The concept of percolated perpendicular media (PPM) for magnetic data storage is expected to surpass the areal storage density of 1 Tbit in -², which is regarded as the fundamental limit of conventional granular CoCrPt:oxide based recording media. PPM consist of a continuous ferromagnetic thin film with densely distributed defects acting as pinning sites for magnetic domain walls. In this study, practical realizations of PPM were fabricated by the deposition of [Co/Pt]8 multilayers with perpendicular magnetic anisotropy onto nanoperforated templates with various perforation diameters and periods. The structural defects given by the templates serve as pinning sites for the magnetic domain walls within the [Co/Pt]8 multilayers. Magnetometry at both the integral and the local level was employed to investigate the influence of the template on the magnetization reversal and the domain wall pinning. It was found, that magnetic domains can be pinned at the ultimate limit, between three adjacent pinning sites. The coercivity and the depinning field, which both are a measure for the strength of the magnetic domain wall pinning, were found to increase with increasing perforation diameter. The size of magnetic domains within the magnetic film appeared not to depend solely on the diameter of the nanoperforations or on the period of the template, but on the ration between diameter and period. By means of micromagnetic simulations it was found, that the presence of ferromagnetic material within the pinning site given supports the pinning of magnetic domain walls, compared to a pinning site that is solely given by a hole in the magnetic thin film. Investigation of the evolution of the magnetization in magnetic fields smaller than the coercive field revealed, that the energy barrier against thermally induced magnetization reversal is sufficiently large to provide long-term (> 10 years) stability of an arbitrary magnetization state. This could also be qualitatively supported by micromagnetic simulations. Static read/write tests with conventional hard disk recording heads revealed the possibility of imprinting bit patterns into the PPM under study. The minimum bit pitch that could be read back thereby depended on the period of the nanoperforated template.

Gegenstand dieser Arbeit ist die Modifizierung von Oberflächen durch die Abscheidung alternierender Schichtsysteme auf Kohlenstofffasern und die Abscheidung von Aluminiumoxid auf organischen Membranen. Im ersten Kapitel wird das Vorgehen zur Abscheidung von organischen und anorganischen Schichten auf Kohlenstofffasern mittels der Atomlagenabscheidung und der oberflächeninitiierten Gasphasenabscheidung betrachtet. Dabei wird als Erstes auf die Abscheidung von Einzellagen und deren Optimierung eingegangen sowie im Anschluss auf die Übertragung dieser Parameter auf die Abscheidung von alternierenden Multilagensystemen. Mittels elektronenmikroskopischen-Untersuchungen, Rasterelektronenmikroskopie und energiedispersiver Röntgenspektroskopie, wird die Abscheidung der Materialien untersucht. Weiterhin können mit Hilfe von thermogravimetrischen Analysen die Oxidationsbeständigkeit der beschichteten Kohlenstofffasern sowie die einzelnen Schichtdicken bestimmt werden. Im zweiten Kapitel wird auf die Beschichtung von organischen Membranen eingegangen. Das Hauptaugenmerk liegt dabei auf der Beschichtung von nicht-hierarchisch und hierarchisch strukturierten Membranen mit Aluminiumoxid. Dafür werden die Atomlagenabscheidung und die Grenzflächenreaktion der Gasphase mit der im Feststoff gebundenen Flüssigphase angewendet. Unter Anwendung dieser beiden Verfahren ist es gelungen, dünne und gleichmäßige Schichten auf den Membranen abzuscheiden. Die Charakterisierung erfolgte mittels Rasterelektronenmikroskopie und energiedispersiver Röntgenspektroskopie. Zum Schluss wurden Filtrationsexperimente zum Vergleich der Stabilität und Durchflussraten der beschichteten mit den unbeschichteten Membranen durchgeführt.

Die thermoelektrische Energiekonversion auf der Basis des Seebeck-Effekts ist eine Methode zur direkten Erzeugung elektrischer Energie aus thermischer Energie. Für die wesentlichen anwendungsrelevanten Parameter Temperaturbereich, elektrische Leistung und Herstellungskosten sind Materialauswahl und Aufbau der TEG entscheidend. In der vorliegenden Arbeit wurden erstmalig thermoelektrische Oxidkeramiken in monolithischen TEG verwendet, die auf der Grundlage des transversalen thermoelektrischen Effekts arbeiten. Die TEG wurden mit industriell skalierbaren Keramiktechnologien hergestellt, untersucht und hinsichtlich ihrer Parameter detailliert theoretisch und experimentell bewertet. Als Modellsystem für die Materialien wurde La1-xSrxCuO4 in Kombination mit Ag bzw. Ag6Pd1 verwendet. Es konnte belegt werden, dass diese monolithischen TEG im Bereich kleiner elektrischer Leistungen eine vorteilhafte Alternative zu herkömmlichen longitudinalen thermoelektrischen Generatoren sein können.

