PU leached membrane, despite the lower degree of crystallinity and molar weight. Also, the PU-PETT 5% membrane exhibited the ability of calcium phosphate biomineralization, good wettability, higher stability hydrolytic degradation and greater swelling as compared to linear PU membrane. Thus, it can be concluded that the membrane PU-PETT 5% exhibited characteristics suitable for use as biomaterials in tissue engineering. / Poliuretanos (PU) t?m sido amplamente utilizados como biomaterial por possuir boa compatibilidade e desej?veis propriedades mec?nicas e os poliuretanos ramificados tem apresentado al?m destas caracter?sticas, apreci?vel estabilidade a degrada??o hidrol?tica e enzim?tica. Dentro deste contexto, este trabalho teve como objetivo sintetizar poliuretanos ramificados est?veis a partir da adi??o de pentaeritritol e avaliar seu potencial uso como suportes em engenharia tecidual. Para a s?ntese do PU ramificado foi utilizado o poliol policaprolactona diol (PCL) e pentaeritritol (PETT) em diferentes quantidades (5, 10 e 15% m/m em rela??o ao poliol), bem como, o hexametilenodiisocianato (HDI). Estes PU ramificados (PU-PETT) foram avaliados quanto ?s propriedades estruturais, morfol?gicas, mec?nicas, t?rmicas e de solubilidade em diversos solventes org?nicos e comparados ao PU linear (sem PETT). Entre os PU ramificados, o PU-PETT 5% apresentou melhores caracter?sticas morfol?gicas e de resist?ncia a tra??o, por isso ele foi utilizado para preparar membranas lixiviadas juntamente com o PU linear. As membranas lixiviadas foram avaliadas quanto as suas propriedades estruturais, morfol?gicas, mec?nicas, t?rmicas, molhabilidade, degrada??o hidrol?tica calcifica??o e grau de inchamento. A membrana lixiviada de PU-PETT 5% apresentou alta porosidade e interconectividade, maior estabilidade t?rmica comparada a membrana lixiviada de PU linear, apesar do menor grau de cristalinidade e massa molar. Al?m disso, a membrana de PU-PETT 5% apresentou habilidade para a biomineraliza??o de fosfato de c?lcio, boa molhabilidade, maior estabilidade a degrada??o hidrol?tica e maior grau de inchamento quando comparado a membrana de PU linear. Com isso, pode-se concluir que a membrana de PU-PETT 5% apresentou caracter?sticas adequadas para uso como biomaterial em engenharia de tecidos.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-12-01T23:35:59Z No. of bitstreams: 1 EllisonMatheusDelioAlcantara_DISSERT.pdf: 1987085 bytes, checksum: 4511f07e0b4aeaea594ec88fad96b400 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-12-05T22:39:58Z (GMT) No. of bitstreams: 1 EllisonMatheusDelioAlcantara_DISSERT.pdf: 1987085 bytes, checksum: 4511f07e0b4aeaea594ec88fad96b400 (MD5) / Made available in DSpace on 2017-12-05T22:39:59Z (GMT). No. of bitstreams: 1 EllisonMatheusDelioAlcantara_DISSERT.pdf: 1987085 bytes, checksum: 4511f07e0b4aeaea594ec88fad96b400 (MD5) Previous issue date: 2017-11-27 / As preocupa??es ambientais v?m aumentando nos ?ltimos anos, principalmente devido ao uso de v?rios produtos derivados de petr?leo, os quais levam anos para se degradar na natureza. Para minimizar esse problema, v?rios estudos focam na utiliza??o de materiais naturais biodegrad?veis. Nesse contexto, verificou-se que a f?cula de mandioca pode ser aproveitada como mat?ria prima para produ??o de um biopol?mero que pode ser utilizado como isolante t?rmico. O biopol?mero foi produzido por um processo de expans?o t?rmica controlada com fra??es volum?tricas de 30% de ?gua e 70% de f?cula de mandioca. Foram analisadas as propriedades f?sicas e t?rmicas do material com intuito de obter dados sobre a viabilidade de seu uso como isolante t?rmico. O material apresentou uma condutividade t?rmica de 0,152 W/mK, podendo ser aplicado como isolante em sistemas quente de at? 270 ?C e um limite de resist?ncia a temperatura de 270?C observado pela an?lise termogravim?trica. O biopol?mero de f?cula de mandioca mostrou-se eficiente quanto ? isola??o t?rmica, devido possuir propriedades semelhantes ?s