Made available in DSpace on 2014-12-17T14:07:03Z (GMT). No. of bitstreams: 1 RobertoALS_TESE1.pdf: 2084680 bytes, checksum: 363c20f74fc941226fbec8734689dfb7 (MD5) Previous issue date: 2010-05-24 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Piau? state is a major producer of traditional red ceramic burning as bricks, tiles and ceramic tiles, with its main production center located in the city of Teresina. The state has large reserves of raw materials that can be used in the ceramic coating as clays, quartz, talc and carbonates. However, in the preparation of ceramic bodies using only a mixture of clays with different characteristics. The study aims to evaluate the effect of adding two types of carbonates in the ceramic semiporous mass coating produced in Piau? and then to verify the potential use of these carbonates as supplementary raw material product manufactured or the feasibility of obtaining a ceramic plate that meets the specifications for the porous coating. For this, were characterized the ceramic Piau? coating mass, a calcitic carbonate and a dolomitic, were made in the levels of 2, 4, 8, 16, and 32%. The masses were formed by pressing and burneds in two environments: a laboratory furnace (1080?C, 1120?C, 1140?C, and 1160?C) and an industrial furnace (1140?C). Then, following tests of linear shrinkage water absorption, apparent porosity, bulk density and flexural strength. Furthermore, the fired specimens were tested for their macrostructure and microstructure. The results showed the possibility of using the carbonate in ceramic mass flooring produced in Piau?, as added in small proportions improved dimensional stability and increased mechanical strength of ceramics pieces. It also proved itself possible to produce porous coating when added in higher levels / O Estado do Piau? ? um grande produtor de cer?micas tradicionais de queima vermelha como tijolos, telhas e revestimentos cer?micos, com seu principal p?lo produtivo localizado no munic?pio de Teresina. O Estado possui grandes reservas de mat?rias-primas que podem ser utilizadas no setor cer?mico de revestimento como argilas, quartzo, talco e carbonatos. Por?m, na elabora??o das massas cer?micas se utiliza uma mistura de argilas com caracter?sticas diferentes. O presente trabalho tem como objetivo avaliar o efeito da adi??o de dois tipos de carbonatos em uma massa cer?mica de revestimento semiporoso produzido no Piau?, e assim verificar a potencialidade da utiliza??o destes carbonatos como mat?ria-prima complementar do produto fabricado ou a viabilidade de se obter uma placa cer?mica que atenda as especifica??es para o revestimento poroso. Para isso, foram caracterizadas a massa cer?mica de revestimento piauiense, um carbonato calc?tico e outro dolom?tico, ambos oriundos de jazidas localizadas pr?ximas a Teresina - PI. As adi??es na massa cer?mica de cada carbonato foram feitas nos teores de 2, 4, 8, 16 e 32%. As massas foram conformadas por prensagem e queimadas em dois ambientes: forno de laborat?rio (1080?C, 1120?C, 1140?C e 1160?C) e forno industrial (1140?C). Em seguida, realizados ensaios tecnol?gicos de perda ao fogo, retra??o linear, absor??o de ?gua, porosidade aparente, massa espec?fica aparente e resist?ncia mec?nica ? flex?o. Al?m disso, as amostras queimadas foram avaliadas em sua macroestrutura e microestrutura. Os resultados mostraram a possibilidade de se utilizar os carbonatos na massa cer?mica do revestimento produzido no Piau?, pois adicionado em pequenas propor??es melhorou a estabilidade dimensional e aumentou a resist?ncia mec?nica das pe?as cer?micas. Tamb?m se mostrou vi?vel para produ??o de revestimento poroso quando adicionado em teores mais elevados

Made available in DSpace on 2014-12-17T14:57:40Z (GMT). No. of bitstreams: 1 OsvaldoCS.pdf: 1194235 bytes, checksum: da247435df103f473806af70be8f1c3e (MD5) Previous issue date: 2007-06-01 / The study of the physical and mechanic properties is an analysis of unquestioned importance on the production of the ceramic materials. In the region of the Rec?ncavo Baiano, there are ceramic and small brick factories, that still use rudimentary techniques, where the necessity of characterization of raw materials is denounced by the quality of the final product. The present work has for objective to study the behavior of the clay proceeding from the region of the Rec?ncavo, between the cities of Candeias and Cama?ari/Ba, with addition of 5, 10 and 15% by weight of brick scraps, trying to optimize the physic and mechanical properties of the final product, aiming a better possibility of being manufactured, mechanic resistance, low linear retraction and water absorption. The brick scraps and the clay were characterized by FRX, DRX, TG, ATD and the granulometric analysis. Samples for testing where prepared by uniaxial pressing at 25Mpa, in 60x20x5mm size. The evaluated technological properties were: linear retraction, water absorption, apparent porosity and flexural strength. The samples were burned in electric oven in the temperatures of 850?, 950? and 1050?C and compared its mechanical properties and the gresification. With addition of 15% by weight of brick scraps and burning at 900?