The rapidly increasing power conversion efficiencies (PCEs) of organic solar cells (OSCs) above 10% were made possible by concerted international research activities in the last few years, aiming to understand the processes that lead to the generation of free charge carriers following photon absorption. Despite these efforts, many details are still unknown, especially how these processes can be improved already at the drawing board of molecular design. To unveil this information, dicyanovinyl end-capped oligothiophene derivatives (DCVnTs) are used as a model system in this thesis, allowing to investigate the impact of small structural changes on the molecular properties and the final solar cells. On thin films of a methylated DCV4T derivative, the influence of the measurement temperature on the charge carrier generation process is investigated. The observed temperature activation in photoinduced absorption (PIA) measurements is attributed to an increased charge carrier mobility, increasing the distance between the charges at the donor/acceptor (D/A) interface and, thus, facilitating their final dissociation. The correlation between the activation energy and the mobility is confirmed using a DCV6T derivative with lower mobility , exhibiting a higher activation energy for charge carrier generation. Another parameter to influence the charge carrier generation process is the molecular structure. Here, alkyl side chains with varying length are introduced and their influence on the intramolecular energy levels as well as the absorption and emission properties in pristine and blend films with the acceptor C60 are examined. The observed differences in intermolecular order (higher order for shorter side chains) and phase separation in blend layers (larger phase separation for shorter side chains) are confirmed in PIA measurements upon comparing the temperature dependence of the triplet exciton lifetimes. A proposed correlation between the side chain length and the coupling between D and A, which is crucial for efficient charge transfer, is not confirmed. The presented flat heterojunction solar cells underline this conclusion, giving similar photocurrent densities for all compounds. Differences in PCE are related to shifts of the energy levels and the morphology of the blend layer in bulk heterojunction devices. Furthermore, the impact of the electric field on the charge carrier generation yield is investigated in a proof-of-principle study, introducing PIA measurements in transmission geometry realized using semitransparent solar cells. The recombination analysis of the photogenerated charge carriers reveals two recombination components. Trapped charge carriers or bound charge pairs at the D/A interface are proposed as an explanation for this result. The miscibility of D and A, which can be influenced by heating the substrate during layer deposition, is of crucial importance to obtain high PCEs. In this work, the unusual negative influence of the substrate temperature on DCV4T:C60 blend layers in solar cells is investigated. By using optical measurements and structure determination tools, a rearrangement of the DCV4T crystallites is found to be responsible for the reduced absorption and, therefore, photocurrent at higher substrate temperature. The proposed blend morphology at a substrate temperature of 90° C is characterized by a nearly complete demixing of the D and A phases. This investigation is of particular relevance, because it shows the microscopic origins of a behavior that is contrary to the increase of the PCE upon substrate heating usually reported in literature. Finally, the optimization steps to achieve a record PCE of 7.7% using a DCV5T derivative as donor material are presented, including the optimization of the substrate temperature, the active layer thickness, and the transport layers. / Der rasante Anstieg des Wirkungsgrads von organischen Solarzellen über die Marke von 10% war nur durch länderübergreifende Forschungsaktivitäten während der letzten Jahre möglich. Trotz der gemeinsamen Anstrengungen, die Prozesse, die zwischen der Absorption der Photonen und der Ladungsträgererzeugung liegen, genauer zu verstehen, sind einige Fragen jedoch immer noch ungelöst, z.B. wie diese Prozesse schon auf dem Reißbrett durch die gezielte Änderung bestimmter Molekülstrukturen optimiert werden können. Um dieses Ziel zu erreichen, werden in dieser Arbeit Dicyanovinyl-substituierte Oligothiophene (DCVnTs) verwendet. Diese Materialien bieten die Möglichkeit, kleine strukturelle Änderungen vorzunehmen, deren Einfluss auf die molekularen und auf die Solarzelleneigenschaften untersucht werden soll. Der Einfluss der Messtemperatur auf den Prozess der Ladungsträgertrennung wird hier an einer methylierten DCV4T-Verbindung in einer dünnen Schicht untersucht. Die bei photoinduzierter Absorptionsspektroskopie (PIA) beobachtete Aktivierung dieses Prozesses mit zunehmender Temperatur wird auf eine erhöhte Ladungsträgerbeweglichkeit zurückgeführt. Der dadurch erhöhte effektive Abstand der Ladungen an der Grenzfläche zwischen Donator (D) und Akzeptor (A) erleichtert die endgültige Trennung der Ladungsträger. Durch den Vergleich mit einer DCV6T-Verbindung wird der Zusammenhang zwischen der Aktivierungsenergie und der Beweglichkeit bekräftigt. Die kleinere Beweglichkeit äußert sich dabei in einer größeren Aktivierungsenergie. Darüber hinaus kann der Ladungsträgergenerationsprozess auch von der Molekülstruktur abhängen. In dieser Arbeit wird untersucht, wie sich die Länge von Alkylseitenketten auf die Energieniveaus der Moleküle, aber auch auf die Absorptions- und Lumineszenzeigenschaften der Materialien in reinen und in Mischschichten mit dem Akzeptor C60 äußert. Die ermittelten Unterschiede bezüglich der Molekülordnung (geordneter für kürzere Seitenketten) und der Phasengrößen in Mischschichten (größere Phasen bei kürzerer Kettenlänge) werden in der Untersuchung der Temperaturabhängigkeit der Lebensdauer von Triplettexzitonen mittels PIA-Messungen bestätigt. Für Solarzellen ist von Bedeutung, ob sich die Seitenkettenlänge auf die Wechselwirkung zwischen D und A auswirkt. Der vermutete Zusammenhang wird hier nicht bestätigt. Ein ähnlicher Photostrom für alle untersuchten Verbindungen in Solarzellen mit planaren Heteroübergängen unterstreicht diese Schlussfolgerung. Unterschiede im Wirkungsgrad werden auf Änderungen der Energieniveaus und die Morphologie in Mischschichtsolarzellen zurückgeführt. Des Weiteren wird in einer Machbarkeitsstudie der Einfluss des elektrischen Felds auf die Generationsausbeute freier Ladungsträger untersucht. Dafür werden halbtransparente Solarzellen verwendet, die es ermöglichen, PIA-Messungen in Transmissionsgeometrie durchzuführen. Als mögliche Erklärung für das Auftreten zweier Rekombinationskomponenten in der Analyse des Rekombinationsverhaltens der durch Licht erzeugten Ladungsträger werden eingefangene Ladungsträger und gebundene Ladungsträgerpaare an der D/A-Grenzfläche genannt. Das Mischverhalten von D und A kann durch ein Heizen des Substrates während des Verdampfungsprozesses eingestellt werden, was von entscheidender Bedeutung für eine weitere Steigerung des Wirkungsgrades ist. Für DCV4T:C60-Mischschichtsolarzellen wird jedoch eine Verschlechterung des Wirkungsgrads zu höheren Substrattemperaturen beobachtet. Durch optische Messungen und Methoden zur Schichtstrukturbestimmung wird dieser Effekt auf eine Umordnung der DCV4T-Kristallite für hohe Substrattemperaturen und die damit verbundene Verringerung der Absorption und damit auch des Photostroms zurückgeführt. Bei einer Substrattemperatur von 90° C sind die D- und A-Komponenten fast vollständig entmischt. Dieses Beispiel ist von besonderer Bedeutung, weil hier die Ursachen für ein Verhalten aufgezeigt werden, das entgegen den Beispielen aus der Literatur eine Abnahme des Wirkungsgrads beim Aufdampfen der aktiven Schicht auf ein geheiztes Substrat zeigt. Schließlich werden die Optimierungsschritte dargelegt, mit denen Solarzellen mit einer DCV5T-Verbindung als Donatormaterial auf einen Rekordwirkungsgrad von 7,7% gebracht werden. Dabei wird die Substrattemperatur, die Dicke der aktiven Schicht und die Transportschichten angepasst.

