Made available in DSpace on 2016-12-08T15:56:18Z (GMT). No. of bitstreams: 1 Adilson Schackow.pdf: 13593160 bytes, checksum: 9e12d90fa2d30a305f04c4ad7adb4a6a (MD5) Previous issue date: 2015-07-14 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The search for sustainable, economic, social and technological development has intensified the study of the use of recycled materials or wastes in order to minimize environmental impacts and also to reduce production costs. In this sense this work aims to develop a methodology for the production of mortars optimized from the point of view of properties and cost, from particulate clay bricks waste (CBW) of red ceramic, as partial replacement of Portland cement. The first part of the study deals with the characterization of the as-prepared ceramic clay masses (CCM) and CBWs from four industries of the northern region of Santa Catarina: Ceramic A and B (Joinville/SC), Ceramic C (Garuva/SC) and Ceramic D (São Bento do Sul/SC). The characterization of ceramic clay masses included XRD, XRF, FTIR, DSC and SEM analyses. The characterization of CBW also included techniques to determine the pozzolanic activity, particle size, surface area (B.E.T.) and density. The consumption of calcium hydroxide (CH) of the cement paste formed with CBW was also measured. After analyzing the characteristics of the CCMs and CBWs it was possible to determine which of the researched sources has the greatest potential for use as a substitute for Portland cement. The results indicated that the CBW from industry B (CBW-B) has greater potential to react with CH, followed by CBWs from industries A, C, and D. Fractional factorial design techniques for the design and analysis of experiments were used to evaluate the performance of each CBW in properties such as consistency and compressive strength (CS) of mortars and determine the influence of these three factors on properties: CBW content in replacement of cement (10, 25 and 40% by weight), water-cement ratios (W/C of 2.50, 2.85 and 3.2) and fineness of the CBW (125, 75 and 45 μm). It could be concluded that the CBW-B had the best performance to compressive strength (4.28 MPa) starting from a consistency index of about 260 mm. This result was obtained for a 14 replacement of 15% of cement by CBW-B, and a W/C of 2.5 (75 μm fineness). It was also possible to identify mixtures with minimized financial costs through numerical optimization. To give sequence to work, the CBW-A was chosen (since it presents results comparable to those of the CBW-B, because the industry A generates the largest amount of waste, and because it leads to a larger usage of waste, which is also interesting from the environmental point of view) to a series of other tests, to evaluate the effect of CBW-A on properties such as: consistency; setting time; water retention; porosity and water absorption; water absorption by capillarity; compressive strength at 28 and 90 days (CS28 and CS90); resistance to sodium chloride and sulfate; natural carbonation and tensile bonding strength. Unlike the factorial design, in the mixtures in this next research stage only the CBW-A content was varied (0, 10, 25 and 40% by weight).The W/C and CBW fineness factors were kept constant. The use of the CBW-A revealed positive effects on several physical properties such as increased water retention, increased CS28 and CS90, and decreased porosity and water absorption. However, it had a negative effect on the durability of the mortars (attack by sulfates), tensile bonding strength and setting time, but not so far as to make it impossible to use. The microstructures of mortars and pastes were also analyzed by SEM images and EDX. The mortars containing CBW-A showed a denser cement matrix due to CH consumption and additional formation of calcium silicate hydrate (C-S-H), evidencing the pozzolanic effect of the waste. Thus, the methodology followed in this work, aimed at identifying optimized mortars containing brick waste, in terms of cost and properties, provided the criteria for the selection of waste and its effects on the properties studied, from the origin