Submitted by MOISÉS DE SOUZA ARANTES NETO null (netomoises@yahoo.com.br) on 2016-09-17T18:56:55Z No. of bitstreams: 1 TESE_MOISES.pdf: 4715185 bytes, checksum: 9cf8bc8dfb49ce2c52b41de92483c1cf (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-09-21T16:55:10Z (GMT) No. of bitstreams: 1 arantesneto_ms_dr_ilha.pdf: 4715185 bytes, checksum: 9cf8bc8dfb49ce2c52b41de92483c1cf (MD5) / Made available in DSpace on 2016-09-21T16:55:10Z (GMT). No. of bitstreams: 1 arantesneto_ms_dr_ilha.pdf: 4715185 bytes, checksum: 9cf8bc8dfb49ce2c52b41de92483c1cf (MD5) Previous issue date: 2016-08-18 / O avanço tecnológico das últimas décadas proporcionou avanços significativos tanto na obtenção quanto nas aplicações dos vidros. Estes materiais possuem aspectos fundamentais, as quais os colocam como alternativas viáveis para aplicações na óptica, em espelhos primários de telescópios e até dispositivos fotônicos de fibras em escala nanométricas. Os vidros à base de óxido de telúrio são uma opção para substituir ou melhorar as características de sistemas vítreos convencionais como os vidros silicatos. As propriedades ópticas e estruturais dos vidros teluritos têm direcionado as pesquisas para diversas aplicações. Neste trabalho amostras de vidros teluritos foram obtidas a partir da matriz 80TeO2•(20 – x)WO3 •(x)Bi2O3(mol %) preparadas pelo método de fusão/resfriamento. Estas amostras foram caracterizadas térmica e estruturalmente como objetivo de estudar o controle e distribuição do tamanho dos cristais na matriz vítrea por meio de duas etapas de tratamento térmico, estudar os processos de nucleação e crescimento de cristais e também estudar a cristalização induzida no vidro. Usando duas etapas de tratamento térmico obteve-se vitrocerâmicas com distribuição uniforme dos tamanhos dos cristais. Com a técnica de análise térmica diferencial (ATD), associada ao método de Matusita, os resultados indicaram que as amostras foram nucleadas durante o recozimento usado para retirar as tensões mecânicas remanescentes do processo de fusão/resfriamento. A cristalização induzida foi estudada usando a difração de Raios–X (DRX). Os resultados possibilitaram observar a formação de duas fases cristalinas após o tratamento térmico na temperatura de 400°C, a fase δ–Te0,95W0,05O2,05e a fase δ–Bi2O3. Com os tratamentos posteriores também foram formadas as fases α–TeO2 e γ–TeO2.O estudo da cristalização induzida também foi acompanhado pela Espectroscopia Raman, que possibilitou a identificação dos modos vibracionais dos polimorfos do TeO2. / The technological advance of the last decades has provided significant advances both in obtaining and in the applications of glass. These materials have fundamental aspects, which put them as viable alternatives for applications in optics, in primary mirrors of telescopes and even photonic devices fibers in nanometric scale. The glasses of tellurium oxide base are an option to replace or enhance the characteristics of conventional vitreous systems such as silicate glasses. Optical and structural properties of tellurite glasses have directed research for various applications. In this work, samples of tellurite glasses were obtained from the matrix 80TeO2•(20 – x)WO3•(x)Bi2O3(mol%) prepared by the method of melting/cooling. These samples were characterized by thermal and structurally in order to study the control and size distribution of crystals in the glass matrix by two-step heat treatment, study the nucleation process and growth of crystals and study induced crystallization in the glass. Using two-step heat treatment was obtainedglass-ceramics with uniform distribution of crystal sizes. With the differential thermal analysis (DTA) associated with Matusita method, the results indicated that the samples were nucleated during annealing used to remove the remaining mechanical stresses of the melting/cooling process. The induced crystallization was studied using X-ray diffraction (XRD). It was possible to observe the formation of two crystalline phases after the heat treatment at 400°C, the δ–Te0,95W0,05O2,05 and δ–Bi2O3 phases.With subsequent treatments were also formed the α–TeO2 and γ–TeO2 phases. The induced crystallization of the study was accompanied by Raman spectroscopy, which allowed the identification of vibrational modes of polymorphs of TeO2.