-1000?C the samples showed properties superior to that clay / O estudo das propriedades f?sicas e mec?nicas ? uma an?lise de import?ncia inquestion?vel na produ??o dos materiais cer?micos. Na regi?o do Rec?ncavo Baiano, encontram-se cer?micas e pequenas olarias, que ainda utilizam t?cnicas rudimentares, onde a necessidade de caracteriza??o das mat?rias-primas ? denunciada pela qualidade do produto final. O presente trabalho tem por objetivo estudar o comportamento da argila proveniente da regi?o do Rec?ncavo Baiano, compreendida entre os munic?pios de Candeias e Cama?ari, com adi??o de 5, 10 e 15% em peso de rejeitos cer?micos, procurando otimizar as propriedades f?sico-mec?nicas do produto final, visando uma melhor trabalhabilidade, resist?ncia mec?nica e baixas retra??o linear e absor??o de ?gua. O rejeito cer?mico e a argila foram caracterizados por FRX, DRX, TG, ATD e analise granulom?trica. Foram preparados corpos-de-prova com dimens?es de 60x20x5mm, por prensagem uniaxial a 25MPa. As propriedades tecnol?gicas avaliadas foram: retra??o linear, absor??o de ?gua, porosidade aparente e resist?ncia mec?nica ? flex?o. Os corpos foram sinterizados em forno resistivo nas temperaturas de 850?, 950? e 1050?C e comparadas suas propriedades mec?nicas e a gresifica??o. Obteve-se para os corpos com incorpora??o de 15% em peso de rejeitos cer?micos, propriedades superiores as da argila, nas temperaturas entre 900? e 1000? C

Made available in DSpace on 2014-12-17T14:07:00Z (GMT). No. of bitstreams: 1 RenataPAS_DISSERT.pdf: 2030872 bytes, checksum: b1f1838ae20a1cf415bfd28d267a0046 (MD5) Previous issue date: 2011-10-17 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / The effluents released by the textile industry have high concentrations of alkali, carbohydrates, proteins, in addition to colors containing heavy metals. Therefore, a filter was prepared aiming primarily to the removal of color. In order to prepare this filter, rice hulls and diatomite were used, which have in their structure, basically amorphous hydrated silica. The silica exists in three crystalline forms: quartz, tridymite and cristobalite. In accordance with the above considerations, this study was divided into two stages; the first corresponds to the preparation of the filter and the second to carry out the tests in the effluent/filter in order to verify the efficiency of the color removal. First, the raw material was subjected to a chemical analysis and XRD, and then the diatomite was mixed, via humid, with a planetarium windmill with 20 %, 40 %, 60 % and 80 % of rice husk ash. To the mixture, 5 % carboxymethylcellulose (CMC) was added as a binder at room temperature. The samples were uniaxially compacted into metallic matrix of 0.3 x 0.1 cm? of area at a pressure of 167 MPa by means of hydraulic press and then sintered at temperatures of 1,000 ?C, 1,200 ?C and 1,400 ?C for 1 h and submitted to granulometry test using laser, linear retraction, water absorption, apparent porosity and resistance to bending, DTA, TMA and XRD. To examine the pore structure of the samples scanning electron microscope (SEM) was used. Also tests were carried out in a mercury porosimeter to verify the average size of the pores and real density of the samples. In the second stage, samples of the effluent were collected from a local industry, whose name will be preserved, located in Igap?, in the State of Rio Grande do Norte - RN. The effluent was first pretreated before filtration and then subjected to a treatment of flotation. The effluent was then characterized before and after filtration, with parameters of color, turbidity, suspended solids, pH, chemical and biochemical oxygen demand (COD and BOD). Thus, through the XRD analysis the formation of cristobalite α in all samples was observed. The best average size of pore was found to be 1.75 μm with 61.04 % apparent porosity, thus obtaining an average 97.9 % color removal and 99.8 % removal of suspended solid / Os efluentes liberados pela ind?stria t?xtil possuem altas concentra??es de ?lcalis, carboidratos, prote?nas, al?m de corantes contendo metais pesados. Assim, foi produzido um filtro visando principalmente ? remo??o da cor. Para sua obten??o foi usado a casca de arroz carbonizada e a diatomita, que possuem basicamente s?lica amorfa hidratada na estrutura. A s?lica apresenta-se sob tr?s formas cristalinas: Quartzo, tridimita e cristobalita. De acordo com as considera??es citadas, este estudo foi divido em duas etapas, a primeira etapa corresponde ? obten??o do filtro e a segunda parte a realiza??o dos ensaios no efluente/filtro, tendo em vista verificar a efici?ncia da remo??o da cor. Primeiramente, a mat?ria-prima foi submetida a uma an?lise qu?mica e de DRX, em seguida a diatomita foi misturada, via ?mido, em um moinho planet?rio com 20 %, 40 %, 60 % e 80 % de cinza de casca de arroz. Foi adicionada a mistura 5 % de carboximetilcelulose (CMC) como ligante a temperatura ambiente. Os corpos de prova foram compactados uniaxialmente em matriz met?lica de 0,3 x 0,1 cm? de ?rea a uma press?o de 167 MPa atrav?s de prensa hidr?ulica e posteriormente sinterizados em temperaturas de 1.000?C, 1.200?C e 1.400?C por 1 h e submetidos a ensaios de granulometria a laser, retra??o linear, absor??o de ?gua, porosidade aparente, resist?ncia ? flex?o, DTA, DTG e DRX. Para analisar a estrutura de poros das amostras foi utilizado um microsc?pio eletr?nico de varredura (MEV) e foi realizados ensaios em um poros?metro de merc?rio para verificar o tamanho m?dio dos poros e densidade real das amostras. Na segunda etapa, foi feito a coleta das amostras do efluente de uma empresa, cujo nome ser? preservado, alocada em Igap? RN. O efluente sofreu um pr?-tratamento antes da filtra??o sendo assim submetido a um tratamento de flota??o. O efluente foi ent?o caracterizado antes e depois da filtra??o, com par?metros de cor, turbidez, s?lidos suspensos, pH, demanda qu?mica e bioqu?mica de oxig?nio (DQO e DBO). Assim, atrav?s da analise de DRX, foi observado forma??o de cristobalita α em todas as amostras. O melhor tamanho m?dio de poro encontrado foi de 1,75 μm com porosidade aparente foi 61,04 %, obtendo assim uma remo??o de cor m?dia de 97,9 % e remo??o de s?lido suspensos de 99,8 %