de isolantes t?rmicos dispon?veis comercialmente. Al?m disso, foram realizadas an?lises de inflamabilidade, a qual o material se apresentou como n?o inflam?vel. Al?m disso, analisou-se dureza caracterizando-o como um material duro. Diante disso, o material mostrou-se promissor a ser aplicado como isolante t?rmico. Essas an?lises foram fundamentadas em normas ABNT, ASTM e UL-94 e os resultados obtidos experimentalmente comprovam que o biopol?mero de f?cula de mandioca pode ser utilizado para fins de isolamento t?rmico. / Environmental concerns have been rising in recent years, mainly due to the use of various petroleum products, which take years to degrade in nature. To minimize this problem, several studies focus on the use of natural biodegradable materials. In this context, it has been found that manioc starch can be used as raw material for the production of a biopolymer that can be used as a thermal insulation. The biopolymer was produced by a controlled thermal expansion process with volumetric fractions of 30% water and 70% cassava starch. The physical and thermal properties of the material were analyzed in order to obtain data on the feasibility of its use as thermal insulation. The material had a thermal conductivity of 0.152 W / mK, and can be applied as an insulator in hot systems up to 270 ? C and a temperature resistance limit of 270 ? C observed by thermogravimetric analysis. Cassava starch biopolymer proved to be efficient in thermal insulation, due to its properties similar to those of commercially available thermal insulators. In addition, flammability analyzes were performed, to which the material presented as non-flammable. In addition, hardness was analyzed by characterizing it as a hard material. In view of this, the material proved promising to be applied as a thermal insulation. These analyzes were based on ABNT, ASTM and UL-94 standards and the results obtained experimentally prove that the biopolymer of cassava starch can be used for thermal insulation purposes.

Made available in DSpace on 2014-12-17T14:19:59Z (GMT). No. of bitstreams: 1 MichelleFB_DISSERT.pdf: 4773085 bytes, checksum: 8456dec6bf8638729a69f19a44a47e95 (MD5) Previous issue date: 2009-12-22 / Taking the narrative of life of three women (homeless), Maria Jos? (residente of a psychiatric hospital) and Maria de La Luz Cervantes (fictional character of Gabriel Garcia Marquez, accidentally intern in a psychiatric hospital), the dissertation "Marias: Biopolitics, bare life and their stories" brings Giorgio Agamben's theories referring to Naked Life and Homo Sacer, Michel Foucault's with the biopolitics and resiliences written by Boris Cyrulnik. Its on these three women life stories that the dissertation develops a imaginary concentration camp to work their lives and bodies subjection to the external power, the biopolitic / A partir da narrativa de vida de tr?s mulheres, Maria Firmino (moradora de rua), Maria Jos? (moradora de um hospital psiqui?trico) e Maria de La Luz Cervantes (personagem fict?cia do conto de Gabriel Garcia M?rquez, interna acidentalmente num hospital psiqui?trico), a disserta??o Marias: Biopol?tica, Vida Nua e Resili?ncias traz as teorias de Giorgio Agamben referente ? Vida Nua e Homo Sacer, Michel Foucault com a biopol?tica e as resili?ncias escritas por Boris Cyrulnik. S?o nas hist?rias de vida destas tr?s mulheres que a disserta??o desenvolve um campo de concentra??o imagin?rio para trabalhar a sujei??o de suas vidas e corpos ao poder externo, ? biopol?tica