Orientador: Keizo Yukimitu / Resumo: O avanço tecnológico das últimas décadas proporcionou avanços significativos tanto na obtenção quanto nas aplicações dos vidros. Estes materiais possuem aspectos fundamentais, as quais os colocam como alternativas viáveis para aplicações na óptica, em espelhos primários de telescópios e até dispositivos fotônicos de fibras em escala nanométricas. Os vidros à base de óxido de telúrio são uma opção para substituir ou melhorar as características de sistemas vítreos convencionais como os vidros silicatos. As propriedades ópticas e estruturais dos vidros teluritos têm direcionado as pesquisas para diversas aplicações. Neste trabalho amostras de vidros teluritos foram obtidas a partir da matriz 80TeO2•(20 – x)WO3 •(x)Bi2O3(mol %) preparadas pelo método de fusão/resfriamento. Estas amostras foram caracterizadas térmica e estruturalmente como objetivo de estudar o controle e distribuição do tamanho dos cristais na matriz vítrea por meio de duas etapas de tratamento térmico, estudar os processos de nucleação e crescimento de cristais e também estudar a cristalização induzida no vidro. Usando duas etapas de tratamento térmico obteve-se vitrocerâmicas com distribuição uniforme dos tamanhos dos cristais. Com a técnica de análise térmica diferencial (ATD), associada ao método de Matusita, os resultados indicaram que as amostras foram nucleadas durante o recozimento usado para retirar as tensões mecânicas remanescentes do processo de fusão/resfriamento. A cristalização induzida foi estudad... (Resumo completo, clicar acesso eletrônico abaixo) / Doutor

Les matrices vitreuses aluminosilicatées de lanthanides {SiO2 –Al2O3 – (CaO) – Y2O3 – La2O3} constituent, une matrice potentielle d’intérêt nucléaire, dans le cadre du stockage des déchets des actinides. Alors que de nombreuses études sont encore menées pour établir leurs propriétés macroscopiques (durabilité, mécanismes de vitrification, etc…), nous nous sommes attachés à décrire l’environnement proche des noyaux qui composent le réseau, c'est-à-dire leur structure à une échelle locale. Les verres aluminosilicatés sont constitués de tétraèdres d’aluminium et de silicium. Plus précisément, ils sont constitués d’entités Qn(mAl) silicium et d’entités qn(mSi) aluminium. Cependant, il est rare d’aboutir à une description en ces termes. La Résonance Magnétique Nucléaire haute résolution solide (RMN MAS 27Al et 29Si) est un des moyens d’y parvenir. Nous proposons ici le développement de séquences d’impulsions permettant l’identification de ces unités puis la description de leurs connectivités via leurs liaisons chimiques, basées sur le filtrage des cohérences MultiQuanta associées aux couplages scalaires J2 (Si-O-Si) et J2 (Si-O-Al). Cette approche RMN permet donc d’affiner la compréhension des réseaux aluminosilicatés quels qu’ils soient. Couplé à la spectroscopie RAMAN, elle a pu ensuite nous servir comme référence pour établir la structure et le comportement à long terme de ces matrices, suite à des expériences de lixiviation statique et d’irradiation a pratiquées au cyclotron du CEMHTI. / Aluminosilicate glasses of rare earth {SiO2 –Al2O3 – (CaO) – Y2O3 – La2O3} can be considered like a potential matrix of nuclear waste. This type of glass appears to be suitable matrix for the specific immobilization of trivalent actinides. Whereas many studies dealt with the macroscopic properties of these matrix (durability, mechanism, etc…), we investigate here the local environment surrounding the nucleus constituting the vitreous network. Thus, we can say that we investigate the local structure of the glass. Aluminosilicate glasses are constituted with silicon and aluminium tetrahedra. They are more especially based on a mixture of silicon Qn(mAl) and aluminium qn(mSi) units. Up to now, few experiments allow to describe the vitreous network with this terminology. A solution is the High Resolution Solid State NMR : 27Al and 29Si 1D or 2D MAS NMR experiments. We proposed here to provide and improve NMR pulse sequence to evidence NMR signatures of chemically bounded Al-O-Si and Si-O-Si molecular motifs and to establish an approximate picture of medium range order, thanks to 27Al/29Si heteronuclear and 29Si/29Si homonuclear NMR experiments associated to MultiQuantum filtering based on indirect scalar coupling J2 Al-O-Si/J2 (Si-O-Si) and. Combining RAMAN spectroscopy, Spin counting and MultiQuantum filtering allow establishing an approximate and new picture of medium range order in aluminosilicate compounds. Thus, they offer a reference to describe the changes in the structure and the long term behavior of our aluminosilicate glasses of rare earth, induced by static lixiviation and a irradiation practiced to cyclotron in CEMHTI laboratory .