to the final product. / A busca pelo desenvolvimento sustentável, econômico, social e tecnológico tem intensificado o estudo da utilização de materiais reciclados ou rejeitos na tentativa de minimizar impactos ambientais e também de reduzir custos de produção. Neste sentido este trabalho tem o objetivo de desenvolver uma metodologia para a produção de argamassas otimizadas, do ponto de vista das propriedades e custo, a partir de rejeitos particulados de tijolos (RPT) de cerâmica vermelha, em substituição parcial ao cimento Portland. A primeira parte do estudo trata da caracterização das massas cerâmicas argilosas in natura (MCA) e dos RPTs de quatro empresas da região norte de Santa Catarina: Cerâmica A e B (Joinville/SC), Cerâmica C (Garuva/SC) e Cerâmica D (São Bento do Sul/SC). A caracterização das massas cerâmicas argilosas in natura foi realizada através das técnicas de DRX, FRX, FTIR, DSC e MEV. Na caracterização dos RPTs utilizaram-se ainda técnicas para determinação da atividade pozolânica, granulometria, área superficial (B.E.T.) e massa específica. O consumo de hidróxido de cálcio (CH) da pasta cimentícia formada com RPTs também foi medido. Após a análise das características das massas cerâmicas argilosas in natura e dos RPTs foi possível determinar qual das fontes pesquisadas de rejeito possui o maior potencial para uso como substituto ao cimento Portland. Os resultados indicaram que o RPT da empresa B (RPT-B) possui maior potencial para reatividade com o CH, seguido pelos RPTs das empresas A, C, e D. Foram utilizadas técnicas de planejamento fatorial fracionado para o projeto e análise dos experimentos para medir o desempenho de cada RPT em propriedades como resistência à compressão (RC) e consistência de argamassas, visando avaliar a influência de três fatores nessas propriedades: teor de RPT em substituição ao cimento (10, 25 e 40 %, em massa), relações água-cimento (W/C, de 2,50, 2,85 e 3,2), e finura do RPT (125, 75 e 45 μm). Pôde-se concluir que o RPT-B obteve o melhor desempenho para resistência à compressão (4,28 MPa) considerando um índice de consistência de cerca de 260 mm. Esse resultado foi encontrado para uma substituição de 15% de 12 cimento por RPT-B, e para um fator W/C de 2,5 (finura de 75 μm). Foi possível também identificar misturas com custo financeiro minimizado a partir de otimização numérica. Para dar sequência ao trabalho, foi escolhido o RPT-A (por apresentar resultados comparáveis com os do RPT-B, porque a empresa A gera a maior quantidade de rejeitos, e porque a sua utilização requer um maior consumo de rejeito, o que também é interessante do ponto de vista ambiental) para uma série de outros ensaios, visando avaliar o efeito do RPT-A em várias propriedades, tais como: consistência; tempo de pega; retenção de água; porosidade aparente e absorção de água; absorção de água por capilaridade; resistência à compressão aos 28 e 90 dias (RC28 e RC90); resistência ao cloreto e ao sulfato de sódio; carbonatação natural e resistência de aderência à tração. Diferentemente das misturas do projeto fatorial, as misturas desta outra fase da pesquisa tiveram apenas o teor de RPT-A variado (0, 10, 25 e 40 %, em massa). Os fatores W/C e finura do RPT permaneceram fixos. O uso do RPT-A revelou efeitos positivos sobre várias propriedades físicas como o aumento da retenção de água, aumento da RC28 e RC90, diminuição da porosidade e da absorção de água. Entretanto, causou um efeito negativo na durabilidade das argamassas (ataque por sulfatos), na aderência e no tempo de pega, mas não ao ponto de inviabilizar o seu uso. As microestruturas das argamassas e pastas também foram analisadas através de imagens MEV e EDS. As argamassas contendo RPT-A apresentaram uma matriz cimentícia mais densa devido ao consumo de CH e a evidenciando o efeito pozolânico do rejeito. Assim, a metodologia desenvolvida neste trabalho, visando a obtenção de argamassas contento rejeitos de tijolos, otimizadas em termos de propriedades e custo, forneceu os critérios para a seleção dos rejeitos e seus efeitos nas propriedades estudadas, desde a origem até o produto final.