Made available in DSpace on 2014-12-17T15:12:12Z (GMT). No. of bitstreams: 1 BenjamimJGF_DISSERT.pdf: 516827 bytes, checksum: ce4125dceaf84c5140066d093f16dadc (MD5) Previous issue date: 2010-04-28 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The fundamental question developed in this research is to consider the possible meanings of biopolitics in the thought of Michel Foucault. In the first chapter of this study seeks to examine the rationality of biopower. It is able to show the rationality of acting as a social machinery for the manufacture of the subjectivity of individuals, biopolitics as a producer of bodies and subjectivity. The theme of biopolitics appears as inspiration of Nietzsche's metaphor of war. The idea that history is the war for dominance of the bodies. In the second chapter, the (bio) political will and political thought of resistance, fighting criticism as an attitude of revolt of the subject before his condition subjugated. The biopolitical here is intended as a conceptual tool for reading the thought / Foucault's work. A resistance that can be thought of as a biopolitical as a "refractoriness reflected". The third chapter will seek to show how the Foucault argues that power was already present the ethics of self-care. If the subject is a product, is captured by the discourse of biopower that manufactures its subjectivity, self care, it's time to think about the inner contents. Self care is something that offers resistance, as a possibility to think that these contents are constructed historically, and that therefore it is possible to reestablish the self-care is a policy of fighting these sedimented content that promotes colonization of the subjects. You can move from ruler to ruled itself, although this pursuit of liberty is always unfinished, always be a tension, a desire for freedom that can be undertaken not as a state, but at least the minimum and temporarily in other forms of existence, and other ways of relating, other ways of sociability, friendship, sexuality / A quest?o fundamental desenvolvida nesta pesquisa consiste em pensar sobre os poss?veis sentidos da biopol?tica no pensamento de Michel Foucault. No primeiro cap?tulo desse estudo procura-se analisar a racionalidade do biopoder. Trata-se de apresentar a racionalidade do poder funcionando como uma maquinaria social na fabrica??o da subjetividade dos indiv?duos, a biopol?tica como produtora de corpos e da subjetividade. O tema da biopol?tica aparece como inspira??o da met?fora nietzscheana da guerra. A id?ia de que a hist?ria ? a guerra pelo dom?nio dos corpos. No segundo cap?tulo, a (bio)pol?tica ser? pensada como pol?ticas de resist?ncias, lutas cr?ticas, como uma postura de revolta do sujeito diante de sua condi??o de assujeitado. O biopol?tico, aqui, ? pensado como uma ferramenta conceitual para a leitura do pensamento/obra de Foucault. Uma resist?ncia que pode ser pensada como uma biopol?tica, como uma indocilidade refletida . No terceiro cap?tulo, procurar-se-? mostrar como no Foucault que discute o poder j? estava presente a ?tica do cuidado de si. Se o sujeito ? produto, ? capturado pelo discurso do biopoder que fabrica sua subjetividade, o cuidado de si, ? a hora de pensar os conte?dos interiores. O cuidado de si ? algo que se oferece como resist?ncia, como uma possibilidade de pensar que esses conte?dos s?o constru?dos historicamente, e que portanto, ? poss?vel refundar-se. o cuidado de si ? uma pol?tica de combate a esses conte?dos sedimentados que promove a coloniza??o dos sujeitos. ? poss?vel passar de governado a governante de si, embora essa busca de liberdade seja sempre inacabada, seja sempre uma tens?o, uma vontade de liberdade que pode se realizar n?o como um estado, mas pelo menos m?nima e provisoriamente em formas outras de exist?ncia, e modos outros de se relacionar, maneiras outras de sociabilidade, de amizade, de sexualidade