Au cours de ce projet, nous avons utilisé la microspectroscopie Raman et de photoluminescence pour étudier des matériaux bidimensionnels (graphène et dichalcogénures de métaux de transition) et des hétérostructures de van der Waals. Tout d’abord, à l’aide de transistors de graphène munis d’une grille électrochimique, nous montrons que la spectroscopie Raman est un outil extrêmement performant pour caractériser précisément des échantillons de graphène. Puis, nous explorons l’évolution des propriétés physiques de N couches de dichalcogénures de métaux de transition semi-conducteurs, en particulier de ditellurure de molybdène (MoTe2) et de diséléniure de molybdène (MoSe2). Dans ces structures lamellaires, nous observons la séparation de Davydov des phonons optiques au centre de la première zone de Brillouin, que nous décrivons à l’aide d’un modèle de chaîne linéaire. Enfin, nous présentons une étude toute optique du transfert de charge et d’énergie dans des hétérostructures de van der Waals constituées de monocouches de graphène et de MoSe2. Ce travail de thèse met en évidence la riche photophysique de ces matériaux atomiquement fins et leur potentiel en vue de la réalisation de nouveaux dispositifs optoélectroniques. / In this project, we have used micro-Raman and micro-photoluminescence spectroscopy to study two-dimensional materials (graphene and transition metal dichalcogenides) and van der Waals heterostructures. First, using electrochemically-gated graphene transistors, we show that Raman spectroscopy is an extremely sensitive tool for advanced characteri-zations of graphene samples. Then, we investigate the evolution of the physical properties of N-layer semiconducting transition metal dichalcogenides, in particular molybdenum ditelluride (MoTe2) and molybdenum diselenide (MoSe2). In these layered structures, theDavydov splitting of zone-center optical phonons is observed and remarkably well described by a ‘textbook’ force constant model. We then describe an all-optical study of interlayer charge and energy transfer in van der Waals heterostructures made of graphene and MoSe2 monolayers. This work sheds light on the very rich photophysics of these atomically thin two-dimensional materials and on their potential in view of optoelectronic applications.

Siliziumnanodrähte (SiNWs) bieten eine aussichtsreiche Grundlage zur Entwicklung neuartiger nanoelektronischer Bauelemente, wie Feldeffekttransistoren oder Sensoren. Dabei ist insbesondere die Oxidation der Drähte interessant, weil diese weitreichenden Einfluss auf die elektronischen Eigenschaften der Bauelemente hat, die aus den SiNWs gefertigt werden. Die Größe der untersuchten Strukturen erfordert eine atomistische Analyse des Oxidationsprozesses. In der vorliegenden Arbeit wird der bisher wenig verstandene Beginn der Oxidation dünner Drähte molekulardynamisch simuliert, wobei als Potential ein reaktives Kraftfeld dient. Dabei wird sich intensiv mit dem Transfer elektrischer Ladungen zwischen Atomen unterschiedlicher Elektronegativitäten während der Simulationen auseinandergesetzt. Desweiteren werden Strukturen, die während der Oxidation von SiNWs der Orientierungen <100> und <110> bei Temperaturen von 300 K und 1200 K entstehen, untersucht. Ein Fokuspunkt dieser Untersuchungen ist die Analyse der Anzahl am Draht adsorbierter Sauerstoffatome während der frühen Oxidationsphase. Darüber hinaus wird die Dichte der entstehenden Strukturen beleuchtet. Dies geschieht mit einer hohen radialen Auflösung und erstmalig während der gesamten Simulation. Hierbei zeigt sich, dass während des Übergangs von kristallinem Silizium zu amorphem Siliziumdioxid zwischen den Siliziumatomen Sauerstoff eingelagert wird, die Kristallstruktur des Siliziums sich zunächst jedoch noch nicht auflöst. Dadurch entsteht ein charakteristisches Muster hoher und niedriger Dichten, das von der ursprünglichen Kristallstruktur des SiNW abhängt.:Abbildungsverzeichnis Abkürzungsverzeichnis Symbolverzeichnis 1 Einleitung 2 Einführung zu Siliziumnanodrähten 2.1 Kristallstuktur von Silizium 2.2 Ideale Siliziumnanodrähte 2.3 Herstellung von Siliziumnanodrähten 3 Grundlagen der Molekulardynamik 3.1 Newtonsche Axiome 3.2 Einige grundlegende Begriffe der statistischen Physik 3.3 Molekulardynamik 3.4 Reaktives Kraftfeld 3.5 Methoden zur Beschreibung des Ladungstransfers 3.6 Thermostat und Barostat 3.7 Large-scale Atomic/Molecular Massively Parallel Simulator 4 Entwicklung des Modellsystems 4.1 Ausgangsstruktur 4.2 Vorrelaxation 4.3 Ablauf der Oxidation 4.4 Verwendeter ReaxFF-Parametersatz 4.5 Optimierung der Zeitschrittweite 4.5.1 Modellsystem, Relaxation und Oxidation 4.5.2 Festlegung der Zeitschrittweite 4.6 Optimierung der Systemlänge 4.6.1 Modellsystem, Relaxation und Oxidation 4.6.2 Festlegung der Systemlänge 4.7 Einfluss des globalen, instantanen Ladungstransfers auf die Simulation 4.7.1 Festlegung des Einsetzabstands 4.7.2 Vergleich mit Daten von Khalilov et al. 5 Variation von System- und Einsetztemperatur sowie Drahtorientierung 5.1 Variation von System- und Einsetztemperatur 5.1.1 Untersuchung des Oxidationsgrads 5.1.2 Untersuchung von Dichten und Grenzflächenpositionen 5.2 Variation der Drahtorientierung 5.2.1 Untersuchung des Oxidationsgrads 5.2.2 Untersuchung von Dichten und Grenzflächenpositionen 6 Zusammenfassung und Ausblick 6.1 Zusammenfassung 6.2 Ausblick Literaturverzeichnis

Key issues in improving small molecule organic solar cells (SMOSC) are the need for new absorber materials and optimized active layer morphology. This thesis deals with the improvement of SMOSC on the donor material side. Promising donor materials (D) are provided by dicyanovinyl endcapped oligothiophenes DCV2-nT (n = 3, . . . , 6) synthesized in the group of Prof. Bäuerle at the University of Ulm. Here, DCV2-nT (n = 3, 5) with different alkyl side chains are characterized. Side chain variations mainly influence the aggregation of molecules in pristine films as well as in blend films with the commonly used acceptor (A) fullerene C60. With changes in the layer morphology, important physical properties in thin film like absorption spectra, energy levels, as well as excited state properties are changed. The focus of this work are excited state properties accessed by photoinduced absorption spectroscopy (PIA). PIA probes the long living excited states in pristine and blend films, i. e. triplet excitons, anions, and cations. For a series of four dicyanovinyl-terthiophenes DCV2-3T (without side chains, with two methyl, two butyl, and four butyl side chains) a systematic study of the effect of alkyl side chains on the aggregation in neat and blend film is discussed. In consequence the efficiency of the energy transfer mechanism between DCV2-3T and C60 is affected. It turns out that in solution spectra and cyclic voltammetry (CV) measurements, the variation of alkyl side chains has almost no influence. However, in thin film there is strong impact on the molecular arrangement confirmed by strongly varying absorption spectra, ionization potentials, and surface roughnesses. Furthermore, PIA measurements reveal that the energy transfer efficiency between D and A in general decreases with increasing side chain length, but is most efficient for a compound with methyl side chains. For blends of dicyanovinyl-quinquethiophenes (DCV2-5T) with C60, the layer morphology is influenced by two different methods. On one hand substrate heating is applied while deposition of the active layer, on the other hand DCV2-5Ts with different alkyl side chains (four methyl and four butyl side chains) are