Bei der quasi-simultanen Deposition massenselektierter Kohlenstoff- und Metallionen mit Energien jenseits thermischer Energien treten verschiedene Morphologien auf abhängig vom verwendeten Metall und den eingestellten Depositionsparametern. Die Abmessungen der auftretenden Strukturen liegen im Nanometerbereich. Die Materialien sind deshalb für zukünftige potentielle Anwendungen in verschiedenen Bereichen der Nanotechnologie von Interesse.Die vorliegende Arbeit beschäftigt sich mit der Strukturanalyse von kupfer-, silber-, gold- oder eisenhaltigen amorphen Kohlenstoffschichten. Dabei wurden unter anderem die Rutherford Rückstreuungsspektroskopie, die hochauflösende Transmissionselektronenmikroskopie und die energiedispersive Röntgenspektroskopie angewandt.Die dünnen Schichten weisen die folgenden Morphologien auf: Die kupferhaltigen Proben bestehen aus Kupfer-Nanopartikeln deren Durchmesser zwischen 3 und 9 nm variieren und gleichmäßig in der amorphen Kohlenstoffmatrix verteilt sind. Der mittlere Durchmesser steigt mit dem Kupfergehalt an. Die silberhaltigen Proben trennen sich in eine reine amorphe Kohlenstoffschicht mit Silberpartikeln an der Oberfläche. Sowohl die gold- wie auch die eisenhaltigen Schichten weisen eine Multilagenstruktur auf, wobei metallreiche Lagen mit erhöhter Partikeldichte durch amorphe Kohlenstofflagen voneinander getrennt sind. Die Lagenabstände sind im Falle der Gold-Kohlenstoffschichten bis zu ca. 15 nm, bei den Eisen-Kohlenstoffschichten um die 7 nm.Die Entstehung der verschiedenen Strukturen kann nicht auf herkömmlich Selbstorganisationseffekte, die auf Diffusion und Gleichgewichtsthermodynamik beruhen zurückgeführt werden. Stattdessen wurden ioneninduzierte Transportmechanismen, Sputtereffekte und die Stabilität kleiner Metallpartikel berücksichtigt, um die Strukturbildung zu modellieren.In der Literatur wurden in letzter Zeit ähnliche Multilagenstrukturen von Metall-Kohlenstoffschichten diskutiert, die durch Magnetronsputterdeposition hergestellt wurden. Erste Experimente wurden nun an einer RF Magnetronsputterdepositionsanlage durchgeführt um zu untersuchen, ob die zugrundeliegenden Mechanismen hier die gleichen sind wie im Falle der oben beschriebenen ionenstrahldeponierten Schichten. Bisher konnte jedoch keine Multilagenbildung bestätigt werden.