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-01-10T15:32:21Z No. of bitstreams: 1 KarlaSamaraRochaSoares_TESE.pdf: 2883085 bytes, checksum: 02667bee72d9ca986a7f49f759803663 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-01-11T15:56:53Z (GMT) No. of bitstreams: 1 KarlaSamaraRochaSoares_TESE.pdf: 2883085 bytes, checksum: 02667bee72d9ca986a7f49f759803663 (MD5) / Made available in DSpace on 2017-01-11T15:56:53Z (GMT). No. of bitstreams: 1 KarlaSamaraRochaSoares_TESE.pdf: 2883085 bytes, checksum: 02667bee72d9ca986a7f49f759803663 (MD5) Previous issue date: 2016-05-31 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Acidentes com animais pe?onhentos representam um s?rio problema de sa?de p?blica em diversos pa?ses, destacando-se os acidentes of?dicos e escorpi?nicos. No Brasil, as serpentes do g?nero Bothrops e os escorpi?es pertencentes ao g?nero Tityus, s?o as de maior relev?ncia cl?nica. O tratamento para o envenenamento consiste em administra??o de soros antiof?dico e antiescorpi?nico. Vacinas que utilizam ant?genos puros e vias de administra??o alternativa requerem o uso de adjuvantes potentes e um sistema de entrega de ant?geno eficaz. Nanossistemas v?m sendo investigados como sistemas de libera??o para macromol?culas terap?uticas. A quitosana, devido as suas propriedades, tem sido extensivamente investigada na formula??o de nanocarreadores, particularmente de genes e prote?nas. Este estudo teve como objetivo a obten??o de nanopart?culas de quitosana (CNP) com base na gelifica??o i?nica para carrear prote?nas/pept?deos terap?uticos utilizados na imunoterapia e avalia??o do potencial imunoadjuvante dessas nanopart?culas na produ??o de soros antivenenos. CNP foram obtidas por gelifica??o i?nica, com tamanho m?dio de 160 nm, caracterizadas f?sico-quimicamente e o perfil de libera??o avaliado, demonstrando se tratar de um sistema de libera??o modificado. A estabilidade dos sistemas foi avaliada por 7 semanas, observando-se uma maior estabilidade dos sistemas associados aos venenos. Animais experimentais foram imunizados durante 6 semanas com 100 ?L de veneno das serpentes atrav?s inje??es subcut?neas, em diferentes concentra??es (5,0 ou 10,0%), encapsuladas em CNP ou associados ao hidr?xido de alum?nio (HA). Os resultados demonstram que os t?tulos de anticorpos obtidos para os animais vacinados com os nanossistemas foram equivalentes ou maiores aos obtidos para os animais vacinados com o HA, com a vantagem desses serem menos inflamat?rios que o HA, exigindo uma menor quantidade de ant?geno a ser administrada, por se tratar de um sistema de liberta??o modificada, revelando a obten??o de um novo sistema nanoparticulado com potencial aplica??o na soroterapia. / Accidents with venomous animals represent a serious public health problem in many countries of the world, with emphasis to snake and scorpion accidents. In Brazil, Bothrops snakes are the most clinically relevant. Regarding scorpions, the genus Tityus includes the species of higher medical importance. Treatment for envenomation consists mainly in the administration of antivenom sera. Vaccines using pure antigens in alternative administration routes require the use of potent adjuvants and an effective antigen delivery system. Nanosystems are being investigated as delivery systems for therapeutic macromolecules. Chitosan, due to its properties, has been extensively investigated in nanocarriers formulations, particularly for genes and proteins. This study aimed to obtain chitosan nanoparticles (CNP) based on ionic gelation for the delivery of therapeutic proteins/peptides used in immunotherapy, as well as to evaluate the immunoadjuvant potential of these nanoparticles in the production of antivenom serums. CNP were obtained by ionic gelation, with an average size of 160 nm. Physicochemical characterization and evaluation of the release profile demonstrated that it is a modified release system. The stability of different systems was evaluated for 7 weeks, observing a greater stability of the systems associated with venoms. Experimental animals were immunized subcutaneously for 6 weeks with 100 uL snake venoms at different concentrations (5.0 or 10.0%), either encapsulated in CNP or associated with aluminum hydroxide (AH). The results demonstrate that the antibody titers observed for animals vaccinated with the studied nanosystems were equivalent or higher than those observed for animals vaccinated with HA. Further advantages of the nanosystems were to be less inflammatory, and to require smaller amounts of antigen to be administered, because it is a modified-release system, with potential application in anti-venom serum therapy.