Nesta tese, apresentamos três estudos envolvendo técnicas de ressonância paramagnética eletrônica (RPE) de onda contínua e pulsada nas bandas X e Q em vidros e nanocompósitos dopados com íons de metais de transição. O objetivo geral deste texto é evidenciar a complementariedade destas técnicas no estudo destes materiais. Os dois primeiros estudos focam-se em vidros e vitro-cerâmicas dopados com íons de metais de transição. O objetivo destes estudos é analisar o efeito dos tratamentos térmicos no espectro de RPE das amostras. O primeiro estudo trata de vidros fosfo-germanato dopados com íons de vanádio e os resultados de RPE de onda contínua mostram que, para a amostra sem tratamento térmico e para a amostra tratada em temperaturas menores do que 470 °C, apenas um sítio de vanádio é observado enquanto que, para as amostras tratadas com temperaturas acima de 470 °C, um segundo sítio de vanádio, mais distorcido do que anterior, aparece. Experimentos de ESEEM e HYSCORE observaram a interação entre os íons de vanádio e núcleos 31P próximos e pudemos estimar a máxima densidade de spin transferida pelo mecanismo through-bond e máxima distância média entre o íon paramagnético e os núcleos 31P. O segundo estudo trata de um vidro fluorosilicato dopado com íons Cu2+ e os resultados de RPE de onda contínua não mostram alterações relevantes no sítio paramagnético devido ao tratamento térmico. Experimentos de ESEEM e HYSCORE mostraram picos devido a interação desse íon com núcleos 19F, 207Pb, 111Cd e 113Cd. O terceiro estudo foca-se numa argila natural laminar contendo íons Cu2+ e moléculas de polioxietileno (PEO). O objetivo deste estudo é analisar a complexação do íon Cu2+ com as moléculas de PEO e moléculas de água no espaço interlaminar da argila. Os resultados de RPE de onda contínua não evidenciaram alterações na coordenação do íon Cu2+ através dos dois métodos de preparação propostos. Os experimentos de ESEEM E HYSCORE mostraram que, para o método onde o complexo PEO-Cu é inserido no espaço interlaminar da argila, o íon Cu2+ interage apenas com prótons em, pelo menos, duas conformações diferentes. Nossa hipótese é que observamos prótons tanto da molécula de PEO quanto de moléculas de água. No método onde moléculas de PEO são inseridas no espaço interlaminar da argila previamente preenchido com íons Cu2+, tal hipótese não pode ser feita. Ainda, observamos outro centro paramagnético nas amostras oriundo de vacâncias de oxigênio nas lâminas da argila. / This thesis contains three studies where X- and Q-Band continous-wave electron paramagnetic resonance (CW-EPR) and pulsed EPR techniques were applied in glasses and nanocomposites doped with transition metal ions. Our general goal is to show the complementarity of these techniques for the study of this materials. The first two studies focus on glasses and glass-ceramics doped with transition metal ions and the main goal is to analyse the effect of sample heat treatments on the EPR spectra. The first study focuses on phospho-germanate glasses and the CW-EPR results show that, for non-treated samples or for heat-treated samples at temperatures below 470°C, only one vanadium site is observed, while for samples heat-treated at higher temperatures a second, more ditorted site is produced. ESEEM and HYSCORE experiments observe the interaction between vanadium ions and near 31P nuclei. The maximum spin density transfer by the through-bond mechanism and maximum average distance between the two species could be estimanted. The second study focuses on fluorosilicate glasses doped with Cu2+ and the CW-EPR results show no relevant changes in the paramagnetic site upon heat treatment. ESEEM and HYSCORE experiments display peaks due to the interaction between Cu2+ ions and 19F, 207Pb, 111Cd e 113Cd nuclei. The third study focus on a natural bentonite clay containing copper ions and polioxiethilene (PEO) molecules. The main goal of this study is to analyze the complexation of the Cu2+ ions with the PEO and water molecules in the interlaminar space of the clays. CW-EPR results does not show any changes in the Cu2+ coordination caused by the two preparation methods proposed. ESEEM and HYSCORE experiments, however, showed that, for the method where the PEO-Cu complex is inserted in the interlaminar space, the paramagnetic ion interacts only with protons in at least two different conformations. Our hypothesis is that both protons from the PEO chain and water molecules are being observed. In the method where PEO molecules are inserted in the material, which was previosly filled with Cu2+ ions, no such assignment could be made. In addition, another paramagnetic center is observed and associated with oxigen vacancies in the sheets of the clay.