Made available in DSpace on 2014-12-17T14:57:38Z (GMT). No. of bitstreams: 1 ElianaMC.pdf: 1221443 bytes, checksum: c2ecaef1ae772fb4d8e14dd13d82d037 (MD5) Previous issue date: 2007-06-02 / The potential market of the metropolitan area of Salvador accounts for the estimated consumption of roughly 800 million horizontally perforated extruded clay bricks a year. The growing demand of consumers along with the competitiveness of the structural ceramic sector has driven forward a number of recent efforts and investments towards improving the quality of structural ceramics. In this scenario, the present study focused on sampling and evaluating the conformity of 8-hole horizontally perforated extruded clay bricks manufactured by different plants (A, B and C) in the metropolitan area of Salvador. In addition, representative clay and sandy-clay materials were collected from each plant and characterized by conventional physical, chemical and mineralogical techniques. Finally, experimental compositions designated as A, B and C, according to the source, were prepared by mixing different contents of the raw materials collected in the plants, fired at different temperatures and characterized. The results revealed a series of non conformities regarding ABNT guidelines. The characterization of raw materials revealed the presence of kaolinite and ilite in concentrations ranging from 64 to 90 wt.% along with free quartz (10 - 25%). The sandy-clay samples consisted basically of kaolinite. All raw materials depicted low contents of organics, amorphous constituents, alkaline oxides and feldspar. An analysis of the firing behavior of all different ceramic compositions revealed that the linear contraction of composition A was rather significant considering the temperature range evaluated, and it justifies the significant dimensional non conformity that was shown by bricks made with the ceramic A / O mercado potencial de cer?mica estrutural na regi?o metropolitana de Salvador ? respons?vel pelo consumo de mais de 800 milh?es de pe?as/ano. Com um com?rcio cada vez mais exigente e competitivo torna-se necess?rio que as ind?strias ceramistas invistam em a??es que visem aperfei?oar a qualidade de seus produtos. O objetivo desse estudo foi avaliar o ?ndice de conformidade de blocos cer?micos e caracterizar a mat?ria-prima. Foram empregadas as normas ABNT para an?lise de conformidade de blocos cer?micos em tr?s ind?strias (A, B e C) da Regi?o Metropolitana do Salvador, bem como t?cnicas para caracteriza??o qu?mica, f?sica e mec?nica das mat?rias-primas e formula??o e an?lise das massas. Com base nos resultados alcan?ados pode-se concluir que os blocos cer?micos fabricados pelas ind?strias pesquisadas n?o apresentam conformidade com as normas t?cnicas brasileiras. Os argilominerais encontrados nas mat?rias-primas estudadas (massas A, B e C) foram a caulinita e a ilita que ficaram entre 64 a 90% e o teor de quartzo livre entre 10 e 25%. Os arenosos s?o predominantemente argilas caulin?ticas. Os materiais caracterizados apresentaram baixa concentra??o de materiais amorfos, baixo teor de ?xidos alcalinos e, conseq?entemente, concentra??es muito baixas de feldspatos. A an?lise das curvas de gresifica??o das massas demonstra que a inclina??o da curva de retra??o linear ? mais acentuada para a massa A, na faixa de temperatura estudada, e justifica a significativa n?o conformidade dimensional verificada nos blocos produzidos pela cer?mica A

A alvenaria estrutural é um dos mais antigos sistemas construtivos existentes. Atualmente estruturas em alvenaria encontram uma vasta aplicação em construções residenciais, sobretudo em obras de interesse social. No entanto, ao contrário das estruturas de concreto, cujo comportamento durante exposição ao fogo e sua resistência residual tem estudos e resultados amplamente disseminados, pouco se sabe a respeito do comportamento de estruturas de alvenaria submetidas à ocorrência de sinistros dessa natureza. Com a intensificação das preocupações acerca da segurança das edificações e de seus usuários em situações de incêndio, faz-se cada vez mais imprescindível o conhecimento do comportamento dos sistemas empregados atualmente na construção civil perante a ação de altas temperaturas. Tendo isso em vista, o presente trabalho teve por objetivo a realização de uma análise dos danos e do comportamento apresentados por amostras de alvenaria com função estrutural ao serem expostas ao aquecimento excessivo. Foram avaliadas nesse estudo paredes de pequenas dimensões executadas com blocos estruturais cerâmicos. Visando simular condições mais próximas da realidade, foram restringidas, com o auxílio de macacos hidráulicos, as laterais das amostras, para que houvesse