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-04-03T21:33:40Z No. of bitstreams: 1 DaniguiReniguiMartinsDeSouza_DISSERT.pdf: 915908 bytes, checksum: 4d2e4aa8ff487752ec8f6522aad615e8 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-04-10T18:23:44Z (GMT) No. of bitstreams: 1 DaniguiReniguiMartinsDeSouza_DISSERT.pdf: 915908 bytes, checksum: 4d2e4aa8ff487752ec8f6522aad615e8 (MD5) / Made available in DSpace on 2017-04-10T18:23:44Z (GMT). No. of bitstreams: 1 DaniguiReniguiMartinsDeSouza_DISSERT.pdf: 915908 bytes, checksum: 4d2e4aa8ff487752ec8f6522aad615e8 (MD5) Previous issue date: 2017-02-03 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / O conceito de biopol?tica tem se tornado um rico instrumento de an?lise ou uma esclarecedora chave hermen?utica para a reflex?o contempor?nea sobre a l?gica do poder, a genealogia do governo e o significado da pol?tica no mundo moderno. As diferentes concep??es de biopol?tica t?m cada qual suas especificidades. O foco da abordagem do presente estudo ser? exclusivamente o diagn?stico biopol?tico do presente elaborado por Agamben, no qual o conceito de biopol?tica est? centrado na politiza??o da vida biol?gica. Procuramos mostrar o modo como a ?arqueologia da biopol?tica? empreendida por Agamben pode ser compreendida a partir da an?lise de quatro no??es fundamentais, quais sejam: poder soberano, vida nua, estado de exce??o e campo. Analisamos, primeiro, de que modo Agamben pensou a associa??o entre o dom?nio pol?tico e a animaliza??o do homem a partir das lacunas deixadas pelas investiga??es de Arendt e Foucault. Em um segundo momento, examinamos a rela??o entre a organiza??o soberana dos corpos e o estado de exce??o. No terceiro passo de nosso percurso, analisamos a politiza??o da vida nua e a produ??o do homo sacer, a sacralidade da vida. Em uma quarta e ?ltima etapa, esclarecemos de que modo Agamben pensou o ?campo? como ?n?mos? secreto da biopol?tica na modernidade. Trata-se de explicitar de que forma a reflex?o de Agamben sobre o nexo existente entre poder pol?tico e vida nua se articula em torno desses quatro aspectos estruturantes. Buscamos evidenciar a relevante contribui??o que o pensamento de Agamben oferece para o diagn?stico cr?tico da racionalidade pol?tica nas sociedades contempor?neas, aprimorando nossa compreens?o sobre as novas formas do poder na modernidade tardia. / The concept of biopolitics is a rich instrument of analysis and interpretation of the logic of power, the genealogy of government and the meaning of politics in the modern world. The different conceptions of biopolitics each have their specificities. The focus of the present study will be exclusively the biopolitical diagnosis of the present elaborated by Agamben, in which the concept of biopolitics is centered on the politicization of biological life. We seek to show how Agamben's ?archeology of biopolitics? can be understood from the analysis of four fundamental notions: sovereign power, bare life, state of exception, and field. We first analyze how Agamben thought the association between the political domain and the animalization of man from the gaps left by the investigations of Arendt and Foucault. In a second moment, we examine the relationship between the sovereign organization of bodies and the state of exception. In the third chapter, we analyze the politicization of natural life and the production of homo sacer, the sacred life. In the fourth chapter, we clarified how Agamben thought of the ?field? as a secret ?notion? of biopolitics in modernity. Therefore, we seek to show how Agamben's reflection on the nexus between political power and bare life is articulated around these four structuring aspects. We seek to highlight the relevant contribution that Agamben's thinking offers to the critical diagnosis of political rationality in contemporary societies, enhancing our understanding of the new forms of power in late modernity.