Made available in DSpace on 2014-12-17T14:07:02Z (GMT). No. of bitstreams: 1 PriscyllaCAGpdf.pdf: 2221940 bytes, checksum: 25a80df63d59147dc3816d52fcd0e65b (MD5) Previous issue date: 2009-08-21 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / This work main objective is to study the use of bricks in barium X-rays rooms in order to contribute to the optimization of shielding rooms diagnosis. The work was based on experimental measurements of X-ray attenuation (40 to 150 kV), using ceramic seal bearing the incorporation of barium sulfat (BaSO4). Different formulations were studied in three different firing temperatures and evaluated for incorporation in the ceramic body. The composition of 20% of barite processed at a temperature of 950 ? C showed better physical and mechanical properties, is considered the most suitable for the purpose of this work. Were produced bricks sealing composition formulated based on that presented the best technological features. These blocks were tested physically as a building material and wall protective barrier. Properties such as visual, deviation from the square, face flatness, water absorption and compressive strength were evaluated for all the blocks produced. The behavior of this material as attenuator for X-rays was investigated by experimental results which take into account mortar manufacturers barium through the different strains and compared with the reference material (Pb). The simulation results indicated that the ceramic block barium shows excellent properties of attenuation equivalence lead taking into account the energy used in diagnostic X-ray / Este trabalho tem por finalidade principal estudar a utiliza??o de blocos cer?micos baritados em salas de radia??o X, visando contribuir para a otimiza??o da blindagem de salas de diagn?stico. O trabalho foi baseado em medidas experimentais de atenua??o da radia??o X (40 a 150 kV), empregando material cer?mico de veda??o contendo a incorpora??o de sulfato de b?rio (BaSO4). Diferentes formula??es foram estudadas em tr?s temperaturas de queima diferentes e avaliadas as incorpora??es na massa cer?mica. A composi??o de 20% de barita processada a temperatura de 950?C, apresentou melhores propriedades f?sicas e mec?nicas, sendo considerada a mais adequada para a proposta deste trabalho. Foram produzidos blocos cer?micos de veda??o baseados na composi??o formulada que apresentou melhores caracter?sticas tecnol?gicas. Estes blocos foram testados fisicamente como material construtivo de parede e barreira protetora. Propriedades como caracter?sticas visuais, desvio com rela??o ao esquadro, planeza das faces, absor??o de ?gua e resist?ncia ? compress?o foram avaliadas para todos os blocos produzidos. O comportamento deste material como atenuador para a radia??o X foi investigado por meio de resultados experimentais que levaram em considera??o fabricantes de argamassas baritadas atrav?s das diferentes tens?es e comparado com o material de refer?ncia (Pb). Os resultados obtidos nas simula??es indicaram que o bloco cer?mico baritado demonstra ?timas propriedades de atenua??o em equival?ncia ao chumbo levando-se em conta as energias usadas em raios X diagn?stico

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-01-27T12:19:00Z No. of bitstreams: 1 CassioFreireCamara_TESE.pdf: 3299867 bytes, checksum: 6633fd802189d4523b85b604decfb3c5 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-01-27T15:44:27Z (GMT) No. of bitstreams: 1 CassioFreireCamara_TESE.pdf: 3299867 bytes, checksum: 6633fd802189d4523b85b604decfb3c5 (MD5) / Made available in DSpace on 2017-01-27T15:44:27Z (GMT). No. of bitstreams: 1 CassioFreireCamara_TESE.pdf: 3299867 bytes, checksum: 6633fd802189d4523b85b604decfb3c5 (MD5) Previous issue date: 2016-05-20 / A alvenaria estrutural ? um m?todo construtivo muito antigo, no qual as alvenarias das edifica??es t?m a funcionalidade estrutural al?m de veda??o, e foi o primeiro m?todo utilizado pelo homem para constru??o de abrigos permanentes. Esta modalidade executiva possibilita uma maior economia nos custos das edifica??es, entretanto exige um maior controle na confec??o e aplica??o dos blocos. Outro par?metro importante diz respeito ao p? de brita, res?duos dos britadores, pois n?o possuem utilidade em qualquer cadeia produtiva e assim, s?o depositados em aterros ou na natureza, degradando a qualidade do meio ambiente. Baseado neste ensejo, o reaproveitamento deste res?duo, aliado ? ind?stria ceramista, possibilita m?tuos benef?cios, pois diminui o estoque do rejeito dos britadores, elimina o impacto ambiental, reduz os custos de confec??o dos blocos e eleva a resist?ncia das alvenarias. Dentro deste contexto, este trabalho tem como objetivo estudar o comportamento do ?bloco cer?mico h?brido?, verificando os efeitos da incorpora??o do p? de brita na massa argilosa do bloco cer?mico sob as exig?ncias da Norma NBR-15270. As mat?rias primas foram coletadas em Caic?