used. Deposition on a heated substrate (80°C) results in an improved solar cell performance, assigned to the formation of a sufficient phase separation of D and A phase in the active layer. This leads to reduced recombination losses and closed percolation paths. The morphological change can be correlated to an increased lifetime of cations. In blends deposited on a heated substrate, the donor cation lifetime increases by almost one order of magnitude from around 10 μs to ≈ 80 μs. This increase of carrier lifetime is both detected optically by PIA as well as electrically by impedance spectroscopy. The increase in lifetime is consequently assigned to a better spatial separation of positive and negative charges induced by the phase separation. Comparing DCV2-5T with methyl and butyl side chains results in a similar effect: The dicyanovinyl-quinquethiophene with methyl side chains leads to an improved solar cell device performance compared to devices comprising the compound with butyl side chains as donor. The improved device performance is again accompanied by an increase in cation lifetime detected by PIA.:Contents Publications 1. Introduction 2. Organic semiconductors 2.1. Introduction 2.2. Optical excitations in organic semiconductors 2.2.1. Energy levels: single molecules to molecular solids 2.2.2. Absorption and emission spectra 2.3. Transport in organic semiconductors 2.3.1. Exciton motion 2.3.2. Charge transport 2.3.3. Amorphous organic semiconductors 3. Organic photovoltaics 3.1. Introduction 3.2. Solarenergyconversion 3.2.1. Quasi Fermi levels 3.2.2. p-n junction 3.3. Organic solar cells 3.3.1. Charge generation mechanisms 4. Experimental methods 4.1. Sample preparation 4.2. Photoinduced absorption spectroscopy 4.2.1. PIA setup 4.2.2. Recombination dynamics 4.3. Solar cell characterization 4.3.1. External quantum efficiency 4.3.2. J-V characteristics 4.4. Absorption and emission spectroscopy 4.5. Determination of energy levels 4.5.1. Ultraviolet photo electron emission spectroscopy 4.5.2. Cyclic voltammetry 4.6. Atomic force microscopy 4.7. Density functional theory calculations 4.8. Impedance spectroscopy 5. Dicyanovinyl-oligothiophenes 5.1. Introduction 5.2. The DCV2-nT:C60 interface 5.3. Processability 6. Side chain variations on DCV2-3T 6.1. Introduction 6.2. Density functional theory calculations 6.2.1. Excited state transitions 6.3. Absorption and Emission in solution and thin film 6.3.1. Blend layer absorption spectra 6.3.2. Photoluminescence spectra of neat and blend films 6.4. Energy levels of the DCV2-3T series 6.5. Atomic force microscopy 6.6. Photoinduced absorption spectroscopy 6.6.1. PIA signatures of charged states 6.6.2. Recombination dynamics 6.6.3. Efficiency of the ping pong effect 6.7. Conclusion 7. Influencing the morphology of DCV2-5T:C60 blend layers 7.1. Introduction 7.2. Properties of the DCV2-5T:C60 interface 7.2.1. Analysis of the DCV2-5T triplet transition 7.2.2. Analysis of the DCV2-5T cation transitions 7.2.3. Suggested energy level scheme for neat and blend layer 7.3. Temperature evolution of excited state properties 7.4. Effect of substrate heating on excited state lifetime and generation rate 7.4.1. Solar cell devices 7.4.2. Photoinduced absorption 7.4.3. Impedance spectroscopy 7.5. Conclusion 8. Side chain variations on DCV2-5T 8.1. Introduction 8.2. Atomic force microscopy 8.3. Energy levels 8.4. Mip solar cells 8.4.1. Flat heterojunctions 8.4.2. Bulk heterojunctions 8.4.3. Discussion of Voc 8.5. Photoinduced absorption 8.5.1. Comparison at room temperature 8.6. Conclusion 9. Conclusion and Outlook 9.1. Conclusion 9.2. Outlook A. Appendix Bibliography / Die Entwicklung neuer Absorber-Materialien sowie die Morphologie der photo- aktiven Schicht sind zentrale Themen hinsichtlich der Optimierung organischer Solarzellen aus kleinen Molekülen. In der vorliegenden Arbeit werden diese beiden Aspekte von Seiten des Donor-Materials (D) her behandelt. Die Material- klasse der Dicyanovinyl-Oligothiophene DCV2-nT(n=3,...,6) (synthetisiert in der Arbeitsgruppe von Prof. Bäuerle an der Universität Ulm) dient dabei als Ausgangspunkt. Insbesondere werden DCV2-nT-Moleküle (n = 3, 5) mit verschiedenen Alkyl-Seitenketten charakterisiert. Die Variation der Seitenketten beeinflusst in erster Linie die Anordnung der Moleküle in Einzel- sowie in Mischschichten mit dem typischerweise verwendeten Akzeptor-Material Fulleren C60 (A). Als Folge der Schichtmorphologie ändern sich physikalische Eigenschaften wie u. a. Absorptions- spektren, Energieniveaus sowie die Eigenschaften angeregter Zustände. Angeregte Zustände, wie Triplett-Exzitonen, Anionen und Kationen werden in dieser Arbeit mittels photoinduzierter Absorptionsspektroskopie (PIA) charakterisiert. Anhand einer Serie von vier Dicyanovinyl-Tertiophenen DCV2-3T (ohne Seiten- ketten, mit zwei Methyl-, zwei Butyl-, und vier Butyl-Seitenketten) werden systematisch Einflüsse der Seitenketten auf die Aggregation der Moleküle in Einzel- und Mischschichten untersucht. Besonderes Augenmerk liegt dabei auf dem Effekt der Seitenketten auf den Energie-Transfer-Mechanismus zwischen D und A. In Lösungsmittelspektren und Cyclovoltammetrie-Messungen ist fast keine Änderung durch die Seitenketten erkennbar. Im Dünnfilm hingegen besteht ein starker Einfluss auf die molekulare Anordnung, erkennbar in einer starken Variation der Absorptionsspektren, Ionisationspotentiale und Oberflächen-Topographie. PIA- Messungen zeigen weiterhin, dass im Allgemeinen die Effizienz des Energie-Transfer- Mechanismus mit zunehmender Länge der Alkyl-Ketten abnimmt. Der effizienteste Transfer besteht jedoch für die Verbindung mit Methyl-Seitenketten. In Mischschichten aus Dicyanovinyl-Quinquethiophenen (DCV2-5T) und C60 werden hier zwei Methoden zur Beeinflussung der Schichtmorphologie verfolgt. Zum einen wird die aktive Schicht auf einem geheizten Substrat abgeschieden, zum anderen werden DCV2-5T-Moleküle mit Methyl- und Butyl-Seitenketten als Donor verwendet. Das Abscheiden der aktiven Schicht auf einem geheizten Substrat (80 °C) führt zu einer verbesserten Solarzellenleistung, was auf die Bildung einer hin- reichenden Phasenseparation von D- und A-Phasen in der aktiven Schicht zurückzuführen ist. Die Phasenseparation bewirkt eine Reduktion von Rekombinationsverlusten und die Bildung geschlossener Perkolationspfade. Die morphologische Änderung korreliert mit einem Anstieg der Ladungsträger-Lebensdauer um fast eine Größenordnung von etwa 10 μs auf ≈ 80 μs. Der Anstieg kann sowohl optisch durch PIA, als auch elektrisch mittels Impedanz-Spektroskopie detektiert werden. Eine höhere Lebensdauer der Ladungsträger kann letztlich auf eine größere räumlichen Separation der positiven und negativen Ladungsträger zurückgeführt werden, induziert durch die Phasenseparation. Ein Vergleich von DCV2-5T-Molekülen mit Methyl- und Butyl-Seitenketten führt zu ähnlichen Resultaten: Solarzellen mit DCV2-5T substituiert mit Methyl- Seitenketten sind effizienter als die der butyl-substituierten Moleküle. Dies korreliert wiederum mit einer signifikant erhöhten Lebensdauer der Ladungsträger in Mischschichten der methyl-substituierten Verbindung.:Contents Publications 1. Introduction 2. Organic semiconductors 2.1. Introduction 2.2. Optical excitations in organic semiconductors 2.2.1. Energy levels: single molecules to molecular solids 2.2.2. Absorption and emission spectra 2.3. Transport in organic semiconductors 2.3.1. Exciton motion 2.3.2. Charge transport 2.3.3. Amorphous organic semiconductors 3. Organic photovoltaics 3.1. Introduction 3.2. Solarenergyconversion 