No description available.

In the present work, the influence of the morphology of thin ferromagnetic films on their static as well as dynamic magnetic properties was investigated by means of broadband ferromagnetic resonance (FMR). Using an ion beam erosion process the surface of the substrates was periodically modulated (ripples), where the modulation wavelength is determined by the ion energy. In this way a well-controllable roughness profile evolves ranging from a few ten up to several hundreds of nanometers in wavelength. The substrate’s surface profile in turn is repeated by films grown on top offering an easy and fast approach to investigate morphology influences on the magnetic properties. This work aims on modifications of the magnetic anisotropy as well as the FMR linewidth of the magnetic relaxation process. Prior to magnetic investigations the existing FMR setup was extended to measure FMR spectra at a fixed microwave frequency while sweeping the external magnetic field. Furthermore, a software toolbox was developed to perform the data processing and evaluation. Starting with the morphology influence on the magnetic anisotropy 10 nm thin Fe, Co, and Ni81Fe19 (Permalloy ≡ Py) films were deposited on rippled Si substrates. Due to Si displacements during ion erosion and natural oxidation the rippled Si substrates exhibit an amorphous surface causing a polycrystalline material growth. This leads to a suppression of magneto-crystalline anisotropy leaving only morphology-induced anisotropy contributions. Here, a uniaxial magnetic anisotropy (UMA) was observed that aligns its easy axis with the ripple ridges, whereas its strength decays with increasing ripple wavelength for all materials. From thickness-dependent measurements two characteristic regions were determined with competing uniaxial volume and surface anisotropy contributions. Underlined by micromagnetic simulations a dominant volume contribution was found in the thin region accompanied by magnetic moments nearly following the surface corrugation. In the thick region the UMA is controlled by dipolar stray fields at the surface. In contrast to Si, ion eroded MgO keeps its crystal structure offering epitaxial growth of 10 nm thin single-crystalline Fe films. Consequently, a superposition of morphology-induced UMA and magneto-crystalline cubic anisotropy was observed. The direction of the ripple ridges is predetermined by the incident ion beam, which allows to freely orient the UMA’s direction with respect to the cubic anisotropy, offering a possibility for anisotropy engineering. In comparison to the planar reference case rippled magnetic films exhibit lower intrinsic and extrinsic relaxation contributions. For the final part, 30 nm Py was grown on rippled Si covering modulation wavelengths λ ranging from 27 to 432 nm. Using magnetic force microscopy and holography measurements the dipolar stray fields above and inside the magnetic layer were characterized. For λ ≥ 222 nm, the stray fields act as scattering centers for spin waves triggering two-magnon scattering (TMS). This causes an apparent line broadening generating distinct peaks in the frequency-dependent linewidth whose position can be tuned by altering λ. These effects are understood in the framework of a perturbation theory of spin waves in periodically perturbed films recently presented in the literature. Furthermore, the in-plane angular dependence of the linewidth revealed a two-fold symmetry, which is not present for vanishing TMS at small λ. / In Rahmen dieser Arbeit wurde der Einfluss der Morphologie eines dünnen ferromagnetischen Films auf dessen statische und dynamische Eigenschaften mittels breitbandiger ferromag- netischer Resonanz (FMR) untersucht. Durch Ionenstrahl-Erosion wurde die Oberfläche des verwendeten Substrats periodisch moduliert (Ripple), wobei die Wellenlänge der Modulation durch die Ionenenergie bestimmt ist. Dies ermöglicht die kontrollierte Herstellung rauer Oberflächen mit Wellenlängen zwischen wenigen zehn bis zu einigen hundert Nanometern. Werden auf diesen Oberflächen Filme abgeschieden, übernehmen diese die Modulation. Somit ergibt sich eine einfache und schnelle Untersuchungsmöglichkeit der magnetischen Filmeigenschaften in Hinblick auf die Morphologie. Das Ziel dieser Arbeit ist die Untersuchung von Morphologieeinflüssen auf die magnetische Anisotropie sowie FMR-Linienbreite. Im Vorfeld der magnetischer Untersuchungen wurde der bestehende FMR-Aufbau um einen Messmodus erweitert, sodass Messungen bei fester Mikrowellenfrequenz und gleichzeitigem Durchfahren eines externen magnetischen Feldes möglich wurden. Weiterhin wurde ein Softwarepaket für die Datenauswertung entwickelt. Beginnend mit dem Morphologieeinfluss auf die magnetische Anisotropie wurden 10 nm dünne Fe, Co und Ni81Fe19 (Permalloy ≡ Py) Filme auf periodisch moduliertem Si abgeschieden. Durch Versetzungen während der Ionenstrahl-Erosion und Bildung einer natürlichen Oxidschicht bildet sich bei den verwendeten Substraten eine amorphe Oberfläche, was zu polykristallinem Schichtwachstum führt. Dadurch wird die magneto-kristalline Anisotropie unterdrückt und morphologie-induzierte Beiträge bestimmen die Anisotropie. Beobachtet wurde eine induzierte uniaxiale magnetische Anisotropie (UMA), deren leichte Richtung sich entlang der Ripple-Wellenzüge ausrichtet. Mittels schichtdickenabhängigen Messungen wurden zwei charakteristische Regionen mit konkurrierender uniaxialer Volumen- und Oberflächenanisotropie ermittelt. Dabei ist die Volumenkomponente im Bereich dünner Schichten vorherrschend und die magnetischen Momente richten sich entlang der Oberflächenmodulation aus. Für dickere Schichten ist die UMA dahingegen durch dipolare Streufelder bestimmt. Die experimentellen Funde werden in beiden Bereichen durch mikromagnetische Simulationen untermauert. Im Gegensatz zu erodiertem Si behält MgO seine Kristallstruktur, was epitaktisch gewachsene, einkristalline Fe-Schichten von 10 nm Dicke ermöglicht. Folglich wurde eine Überlagerung aus induzierter und kristalliner Anisotropie beobachtet. Dadurch, dass die Richtung der Ripple durch die Richtung des Ionenstrahls während der Erosion vorgegeben wird, lässt sich die UMA frei gegen die kristalline Anisotropie drehen, was wiederum Möglichkeiten zur gezielten Beeinflussung der Anisotropie bietet. Im Hinblick auf die dynamischen magnetischen Eigenschaften führen Ripple zu einer Verringerung der intrinsischen und extrinsischen Relaxationsbeiträge. Für den letzten Teil der Arbeit wurde 30 nm dünnes Py auf Si-Ripple gewachsen, wobei ein Wellenlängenbereich von λ = 27 nm bis 432 nm abgedeckt wurde. Mit Hilfe von magnetischer Kraftmikroskopie und Holographie wurden die dipolaren Streufelder über und in den Filmen untersucht. Ab λ ≥ 222 nm ermöglichen diese dipolaren Felder eine Streuung von Spinwellen, sodass Zwei-Magnonen-Streuung (TMS) auftritt. Dies führt zu einer scheinbaren Linienverbreiterung und äußert sich durch einzelne Peaks in der frequenzabhängigen Linienbreite. Letztere lassen sich in ihrer Frequenzposition durch die Wellenlänge des Substrates beeinflussen und können mittels einer kürzlich in der Literatur veröffentlichten Störungstheorie für Spinwellen in periodisch gestörten Filmen erklärt werden. Weiterhin wurde in der winkelabhängigen Linienbreite eine zweifache Symmetrie beobachtet, welche durch die TMS hervorgerufen wird und folglich nicht bei kleinen Wellenlängen zu beobachten ist.