/RN, no caso do p? de brita, e em Assu/RN, no caso da argila, tendo sido formuladas incorporando os percentuais de 0%, 5%, 10% e 15% de res?duo. As amostras foram sinterizadas ? temperatura de 990?C, ? taxa de aquecimento de 5?C/min com isoterma de uma hora e submetidas a ensaios tecnol?gicos, como retra??o linear, absor??o de ?gua, porosidade aparente e resist?ncia ? compress?o. O resultado significativo obtido foi com a formula??o de 10% de res?duo incorporado, o qual elevou a resist?ncia ? compress?o dos blocos em m?dia de 26,41% e at? 58%. / The structural masonry is a very old construction method, where the walls of the buildings have structural functionality beyond seal, and it was the first method used by man to build permanent shelters. This executive mode enables greater savings in the buildings costs, but requires more control in the manufacture and application of the blocks. Another important parameter concerns the gravel dust, waste crushers, because they have no utility in any production chain and so are landfilled or deposited in nature, degrading the quality of the environment. Based on this, the reuse of this waste, together with ceramics industry, enables mutual benefits because it reduces the stock of waste crushers, eliminates the environmental impact, reduces the manufacturing costs of the blocks and increases the strength of masonry. Within this context, this work aims to study the behavior of the "hybrid ceramic block" by checking the effects of the incorporation of gravel dust in the clay mass of the ceramic block in the light of the requirements of the NBR-15270. The raw materials were collected in Caic?/RN, in the case of the gravel dust, and Assu/RN, in the case of clay, and were formulated incorporating the percentage of 0%, 5%, 10% and 15% residue. The samples were sintered at 990?C temperature, the heating rate of 5?C/min with an isothermal hour and subjected to technological testing as linear shrinkage, water absorption, porosity and compressive strength. The best result obtained in the study was 10% corporate residue which increased the compressive strength of the blocks on average 26,41% and up to 58%.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-07-03T13:37:23Z No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-07-06T16:06:51Z (GMT) No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) / Made available in DSpace on 2017-07-06T16:06:51Z (GMT). No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) Previous issue date: 2016-05-30 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Os materiais cer?micos, tais como a alumina (Al2O3) e o cobalto (Co), apresentam caracteristicas relevantes para aplica??o como ferramentas de corte, e dentre estas se destacam a elevada dureza e o alto ponto de fus?o. No entanto, a sua aplica??o ? limitada pela sua baixa tenacidade e baixa resist?ncia mec?nica. Desta forma, a fim de aumentar a tenacidade do material, mantendo-se as elevadas propriedades mec?nicas, alguns metais, como por exemplo, o cobalto (Co), t?m sido usados na tentativa de se produzir um material mais tenaz. Neste trabalho, estudouse o efeito da moagem de alta energia e da adi??o de (%p.) Co na densifica??o e microestrutura, assim como, nas propriedades mec?nicas do composto Al2O3-Co. Os p?s-particulados (Al2O3 e Co), com percentuais de 5 e 20%p. de cobalto, foram mo?dos em um moinho planet?rio durante 50 horas, e amostras de p?s foram coletadas nos intervalos de 2, 10, 15, 20, 30,40 e 50 horas. Os p?s mo?dos foram caracterizados por difra??o de raios-X (DRX), an?lises particulom?tricas, microscopia eletr?nica de varredura (MEV); e compactados em uma matriz cil?ndrica sob uma press?o uniaxial de 100 MPa. Posteriormente, os compactados a verde foram sinterizados em um forno resistivo nas temperaturas de 1200 a 1500 ?C, por 60 minutos, sob uma atmosfera de arg?nio com taxa de aquecimento de 10?C/min. Os corpos de prova sinterizados foram caracterizados por DRX, MEV e energia dispersiva (EDS). A densidade foi medida usando o m?todo geom?trico (massa/volume), e os melhores valores foram obtidos para as amostras sinterizadas a temperatura de 1500 ?C, sendo a densidade relativa igual a 78 %, seguido das sinterizadas a temperaturas de 1350?C e 1300?C, que apresentaram as respectivas densidades 68 %, e 62 %. / Ceramic materials, such as alumina (Al2O3) and cobalt (Co), present characteristics like high hardness and the high melting point for application as cutting tools. However, its application is limited because of its low toughness and low mechanical strength. Thus, in order to increase the toughness and maintaining the high mechanical properties, some metals such as cobalt (Co) have been used. In this work, the effect of the high energy milling and different amount of Co on densification, microstructure and mechanical properties of the Al2O3-Co compound were studied. The particulate powders (Al2O3 and Co), with 5 and 20 wt% of cobalt, were milled in a planetary milling for 50 hours, and powder mixture samples were collected at the intervals of 2, 10, 15, 20, 30, 40 and 50 hours. The milled powders were characterized by X-ray diffraction (XRD), particulometric analyzes, scanning electron microscopy (SEM); And compacted in a cylindrical matrix under a uniaxial pressure of 100 MPa. Subsequently, green compacts were sintered in a resistance furnace at 1200 to 1500 ?C with holding time of 60 minutes under an argon atmosphere with a heating rate of 10 ?C/min. The sintered samples were characterized by XRD, SEM and EDS. Density was measured using the geometric method (mass/volume), and the best values were obtained for the samples sintered at 1500 ?C with relative density of 78% compared with sample sintering at 1350 and 1300 ?C which presented relative densities of 68% and 62% respectively.