contenção da dilatação das mesmas. Com o intuito de verificar diferentes tipologias de alvenarias, foram utilizados três blocos distintos: de 14 cm de largura, com resistências de 7 e 10 MPa, e de 19 cm de largura, com 7 MPa de resistência à compressão. Também foram variadas as espessuras das juntas entre as unidades e a argamassa de assentamento das mesmas, a fim de compreender a importância desses fatores para o comportamento das amostras, e, por fim, foram ensaiadas amostras com revestimento na face exposta As miniparedes foram acopladas a um forno de resistências elétricas e submetidas a um aquecimento próximo à curva padrão determinada por norma, até a temperatura máxima de 950ºC, a qual foi mantida pelo período de 4 horas. Foram mensurados, além da temperatura dentro do forno, no interior da parede e na superfície das amostras, os deslocamentos transversais ocorridos durante o ensaio. Também se utilizaram transdutores de deslocamento para verificar a dilatação dos blocos e o esmagamento ou abertura das juntas. Imagens termográficas da face oposta ao aquecimento foram capturadas no decorrer da exposição. Ao final das análises, pôde-se inferir que as miniparedes ensaiadas apresentaram bom desempenho frente à ação das altas temperaturas, mantendo sua estanqueidade, isolamento térmico e resistência mecânica. A restrição lateral não ocasionou desplacamentos dos blocos, no entanto, pôde-se observar transferência de tensão para os mesmos quando utilizadas nas juntas argamassas pouco flexíveis. O deslocamento transversal apresentado pelas amostras indicou deflexão em direção ao forno durante o aquecimento, com posterior reversão do sentido. Tal deflexão foi atenuada pela redução da espessura das juntas, pelo uso de argamassas menos flexíveis e pelo aumento da resistência e largura dos blocos. As alvenarias de 19 cm de largura e, especialmente, as dotadas de revestimento apresentaram melhor desempenho térmico que as demais. / Structural masonry is one of the oldest existing building systems. Nowadays, masonry structures find a wide application in residential constructions, mainly in those with social interest. However, unlike concrete structures, whose behavior during fire exposure and its residual resistance have widely disseminated studies and results, there is a lack of knowledge about the behavior of masonry structures submitted to fire. Because of the spread of concerns about the safety of buildings and their users in fire situations, it becomes essential to know the behavior of the systems currently used in civil construction when exposed to high temperatures. With this in view, the present study intended to analyze the damage and the behavior of structural masonry samples exposed to heating. This study evaluated clay hollow-bricks small walls, and, in order to simulate real conditions, the boundaries of the samples were restrained, with the aid of hydraulic jacks, aiming to restrain the deformation. In order to verify different types of masonry, three different blocks were used: 14 cm wide, with nominal strength of 7 and 10 MPa, and 19 cm wide, with 7 MPa of compressive strength. The thicknesses of the joints and the mortar were also varied, in order to understand the importance of these factors in the behavior of the samples, and, finally, samples were tested with a mono-layer coating at the exposed face. The small walls were coupled to an electrical furnace and subjected to a heating approximately equal to the standard curve, up to the maximum temperature of 950ºC, which was maintained for 4 hours The deflections of the samples during the test were measured, beyond the temperature inside the furnace, in the center of wall and at the non-exposed surface. Clip gages were also used to verify the expansion of the blocks and the crushing or opening of the mortar joints. Thermographic images of the opposite face were captured during the testing. At the end of this research, it was possible to affirm that the walls had good behavior against the high temperatures, maintaining their integrity, thermal insulation and load-bearing capacity. The restriction of the boundaries did not cause the spalling of the blocks, however, it was possible to observe the stress transfer to them in samples with rigid joint mortar. The deflection of the samples increases towards the furnace during the heating, and, then, they show the phenomenon of “reverse bowing”, changing the direction of the displacements. Reducing the thickness and increasing the stiffness of the joint mortars, as well as the increase in block strength and width attenuated such deflection. The masonry 19 cm width and, specially, the ones with coating shows better thermal performance, comparing to the others.