3.2.1. Quasi Fermi levels 3.2.2. p-n junction 3.3. Organic solar cells 3.3.1. Charge generation mechanisms 4. Experimental methods 4.1. Sample preparation 4.2. Photoinduced absorption spectroscopy 4.2.1. PIA setup 4.2.2. Recombination dynamics 4.3. Solar cell characterization 4.3.1. External quantum efficiency 4.3.2. J-V characteristics 4.4. Absorption and emission spectroscopy 4.5. Determination of energy levels 4.5.1. Ultraviolet photo electron emission spectroscopy 4.5.2. Cyclic voltammetry 4.6. Atomic force microscopy 4.7. Density functional theory calculations 4.8. Impedance spectroscopy 5. Dicyanovinyl-oligothiophenes 5.1. Introduction 5.2. The DCV2-nT:C60 interface 5.3. Processability 6. Side chain variations on DCV2-3T 6.1. Introduction 6.2. Density functional theory calculations 6.2.1. Excited state transitions 6.3. Absorption and Emission in solution and thin film 6.3.1. Blend layer absorption spectra 6.3.2. Photoluminescence spectra of neat and blend films 6.4. Energy levels of the DCV2-3T series 6.5. Atomic force microscopy 6.6. Photoinduced absorption spectroscopy 6.6.1. PIA signatures of charged states 6.6.2. Recombination dynamics 6.6.3. Efficiency of the ping pong effect 6.7. Conclusion 7. Influencing the morphology of DCV2-5T:C60 blend layers 7.1. Introduction 7.2. Properties of the DCV2-5T:C60 interface 7.2.1. Analysis of the DCV2-5T triplet transition 7.2.2. Analysis of the DCV2-5T cation transitions 7.2.3. Suggested energy level scheme for neat and blend layer 7.3. Temperature evolution of excited state properties 7.4. Effect of substrate heating on excited state lifetime and generation rate 7.4.1. Solar cell devices 7.4.2. Photoinduced absorption 7.4.3. Impedance spectroscopy 7.5. Conclusion 8. Side chain variations on DCV2-5T 8.1. Introduction 8.2. Atomic force microscopy 8.3. Energy levels 8.4. Mip solar cells 8.4.1. Flat heterojunctions 8.4.2. Bulk heterojunctions 8.4.3. Discussion of Voc 8.5. Photoinduced absorption 8.5.1. Comparison at room temperature 8.6. Conclusion 9. Conclusion and Outlook 9.1. Conclusion 9.2. Outlook A. Appendix Bibliography

As the third generation of luminescent materials, thermally activated delayed fluorescence (TADF)-type compounds have great potential as emitter molecules in OLEDs allowing for electro-fluorescence with 100 % internal quantum efficiency. For organic electronics, the general wide range of applications from OLEDs, bio-fluorescence imaging to sensor technologies and photonic energy storages roots on the enormous variety of organic materials. Especially in the field of metal- free aromatic designs, the range of possible materials showing diverse triplet harvesting effects is immense, making material development a highly complex task. Firstly, initial efforts in the understanding of the basic concepts behind TADF will be highlighted. A rational design strategy for TADF materials will be illustrated on an innovative material series based on phenylcarbazoles. A reasonable branch of isomers are theoretically constructed and slight stoichiometric modifications are performed to understand how molecular structure and intramolecular steric hindrance affects reverse intersystem crossing (RISC), while simultaneously revealing the strategy for deep blue TADF. The rational design of a bluish green TADF material called 5CzCF3Ph providing CIEy ≤ 0.4 is demonstrated, enabling peak EQE values of 12.1 % with a promising LT50 of 2 hrs at 500 cd∙m-2. Subsequently, the photophysics of five newly designed trimeric donor (D)-acceptor (A)-donor (D) type material compounds, analogue concepts to archetypical TADF designs, highlight the importance of intramolecular electronic couplings between adjacent triplet states for adiabatically-driven TADF, revealing the mechanism of local type triplet state perturbations on 3CT states. The most promising candidate (DMAC-PTO-DMAC) is disclosed and in turn optimized to meet required conditions for deep blue TADF emission. Ultimately, a deep blue luminescent material called isoDMAC-PTO is developed, featuring CIE coordinates of (0.16, 0.14) with an overall quantum yield of (86.4 ± 0.5) %. The focus switches to the fundamental understanding of the underlying mechanism giving rise to TADF in small molecules, leaving the scope of deep blue emission. While investigating the photophysical properties of a synthesized donor (D)-acceptor (A) type thermally activated delayed fluorescence (TADF) emitter named methyl 2-(9,9-dimethylacridin-10-yl)benzoate (DMAC-MB), it is possible to identify the excited state dynamics mediating the spin-flip process and hence the reutilization of non-radiative triplet states allowing for an internal quantum efficiency approaching unity. As experimentally observed by detailed temperature- and time-dependent transient photoluminescence (PL) measurements and consolidated by comprehensive quantum-chemical considerations, excited state configuration interaction by non-adiabatic couplings are anticipated as key property behind triplet up-conversion in the vicinity of conical intersections, contributing to recent research facing the exciton management within the auspicious field of TADF. For the first time, this thesis reports that even a TADF-silent molecule can be converted into efficient TADF systems by increasing the donor π- conjugation length through polymerization of the building block itself. With a total photoluminescence quantum yield up to 71 %, comprehensible research illustrates an efficient thermally activated delayed fluorescence polymer P1, based solely on non-TADF chromophores represented by a model compound 2 (PLQY of 3 % at RT). Finally, as predicted by TDDFT calculations and shown for the first time in the aspiring field of TADF, a thermally activated delayed fluorescence polymer based on a merely radiative, solely phosphorescent repeating unit is demonstrated. Intramolecular π-conjugation is exploited to trigger the charge-transfer excited state energy, revealing a general design tool to provoke TADF, reserved in particular for polymers. While the introduced twisted methyl 2-(9,9-dimethylacridin-10-yl) benzoate (DMAC-MB) reveals efficient thermally activated delayed fluorescence (TADF), a modified analogue 9,9-Dimethyl-5H,9H-quinolino[3,2,1-de]acridin-5-one (DMAC-ACR) shows emerging room temperature phosphorescence (RTP). As for TADF, intramolecular non-adiabatic couplings are unlocked as key feature actuating persistent RTP, linking photophysical analogies between TADF and RTP to structural self-similarities. Last but not least, degradation processes in TADF materials will be addressed. A correlation between theoretically calculated bond-dissociation energies (BDEs) and phenomenological observations reveals that low BDEs, in particular along pronounced charge-transfer bonds, ultimately lead to irreversible TADF material degradation induced by bi-molecular processes comprising TPQ as well as TTA. Finally, this thesis reveals the photophysics of 24 newly designed, synthesized and characterized TADF materials and demonstrates a fundamentally new approach for RTP, based on structural analogues to TADF. Far reaching design principles as conjugation induced TADF in polymers, as well as new design strategies selectively incorporating virbonic couplings yield device performances comprising LT50 of 2 hrs at 500 cd∙m-2 and targeted deep blue emission with CIE (0.16, 0.14). While lighting the way for TADF as future luminescent OLED materials, intrinsic material instabilities due to low bond-dissociation energies are disclosed as key-issues for tomorrows research.

