Dissertação (Mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. / Made available in DSpace on 2012-10-18T21:37:35Z (GMT). No. of bitstreams: 0Bitstream added on 2016-01-09T01:52:06Z : No. of bitstreams: 1 152470.pdf: 12888113 bytes, checksum: ae068c2443f701a8f5e68314c947cda0 (MD5) / Os objetivos deste estudo in situ foram avaliar as possíveis alterações quanto a microdureza e a morfologia superficial, de fragmentos de esmalte decíduo humano após a aplicação das soluções de diaminofluoreto de prata a 12%( Bioride) e 30% (Safluoraide di Walter), considerando-se quatro diferentes períodos de tempo de aplicação.

Resumo

Made available in DSpace on 2014-06-11T19:28:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2003-12-01Bitstream added on 2014-06-13T18:32:31Z : No. of bitstreams: 1 nassar_po_me_arafo.pdf: 1193015 bytes, checksum: 40452517ded346fcde49af240f22a5a6 (MD5) / A administração da CsA tem sido associada a osteopenia ou aumento na remodelação óssea. O objetivo do estudo foi avaliar o efeito da CsA no processo alveolar de ratos com doença periodontal induzida, por meio de análises sérica, estereométrica, histológica e histométrica. 24 ratos foram divididos em 4 grupos de 6 animais cada: Grupo 1: Controle; Grupo 2: ligadura ao redor do 1° molar inferior; Grupo 3: ligadura ao redor do 1° molar inferior e tratamento com CsA a 10mg/Kg de peso corporal/dia; Grupo 4: tratamento com CsA a 10mg/Kg de peso corporal/dia. Após 30 dias os animais foram sacrificados e os níveis séricos de cálcio e fosfatase alcalina foram mensurados. Após análise histológica, uma análise histométrica da junção cemento-esmalte até a crista óssea alveolar, da área de tecido ósseo e de reabsorção, mais espessura de cemento foi realizada conjuntamente com os parâmetros estereológicos: densidade volumétrica de osteoclastos multinucleados (Vo), osso alveolar (V-osso), medula (V-medula) e relação de superfície reabsorvida/superfície óssea (Sr/So) foram analisados na região mesial do osso alveolar. Diminuição significante foi observada no cálcio sérico nestes grupos que receberam terapia com CsA. Não foi observada mudança significante na fosfatase alcalina sérica. A terapia com CsA combinada com ligadura diminuiu o V-osso e aumentou o Vo, V-medula e Sr/So na superfície mesial dos primeiros molares inferiores, dados esses concordantes com a análise histométrica e comprovada pela leitura histológica. Além disso a espessura de cemento foi aumentada nos grupos tratados com CsA em relação aos não tratados. Entretanto, apesar da falta de efeitos diretos na altura do osso alveolar, a terapia com CsA intensifica o desequilíbrio da homeostasia do osso alveolar em ratos com doença periodontal induzida. / The administration of CsA has been associated with significant bone loss and increased bone remodeling. The present investigation was designed to evaluate the effects of CsA on alveolar bone of rats subjected to experimental periodontitis, using serum, stereometric and histological analysis. 24 rats were divided in groups 6 animal each: 1-control; 2-rats with ligature around the lower 1st.molars; 3-rats with ligature around the lower 1st.molars and were treated with 10mg/kg body weight/day CsA; 4-rats were treated with 10mg/kg body weight/day CsA. At the end 30 days, rats were sacrificed and calcium and alkaline phosphatase levels were measured. After histological processing, the histomorfometric analysis of the distance cemento-enamel junction and alveolar bone crest, bone area, eroded bone area and cemento surface together with stereological parameters: volume densities of multinucleated osteoclasts(Vo), alveolar bone(V-bone), marrow(V-marrow), and relation of eroded surface/bone surface(Es/Bs) were assessed at the mesial region of the alveolar bone. Significant decreases in serum calcium were observed in groups with CsA therapy. No significant changes in serum alkaline phosphatase were observed. The CsA therapy combined with ligature placement decreased the V-bone and increased the Vo, V-marrow and Es/Bs at the mesial surface and the results at the histologic and histomorfometric analysis showed the same combination and changes. Significant increase on the cemento height were observed in the CsA therapy groups. Therefore, in spite of the lack of a direct effect on the alveolar bone height, the CsA therapy intensified the imbalance of the alveolar bone homeostasia in a rat model of experimental periodontitis.