Theoretische Berechnungen sagen für tetragonal gedehntes Fe-Co eine hohe magnetokristalline Anisotropie voraus, wie sie für seltenerdfreie Dauermagnetwerkstoffe vorteilhaft wäre. In dieser experimentellen Arbeit werden epitaktische Fe-Co-Schichten strukturell und magnetisch charakterisiert. Zur Untersuchung der Dehnung in diesen Schichten eignen sich AuxCu100-x-Pufferschichten besonders, da über die Stöchiometrie (x) deren lateraler Gitterparameter eingestellt werden kann. Wird Fe-Co auf einer solchen Pufferschicht abgeschieden, erfolgt aufgrund dessen hoher elastischer Energie schon in den ersten Monolagen eine vollständige Relaxation der pufferinduzierten Dehnung. In ternären Fe-Co-X-Schichten, in denen kleine X-Atome (X = B, C oder N) Oktaederlücken besetzen, wird jedoch eine spontane tetragonale Dehnung c/a bis zu 1,05 beobachtet. Entlang der gedehnten c-Achse tritt eine uniaxiale magnetokristalline Anisotropie auf, die für B- oder C-Zulegierungen von 2 at% eine maximale Anisotropiekonstante von 0,4 MJ/m³ zeigt. Wird der X-Gehalt weiter erhöht, nehmen die Kristallinität der Schichten und die magnetische Anisotropie ab. Neben der magnetokristallinen Anisotropie des Schichtvolumens wird an den Fe-Co(-X)-Schichten eine hohe Grenzflächenanisotropie beobachtet. Der Beitrag der freien Oberfläche übersteigt den der Au-Cu-Grenzfläche dabei deutlich. / Theoretical calculations predict a high magnetocrystalline anisotropy for tetragonally strained Fe-Co, which would be beneficial for rare-earth free permanent magnet materials. In this experimental work, epitaxial Fe-Co films are investigated structurally and magnetically. AuxCu100-x buffer layers are very suitable to study the strain in these films since their in-plane lattice parameter can be tailored via the applied stoichiometry (x). However, when Fe-Co is deposited on such a buffer layer, the induced strain of the Fe-Co lattice relaxes completely within the first monolayers, due to its high elastic energy. In ternary Fe-Co-X films, where small atoms X like B, C or N occupy octahedral interstitial sites, a spontaneous strain c/a up to 1.05 is observed. A uniaxial magnetocrystalline anisotropy along the strained c axis appears. Their maximum anisotropy constant is 0.4 MJ/m³ for B or C contents of 2 at%. If the X content is further increased, the crystallinity and thus, the magnetic anisotropy of the films degrade. Together with the magnetocrystalline anisotropy of the films’ volumes, a high interface anisotropy is observed for the Fe-Co(-X) films. The contribution of the free surface clearly exceeds the contribution of the Au-Cu interface.

The concept of percolated perpendicular media (PPM) for magnetic data storage is expected to surpass the areal storage density of 1 Tbit in -², which is regarded as the fundamental limit of conventional granular CoCrPt:oxide based recording media. PPM consist of a continuous ferromagnetic thin film with densely distributed defects acting as pinning sites for magnetic domain walls. In this study, practical realizations of PPM were fabricated by the deposition of [Co/Pt]8 multilayers with perpendicular magnetic anisotropy onto nanoperforated templates with various perforation diameters and periods. The structural defects given by the templates serve as pinning sites for the magnetic domain walls within the [Co/Pt]8 multilayers. Magnetometry at both the integral and the local level was employed to investigate the influence of the template on the magnetization reversal and the domain wall pinning. It was found, that magnetic domains can be pinned at the ultimate limit, between three adjacent pinning sites. The coercivity and the depinning field, which both are a measure for the strength of the magnetic domain wall pinning, were found to increase with increasing perforation diameter. The size of magnetic domains within the magnetic film appeared not to depend solely on the diameter of the nanoperforations or on the period of the template, but on the ration between diameter and period. By means of micromagnetic simulations it was found, that the presence of ferromagnetic material within the pinning site given supports the pinning of magnetic domain walls, compared to a pinning site that is solely given by a hole in the magnetic thin film. Investigation of the evolution of the magnetization in magnetic fields smaller than the coercive field revealed, that the energy barrier against thermally induced magnetization reversal is sufficiently large to provide long-term (> 10 years) stability of an arbitrary magnetization state. This could also be qualitatively supported by micromagnetic simulations. Static read/write tests with conventional hard disk recording heads revealed the possibility of imprinting bit patterns into the PPM under study. The minimum bit pitch that could be read back thereby depended on the period of the nanoperforated template.