Este trabalho apresenta um estudo sobre a modificação e cristalização superficial dos sistemas vítreos 40BaO-45B2O3-15TiO2 (BBT) e 42BaO-42B2O3-16SiO2 (BBS) utilizando a radiação proveniente de um laser modulado de CO2. Três diferentes parâmetros experimentais foram avaliados: a potência do laser, o tempo de exposição à radiação e a presença de micropartículas da fase ?-BaB2O4 (?-BBO) na superfície da amostra. As modificações causadas pela exposição das amostras à radiação laser foram caracterizadas através das técnicas de perfilometria, microscopia óptica, espectroscopia micro-Raman e difração de raios X. De uma maneira geral, os resultados mostram que a escolha adequada da potência do laser e do tempo de exposição à radiação leva a uma modificação superficial ou a uma modificação seguida da cristalização superficial da região exposta a radiação. A presença de micropartículas da fase ?-BBO na superfície da amostras influi de maneira significativa no processo de modificação e cristalização superficial. A presença dessas micropartículas induziu a cristalização da fase ?-BBO com um relativo alto grau de orientação preferencial na direção (006), permitindo a observação visual do efeito de geração de segundo harmônico em algumas amostras. Estudos de micro-fotoluminescência mostraram que o íon Sm3+ quando adicionado a matriz vítrea BBT apresenta um alto grau de desordem mesmo em amostras cristalizadas. No entanto, para a matriz BBS, este estudo mostra uma possível incorporação do íon terra-rara na região cristalizada. / This work describes a study regarding the permanent modification and/or crystallization of 40BaO-45B2O3-15TiO2 (BBT) and 40BaO-45B2O3-16SiO2 (BBS) glass compositions when exposed to a continuous CO2 laser beam radiation. The effect of three experimental parameters was evaluated: the laser power, the radiation time exposure and the presence of micro-particles of the ?-BaB2O4 crystalline phase on the glass sample surface prior to radiation. The geometry of permanent modification and the crystallization process were characterized by using the perfilometry, optical microscopy, Micro-Raman spectroscopy and X-ray diffraction (XRD) techniques. The results show that the surface modification and crystallization can be controlled by a suitable choice of the laser power and radiation time exposure. In all samples, it was observed that the presence of ?-BaB2O4 micro-particles on the sample surface affects significantly equally the permanent modification and the crystallization process. The preferential orientation of the ?-BaB2O4 on the (006) plane direction allowed the observation of a relative high intense second harmonic generation effect. The micro-photoluminescence study shows that the Sm3+ ion in BBT glass sample present a high degree of disorder, even in the crystallized samples. On the other hand, when added to the BBS glass sample, it seems that the Sm3+ ions are incorporated onto the crystallized region.