Kohlenstofffaserverstärkter Kohlenstoff weist ausgezeichnete thermische, mechanische und chemische Eigenschaften auf. Aufgrund seiner Faserarchitektur und Porosität zeigt dieser eine mit metallischen und polymeren Werkstoffen vergleichbar hohe Schadenstoleranz. Die Herstellung komplexer Leichtbaustrukturen aus C/C-Verbunden ist jedoch zeit- und kostenintensiv. Ein neuer Ansatz stellt die Integration geometrisch simpler C/C-Verbunde in komplexe, problemlos zu realisierende polymere Strukturen dar. Ein derartiges Werkstoffkonzept vereint die Vorteile seiner Komponenten in einem ganzheitlichen Werkstoffsystem. Einen Nachteil stellt jedoch die geringe wechselseitige Adhäsion seiner Komponenten dar. Die Innovation dieses Beitrags stellt sich einerseits der Herausforderung die mechanischen Eigenschaften der C/C-Verbunde in Abhängigkeit der intrinsischen Porosität zu beeinflussen. Dies geschieht durch Veränderung der chemischen und physikalischen Vernetzungsbedingungen des Matrixprecursors. Andererseits soll die dadurch herrührende inhärente Porosität zur Vergrößerung der wirksamen äußeren Oberfläche und zur gezielten Verbesserung der Adhäsion zum Polymer führen. Es wird ein Kohlenstoffprecursor mit variabler offener Porosität entwickelt und daraus neuartige verschiedenporöse C/C-Verbunde hergestellt und untersucht. Im Anschluss werden die verschiedenporösen C/C-Verbunde mit ausgewählten Polymeren unter definierten Konsolidierungsparametern thermisch gefügt und deren wechselseitiges Adhäsionsverhalten bewertet. / Fibre-reinforced ceramic matrix composite materials are characterized by excellent thermal, mechanical and chemical properties. Their high tolerance regarding damaging is a result of the intrinsic fibre structure and porosity. Due to this fact, they offer outstanding dampening characteristics, as is the case for polymeric materials. The production of complex structures is very time consuming and expensive. The integration of simple geometric ceramic composite materials in complex polymeric structures is regarded as a new approach for the production of these materials. These easy-to-produce hybrid ceramic/polymer compound materials combine the advantages of ceramics and polymers in one material system. However, one main disadvantage of these materials is the mutual adhesion of the two components. This article deals with the challenge of the manipulation of the mechanical properties of the C/C composites depending on the intrinsic porosity. This is realized by altering the physical and chemical wetting/coating conditions of the matrix precursor. In addition, the inherent porosity is supposed to increase the effective outer surface and specifically improve the adhesion. For this purpose, a novel carbon precursor with an adjustable open porosity is developed and investigated further. During this different versions of the CFRP and various C/C materials of different production steps are produced and examined. The variation of the precursors is supposed to take place in the polymeric state. The different C/C composites are subsequently thermally bonded with selected polymers and defined consolidation parameters. The mutual joining and connection behaviour is investigated further.

Die mikromechanische Gleichspannungswandlung basierend auf verschiebungsabhängigen Kapazitäten stellt eine Alternative zu etablierten rein elektronischen Wandlern für den Spezialfall der kapazitiven oder piezoelektrischen Verbraucher dar. Durch ihre kleine Bauform und den Verzicht auf Induktivitäten bietet sie den Vorteil der On-Chip-MEMS- und CMOS-Integration und ermöglicht die Bereitstellung hoher elektrischer Gleichspannungen aus den verfügbaren Grundspannungen der Elektronik (z. B. 3, 5 bzw. 12 V). Von hohen Polarisationsspannungen profitieren nicht nur kapazitive Sensoren und Aktoren, sondern auch piezoelektrische Messverfahren. Diese Arbeit stellt eine umfangreiche Übersicht und Bewertung der möglichen Bauformen mikromechanischer Gleichspannungswandler sowie die konkrete Umsetzung, Charakterisierung und Modellbildung eines resonant arbeitenden Wandlers vor. Es wird auf Besonderheiten und Probleme im Entwurf eingegangen und ausgehend von den Ergebnissen ein Konzeptentwurf für einen optimierten resonanten Gleichspannungswandler erarbeitet.:1 Einleitung 2 Theoretische Grundlagen 3 Ausführungsvarianten von MEMS-DC/DC-Wandlern 4 Designstudie und Umsetzung des resonanten Funktionsprinzips 5 Zusammenfassung und Ausblick / Micromechanical DC/DC conversion based on variable capacitances is an alternative to established electronic voltage converters, which does not require bulky inductors and is suitable for capacitive and piezoelectric loads. The converters are capable of boosting up the polarization voltage from CMOS and electronic levels (3, 5, 12 V), which is beneficial not only for capacitive sensors and actuators but also for piezoelectric sensing. Advantages of this method are the on-chip- and CMOS-integrability. This thesis introduces a comprehensive overview and evaluation of possible designs as well as the practical application, characterization and modeling of a resonant micromechanical DC/DC converter. Innovative claims include a test board for the characterization of resonant DC/DC converters and a SPICE behavioral model of the device, considering parasitic effects. Characteristics and problems of the design are discussed and the results are used to demonstrate an optimized conceptual design of a resonant DC/DC converter.:1 Einleitung 2 Theoretische Grundlagen 3 Ausführungsvarianten von MEMS-DC/DC-Wandlern 4 Designstudie und Umsetzung des resonanten Funktionsprinzips 5 Zusammenfassung und Ausblick