No contexto do crescimento do processo construtivo em alvenaria estrutural, destaca-se o uso do bloco cerâmico consolidado com a criação de sua norma específica de projeto, execução e controle de obras, a NBR 15812, partes 1 e 2 (ABNT, 2010). Desde a difusão da alvenaria estrutural, mudanças nas técnicas construtivas vêm ocorrendo, como por exemplo, o não preenchimento das juntas verticais de assentamento dos blocos. Outra prática que tem sido utilizada é o grauteamento da alvenaria. No entanto, ainda não está estabelecido se o não preenchimento da junta vertical compromete o desempenho da alvenaria ou qual a resistência necessária ao graute para aumentar a resistência da alvenaria. Diante disto, o trabalho objetiva contribuir com o estudo do não preenchimento das juntas verticais avaliando o seu efeito na resistência à compressão e ao cisalhamento de pequenas paredes e também pesquisar a influência do graute em prismas e pequenas paredes submetidos à compressão. Com as análises dos resultados pode-se concluir que o não preenchimento das juntas verticais não exerceu influência nos valores de resistência à compressão e também nos módulos de elasticidade longitudinal das pequenas paredes ensaiadas. No entanto, influenciou significativamente os resultados do ensaio de compressão diagonal para avaliar a resistência ao cisalhamento, apesar do módulo de deformação transversal ter sido considerado equivalente. Os resultados do estudo preliminar em prismas mostraram que a média da resistência à compressão em relação à área bruta do prisma grauteado, utilizando o Graute A e o Graute C, foi equivalente à média do prisma oco. Assim, foi escolhido o Graute A para a confecção de pequenas paredes e prismas. Pode-se concluir com os resultados das pequenas paredes grauteadas que houve um aumento significativo da resistência à compressão em relação à área bruta, mas em relação à área líquida, os valores encontrados foram equivalentes às pequenas paredes ocas. Portanto o aumento na resistência à compressão na pequena parede foi proporcional ao ganho de área dado pelo grauteamento de seus vazios, diferentemente do comportamento observado nos prismas. / In the context of growth of structural masonry construction process, it highlight the use of the ceramic block consolidated with the creation of its specific standard of design, execution and control, the NBR 15812, Parts 1 and 2 (ABNT, 2010). Since the propagation of structural masonry, changes have occurred in the construction techniques, such as don\'t fill the vertical joints of the masonry wall. Another technique that has been used is the grouted masonry. However, it is not yet established if the unfilled vertical joints compromise the performance of masonry or which strength is necessary to the grout to increase the strength of the masonry. Therewith, the paper aims to contribute to the study of unfilled vertical joints by analyzing its effect on compressive strength and shear strength of small walls and also investigate the influence of grout in prisms and small walls under compression. With the analysis of the results we can conclude that do not fill the vertical joints had no influence on the values of compressive strength and elastic modulus of the small walls tested. However, it significantly affects the results of the diagonal compression test to evaluate shear strength, despite the shear elastic modulus being considered equivalent. The results of the preliminary study in prisms showed that the average of the compressive strength in relation to the gross area of the grouted prism using the Grout A and the Grout C were equivalent to the average of hollow prism. Thus, small walls and prisms with the Grout A were made. It can be concluded with the results of grouted small walls that there was a significant increase in compressive strength with respect to the gross area, but in relation to the net area, were similar to the hollow small wall. Therefore the increase in the compressive strength in a small wall is proportional to the gain of the area given by the grout, unlike the behavior observed in the prisms.

This essay focuses on the topics of sexism and the function of gender and oppression in Monica Ali’s Brick Lane. Instances in the novel are related to real world incidents in order to show how Ali, in spite of her Western upbringing and perspective, has accurately depicted several problematical cases of injustice in Muslim culture. Even though Ali has been criticized for her, supposedly, incorrect portrayal of Bangladeshis in London, this essay will argue that the topics of the novel remain relevant in the larger scheme of Muslim society.