Resumo: O objetivo deste estudo foi investigar in vitro a capacidade de infiltracao bacteriana atraves da interface implante/conector protetico em sistemas de implantes dentarios de conformacao hexagonal. Para a obtencao dos isolados bacterianos, amostras de saliva e subgengivais foram coletadas de 4 pacientes voluntarios que apresentavam doenca periodontal, segundo aprovacao do Comite de Etica em Pesquisa responsavel. Apos o cultivo, os micro-organismos isolados foram caracterizados por meio de testes bioquimicos e selecionados para os ensaios in vitro. No estudo da infiltracao bacteriana in vitro foram utilizados um total de 34 modelos de implantes comerciais SYSTHEXR, com os respectivos conectores proteticos de conformacoes Hexagono Interno (HI) e Hexagono Externo (HE). Os implantes testados receberam 0,1 ƒÊL de inoculo contendo mistura dos micro-organismos previamente selecionados, Aggregatibacter actinomycetemcomitans e Streptococcus oralis, os quais foram introduzidos na regiao interna do implante. Os respectivos conectores proteticos foram adaptados e fechados seguindo as especificacoes do fabricante. As unidades foram incubadas em caldo BHI (Brain Heart Infusion) esterilizado durante periodo maximo de 20 dias, com amostragens diarias visando detectar a presenca de crescimento bacteriano por meio turbidez do meio de cultura. Quando na observacao de turbidez ou apos o periodo de incubacao, as amostras eram fixadas para observacao em Microscopia Eletronica de Varredura (MEV) com aumentos variando de 20X a 4000X. Ambos os modelos de conexoes apresentaram infiltracao bacteriana, em intensidades diferentes. Apos analise, houve correlacao estatisticamente significativa entre a media das maiores distancias na interface implante/conector protetico e o nivel infiltracao bacteriana. O melhor sistema de selamento entre as conformacoes estudadas, em relacao a infiltracao bacteriana, pareceu ser a conformacao Hexagono Externo.

Orientador: Prof. Dr. Antônio Adilson Soares de Lima / Dissertação (mestrado) - Universidade Federal do Paraná, Setor de Ciências da Saúde, Programa de Pós-Graduação em Odontologia. Defesa: Curitiba, 2017 / Inclui referências / Resumo: As bebidas alcoólicas são muito populares e consumidas mundialmente. Indivíduos que consomem habitualmente este tipo de bebida geralmente apresentam uma prevalência maior de erosão dentária. O objetivo deste trabalho foi avaliar o potencial erosivo in vitro de três diferentes bebidas alcoólicas comercializadas no Brasil no esmalte dentário bovino. Dentes bovinos foram seccionados em blocos de 4 mm x 4 mm cada, totalizando 144 amostras de esmalte. As amostras eram dividas em três grupos experimentais (cerveja, vodca e cachaça) e um controle (água destilada). Metade de cada amostra foi coberta com fita adesiva (lado controle) deixando exposto uma área de 2 mm x 2 mm (lado experimental). Cada amostra ficou imersa separadamente em 10 mL das respectivas bebidas por 1, 12 ou 24 horas (n=12). O pH, a concentração de cálcio e fósforo liberadas nas bebidas, a microdureza superficial e a topografia foram avaliadas. As bebidas alcoólicas avaliadas apresentaram um pH ácido, com exceção do pH inicial da vodca. Houve uma correlação negativa forte entre a microdureza e o tempo de exposição dos grupos experimentais (r Cerveja= -0,95/ r Vodca = -0,85/ r Cachaça = -0,92). Em todos os grupos experimentais houve diferença significativa da microdureza após 12 e 24 horas de exposição (p<0,001) quando se comparou a microdureza inicial com a final do lado experimental. Ocorreu o aumento da concentração de cálcio e fósforo nas bebidas com o passar do tempo nos grupos experimentais. Houve diferença estatisticamente significativa quando comparada a concentração desses dois minerais após 1 hora de exposição com os demais tempos para os grupos da vodca e