Die vorliegende Dissertation beschäftigt sich mit dem elektrochemischen Verhalten verschiedener Ferrocenyl-substituierter Thiophene. Dabei wird sich zunächst mit dem elektrochemischen Verhalten der Serie der Ferrocenylthiophene beschäftigt, die Anzahl der Ferrocenyleinheiten variiert von n = 1 – 4. Die Abhängigkeit der elektronischen Eigenschaften von numerischen und konstitutionellen Veränderungen der redox-aktiven Gruppen wird evaluiert. Daraus resultierend wird sich einer eingehenderen Untersuchung und Modifikation des 2,5-Diferrocenylthiophen-Motivs zugewandt. Diese Modifikationen werden im Kontext möglicher Ladungstransferprozesse zwischen den Ferrocenyleinheiten in den verschiedenen Redoxzuständen und unter Beeinflussung durch den Thiophen-Brückenliganden diskutiert. Es folgen des Weiteren Ausführungen zu Substitutionen an den Ferrocenylen (Einführung elektronen-ziehender Funktionalitäten) sowie der Vergleich zwischen einer Thiophen- und der Ethylendioxythiophen-Brückeneinheit. Anschließend wird sich mit der elektronischen Variation des Brückenliganden durch die Einführung von N-haltigen Substituenten befasst. In den abschließenden Kapiteln wird der Einfluss zusätzlicher σ- (Fischercarben-Komplexe) oder π-gebundener ([Ru(η5-C5H5)]+/[Ru(η5-C5Me5)]+) Übergangsmetallkomplexfragmente auf Ladungstransferwechselwirkungen im 2,5-Diferrocenylthiophen in verschiedenen Redoxzuständen beleuchtet.

Das Verstehen der elektronischen Prozesse in Nano-Hybridsystemen, bestehend aus Molekülen und Halbleiterstrukturen, eröffnet neue Möglichkeiten für optoelektronische Bauteile. Dafür benötigt es nanoskopische und gleichzeitig atomare Modelle und somit angepasste Rechenmethoden. Insbesondere "Standard"-Ansätze für die Dynamik offener Quantensysteme werden mit zunehmender Systemgröße jedoch sehr ineffizient. In dieser Arbeit wird eine neue Methode basierend auf einer stochastischen Schrödinger-Gleichung etablieren. Diese umgeht die numerischen Limits der Quanten-Mastergleichung und ermöglicht Simulationen von imposanter Größe. Ihr enormes Potenzial wird hier in Studien zu Anregungsenergietransfer und Ladungsseparation an zwei realistischen Nano-Hybridsystemen demonstriert: para-sexiphenyl Moleküle auf einer flachen ZnO Oberfläche (6P/ZnO), und ein tubuläres C8S3 Farbstoffaggregat gekoppelt an einen CdSe Nanokristall (TFA/NK). Im 6P/ZnO System findet nach optischer Anregung Energietransfer vom 6P Anteil zum ZnO statt. Direkt an der Grenzfläche können Frenkel-Exzitonen zusätzlich Ladungsseparation initiieren, wobei Elektronen ins ZnO transferiert werden und Löcher im 6P Anteil verbleiben. Beide Mechanismen werden mittels laserpulsinduzierter ultraschneller Wellenfunktionsdynamik simuliert. Danach wird die langsamere dissipative Lochkinetik im 6P Anteil studiert. Hierfür wird die eigene Simulationstechnik der stochastischen Schrödinger-Gleichung verwendet. Die Studie an der TFA/NK Grenzfläche basiert auf einer gigantischen equilibrierten Aggregatstruktur aus 4140 Molekülen. Ein generalisiertes Frenkel-Exzitonenmodell wird benutzt. Der Ansatz der stochastischen Schrödinger-Gleichung ermöglicht bemerkenswerte Einblicke in die Aggregat-interne Exzitonenrelaxation. Danach werden inkohärente Raten des Exzitonentransfers zum NK berechnet. Unterschiedliche räumliche Konfigurationen werden untersucht und es wird diskutiert, warum das Förster-Modell hier keine Gültigkeit besitzt. / Understanding the electronic processes in hybrid nano-systems based on molecular and semiconductor elements opens new possibilities for optoelectronic devices. Therefore, it requires for models which are both nanoscopic and atomistic, and so for adapted computational methods. In particular, "standard" methods for open quantum system dynamics however become very inefficient with increasing system size. In this regard, it is a key challenge of this thesis, to establish a new stochastic Schrödinger equation technique. It bypasses the computational limits of the quantum master equation and enables dissipative simulations of imposing dimensionality. Its enormous potential is demonstrated in studies on excitation energy transfer and charge separation processes in two realistic nanoscale hybrid systems: para-sexiphenyl molecules deposited on a flat ZnO surface (6P/ZnO), and a tubular dye aggregate of C8S3 cyanines coupled to a CdSe nanocrystal (TDA/NC). After optical excitation, the 6P/ZnO system exhibits exciton transfer from the 6P part to the ZnO. Close to the interface, Frenkel excitons may further initiate charge separation where electrons enter the ZnO and holes remain in the 6P part. Both mechanisms are simulated in terms of laser-pulse induced ultrafast wave packet dynamics. Afterwards, slower dissipative hole motion in the 6P part is studied. For this purpose, the own stochastic Schrödinger equation simulation technique is applied. The study on the TDA/NC interface is based on a gigantic equilibrated nuclear structure of the aggregate including 4140 dyes. A generalized Frenkel exciton model is employed. Thanks to the stochastic Schrödinger equation approach, energy relaxation in the exciton band of the TDA is simulated in outstanding quality and extend. Then, incoherent rates for exciton transfer to the NC are computed. Different spatial configurations are studied and it is discussed why the Förster model possesses no validity here.

The rapidly increasing power conversion efficiencies (PCEs) of organic solar cells (OSCs) above 10% were made possible by concerted international research activities in the last few years, aiming to understand the processes that lead to the generation of free charge carriers following photon absorption. Despite these efforts, many details are still unknown, especially how these processes can be improved already at the drawing board of molecular design. To unveil this information, dicyanovinyl end-capped oligothiophene derivatives (DCVnTs) are used as a model system in this thesis, allowing to investigate the impact of small structural changes on the molecular properties and the final solar cells. On thin films of a methylated DCV4T derivative, the influence of the measurement temperature on the charge carrier generation process is investigated. The observed temperature activation in photoinduced absorption (PIA) measurements is attributed to an increased charge carrier mobility, increasing the distance between the charges at the donor/acceptor (D/A) interface and, thus, facilitating their final dissociation. The correlation between the activation energy and the mobility is confirmed using a DCV6T derivative with lower mobility , exhibiting a higher activation energy for charge carrier generation. Another parameter to influence the charge carrier generation process is the molecular structure. Here, alkyl side chains with varying length are introduced and their influence on the intramolecular energy levels as well as the absorption and emission properties in pristine and blend films with the acceptor C60 are examined. The observed differences in intermolecular order (higher order for shorter side chains) and phase separation in blend layers (larger phase separation for shorter side chains) are confirmed in PIA measurements upon comparing the temperature dependence of the triplet exciton lifetimes. A proposed correlation between the side chain length and the coupling between D and A, which is crucial for efficient charge transfer, is not confirmed. The presented flat heterojunction solar cells underline this conclusion, giving similar photocurrent densities for