Foram estudados compósitos poluméricos e vidros fluoroindatos utilizando as espectroscopias de Ressonância Magnética Nuclear (RMN) pulsada e Ressonância Paramagnética Eletrônica (RPE). O estudo de RMN do 1H nos compósitos baseado no polímero polióxido de etileno e partículas de carbono permitiu diferenciar as mobilidades das cadeias poluméricas e identificar as contribuições destas fases. A partir das medidas de RPE foi possível sugerir uma interpretação das interações entre as partículas de carbono nos compósitos. Nos vidros fluoroindatos foi estudado o processo de cristalização, sendo acompanhada sua influência na relaxação nuclear do 19F. A cristalização foi observada por RPE nos vidros dopados com Cu2+, Mn2+ e Gd3+, sendo verificadas as alterações locais causadas por este processo. / Polymeric composites and fluoroindate glasses were studied using pulsed Nuclear Magnetic Resonance (NMR) and Electron Paramagnetic Resonance (EPR) spectroscopies. Study of the composite formed by the polymer poly-ethylene oxide and carbon particles allowed us to distinguish the mobilities of polimeric chains and to identify the contributions from different phases. From EPR measurements it was possible to suggest an interpretation of the interactions between carbon particles in the composites. The main objective in the fluoroindate glasses study was to follow the crystallzation process. The 19F NMR measurements allowed to the observation of the influence of this process in the nuclear relaxation. The crystallization was also tracked by EPR spectroscopy in the doped glasses with the paramagnetic ions Cu2+, Mn2+ and Gd3+. This was accomplished by observing the local alterations caused by that process.

Há um crescente interesse científico e tecnológico voltado para compostos cristalinos de óxido de bismuto com óxidos de germânio, silício ou titânio, por exibirem propriedades eletro e magnetoópticas, fotocondutivas e piezoelétricas. Sistemas vítreos com propriedades similares a estes compostos são de alto interesse, devido ao baixo custo e facilidade no procedimento de preparação em relação aos monocristais. Este trabalho teve como finalidade analisar o efeito de adição de óxidos de boro e gálio, ao sistema binário composto por óxido de bismuto com óxidos de germânio. A amostra vítrea de composição 45BiO1.5:40BO1.5:15GeO2 (BBG-8), apresentou alta reprodutibilidade e estabilidade térmica (ΔT=132, Hr=0.34 e S=26.74), sendo assim, selecionada para o estudo da cristalização. As fases cristalizadas nesta amostra, durante tratamento térmico, foram determinadas por análises de difração de raios-X e medidas composicionais. Foram cristalizadas as fases Bi6B10O24 e Bi4Ge3O12, sendo a última, a fase de interesse para nosso estudo. Métodos térmicos foram utilizados no estudo da cristalização da fase Bi4Ge3O12, possibilitando a verificação da energia de ativação (≈ 54Kcal/mol) pelos métodos de Ozawa e Chen, e a direcionalidade do crescimento dos cristais (nmédio=1.12). A fim de obtermos mais informações a respeito de cristalização utilizamos óptica eletrônica. / The sillenite crystals, Bi12MO20 (M = Ge, Si, Ti), are interesting for applications such as optical memories, holography or optical phase conjugating devices. The eulytite crystals, Bi4M3O12, have been studied for their electro-optical, electromechanical and luminescence properties. These crystals am used as scintillators or, when doped with rare-earth elements, as laser materials. The study of glass systems, having properties similar to those crystals, is of high interest because of the lower cost and easier preparation procedures with respect to single crystals. The purpose of this work is the study of interaction of B2O3 and Ga2O3 with binary system Bi2O3-GeO2. The glassy sample BBG-8 (45BiO1.5:40BO1.5:15GeO2), was chosen far crystallition study, due to its high reproducibility and thermal stability. The presence of crystalline phases (Bi6B10O24 and Bi4Ge3O12), obtained after heat treatment, was investigated by powder X-ray diffraction and compositional analysis. The crystalline eulytite phase (Bi4Ge3O12) is an interest of our study. Thermal methods were used on the study of Bi4Ge3O12crystallization process of the sample BBG-8, and the value obtained, by means of Ozawa and Chen methods, was approximately 54Kcal/mol, and the directionality of crystal growth (n average) was equal to 1.12. To obtain further information on the crystallization mechanism we also performed microphotographic analysis.