da cachaça (Cálcio e Fósforo) e no grupo da cerveja apenas para a concentração de cálcio. A topografia do esmalte exposto às diferentes bebidas era mais irregular quando comparado ao do lado controle. Todas as bebidas alcoólicas avaliadas afetaram negativamente a estrutura do esmalte dentário in vitro, causando erosão dentária em diferentes padrões. Palavras-chave: Esmalte Dentário. Erosão Dentária. Desmineralização do Dente. Solubilidade do Esmalte Dentário.Técnicas in vitro. Bebidas Alcoólicas. / Abstract: Alcoholic beverages are very popular and consumed Worldwide. Individuals who regularly consume this type of drink usually have a higher prevalence of erosion. The objective of this study was to evaluate the in vitro erosive potential of bovine dental enamel from three different alcoholic beverages sold in Brazil. Bovine teeth were sectioned in blocks of 4 mm x 4 mm each, totaling 144 enamel samples. The samples were divided into three experimental groups (beer, vodka and ?cachaça?) and one control group (distilled water). Half of each sample was covered with adhesive tape (control side) leaving exposed an area of 2 mm x 2 mm (experimental side). Each sample was immersed separately in 10 mL of the respective beverages for 1, 12 or 24 hours (n=12). The pH, concentration of calcium and phosphorus lost in beverages, surface microhardness and enamel topography were evaluated. The alcoholic beverages evaluated had an acidic pH, except for the initial pH of vodka. There was a strong negative correlation between the microhardness and the exposure time of the experimental groups (r Beer= -0,95/ r Vodka = -0,85/ r Cachaça = -0,92). In all experimental groups, there was a significant difference in microhardness after 12 and 24 hours of exposure when the initial microhardness was compared with the final of the experimental side (p<0.001). The concentration of calcium and phosphorus increased in the beverages over time in the experimental groups. There was a statistically significant difference when the concentration of these two minerals was compared after 1 hour with the other times for the vodka and cachaça groups (Calcium and Phosphorus) and in the beer group only for the calcium concentration. The topography of the enamel exposed to the different beverages was more irregular when compared to the control side. All evaluated alcoholic beverages affected negatively the dental enamel structure in vitro, causing dental erosion in different patterns. Keywords: Dental Enamel. Tooth Erosion. Tooth Demineralization. Dental Enamel Solubility. In vitroTechniques. Alcoholic Beverages.

Objetivo: Comparar in vitro la rugosidad superficial de 2 resinas Bulk Fill utilizando dos sistemas de pulido de cauchos abrasivos: JOTA® (Suiza) (oxido de aluminio, carburo de silicio y silicona) y Optimize® (TDV) (Alemania) (silicona-oxido de aluminio). Materiales y métodos: Se utilizaron 60 especímenes de resina divididos en cuatro grupos G1: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos)/ sistema de pulido JOTA®(Suiza), G2: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos)/sistema de pulido Optimize® (TDV) (Alemania), G3: Aura Bulk Fill (SDI, Brasil) / sistema de pulido JOTA® (Suiza) y G4: Aura Bulk Fill (SDI, Brasil) /sistema de pulido Optimize® (TDV) (Alemania). Todos los especímenes fueron confeccionados con una matriz metálica (6mm x 4mm), donde se insertó las resinas con una espátula de resina (TNCIGFT2 Hu Friedy), y se fotoactivó con la lámpara Elipar LedTM (3M-ESPE), con una intensidad 1200 mW/cm2. Inmediatamente, se midió la rugosidad inicial de todos los grupos con el rugosímetro Mitutoyo SJ-210P (China). Posteriormente, se realizó los pulidos con los dos sistemas de cauchos según cada grupo, y se procedió a medir la rugosidad final. Resultados: Se encontró diferencia estadísticamente