all compounds. Differences in PCE are related to shifts of the energy levels and the morphology of the blend layer in bulk heterojunction devices. Furthermore, the impact of the electric field on the charge carrier generation yield is investigated in a proof-of-principle study, introducing PIA measurements in transmission geometry realized using semitransparent solar cells. The recombination analysis of the photogenerated charge carriers reveals two recombination components. Trapped charge carriers or bound charge pairs at the D/A interface are proposed as an explanation for this result. The miscibility of D and A, which can be influenced by heating the substrate during layer deposition, is of crucial importance to obtain high PCEs. In this work, the unusual negative influence of the substrate temperature on DCV4T:C60 blend layers in solar cells is investigated. By using optical measurements and structure determination tools, a rearrangement of the DCV4T crystallites is found to be responsible for the reduced absorption and, therefore, photocurrent at higher substrate temperature. The proposed blend morphology at a substrate temperature of 90° C is characterized by a nearly complete demixing of the D and A phases. This investigation is of particular relevance, because it shows the microscopic origins of a behavior that is contrary to the increase of the PCE upon substrate heating usually reported in literature. Finally, the optimization steps to achieve a record PCE of 7.7% using a DCV5T derivative as donor material are presented, including the optimization of the substrate temperature, the active layer thickness, and the transport layers.:Abstract - Kurzfassung Publications Contents 1 Introduction 2 Elementary Processes in Organic Semiconductors 2.1 Introduction 2.2 Optical Excitations in Organic Materials 2.2.1 Introduction 2.2.2 Radiative Processes: Absorption and Emission 2.2.3 Non-radiative Relaxation Processes 2.2.4 Triplet Excitons and Intersystem Crossing 2.3 Polarization Effects and Disorder 2.4 Transport Processes in Disordered Organic Materials 2.4.1 Charge Transport 2.4.1.1 The Bässler Model 2.4.1.2 Marcus Theory for Electron Transfer 2.4.1.3 Small Polaron Model 2.4.1.4 Functional Dependencies of the Charge Carrier Mobility 2.4.2 Diffusive Motion 2.4.3 Exciton Transfer Mechanisms 2.4.4 Characteristics of Exciton Diffusion 2.5 Charge Photogeneration in Pristine Materials 3 Organic Photovoltaics 3.1 General Introduction to Solar Cell Physics 3.2 Introduction to the Donor/Acceptor Heterojunction Concept 3.3 The Open-Circuit Voltage in Organic Solar Cells 3.4 Doping of Organic Semiconductors 3.5 Introduction to the p-i-n Concept 3.6 Charge Transfer Excitons in Donor/Acceptor Heterojunction Systems 3.6.1 Introduction 3.6.2 Verification of Charge Transfer Excitons in Donor/Acceptor Systems 3.7 The Process Cascade for Free Charge Carrier Generation in Donor/Acceptor Heterojunction Systems 3.7.1 The Initial Charge Transfer Step 3.7.2 The Binding Energy of the Charge Transfer Exciton 3.7.3 \"Hot\" Charge Transfer Exciton Dissociation 3.7.4 \"Cold\" Charge Transfer Exciton Dissociation 3.7.5 Supposed Influence Factors on Charge Transfer Exciton Dissociation 3.7.6 Recombination Pathways for Charge Transfer Excitons 3.7.7 Free Charge Carrier Formation and Recombination 4 Experimental Methods 4.1 Sample Preparation 4.2 Material Characterization Methods 4.2.1 Optical Characterization 4.2.2 Cyclic Voltammetry 4.2.3 Ultraviolet Photoelectron Spectroscopy 4.2.4 Atomic Force Microscopy 4.2.5 Grazing Incidence X-Ray Diffraction 4.2.6 Organic Field-Effect Transistor 4.3 Photoinduced Absorption Spectroscopy 4.3.1 Introduction 4.3.2 Derivation of the PIA Signal 4.3.3 Recombination Dynamics 4.3.4 Intensity Dependence of the PIA Signal 4.4 Solar Cell Characterization 4.4.1 External Quantum Efficiency 4.4.2 Spectral Mismatch Correction 4.4.3 Current-Voltage Characteristics 4.4.4 Optical Device Simulations 4.4.5 Optical Device Transmission Measurements 5 The Oligothiophene Material System 5.1 Introduction 5.2 Thermal Stability 5.3 Energy Levels 5.4 Optical Properties of the Pristine Materials 5.5 The Donor/Acceptor Couple: DCVnT and C60 5.6 Solar Cell Devices 5.7 Summary 6 Temperature Dependence of Charge Carrier Generation 6.1 Introduction 6.2 Principal Introduction to the PIA Measurements 6.2.1 Interpretation of the Spectra 6.2.2 Interpretation of the Frequency Scans 6.3 Temperature Dependence of the Spectra 6.4 Discussion of the Temperature Dependent Processes in the Blend Layer 6.5 Temperature Activated Free Charge Carrier Generation 6.5.1 Evaluation of the Activation Energy for the DCV4T-Me:C60 Blend 6.5.2 Comparison to a Sexithiophene Derivative (DCV6T-Me) 6.6 Summary 7 Side Chain Investigation on Quaterthiophene Derivatives 7.1 Energy Levels 7.2 Optical Properties 7.2.1 Solution and Pristine Films 7.2.2 Mixed Films with C60 7.3 Influence of the Side Chain Length on the Intermolecular Coupling 7.3.1 PIA Spectra of Pristine and Blend Layers at 10K 7.3.2 Recombination Analysis for Pristine and Blend Films at 10K 7.4 The Influence of the Side Chain Length on the Offset Charge Carrier Generation Rate at Low Temperature 7.5 In the High-Temperature Limit: Implications for Solar Cell Devices 7.5.1 PIA Spectra in Pristine and Blend Films at 200K 7.5.2 Recombination Analysis: Triplet Excitons and Free Charge Carriers 7.6 Solar Cells 7.6.1 Flat Heterojunction Devices 7.6.2 Bulk Heterojunction Devices 7.7 Summary 8 Electric-Field Dependent PIA Measurements on Complete Solar Cell Devices 8.1 Introduction 8.2 Semitransparent Organic Solar Cells 8.3 Photoinduced Absorption Measurements 8.4 Summary and Outlook 9 The Effect of Substrate Heating During Layer Deposition on the Performance of DCV4T:C60 BHJ Solar Cells 9.1 Introduction 9.2 The Importance of Morphology Control for BHJ Solar Cells 9.3 The Impact of Substrate Heating on DCV4T:C60 BHJ Solar Cells 9.4 Absorption and Photoluminescence 9.5 Topographical Investigations (AFM) 9.6 X-ray Investigations 9.6.1 1D GIXRD Measurements 9.6.2 2D GIXRD Measurements 9.7 Proposed Morphological Picture and Confirmation Measurements 9.7.1 Morphology Sketch of the DCV4T:C60 Blend Layer 9.7.2 Confirmation Measurements 9.8 The Equivalence of Temperature and Time 9.9 Summary 10 Record Solar Cells Using DCV5T-Me33 as Donor Material 10.1 Introduction 10.2 The Influence of the Substrate Temperature 10.3 Determination of the Optical Constants 10.4 Stack Optimization 10.5 Summary and Outlook 11 Conclusions and Outlook 11.1 Summary of the Photophysical Investigations 11.2 Summary of Device Investigations 11.3 Future Challenges Appendix A Detailed Description of the Experimental Setup for PIA Spectroscopy Appendix B Determination of the Triplet Level by Differential PL Measurements Appendix C Additional Tables and Figures Appendix D Reproducibility of the Solar Cell Results (Statistics) Appendix E Lists Bibliography Acknowledgments / Der rasante Anstieg des Wirkungsgrads von organischen Solarzellen über die Marke von 10% war nur durch länderübergreifende Forschungsaktivitäten während der letzten Jahre möglich. Trotz der gemeinsamen Anstrengungen, die Prozesse, die zwischen der Absorption der Photonen und der Ladungsträgererzeugung liegen, genauer zu verstehen, sind einige Fragen jedoch immer noch ungelöst, z.B. wie diese Prozesse schon auf dem Reißbrett durch die gezielte Änderung bestimmter Molekülstrukturen optimiert werden können. Um dieses Ziel zu erreichen, werden in dieser Arbeit Dicyanovinyl-substituierte Oligothiophene (DCVnTs) verwendet. Diese Materialien bieten die Möglichkeit, kleine strukturelle Änderungen vorzunehmen, deren Einfluss auf die molekularen und auf die Solarzelleneigenschaften untersucht werden soll. Der Einfluss der Messtemperatur auf den Prozess der Ladungsträgertrennung wird hier an einer methylierten DCV4T-Verbindung in einer dünnen Schicht untersucht. Die bei photoinduzierter Absorptionsspektroskopie (PIA) beobachtete Aktivierung dieses Prozesses mit zunehmender Temperatur wird auf eine erhöhte Ladungsträgerbeweglichkeit zurückgeführt. Der dadurch erhöhte effektive Abstand der Ladungen an der Grenzfläche zwischen Donator (D) und Akzeptor (A) erleichtert die endgültige Trennung der Ladungsträger. Durch den Vergleich mit einer DCV6T-Verbindung wird der Zusammenhang zwischen der Aktivierungsenergie und der Beweglichkeit bekräftigt. Die kleinere Beweglichkeit äußert sich dabei in einer größeren Aktivierungsenergie. Darüber hinaus kann der Ladungsträgergenerationsprozess auch von der Molekülstruktur abhängen. In dieser Arbeit wird untersucht, wie sich die Länge von Alkylseitenketten auf die Energieniveaus der Moleküle, aber auch auf die Absorptions- und Lumineszenzeigenschaften der Materialien in reinen und in Mischschichten mit dem Akzeptor C60 äußert. Die ermittelten Unterschiede bezüglich der Molekülordnung (geordneter für kürzere Seitenketten) und der Phasengrößen in Mischschichten (größere Phasen bei kürzerer Kettenlänge) werden in der Untersuchung der Temperaturabhängigkeit der Lebensdauer von Triplettexzitonen mittels PIA-Messungen bestätigt. Für Solarzellen ist von Bedeutung, ob sich die Seitenkettenlänge auf die Wechselwirkung zwischen D und A auswirkt. Der vermutete Zusammenhang wird hier nicht bestätigt. Ein ähnlicher Photostrom für alle untersuchten Verbindungen in Solarzellen mit planaren Heteroübergängen unterstreicht diese Schlussfolgerung. Unterschiede im Wirkungsgrad werden auf Änderungen der Energieniveaus und die Morphologie in Mischschichtsolarzellen zurückgeführt. Des Weiteren wird in einer Machbarkeitsstudie der Einfluss des elektrischen Felds auf die Generationsausbeute freier Ladungsträger untersucht. Dafür werden halbtransparente Solarzellen verwendet, die es ermöglichen, PIA-Messungen in Transmissionsgeometrie durchzuführen. Als mögliche Erklärung für das Auftreten zweier Rekombinationskomponenten in der Analyse des Rekombinationsverhaltens der durch Licht erzeugten Ladungsträger werden eingefangene Ladungsträger und gebundene Ladungsträgerpaare an der D/A-Grenzfläche genannt. Das Mischverhalten von D und A kann durch ein Heizen des Substrates während des Verdampfungsprozesses eingestellt werden, was von entscheidender Bedeutung für eine weitere Steigerung des Wirkungsgrades ist. Für DCV4T:C60-Mischschichtsolarzellen wird jedoch eine Verschlechterung des Wirkungsgrads zu höheren Substrattemperaturen beobachtet. Durch optische Messungen und Methoden zur Schichtstrukturbestimmung wird dieser Effekt auf eine Umordnung der DCV4T-Kristallite für hohe Substrattemperaturen und die damit verbundene Verringerung der Absorption und damit auch des Photostroms zurückgeführt. Bei einer Substrattemperatur von 90° C sind die D- und A-Komponenten fast vollständig entmischt. Dieses Beispiel ist von besonderer Bedeutung, weil hier die Ursachen für ein Verhalten aufgezeigt werden, das entgegen den Beispielen aus der Literatur eine Abnahme des Wirkungsgrads beim Aufdampfen der aktiven Schicht auf ein geheiztes Substrat zeigt. Schließlich werden die Optimierungsschritte dargelegt, mit denen Solarzellen mit einer DCV5T-Verbindung als Donatormaterial auf einen Rekordwirkungsgrad von 7,7% gebracht werden. Dabei wird die Substrattemperatur, die Dicke der aktiven Schicht und die Transportschichten angepasst.:Abstract - Kurzfassung Publications Contents 1 Introduction 2 Elementary Processes in Organic Semiconductors 2.1 Introduction 2.2 Optical Excitations in Organic Materials 2.2.1 Introduction 2.2.2 Radiative Processes: Absorption and Emission 2.2.3 Non-radiative Relaxation Processes 2.2.4 Triplet Excitons and Intersystem Crossing 2.3 Polarization Effects and Disorder 2.4 Transport Processes in Disordered Organic Materials 2.4.1 Charge Transport 2.4.1.1 The Bässler Model 2.4.1.2 Marcus Theory for Electron Transfer 2.4.1.3 Small Polaron Model 2.4.1.4 Functional Dependencies of the Charge Carrier Mobility 2.4.2 Diffusive Motion 2.4.3 Exciton Transfer Mechanisms 2.4.4 Characteristics of Exciton Diffusion 2.5 Charge Photogeneration in Pristine Materials 3 Organic Photovoltaics 3.1 General Introduction to Solar Cell Physics 3.2 Introduction to the Donor/Acceptor Heterojunction Concept 3.3 The Open-Circuit Voltage in Organic Solar Cells 3.4 Doping of Organic Semiconductors 3.5 Introduction to the p-i-n Concept 3.6 Charge Transfer Excitons in Donor/Acceptor Heterojunction Systems 3.6.1 Introduction 3.6.2 Verification of Charge Transfer Excitons in Donor/Acceptor Systems 3.7 The Process Cascade for Free Charge Carrier Generation in Donor/Acceptor Heterojunction Systems 3.7.1 The Initial Charge Transfer Step 3.7.2 The Binding Energy of the Charge Transfer Exciton 3.7.3 \"Hot\" Charge Transfer Exciton Dissociation 3.7.4 \"Cold\" Charge Transfer Exciton Dissociation 3.7.5 Supposed Influence Factors on Charge Transfer Exciton Dissociation 3.7.6 Recombination Pathways for Charge Transfer Excitons 3.7.7 Free Charge Carrier Formation and Recombination 4 Experimental Methods 4.1 Sample Preparation 4.2 Material Characterization Methods 4.2.1 Optical Characterization 4.2.2 Cyclic Voltammetry 4.2.3 Ultraviolet Photoelectron Spectroscopy 4.2.4 Atomic Force Microscopy 4.2.5 Grazing Incidence X-Ray Diffraction 4.2.6 Organic Field-Effect Transistor 4.3 Photoinduced Absorption Spectroscopy 4.3.1 Introduction 4.3.2 Derivation of the PIA Signal 4.3.3 Recombination Dynamics 4.3.4 Intensity Dependence of the PIA Signal 4.4 Solar Cell Characterization 4.4.1 External Quantum Efficiency 4.4.2 Spectral Mismatch Correction 4.4.3 Current-Voltage Characteristics 4.4.4 Optical Device Simulations 4.4.5 Optical Device Transmission Measurements 5 The Oligothiophene Material System 5.1 Introduction 5.2 Thermal Stability 5.3 Energy Levels 5.4 Optical Properties of the Pristine Materials 5.5 The Donor/Acceptor Couple: DCVnT and C60 5.6 Solar Cell Devices 5.7 Summary 6 Temperature Dependence of Charge Carrier Generation 6.1 Introduction 6.2 Principal Introduction to the PIA Measurements 6.2.1 Interpretation of the Spectra 6.2.2 Interpretation of the Frequency Scans 6.3 Temperature Dependence of the Spectra 6.4 Discussion of the Temperature Dependent Processes in the Blend Layer 6.5 Temperature Activated Free Charge Carrier Generation 6.5.1 Evaluation of the Activation Energy for the DCV4T-Me:C60 Blend 6.5.2 Comparison to a Sexithiophene Derivative (DCV6T-Me) 6.6 Summary 7 Side Chain Investigation on Quaterthiophene Derivatives 7.1 Energy Levels 7.2 Optical Properties 7.2.1 Solution and Pristine Films 7.2.2 Mixed Films with C60 7.3 Influence of the Side Chain Length on the Intermolecular Coupling 7.3.1 PIA Spectra of Pristine and Blend Layers at 10K 7.3.2 Recombination Analysis for Pristine and Blend Films at 10K 7.4 The Influence of the Side Chain Length on the Offset Charge Carrier Generation Rate at Low Temperature 7.5 In the High-Temperature Limit: Implications for Solar Cell Devices 7.5.1 PIA Spectra in Pristine and Blend Films at 200K 7.5.2 Recombination Analysis: Triplet Excitons and Free Charge Carriers 7.6 Solar Cells 7.6.1 Flat Heterojunction Devices 7.6.2 Bulk Heterojunction Devices 