Vidros metálicos maciços fazem parte de um novo grupo de materiais de características distintas das ligas metálicas convencionais. O processamento dessas ligas ainda não foi bem consolidado nos centros de pesquisa brasileiros devido à dificuldade de processamento. Este trabalho descreve o desenvolvimento de um sistema de síntese e coquilhamento para a obtenção de vidros metálicos maciços. O sistema foi avaliado quanto ao desempenho e repetibilidade das amostras. A liga Cu46Zr42Al7Y5, formadora de vidro, foi processada e analisada através da caracterização por difração de raios-X (DRX), calorimetria exploratória diferencial (DSC) e microscopia eletrônica de varredura (MEV). Foram obtidas duas amostras com estrutura totalmente amorfa em espessuras médias de até 1,5 mm e uma amostra com aproximadamente 5,5 mm de espessura amorfa. A temperatura de transição vítrea observada foi igual às relatadas na literatura científica. Assim, o sistema desenvolvido mostrou-se eficiente para o controle da atmosfera, resfriamento rápido das amostras e outras variáveis que são obrigatórias para o sucesso na formação de estruturas amorfas em ligas por fundição. / Bulk metallic glasses are new materials with different features in comparison with conventional metallic alloys. The processing techniques of such alloys are still not consolidated in Brazilian research centers because of inherent processing difficulties. This work describes the development of a system for the synthesis and casting of bulk metallic glassy samples. The system was evaluated by its performance and alloys repeatability. The Cu46Zr42Al7Y5 alloy was processed and analyzed for the formation of amorphous structure through X-ray diffraction (XRD), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). It was produced two samples with fully amorphous structure at average thickness of 1.5 mm and one sample reaching around 5.5 mm of fully glassy structure. The same glass transition temperature reported on scientific literature was found in the alloys processed in the present work. Thus, the system has shown efficiency on atmosphere control, sample quenching and others important variables that are, by default, necessary to succeed in amorphous structure formation.

Orientador: Lucila Chebel Labaki / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-08T09:29:44Z (GMT). No. of bitstreams: 1 Castro_AdrianaPetitodeAlmeidaSilva_D.pdf: 2534532 bytes, checksum: 4ea70ab9e519a13a5ddf61c29646f7b7 (MD5) Previous issue date: 2006 / Resumo: O desempenho térmico de uma edificação depende de fatores como implantação, orientação, materiais e componentes construtivos, que devem ser adequadamente definidos para diferentes condições climáticas. O edifício atua como mecanismo de controle das variáveis do clima, através de sua envoltória (paredes, piso, cobertura e aberturas) e dos elementos do entorno, e deve ser projetado de modo a proporcionar conforto e eficiência energética. Entre os componentes da construção, os vidros funcionam como um dos elementos de maior potencialidade de aquecimento interno. Devido à sua transparência à radiação solar, possibilitam facilmente o ingresso de grande parte dessa energia no ambiente. No presente rabalho estudou-se o comportamento de superfícies transparentes em fachadas, em situação real, através de medições em seis células-teste, de dimensões 2,00 x 2,50m. Analisou-se in loco o comportamento térmico de vidros, comercialmente disponíveis no mercado, cuja caracterização, do ponto de vista da transmissão espectral, já era conhecida através de técnica espectrofotométrica. Foram selecionados 14 tipos de vidros: cinco planos, quatro refletivos pirolíticos, três refletivos metalizados a vácuo e dois laminados, os quais foram instalados em aberturas de 1,00 X 1,20m nas células-teste, localizadas em fachadas com orientação norte e oeste. A análise foi realizada separadamente para as duas orientações. Avaliou-se o desempenho térmico de cada vidro, tendo o incolor, de espessura 4mm, como referência. A metodologia utilizada consistiu na aquisição de dados mensuráveis de parâmetros ambientais: temperaturas superficiais internas dos vidros, temperaturas de bulbo seco no ambiente interno e temperaturas do ar externo. O fator de ganho solar foi calculado a partir dos resultados de absortância dos diferentes materiais, obtidos por análise espectrofotométrica, e diferenças entre as temperaturas interna e externa. Os resultados mostram o alto ganho de calor através dos vidros planos, sendo o incolor o de pior desempenho térmico, com maior ganho, seguido pelo bronze, cinza e verde. Os vidros refletivos metalizados a vácuo apresentam o melhor desempenho