Les fines de lavage de carrières sont à l’heure actuelle peu valorisées. Pourtant, leurs caractéristiques physiques font de ces fines une matière première intéressante pour le domaine de la construction. L’objectif de cette thèse est de développer la formulation de produits préfabriqués non porteurs à base de fines de lavage, en considérant ces fines comme de la terre crue. Deux catégories de produits préfabriqués sont visées : un produit dit « lourd » (brique de terre comprimée) et un produit « léger » (carreau). Pour la valorisation en BTC, une étude de compacité par essai Proctor a permis de cibler la teneur en eau de fabrication et la masse volumique sèche à obtenir. Les performances mécaniques des briques ont été améliorées par surcompactage, renforcement granulaire et traitement au liant hydraulique. L’étude de formulation du carreau a associé les fines de lavage et la chènevotte. La consistance des mélanges à l’état frais a été étudiée avec le consistomètre VEBE. Les performances mécaniques en flexion et en compression des mélanges fibrés ont été mesurées. De la chaux et un superplastifiant ont été ajoutés dans la formulation pour satisfaire aux conditions de tenue mécanique. Les deux voies de valorisation ont été validées par mesures des performances physico-mécaniques sur produits fabriqués à l’échelle industrielle. La formulation optimale de BTC valorise près de 80% de fines de lavage et se classe dans la catégorie BTC 40 de la norme expérimentale XP13-901 (brique faiblement capillaire et résistante à la projection en eau). La formulation optimale de carreau se compose de 60% de fines de lavage, et répond aux exigences mécaniques des carreaux de plâtre. / Currently, few re-use ways are developed with clay fines from washing units in quarries. However, these clayey fines represent interesting materials for construction domain. This research work aims to develop non-load bearing precast products and to re-use these fines without thermal treatment as for unfired clay products. Two types of precast products are wished: a “heavy” product (compressed earth brick) and a “light” product (tile hemp-clay).For the CEB re-use way, the level of compaction has to be high. Proctor tests have been done to define the moisture content and dry density to obtain. Mechanical performances of bricks have been increased by overcompaction, granular reinforcement and lime treatment.For the tile re-use way, mixes with quarry fines and hemp have been studied. The behaviour of fresh material has been studied with VEBE consistometer. Flexural and compression strengths have been measured on hardened mixes. Lime and water-reducing agent have been necessary for a good mechanical behaviour.The two re-use ways have been validated by measuring mechanical and physical performances of products manufactured at industrial scale. The optimal mix for CEB includes almost 80% of quarry fines. The CEB is classed in BTC40 category according to experimental standard XP13-901 (brick with a low water absorption level and resistant to water spray). The optimal mix for tile includes 60% of quarry fines and satisfies mechanical requirements for gypsum blocks.

Made available in DSpace on 2016-07-18T17:46:23Z (GMT). No. of bitstreams: 1 Resumo.pdf: 12526 bytes, checksum: df6cf084d4a63552ea7bebde6c4b1dd4 (MD5) Previous issue date: 2016-05-13 / The environmental impact problem of solid waste generated by consumption is the responsibility of every citizen. Respect for the law and protecting the environment is part of the environmental management process for the benefit of society and future generations. In this context, resolution should be sought alternatives and / or minimize this problem. This work aims to study the manufacture and structural characterization of ecological bricks of adobe type using as ultisol matrix and oxisol the Pontal do Paranapanema region and recyclable materials from the selective collection, construction and sugar industry (plaster, PET, EPS, vinasse) for potential application in sustainable housing. The methodology involved the study: physical characterization of the raw material (grain size, proctor-normal permeability test and chemical analysis of vinasse), the manufacturing process of ecological bricks and physical characterization (mechanical compression, water absorption, dry density, moisture content, behavior, stress / strain, acoustic behavior, temperature resistance, thermal analysis, electronic microscopy, mass comparison and compressive strength of the manufactured bricks) and recycling of green bricks (grain size and reuse). ecological bricks were obtained with different traits containing ultisol or oxisol, plaster, PET, EPS, vinasse and lime. Among the lines manufactured with ultisol only 2A trait and oxisol only 2L trait attended NBR 8492/12. The result of the physical characterization ecological bricks made in the above traits indicate that viability in the manufacture of green bricks with the proposed recyclable materials, and are potential for use in sustainable buildings. / O problema de impacto ambiental dos resíduos sólidos gerados pelo consumo é de responsabilidade de todo o cidadão. O respeito à legislação e à proteção do meio ambiente faz parte do processo da gestão ambiental em benefício da sociedade e das futuras gerações. Neste contexto deve se buscar alternativas de resolução e/ou minimização deste problema. Este trabalho tem como objetivo estudar a fabricação e caracterização estrutural de tijolos ecológicos do tipo adobe utilizando como matriz argissolo e latossolo da Região do Pontal do Paranapanema e materiais recicláveis da coleta seletiva, construção civil e indústria canavieira (reboco, PET, EPS, vinhaça) para potencial aplicação em habitações sustentáveis. A metodologia empregada envolveu o estudo: da caracterização física da matéria prima (granulometria, proctor-normal, ensaio de permeabilidade e análise química da vinhaça), do processo de fabricação dos tijolos ecológicos, bem como da caracterização física (compressão mecânica, absorção hídrica, densidade seca, teor de umidade, comportamento tensão/deformação, comportamento acústico, resistência à temperatura, análise térmica, microscopia eletrônica de varredura, comparação de massa e resistência à compressão dos tijolos fabricados) e da reciclagem dos tijolos ecológicos (granulometria e reaproveitamento). Foram obtidos tijolos ecológicos com diferentes traços contendo argissolo ou latossolo, reboco, PET, EPS, vinhaça e cal. Dentre os traços fabricados com argissolo apenas o traço 2A e com o latossolo apenas o traço 2L atenderam a NBR 8492/12. Os resultados da caracterização física dos tijolos ecológicos fabricados nos traços citados indicam que há viabilidade na fabricação dos tijolos ecológicos propostos com os materiais recicláveis, bem como são potenciais para serem utilizados em construções sustentáveis.