Im Forschungsprojekt wurde eine Bauweise für ein modular aufgebautes und flexibel einsetzbares Gestellsystem entwickelt, welches durch integrativen Leichtbau den vorteilhaften Einsatz von Holzfurnierlagenverbund-werkstoffen (WVC) für Verarbeitungs- und Fördermaschinen ermöglicht. Die ingenieurtechnisch relevanten Eigen-schaften des Holzbasiswerkstoffs (u.a. strukturelle Dämpfungseigenschaft) wurden ermittelt und darauf aufbauend ein Profil als Strukturelement des Gestellsystems entwickelt. Hier lag besonderes Augenmerk auf der Gestaltung des Profilquerschnitts. Es wurden verschiedene Querschnittsgeometrien vergleichend untersucht, wobei sich ein ge-schlossenes Kastenprofil als günstig erwies. Ausgehend vom entwickelten Profil wurde die für ein modulares Sys-tem notwendige Verbindungstechnik konzipiert. Folgend wurde schrittweise die modulare Bauweise in Strukturein-heiten umgesetzt sowie parallel Untersuchungen zu Steifigkeit und Festigkeit der Profile fortgeführt. Während der Erprobung von Struktureinheiten unter praxisnahen Bedingungen wurden gewisse konstruktive Verbesserungspo-tentiale deutlich. Diese Änderungen sowie die gewonnenen Erkenntnisse aus der Material- und Strukturprüfung kamen im Prototyp zur Umsetzung. Schallpegelprofile verschiedener fördertechnischer Anlagen und des entwickel-ten Prototypen wurden abschließend aufgenommen und verglichen. / Aim of the present study was to develop a modular designed and widely employable rack system. Positive properties of wood based materials (WVC) in lightweight structures were identified and integrated for the application in fabri-cation and conveyer technologies. For this purpose relevant properties of wood materials had been investigated (e.g. damping properties). The results of these analyses were the basis for the development of a beam profile, the basic structural design element for the future rack system. The most effort was put into finding the optimal beam cross section. Several different cross sections had been compared, a square sectional beam profile showed the best per-formance. Based on the square sectional beam profile proper connection methods for the modular rack were devel-oped. Structural units were subsequently realized step by step, while the investigation of stiffness and strength of the profiles was continued. The testing of the structural units under simulated field conditions revealed some minor constructional improvement capabilities. The constructional improvements and the knowledge from the material and profile testing were put into practice in the prototype. Finally sound measurements were carried out to compare several conveyors made of different materials (including the prototype) in respect to the emitted sound level.

Die vollständige Ausnutzung des Leichtbaupotentials bei der Dimensionierung von mehrschichtigen endlosfaserverstärkten Strukturbauteilen erfordert die Bereitstellung von geeigneten Optimierungswerkzeugen, da bei der Auslegung eine große Anzahl von Entwurfsvariablen zu berücksichtigen sind. In dieser Arbeit werden Optimierungsalgorithmen und -strategien zur Lösung wissenschaftlicher Fragestellungen für industrielle Anwendungen bei der Konstruktion von entsprechenden Faserkunststoffverbunden entwickelt und bewertet. Um das breite Anwendungsspektrum aufzuzeigen, werden drei unterschiedliche repräsentative Problemstellungen bearbeitet. Dabei wird für Mehrschichtverbunde die Festigkeitsoptimierung hinsichtlich eines bruchtypbezogenen Versagenskriteriums vorgenommen, ein Dämpfungsmodell zur Materialcharakterisierung entworfen sowie eine bivalente Optimierungsstrategie zur Auslegung von gewickelten Hochdruckbehältern erstellt. Die Grundlage der entwickelten Methoden bilden dabei jeweils stochastische naturanaloge Optimierungsheuristiken, da die betrachteten Aufgabenstellungen nicht konvex sind und derartige Verfahren flexibel eingesetzt werden können. / The full utilization of the light weight potential in the dimensioning of multilayer fiber reinforced composites requires suitable optimization tools, since a large number of design variables has to be taken into account. In this work, optimization algorithms and strategies for the solution of scientific questions for industrial applications are developed and evaluated in the design of corresponding fiber-plastic composites. In order to show the wide range of applications, three different representative topics have been chosen. It will carry out a strength optimization for multilayer composites with regard to a type-related failure criterion, devolop a damping model for material characterization and established a bivalent optimization strategy for the design of wound high-pressure vessels. The developed methods are based on stochastic natural-analog optimization heuristics, since the considered tasks are not convex and such methods can be used in a very flexible manner.