térmico, dentre os materiais analisados, quando se tem como objetivo atenuar o ganho de calor e projetar edificações com menor consumo energético para refrigeração / Abstract: Thermal performance of buildings depends on several factors, such as implantation, orientation, materials and building components, which should be appropriately defined for different climate conditions. The building acts as a controller of the climatic variables, through the building envelope (walls, floor, roof and openings) and the nearby elements. Building design must provide indoor comfort and energy efficiency. Glazing easily allows the penetration of solar radiation into buildings, due to its transparency to solar radiation. So glasses must be carefully considered in building design, having in mind their potential for internal heating. In this work studies about the behavior of transparent façades, in real conditions, were carried out through measurements in six test-cells with dimensions 2,00 x 2,50m. Fourteen types of glasses were selected: five float glasses, four reflective glasses produced by pyrolitic process, three reflective ones obtained by vacuum metal deposition and two laminated glasses. Their spectral behavior was known from previous spectrophotometric studies. The glasses were installed in 1,00 X 1,20m openings in two façades facing north and west, separately. The colorless 4mm float glass was taken as reference. Internal surface temperatures of glasses, internal dry bulb temperatures and outdoor temperatures were collected. Solar gain factor was calculated on the basis of absortance values, obtained from spectrophotometrical nalysis, and temperature differences inside and outside the cells. Results show a high heat gain through float glasses, with the worst thermal behavior for the colorless one, followed by bronze, gray and green. Furthermore, reflective glasses obtained by vacuum metal deposition present the best thermal performance for the purpose of heat gain attenuation and to design buildings with the least energy consumption for cooling / Doutorado / Edificações / Doutor em Engenharia Civil

Neste trabalho foi investigada uma mudança na linha base observada em curvas de calorimetria exploratória diferencial em um trabalho onde microesferas de vidros aluminossilicatos contendo Ho foram estudados para a aplicação em radioterapia interna seletiva para o tratamento de carcinoma hepatocelular. Os vidros com composição nominal 53,7 SiO2 .10,5 Al2O3 . 35,8 MgO em %mol foram produzidos pelo método de fusão tradicional. As fritas obtidas foram moídas e peneiradas na faixa de 45 a 63 μm. O material foi utilizado para produzir microesferas pelo método de esferolização por queda gravitacional. O pó de vidro e as microesferas foram caracterizados por espectrometria de fluorescência de raios X, difração de laser, difração de raios X, calorimetria exploratória diferencial, análise térmica diferencial, termogravimetria, espectrometria de massa e microscopia eletrônica de varredura. Após as análises térmicas foram formadas pastilhas nos cadinhos que foram analisadas por microscopia eletrônica de varredura, difração de raios X e picnometria a gás He. A mudança na linha base foi associada ao processo de sinterização por fluxo viscoso e ocorre devido a diminuição do fluxo de calor detectado devido à retração da amostra. Outros processos como cristalização concomitante com a sinterização também foram estudados. / In this work a difference in the baseline in differential scanning calorimetry analyses, observed in a work where aluminosilicate glasses microspheres containing Ho were studied for application in selective internal radiotherapy as hepatocellular carcinoma treatment, was studied. The glasses with nominal composition 53,7 SiO2 .10,5 Al2O3 . 35,8 MgO in %mol were produced from traditional melting. The frits obtained were milled and sieved in the range of 45 a 63 μm. The material was used to produce glass microspheres by the gravitational fall method. The glass powder and the microspheres were characterized by X ray fluorescence spectrometry, laser diffraction, X ray diffraction, differential scanning calorimetry, differential thermal analysis, thermogravimetry, mass spectrometry, and scanning electron microscopy. After the thermal analyses, pellets were formed in the crucibles and were analyzed by scanning electron microscopy, X ray diffraction, and He picnometry. The difference in the baseline was associated to the viscous flow sintering process and happens because of the decrease in the detected heat flow due to the sample shrinkage. Other events as concurrent crystallization with the sintering process were also studied.