This work deals with the structural and dielectric properties of Bariumtitanate (BTO) / Strontiumtitanate (STO) superlattices. The investigations were carried during the research for a doctoral thesis on the IFW Dresden, Institute for Metallic Materials (under supervision of Prof. Schulz). These multilayers have been prepared on single crystalline STO of (100) and (111) orientated substrates. All films where grown in an epitaxial mode. Additional superlattices and Bariumstrontiumtitanate (BSTO) thin films on silicon substrates with platinum bottom electrodes have been prepared. Thereby, (111) fibre-textured polycrystalline superlattices were produced. According to our knowledge this result was achieved for the first time (is unique in the world at the moment). According to high resolution TEM investigations of (001) oriented superlattices multilayers with atomically thin interfaces without noticeable interdiffusion have been prepared. XRD pattern of a multilayer consisting of BTO and STO monolayers that have only a thickness adequate one unit cell of BTO respective STO confirm this assumption. Multilayers on (111) oriented STO substrates show a much higher interface roughness than (001) orientated films. Regarding to the examinations in this thesis it is suggested that the roughness is correlated with the reduction of internal stresses by deformation of the stack and not with interdiffusion between the monolayers. For electrical measurements the film thickness has been varied from 30 nm to 300 nm and the periodicity in the range from 0.8 nm to 20 nm. Additionally, BSTO films of equivalent thickness and integral chemical composition were produced. Dielectical measurements were carried out in the temperature range from 20 K to 600 K and hysteresis measurements were done. It has to be pointed out, that multilayers have always lower dielectrical performances then BSTO films. In all cases the dielectric constant (DC) decreases with decreasing film thickness. Multilayers of a small periodicity show the highest DC?s, decreasing with increasing monolayer thickness in all cases. The maximum of DC shifted with decreasing film thickness to higher temperatures thus correlating with an increase of the out of plane lattice parameter. In this paper the mismatch between the stack respectivly the BSTO layers and the substrate has widely been discussed. In the case of BSTO the dielectric data can be qualitatively explained with the theory of strained films, developed mainly by Pertsev, under the assumption of a strain gradient in the thin film. Strain effects do also play an important role in ferroelectric multilayers as well as size and coupling effects between the monolayers. An adequate theory for the description of the dielectric behaviour of the ferroelectric superlattice produced during this research does yet not exist. Some thesis where pointed out, which effects have to be essentially included in to a consistent theory of ferroelectric multilayer. Some practical tips are also given, how to prepare monolayers and superlattices with very high DC and exellent hysteretic behaviour. / Es wurden (001) und (111) orientierte symmetrische BTO/STO-Multilagen auf niobdotierten STO-Einkristallen abgeschieden. Hierbei wurde sowohl die Gesamtschichtdicke, als auch deren Periodizität variiert. Zum Vergleich wurden weiterhin Ba0.5Sr0.5TiO3-Mischschichten unterschiedlicher Dicke präpariert. Aus den HRTEM und XRD Untersuchungen kann geschlossen werden, dass alle erhaltenen Schichten sowohl phasenrein als auch perfekt biaxial texturiert sind. Im Falle der (001) orientierten Multilagen konnten atomar scharfe Grenzflächen zwischen Einzellagen erhalten werden, wobei sich die Einzellagendicke bis auf eine Monolage (0.4 nm) reduzieren lässt. Aus der Schichtdickenabhängigkeit von d(001), dem mittleren out-of-plane Gitterparameter der Schicht, wird geschlossen, dass die Schichten auf den STO-Einkristallen Spannungsgradienten in den Schicht-normalen besitzen und an der Grenzfläche zum Substrat am stärksten verspannt sind. Die (111) orientierten Multilagen auf den STO-Einkristallen zeigen gegenüber den Schichten auf den (100) orientierten STO-Einkristallen eine deutlich erhöhte Interfacerauhigkeit. Vermutet wird, dass dies einerseits durch die andere kristallographische Orientierung der Wachstumsnormalen bedingt ist, weil damit jeweils keine geschlossenen SrO- bzw. BaO- und TiO3-Lagen ausgebildet werden. Andererseits zeigen die TEM-Aufnahmen eine deutliche Zunahme der Welligkeit der Einzellagen mit wachsendem Abstand vom Substrat, die rein mechanischen Effekten zugeschrieben wird. Die Verwölbung der Einzellagen könnte damit der Reduzierung der mechanischen Energie innerhalb des Systems dienen, wobei die Netzebenen dem Verlauf der Einzellagen folgen. Auf platinbeschichteten Siliziumsubstraten konnten erstmals phasenreine (111) fasertexturierte Mischschichten und BTO/STO-Multilagen abgeschieden werden. Grundlage hierfür war die Optimierung des Pt/Ti/SiO2/Si Schichtsystems hinsichtlich seiner thermischen Stabilität bis zu 800°C. Die Textur der Schichten wird von der Platingrundelektrode übernommen und deren Rauhigkeit teilweise verstärkt. Eine mechanische Verwölbung der Einzellagen konnte hier nicht beobachtet werden. Für die elektrischen Messungen wurden auf allen Schichten etwa 50 nm dicke Platinelektroden durch eine Hartmaske mittels Elektronenstrahlverdampfung im Hochvakuum bei etwa 300°C aufgebracht. Anschließend wurden die Schichten an Luft getempert, um das Sauerstoffdefizit, dass sich bei der Elektrodenabscheidung einstellt, auszugleichen. Die elektrischen Messungen zeichnen sich durch den sehr großen untersuchten Temperaturbereich aus. Temperaturabhängige Messungen im Bereich von 30-600 K finden sich für ferroelektrische Dünnschichten sehr selten in der Literatur und stellen für BTO/STO-Multilagen ein Novum dar. Auch die biasabhängige und teilweise auch temperaturabhängige Messung der Kapazität der Multilagen (C-V-Messungen) ist bisher einmalig. Durch die temperaturabhängigen Hysteresemessungen wurden Einblicke in den elektrischen Polungszustand der Schichten erhalten. Dadurch wird eine sinnvolle Interpretation der ε(T)-Kurven erst möglich. Der Vorteil der Integration des Polarisationsstromes unter Verwendung einer Dreieckspannung als Messsignal besteht in der direkten physikalischen Aussage der Strom-Spannungskurven über die Schaltspannung der Schichten.