Made available in DSpace on 2014-12-17T14:07:08Z (GMT). No. of bitstreams: 1 EricaNMGP_TESE.pdf: 149123 bytes, checksum: d13a2a775b94d69d52d9e403106d2117 (MD5) Previous issue date: 2011-06-01 / The development of activities the of oil and gas sector have promoted the search for suitable materials for cementing oil wells. In the state of the Rio Grande do Norte, the integrity of the cement sheath tends to be impaired during steam injection, a procedure necessary to increase oil recovery in reservoirs with low-viscosity oil. The geopolymer is a material that can be used as alternative cement, since it has been used in the production of fire-resistant components, building structures, and for the control of toxic or radioactive residues. Geopolymers result from condensation polymer alkali aluminosilicates and silicates resulting three-dimensional polymeric structures. They are produced in a manner different from that of Portland cement, which is made an activating solution that is mixed with geopolymer precursor. Among the few works studied allowed us to conclude that the pastes prepared with metakaolin as precursor showed better performance of its properties. Several studies show the addition of waste clay as a means of reducing cost and improving end of the folder properties. On this basis, the goal is to study the influence of the addition of ceramic waste in geopolymer paste. To develop the study of rheology tests were carried out, filtered, thickening time, compressive strength, free water, specific gravity and permeability, according to the American Pretoleum Institute (API). The results for all formulations studied show that the folders have high mechanical strength to a light paste; low filtrate volume, absence of free water, very low permeability, slurry, consistent with a light paste, and thickening time low that can be corrected with the use of a retardant handle. For morphological characterization, microstructural, physical, chemical and thermal tests were carried out by XRD, MEV, DTA, TG, FTIR. In the trial of XRD, it was found that geopolymer is an amorphous material, with a peak of crystalline kaolinite. In tests of TG / DTA, revealed the presence of a significant event, which represents the mass loss related to water, and also observed the reduction of weight loss by increasing the concentration of ceramic waste. In the trial of MEV, we found a uniform matrix without the presence of other phases. In the trial of FT-IR, we observed the presence of the band related to water. From all results it was determined that the optimum concentration range of use is between 2.5 and 5% of waste ceramic / O desenvolvimento das atividades do setor de petr?leo e g?s tem promovido a busca de materiais mais adequados para cimenta??o de po?os de petr?leo. No estado do RN, a integridade da bainha cimentante tende a ser prejudicada durante a inje??o de vapor, procedimento necess?rio para aumentar a recupera??o do petr?leo em reservat?rios com ?leo de alta viscosidade. O geopol?mero ? um material que pode ser utilizado como cimento alternativo, uma vez que vem sendo empregado na produ??o de componentes resistentes ao fogo, na constru??o de estruturas, e para o controle de res?duos t?xicos ou radioativos. Geopol?meros resultam da condensa??o polim?rica de aluminosilicatos e silicatos alcalinos originando estruturas polim?ricas tridimensionais. S?o produzidos de uma maneira distinta daquela do cimento Portland, onde ? feita uma solu??o ativadora que ? misturada ao precurssor geopolim?rico. Dentre os trabalhos estudados, alguns permitiram-nos concluir que as pastas preparadas com metacaulim como precursor apresentaram melhor desempenho de suas propriedades. V?rios estudos apresentam a adi??o de res?duos argilosos como forma de redu??o do custo final e melhoria das propriedades da pasta. Com base nisso, o objetivo do trabalho ? estudar a influ?ncia da adi??o de rejeito cer?mico em pastas geopolim?ricas. Para o desenvolvimento do estudo foram realizados testes de reologia, filtrado, tempo de espessamento, resist?ncia ? compress?o, ?gua livre, peso espec?fico e permeabilidade, de acordo com o American Pretoleum Institute (API). Os resultados encontrados para todas as formula??es demonstram que as pastas estudadas apresentam resist?ncia mec?nica elevada para uma pasta leve; volume de filtrado baixo; aus?ncia de ?gua livre; permeabilidade muito baixa; pasta flu?da, coerente com uma pasta leve; e tempo de espessamento baixo, que pode ser corrigido com a utiliza??o de um retardador de pega. Para caracteriza??o morfol?gica, microestrutural, f?sico-qu?mica, qu?mica e t?rmica, foram realizadas caracteriza??es por DRX, MEV, DTA, TG, FT-IR. No ensaio de DRX, verificou-se que o geopol?mero ? um material amorfo, com um pico cristalino de caulinita. Nos testes de TG/DTA, foi observado a presen?a de um evento significativo, que representa a perda de massa referente a ?gua, sendo observado tamb?m a redu??o da perda de massa com o aumento da concentra??o de rejeito cer?mico. No ensaio de MEV, encontrou-se uma matriz uniforme e nos espectros de FT-IR, observou-se a presen?a da banda referente ? ?gua. A partir de todos os resultados foi poss?vel determinar que a faixa de concentra??o ?tima de rejeito cer?mico para uso em pastas geopolim?ricas ? entre 2,5 e 5 %