The subject of the thesis is the investigation of asymptotic properties of solutions of the Cauchy problem for structurally damped sigma-evolution operators with time dependent, monotonous, dissipation term. An appropriate energy for solutions of the sigma-evolution equations is defined and some estimates for energies of higher order are proved. In the scale invariant case the optimality of these estimates is shown. Further, the influence of properties of the time dependent dissipation on L^p-L^q estimates for the energy with p and q bigger or equal to 2 and from the conjugate line is clarified. Also smoothing properties of the operators under consideration are investigated. The connection between the regularity of the data and the regularity of the solution in terms of L^2 based Gevrey spaces is considered. Finally, L^1-L^1-estimates in the special case delta = sigma/2 and decreasing dissipative coefficient. / Thema der vorliegenden Dissertation ist die Untersuchung asymptotischer Eigenschaften von Lösungen des Cauchy Problems für strukturell gedämpfte sigma-Evolutions-Operatoren mit zeitabhängigem, monotonen Dissipationskoeffizienten. Es wird eine geeignete Energie definiert und für diese Abschätzungen, auf für entsprechende Energien höherer Ordnung gezeigt. Darüber hinaus wird der Einfluss des Dissipationskoeffizienten auf L^p-L^q Abschätzungen auf und entfernt von der konjugierten Linie untersucht. Im skaleninvarianten Fall wird die Schärfe der Abschätzungen bewiesen. Weiterhin wird der Zusammenhang zwischen der Regularität der Daten und der der Lösung in Termen von L^2-basierten Gevrey-Räumen untersucht. Schließlich werden L^1-L^1-Abschätzungen für den Spezialfall delta = sigma/2 und monoton fallenden Dissipationskoeffizienten gezeigt.

In the present work, the implications of ion irradiation on the magnetostatic and dynamic properties of soft magnetic Py/Ta (Py = Permalloy: Ni80Fe20) single and multilayer films have been investigated with the main objective of finding a way to determine their saturation magnetization. Both polar magneto-optical Kerr effect (MOKE) and vector network analyzer ferromagnetic resonance (VNA-FMR) measurements have proven to be suitable methods to determine µ0MS, circumventing the problem of the unknown effective magnetic volume that causes conventional techniques such as SQUID or VSM to fail. Provided there is no perpendicular anisotropy contribution in the samples, the saturation magnetization can be determined even in the case of strong interfacial mixing due to an inherently high number of Py/Ta interfaces and/or ion irradiation with high fluences. Another integral part of this work has been to construct a VNA-FMR spectrometer capable of performing both azimuthal and polar angle-dependent measurements using a magnet strong enough to saturate samples containing iron. Starting from scratch, this comprised numerous steps such as developing a suitable coplanar waveguide design, and writing the control, evaluation, and fitting software. With both increasing ion fluence and number of Py/Ta interfaces, a decrease of saturation magnetization has been observed. In the case of the 10×Py samples, an immediate decrease of µ0MS already sets in at small ion fluences. However, for the 1×Py and 5×Py samples, the saturation magnetization remains constant up to a certain ion fluence, but then starts to rapidly decrease. Ne ion irradiation causes a mixing and broadening of the interfaces. Thus, the Py/Ta stacks undergo a transition from being polycrystalline to amorphous at a critical fluence depending on the number of interfaces. The saturation magnetization is found to vanish at a Ta concentration of about 10–15 at.