In the present work, the implications of ion irradiation on the magnetostatic and dynamic properties of soft magnetic Py/Ta (Py = Permalloy: Ni80Fe20) single and multilayer films have been investigated with the main objective of finding a way to determine their saturation magnetization. Both polar magneto-optical Kerr effect (MOKE) and vector network analyzer ferromagnetic resonance (VNA-FMR) measurements have proven to be suitable methods to determine µ0MS, circumventing the problem of the unknown effective magnetic volume that causes conventional techniques such as SQUID or VSM to fail. Provided there is no perpendicular anisotropy contribution in the samples, the saturation magnetization can be determined even in the case of strong interfacial mixing due to an inherently high number of Py/Ta interfaces and/or ion irradiation with high fluences. Another integral part of this work has been to construct a VNA-FMR spectrometer capable of performing both azimuthal and polar angle-dependent measurements using a magnet strong enough to saturate samples containing iron. Starting from scratch, this comprised numerous steps such as developing a suitable coplanar waveguide design, and writing the control, evaluation, and fitting software. With both increasing ion fluence and number of Py/Ta interfaces, a decrease of saturation magnetization has been observed. In the case of the 10×Py samples, an immediate decrease of µ0MS already sets in at small ion fluences. However, for the 1×Py and 5×Py samples, the saturation magnetization remains constant up to a certain ion fluence, but then starts to rapidly decrease. Ne ion irradiation causes a mixing and broadening of the interfaces. Thus, the Py/Ta stacks undergo a transition from being polycrystalline to amorphous at a critical fluence depending on the number of interfaces. The saturation magnetization is found to vanish at a Ta concentration of about 10–15 at.% in the Py layers. The samples possess a small uniaxial anisotropy, which remains virtually unaffected by the ion fluence, but slightly reduces with an increasing number of Py/Ta interfaces. In addition to magnetostatics, the dynamic properties of the samples have been investigated as well. The Gilbert damping parameter α increases with both increasing number of Py/Ta interfaces and higher ion fluences, with the former having a stronger influence. The inhomogeneous linewidth broadening ΔB0 increases as well with increasing number of Py/Ta interfaces, but slightly decreases for higher ion fluences. / In dieser Dissertation ist der Einfluss von Ionenbestrahlung auf die magnetostatischen und dynamischen Eigenschaften von weichmagnetischen Py/Ta-Einzel- und Multilagen (Py = Permalloy: Ni80Fe20) untersucht worden, wobei das Hauptziel gewesen ist, eine Methode zur Bestimmung der Sättigungsmagnetisierung zu finden. Sowohl polare magneto-optische Kerr-Effektmessungen (MOKE) als auch ferromagnetische Resonanzmessungen mittels eines Vektornetzwerkanalysators (VNA-FMR) haben sich als geeignet erwiesen, um µ0MS zu bestimmen, wobei das Problem des unbekannten effektiven magnetischen Volumens umgangen wird, welches bei der Verwendung von Techniken wie SQUID oder VSM auftreten würde. Unter der Voraussetzung, dass die Proben keinen senkrechten magnetischen Anisotropiebeitrag besitzen, kann die Sättigungsmagnetisierung selbst im Fall starker Grenzflächendurchmischung infolge einer großen Anzahl an Py/Ta-Grenzflächen und/oder Ionenbestrahlung