Made available in DSpace on 2014-12-17T14:07:17Z (GMT). No. of bitstreams: 1 OsvaldoCS_TESE.pdf: 5419870 bytes, checksum: 262730b1c0403826588e3ca7137507e0 (MD5) Previous issue date: 2013-07-19 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The production of waste from urban and industrial activities is one of the factors of environmental contamination and has aroused attention of the scientific community, in the sense of its reuse. On the other hand, the city of Salvador/Ba, with approximately 262 channels, responsible for storm water runoff, produces every year, by the intervention of cleaning and clearing channels, a significant volume of sediments (dredged mud), and thus an appropriate methodology for their final destination. This study aims to assess the influence of incorporation of these tailings in arrays of clay for production of interlocked block ceramic, also known as ceramic paver. All the raw materials from the metropolitan region of Salvador (RMS) were characterized by x-ray fluorescence, x-ray diffraction, thermal analysis (TG and TDA), particle size analysis and dilatometry. With the use of statistical experimental planning technique, ternary diagram was defined in the study region and the analyzed formulations. The specimens were prepared with dimensions of 60x20x5mm?, by uniaxial pressing of 30 MPa and after sintering at temperatures of 900?, 1000? and 1100?C the technological properties were evaluated: linear shrinkage, water absorption, apparent porosity, apparent specifies mass, flexural rupture and module. For the uniaxial compression strength used cylindrical probe body with ? 50 mm. The standard mass (MP) was prepared with 90% by weight of clay and 10% by weight of Channel sediment (SCP), not being verified significant variations in the properties of the final product. With the incorporation of 10% by weight of manganese residue (PFM) and 10% by weight of the Ceramic waste (RCB) in the mass default, in addition to adjusting the plasticity due to less waste clay content, provided increased linear firing shrinkage, due the significant concentration of K2O, forming liquid phase at low temperature, contributing to decreased porosity and mechanical resistance, being 92,5 MPa maximum compressive strength verified. After extract test leachate and soluble, the piece containing 10% of the PFM, was classified as non-hazardous and inert material according to NBR10004/04 ABNT. The results showed the feasibility on using waste, SCP, RCB and PFM clay mass, at temperatures above 900?C, paver ceramic production, according to the specifications of the technical standards, so that to exceed the 10% of the PFM, it becomes imperative to conduct studies of environmental impacts / A produ??o de res?duos provenientes das atividades urbanas e industriais ? um dos fatores de contamina??o ambiental e tem despertado aten??o da comunidade cientifica, no sentido do seu reaproveitamento. Por outro lado, a cidade do Salvador/Ba, com aproximadamente 262 canais, respons?veis pelo escoamento de ?guas pluviais, produz todo ano, pela necessidade de interven??o de limpeza e desobstru??o de canais, um volume significativo de sedimentos (lama dragada), impondo dessa forma uma metodologia adequada para sua destina??o final. Este trabalho tem como objetivo avaliar a influ?ncia da incorpora??o desses rejeitos em matrizes de argila para produ??o de bloco intertravado cer?mico, tamb?m conhecido como paver cer?mico. Todas as mat?rias primas oriundas da Regi?o Metropolitana de Salvador (RMS) foram caracterizadas por fluoresc?ncia de raios -X, difra??o de raios -X, analise t?rmica (TG e TDA), analise granulom?trica e dilatometria. Com a utiliza??o da t?cnica estat?stica de planejamento experimental, foi definida em diagrama tern?rio a regi?o de estudo e as formula??es analisadas. Foram preparados os corpos de prova com dimens?es de 60x20x5mm3, por prensagem uniaxial de 30 MPa e, ap?s sinteriza??o nas temperaturas de 900?, 1000? e 1100?C, as propriedades tecnol?gicas avaliadas foram: retra??o linear, absor??o de ?gua, porosidade aparente, massa especifica aparente, m?dulo de ruptura ? flex?o. Para a