significativa en la rugosidad del grupo G1. Esta diferencia es mayor a la de los demás grupos evaluados, y que la menor diferencia en la rugosidad fue la encontrada en el grupo G2. Asimismo, se encontró diferencia estadísticamente significativa en la comparación realizada entre las resinas evaluadas y los sistemas de pulido evaluados. Conclusiones: La rugosidad superficial encontrada en la evaluación de la resina Bulk Fill Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos), con el sistema de pulido JOTA® (Suiza) presenta una menor rugosidad que la resina Aura Bulk Fill (SDI, Brasil) con los dos sistemas de pulido evaluados. / Objective: Comparison in vitro the superficial roughness of two Bulk Fill resins using two polishing systems of abrasives rubbers: JOTA® (Switzerland) (aluminum oxide, silicium carbide and silicone) and Optimize® (TDV) (Germany) (silicone- aluminum oxide). Materials and methods: Were used 60 resin specimens of resin divided in four groups G1: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA)/ polishing system JOTA®( Switzerland), G2: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA)/polishing system Optimize® (TDV) (Germany), G3: Aura Bulk Fill (SDI, Brazil) / polishing system JOTA® (Switzerland) y G4: Aura Bulk Fill (SDI, Brazil) / polishing system Optimize® (TDV) (Germany). All the specimens were made in a metal matrix (6mm x 4mm), were the resins were inserted with a resin spatula (TNCIGFT2 Hu Friedy), and fotoactivated with a lamp Elipar LedTM (3M-ESPE), with an intensity of 1200 mW/cm2. Immediately, the initial roughness of all groups is measured with the Roughness meter Mitutoyo SJ-210P (China). Subsequently, the polishing was executed out with the two rubber systems according to each group, and the final roughness was measured. Results: Statistically significant difference was found on the roughness of G1. This is even greater than all the groups evaluated, and that the smallest difference was in the G2 group. A statistically significant difference was found when comparing the two resins with the polishing systems evaluated. Conclusions: The surface roughness found in the evaluation of Bulk Fill Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA), with the JOTA® (Switzerland) polishing system presents the lower roughness than Aura Bulk Fill resin (SDI, Brazil) with the two polishing systems evaluated.

Objetivo: Comparar la microdureza y rugosidad superficial in vitro en resinas Bulk Fill después de un desafío abrasivo con pasta blanqueadora. Materiales y métodos: Noventa especímenes de resinas Bulk Fill Filtek™ Bulk Fill (FB), Tetric® N-Ceram Bulk Fill (TNC), Opus Bulk Fill (OBF) fueron divididos en 6 grupos (n=15). El desafío abrasivo in vitro fue realizado con un cepillo eléctrico Oral B y una solución de 3,3 ml de pasta dental / agua destilada por 30 s. La microdureza y rugosidad superficial inicial y final fue evaluada a los 15 y 30 días. Los datos fueron analizados mediante estadística descriptiva e inferencial (U Mann Whitney) Resultados: La rugosidad superficial a los 15 días fue: FB (0.09± 0.03µm/0.17± 0.10 µm); TNC (0.16 ± 0.09 µm/0.20± 0.09µm) y OBF (0.13±0.09 µm/0.18±0.06 µm). A los 30 días fue: FB (0.10 ± 0.05 µm/0.12 ±0.06 µm); TNC (0.07±0.04 µm/0.16±0.07µm) y OBF (0.11±0.03 µm/0.22±0.12 µm). Hubo diferencias estadísticamente significativas para FB (p=0.003) y OBF (p=0.0008) a los 15 días. A los 30 días, las resinas que presentaron un aumento significativo en los valores de rugosidad fueron OBF (p<0.0001) y TNC (p=0.0011). En la microdureza superficial, a los 15 días fue: FB (63.49±15.10 kg/mm2 / 65.53±8.21kg/mm2); TNC (47.67±6.20 kg/mm2 / 46.67±6.43 kg/mm2) y OBF (47.33±4.57 kg/mm2 / 45.4±4.32 kg/mm2). Existe una disminución a los 15 días en la resina OBF (p=0.0001). Conclusiones: Existe un aumento en la rugosidad