Tegeltillverkning har i industriell form funnits på Gotland i över 100 år. Mellan 1903–1970 fanns det ett Tegelbruk i Havdhem som kom att dominera den gotländska marknaden. Tegelproduktionens utveckling övertid har lokalt speglat hur det har sett ut nationellt men i mindre skala. Den har även påverkats mycket av den lokala näringsutvecklingen. Havdhems tegelbruk startades på samhällsaktörers initiativ för att hjälpa det ökade behovet av tegelrör för täckdikning. Tegelrören kom att bli den viktigaste produkten för bruket som även tillverkade murtegel, håltegel och fasadtegel. Tegelbrukets produktionsvolym under dess glansperiod låg på 3 miljoner per år och hade 25 årsanställda. Den centrala orsaken till brukets nedläggning var en kraftig brand i december 1970.   Havdhemsteglet bestod av en lera med låg järnoxidhalt vilket resulterade i ett ljusrött tegel. Leran hämtades lokalt från tre olika lertag. Bruket har tillverkat både rött och gult tegel och har köpt in råmaterial för att påverka färgen. Ett av byggnadsverken som stoltserar med Havdhemstegel är Visby vattenledningstorn som byggdes 1925. Vattenledningstornet är byggt med det för Havdhem typiska ljusröda teglet. / Brick manufacturing in industrial form has been used on Gotland for over 100 years. Between 1903 and 1970, there was a tilery in Havdhem, in the south of Gotland, that came to dominate the Gotlandic market. The brick productions development has locally reflected how it has looked nationally but on a smaller scale. The brick industry has also been influenced by the local business development. Havdhems tilery was started through community-active initiatives to help increase the need for brick pipes for field drainage. The brick pipes became the most important product for the factory. The tilery also manufactured several different kinds of bricks. The tilery’s production volume during its high period was 3 million per year and had 25 full-time employees. The central reason for the closure of the factory was a severe fire in December 1970.   Havdhems bricks consisted of a clay composition with a low iron-oxide content which creates a lighter red brick. The clay was sourced locally from three different clay quarries. The factory has manufactured both red and yellow bricks and has purchased raw materials to influence the color. One of the buildings that boasts Havdhems clay bricks is the Visby water conduit tower, which was built in 1925. The water conduit tower was built with the representative light red brick.

This thesis describes the design and solution of the object for education of preschool aged children The nursery school situated in Ostrava consists of two classes, each with capacity of 20 children. Outdoor playground and parking lots for visitors and employees are included in the project. Building is designed as double-storeyed with partial basement and with extensive green roof. Floor plan is irregular, corresponds to few slipped (blended?) rectangles. Walls are made of ceramic blocks, ceilings is made of precast cencrete panels Spiroll.

Diploma thesis deals with structural design of new building for retirement people in Rychnov nad Kněžnou. The building has three floors with partial basement. There are nursing spaces, dining room with kitchen, chemist´s shop, surgery, hairdresser´s, pedicure and massage on the first floor. The second floor is used for accomodation, nursing services and there is terrace. The third floor is used for accomodation and social activities. The technical facilities, storage spaces and bicycle rooms are in basement. The structural masonry system is with Ytong blocks. The building has warm flat roof.