% in the Py layers. The samples possess a small uniaxial anisotropy, which remains virtually unaffected by the ion fluence, but slightly reduces with an increasing number of Py/Ta interfaces. In addition to magnetostatics, the dynamic properties of the samples have been investigated as well. The Gilbert damping parameter α increases with both increasing number of Py/Ta interfaces and higher ion fluences, with the former having a stronger influence. The inhomogeneous linewidth broadening ΔB0 increases as well with increasing number of Py/Ta interfaces, but slightly decreases for higher ion fluences. / In dieser Dissertation ist der Einfluss von Ionenbestrahlung auf die magnetostatischen und dynamischen Eigenschaften von weichmagnetischen Py/Ta-Einzel- und Multilagen (Py = Permalloy: Ni80Fe20) untersucht worden, wobei das Hauptziel gewesen ist, eine Methode zur Bestimmung der Sättigungsmagnetisierung zu finden. Sowohl polare magneto-optische Kerr-Effektmessungen (MOKE) als auch ferromagnetische Resonanzmessungen mittels eines Vektornetzwerkanalysators (VNA-FMR) haben sich als geeignet erwiesen, um µ0MS zu bestimmen, wobei das Problem des unbekannten effektiven magnetischen Volumens umgangen wird, welches bei der Verwendung von Techniken wie SQUID oder VSM auftreten würde. Unter der Voraussetzung, dass die Proben keinen senkrechten magnetischen Anisotropiebeitrag besitzen, kann die Sättigungsmagnetisierung selbst im Fall starker Grenzflächendurchmischung infolge einer großen Anzahl an Py/Ta-Grenzflächen und/oder Ionenbestrahlung mit hohen Fluenzen bestimmt werden. Ein weiterer wesentlicher Bestandteil dieser Arbeit ist die Konstruktion eines VNA-FMR-Spektrometers gewesen, welches vollautomatisiert ist, polare und azimutale Winkelabhängigkeiten messen kann und einen Magneten besitzt, der Proben, die Eisen beinhalten, sättigen kann. Von Grund auf beginnend umfasste dies zahlreiche Schritte wie z. B. die Entwicklung eines geeigneten koplanaren Wellenleiterdesigns sowie das Schreiben von Steuerungs-, Auswertungs- und Fitprogrammen. Mit steigender Fluenz und Zahl an Py/Ta-Grenzflächen ist eine Abnahme der Sättigungsmagnetisierung beobachtet worden. Im Fall der 10×Py-Proben findet diese bereits bei kleinen Fluenzen statt. Im Gegensatz dazu bleibt µ0MS der 1×Py- und 5×Py-Proben bis zu einer bestimmten Fluenz konstant, bevor sie sich dann umso schneller verringert. Die Bestrahlung mit Ne-Ionen verursacht eine Durchmischung und Verbreiterung der Grenzflächen. Infolgedessen erfahren die Py/Ta-Proben bei einer kritischen Fluenz, die von der Zahl der Grenzflächen abhängig ist, einen Phasenübergang von polykristallin zu amorph. Die Sättigungsmagnetisierung verschwindet ab einer Ta-Konzentration von etwa 10–15 Atom-% in den Py-Schichten. Die Proben besitzen eine kleine uniaxiale Anisotropie, die praktisch unbeeinflusst von der Fluenz ist, sich jedoch mit steigender Zahl an Py/Ta-Grenzflächen leicht verringert. Neben den statischen sind auch die dynamischen magnetischen Eigenschaften der Proben untersucht worden. Der Gilbert-Dämpfungsparameter α erhöht sich sowohl mit steigender Zahl an Py/Ta-Grenzflächen als auch mit höheren Fluenzen, wobei Erstere einen größeren Einfluss hat. Die inhomogene Linienverbreiterung ΔB0 nimmt ebenfalls mit steigender Zahl an Py/Ta-Grenzflächen zu, verringert sich jedoch bei größeren Fluenzen leicht.