mit hohen Fluenzen bestimmt werden. Ein weiterer wesentlicher Bestandteil dieser Arbeit ist die Konstruktion eines VNA-FMR-Spektrometers gewesen, welches vollautomatisiert ist, polare und azimutale Winkelabhängigkeiten messen kann und einen Magneten besitzt, der Proben, die Eisen beinhalten, sättigen kann. Von Grund auf beginnend umfasste dies zahlreiche Schritte wie z. B. die Entwicklung eines geeigneten koplanaren Wellenleiterdesigns sowie das Schreiben von Steuerungs-, Auswertungs- und Fitprogrammen. Mit steigender Fluenz und Zahl an Py/Ta-Grenzflächen ist eine Abnahme der Sättigungsmagnetisierung beobachtet worden. Im Fall der 10×Py-Proben findet diese bereits bei kleinen Fluenzen statt. Im Gegensatz dazu bleibt µ0MS der 1×Py- und 5×Py-Proben bis zu einer bestimmten Fluenz konstant, bevor sie sich dann umso schneller verringert. Die Bestrahlung mit Ne-Ionen verursacht eine Durchmischung und Verbreiterung der Grenzflächen. Infolgedessen erfahren die Py/Ta-Proben bei einer kritischen Fluenz, die von der Zahl der Grenzflächen abhängig ist, einen Phasenübergang von polykristallin zu amorph. Die Sättigungsmagnetisierung verschwindet ab einer Ta-Konzentration von etwa 10–15 Atom-% in den Py-Schichten. Die Proben besitzen eine kleine uniaxiale Anisotropie, die praktisch unbeeinflusst von der Fluenz ist, sich jedoch mit steigender Zahl an Py/Ta-Grenzflächen leicht verringert. Neben den statischen sind auch die dynamischen magnetischen Eigenschaften der Proben untersucht worden. Der Gilbert-Dämpfungsparameter α erhöht sich sowohl mit steigender Zahl an Py/Ta-Grenzflächen als auch mit höheren Fluenzen, wobei Erstere einen größeren Einfluss hat. Die inhomogene Linienverbreiterung ΔB0 nimmt ebenfalls mit steigender Zahl an Py/Ta-Grenzflächen zu, verringert sich jedoch bei größeren Fluenzen leicht.

No description available.

Der Einsatz nanostrukturierter Magnetmaterialien als Speicherschichten in Festplatten stellt ein vielversprechendes Konzept zur weiteren Erhöhung der erreichbaren Speicherdichten im Vergleich zu den heute eingesetzten granularen Medien dar. Für die Realisierung dieses Konzeptes ist eine detaillierte Kenntnis der Struktureigenschaften und deren Einfluss auf das magnetische Verhalten der einzusetzenden Schichten erforderlich. Für die vorliegende Arbeit wurden drei verschiedene magnetische Materialien ausgewählt und insbesondere mit elektronenmikroskopischen Methoden in struktureller Hinsicht untersucht. Dazu zählen ferromagnetische (FePt)(100-x)Cu(x) -Schichten, ferromagnetische [Co/Pt]n -Multilagen sowie ferrimagnetische Fe(100-x)Tb(x) -Schichten. Der Schwerpunkt der Untersuchungen lag dabei auf der Korrelation zwischen strukturellen und magnetischen Eigenschaften sowie im Einfluss der Nanostrukturierung auf das magnetische Verhalten der Schichten. In dieser Hinsicht wurden Aspekte der durch die Struktur bedingten magnetischen Anisotropie in Form von magnetokristalliner und Grenzflächenanisotropie betrachtet. Zudem wurde das Kopplungsverhalten zwischen einzelnen Strukturelementen in nanostrukturierten Schichten untersucht. Aufbauend auf die Untersuchung der drei genannten Materialien wurden [Co/Pt]n und Fe(100-x)Tb(x) ausgewählt zum Aufbau eines Systems mit zwei magnetischen Komponenten: Fe(80)Tb(20) / [Co/Pt]10. Die Untersuchungen konzentrierten sich dabei auf die Morphologie der Grenzfläche zwischen den beiden Bestandteilen und deren Einfluss auf den Exchange Bias, der in diesem System vorliegt.