resist?ncia ? compress?o uniaxial utilizou-se o corpo de prova cil?ndrico com ? de 50mm. A massa padr?o (MP) foi preparada com 90% em peso de argila e 10% em peso do sedimento de canais (SCP), n?o sendo verificadas varia??es significativas nas propriedades do produto final. Com a incorpora??o de 10% em peso do res?duo de mangan?s (PFM) e 10% em peso do rejeito cer?mico (RCB) na massa padr?o, al?m do ajuste da plasticidade, em fun??o de menor teor de argilominerais dos res?duos, proporcionou aumento da retra??o linear de queima, devido a significativa concentra??o de K2O, formando fase liquida em baixa temperatura, contribuindo para diminui??o da porosidade e aumento da resist?ncia mec?nica, sendo 92,5 MPa a m?xima resist?ncia ? compress?o verificada. Ap?s teste do extrato lixiviado e solubilizado, a pe?a contendo 10% do PFM, foi classificada como material n?o perigoso e inerte segundo NBR10004/04 da ABNT. Os resultados mostraram viabilidade na utiliza??o dos res?duos SCP, RCB e PFM em massa argilosa, em temperaturas acima de 900?C, para produ??o de bloco intertravado, paver cer?mico, de acordo com as especifica??es das normas t?cnicas, de forma que, para teores superiores a 10% do PFM, torna-se imperativo a realiza??o de estudos de impactos ambientais

Made available in DSpace on 2014-12-17T14:07:21Z (GMT). No. of bitstreams: 1 ClawsioRCS_TESE.pdf: 6209957 bytes, checksum: 4a85a36be678a5c36d937dd4cb67fe7c (MD5) Previous issue date: 2014-04-28 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Doped lanthanum chromite ( LaCrO3 ) has been the most common material used as interconnect in solid oxide fuel cells for high temperature ( SOFC-HT ) that enabling the stack of SOFCs. The reduction of the operating temperature, to around 800 ? C, of solid oxide fuel cells enabled the use of metallic interconnects as an alternative to ceramic LaCrO3, From the practical point of view, to be a strong candidate for interconnect the material must have good physical and mechanical properties such as resistance to oxidizing and reducing environments, easy manufacture and appropriate thermo-mechanical properties. Thus, a study on the physic-mechanical interconnects La0,8Sr0,2Cr0,92Co0,08O3 ceramics for SOFC -AT obtained by the method of combustion , as well as thermo-mechanical properties of metallic interconnects (AISI 444) covered with La0,8Ca0,2CrO3 by deposition technique by spray-pyrolysis fuel cells for intermediate temperature (IT-SOFCs). The La0,8Sr0,2Cr0,92Co0,08O3 was characterized by X -ray diffraction(XRD) , density and porosity , Vickers hardness (HV) , the flexural strength at room temperature and 900 ?C and scanning electron microscopy (SEM). The X -ray diffraction confirmed the phase formation and LaCrO3 and CoCr2O4, in order 6 GPa hardness and mechanical strength at room temperature was 62 MPa ceramic Interconnector. The coated metal interconnects La0,8Ca0,2CrO3 passed the identification by XRD after deposition of the film after the oxidation test. The oxidative behavior showed increased resistance to oxidation of the metal substrate covered by La0,8Ca0,2CrO3 In flexural strength of the coated metal substrate, it was noticed only in the increased room temperature. The a SEM analysis proved the formation of Cr2O3 and (Cr,Mn)3O4 layers on metal substrate and confirmed the stability of the ceramic La0,8 Ca0,2CrO3 film after oxidative test / A cromita de lant?nio (LaCrO3) dopada tem sido o material mais utilizado como interconector nas pilhas a combust?vel de ?xido s?lido de alta temperatura(PaCOS-AT), possibilitando o empilhamento(stack) da PaCOS. A redu??o da temperatura de opera??o, em torno de 800 ?C, das pilhas a combust?vel de ?xido s?lido, tornou poss?vel o uso de interconectores met?licos como alternativa aos LaCrO3 cer?micos. Do ponto de vista pr?tico para o material ser forte candidato a interconector deve ter boas propriedades f?sicas e mec?nicas, como resist?ncia a ambientes oxidantes e redutores, f?cil fabrica??o e propriedades termo-mec?nicas adequadas. Por este motivo realizou-se um estudo sobre as propriedades fisico-mec?nicas de interconectores de La0,8Sr0,2Cr0,92Co0,08O3 cer?mico para PaCOS-AT obtido pelo m?todo da combust?o, como tamb?m sobre as propriedades termo-mec?nicas de interconectores met?licos (AISI 444) recobertos com La0,8Ca0,2CrO3 pela t?cnica de deposi??o por spray-pir?lise para Pilhas a combust?vel de temperatura intermediaria (PaCOS-TI). A La0,8Sr0,2Cr0,92Co0,08O3 foi caracterizada por meio de difra??o de raios X (DRX), densidade e porosidade, dureza Vickers (HV), resist?ncia mec?nica a flex?o na temperatura ambiente e a 900?C e microscopia eletr?nica de varredura (MEV). A difra??o de raios X comprovou a forma??o das fases LaCrO3 