superficial de las resinas Bulk Fill a los 15 y 30 días. Hubo una disminución en la microdureza superficial para la resina Opus Bulk Fill a los 15 días. Aim: To compare in vitro the microhardness and surface roughness in Bulk Fill composites after an abrasive challenge with whitening toothpaste. Materials and methods: Ninety specimens of Bulk Fill Filtek ™ Bulk Fill (FB), Tetric® N-Ceram Bulk Fill (TNC), Opus Bulk Fill (OBF) composite were divided into 6 groups (n = 15).The in vitro abrasive challenge was performed with an Oral B electric toothbrush and a 3,3 ml solution of toothpaste / distilled water for 30 s. The microhardness and initial and final surface roughness was evaluated at 15 and 30 days. The data were analyzed by descriptive and inferential statistics ¬(Mann Whitney U Test). Results: The surface roughness at 15 days was: FB (0.09 ± 0.03μm / 0.17 ± 0.10 μm); TNC (0.16 ± 0.09 μm / 0.20 ± 0.09μm) and OBF (0.13 ± 0.09 μm / 0.18 ± 0.06 μm). At 30 days it was: FB (0.10 ± 0.05 μm / 0.12 ± 0.06 μm); TNC (0.07 ± 0.04 μm / 0.16 ± 0.07μm) and OBF (0.11 ± 0.03 μm / 0.22 ± 0.12 μm). There were statistically significant differences for FB (p = 0.003) and OBF (p = 0.0008) at 15 days. After 30 days, the Bulk Fill composite that showed significant increases in the roughness values were OBF (p <0.0001) and TNC (p = 0.0011). The surface microhardness at 15 days was: FB (63.49 ± 15.10 kg / mm2 / 65.53 ± 8.21kg / mm2); TNC (47.67 ± 6.20 kg / mm2 / 46.67 ± 6.43 kg / mm2) and OBF (47.33 ± 4.57 kg / mm2 / 45.4 ± 4.32 kg / mm2). There was a decrease after 15 days in the OBF composite (p = 0.0001). Conclusions: There was an increase in the surface roughness of Bulk Fill composite at 15 and 30 days. There was a decrease in surface microhardness for the Opus Bulk Fill composite after 15 days. / Tesis

Objetivo: El objetivo del estudio es evaluar la resistencia a la tracción diametral y microdureza del cemento experimental y de materiales de restauración temporal utilizados en endodoncia (Óxido de zinc y Eugenol, Ionómero de vidrio convencional, Clip F® y Coltosol® F). Materiales y métodos: El estudio fue de tipo experimental in vitro. Se confeccionaron 11 muestras para cada cemento provisional, por cada propiedad a evaluar. Posteriormente, las muestras fueron almacenadas a temperatura ambiente por 24 h. Se midió la resistencia a la tracción diametral por compresión a través de la máquina de ensayo universal Instron® y la microdureza a través del Microdurómetro punta Vickers. Los resultados fueron analizados mediante estadística descriptiva univariada y para el análisis bivariado se realizó la prueba de Kruskal Wallis. Resultados: El cemento experimental obtuvo valores mayores de resistencia a la tracción diametral (0.77 MPa + 0.34) en comparación al Coltosol ® F (0.41 MPa + 0.13). Además, obtuvo mayores resultados de microdureza (9,45 HV + 0.66) en comparación al Coltosol ® F (6.50 HV + 0.61) y Óxido de zinc y Eugenol (5,62 HV + 0.61). Sin embargo, presentó menores valores de resistencia a la tracción diametral en comparación del ionómero de vidrio (24.46 + 4.55) y Clip F® (23.06 + 2.91). Asimismo, presento menores valores de microdureza comparado con el Ionómero de vidrio convencional (38.62 + 0.67) y Clip F® (26.03 + 1.07). En ambas propiedades se encontraron diferencias estadísticamente significativas (p<0.05). Conclusiones: El cemento experimental no demostró ser un buen material a comparación del Ionómero de vidrio convencional y el Clip F®. Sin embargo, obtuvo mejores valores que el Óxido de zinc y Eugenol, y Coltosol®; los cuales son empleados comúnmente en el ámbito odontológico a pesar de tener propiedades deficientes. / Objective: The objective of this study is to evaluate the diametral tensile strength and microhardness of an experimental cement and temporary restorative materials