In the present work, the influence of the morphology of thin ferromagnetic films on their static as well as dynamic magnetic properties was investigated by means of broadband ferromagnetic resonance (FMR). Using an ion beam erosion process the surface of the substrates was periodically modulated (ripples), where the modulation wavelength is determined by the ion energy. In this way a well-controllable roughness profile evolves ranging from a few ten up to several hundreds of nanometers in wavelength. The substrate’s surface profile in turn is repeated by films grown on top offering an easy and fast approach to investigate morphology influences on the magnetic properties. This work aims on modifications of the magnetic anisotropy as well as the FMR linewidth of the magnetic relaxation process. Prior to magnetic investigations the existing FMR setup was extended to measure FMR spectra at a fixed microwave frequency while sweeping the external magnetic field. Furthermore, a software toolbox was developed to perform the data processing and evaluation. Starting with the morphology influence on the magnetic anisotropy 10 nm thin Fe, Co, and Ni81Fe19 (Permalloy ≡ Py) films were deposited on rippled Si substrates. Due to Si displacements during ion erosion and natural oxidation the rippled Si substrates exhibit an amorphous surface causing a polycrystalline material growth. This leads to a suppression of magneto-crystalline anisotropy leaving only morphology-induced anisotropy contributions. Here, a uniaxial magnetic anisotropy (UMA) was observed that aligns its easy axis with the ripple ridges, whereas its strength decays with increasing ripple wavelength for all materials. From thickness-dependent measurements two characteristic regions were determined with competing uniaxial volume and surface anisotropy contributions. Underlined by micromagnetic simulations a dominant volume contribution was found in the thin region accompanied by magnetic moments nearly following the surface corrugation. In the thick region the UMA is controlled by dipolar stray fields at the surface. In contrast to Si, ion eroded MgO keeps its crystal structure offering epitaxial growth of 10 nm thin single-crystalline Fe films. Consequently, a superposition of morphology-induced UMA and magneto-crystalline cubic anisotropy was observed. The direction of the ripple ridges is predetermined by the incident ion beam, which allows to freely orient the UMA’s direction with respect to the cubic anisotropy, offering a possibility for anisotropy engineering. In comparison to the planar reference case rippled magnetic films exhibit lower intrinsic and extrinsic relaxation contributions. For the final part, 30 nm Py was grown on rippled Si covering modulation wavelengths λ ranging from 27 to 432 nm. Using magnetic force microscopy and holography measurements the dipolar stray fields above and inside the magnetic layer were characterized. For λ ≥ 222 nm, the stray fields act as scattering centers for spin waves triggering two-magnon scattering (TMS). This causes an apparent line broadening generating distinct peaks in the frequency-dependent linewidth whose position can be tuned by altering λ. These effects are understood in the framework of a perturbation theory of spin waves in periodically perturbed films recently presented in the literature. Furthermore, the in-plane angular dependence of the linewidth revealed a two-fold symmetry, which is not present for vanishing TMS at small λ. / In Rahmen dieser Arbeit wurde der Einfluss der Morphologie eines dünnen ferromagnetischen Films auf dessen statische und dynamische Eigenschaften mittels breitbandiger ferromag- netischer Resonanz (FMR) untersucht. Durch Ionenstrahl-Erosion wurde die Oberfläche des verwendeten Substrats periodisch moduliert (Ripple), wobei die Wellenlänge der Modulation durch die Ionenenergie bestimmt ist. Dies ermöglicht die kontrollierte Herstellung rauer Oberflächen mit Wellenlängen zwischen wenigen zehn bis zu einigen hundert Nanometern. Werden auf diesen Oberflächen Filme abgeschieden, übernehmen diese die Modulation. Somit ergibt sich eine einfache und schnelle Untersuchungsmöglichkeit der magnetischen Filmeigenschaften in Hinblick auf die Morphologie. Das Ziel dieser Arbeit ist die Untersuchung von