7.7 Summary 8 Electric-Field Dependent PIA Measurements on Complete Solar Cell Devices 8.1 Introduction 8.2 Semitransparent Organic Solar Cells 8.3 Photoinduced Absorption Measurements 8.4 Summary and Outlook 9 The Effect of Substrate Heating During Layer Deposition on the Performance of DCV4T:C60 BHJ Solar Cells 9.1 Introduction 9.2 The Importance of Morphology Control for BHJ Solar Cells 9.3 The Impact of Substrate Heating on DCV4T:C60 BHJ Solar Cells 9.4 Absorption and Photoluminescence 9.5 Topographical Investigations (AFM) 9.6 X-ray Investigations 9.6.1 1D GIXRD Measurements 9.6.2 2D GIXRD Measurements 9.7 Proposed Morphological Picture and Confirmation Measurements 9.7.1 Morphology Sketch of the DCV4T:C60 Blend Layer 9.7.2 Confirmation Measurements 9.8 The Equivalence of Temperature and Time 9.9 Summary 10 Record Solar Cells Using DCV5T-Me33 as Donor Material 10.1 Introduction 10.2 The Influence of the Substrate Temperature 10.3 Determination of the Optical Constants 10.4 Stack Optimization 10.5 Summary and Outlook 11 Conclusions and Outlook 11.1 Summary of the Photophysical Investigations 11.2 Summary of Device Investigations 11.3 Future Challenges Appendix A Detailed Description of the Experimental Setup for PIA Spectroscopy Appendix B Determination of the Triplet Level by Differential PL Measurements Appendix C Additional Tables and Figures Appendix D Reproducibility of the Solar Cell Results (Statistics) Appendix E Lists Bibliography Acknowledgments

Organic solar cells (OSCs) based on non-fullerene acceptors (NFAs) have attracted a great deal of attention in recent years due to their rapidly increasing efficiency and enormous potential. In this work, the optical and electronic properties of systems containing the very promising non-fullerene acceptor PYT have been thoroughly studied with the use of the density functional theory (DFT) and the time-dependent density functional theory (TDDFT). By changing the electron linker from thiophene to furan and selenophene, respectively, the PYT was divided into three variants, each of which was studied independently. In addition, these three systems were combined with the donor PBDB-T to generate two distinct interface conformations. The properties studied in this work include the optimized geometries, HOMO-LUMO levels, UV-Vis spectra, frontier molecular orbitals (FMOs), natural transition orbitals (NTOs), density of states (DOS), dipole moments, open-circuit voltages, exciton binding energies, and local exciton (LE) and charge transfer (CT) energies. The calculations were performed in chlorobenzene solution utilizing the polarizable continuum model (PCM). It was discovered that PBDB-T/PY-Se exhibited remarkable flatness employing the π-π stacking conformation which corresponds well with the excellent D/A compatibility observed experimentally. All interfaces displayed appropriate positioning of the HOMO-LUMO levels, with the acceptor dominating the LUMO and the donor dominating the HOMO, with HOMO-LUMO gaps ranging between 1.34 and 1.38 eV. The differences in the interchanging of the electron linker were not that significant, and neither was the change in interface conformation in terms of the HOMO-LUMO levels. This may indicate that the system can be effective even without the presence of a π-π stacking conformation. The first excited states for all interface systems were shown to be pure CT transitions, and on average, 80% of the states exhibit CT character. The remaining contributions consisted of transitions within the pure materials, with a larger contribution within the acceptor. The theoretical results of this study indicate that systems containing the novel polymer acceptor PYT and its variants PY-O and PY-Se exhibit very intriguing properties, and further development of OSCs containing these polymers might further aid in the development of high-performance OSCs. / Organiska solceller (OSC) baserade på icke-fullerenacceptorer (NFA) har väckt stor uppmärksamhet de senaste åren på grund av dess snabbt ökande effektivitet och enorma potential. I detta arbete har de optiska och elektroniska egenskaperna hos system innehållande den mycket lovande icke-fullerenacceptorn PYT studerats grundligt med användning av täthetsfunktionalteorin (DFT) och den tidsberoende täthetsfunktionalteorin (TDDFT). Genom att ändra elektronförbindelsen från tiofen till furan respektive selenofen så delades PYT upp i tre varianter som var och en studerades oberoende av varandra. Dessutom kombinerades dessa tre system med donatorn PBDB-T för att generera två distinkta gränssnittskonformationer. Egenskaperna som studeras i detta arbete inkluderar optimerade geometrier, HOMO-LUMO-nivåer, UV-vis spektra, gränsmolekylära orbitaler (FMO), naturliga övergångsorbitaler (NTO), tillståndstäthet (DOS), dipolmoment, tomgångsspänning, excitonbindningsenergi samt lokal exciton (LE) och laddningsöverförings (CT) energier. Beräkningarna utfördes i klorbensenlösning med användning av den polariserbara kontinuummodellen (PCM). I resultatet uppvisade PBDB-T/PY-Se en anmärkningsvärd planhet med användning av π-π staplingskonformationen som överensstämmer väl med den utmärkta D/A-kompatibiliteten som observerats experimentellt. Alla gränssnitt visade lämplig positionering av HOMO-LUMO-nivåerna, med acceptorn som dominerade LUMO och donatorn som dominerade HOMO, med HOMO-LUMO-gap mellan 1.34 och 1.38 eV. Skillnaderna i utbytet av elektronförbindelsen visade sig inte vara signifikanta och inte heller skillnaden i gränssnittskonformation när det gäller HOMO-LUMO-nivåerna. Detta kan indikera att systemet kan vara effektivt även utan förekomst av π-π staplingskonformation. De första exciterade tillstånden för alla gränssnittssystem visade sig vara rena CT-övergångar och i genomsnitt uppvisade 80% av tillstånden CT-karaktär. Resterande andel bestod av övergångar inom de rena materialen med en större andel inom acceptorn. De teoretiska resultaten av denna studie indikerar att system innehållande den nya polymeracceptorn PYT och dess varianter PY-O och PY-Se uppvisar mycket spännande egenskaper samt att vidareutveckling av OSC:er som innehåller dessa polymerer ytterligare kan hjälpa till i utvecklingen av högpresterande OSC:er.

Thin metallic films with magnetic properties like magnetite are an interesting material in current technological applications. In the presented work the iron oxide films are grown by molecular beam epitaxy on MgO(001) substrates at temperatures between room temperature and 600K. The film and surface structure are investigated by x-ray reflectometry (XRR), x-ray diffraction (XRD) and low energy electron diffraction (LEED). The chemical properties are investigated by x-ray photoelectron spectroscopy (XPS). Furthermore, charge transfer multiplet (CTM) calculations are performed as a means to gain additional information from photoemission spectra. It is shown that only for temperatures higher than 500K the oxide film forms a spinel structure. A previously unobserved (2x1) surface reconstruction in two orthogonal domains is found for various preparation conditions. The application of CTMs results in good quantitative and qualitative agreement to other methods for the determination of the film stoichiometry. In addition CTMs can well describe the segregation of Mg atoms into the oxide film either during film growth or during film annealing. It is found that initially Mg substitutes Fe on all possible lattice sites, only for prolonged treatment at high temperature do Mg atoms favour the octahedral lattice sites of divalent Fe.