used in endodontics (Zinc Oxide and Eugenol, conventional glass ionomer, Clip F® and Coltosol® F). Material and methods: The sample of this in vitro study consisted in 11 samples were made from each provisional restorative materials, for each property to be evaluated. The samples were stored at room temperature for 24 h. The diametral tensile strength by compression was measured through the Instron® universal testing machine and the microhardness through the Vickers tip microdurometer. The results were analyzed using univariate descriptive statistics and the Kruskal Wallis test was performed for the bivariate analysis. Results: In this study, the experimental cement obtained higher values of diametral tensile strength (0.77 MPa + 0.34) in comparison of Coltosol® F (0.41 MPa + 0.13). In addition, it obtained higher microhardness results (9.45 HV + 0.66) in comparison of Coltosol ® F (6.50 HV + 0.61) and Zinc Oxide and Eugenol (5.62 HV + 0.61). However, lower diametral strength values were observed compared to glass ionomer (24.46 + 4.55) and Clip F® (23.06 + 2.91). Also, the microhardness values were lower compared to the conventional glass ionomer (38.62 + 0.67) and the Clip F® (26.03 + 1.07). In both properties, statistically significant differences were found (p <0.05). Conclusions: The experimental cement did not prove to be a good material compared to the conventional glass ionomer and the Clip F®. However, it obtained better results than Zinc Oxide and Eugenol, and Coltosol® F; which are commonly used in the dental field despite having poor properties. / Tesis

Objetivo: Comparar in vitro, la resistencia compresiva de cinco cementos ionómeros de vidrio: KetacTM Molar Easymix (3M ESPE), Gc Fuji IX GP, GC EQUIATM Fil (Gc corporation), Maxxion R (FGM), y KetacTM Universal HM (3M ESPE); tras 24 horas, 7 y 60 días de mezclado. Materiales y métodos: Se seleccionaron tres cementos de ionómero de vidrio de alta viscosidad: KetacTM Molar Easymix (3M ESPE), Gc Fuji IX GP, GC EQUIATM Fil (Gc corporation), y dos cementos de ionómero de vidrio convencionales: Maxxion R (FGM), KetacTM Universal HM (3M ESPE), indicados para el Tratamiento Restaurador Atraumático (TRA). La manipulación fue realizada en estricto cumplimiento con las indicaciones del fabricante. La unidad de análisis fue conformada por cilindros de ionómero de vidrio (2 mm de alto x 4 mm de diámetro), elaborados en una matriz metálica. Se crearon 15 especímenes por cada grupo de estudio, obteniendo un total de 225 especímenes. La prueba de resistencia a la compresión se dio mediante la máquina universal Instron® colocando los especímenes uno por uno verticalmente. La carga compresiva inicial tuvo una velocidad de 1mm/min hasta que la muestra se fracturase, y los resultados se registraron en megapascales (MPa). Resultados: El ionómero encapsulado GC EQUIATM Fil (Gc corporation) mostró mayores valores de resistencia compresiva a las 24 horas (299.80 MPa), mientras que a los 7 y 60 días fue el KetacTM Universal HM (3M ESPE), 77.04 MPa y 75.48 MPa, respectivamente. Por otro lado, existen diferencias significativas en la comparación de cada cemento de ionómero de vidrio en los tres tiempos de evaluación. Así como también, existen diferencias significativas en los tres tiempos evaluados: 24 horas: GC GC EQUIATM Fil (Gc corporation), a los 7 y 60 días KetacTM Universal HM (3M ESPE). Conclusión: El ionómero encapsulado GC EQUIATM Fil (Gc corporation) mostró mayores valores de resistencia compresiva a las 24 horas. Existen diferencias significativas en la comparación de cada cemento de ionómero de vidrio a lo largo de los tres tiempos, asimismo en cada tiempo de evaluación: 24 horas: GC EQUIATM Fil (Gc corporation), a los 7 y 60 días KetacTM Universal HM (3M ESPE). Objective: The aim of the present research was to compare in