Morphologieeinflüssen auf die magnetische Anisotropie sowie FMR-Linienbreite. Im Vorfeld der magnetischer Untersuchungen wurde der bestehende FMR-Aufbau um einen Messmodus erweitert, sodass Messungen bei fester Mikrowellenfrequenz und gleichzeitigem Durchfahren eines externen magnetischen Feldes möglich wurden. Weiterhin wurde ein Softwarepaket für die Datenauswertung entwickelt. Beginnend mit dem Morphologieeinfluss auf die magnetische Anisotropie wurden 10 nm dünne Fe, Co und Ni81Fe19 (Permalloy ≡ Py) Filme auf periodisch moduliertem Si abgeschieden. Durch Versetzungen während der Ionenstrahl-Erosion und Bildung einer natürlichen Oxidschicht bildet sich bei den verwendeten Substraten eine amorphe Oberfläche, was zu polykristallinem Schichtwachstum führt. Dadurch wird die magneto-kristalline Anisotropie unterdrückt und morphologie-induzierte Beiträge bestimmen die Anisotropie. Beobachtet wurde eine induzierte uniaxiale magnetische Anisotropie (UMA), deren leichte Richtung sich entlang der Ripple-Wellenzüge ausrichtet. Mittels schichtdickenabhängigen Messungen wurden zwei charakteristische Regionen mit konkurrierender uniaxialer Volumen- und Oberflächenanisotropie ermittelt. Dabei ist die Volumenkomponente im Bereich dünner Schichten vorherrschend und die magnetischen Momente richten sich entlang der Oberflächenmodulation aus. Für dickere Schichten ist die UMA dahingegen durch dipolare Streufelder bestimmt. Die experimentellen Funde werden in beiden Bereichen durch mikromagnetische Simulationen untermauert. Im Gegensatz zu erodiertem Si behält MgO seine Kristallstruktur, was epitaktisch gewachsene, einkristalline Fe-Schichten von 10 nm Dicke ermöglicht. Folglich wurde eine Überlagerung aus induzierter und kristalliner Anisotropie beobachtet. Dadurch, dass die Richtung der Ripple durch die Richtung des Ionenstrahls während der Erosion vorgegeben wird, lässt sich die UMA frei gegen die kristalline Anisotropie drehen, was wiederum Möglichkeiten zur gezielten Beeinflussung der Anisotropie bietet. Im Hinblick auf die dynamischen magnetischen Eigenschaften führen Ripple zu einer Verringerung der intrinsischen und extrinsischen Relaxationsbeiträge. Für den letzten Teil der Arbeit wurde 30 nm dünnes Py auf Si-Ripple gewachsen, wobei ein Wellenlängenbereich von λ = 27 nm bis 432 nm abgedeckt wurde. Mit Hilfe von magnetischer Kraftmikroskopie und Holographie wurden die dipolaren Streufelder über und in den Filmen untersucht. Ab λ ≥ 222 nm ermöglichen diese dipolaren Felder eine Streuung von Spinwellen, sodass Zwei-Magnonen-Streuung (TMS) auftritt. Dies führt zu einer scheinbaren Linienverbreiterung und äußert sich durch einzelne Peaks in der frequenzabhängigen Linienbreite. Letztere lassen sich in ihrer Frequenzposition durch die Wellenlänge des Substrates beeinflussen und können mittels einer kürzlich in der Literatur veröffentlichten Störungstheorie für Spinwellen in periodisch gestörten Filmen erklärt werden. Weiterhin wurde in der winkelabhängigen Linienbreite eine zweifache Symmetrie beobachtet, welche durch die TMS hervorgerufen wird und folglich nicht bei kleinen Wellenlängen zu beobachten ist.

Durch die laterale Modifizierung der magnetischen Eigenschaften von austauschgekoppelten NiFe/IrMn-Schichten wurden weichmagnetische Schichten geschaffen, die sowohl neue statische als auch dynamische hybride Eigenschaften zeigen. Als laterale Strukturierungsmethoden wurden hierbei die lokale Oxidation sowie Ionenimplantation verwendet. Mit Hilfe dieser Verfahren ist es gelungen spezifische magnetische Domänenkonfigurationen mit Streifenstrukturen nominell antiparalleler Magnetisierungsausrichtung in die Schichten einzuprägen. In Abhängigkeit der Strukturorientierung sowie Streifenperiode konnte direkt das Ummagnetisierungsverhalten sowie die magnetische Resonanzfrequenz und Dämpfung der Schichten modifiziert werden. Die neuen dynamischen Eigenschaften wie z.B. eine hybride Resonanzfrequenz werden hierbei im Rahmen der Kopplung über dynamische Ladungen und die direkte Beeinflussung des effektiven Feldes des künstlich eingebrachten Domänenzustandes diskutiert. Die vorgestellten Ergebnisse belegen somit das große Potential der lateralen Magneto-Strukturierung zur Einstellung spezifischer statischer wie auch dynamischer Eigenschaften magnetisch dünner Schichten.