e CoCr2O4, dureza na ordem de 6 GPa e resist?ncia mec?nica a temperatura ambiente de 62 MPa do interconector cer?mico. A avalia??o das fases formadas no interconector met?lico recoberto com La0,8Ca0,2CrO3 tanto na deposi??o quanto ap?s o ensaio oxidativo foi realizado por DRX. O comportamento oxidativo evidenciou o aumento da resist?ncia a oxida??o do substrato met?lico recoberto por La0,8Ca0,2CrO3. Na resist?ncia mec?nica a flex?o do substrato met?lico recoberto, notou-se o aumento apenas na temperatura ambiente. Com aux?lio do MEV comprovou-se a forma??o das camadas de Cr2O3 e (Cr,Mn)3O4 sobre o substrato met?lico e confirmou-se a estabilidade do filme cer?mico de La0,8Ca0,2CrO3 ap?s o ensaio oxidativo

Made available in DSpace on 2014-12-17T14:08:39Z (GMT). No. of bitstreams: 1 PauloDPS_DISSERT_partes_autorizadas.pdf: 366490 bytes, checksum: 3e5abdd24789d0e82844edffadbb1a3e (MD5) Previous issue date: 2010-03-05 / Petr?leo Brasileiro SA - PETROBRAS / Steam injection is the most used thermal recovery method of oil nowadays because of the high degree of development of the technique that allows high recovery factors. However, injection of superheated steam into the reservoir affects the entire structure of the well, including the cemented layer that presents a retrogression of compressive strength and increases the permeability due to formation of more crystalline and denser phases at temperatures above 110 ?C. These changes result in failures in the cement that favor the entrance of formation fluids into the annulus space resulting in unsafe operations and restrictions in the economic life of the well. But the strength retrogression can be prevented by partial replacement of cement by silica-based materials that reduce the CaO/SiO2 ratio of cement slurries changing the trajectory of the reactions, converting those deleterious phases in phases with satisfactory mechanical strength and permeability. The aim of this study was to evaluate the behavior of a ceramic waste material rich in silica in partial and total substitution of a mineral additive used to fight the strength retrogression of cement slurries subjected to high temperatures. The evaluation was made by compression, X-ray diffraction (XRD) and thermogravimetry (TG/DTG). The samples were submitted to a cycle of low temperature (38 ?C) for 28 days and a cycle of low temperature followed by exposure to 280 ?C and 1000 psi by 3 days. The results showed that slurries with additions of up to 30% of the waste material are not enough to prevent the strength retrogression, while slurries with additions of the waste material combined with silica flour in various proportions produced hydrated products of low Ca/Si ratios that maintained the compressive strength at satisfactory levels / A inje??o de vapor ? o m?todo t?rmico de recupera??o de ?leo mais utilizado atualmente em virtude do alto grau de desenvolvimento da t?cnica que permite elevados fatores de recupera??o. No entanto, inje??o de vapor superaquecido no reservat?rio faz com que toda estrutura do po?o seja afetada pela alta temperatura, inclusive a camada cimentada, que apresenta uma retrogress?o da resist?ncia ? compress?o e um aumento da permeabilidade devido ? forma??o de fases mais cristalinas e mais densas sob temperaturas superiores a 110 ?C. Essas altera??es d?o origem a falhas no cimento que propiciam a entrada de fluidos da forma??o para o espa?o anular, resultando em uma opera??o insegura e limita??es na vida econ?mica do po?o. Por?m, a retrogress?o da resist?ncia pode ser evitada atrav?s da substitui??o parcial do cimento por materiais a base s?lica, os quais reduzem a raz?o CaO/SiO2 das pastas de cimento, modificando, assim, a trajet?ria das rea??es, transformando aquelas fases delet?rias em fases com resist?ncia mec?nica e permeabilidade satisfat?rias. O objetivo desse estudo foi avaliar o comportamento de um res?duo cer?mico rico em s?lica em substitui??o parcial e total de um aditivo mineral de uso consagrado no combate a retrogress?o da resist?ncia de pastas de cimento submetidos a altas temperaturas. A avalia??o se deu atrav?s de ensaios de resist?ncia ? compress?o, t?cnicas de difra??o de raios X (DRX) e termogravimetria (TG/DTG) das pastas submetidas a um ciclo de baixa temperatura (38 ?C) por 28 dias e, tamb?m, um ciclo de baixa temperatura seguido de cura a 280 ?C e 1000 psi por 3 dias. Os resultados mostraram que pastas contendo adi??es de at? 30% do res?duo n?o foram suficientes para evitar a retrogress?o da resist?ncia, enquanto pastas contendo adi??es do res?duo de maneira combinada com a s?lica flour formaram produtos hidratados de baixa rela??o Ca/Si que fizeram com que a resist?ncia se mantivesse em n?veis satisfat?rios