vitro the compressive strength of five glass ionomer cements: KetacTM Molar Easymix (3M ESPE), Gc Fuji IX GP, GC EQUIATM Fil (Gc corporation), Maxxion R (FGM), and KetacTM Universal HM (3M ESPE); after 24 hours, 7 days and 60 days after the mixing process. Materials and methods: Three high-viscosity glass ionomer cements were selected for the present in vitro study: KetacTM Molar Easymix (3M ESPE), Gc Fuji IX GP, GC EQUIATM Fil (Gc corporation), and also two conventional glass ionomer cements: Maxxion R (FGM), and KetacTM Universal HM (3M ESPE), recommended for the Atraumatic Restorative Treatment (ART). The mixing process was performed strictly respecting the manufacturer recommendations. The analysis unit was made of glass ionomer cylinders of 2mm high and 4mm in diameter, prepared with a metallic matrix. 15 samples were created for each study group, obtaining a total of 225 samples. The compressive strength was evaluated by Instron® universal machine placing the specimens one by one vertically, with a speed of 1mm / min until the sample fractured, and the results were registered in MPa. Results: The encapsulated ionomer GC EQUIATM Fil (Gc corporation) showed higher values of compressive strength at 24 hours (299.80 MPa), while at 7 and 60 days it was KetacTM Universal HM (3M ESPE), 77.04 MPa and 75.48 MPa, respectively. On the other hand, there are significant differences in the comparison of each glass ionomer cement in the three evaluation times. As well as, there are significant differences in the three times evaluated: 24 hours: GC EQUIATM Fil (Gc corporation), at 7 and 60 days KetacTM Universal HM (3M ESPE). Conclusion: The encapsulated ionomer GC EQUIATM Fil (Gc corporation) showed higher values of compressive strength at 24 hours. There are significant differences in the comparison of each glass ionomer cement over the three times, also at each evaluation time: 24 hours: GC EQUIATM Fil (Gc corporation), at 7 and 60 days KetacTM Universal HM (3M ESPE). / Tesis

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciencias da Saude / Made available in DSpace on 2012-10-16T01:02:06Z (GMT). No. of bitstreams: 0Bitstream added on 2016-01-08T15:40:16Z : No. of bitstreams: 1 98177.pdf: 3869763 bytes, checksum: 85f60c028a67589e4a18b026a095ada2 (MD5) / Este resumo avalia as diferenças de resistência à remoção de coroas da liga de cobre/alumínio cimentadas a fundações de amálgama, retidas com "amalgapin". Foram formados quatro grupos (A, B, C e D), com dez corpos de prova para cada grupo. Os corpos de prova utilizados foram molares de tamanho parecidos. Os grupos A e B sofreram desgastes parciais em todas as cúspides; no grupo C foram mantidas duas cúspides sem nenhum desgaste, e no grupo D deixou-se, somente, uma cúspide intacta. Os dentes foram preparados para receberem restaurações de amálgama, retidas com dois, três, quatro e seis pinos de amálgama, "amalgapin". Após isto, submeteu-se todos os corpos de prova a preparo para receberem coroas metálicas totais da liga cobre/alumínio. Os preparos tinham a altura cérvico-oclusal de 4 mm. Todos foram preparados com chanfrado até aprofundarem 2 mm na direção cervical em estrutura dentária. Os outros 2 mm eram confeccionados em amálgama (grupo A e B) e em amálgama/dentina (grupos C e D). Os quarentas corpos de prova foram cimentados, receberam coroas totais metálicas fundidas da liga cobre/alumínio e foram submetidos à força de tração para verificação da resistência direta das coroas e indireta das fundações retidas com pinos de amálgama "amalgapin". Através dos resultados obtidos nesta pesquisa foi possível concluir que: não houve diferença estatisticamenre significante com relação à influência do número de "amalgapin" na resistência à remoção de coroas totais metálicas cimentadas em fundações com coroas recontruídas com amálgama.